STRUCTURE AND MAGNETIC PROPERTIES OF LaCo13-BASED ALLOYS

The structure and magnetic properties of two series of LaCois-based alloys, LaCo_13-xFe_x(0≤x≤6) and La_1-xR_x(Co, Fe)₁₃ (x=0.1,0.2; R=Y, Ge, Pr, Nd Sm, Gd, Tb, Dy, Ho, Er, and Yb), are studied by X-ray diffraction and magnetic mea- surements. In the above-mentioned composotions, all the samples display a structure of NaZn₁₃ type (space group: Fm3c). In LaCo_13-xFe_x system, as the iron content increases, its Curie temperature decreases, while thc magnetic moment per 3d atom increases. This may be explained by a rigid band model. In the other alloy system, the Curie temperature goes through a maxium at R=Gd, and this reflects the influ- ence of R - T interaction. It is also observed that saturation magnetization varies with R and gets lower when R is a heavy rare earth element. The contribution of R is close to that of a free-ion moment. La_0.9Pr_0.1Co₉Fe₄ has the largest value 29μ_B/f.u.     

R13Fe74Si13三元合金的结构与磁性

本文对R₁₃Fe₇₄Si₁₃(R=Ce,Pr,Nd,Gd,Tb,Dy,Ho,Er,Y)三元合金的结构和磁性进行了研究。结果表明,R₁₃Fe₇₄Si₁₃的主相为R₂(Fe_0.85Si_0.1517赝二元金属间化合物,而不出现类似于R₂Fe₁₄B的三元 关键词：     

磁场诱导制备Bi-Mn合金的结构和低温磁性研究

系统研究了在外加诱导磁场下制备的Bi-Mn 6%合金的结构和低温磁特性.结果表明,在外加诱导磁场下制备的Bi-Mn 6%合金呈现典型的双相结构和各向异性特征,MnBi相c轴沿外加诱导磁场方向定向排列.发现MnBi相的矫顽力随温度的升高而增大,而饱和磁化强度则随温度的升高而减小.MnBi相的自旋重定向温度TSR随测量磁场的增大逐渐向低温区移动,在高的外加测量磁场下这种自旋重定向特征消失,发现了TSR随外加诱导制备磁场的增大而逐渐向高温区移动.对磁场诱导制备织构化MnBi相和该类材料磁各向异性能的物理机制进行了分析和讨论.     

Ho2Fe17Cx的结构与磁性

用快速急冷方法制备了Ho₂Fe₁₇C_x化合物,研究了它们的形成、结构与磁性。这些化合物在高温下是稳定的,随C含量的增加,晶体结构由六角Th₂Ni₁₇型转变为菱形Th₂Zn₁₇型。测量了Ho₂Fe₁₇C_x化合物在1.5K和室温下的饱和磁化强度,得到每个Fe原子磁矩近似与C含量无关。C原子的引 关键词：     

a-TM-Zr合金的磁性质与invar效应

本文报道液氮温度下a-Fe_90-xCo_xZr₁₀(x=0,4,10,20)和Fe_90-yCr_yZr₁₀(y=4,7,13,16)系列合金的穆斯堡尔谱,结果表明,上述合金存在两种不同的磁状态,它们的超精细参数随3d过渡金属的平均外层电子数α的变化曲线在α=8附近存在异常现象,这体现了低Co,Cr的a-Fe-(Co,Cr)-Zr合金的invar效应,约化超精细场随约化温度的变化结 关键词：     

非晶态Fe86M4Zr10合金的磁性和电性

本文研究了非晶态Fe₈₆M₄Zr₁₀(M=V,Cr,Mn,Fe,CO,Ni,Cu,B,Si)合金的基本磁性和低温电性,讨论了不同元素M的掺杂对FeZr合金居里温度和磁矩的影响,并用相干交换散射模型解释了样品在居里温度附近出现的电阻率极小。 关键词：     

R2Fe17C化合物的结构与内禀磁性的研究

本文系统研究了R₂Fe₁₇C(R=Y.Sm,Gd,Tb.Dy,Er)化合物的结构与内禀磁性,并与相应的R₂Fe₁₇化合物进行了比较。R₂Fe₁₇C的居里温度比相应R₂Fe₁₇的居里温度增加大约200K。本文讨论了C原子对该化合物结构与磁性的影响,同时,还对Sm₂(Fe_1-xCo_{x 关键词：}     

Y3Fe5-xMnxO12的磁结构和磁性能

对多晶Y₃Fe₃Fe_5-xMn_xO₁₂(x=0.05和0.09),得到300K下的中子衍射曲线。发现当x=0.05时,Mn³⁺离子占据16a和24d位置的几率分别为0.72和0.28;当x=0.09时,Mn³⁺离子全部占据16a位置;还得到两种组分16a和24d位置各自的磁矩值。在外磁场(800—10KOe)下测量Y₃Fe_5-xMn_xO₁₂(x=0—0.11)的磁化曲线,温度范围是1.5—300K。得到饱和磁矩值;并利用趋近饱和定律确定1.5K下的磁晶各向异性常数k₁值,发现|k₁|值随含锰量增加而减小。 关键词：     

