Ce0.35Zr0.55La0.10O1.95对低贵金属Pt-Rh型三效催化剂性能的影响

采用共沉淀技术制备了Ce0.35Zr0.55La0.10O1.95固溶体, 其织构和结构性能以及氧化还原性能分别采用BET、XRD和程序升温(TP)技术进行了表征. 制备了低贵金属Pt-Rh型三效催化剂, 考察了Ce0.35Zr0.55La0.10O1.95对催化剂性能的影响. XRD和BET的结果表明, 经600 ℃焙烧5 h后, Ce0.35Zr0.55La0.10O1.95具有与Ce0.50Zr0.50O2相似的立方结构和高的比表面积；经1000 ℃焙烧5 h后, 仍能保持稳定的立方结构和47.25 m2•g−1的比表面积, 表现出优越的织构性能和高的热稳定性. H2-TPR和O2-TPO的结果表明, Ce0.35Zr0.55La0.10O1.95具有比Ce0.50Zr0.50O2更好的氧化还原性能. 和含Ce0.50Zr0.50O2的催化剂相比, 含Ce0.35Zr0.55La0.10O1.95的催化剂具有较宽的工作窗口, 优越的低温起燃性能, 较强的水气变换能力；催化剂经1000 ℃高温水热老化5 h后, 仍具有良好的催化活性, 表现出了优异的抗老化性能.     

CeO2-ZrO2-Y2O3对Pt-Rh型三效催化剂性能的影响

采用共沉淀法技术制备了Ce0.35Zr0.55Y0.10固溶体,并对其进行了比表面积、储氧量的测试和XRD的表征.将其用于低贵金属Pt-Rh型三效催化剂的制备,考察了CeO2-ZrO2-Y2O3对三效催化剂性能的影响.结果表明,Ce0.35Zr0.55Y0.10具有与Ce0.50Zr0.50O2相似的立方结构和相近的储氧量,经高温(1000 ℃)后仍能保持较大的比表面积(38.66 m2·g-1).和含Ce0.50Zr0.50O2的三效催化剂相比,含CeO2-ZrO2-Y2O3的三效催化剂经高温老化后,C3H8,CO,NO仍具有较高的转化率和较低的起燃温度.     

不同配比的Pd, Pt, Rh三效催化剂性能研究

为了降低催化剂成本, 开发单钯或含钯催化剂是现在汽车尾气净化领域研究热点之一. 本文介绍了不同Pd, Pt,Rh配比催化剂的性能, 包括新鲜的和1100 ℃, 50 h老化后的空燃比特性和起燃温度特性, 并对实验结果进行比较和分析.     

Ce0.67Zr0.33O2材料的制备和表征及其负载单Pd三效催化剂的性能

采用共沉淀法、均匀沉淀法、微乳法和水热法四种方法制备了铈锆固溶体(CZ),对其进行了X射线衍射和N2吸附脱附分析.以CZ为载体制备了负载单Pd三效催化剂,并对催化剂进行了氧化还原性能测试.结果表明,制备方法对CZ载体的物理、化学性能有显著的影响,而其负载单Pd催化剂的催化活性与CZ载体比表面积的大小没有明显的对应关系.采用共沉淀法制备的CZ载体具有相对良好的热稳定性以及储放氧能力,其负载单Pd催化剂在老化前后表面PdO物种有良好的还原性能,并表现出优异的三效催化性能.     

