Atom transfer radical polymerization of acrylates in an ionic liquid: Synthesis of block copolymers

Atom transfer radical polymerization (ATRP) of acrylates in ionic liquid, 1‐butyl‐3‐methylimidazolium hexaflurophospate, with the CuBr/CuBr₂/amine catalytic system was investigated. Sequential polymerization was performed by synthesizing AB block copolymers. Polymerization of butyl acrylate (monomer that is only partly soluble in an ionic liquid forming a two‐phase system) proceeded to practically quantitative conversion. If the second monomer (methyl acrylate) is added at this stage, polymerization proceeds, and block copolymer formed is essentially free of homopolymer according to size exclusion chromatographic analysis. The number‐average molecular weight of the copolymer is slightly higher than calculated, but the molecular weight distribution is low (M_w/M_n = 1.12). If, however, methyl acrylate (monomer that is soluble in an ionic liquid) is polymerized at the first stage, then butyl acrylate in the second‐stage situation is different. Block copolymer free of homopolymer of the first block (with M_w/M_n = 1.13) may be obtained only if the conversion of methyl acrylate at the stage when second monomer is added is not higher than 70%. Matrix‐assisted laser desorption/ionization time‐of‐flight analysis confirmed that irreversible deactivation of growing macromolecules is significant for methyl acrylate polymerization at a monomer conversion above 70%, whereas it is still not significant for butyl acrylate even at practically quantitative conversion. These results show that ATRP of butyl acrylate in ionic liquid followed by addition of a second acrylate monomer allows the clean synthesis of block copolymers by one‐pot sequential polymerization even if the first stage is carried out to complete conversion of butyl acrylate. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2799–2809, 2002     

Synthesis and copolymerization of new phosphorus‐containing acrylates

Two phosphorus‐containing acrylate monomers were synthesized from the reaction of ethyl α‐chloromethyl acrylate and t‐butyl α‐bromomethyl acrylate with triethyl phosphite. The selective hydrolysis of the ethyl ester monomer with trimethylsilyl bromide (TMSBr) gave a phosphonic acid monomer. The attempted bulk polymerizations of the monomers at 57–60 °C with 2,2′‐azobisisobutyronitrile (AIBN) were unsuccessful; however, the monomers were copolymerized with methyl methacrylate (MMA) in bulk at 60 °C with AIBN. The resulting copolymers produced chars on burning, showing potential as flame‐retardant materials. Additionally, α‐(chloromethyl)acryloyl chloride (CMAC) was reacted with diethyl (hydroxymethyl)phosphonate to obtain a new monomer with identical ester and ether moieties. This monomer was hydrolyzed with TMSBr, homopolymerized, and copolymerized with MMA. The thermal stabilities of the copolymers increased with increasing amounts of the phosphonate monomer in the copolymers. A new route to highly reactive phosphorus‐containing acrylate monomers was developed. A new derivative of CMAC with mixed ester and ether groups was synthesized by substitution, first with diethyl (hydroxymethyl)phosphonate and then with sodium acetate. This monomer showed the highest reactivity and gave a crosslinked polymer. The incorporation of an ester group increased the rate of polymerization. The relative reactivities of the synthesized monomers in photopolymerizations were determined and compared with those of the other phosphorous‐containing acrylate monomers. Changing the monomer structure allowed control of the polymerization reactivity so that new phosphorus‐containing polymers with desirable properties could be obtained. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2207–2217, 2003     

Controlled synthesis of new amphiphilic glycopolymers with liquid crystal grafts

A cholesterol‐based liquid crystal monomer, diethylene glycol cholesteryl ether acrylate (DEGCholA), has been successfully polymerized by atom transfer radical polymerization (ATRP) for the first time. Appropriate experimental conditions to control the polymerization of DEGCholA have been investigated using a model initiator (ethyl 2‐bromoisobutyrate) in tetrahydrofuran (THF) or toluene at 60 °C. Well‐controlled ATRP of DEGCholA was obtained using N,N,N′,N′,N″‐pentamethyldiethylenetriamine as ligand in THF at 60 °C. These conditions were then applied to initiate the ATRP of DEGCholA from multifunctional macroinitiators based on dextran. Using a protection/deprotection synthetic scheme, novel graft glycopolymers (Dex‐g‐PDEGCholA) have been synthesized. The mesomorphic properties of DEGCholA, PDEGCholA, and Dex‐g‐PDEGCholA have been studied by thermal polarizing optical microscopy, differential scanning calorimetry, and X‐ray scattering. PDEGCholA and Dex‐g‐PDEGCholA show an interdigitated smectic A phase (SmA_d) between T_g (～30 °C) and around 170 °C. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 3829–3839     

