Structural, optical and electrical characterization of antimony-substituted tin oxide nanoparticles

Antimony-doped tin oxide (ATO) nanostructures were prepared using chemical precipitation technique starting from SnCl₂, SbCl₃ as precursor compounds. The antimony composition was varied from 5 to 20 wt%. The lower resistance was observed at composition of Sn:95 and Sb:05, when compared with undoped and higher doping concentration of antimony. The average crystalline size of undoped and doped tin oxide was calculated from the X-ray diffraction (XRD) pattern and found to be in the range of 30-11 nm and it was further confirmed from the transmission electron microscopy (TEM) studies. The scanning electron microscopy (SEM) analysis showed that the nanoparticles agglomerates forming spherical-shaped particles of few hundreds nanometers. The samples were further analyzed by energy dispersive spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR) and electrical resistance measurements.     

Synthesis of nanocrystalline and mesoporous zinc sulphide from a single precursor Zn(SOCCH3)2Lut2 complex

We report the formation of mesoporous zinc sulphide, composed by the fine network of nanoparticles, which was formed via a single precursor Zn(SOCCH₃)₂Lut₂ complex. The complex was chemically synthesized using zinc carbonate basic, 3,5-lutidine and thioacetic acid, in air. The metal precursor complex was characterized using different conventional techniques. Thermogravimetric analysis (TGA) result indicates that the decomposition of the complex starts at 100 °C and continues up to 450 °C, finally yielding ZnS. ZnS nanocrystals were characterized by powder X-ray diffraction (XRD) technique, field emission scanning electron microscopy (FESEM), N₂-sorption isotherm, UV-vis spectroscopy and photoluminescence (PL) spectroscopy. The grain diameter of nanocrystals was found to be 4-5 nm. The material followed Type-IV N₂-sorption isotherm, which is the characteristic of mesoporous materials. The band gap energy, as obtained from optical measurements was around 3.8 eV.     

Barium molybdate and barium tungstate nanocrystals synthesized by a cyclic microwave irradiation

BaMoO₄ and BaWO₄ nanocrystals were synthesized from Ba(NO₃)₂ and Na₂MeO₄ (Me=Mo and W) solutions using 50% of 600 W microwave irradiation for 20 min. The products were characterized using X-ray diffraction (XRD), Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), selected area electron diffraction (SAED) and photoluminescence (PL) spectrophotometry. They show that the products are good dispersed nanocrystals (poly-nanocrystals) of single-phase scheelite tetragonal structure with the vibration modes corresponding to the molybdate and tungstate compounds. Their photoluminescence was detected at 415 and 392 nm for BaMoO₄ and BaWO₄, respectively.     

The colloidal stability and core-shell structure of magnetite nanoparticles coated with alginate

The adsorption of alginate (Alg) onto the surface of in water dispersed Fe₃O₄ nanoparticles and zeta potential of alginate-coated Fe₃O₄ nanoparticles have been investigated to optimize the colloidal stability of Alg-coated Fe₃O₄ nanoparticles. The adsorption amount of Alg increased with the decrease of adsorption pH. The zeta potential of Fe₃O₄ nanoparticles shifted to a lower value after adsorption of Alg. The lower adsorption pH was the lower zeta potential of Fe₃O₄ nanoparticles became. The Alg-coated Fe₃O₄ nanoparticles were found to be stabilized by steric and electrostatic repulsions. Those prepared at pH 6 were not stable around pH 5, and those prepared at pH 4 became unstable at pH below 3.5. Alg of M_w 45 kDa was a little bit more adsorbed onto nanoparticles surface than that of M_w 24 kDa. An average Fe₃O₄ core size of 9.3 ± 1.7 nm was found by transmission electronic microscopy. An average hydrodynamic diameter of 30-150 nm was measured by photon correlation spectroscopy. However, an average core size of 10 nm and an average hydrodynamic diameter of 38 nm were estimated from the magnetization curve of the concentrated magnetic fluids (MFs). The maximum available saturation magnetization of MFs was about 3.5 kA/m.     

