High-pressure transitions in MgAl2O4 and a new high-pressure phase of Mg2Al2O5

Phase transitions in MgAl₂O₄ were examined at 21-27 GPa and 1400-2500 °C using a multianvil apparatus. A mixture of MgO and Al₂O₃ corundum that are high-pressure dissociation products of MgAl₂O₄ spinel combines into calcium-ferrite type MgAl₂O₄ at 26-27 GPa and 1400-2000 °C. At temperature above 2000 °C at pressure below 25.5 GPa, a mixture of Al₂O₃ corundum and a new phase with Mg₂Al₂O₅ composition is stable. The transition boundary between the two fields has a strongly negative pressure-temperature slope. Structure analysis and Rietveld refinement on the basis of the powder X-ray diffraction profile of the Mg₂Al₂O₅ phase indicated that the phase represented a new structure type with orthorhombic symmetry (Pbam), and the lattice parameters were determined as a=9.3710(6) Å, b=12.1952(6) Å, c=2.7916(2) Å, V=319.03(3) Å³, Z=4. The structure consists of edge-sharing and corner-sharing (Mg, Al)O₆ octahedra, and contains chains of edge-sharing octahedra running along the c-axis. A part of Mg atoms are accommodated in six-coordinated trigonal prism sites in tunnels surrounded by the chains of edge-sharing (Mg, Al)O₆ octahedra. The structure is related with that of ludwigite (Mg, Fe²⁺)₂(Fe³⁺, Al)(BO₃)O₂. The molar volume of the Mg₂Al₂O₅ phase is smaller by 0.18% than sum of molar volumes of 2MgO and Al₂O₃ corundum. High-pressure dissociation to the mixture of corundum-type phase and the phase with ludwigite-related structure has been found only in MgAl₂O₄ among various A²⁺B³⁺₂O₄ compounds.     

Structural and magnetic characterization of BiFexMn2-xO5 oxides (x=0.5, 1.0)

The title compounds have been synthesized by a citrate technique followed by thermal treatments in air (BiFe_0.5Mn_1.5O₅) or under high oxygen pressure conditions (BiFeMnO₅), and characterized by X-ray diffraction (XRD), neutron powder diffraction (NPD) and magnetization measurements. The crystal structures have been refined from NPD data in the space group Pbam at 295 K. These phases are isostructural with RMn₂O₅ oxides (R=rare earths) and contain infinite chains of Mn⁴⁺O₆ octahedra sharing edges, linked together by (Fe,Mn)³⁺O₅ pyramids and BiO₈ units. These units are strongly distorted with respect to those observed in other RFeMnO₅ compounds, due to the presence of the electronic lone pair on Bi³⁺. It is noteworthy the certain level of antisite disorder exhibited in both samples, where the octahedral positions are partially occupied by Fe cations, and vice versa. BiFe_xMn_2−xO₅ (x=0.5, 1.0) are short-range magnetically ordered below 20 K for x=0.5 and at 40 K for x=1.0. The main magnetic interactions seem to be antiferromagnetic (AFM); however, the presence of a small hysteresis in the magnetization cycles indicates the presence of some weak ferromagnetic (FM) interactions.     

Synthesis and crystal structure of Bi6.4Pb0.6P2O15.2: A new polymorph in the series Bi6+xM1−xP2O15+y

Bi_6.4Pb_0.6P₂O_15.2 is a polymorph of structures with the general stoichiometry Bi_6+xM_1−xP₂O_15+y. However, unlike previously published structures that consist of layers formed by edge sharing OBi₄ tetrahedra bridged by PO₄ and TO₆ (T=transition metal) tetrahedra and octahedra the title compound's structure is more complex. It is monoclinic, C2, a=19.4698(4) Å, b=11.3692(3) Å, c=16.3809(5) Å, β=101.167(1)°, Z=10. Single-crystal X-ray diffraction data were refined by least squares on F² converging to R₁=0.0387, wR₂=0.0836 for 7023 intensities. The crystal twins by mirror reflection across (001) as the twin plane and twin component 1 equals 0.74(1). Oxygen ions are in tetrahedral coordination to four metal ions and the O(BiPb)₄ units share corners to form layers that are part of the three-dimensional framework. Eight oxygen ions form a cube around the two crystallographically independent Pb ions. Pb-O bond lengths vary from 2.265(14) to 2.869(14) Å. Pairs of such cubes share an edge to form a Pb₃O₂₀ unit. The two oxygen ions from the unshared edges are part of irregular Bi polyhedra. Other oxygen ions of Bi polyhedra are part only of O(BiPb)₄ units, and some oxygen ions of the polyhedra are also part of PO₄ tetrahedra. One, two, three and or four PO₄ moieties are connected to the Bi polyhedra. Bi-O bond lengths ?3.1 Å vary from 2.090(12) to 3.07(3) Å. The articulations of Pb cubes, Bi polyhedra and PO₄ tetrahedra link into the three-dimensional structure.     