NEUTRON-POWDER-DIFFRACTION STUDY OF THE STRUCTURE AND MAGNETIC PROPERTIES OF Nd2Fe14Si3

The crystal and magnetic structures of Nd₂Fe₁₄Si₃ at room temperature were refined by Rietveld analysis of neutron-powder-diffraction data. It was found that silicon atoms occupy preferentially both 18h and 18f of Th₂Zn₁₇-type structure with occupancies 0.36 and 0.14, respectively, The Fe-Fe bond-lengths computed with the refined crystallographic parameters have optimum values, as compared with those of Nd₂Fe₁₇ compounds, which can explain well why the Curie temperature rises strongly when the unit cell volume reduces with the substitution of silicon for iron in Nd₂Fe₁₇.     

机械合金化Fe-Si合金的微结构与磁性

用机械合金化方法制备了不同成分的Fe-Si合金．其晶粒具有α-Fe结构，粒径为十几到几十纳米，且晶格存在严重畸变．它们的饱和磁化强度σ_s与Si含量近似成线性关系，只是稍小于相应的单晶和多晶Fe-Si合金，而其矫顽力H_c和有效各向异性常数K_eff却远大于相应的单晶和多晶Fe-Si合金．它们的磁谱除Fe₇₅Si₂₅外都是弛豫型的，其磁导率的大小与相应的铁氧体复合材料差不多．在它们的磁化过程中，畴壁位移 关键词：     

Nd2(Fe,Si)17合金的结构与磁性

本文对Nd-Fe-Si三元系富铁区域相的结构和磁性进行了研究。结果表明,Nd-Fe-Si三元系富铁区域(Fe>40at％),除出现NdFe₂Si₂三元金属间化合物外(Si>20at％),同时只出现Nd₂(Fe,Si)₁₇赝二元金属间化合物,其中Si取代9d位的Fe原子,而不能形成类似于Nd₂Fe₁₄B的三元金属间化合物,Si取代Nd₂Fe₁₇中的9d位Fe原子后,使晶胞体积缩小;使饱和磁化强度减小;同时使Fe次晶格的铁磁相互作用增强,导致居里温度增高;还使得Fe次晶格的易面各向异性减弱,造成室温下各向异性场减小。 关键词：     

非晶态Fe90-xMnxZr10合金的磁性

本文报道用单辊急冷方法制备的非晶态合金Fe_90-xMn_xZr₁₀(x=0,4,6,10,15)的磁性,讨论了样品中每个原子的平均磁矩和居里温度T_c随Mn含量x的变化以及类自旋玻璃特性,给出了非晶态Fe_90-xMn_xZr₁₀合金的磁相图。观察到非晶态Fe₈₄Mn₆Zr₁₀合金晶化后的热磁曲线 关键词：     

STRUCTURE AND MAGNETIC PROPERTIES OF NITRIDES R3Fe29-xCrxN4

A systematic investigation of nitrides R₃Fe_29-xCr_xN₄(R=Y, Ce, Nd, Sm, Gd, Tb, and Dy) has been performed. The nitrogen concentration in the nitride R₃Fe_29-xCr_xN_y was determined to be y=4. Nitrogenation leads to a relative volume expansion of about 5.3%. The lattice constants and unit cell volume decrease with in creasing rare earth atomic number from Nd to Dy, reflecting the lanthanide contraction. In average, the increase of Curie temperature upon nitrogenation is about 200 K, compared with its parent compound. The nitrogenation also results in a remarkable improvement in the saturation magnetization and anisotropy fields for R₃Fe_29-xCr_xN₄ at 4.2 K and room temperature, comp ared with their parent compounds. A spin reorientation of Nd₃Fe_24.5 Cr_4.5N₄ occurs at around 368 K, which is 138 K higher than that of Nd₃Fe_24.5Cr_4.5.Magnetohistory effects of R₃Fe_29-xCr_xN₄(R=Nd and Sm) are observed in a low field of 0.04 T. First order magneti zation process occurs in Sm₃Fe_24.0Cr_5.0N₄ in magnetic fields of around 3.0 T at 4.2 K. After nitrogenation the easy magnetization direction of Sm₃Fe_24.0Cr_5.0 is changed from the easy cone structure to the uniaxial. The excellent intrinsic magnetic properties of Sm₃Fe_24.0Cr_5.0N₄ make this compound a hopeful candidate for new high performance permanent magnets.     

