Large spontaneous Hall angle in [Co,CoFe/Pt] multilayer

We have quantitatively investigated the Hall effect in [Co, CoFe/Pt] multilayer films. The [Co, CoFe/Pt] multilayers exhibit large spontaneous Hall resistivity (ρ_H) and Hall angle (ρ_H/ρ). Even though the Hall resistivity in [Co, CoFe/Pt] multilayer films (2.7–4 × 10⁻⁷ Ω cm) is smaller than that of amorphous RE–TM alloy films which show large spontaneous Hall resistivity (<2 × 10⁻⁶ Ω cm), the Hall angle of multilayer (6–8%) is almost twice than that in amorphous rare earth–transition metal alloy films (∼3%). The Hall angle provides evidence of the effects of the exchange interaction of the Hall scattering. The exchange is between conduction electron spins and the localized spins of the transition metal. The large Hall angle of [Co, CoFe/Pt] multilayer can be considered due to the high spin polarization and high Curie temperature of Co and CoFe transition metal layers. Even though the role of interfaces and surfaces in the magnetic properties of multilayer films may dominate that of the bulk, the Hall effects in [Co, CoFe/Pt] multilayer may be mainly dominated by the bulk effect.     

Magnetization reversal in [Ni/Pt]6/Pt(x)/[Co/Pt]6 multilayers

The magnetization reversal is studied in magnetron sputtered artificial superstructures of the form [Ni/Pt]₆/Pt(x)/[Co/Pt]₆ with perpendicular anisotropy, in which the [Co/Pt]₆ stacks have higher coercivity than the [Ni/Pt]₆. For x≥2 nm the two stacks reverse separately and exhibit characteristic stepped loops with a “plateau” in the region between the two switching fields. First-Order Reversal Curves (FORCs) reveal that the maximum coupling is obtained for x=1.5 nm. While each of the Ni/Pt and Co/Pt stacks by itself is thin enough to reverse in large domains when they are coupled, formation of maze like domains is observed. In this case some reversibility of the demagnetization curves associated with interfacial domain wall pinning appears while in the rest of the cases the reversal mechanism is based on lateral domain wall pinning with low reversibility. In the loops monitored by Extraordinary Hall Effect (EHE) measurements this “plateau” appears as a hump due to the different sign of the EHE coefficient between the [Ni/Pt]₆ and [Co/Pt]₆.     

Magnetic field dependence of asymmetry in the magnetization reversal of ultrathin Co films and Co/Pt multilayers with perpendicular anisotropy

We studied the magnetization reversal in ultrathin [Co/Pt]_n films (n=1, 2, and 4) using magneto-optical Kerr microscopy. These materials demonstrate unusual asymmetries in the activity of nucleation centers and domain wall motion. It was found that application of very high holding magnetic field prior to magnetization reversal, exceeding some critical value much larger than the apparent saturation field, suppresses the subsequent ‘asymmetric’ nucleation centers, activity. We revealed that the ‘asymmetric’ nucleation centers become active again after subsequent reversal cycles coming from a smaller holding field and studied how the asymmetry returns with the decrease of applied holding field. It was found that in low-coercivity ultrathin Co films, the asymmetry in domain wall velocity decreased sharply with the applied field increase and disappeared when the reversal field is greater than μ₀H=1.5 mT.     

Measurement of the nucleation and domain depinning field in a single Co/Pt multilayer dot by Anomalous Hall effect

Co/Pt multilayer dots with perpendicular anisotropy and with diameters of 250 and 350 nm were fabricated on top of a Hall cross configuration. The angular dependence of the magnetic reversal of the individual dot was investigated by Anomalous Hall effect measurements. At near in-plane angles (85° with the magnetic easy axis) the dot switches partially into a stable two-domain state. This allows for separate analysis of the angular dependence of both the field required for nucleation of a reversed domain, and the field required for depinning of the domain wall. The angular dependence of the depinning field fits accurately to a 1/cos(θ) behavior, whereas the angular dependence of the nucleation field shows a minimum close to 45°. The latter dependency can be accurately fitted to the modified Kondorsky model proposed by Schumacher [1].     

Competition between domain walls and the reverse magnetization in the magnetic relaxation of a Pt/Co/Ir/Co/Pt spin switcher

A multilayer Pt/Co/Ir/Co/Pt/GaAs heterostructures demonstrates a long term (to several hours) magnetic relaxation between two stable states of the magnetization of the system. The magnetization reversal of the heterostructure layers occurs both due to the formation of nuclei of the reverse magnetization domains and as a result of their further growth by means of motion of domain walls. The competition between two these processes provides a nonexponential character of the magnetic relaxation. At 300 K, the contributions of these processes to the relaxation are commensurable, while, at temperatures lower than 200 K, the contribution of the nucleation is suppressed and the magnetic relaxation occurs as a result of motion of the domain walls.     