碱土金属氟化物促进Eu2O3催化剂的甲烷氧化偶联性能

考察了碱土金属氟化物促进的Ｅｕ２Ｏ３在甲烷氧化偶联反应中的催化性能。发现在Ｅｕ２Ｏ３中添加碱土金属氧化物后，碳二烃（Ｃ２）的选择性和收率都有明显提高。当Ｅｕ２Ｏ３摩尔含量相同时，催化性能按ＣａＦ２－Ｅｕ２Ｏ３＝ＢａＦ２－Ｅｕ２Ｏ３〈ＳｒＦ２－Ｅｕ２Ｏ３顺序递增，ＸＲＤ分析结果表明，在新鲜的ＢａＦ２－Ｅｕ２Ｏ３催化剂中了菱形ＥｕＯＦ新相，而在其它两类催化剂中氟氧离子交换不明显，这种差异与碱土金属氟化     

铈锆比对低贵金属Pt＋Rh/Ce0.3＋xZr0.6－xY0.1O1.95＋Al2O3三效催化剂性能的影响

用共沉淀法制得一系列铈锆比不同的Ce_0.3＋xZr_0.6－xY_0.1O_1.95储氧材料, 并用于制备了一系列低贵金属Pt＋Rh/Ce_0.3＋xZr_0.6－xY_0.1O_1.95＋Al₂O₃三效催化剂. 用比表面、程序升温还原以及X射线衍射对该系列催化剂进行表征, 结果发现, 催化剂的活性与催化剂中贵金属的还原性能密切相关, 低铈储氧材料比高铈储氧材料更有利于促进贵金属还原, 因而含低铈储氧材料催化剂的活性明显优于含高铈储氧材料催化剂的活性, Pt＋Rh/Ce_0.35Zr_0.55Y_0.1O_1.95＋Al₂O₃的活性最佳, 对HC, CO和NO的起燃温度最低分别为: 235, 175, 200 ℃. 样品经1000 ℃水热老化之后, 贵金属Pt被烧结而发生迁移, 使得催化剂的活性及还原性能变差, 含低铈材料的催化剂的抗老化性能优于含高铈材料的催化剂, 其中Pt＋Rh/Ce_0.35Zr_0.55Y_0.1O_1.95＋Al₂O₃的抗老化性能最好.     

制备方法对Pd/Ce-Zr-Mn-Al-O材料催化性能的影响研究

通过溶胶凝胶法、浸渍法和共沉淀法制备含贵金属Pd的Ce-Zr-Mn-Al-O固溶体材料,并对新鲜和老化样件材料的BET、孔容、孔径、TPR等表征研究,结果表明:采用溶胶凝胶法制备的材料在新鲜和老化条件下具有良好的储氧能力(OSC)和表征特性,将不同制备方法所得的材料制成催化剂样件在发动机台架进行连续空燃比和连续温度实验,台架数据结果表明采用溶胶凝胶法制备的催化剂在处理HC和NOx时表现出优良的特性,催化剂对总碳氢化合物(THC)和NOx的初始转化能力和偏稀条件下NOx的处理具有较强的适应能力,该方法制备的催化剂应用到CNG发动机上也取得了良好的效果。     

铈锆比对低贵金属Pt＋Rh/Ce0.3＋xZr0.6－xY0.1O1.95＋Al2O3三效催化剂性能的影响

用共沉淀法制得一系列铈锆比不同的Ce_0.3＋xZr_0.6－xY_0.1O_1.95储氧材料, 并用于制备了一系列低贵金属Pt＋Rh/Ce_0.3＋xZr_0.6－xY_0.1O_1.95＋Al₂O₃三效催化剂. 用比表面、程序升温还原以及X射线衍射对该系列催化剂进行表征, 结果发现, 催化剂的活性与催化剂中贵金属的还原性能密切相关, 低铈储氧材料比高铈储氧材料更有利于促进贵金属还原, 因而含低铈储氧材料催化剂的活性明显优于含高铈储氧材料催化剂的活性, Pt＋Rh/Ce_0.35Zr_0.55Y_0.1O_1.95＋Al₂O₃的活性最佳, 对HC, CO和NO的起燃温度最低分别为: 235, 175, 200 ℃. 样品经1000 ℃水热老化之后, 贵金属Pt被烧结而发生迁移, 使得催化剂的活性及还原性能变差, 含低铈材料的催化剂的抗老化性能优于含高铈材料的催化剂, 其中Pt＋Rh/Ce_0.35Zr_0.55Y_0.1O_1.95＋Al₂O₃的抗老化性能最好.     