Ce1-xYxFe2的电子结构和磁性质

关键词：     

Si对Nd2Fe14B四方相结构和磁性的影响

本文对Si加入Nd₂Fe₁₄B四方相后所形成的合金相的结构和磁性进行了研究。结果表明,Si加入Nd₂Fe₁₄B四方相后并不破坏它的结构(Si的含量可达B的两倍),而形成Nd₂(Fe,Si)₁₄B赝三元金属间化合物。随着Si含量的增加,晶格常数和饱和磁化强度随之减小,但居里温度则随之增加。Si的加入,并不改变Nd₂Fe₁₄B的室温各向 关键词：     

氢对几种非晶态合金磁性的影响

本文研究了电解充氢对3种不同成分的非晶态合金磁性的影响。实验结果表明,充氢后试样变得很脆,软磁特性显著变劣,但饱和磁化强度σ₃和平均超精细场H_f显著提高。将试样在室温下放置,随着氢气的外逸,磁性、韧性以及H_f可得到逐步恢复。 关键词：     

[Cu_2■_4(DMF_2)]·4DMF的EPR谱、磁性与电子结构研究

在室温、77K条件下,对簇合物的固态和溶液样品进行了 EPR谱的测定,获得三套谱图(Ⅰ、Ⅱ、Ⅲ);其分别归属于簇合物中未配对电子的两种形式:(1)类似于自由的单铜离子的未配对电了(Ⅰ、Ⅱ两套谱).(2)双铜未配对电子偶合成的三重态(Ⅲ套谱).文中用双铜的三重态自旋哈密顿公式计算三重态EPR谱的参数.题目化合物(1)与双铜簇合物(2 )相比较,在配体结构上稍有不同(前者,甲苯胺中的甲基是连接于苯环的间位;而后者,甲基是连接于苯环的对位),由此引起一些磁性参数:有效磁矩μ_(eff)、磁交换相互作用参数J、相对的电子自旋浓度ρ和EPR谱的超精细结构(h.f.s)参数都有所不同.     

Ni—Fe—Nb及Ni—Fe—Nb—Al合金磁性和结构的初步研究

对两类合金,即Ni-Fe-Nb和Ni-Fe-Nb-Al合金的热处理和磁性进行了实验。Ni-Fe-Nb合金经高温处理后与工业常用的钼坡莫合金同样具有较高的起始磁导率和最大磁导率。我们对Ni-Fe-Nb和4钼坡莫合金的物理参数进行了比较。Ni-Fe-Nb-Al合金有较高的硬度和电阻率。经过两次联合处理,可以达到较为适用的磁导率值。Ni-Fe-Nb-Al合金经高温缓慢冷却发生了调幅结构,调幅结构的周期约50单胞(数)或160埃。Ni-Fe-Nb-Al合金经970℃加热后快速冷却可以抑制调幅结构。具有调幅结构的材料硬度较高,矫顽力也略为增高。 关键词：     

EFFECT OF THE SUBSTITUTION OF Ga ON THE STRUCTURE AND MAGNETIC PROPERTIES OF Dy2Fe17 COMPOUND

Dy₂Fe_17-xGa_x (x = 0,1,2,3,4, 5 and 6) compounds were prepared by arc melting. These compounds are of single phase, having a hexagonal Th₂Ni₁₇-type structure fox x=0 and rhombohedral Th₂Zn₁₇-type structure for x≥1. The substitution of Ga for Fe in the Dy₂Fe₁₇ leads to a linear increase of unit-cell volumes. The saturation magnetization M_s at 1.5K is found to decrease linearly with increasing Ga concentration, from 65emu/g for x= 0 to 5emu/g for x = 6; and the Fe magnetic moment μ_Fe is almost independent of Ga concentration. The Curie temperature T_C is found first to increase with increasing Ga content x, and goes through a maximum value of 559 K at about x = 3, then decreases. The sharp increase of T_C at lower Ga content may result from the increase of unit cell volumes. Dy₂Fe_17-xGa_x compounds with x≤5 exhibit easy plane anisotropy at room temperature, and those with x = 6 possess easy-axis.     

非晶Nd3Fe81B16合金的晶化及其对磁性和M?ssbauer谱的影响

本文报道利用单辊方法制备的非晶Nd₃Fe₈₁B₁₆合金的晶化及其对磁性和M?ssbauer谱的影响。发现在非晶Fe₈₁B₁₉合金中用3at％Nd取代B,使非晶Fe₈₁B₁₉合金的晶化温度提高88℃。在适当的退火条件下晶化后样品在室温下的磁性是:σ_s=189emu/g,σ_r/σ_s=0.7,_iH_c=2.15kOe,B_r≈12kG,_bH_c=2kOe,(BH)_max≈8MGOe。与目前广泛使用的六角铁氧体相比,_bH_c相近,但B_r和(BH)_max远比六角铁氧体高。这种材料仅含有少量的Nd,因此可能开发为一种新的廉价永磁材料。本文对少量Nd的添加对非晶FeB合金的晶化温度,磁性和M?ssbauer谱的影响进行了讨论。初步探讨了高矫顽力的来源,认为它的磁化和反磁化过程可以用畴壁钉扎理论解释。 关键词：