Crystal structure, thermal expansion and conductivity of anisotropic La1−xSrxGa1−2xMg2xO3−y (x=0.05, 0.1) single crystals

Crystal structure and anisotropy of the thermal expansion of single crystals of La_1−xSr_xGa_1−2xMg_2xO_3−y (x=0.05 and 0.1) were measured in the temperature range 300-1270 K. High-resolution X-ray powder diffraction data obtained by synchrotron experiments have been used to determine the crystal structure and thermal expansion. The room temperature structure of the crystal with x=0.05 was found to be orthorhombic (Imma, Z=4, a=7.79423(3) Å, b=5.49896(2) Å, c=5.53806(2) Å), whereas the symmetry of the x=0.1 crystal is monoclinic (I2/a, Z=4, a=7.82129(5) Å, b=5.54361(3) Å, c=5.51654(4) Å, β=90.040(1)°). The conductivity in two orthogonal directions of the crystals has been studied. Both, the conductivity and the structural data indicate three phase transitions in La_0.95Sr_0.05Ga_0.9Mg_0.1O_2.92 at 520-570 K (Imma-I2/a), 770 K (I2/a-R3c) and at 870 K (R3c-R-3c), respectively. Two transitions at 770 K (I2/a-R3c) and in the range 870-970 K (R3c-R-3c) occur in La_0.9Sr_0.1Ga_0.8Mg_0.2O_2.85.     

An X-ray diffraction, magnetic susceptibility and spectroscopic studies of Yb2−xCrxO3

Polycrystalline samples with general formula Yb_2−xCr_xO₃ (0<x<0.03), obtained by sol-gel method and analyzed by X-ray diffraction, formed solid solutions over all the mentioned range. Cr showed a maximum solubility of 2.8 mol% in Yb₂O₃ sesquioxide at 1000 °C. A preferential substitution of Cr³⁺ ions over two cationic sites, 8b and 24d in the space group Ia-3 was found. The lattice parameters a are found to vary linearly (10.4402(4) Å <a<10.4372(1) Å) with the composition x. The two independent atoms Yb/Cr have octahedral coordination; however, the degrees of distortion of their coordination polyhedron are different. Replacing Yb³⁺ by Cr³⁺ introduces slight changes in the atomic coordinates leading to an increase of the mean cation-anion distances. The ability of Raman spectroscopy to detect changes in local coordination is utilized. A pseudo-tetrahedral coordination for the Cr³⁺ in the 24d site was found. Magnetic susceptibility measurements of all samples were done in a temperature range of 2-50 K. For T<37 K, the inverse paramagnetic susceptibilities depend linearly on temperature. However, in the high-temperature region, for T>37 K, the inverse paramagnetic susceptibilities are non-linear versus temperature. This deviation from the Curie-Weiss behaviour was discussed.     