On the Bulk Properties of a Poly(Bicycloacrylate) Carrying Semifluorinated Side Groups

We prepared a novel fluorinated polymer from a bicycloacrylate monomer, (1H,1H,2H,2H)-perfluorododecyl 2-(bicyclo[3.1.0]hex-1-yl)acrylate, by radical ring opening polymerization. The bulk properties of the polymer were investigated by thermal analysis and X-ray diffraction, which proved the existence of a smectic mesophase up to the isotropization temperature of 74 °C. Furthermore, a solid state NMR study was started to characterize domains with different mobility mainly by ¹³C cross-polarization magic angle spinning and T₂ selective experiments. We found that the polymer is a homogeneous sample with the presence of dynamic motions in the kHz regime below the glass transition temperature.     

The influence of N‐vinyl pyrrolidone on polymerization kinetics and thermo‐mechanical properties of crosslinked acrylate polymers

Polymerization of multifunctional acrylate monomers generates crosslinked polymers that are noted for their mechanical strength, thermal stability, and chemical resistance. A common reactive diluent to photopolymerizable formulations is N‐vinyl pyrrolidone (NVP), which is known to reduce the inhibition of free radical photopolymerization by atmospheric oxygen. In this work, the copolymerization behavior of NVP was examined in acrylate monomers with two to five functional groups. At concentrations as low as 2 wt %, NVP increases the polymerization rate in copolymerization with multifunctional acrylate monomer. The relative rate enhancement associated with adding NVP increases dramatically as the number of acrylate double bonds changes from two to five. The influence of NVP on polymerization kinetics is related to synergistic cross‐propagation between NVP and acrylate monomer, which becomes increasingly favorable with diffusion limitations. This synergy extends bimolecular termination into higher double bond conversion through reaction diffusion controlled termination. Copolymerizing concentrations of 5–30 DB% NVP with diacrylate or pentaacrylate monomer also increases Young's modulus and the glass transition temperature (T_g) in comparison to neat acrylate polymers. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4062–4073, 2007     

Perfluorocyclobutyl-containing Amphiphilic Block Copolymers Synthesized by RAFT Polymerization

Amphiphilic block copolymers containing hydrophobic perfluorocyclobutyl‐based (PFCB) polyacrylate and hydrophilic poly(ethylene glycol) (PEG) segments were prepared via reversible addition‐fragmentation chain transfer (RAFT) polymerization. The PFCB‐containing acrylate monomer, p‐(2‐(p‐tolyloxy)perfluorocyclobutoxy)‐phenyl acrylate, was first synthesized from commercially available compounds in good yields, and this kind of acrylate monomer can be homopolymerized by free radical polymerization or RAFT polymerization. Kinetic study showed the 2,2′‐azobis(isobutyronitrile) (AIBN) initiated and cumyl dithiobenzoate (CDB) mediated RAFT polymerization was in a living fashion, as suggested by the fact that the number‐average molecular weights (M_n) increased linearly with the conversions of the monomer, while the polydispersity indices kept less than 1.10. The block polymers with narrow molecular weight distributions (M_w/M_n≦1.21) were prepared through RAFT polymerization using PEG monomethyl ether capped with 4‐cyanopentanoic acid dithiobenzoate end group as the macro chain transfer agent (mPEG‐CTA). The length of the hydrophobic segment can be tuned by the feed ratio of the PFCB‐based acrylate monomer and the extending of the polymerization time. The micellization behavior of the block copolymers in aqueous media was investigated by the fluorescence probe technique.     

