LED白光源用Pr~(3+),Ce~(3+):YAG光纤制备与特性

采用激光加热基座法制备LED白光源用Pr3+,Ce3+:YAG单晶光纤荧光材料,对所制备材料的荧光光学特性进行了实验分析结果表明,在Pr3+和Ce3+共掺发光过程中,Pr3+离子的发光可以通过Ce3+敏化作用使得其610 nm谱线荧光强度得到有效增强;利用所制备Pr3+,Ce3+:YAG单晶光纤荧光材料与蓝色LED合成产生高效LED光纤白光源,光源的色坐标为(x＝0.322,y＝0.335),显色指数84.3,表明光源品质良好,有望用于未来高效大功率光纤白光源.     

Ce^3＋离子敏化Eu^3＋：Cr^3＋：Sm^3＋：YAG外延层的荧光现象

对Ce^3 :Eu^3 :Cr^3 :Sm^3 :YAG外延层中的荧光敏经现象进行了报道和分析，在较高浓度的Ce^3 离子掺杂时，外处层在蓝色、绿色波段出现了新的荧光谱线，可解释为在Ce^3 离子每化作用下，Eu^3 离子产生了由高位激发态能级^5Di(i=1,2,3）直接到基态能级^7Fj(j=0,1,2,3）的辐射跃迁过程，并且这种Ce^3 :Eu^3 :Cr^3 :Sm^3 :YAG外延层还是一种新颖的白色单晶荧光材料。     

LED白光源用Pr3+,Ce3+:YAG光纤制备与特性

采用激光加热基座法制备LED白光源用Pr3+,Ce3+:YAG单晶光纤荧光材料,对所制备材料的荧光光学特性进行了实验分析结果表明,在Pr3+和Ce3+共掺发光过程中,Pr3+离子的发光可以通过Ce3+敏化作用使得其610 nm谱线荧光强度得到有效增强|利用所制备Pr3+,Ce3+:YAG单晶光纤荧光材料与蓝色LED合成产生高效LED光纤白光源,光源的色坐标为(x＝0.322,y＝0.335),显色指数84.3,表明光源品质良好,有望用于未来高效大功率光纤白光源.     

Ba2SiO4荧光粉中Ce3+和Eu2+的光谱性质和能量传递

采用高温固相法合成了绿色荧光粉Ba2SiO4:Ce3 ,Eu2 .测量了它们的吸收光谱、激发光谱和发射光谱,观察到了Ba2SiO4中Ce3 对Eu2 发光的敏化现象,发光的敏化作用缘于Ce3 和Eu2 之间的高效无辐射能量传递.     

基于Ce:YAG单晶的白光发光二极管性能研究

以Ce:YAG单晶取代传统Ce:YAG荧光粉用于制备白光发光二极管(LED),研究了Ce:YAG单晶厚度及驱动电压的变化对其发射光谱、色坐标、亮度、光视效能和色温的影响。研究结果表明,在基于Ce:YAG单晶的白光LED中,发射光的色坐标以及蓝光与黄绿光之间的相对强度可通过对Ce:YAG单晶片厚度的改变进行调整。在恒定电压驱动下,白光LED样品的亮度、光视效能和色温均随单晶片厚度的减小而增加。当Ce:YAG单晶厚度为0.6mm时,可获得较纯的白发射光,并且其色坐标具有较高的可靠性和稳定性,基本不受驱动电压变化的影响。研究结果表明Ce:YAG单晶是一种可用于新型白光LED的理想荧光材料。     

白光LED用新型Ce,Pr掺杂的YAG单晶荧光材料的光谱性能研究

为了改善白光LED用荧光材料效率低、均匀性差、光衰大、寿命短及物化性能差等不足,本文采用单晶荧光材料取代荧光粉来制备白光LED,并对白光LED用新型YAG单晶荧光材料的制备和光谱性能进行了研究.采用提拉法生长了白光LED用Ce∶YAG及Pr,Ce∶YAG晶体,并通过吸收光谱,激发、发射光谱对晶体材料的光谱特性进行表征.研究表明,Ce∶YAG单晶荧光材料可以被发射波长460 nm左右的蓝光芯片有效激发,产生一个范围为480~650 nm宽峰发射.通过Pr3+,Ce3+离子共掺杂可以有效补偿Ce3+离子单掺杂YAG荧光材料发光中的红色发光成分.     