Anomalies in magnetic susceptibility of nonstoichiometric Nd2NiO4+δ (δ=0.049, 0.065, 0.077, 0.234)

We have investigated the influence of oxygen excess on structural and physical properties of the Nd₂NiO_4+δ compounds. Using the citrate method and subsequent annealing in air and in a reducing atmosphere a various oxygen-doped compounds were prepared. X-ray diffraction at room temperature shows that structure is strongly oxygen excess dependent. Thus, by increasing δ by up to 0.077, the compounds adopt a tetragonal structure gradually with a biphasic domain between orthorhombic and tetragonal structures. And at higher δ values, the structure becomes orthorhombic. Moreover, Rietveld analysis shows that for δ<0.077 the presence of two crystalline phases with different oxygen excess: it should be the signature of interstitial oxygen, which is distributed in heterogeneous way. The biphasic products are composed of a stoichiometric Nd₂NiO₄ phase (orthorhombic structure) and a tetragonal Nd₂NiO_4.077 phase. Magnetic susceptibility shows a deviation from Curie-Weiss law for lower oxygen excess (δ?0.077). Moreover, some anomalies in dc magnetic susceptibility curves was observed at 45, 95 and 130 K for δ<0.077. These transitions are connected to the tetragonal phase, and were attributed, respectively, to an antiferromagnetic transition, possible charge ordering and structural transition.     

Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.     

K2Mo4O13 phases prepared by hydrothermal synthesis

Hydrothermal synthesis in the K-Mo oxide system was investigated as a function of the pH of the reaction medium. Four compounds were formed, including two K₂Mo₄O₁₃ phases. One is a new low-temperature polymorph, which crystallizes in the orthorhombic, space group Pbca, with Z=8 and unit cell dimensions a=7.544(1) Å, b=15.394(2) Å, c=18.568(3) Å. The other is the known triclinic K₂Mo₄O₁₃, whose structure was re-determined from single crystal data; its cell parameters were determined as a=7.976(2) Å, b=8.345(2) Å, c=10.017(2) Å, α=107.104(3)°, β=102.885(3)°, γ=109.760(3)°, which are the standard settings of the crystal lattice. The orthorhombic phase converts endothermically into triclinic phase at ca. 730 K with a heat of transition of 8.31 kJ/mol.     

The crystal chemistry of Bi6TP2O15+x, T=Fe, Ni, Zn: Isomorphism and polymorphism, structural relationship to Bi6TiP2O16

The crystal structures of compounds with nominal compositions Bi₆FeP₂O_15+x (I), Bi₆NiP₂O_15+x (II) and Bi₆ZnP₂O_15+x (III) were determined from single-crystal X-ray diffraction data. They are monoclinic, space group I2, Z=2. The lattice parameters for (I) are a=11.2644(7), b=5.4380(3), c=11.1440(5) Å, β=96.154(4)°; for (II) a=11.259(7), b=5.461(4), c=11.109(7) Å, β=96.65(1)°; for (III) a=19.7271(5), b=5.4376(2), c=16.9730(6) Å, β=131.932(1)°. Least squares refinements on F² converged for (I) to R1=0.0554, wR₂=0.1408; for (II) R₁=0.0647, wR₂=0.1697; for (III) R₁=0.0385, wR₂=0.1023. The crystals are complexly twinned by 2-fold rotation about , by inversion and by mirror reflection. The structures consist of edge-sharing articulations of OBi₄ tetrahedra forming layers in the a-c plane that then continue by edge-sharing parallel to the b-axis. The three-dimensional networks are bridged by Fe and Ni octahedra in (I) and (II) and by Zn trigonal bipyramids in (III) as well as by oxygen atoms of the PO₄ moieties. Bi also randomly occupies the octahedral sites. Oxygen vacancies exist in the structures of the three compounds due to required charge balances and they occur in the octahedral coordination polyhedron of the transition metal. In compound (III), no positional disorder in atomic sites is present. The Bi-O coordination polyhedra are trigonal prisms with one, two or three faces capped. Magnetic susceptibility data for compound (I) were obtained between 4.2 and 350 K. Between 4.2 and 250 K it is paramagnetic, μ_eff=6.1 μ_B; a magnetic transition occurs above 250 K.     

Structure and phase composition of nanocrystalline Ce1−xLuxO2−y

The microstructure and phase stability of nanocrystalline mixed oxide Lu_xCe_1−xO_2−y (x=0-1) are described. Nano-sized (3-4 nm) oxide particles were prepared by the reverse microemulsion method. Morphological and structural changes upon heat treatment in an oxidizing atmosphere were studied by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman and Yb³⁺ emission spectroscopy, the latter ion being present as an impurity in the Lu₂O₃ starting material. Up to 950 °C, the samples were single phase, with structure changing smoothly with Lu content from fluorite type (F) to bixbyite type (C). For the samples heated at 1100 °C phase separation into coexisting F- and C-type structures was observed for 0.35<x<0.7. It was also found that addition of Lu strongly hinders the crystallite growth of ceria during heat treatment at 800 and 950 °C.     