Pd/γ-Al2O3三效催化剂中CeO2-ZrO2-La2O3的作用

用浸渍法制备了CeO2-ZrO2-La2O3复合氧化物,用XRD,TG-DTA,拉曼光谱、H2-TPR和BET表面积测定等方法对合成的样品进行了表征,研究了在单钯Pd/γ-Al2O3催化剂中添加CeO2-ZrO2-La2O3对催化剂活性和热稳定性的影响.结果表明,在Pd/γ-Al2O3中加入三元复合氧化物有利于提高三效催化剂的热稳定性,有利于阻止γ-Al2O3在高温时的相变以稳定Al2O3结构,防止在高温条件下催化剂表面积的损失.在Pd的负载量为1 g*L-1条件下,测定了Pd/CeO2-ZrO2-La2O3/γ-Al2O3/蜂窝陶瓷催化剂对CO,C3H6和NO净化的三效活性,研究了催化剂的结构和三效催化活性之间的关系.结果表明,CeO2-ZrO2-La2O3的存在能明显提高Pd基催化剂对CO,C3H6和NO的三效净化活性,扩大催化剂的操作窗口,提高在富氧条件下对NOx的还原性能.     

Influence of Ce0.35Zr0.55La0.10O1.95 Solid Solution on the Performance of Low Pt-Rh Three-way Catalysts

Ce_0.35Zr_0.55La_0.10O_1.95 solid solution was prepared by coprecipitation technique and characterized by specific surface area measurements (BET), X-ray diffraction (XRD), and temperature-programmed (TP) technique. Ce_0.35Zr_0.55La_0.10O_1.95 was used to prepare low Pt-Rh three-way catalyst (TWC) and its influence on the performance of TWC was investigated. The results showed that Ce_0.35Zr_0.55La_0.10O_1.95 had a cubic structure similar to Ce_0.50Zr_0.50O₂ and a large specific area after calcined at 600 °C for 5 h. Furthermore, after being aged at 1000 °C for 5 h, Ce_0.35Zr_0.55La_0.10O_1.95 still maintained a stable cubic structure and a specific surface area of 47.25 m²·g⁻¹. The results of H₂-TPR and O₂-TPO indicated that Ce_0.35Zr_0.55La_0.10O_1.95 had good redox properties. The catalyst containing Ce_0.35Zr_0.55La_0.10O_1.95 possessed a fairly wide range of three-way working-windows, good low-temperature light-off properties, and better ability of water-gas shift. Being hydrothermally aged at 1000 °C, the catalyst containing Ce_0.35Zr_0.55La_0.10O_1.95 still showed good catalytic activity in comparison with Ce_0.50Zr_0.50O₂ TWC, which indicated that Ce_0.35Zr_0.55La_0.10O_1.95 improved the anti-aging properties of the catalyst.     

Ce-Zr-La-Al2O3的制备及负载的单Pd三效催化剂

采用共沉淀和浸渍两种方法制备了Ce-Zr-La-Al2O3(CZLA),对其进行了N2吸附和X射线衍射分析.以CZLA为载体制备了2%Pd/CZLA三效催化剂,并对催化剂进行了程序升温还原和活性测试.结果表明,两种方法制备的CZLA均具有较好的结构、织构和储氧性能,共沉淀法制备的CZLA具有更好的抗老化性能.以CZLA为载体所制备的单Pd三效催化剂表现出低的起燃温度、优异的三效性能,特别是优异的转化NO性能及抗老化性能.     