纳米YAG∶Ce3+, Mn+(Mn+=Ca2+, Gd3+)荧光粉的结构与发光性能

当前商用白光LED器件中YAG∶Ce3+荧光粉的单一黄光发射,导致其缺乏红光限制了器件的应用和发展,在YAG∶Ce3+中掺杂其他离子是解决该问题的有效途径之一。采用溶胶凝胶法制备了系列单掺Ce3+,Ca2+和Gd3+的YAG纳米荧光粉。研究了离子掺杂量对荧光粉的物相、结构、形貌、粒度、发光性能及量子效率的影响,分析了发光机理。结果表明：制备的纳米荧光粉粒径为100～200 nm。Ce3+和Gd3+掺杂时均得到YAG纯相,但晶体结构膨胀,晶面衍射峰向小角度方向移动。样品结晶度随Ce3+和Ca2+(<0.025 mol)掺杂量增大变化不明显,随Gd3+则呈现逐步降低趋势。三种离子掺杂量增大时,Ce3+的晶格能上升,5d能级晶体场劈裂加剧;Gd系列荧光粉激发和发射光谱随掺杂量的增大发生红移,Ce和Ca系列则因掺杂量小表现不明显。荧光粉发光强度随Ce3+掺杂量上升先增大后减小,最佳掺杂量为0.06 mol;随Gd3+掺杂量增加逐步降低;随Ca2+掺杂量增大则急剧下降,0.03 mol掺杂量时荧光强度几乎为零,YAG晶体结构破坏,生成YAM和YAP相。研究的开展,将对后续纳米YAG荧光粉及其相关功能材料的进一步开发使用提供一定的理论依据和实践参考。     

硼酸盐玻璃中某些稀土离子的浓度效应及其能量传递过程

本文系统地报道了硼酸盐玻璃中Ce3+、Sm33+、Eu3+、Ga3+、Tb3+、Dy3+浓度效应,观察到Eu3+、Gd3+、Tb3+在硼酸盐玻璃中随浓度增加其发光强度增强,而Ce3+、Sm3+、Dy3+当其浓度增加到一定数值后,发光强度反而减弱,初步探讨了不同浓度效应的原因.本文还观察到硼玻璃中某些稀土离子对Eu3+、Tb3+离子发光的敏化作用,及讨论了Gd3+和Eu3+、Tb3+之间的能量传递过程,计算其能量传递的效率和几率.估计了能量传递的规律机理.     

Ce~(3+)-Yb~(3+)共掺YAG荧光粉量子剪裁发光的浓度及温度特性

采用高温固相法制备了不同掺杂浓度的YAG∶1%Ce~(3+),x%Yb~(3+)(x=5,10,15,20,25)系列荧光粉。在450 nm蓝光激发下,测试了样品的发射光谱,得到了中心波长在550 nm的可见宽带发射(Ce~(3+):5d→4f)和1 030 nm的近红外发射(Yb~(3+):2F_(5/2)→2F_(7/2))。可见和近红外发射强度随Yb~(3+)掺杂浓度的变化表明Ce~(3+)到Yb~(3+)存在能量传递过程,并得到Yb~(3+)的猝灭浓度为15%。在低温条件下(80~300 K)测试YAG∶1%Ce~(3+),15%Yb~(3+)样品的发射光谱和拉曼光谱,通过对其量子剪裁发光温度特性的分析,描述了基质声子在Ce~(3+)到Yb~(3+)的能量传递过程中起到的重要作用。     

稀土五磷酸盐(REP5O14)晶体的光谱性质

本文在较前人宽的波段内系统地研究了REP5O14(RE=Ce3+,Pr3+,Nd3+,Sm3+,Eu3+,Gd3+,Tb3+,Dy3+,Ho3+,Er3+,Tm3+,Yb3+)单晶的吸收光谱、激发光谱与荧光光谱.合理地确定了谱项.关于SmP5O14,GdP5O14,DyP5O14,TmP5O14与YbP5O14等晶体光谱的研究,至今尚未见报导.这些晶体系统的光谱数据,对于了解它们的性质及其应用方面,都是很有用的.     