Synthesis and Characterization of the Reduced Single-Layer Manganite Sr2MnO3.5+x

The nuclear and magnetic structures of polycrystalline Sr₂MnO_3.5 have been determined by the Rietveld analysis of neutron powder diffraction data and electron diffraction techniques. The pure Mn³⁺ single-layered phase crystallizes in the primitive monoclinic space-group P2₁/c with lattice constants a=6.8524(3) Å b=10.8131(4) Å c=10.8068(4) Å β=113.247(4)°. The oxygen defects form an ordered superstructure within the perovskite block layers consisting of interconnected MnO₅ square pyramids, slightly different from those observed for the defect perovskites SrMnO_2.5 and Ca₂MnO_3.5. Magnetic susceptibility studies show a broad transition at ∼280 K, which is attributed to an overall antiferromagnetic ordering of spins, which leads to doubling of the unit cell along [100]. The magnetic unit cell comprises ferromagnetic clusters of four corner-sharing MnO₅ pyramids, which are antiferromagnetically aligned to other similar clusters within the perovskite block layers.     

Ferromagnetic ordering in ThSi2 type CeAu0.28Ge1.72

The compound CeAu_0.28Ge_1.72 crystallizes in the ThSi₂ structure type in the tetragonal space group I4₁/amd with lattice parameters a=b=4.2415(6) Å c=14.640(3) Å. CeAu_0.28Ge_1.72 is a polar intermetallic compound having a three-dimensional Ge/Au polyanion sub-network filled with Ce atoms. The magnetic susceptibility data show Curie-Weiss law behavior above 50 K. The compound orders ferromagnetically at ∼8 K with estimated magnetic moment of 2.48 μ_B/Ce. The ferromagnetic ordering is confirmed by the heat capacity data which show a rise at ∼8 K. The electronic specific heat coefficient (γ) value obtained from the paramagnetic temperature range 15-25 K is∼124(5) mJ/ mol K². The entropy change due to the ferromagnetic transition is ∼4.2 J/mol K which is appreciably reduced compared to the value of R ln(2) expected for a crystal-field-split doublet ground state and/or Kondo exchange interactions.     

Synthesis and characterization of the reduced double-layer manganite Sr3Mn2O6+x

The oxygen-deficient Ruddlesden-Popper (RP) phase Sr₃Mn₂O₆ crystallizes with an ordered array of oxygen vacancies to afford a structure in which the Mn³⁺ ions exist in a square-pyramidal environment. The MnO₅ polyhedra are linked through their corners to form a structure that is related to that observed for the single-layered material, Sr₂MnO_3.5. The nuclear and magnetic structures of a polycrystalline sample of Sr₃Mn₂O₆ have been determined using Rietveld analysis of neutron powder diffraction data and electron diffraction techniques. The pure Mn³⁺ double-layered phase crystallizes in a superstructure of the simple RP subcell: tetragonal, P4/mbm, a=10.8686(2) Å and c=20.2051(3) Å.Magnetic susceptibility studies suggest a transition at ∼250 K to a canted antiferromagnetic ordered structure. The magnetic unit-cell consists of ferromagnetic clusters of corner-sharing MnO₅ units, which are antiferromagnetically aligned to other clusters within the layers.     