Stress-induced cubic-tetragonal transformation in partially stabilized ZrO2: Raman spectroscopy study

Regularities of the cubic-tetragonal transformation (C→t′) in partially stabilized zirconia were studied with Raman spectroscopy and high-temperature Raman spectroscopy techniques. New ‘low temperature’ mechanism of tetragonal nanoparticles formation in a volume of cubic solid solution was revealed in ZrO₂-Gd₂O₃ (Eu₂O₃) (6-8 mol%) single crystals. This mechanism includes nucleation of the tetragonal nanoparticles due to diffusionless C→t′ phase transformation at the first stage and gradual decrease of the stabilizer concentration inside t′-domains after subsequent low-temperature annealing. Predominant orientation of tetragonal domains due to the stress-induced C→t′ transformation was registered in ZrO₂-Gd₂O₃ (8 mol%) single crystals.     

Low-temperature sintering and microwave dielectric properties of Ca2Zn4Ti15O36 ceramics

The sintering behavior, microstructures, and microwave dielectric properties of Ca₂Zn₄Ti₁₅O₃₆ ceramics with B₂O₃ addition were investigated. The crystalline phases and microstructures of Ca₂Zn₄Ti₁₅O₃₆ ceramics with 0-10 wt% B₂O₃ addition were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS). The sintering temperature of Ca₂Zn₄Ti₁₅O₃₆ ceramic was lowered from 1170 to 930 °C by 10 wt% B₂O₃ addition. Ca₂Zn₄Ti₁₅O₃₆ ceramics with 8 wt% B₂O₃ addition sintered at 990 °C for 2 h exhibited good microwave dielectric properties, i.e., a quality factor (Qf) 11,400 GHz, a relative dielectric constant (ε_r) 41.5, and a temperature coefficient of resonant frequency (τ_f) 94.4 ppm/°C.     

Characterization of BCN films synthesized by radiofrequency plasma enhanced chemical vapor deposition

Boron carbonitride (BCN) films have been synthesized on Si(1 0 0) substrate by radio frequency plasma enhanced chemical vapor deposition using tris-(dimethylamino)borane (TDMAB) as a precursor. The deposition was performed at the different RF powers of 400-800 W, at the working pressure of 2×10⁻¹ Torr. The formation of the sp²-bonded BCN phase was confirmed by Fourier transform infrared spectroscopy. X-ray photoelectron spectroscopy measurements showed that B atoms were bonded to C and N atoms to form the BCN atomic hybrid configurations with the chemical compositions of B₅₂C₁₂N₃₆ (sample 1; prepared at the RF power of 400 W), B₅₂C₁₀N₃₈ (sample 2; at 500 W) and B₄₆C₁₈N₃₆ (sample 3; at 800 W), respectively. Near-edge X-ray absorption fine structure (NEXAFS) measurements indicated that B atoms were bonded not only to N atoms but also to C atoms to form various configurations of sp²-BCN atomic hybrids. The polarization dependence of NEXAFS suggested that the predominant hybrid configuration of sp²-BCN films oriented in the direction perpendicular to the Si substrate.     

Pulsed laser induced synthesis of scheelite-type colloidal nanoparticles in liquid and the size distribution by nanoparticle tracking analysis

Pulsed laser ablation (PLA) of ceramic target in liquid phase was successfully employed to prepare calcium tungstate (CaWO₄) and calcium molybdate (CaMoO₄) colloidal nanoparticles. The crystalline phase, particle morphology and optical property of the colloidal nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and Raman spectroscopy. The produced stable colloidal suspensions consisted of the well-dispersed nanoparticles showing a spherical shape. The mechanism for the laser ablation and nanoparticle forming was discussed under consideration of photo-ablation process. Nanoparticle tracking analysis using optical microscope combined with image analysis was proposed to determine the size distribution function of the prepared colloidal nanoparticles. The mean size of the CaWO₄ and CaMoO₄ colloidal nanoparticles were 16 and 29 nm, with a standard deviations of 2.1 and 5.2 nm, respectively.     