Dependence of Interlayer AF Coupling on Ferromagnetic Layer Thickness in [Pt/Co]5/Ru/[Co/Pt]5 Multilayers

We study magnetization reversal in the interlayer coupled [Pt/Co]5/Ru/[Co/Pt]5 multilayers （MLs） by means of the measurement of extraordinary Hall effect （EHE）. Fitting experimental data to a simple model, we determine the interlayer coupling strength for various thicknesses of the ferromagnetic layers at a fixed Ru spacer thickness. It is found that the dependence of interlayer coupling strength on the Pt layer thickness is much stronger than the previous report in the ferromagnetic/nonmagnetic/ferromagnetic multilayers.     

Investigation of ferromagnetic coupling between Co layers in a Co/Pt multilayer with perpendicular anisotropy

The coercivity of a Co/Pt multilayer with out-of-plane anisotropy can be lowered greatly if it is grown onto an ultrathin NiO underlayer . By making use of this characteristic, a series of samples glass/NiO(10 Å)/[Co(4 Å)/Pt(5 Å)]₃/Pt(x Å)/[Co(4 Å)/Pt(5 Å)]₃ with different Pt spacer thickness have been prepared to determine the ferromagnetic (FM) coupling between Co layers across the Pt layer. The measurements of major and minor hysteresis loops have shown that the FM coupling between the top and bottom Co/Pt multilayers decreases monotonically with the Pt layer thickness and disappears above the Pt layer thickness of 40 Å. This thickness of 40 Å is much larger than that in the literature. In addition to the FM coupling between the top and bottom Co/Pt multilayers across the Pt spacer, there exists a weak biquadratic coupling, which induces the broad transition of the bottom Co/Pt multilayer.     

Magnetization reversal and domains structures in (Co/Ni/Co/Pt) multilayers

Multilayers of [Co/Ni(t_Ni)/Co/Pt]_×4 are investigated for different Ni insertion layer thicknesses. The resulting magnetic properties and magnetic domain structures are compared with [Co/Ni]_×8 multilayers. As determined by magneto-optical Kerr effect microscopy and a vibrating sample magnetometer measurements, all multilayers exhibited a perpendicular magnetic anisotropy. It is found that the nucleation field and magnetic coercivity of [Co/Ni(t)/Co/Pt]_×4 multilayers are lower than (Co/Ni)_×8 and decreased with Ni thickness. Magnetization decay measurements reveal that these multilayers did not show an exponential decay behavior as was observed in rare earth transition metal alloys. Very narrow wires will remain stables for several hours even with an applied magnetic field closer to the coercivity. Insertion of very thin Ni in (Co/Pt) multilayers offers a good way to optimize the magnetic properties of the material and adjust the domain size for nanowire-based devices.     

Defects mediated diffusion in Pt/Co/Pt multilayers induced by dense electronic excitations

Present study compares the effects of 200 MeV Ag¹⁵⁺ and 100 MeV O⁷⁺ ion irradiations on the structural, interfacial mixing and magnetic properties of annealed Pt/Co/Pt layers fabricated by DC magnetron sputtering. X-ray diffraction analysis shows that ion irradiations coupled with post annealing results in the formation of the face centred tetragonal L1₀ CoPt phase. Irradiation using 200 MeV Ag¹⁵⁺ ions having higher ionizing energy transfer to the film was found to be more efficient in causing structural phase transition as compared with that using 100 MeV energy O⁷⁺ ions having lower ionizing energy transfer at similar fluence. Rutherford back scattering analysis reveals the role of defect mediated inter-atomic diffusion in tailoring the alloy composition of the film irradiated by different energetic ions. A broad magnetic switching field distribution for O⁷⁺ ion irradiated films compared to Ag¹⁵⁺ ion irradiation was evident from the magnetic measurements. The contribution of alloy composition to switching field distribution has been discussed in details. Above results showed that the electronic energy loss and fluence dependent defects, generated by irradiation, played an important role in tuning the structural, atomic diffusion and magnetic reversal properties of Pt/Co/Pt.     