Stereospecific radical polymerization of fluoroalkyl acrylates

The free‐radical polymerization of 2,2,2‐trifluoroethyl acrylate (TFEA), 1,1,1,3,3,3‐hexafluoro‐2‐propyl acrylate (HFiPA) and perfluoro‐tert‐butyl acrylate (PFtBA) was carried out under various conditions and the stereostructure of the obtained polymers was investigated. Most polymerizations of the three monomers afforded polymers rich in diad syndiotacticity (r) in bulk or in solution; the r‐specificity was higher in the HFiPA and PFtBA polymerization than in the TFEA polymerization. Although the tacticity was nearly independent of reaction temperature during the polymerization of TFEA, the r‐specificity increased by lowering the reaction temperature during the polymerization of the other two monomers. The polymerization stereochemistry was also affected by the reaction solvents including toluene, tetrahydrofuran, and fluoroalcohols. It was noted that the stereochemistry of the polymerization of HFiPA and PFtBA also depended on the monomer concentration, and a lower monomer concentration led to a higher r‐specificity. By optimizing the aforementioned reaction conditions, the poly(HFiPA) having r = 81% (polymerization in tetrahydrofuran at −98 °C at [M]_o = 0.2M) and the poly(PFtBA) having r = 77% (polymerization in toluene at −78 °C at [M]_o = 0.2M) were obtained. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1024–1032, 2000     

Synthesis of novel crosslinkable polymers by atom transfer radical polymerization of cardanyl acrylate

In this work, the successful application of atom transfer radical polymerization (ATRP) to cardanyl acrylate, a polymerizable monomer derived from a renewable resource cardanol, is reported. Polycardanyl acrylate and poly(methylmethacrylate)‐cardanyl acrylate copolymers were prepared in bulk ATRP, using Copper(I) bromide/N, N, N′, N′, N″‐pentamethyl diethylene triamine (PMDETA) catalyst system at 95 °C in combination with ethyl‐2‐bromo isobutyrate initiator. The copolymers had mol. wt. (M_n) in the range 8300–2400 g/mol and polydispersity index (PDI) 1.27–2.00, depending upon the [M]₀/[I]₀ ratio. ¹H NMR analysis of the copolymer showed that unsaturation in the side chain of cardanyl acrylate is unaffected under the conditions of ATRP. This was further confirmed by studying the curing reaction of polycardanyl acrylate by supported dynamic mechanical thermal analysis (DMTA) in dual cantilever mode. The thermogravimetric analysis shows that the copolymers have improved thermal stability, by about 35 °C, in comparison with pure PMMA. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5953–5961, 2005     

Radical polymerization and copolymerization of methyl α-(2-carbomethoxyethyl)acrylate,a dimer of methyl acrylate,as a polymerizable α-substituted acrylate

Polymerization and copolymerization of methyl α-(2-carbomethoxyethyl)acrylate (MMEA), which is known as a dimer of methyl acrylate, were studied in relation to steric hindrance-assisted polymerization. The propagating polymer radical from MMEA was detected as a five-line spectrum and quantified by ESR spectroscopy during the bulk polymerization at 40–80°C. The absolute rate constants of propagation and termination (κ_p and κ_t) for MMEA at 60°C (κ_p = 19 L/mol s and κ_t = 5.1 × 10⁵ L/mol s) were evaluated using the concentration of the propagating radical at the steady state. The balance of the propagation and termination rates allows polymer formation from MMEA. The polymerization rate of MMEA at 60°C was less than that of MMA by a factor of about 4 at a constant monomer concentration. Although no influence of ceiling temperature was observed at a temperature ranging from 40 to 70°C, addition-fragmentation in competition with propagation reduced the molecular weight of the polymer. The content of the unsaturated end group was estimated to be 0.1% at 60°C to the total amount of the monomer units consisting of the main chain. MMEA exhibited reactivities almost similar to those of MMA toward polymer radicals. It is concluded that MMEA is one of the polymerizable acrylates bearing a substituted alkyl group as an α-substituent. Characterization of poly(MMEA) was also carried out. © 1996 John Wiley & Sons, Inc.     

Thermal and radiation-induced polymerizations of N-tert-butylacrylamide and (N-tert-butylacrylamide)2–ZnCl2 complex

The thermal and radiation-induced in-source and postirradiation polymerizations of N-tert-butylacrylamide and (N-tert-butylacrylamide)₂–ZnCl₂ complex of this monomer were studied at various temperatures. In in-source, solid-state polymerizations of monomer and complex the conversion was about 95% at 21°C in about eight days. Their postirradiation polymerizations were also studied in solid state. The conversion-time curves of these two systems show an autoacceleration as in-source polymerization. In both types of polymerization the overall rate of polymerization of complex was higher than that of pure monomer at the same polymerization temperature. In investigations of the thermal polymerization of N-tert-butylacrylamide and ZnCl₂-complex it was observed that the ZnCl₂-complex system can be polymerized in air in the molten and solid state. The conversion of monomer to polymer reaches limiting values in solid state in about 1 hr. The thermal polymerization of ZnCl₂-complex in the molten state was also studied and 100% conversion was obtained in 30 min. The thermal polymerization of pure monomer was studied in vacuum and an appreciable amount of polymer was obtained in the molten state; however, the thermal polymerization of this monomer is negligible in solid state. In this work rates of polymerization for N-tert-butylacrylamide and (N-tert-butylacrylamide)₂–ZnCl₂ are compared under various experimental conditions and overall activation energies are calculated.     