整体式Pd/La_2O_3-Al_2O_3和Pd/CeO_2-ZrO_2-Y_2O_3催化剂上汽油车尾气净化性能的比较

采用共沉淀法制备了耐高温高比表面积的La2O3-Al2O3(LA)材料和CeO2-ZrO2-Y2O3(CZY)储氧材料,并用浸渍法制备了整体式Pd/LA和Pd/CZY汽油车尾气净化三效催化剂,考察了它们的三效催化性能和空燃比性能,并单独通过水煤气变换和CO氧化反应性能的考察,探讨了两种催化剂空燃比窗口扩大的原因.结果表明,Pd/CZY催化剂三效窗口明显较宽,且催化氧化CO的性能明显更优;对于CO+NO反应,Pd/CZY催化剂的活性较高.当反应中逐步通入O2后,抑制了该反应的进行,但CO氧化的转化率升高,而NO转化率降低,直至CO+NO反应完全被抑制,表明CO氧化反应对于抑制催化剂在NO贫燃方向的窗口具有一定的作用.另外,Pd/CZY催化剂上对于水煤气变换反应性能明显优于Pd/LA催化剂,在一定温度下逐步通入O2后,不会抑制水煤气变换反应的发生;当逐步通入NO时,可以促进水煤气变换反应的进行,表明Pd/CZY催化剂在富燃时对扩展CO转化窗口的性能明显优于Pd/LA催化剂.     

Pt/MOx-SiO2 (M=Ce,Zr, Al)催化剂对CO和C3H8氧化性能的影响

采用共沉淀法制备质量比为1:1的MOx-SiO2(M=Ce,Zr,Al)复合氧化物,以此为载体采用浸渍法制备了铂基氧化型催化剂.考察了该系列催化剂在模拟柴油车尾气条件下,经SO2硫化前后对C3H8和CO的氧化性能.用X射线衍射(XRD)、低温N2吸附-脱附、氨气/氧气/二氧化碳程序升温脱附(NH3/O2/CO2-TPD)和X射线光电子能谱(XPS)等手段进行了表征.NH3-TPD证实催化剂表面存在多种酸中心,硫化后催化剂表面中强酸中心增多.O2-TPD证实催化剂表面存在α和β氧物种,硫化后催化剂表面氧脱附量减少.其中Pt/Al2O3-SiO2表面酸性最弱和表面氧脱附量最大.XPS结果表明新鲜催化剂经硫化后会使催化剂表面Pt的结合能降低.活性测试结果表明,三种催化剂对CO和C3H8的催化氧化活性均较好,其中Pt/ZrO2-SiO2抗SO2中毒性能最佳,具有良好的应用前景.     

过渡金属修饰对Pt/M-DMSN催化剂丙烷脱氢性能的影响

以两步法制备了一系列过渡金属(M=Fe, Co, Ni, Cu, Zn)修饰的树枝状介孔二氧化硅纳米粒子(DMSN)负载铂(Pt/M-DMSN)催化剂, 并对该系列催化剂进行了丙烷催化脱氢性能评价. X射线衍射(XRD)、 透射电子显微镜(TEM)、 紫外-可见漫反射光谱(UV-Vis DRS)和氢气程序升温还原(H₂-TPR)表征结果表明, 不同过渡金属在DMSN载体表面分散状态不同,且与Pt的相互作用程度不同. 其中Zn-DMSN载体最有利于Pt的分散, 且反应后催化剂上积碳含量最低; Pt/Fe-DMSN催化剂中Pt与载体的相互作用力较强. 通过活性评价结果可知, Pt/Fe-DMSN催化剂表现出最优的丙烷催化脱氢性能, 丙烷初始转化率为44.2%, 反应6 h后丙烷转化率仍可达36.5%.     

Visualization of the Heterogeneity of Cerium Oxidation States in Single Pt/Ce2Zr2Ox Catalyst Particles by Nano‐XAFS

The cerium oxidation states in single catalyst particles of Pt/Ce₂Zr₂O_x (x=7 to 8) were investigated by spatially resolved nano X‐ray absorption fine structure (nano‐XAFS) using an X‐ray nanobeam. Differences in the distribution of the Ce oxidation states between Pt/Ce₂Zr₂O_x single particles of different oxygen compositions x were visualized in the obtained two‐dimensional X‐ray fluorescent (XRF) mapping images and the Ce L_III‐edge nano X‐ray absorption near‐edge structure (nano‐XANES) spectra.