Control of the magnetic domain wall propagation in Pt/Co/Pt ultra thin films using direct mechanical AFM lithography

We create mesoscopic point and line defects by scanning probe lithography to control the magnetization reversal process in Pt/Co/Pt ultra thin film devices. The domain wall propagation near the defects is studied by the Kerr microscopy and extraordinary Hall effect measurements. The observed domain wall pinning is used to block and channel the domain expansion and to create artificial domain patterns.     

Magnetization reversal dynamics in Au/Co/Au(111) ultrathin films: Effect of roughness of the buffer layer

We present a study of the magnetization reversal dynamics in ultrathin Au/Co/Au films with perpendicular magnetic anisotropy, for a Co thickness of 0.5, 0.7 and 1 nm. In these films, the magnetization reversal is dominated by domain nucleation for t_Co=0.5, 0.7 nm and by domain wall propagation for t_Co=1 nm. The prevalence of domain nucleation for the thickness range 0.5-0.7 nm is different from results reported in the literature, for the same system and for the same thickness range, where the magnetization reversal took place mainly by domain wall motion. We attribute this difference to the effect of roughness of the Au buffer layer on the morphology of the magnetic layer.     

Influence of Pt thickness on magnetization reversal processes in (Pt/Co)3 multilayers with perpendicular anisotropy

We present a detailed study of the magnetization reversal in perpendicularly magnetized (Pt/Co)₃ multilayers with different values of the platinum interlayer thickness t_Pt. To study the magnetization reversal in our samples we combined measurements of relaxation curves with the direct visualization of domain structures. Magnetization reversal was dominated by domain wall propagation for t_Pt=1 nm and by domain nucleation for t_Pt=0.2 nm, while a mixed process was observed for t_Pt=0.8 nm. We interpret our results within the framework of a model of thermally activated reversal where a distribution of activation energy barriers is taken into account. The reversal process was correlated with the energy barrier distribution.     

Magnetic relaxation measurements of exchange biased (Pt/Co) multilayers with perpendicular anisotropy

Magnetic relaxation measurements were carried out by magneto-optical Kerr effect on exchange biased (Pt/Co)5/Pt/FeMn multilayers with perpendicular anisotropy. In these films the coercivity and the exchange bias field vary with Pt spacer thickness, and have a maximum for 0.2 nm. Hysteresis loops do not reveal important differences between the reversal for ascending and descending fields. Relaxation measurements were fitted using Fatuzzo’s model, which assumes that reversal occurs by domain nucleation and domain wall propagation. For 2 nm thick Pt spacer (no exchange bias) the reversal is dominated by domain wall propagation starting from a few nucleation centers. For 0.2 nm Pt spacer (maximum exchange bias) the reversal is strongly dominated by nucleation, and no differences between the behaviour of the ascending and descending branches can be observed. For 0.4 nm Pt spacer (weaker exchange bias) the nucleation density becomes less important, and the measurements reveal a much stronger density of nucleation centers in the descending branch.     

Microscopic origin of asymmetric magnetization reversal of Co/Pt multilayers with perpendicular magnetic anisotropy

We have comprehensively investigated asymmetric magnetization reversal behaviors of (x-Å Co/7.7 Å Pt)₅ multilayers (x = 3.1 and 4.7) with perpendicular magnetic anisotropy. Our direct observation of magnetic domain structures by means of magneto-optical microscopy reveals that the asymmetry arises both from nucleation and wall-motion processes. An asymmetric nucleation behavior is observed, which could be originated from the preexisting non-reversed domains which might have a reproducible or random spatial distribution, controllable by tuning the field profile. An asymmetric wall-motion behavior stemming from asymmetric stripe domain evolution is also observed.     

Slow Oscillations of the Perpendicular Magnetization of the Pt/Co/Ir/Co/Pt Spin Valve

The time dependences of the transfer of the magnetic moment between stable magnetic states of heterostructures with two Pt/Co/Ir/Co/Pt ferromagnetic layers with the perpendicular magnetization have been studied. Spontaneous oscillations of the macroscopic magnetization with a period of several hours are observed after switching the magnetic field to a new value. The phase portrait of the magnetic relaxation corresponds to damped oscillations. The macrospin oscillation may be due to the high nucleation rate of the reverse magnetization phase induced by the exchange and magnetic dipole interaction between the phase nucleation centers, which arise in different layers. The changes in the Zeeman energy of the system under magnetic oscillations are considered.     