Ca8Mg(SiO4)4Cl2中Ce3+和Eu2+的光谱性质和能量传递

首次合成了Ｃｅ＾３＋和Ｅｕ＾２＋共激活氯硅酸镁钙Ｃａ８Ｍｇ（ＳｉＯ４）４Ｃｌ２：Ｃｅ＾３＋，Ｅｕ＾２＋高效绿色荧光粉，报道了它们的漫反射光谱、激发和发射光，观察到氯硅酸镁钙中Ｃｅ＾３＋ Ｅｕ＾２＋     

Ln(BO_3,PO_4)[Ln=La,Y]基质中Ce~(3+)、Tb~(3+)、Gd~(3+)的光谱

研究了硼磷酸镧和硼磷酸钇基质中Ce3 +、Tb3+、Gd3+的发射光谱和激发光谱。结果表明 :La(BO3,PO4 ) :Ce ,Tb体系中加入钆后 ,Ce3+的发射降低 ,Tb3+的发射增强 ;Y(BO3,PO4 ) :Ce ,Tb体系中加入钆后 ,Ce3+和Tb3 +的发射均增强 ,且前者增加的幅度高于后者。因此在La(BO3,PO4 ) :Ce ,Tb ,Gd体系中Gd3+离子起着能量传递中间体和敏化剂的作用 ;在Y(BO3,PO4 ) :Ce,Tb ,Gd体系中Gd3 +离子只起敏化剂作用 ,并且阻碍Ce3+→Tb3+的能量传递。与Y(BO3,PO4 ) :Ce,Tb ,Gd相比 ,La(BO3,PO4 ) :Ce,Tb ,Gd对紫外吸收强 ,2 5 4nm激发下发出的光绿色纯度高 ,强度大 ,更适合做荧光灯中的绿粉     

Quantum cutting in Gd2SiO5: Eu3+ by VUV excitation

The emission and excitation spectra of Gd2SiO5: Eu3+ were investigated using the VUVbeam line of the Beijing Synchrotron Radiation Facility (BSRF). The experimental results werediscussed in the frame of visible quantum cutting process involved in Gd3+-Eu3+ system. Upon di-rect excitation into the 6GJ states of Gd3+, two visible photon emissions from Eu3+ were observed.Cursory evaluation proved that Gd2SiO5: Eu3+ is an efficient visible quantum cutter.     

Energy transfer and excitation wavelength dependent long-lasting phosphorescence in Pr activated Y3Al5O12

Long-lasting phosphorescence (LLP) was observed in Pr³⁺-doped Y₃Al₅O₁₂ (YAG:Pr) after it was excited by 240 or 290 nm light. The photoluminescence (PL) and LLP properties were studied. It is interesting that the PL and LLP spectra were different. In the PL emission spectra both the emissions of d-f and f-f transitions of Pr³⁺ ions were observed. However, in the LLP spectra of YAG:Pr the emissions of d-f transition were absent. It is deduced that the differences were due to the energy transfer process between traps and emission centers. On the other hand, significant differences were observed between the two LLP spectra after the sample was excited by 240 and 290 nm lights, respectively. The thermoluminescence (TL) properties were also studied. It is suggested that these studies will be significant for understanding the mechanism of LLP phenomenon.     

Tunable white luminescence and energy transfer in (Cu+)2, Eu3+ codoped sodium silicate glasses

Luminescent properties of (Cu+)2, Eu3+ single-doped and codoped sodium silicate glasses were systematically investigated by excitation spectra, emission spectra, and decay curves. Due to the efficient energy transfer from (Cu+)2 pairs to Eu3+, varied hues from green to yellowish white and eventually to orange were generated by tuning the content of Eu3+. A perfect white-light emission with CIE coordinates (X=0.336,Y=0.346) was realized in (Cu+)2, Eu3+ and Ce3+ codoped samples. Our research indicates the potential application of (Cu+)2, Eu3+ codoped sodium silicate glasses for converting phosphors for UV LED chips to generate white LEDs.     