Transition metal tetramolybdate dihydrates MMo4O13·2H2O (M=Co,Ni) having a novel pillared layer structure

Hydrothermal synthesis in the M/Mo/O (M=Co,Ni) system was investigated. Novel transition metal tetramolybdate dihydrates MMo₄O₁₃·2H₂O (M=Co,Ni), having an interesting pillared layer structure, were found. The molybdates crystallize in the triclinic system with space group P−1, Z=1 with unit cell parameters of a=5.525(3) Å, b=7.058(4) Å, c=7.551(5) Å, α=90.019(10)°, β=105.230(10)°, γ=90.286(10)° for CoMo₄O₁₃·2H₂O, and a=5.508(2) Å, b=7.017(3) Å, c=7.533(3) Å, α=90.152(6)°, β=105.216(6)°, γ=90.161(6)° for NiMo₄O₁₃·2H₂O The structure is composed of two-dimensional molybdenum-oxide (2D Mo-O) sheets pillared with CoO₆ octahedra. The 2D Mo-O sheet is made up of infinite straight ribbons built up by corner-sharing of four molybdenum octahedra (two MoO₆ and two MoO₅OH₂) sharing edges. These infinite ribbons are similar to the straight ones in triclinic-K₂Mo₄O₁₃ having 1D chain structure, but are linked one after another by corner-sharing to form a 2D sheet structure, like the twisted ribbons in BaMo₄O₁₃·2H₂O (or in orthorhombic-K₂Mo₄O₁₃) are.     

Rietveld refinement and photoluminescent properties of a new blue-emitting material: Eu activated SrZnP2O7

A new efficient blue phosphor, Eu²⁺ activated SrZnP₂O₇, has been synthesized at 1000 °C under reduced atmosphere and the crystal structure and photoluminescence properties have been investigated. The crystal structure of SrZnP₂O₇ was obtained via Rietveld refinement of powder X-ray diffraction (XRD) pattern. It was found that SrZnP₂O₇ crystallizes in space group of P2₁/n (no. 14), Z=4, and the unit cell dimensions are: a=5.30906(2) Å, b=8.21392(3) Å, c=12.73595(5) Å, β=90.1573(3)°, and V=555.390(3) Å³. Under ultraviolet excitation (200-400 nm), efficient Eu²⁺ emission peaked at 420 nm was observed, of which the luminescent efficiency at the optimal concentration of Eu²⁺ (4 mol%) was estimated to be 96% as that of BaMgAl₁₀O₁₇:Eu²⁺. Hence, the SrZnP₂O₇:Eu²⁺ exhibit great potential as a phosphor in different applications, such as ultraviolet light emitting diode and photo-therapy lamps.     

Preparation and structural study from neutron diffraction data of Pr5Mo3O16

The title compound has been prepared as polycrystalline powder by thermal treatments of mixtures of Pr₆O₁₁ and MoO₂ in air. In the literature, an oxide with a composition Pr₂MoO₆ has been formerly described to present interesting catalytic properties, but its true stoichiometry and crystal structure are reported here for the first time. It is cubic, isostructural with CdTm₄Mo₃O₁₆ (space group Pn-3n, Z=8), with a=11.0897(1) Å. The structure contains MoO₄ tetrahedral units, with Mo-O distances of 1.788(2) Å, fully long-range ordered with PrO₈ polyhedra; in fact it can be considered as a superstructure of fluorite (M₈O₁₆), containing 32 MO₂ fluorite formulae per unit cell, with a lattice parameter related to that of cubic fluorite (a_f=5.5 Å) as a≈2a_f. A bond valence study indicates that Mo exhibits a mixed oxidation state between 5+ and 6+ (perhaps accounting for the excellent catalytic properties). One kind of Pr atoms is trivalent whereas the second presents a mixed Pr³⁺-Pr⁴⁺ oxidation state. The similarity of the XRD pattern with that published for Ce₂MoO₆ suggests that this compound also belongs to the same structural type, with an actual stoichiometry Ce₅Mo₃O₁₆.     

Crystal structure of BaMg2Si2O7 and Eu luminescence

Crystal structure of BaMg₂Si₂O₇ was determined and refined by a combined powder X-ray and neutron Rietveld method (monoclinic, C2/c, no. 15, Z=8, a=7.24553(8) Å, b=12.71376(14) Å, c=13.74813(15) Å, β=90.2107(8)°, V=1266.44(2) Å³; R_p/R_wp=3.38%/4.77%). The structure contains a single crystallographic type of Ba atom coordinated to eight O atoms with C₁ (1) site symmetry. Under 325-nm excitation Ba_0.98Eu_0.02Mg₂Si₂O₇ exhibits an asymmetric emission band around 402 nm. The asymmetric shape of the emission band is likely associated with a small electron-phonon coupling in BaMg₂Si₂O₇. The integrated intensity of the emission band was observed to remain constant over the temperature range 4.2-300 K.     