Batch emulsion copolymerization of 3‐O‐methacryloyl‐1,2:5,6‐di‐O‐isopropylidene‐α‐D‐glucofuranose and butyl acrylate: Synthesis and properties of the sugar latices

To obtain new polymer latices based on sugar derivative, batch emulsion copolymerizations of 3‐O‐methacryloyl‐1,2:5,6‐di‐O‐isopropylidene‐α‐D ‐glucofuranose (3‐MDG) and n‐butyl acrylate (BA) were carried out at 70 °C, with potassium persulfate as the initiator. 3‐MDG polymerizes faster than BA because of its higher reactivity ratio, r_(3‐MDG) = 1.94 versus r_(BA) = 0.54. The effect of the initial monomer composition on the polymerization rate and the thermal properties of the end copolymers was investigated. The overall rate of polymerization increases by enhancing the sugar content in the initial monomer composition. The glass‐transition temperature is linearly related to the sugar content in the copolymer. The influence of the type of surfactant showed that the particle size increases by changing from ionic to nonionic surfactant. Furthermore, the effect of the added acrylic acid (AA) on the rheological properties suggests that the sugar latices exhibit different non‐Newtonian flows depending on the pH of the latex and on the AA concentration on the particle surface. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 788–803, 2003     

Synthesis of PMMA‐b‐PBA block copolymer in homogeneous and miniemulsion systems by DPE controlled radical polymerization

In this research, poly(methyl methacrylate)‐b‐poly(butyl acrylate) (PMMA‐b‐PBA) block copolymers were prepared by 1,1‐diphenylethene (DPE) controlled radical polymerization in homogeneous and miniemulsion systems. First, monomer methyl methacrylate (MMA), initiator 2,2′‐azobisisobutyronitrile (AIBN) and a control agent DPE were bulk polymerized to form the DPE‐containing PMMA macroinitiator. Then the DPE‐containing PMMA was heated in the presence of a second monomer BA, the block copolymer was synthesized successfully. The effects of solvent and polymerization methods (homogeneous polymerization or miniemulsion polymerization) on the reaction rate, controlled living character, molecular weight (M_n) and molecular weight distribution (PDI) of polymers throughout the polymerization were studied and discussed. The results showed that, increasing the amounts of solvent reduced the reaction rate and viscosity of the polymerization system. It allowed more activation–deactivation cycles to occur at a given conversion thus better controlled living character and narrower molecular weight distribution of polymers were demonstrated throughout the polymerization. Furthermore, the polymerization carried out in miniemulsion system exhibited higher reaction rate and better controlled living character than those in homogeneous system. It was attributed to the compartmentalization of growing radicals and the enhanced deactivation reaction of DPE controlled radical polymerization in miniemulsified droplets. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 4435–4445, 2009     

Kinetic study of light-induced polymerization by real-time UV and IR spectroscopy

Real time ultraviolet (RTUV) spectroscopy was used to study the photolysis kinetics of a radical-type morpholino initiator, during the polymerization of a multiacrylate monomer exposed to UV radiation in bulk, in solution, in a polyurethane-acrylate resin, and in a poly(methyl methacrylate) matrix. The photolysis rate constant k was determined from the exponential loss profile recorded; it was found to vary between 0.1 and 3s^?1, depending on the light intensity and on the monomer concentration. The quenching of the photoinitiator excited states by the acrylate monomer was shown to be an important deactivation pathway which substantially reduces the rate of initiation. The observed influence of the film thickness and photoinitiator concentration on the k value were accounted for by the internal filter effect. Conversion versus time curves were recorded by real time infrared (RTIR) spectroscopy for the various systems examined, thus allowing a direct comparison of both the actual polymerization rate and the residual unsaturation content of the cured polymer. Various factors were shown to be responsible for the early stop of the polymerization, such as depletion of the photoinitiator, O₂ inhibition, or vitrification of the polymer. The photoinitiated cationic ring-opening polymerization of a cycloaliphatic diepoxy monomer was also studied in real time by RTUV and RTIR spectroscopy. Despite a very fast photolysis of the triarylsulphonium initiator, the polymerization of the epoxy monomer developed less rapidly than for the acrylic monomer, with shorter kinetic chain lengths. A linear relationship was found to exist between the decay rate constant and the light intensity, for both the radical and the cationic photoinitiators, as expected for a direct photolysis process.     