Luminescence properties of Tb implanted ZnO

ZnO [0 0 0 1] crystals were irradiated at room temperature with Tb⁺ ions of 400 keV with fluences from 1×10¹⁶ to 2×10¹⁷ cm⁻². The implanted layer was examined by several methods, including radioluminescence (RL), Rutherford backscattering spectrometry (RBS) and optical spectroscopy. The optical extinction spectra were simulated using Mie scattering theory. Absorption spectra predicted by Mie theory for particles of decreasing diameter were compared with those obtained experimentally. Some qualitative agreement between theoretical and experimental data was achieved. It was also shown that the intensities of the characteristic green emission bands associated with Tb produced by ⁵D₄→⁷F_j=5,4 transitions have increased about 8 times after annealing. Optical spectroscopy and radioluminescence data have revealed that the ion implantation is a promising tool for synthesizing Tb nanoparticles in the ZnO surface. The Tb nanoparticles exhibit a rather weak plasma resonance.     

Synthesis process and the luminescence properties of rare earth doped NaLa(WO4)2 nanoparticles

Rare earth doped NaLa(WO₄)₂ nanoparticles have been prepared by a simply hydrothermal synthesis procedure. The X-ray diffraction (XRD) pattern shows that the Eu³⁺-doped NaLa(WO₄)₂ nanoparticles with an average size of 10-30 nm can be obtained via hydrothermal treatment for different time at 180 °C. The luminescence intensity of Eu³⁺-doped NaLa(WO₄)₂ nanoparticles depended on the size of the nanoparticles. The bright upconversion luminescence of the 2 mol% Er³⁺ and 20 mol% Yb³⁺ codoped NaLa(WO₄)₂ nanoparticles under 980 nm excitation could also be observed. The Yb³⁺-Er³⁺ codoped NaLa(WO₄)₂ nanoparticles prepared by the hydrothermal treatment at 180 °C and then heated at 600 °C shows a 20 times stronger upconversion luminescence than those prepared by hydrothermal treatment at 180 °C or by hydrothermal treatment at 180 °C and then heated at 400 °C.     

Nanofibers and nanoplatelets of MoO3 via an electrospinning technique

Polyvinyl alcohol (PVA)/ammonium molybdate composite fibers were prepared by using sol-gel processing and electrospinning technique. After calcinations of the above precursor fibers at 500 °C, MoO₃ nanofibers with a diameter of 100-150 nm were successfully obtained. MoO₃ nanoplatelets and submicron platelets were prepared by further calcinations of the MoO₃ nanofibers at 600 and 700 °C. The products were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM). A possible growth mechanism for the MoO₃ nanofibers and nanoplatelets was suggested.     

Polyol-assisted synthesis of TiO2 nanoparticles in a semi-aqueous solvent

TiO₂ (anatase and rutile) nanoparticles with an average crystallite size of 20-40 nm have been prepared at room temperature by polyol-mediated synthesis technique in a semi-aqueous solvent medium using titanium iso-propoxide as the titanium source, acetone as the oil phase and ethylene glycol as the stabilizer. Phase and microstructure of the resultant materials have been characterized by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy and Raman spectroscopy. Photocatalytic degradation of acetaldehyde using TiO₂ nanoparticles was investigated by gas-chromatography technique.     

Characterization, sintering and dielectric properties of nanocrystalline zinc oxide prepared by a citric acid-based combustion route

Nanosized zinc oxide has been synthesized through a novel single step solution combustion route using citric acid as fuel. The X-ray diffraction (XRD) analysis revealed that the synthesized ZnO nanopowder has the pure wurtzite structure. The phase purity of the nanopowder has been confirmed using differential thermal analysis (DTA), thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FT-IR). The morphology and crystalline size of the as-prepared nanopowder characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) revealed that the powder consisted of a mixture of nanoparticles and nanorods. The nanocrystalline ZnO could be sintered to ∼97% of the theoretical density at 1200 °C in 4 h. The dielectric constant (ε_r) and dielectric loss (ε_i) of sintered ZnO pellets at 5 MHz were 1.38 and 9×10⁻², respectively, at room temperature.     