具有垂直各向异性(Pt/Co)n/FeMn多层膜的交换偏置

采用磁控溅射方法制备了以Pt为缓冲层和保护层的具有垂直各向异性(Pt/Co)_n/ FeMn多层膜.研究结果表明，多层膜的垂直交换偏置场H_ex和反铁磁层厚度的关 系与其具有平面各向异性的交换偏置场随反铁磁层厚度变化趋势相近.随着铁磁层调制周期 数的增加，垂直交换偏置场H_ex相应减小，并且与铁磁层的调制周期数近似成反 比关系.(Pt/Co)₃/FeMn的垂直交换偏置场H_ex已经达到22.3kA/m.为 关键词： 交换偏置 垂直各向异性 多层膜     

Experimental analysis of the fast magnetization dynamics in high perpendicular anisotropy Co/Pt nanostructures

We present preliminary results for magnetization dynamics in high perpendicular anisotropy Co/Pt cross-shaped nanostructures submitted to a single/train out-of-plane field pulses. For this, a fabrication process has been developed to obtain high-quality microwave test structures. Using extraordinary Hall effect, we measure quasistatic hysteresis loops while applying either a single or a train of field pulses of given amplitude (32 mT at maximum), variable duration (0.2–10 ns) and repetition frequency (1–100 kHz). We get that field pulses affect only one side of the hysteresis loops without any clear change in the squareness of the loop. Such behavior can be most probably attributed to pulse-induced nucleation of reverse domains in the cross area. The measured shift in coercive field decreases linearly with the logarithm of the pulse duration and two switching regimes that get connected for pulse duration around 1 ns have been observed. Switching probability with single pulse showed that field pulse of 10 ns and 32 mT of magnitude has the same effect of 2 mT static fields.     

Prediction of a domain-drag effect in uniaxial,non-compensated,ferromagnetic metals

An electric current is predicted to exert a dragging force on ferromagnetic domain walls. The effect arises from the non-uniform current distribution, recently predicted and observed at 4·2 K in the neighborhood of a wall in metals (Co, Ni) with large Hall angle. When the average current density j? exceeds a certain “coercive” value j?_c, the domains are set into motion in the same direction as the charge carriers. When j?j?_c, the wall speed approaches the drift speed of the carriers. Ohm's law fails when the walls move. The limits of very small and of very large Hall angle are both considered, using the single-wall model of Williams, Shockley and Kittel, and also the stratified-medium model of Herring. We assume B = M_s inside each domain; this is appropriate if the sample thickness t in the direction of the saturation magnetization M_s, and the wall spacing a, obey t > a. Materials with large anisotropy field H_A (h.c.p. Co, Gd) are necessary if the field H of the current is not to remove all walls normal to the current. For similar reasons, the sample should be in the shape of a flat ribbon (or rod) normal to M_s, of thickness (or diameter) t obeying t < dH_A/H_c, where H_c is the coercive field and d the wall length in the direction normal to the current and to M_s.     

Adhesion and bonding of Pt/Ni and Pt/Co overlayers: Density functional calculations

The electronic and energetic properties of bimetallic surfaces Pt/Ni(111) and Pt/Co(111) are examined using the FP-LAPW (Full-PotentialLinearized Augmented Plane Wave) method by means of spin-polarized and non-polarized calculations. We present both the results of the shifts in the d-band centers when one metal (Pt) is pseudomorfically deposited on another with smaller lattice constant (Ni, Co) and those corresponding to the surface and adhesion energies. The surface is modeled by a seven layer slab separated in z direction by a vacuum region of six substrate layers. The results obtained for pure Ni, Co and Pt surfaces are presented in order to compare with experimental and theoretical data reported in the literature     

Structural and magnetic properties of Pt in Co/Pt multilayers

[Co(30 Å)/Pt(x Å)]₂₀ multilayers with the Pt layer thicknesses varying from 5 Å to 20 Å were characterized structurally by high angle X-ray diffraction, X-ray reflectivity, X-ray absorption spectroscopy and magnetically by X-ray magnetic circular dichroism. It is found that the structure and magnetic properties of Pt have a strong correlation with the Pt layer thickness. The 20 Å thickness Pt layer is not almost influenced by the adjacent Co layer and the nearest neighbors are dominated by Pt-Pt shells. With decreasing Pt layer thickness, the nearest neighbors are gradually dominated by Pt-Co shells and the Pt-Co intermixing regions also remarkable increase at the interfaces, especially for the 5 Å thickness Pt layer. The orbital and spin magnetic moments as well as the ratio m_orb/m_spin all decrease systematically with increasing Pt layer thickness, indicating that the interface atoms are polarized by direct Pt-Co hybridization, but that the adjacent layers are polarized by Pt-Pt interactions.