Synthesis, structure and physical properties of GdCu4Al and GdCu4Ga

Two non-stoichiometric Gd compounds, GdCu_5−xTr_x (Tr=Al, Ga) have been synthesized from the corresponding elements by high temperature reactions in sealed tantalum containers. They crystallize in the hexagonal CaCu₅-type (Pearson's symbol hP6, space group P6/mmm, No. 191) with lattice parameters determined from single-crystal X-ray diffraction at room temperature as follows: a=5.0831(10) Å; c=4.156(2) Å for GdCu_3.98(4)Al_1.02(4), and a=5.1025(10) Å; c=4.155(2) Å for GdCu_3.9(1)Ga_1.1(1), respectively. Structure refinements from single crystal X-ray diffraction data reveal that substitution of Cu for Al or Ga takes place preferably on one of the two transition metal sites with site symmetry mmm (3g). Both compounds order antiferromagnetically below ∼40 K and ∼36 K, respectively, as determined from temperature dependent dc-magnetization, resistivity and heat-capacity measurements.     

The non-centrosymmetric borate oxides, MBi2B2O7 (M=Ca, Sr)

Two novel noncentrosymmetric borates oxides, MBi₂B₂O₇ or MBi₂O(BO₃)₂ (MCa, Sr), have been synthesized by solid-state reactions in air at temperatures in the 600-700 °C range. Their crystal structures have been determined ab initio and refined using powder neutron diffraction data. CaBi₂B₂O₇ crystallizes in the orthorhombic Pna2₁ space group with a=8.9371(5) Å, b=5.4771(3) Å, c=12.5912(7) Å, Z=4, R_wp=0.118, χ²=2.30. SrBi₂B₂O₇ crystallizes in the hexagonal P6₃ space group with a=9.1404(4) Å, c=13.0808(6) Å, Z=6, R_wp=0.115, χ²=4.15. Large displacement parameters suggest the presence of disorder in SrBi₂B₂O₇ as also revealed by diffuse 2×a superstructure reflections in electron diffraction patterns. Both structures are built of identical (001) neutral layers of corner-sharing BO₃ triangles and MO₆ trigonal prisms forming six-membered rings in which Bi₂O groups are located. Adjacent layers are stacked in a staggered configuration and connected through weak Bi-O bonds. A moderate efficiency for second harmonic generation (SHG) has been measured for a powder sample of CaBi₂B₂O₇ (d_eff=2d_eff(KDP)).     

Structure and properties of the CaFe2O4-type cobalt oxide CaCo2O4

The calcium cobalt oxide CaCo₂O₄ was synthesized for the first time and characterized from a powder X-ray diffraction study, measuring magnetic susceptibility, specific heat, electrical resistivity, and thermoelectric power. CaCo₂O₄ crystallizes in the CaFe₂O₄ (calcium ferrite)-type structure, consisting of an edge- and corner-shared CoO₆ octahedral network. The structure of CaCo₂O₄ belongs to an orthorhombic system (space group: Pnma) with lattice parameters, a=8.789(2) Å, b=2.9006(7) Å and c=10.282(3) Å. Curie-Weiss-like behavior in magnetic susceptibility with the nearly trivalent cobalt low-spin state (Co³⁺, 3d, S=0), semiconductor-like temperature dependence of resistivity (ρ=3×10⁻¹ Ω cm at 380 K) with dominant hopping conduction at low temperature, metallic-temperature-dependent large thermoelectric power (Seebeck coefficient: S=+147 μV/K at 380 K), and Schottky-type specific heat with a small Sommerfeld constant (γ=4.48(7) mJ/Co mol K²), were observed. These results suggest that the compound possesses a metallic electronic state with a small density of states at the Fermi level. The doped holes are localized at low temperatures due to disorder in the crystal. The carriers probably originate from slight off-stoichiometry of the phase. It was also found that S tends to increase even more beyond 380 K. The large S is possibly attributed to residual spin entropy and orbital degeneracy coupled with charges by strong electron correlation in the cobalt oxides.