Ce3+和Tb3+, Eu3+在六方NaLnF4(Ln=La,Gd或Y)中的发光和能量传递

本文报道Ce3+掺杂和Ce3+—Tb3+、Ce3+—Eu3+共掺杂的六方NaLnF4(Ln=La,Gd或Y)发光体的研究结果:氟配位环境使Ce3+在300nm附近发射并有很低的猝灭浓度;阳离子缺陷发光中心可能形成于NaGdF4基质中并被Ce3+—Gd3+共同敏化;Ce3+的发光可以因Tb3+掺杂而增强,反过来Ce3+亦会使Tb3+的5D3/5D4发射强度比减小;Ce3+含量增加使Eu3+的5D2/5D1及5D2/5D0发射强度比减小,这与Ce3+的2F5/2→2F7/2跃迁和Eu3+的5D2→D1跃迁能级差匹配而产生共振能量传递有关。     

RExPr1-xP5O14晶体生长及其光谱

水热法生长了RExPr1-xP5O14单品,RE=La,Ce,Nd,Eu,Gd,Yb,Tm,Y,(x=0.1)单晶的最大线度为2cm。我们研究了原料的合成,观察了吸收,荧光,红外光谱,并计算了22400～16380cm-1范围内的Pr3+离子的振子强度。热重分析观察到在867～930℃有弱的分解。X射线衍射分析指出:结构为单斜晶系,空间群为P21/C;晶胞参数为a=8.73Å,b=9.04Å,c=13.02Å,β=90.5°     

稀土离子(Eu3+,Tb3+,Ce3+)掺杂ZnAl2O4/SiO2微晶玻璃的制备与发光性能

采用凝胶法分别制备出4.5ZnO-5.5Al₂O₃-90SiO₂(ZAS)以及ZAS[DK]:RE³⁺ (RE=Eu,Tb,Ce) 透明微晶玻璃。利用X射线衍射仪(XRD)、透射电子显微镜(TEM)和荧光光谱仪(PL)等测试手段,研究了稀土离子掺杂浓度对ZAS微晶玻璃的结构和发光性能的影响。XRD结果表明,ZAS[DK]:RE³⁺ (RE=Eu,Tb,Ce)微晶玻璃包含ZnAl₂O₄晶相和SiO₂非晶相,ZnAl₂O₄平均晶粒尺寸约为30 nm,稀土离子的掺杂没有显著改变原来的ZnAl₂O₄晶体结构。TEM结果表明,900 ℃时ZnAl₂O₄从ZAS体系中析出。PL光谱显示,Eu³⁺ 存在 ⁵D₀→⁷F₂跃迁,ZAS[DK]:Eu³⁺在611 nm 处发出强烈的红色光;由于Tb³⁺ 的⁵D₄→⁷F₅ 跃迁,ZAS[DK]:Tb³⁺在541 nm 处发出明亮的绿色光;ZAS[DK]:Ce³⁺ 在381 nm处显示了蓝光发射,对应于Ce³⁺ 的5d→4f 轨道跃迁。ZAS[DK]:RE³⁺ (RE=Eu, Tb, Ce)的PL发射光谱存在着浓度猝灭现象,Eu³⁺、Tb³⁺ 和Ce³⁺的最佳单掺杂摩尔分数分别为20%、20%和3%。CIE色度图表明,ZAS[DK]: RE³⁺ (RE=Eu,Tb,Ce)的色坐标分别位于红光、绿光和蓝光区域。实验结果表明,ZAS:RE³⁺ (RE=Eu,Tb,Ce) 微晶玻璃是一种良好的可用于全色显示的白光LED材料。     

掺铈、钆、铽的三磷酸镧的合成及其光谱

本文首次采用溶液沉淀法合成了一系列LaP3O9:Ce、Gd、Tb磷光体.经X射线结构分析表明、它们是较纯的LaP3O9相,系环状结构,属于正交晶系,其晶胞参数为a=11.19(Å),b=8.54(Å),c=7.28(Å).测定了这些化合物的激发和发射光谱、相对亮度及Ce3+的荧光寿命,观察到在此基质中Ce3+与Gd3+光谱重叠,它们之间存在着一定的相互作用,Ce3+能有效地敏化Tb3+,从而大大地增强Tb3+的发射,LaP3O9:Ce、Tb可能成为一种新的高效绿色发光材料.在Ce-Tb共掺的体系中加入少量Gd却使发光亮度稍有下降,这可能是由于Gd3+的竞争吸收和独立发射所致.从Ce3+的荧光寿命变化可知,Ce3+对Gd3+的能量传递较弱,而Ce3+对Tb3+则很有效.     

P5+ Ion Doped Gd2SiO5:Ce3+ Scintillation Crystal

Bulletin of the Lebedev Physics Institute - Ce3+, P5+, Ca2+, and Zn2+ ion doped Gd2SiO5 crystals are grown by the Czochralski method. The pulsed cathodoluminescence spectra, light yield, and...