A comprehensive overview on the structure and comparison of magnetic properties of nanocrystalline synthesized by a thermal treatment method

This study reports the simple synthesis of MFe₂O₄ (where M=Zn, Mn and Co) nanostructures by a thermal treatment method, followed by calcination at various temperatures from 723 to 873 K. Poly(vinyl pyrrolidon) (PVP) was used as a capping agent to stabilize the particles and prevent them from agglomeration. The pyrolytic behaviors of the polymeric precursor were analyzed by use of simultaneous thermo-gravimetry analyses (TGA) and derivative thermo-gravimetry (DTG) analyses. The characterization studies were conducted by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Fourier transform infrared spectroscopy (FT-IR) confirmed the presence of metal oxide bands for all the calcined samples. Magnetic properties were demonstrated by a vibrating sample magnetometer (VSM), which displayed that the calcined samples exhibited different types of magnetic behavior. The present study also substantiated that magnetic properties of ferrite nanoparticles prepared by the thermal treatment method, from viewing microstructures of them, can be explained as the results of the two important factors: cation distribution and impurity phase of α-Fe₂O₃. These two factors are subcategory of the preparation method which is related to macrostructure of ferrite. Electron paramagnetic resonance (EPR) spectroscopy showed the existence of unpaired electrons ZnFe₂O₄ and MnFe₂O₄ nanoparticles while it did not exhibit resonance signal for CoFe₂O₄ nanoparticles.     

Magnetic properties of prussian blue modified Fe3O4 nanocubes

Size controlled cubic Fe₃O₄ nanoparticles in the size range 90–10 nm were synthesized by varying the ferric ion concentration using the oxidation method. A bimodal size distribution was found without ferric ion concentration and the monodispersity increased with higher concentration. The saturation magnetization decreased from 90 to 62 emu/g when the particle size is reduced to 10 nm. The Fe₃O₄ nanoparticles with average particle sizes 10 and 90 nm were surface modified with prussian blue. The attachment of prussian blue with Fe₃O₄ was found to depend on the concentration of HCl and the particle size. The saturation magnetization of prussian blue modified Fe₃O₄ varied from 10 to 80 emu/g depending on the particle size. The increased tendency for the attachment of prussian blue with smaller particle size was explained based on the surface charge. The prussian blue modified magnetite nanoparticles could be used as a radiotoxin remover in detoxification applications.     

Thermochemical behavior of metallic citrate precursors for the production of pure LaAlO3

Pure LaAlO₃ nanoparticles were synthesized, using a citrate-precursor technique. La(NO₃)₃, Al(NO₃)₃, and C₃H₄(OH)(COOH)₃, in a molar ratio of 1:1:4.5, were dissolved in deionized water. The pH of the aqueous solution was adjusted using NH₄OH. After drying, the citrate precursors were charred at 350 °C, followed by calcination at different temperatures. The thermochemical behavior of the charred citrate precursor to form LaAlO₃ was investigated using X-ray diffractometry, infrared spectroscopy, thermogravimetric analysis, and differential thermal analysis. While the charred specimen obtained at pH=2 (without NH₄OH addition) was composed of LaAl(OOCH₂)₃, the charred specimens obtained at pH>2 were composed of LaAlO_3−x−y(CO₃)_x(OH)_2y. All these metallic salts were decomposed at temperatures between 600 and 780 °C to form crystalline LaAlO₃ but calcining the specimens in air at ?800 °C were required to remove all residual chars to produce pure LaAlO₃. At 900 °C, the citrate-derived particles obtained at pH>2 were composed of LaAlO₃ crystallites with an average size of ∼30 nm.     