Development and characterization of reactive extruded PVC/polyacrylate blends

This paper describes a method to obtain polymer blends by the absorption of a liquid solution of monomer, initiator, and a crosslinking agent in suspension type porous poly(vinyl chloride) (PVC) particles, forming a dry blend. These PVC/monomer dry blends are reactively polymerized in a twin‐screw extruder to obtain the in situ polymerization in a melt state of various blends: PVC/poly(methyl methacrylate) (PVC/PMMA), PVC/poly(vinyl acetate) (PVC/PVAc), PVC/poly(butyl acrylate) (PVC/PBA) and PVC/poly(ethylhexyl acrylate) (PVC/PEHA). Physical PVC/PMMA blends were produced, and the properties of those blends are compared to reactive blends of similar compositions. Owing to the high polymerization temperature (180°C), the polymers formed in this reactive polymerization process have low molecular weight. These short polymer chains plasticize the PVC phase reducing the melt viscosity, glass transition and the static modulus. Reactive blends of PVC/PMMA and PVC/PVAc are more compatible than the reactive PVC/PBA and PVC/PEHA blends. Reactive PVC/PMMA and PVC/PVAc blends are transparent, form single phase morphology, have single glass transition temperature (T_g), and show mechanical properties that are not inferior than that of neat PVC. Reactive PVC/PBA and PVC/PEHA blends are incompatible and two discrete phases are observed in each blend. However, those blends exhibit single glass transition owing to low content of the dispersed phase particles, which is probably too low to be detected by dynamic mechanical thermal analysis (DMTA) as a separate T_g value. The reactive PVC/PEHA show exceptional high elongation at break (～90%) owing to energy absorption optimized at this dispersed particle size (0.2–0.8 µm). Copyright © 2005 John Wiley & Sons, Ltd.     

Polymerization and viscoelastic behavior of networks from a dual‐curing,liquid crystalline monomer

The network formation and viscoelastic behavior of a liquid crystalline monomer, whose structure includes both acrylate and acetylene reactive groups, have been studied. By combining both photo and thermal polymerization, the networks can be formed in two separate steps, with the initial photopolymerization dominated by acrylate crosslinking and subsequent thermal polymerization dominated by acetylene crosslinking. In addition, the monomer exhibits a liquid crystalline phase. Photopolymerization while in the liquid crystal phase locks in the molecular ordering. Dynamic mechanical analysis shows that networks formed from the liquid crystalline phase have lower crosslink densities and narrower distributions of molecular weights between crosslinks when compared to networks formed from the isotropic phase (and at higher polymerization temperatures). After thermal postcure at 250°C, the networks formed from the isotropic monomer have a 23% higher dynamic mechanical storage modulus (in the glassy state) than the networks formed from the liquid crystalline monomer. The thermally postcured networks have unusually high glass‐transition temperatures, which exceed 300°C. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 1183–1190, 1999     

The influence of vinyl activating groups on β‐allyl sulfone‐based chain transfer agents for tough methacrylate networks

In radical polymerization of monofunctional monomers, addition fragmentation chain transfer (AFCT) agents are well known to regulate polymerization and yield polymers with lower molecular weights and narrower molecular weight distributions. Papers concerning bulk photopolymerization of monomer mixtures with AFCT agents are rarely found in literature. In this article, AFCT reagents based on β‐allyl sulfones with different vinyl activating groups were synthesized and compared. The compounds were tested in mono‐ and difunctional monomer systems providing information about the influence on photoreactivity, molecular weight, as well as thermal and mechanical properties of the resultant polymers. Where more potent activating groups (‐Ph, ‐CN) markedly influenced polymerization at lower concentrations, the AFCT reagent with an ester activating group reacted at a similar rate to the methacrylate monomer (C_T ≈ 1) and provided the best overall performance. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 1417‐1427     

Particle formation and coagulation in the seeded semibatch emulsion polymerization of butyl acrylate

Particle formation and coagulation in the seeded semibatch emulsion polymerization of butyl acrylate were studied under monomer‐starved conditions. To investigate the importance of the kinetics of the water phase in the nucleation process, the monomer feed rate was used as a variable to alter the monomer concentration in the aqueous phase. The emulsifier concentration in the feed was employed to alter the particle stability. Particle formation and coagulation were discussed in terms of critical surface coverage ratios. Particle coagulation occurred if the particle surface coverage dropped below θ_cr1 = 0.25 ± 0.05. The secondary nucleation occurred above a critical surface coverage of θ_cr2 = 0.55 ± 0.05. The number of particles remained approximately constant if the particle surface coverage was within θ_cr1 = 0.25 < θ < θ_cr2 = 0.55. This surface coverage band is equivalent to the surface tension band of 42.50 ± 5.0 dyne/cm that is required to avoid particle formation and coagulation in the course of polymerization. The kinetics of the water phase was shown to play an important role during homogeneous and micellar nucleations. For any fixed emulsifier concentration in the feed and above θ_cr2, the number of secondary particles increased with monomer concentration in the aqueous phase. Moreover, the presence of micelles in the reaction vessel is not the only perquisite for micellar nucleation to occur, a sufficient amount of monomer should be present in the aqueous phase to enhance the radical capture by partially monomer‐swollen micelles. The rate of polymerization increased with the surfactant concentration in the aqueous phase. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 3612–3630, 2000     

N‐Bromosuccinimide as a thermal iniferter for radical polymerization

N‐Bromosuccinimide (NBS) was used as a thermal iniferter for the initiation of the bulk polymerizations of methyl methacrylate, methyl acrylate, and styrene. The polymerizations showed the characteristics of a living polymerization: both the yields and the molecular weights of the resultant polymers increased linearly as the reaction time increased. The molecular weight distributions of the polymers were 1.42–1.95 under the studied conditions. The resultant polymers could be used as macroiniferters to reinitiate the polymerization of the second monomer. The copolymers poly(methyl methacrylate)‐b‐polystyrene and polystyrene‐b‐poly(methyl methacrylate) were obtained and characterized. End‐group analysis of the resultant poly(methyl methacrylate), poly(methyl acrylate), and polystyrene confirmed that NBS behaved as a thermal iniferter. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2567–2573, 2005     

Polymerization of acrylates by atom transfer radical polymerization. Homopolymerization of 2-hydroxyethyl acrylate

The application of atom transfer radical polymerization (ATRP) to the homopolymerization of 2-hydroxyethyl acrylate, a functional monomer, is reported. The polymerizations exhibit first-order kinetics, and molecular weights increase linearly with conversion. Polydispersities remain low throughout the polymerization (M_w/M_n ≈ 1.2). Reactions were conducted in bulk and in 1 : 1 (by volume) aqueous solution; the latter demonstrates the resilience of ATRP to protic media. Analysis of poly(2-hydroxyethyl acrylate) by MALDI-MS and ¹H-NMR shows M_n,exp to be much closer to M_n,th than those observed by SEC using polystyrene standards. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 1417–1424, 1998     

Solid-state polymerization of long-chain vinyl compounds. III. Mechanism of γ-ray-initiated postpolymerization in layered structures of octadecyl methacrylate and acrylate

The mechanism and kinetics of the γ-ray-initiated postpolymerization of octadecyl methacrylate and acrylate in lamellar crystals were investigated by a simple model. This model assumes that the initiation points are distributed as in a checkerboard and that polymerization probability of the monomer molecules decreases conically around each initiation point. The two-dimensional polymerization can be characterized in this cone model by two parameters, a and r; a represents the polymerizability of the monomer for a given condition, and r depends on the number of initiation points per unit area. G values for the initiation reaction of octadecyl methacrylate and acrylate were estimated as 0.8 and 1.6, respectively. The two-dimensional postpolymerization of long-chain compounds proceeds in two stages. The rate of polymerization is very high and zero order with respect to monomer concentration in the first stage. It is lower and obeys first-order kinetics in the second stage. The rate constants of the zero-and first-order polymerizations were k_p0 = 1.73 molecule sec^-1 and k_p1 = 0.93 sec^?1, respectively, for octadecyl acrylate at 20°C.