Synthesis of quasi-1D cuprous oxide nanostructure and its structural characterizations

A wealth of superfine polycrystalline cuprous oxide (Cu₂O) nanowires have been synthesized with hydrazine hydrated (N₂H₄·H₂O), act as the reducing agent, and Cu(OH)₂ nanowires, act as a soft template and surfactant, at room temperature. Two methods were employed for the synthesis of these nanowires, i.e. with and without capping agent (polyethylene glycol Mw 8000). Techniques of powder X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED) pattern, electron diffraction X-ray (EDX) spectroscopy, and UV-visible (UV-vis) spectroscopy have been used to characterize the morphology, structure, crystallinity, purity, and composition of nanowires. The average diameters of Cu₂O nanowires, prepared with and without capping agent, were observed to be 8-10 and 12-15 nm and lengths of several microns, respectively. It is found that capping agent (PEG) confines the dimensions of synthesized nanowires. In addition, the observed optical band gap of products show blue-shift effect compared to the bulk Cu₂O (E_g=2.17 eV), which ascribe it as a promising material for the conversion between solar energy and electrical or chemical energy.     

Formation of gold nanoparticles in heat-treated reactive co-sputtered Au-SiO2 thin films

In this work, formation of gold nanoparticles in radio frequency (RF) reactive magnetron co-sputtered Au-SiO₂ thin films post annealed at different temperatures in Ar + H₂ atmosphere has been investigated. Optical, surface topography, chemical state and crystalline properties of the prepared films were analyzed by using UV-visible spectrophotometry, atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and X-ray diffractometry (XRD) techniques, respectively. Optical absorption spectrum of the Au-SiO₂ thin films annealed at 800 °C showed one surface plasmon resonance (SPR) absorption peak located at 520 nm relating to gold nanoparticles. According to XPS analysis, it was found that the gold nanoparticles had a tendency to accumulate on surface of the heat-treated films in the metallic state. AFM images showed that the nanoparticles were uniformly distributed on the film surface with grain size of about 30 nm. Using XRD analysis average crystalline size of the Au particles was estimated to about 20 nm.     

Solvothermal synthesis and characterization of CdSe nanocrystals with controllable phase and morphology

Zinc blende (ZB) CdSe hollow nanospheres were solvothermally synthesized from the reaction of Cd(NO₃)₂·4H₂O with a homogeneously secondary Se source, which was first prepared by dissolving Se powder in the mixture of ethanol and oleic acid at 205 °C. As Se power directly reacted with Cd(NO₃)₂·4H₂O in the above mixed solvents, wurtzite (W) CdSe solid nanoparticles were produced. Time-dependent experiments suggested that the formation of CdSe hollow nanospheres was attributed to an inside-out Ostwald ripening process. The influences of reaction time, temperature and ethanol/oleic acid volume ratio on the morphology, phase and size of the hollow nanospheres were also studied. Infrared (IR) spectroscopy investigations revealed that oleic acid with long alkene chains behaved as a reducing agent to reduce Se powder to Se²⁻ in the synthesis. Photoluminescence (PL) measurements showed that the ZB CdSe hollow nanospheres presented an obvious blue-shifted emission by 42 nm, and the W CdSe solid nanoparticles exhibited a band gap emission of bulk counterpart.     

Photocatalytic abilities of gel-derived P-doped TiO2

P-doped TiO₂ nanoparticles were synthesized through hydrolysis and condensation of Ti(OC₂H₅)₄ with H₃PO₄ additions. Effects of [H₃PO₄]/[Ti(OC₂H₅)₄] molar ratios on the anatase-to-rutile phase transformation, crystallite sizes, surface areas, and photocatalytic abilities of the gel-derived P-doped TiO₂ were investigated. The P-doped TiO₂ nanoparticles prepared by [H₃PO₄]/[Ti(OC₂H₅)₄]=0.03 were composed of anatase monophase even at 900 ^oC and possessed very strong photocatalytic ability. Kinetic studies on the P-doped TiO₂ to photocatalytically decompose methylene blue under irradiation of 365 nm UV light found that the P-doped TiO₂ prepared by [H₃PO₄]/[Ti(OC₂H₅)₄]=0.03 and calcined at 800 ^oC had the specific reaction rates, at 25 °C, k_A,m=0.76 m³/(kg min) (based on the mass of P-doped TiO₂) and k_A,BET=46.2×10⁻⁶ m/min (based on the BET surface area of P-doped TiO₂), which is superior to the performance of a commercial product, P25 (k_A,m=0.22 m³/(kg min) and k_A,BET=4.8×10⁻⁶ m/min).