La0.7-xDyxSr0.3MnO3(0.00≤x≤0.30)体系低温磁行为和电阻率的反常

By measuring M-T curves, ρ-T curves and MR-T curves of the samples under different temperatures, the influence of Dy doping (0.00 ≤ x ≤0.30) on the magnetic and electric properties of La0.7-xDyxSr0.3MnO3 has been studied. The experimental results show that, with the increase of the Dy content, the system undergoes a transition from long range ferromagnetic order to the cluster-spin glass state and further to antiferromagnetic order. For the samples with x=0.20 and 0.30, their magnetic behaviors are abnormal at low temperature, and their resistivities at low temperature have a minimum value. These peculiar phenomena not only come from the lattice effect induced by doping, but also from extra magnetic coupling induced by doping.     

La0.7-xGdxSr0.3MnO3中的相分离和输运行为

研究了La0.7-xGdxSr0.3MnO3(x=0．00，0．10，0．15，0．20，0．30，0．40，0．50，0．60，0．70)体系的M-T曲线、M-H曲线、ESR曲线、ρ-T曲线和MR-T曲线。实验结果表明：随着Gd掺杂的增加，体系从长程铁磁有序向自旋团簇玻璃态和反铁磁状态转变，x=0.30和0.40时，样品在Tc以上温区发生相分离；高掺杂时的输运行为在其磁背景下发生异常，Gd掺杂引起的磁结构的变化将导致CMR效应。     

La0.67-xErxSr0.33MnO3 (0.00≤x≤0.20)体系的磁电特性和低温电阻率反常

实验研究了La0.67-xErxSr0.33MnO3(x=0．00，0．10，0．20)体系的M-T曲线、ρ-T曲线和MR-T曲线。结果发现：随掺杂量增加，体系的磁结构从长程铁磁有序向自旋团簇玻璃态过渡，极低温区出现M-T曲线上翘；体系的电阻率随掺杂量的增加而增加，并出现低温极小值现象。体系磁电性质的变化来源于掺杂引起的额外磁性耦合，以及晶格畸变和局域磁矩引起的类似于磁性杂质对电子自旋散射造成的近藤效应(Kondo Effect)。     

La0.7Ca0.3MnO3薄膜庞磁电阻(CMR)现象的分析

针对La0.7Ca0．3MnO3薄膜材料中磁团簇的特性及其对材料庞磁电阻(CMR)现象的影响进行了研究。根据实验数据，利用Wagner等提出的数学模型，对La0.7Ca0.3MnO3薄膜中的磁团簇随温度的变化行为特性进行了研究；通过对La0.7Ca0．3MnO3薄膜相关实验数据的拟合，发现La0．7Ca0．3MnO3薄膜的居里温度范围应当在245～250K之间，从而进一步缩小了该材料居里温度的误差范围；还通过计算MR随磁团簇总角量子数J的变化，研究了制约和影响MR值的主要因素，发现磁团簇尺寸在La0．7Ca0.3MnO3薄膜的CMR现象中扮演了重要角色。     

La0.67Sr0.33Mn1-xCrxO3(0.00≤x≤0.30)的特殊输运行为

研究了La0.67Sr0.33Mn1-xCrxO3(0.00≤x≤0.30)体系的M-T曲线、ρ-T曲线和MR-T曲线. 实验结果表明 Cr对Mn位的替代对居里温度TC影响不明显, 但是随着Cr含量的增加, 电阻率和磁电阻出现双峰行为, CMR效应的温区被极大地拓宽了. 体系的特殊输运行为和异常CMR效应可能是Mn3+-O-Mn4+和Mn3+-O-Cr3+两种通道共存和竞争的结果.     

La0.67Sr0.33Mn1-xCrO3（0.00≤x≤0.30）的特殊输运行为

研究了La0.67Sr0.33Mn1-xCrO3(0.00≤x≤0.30)体系的M-T曲线、p-T曲线和MR-T曲线。实验结果表明：Cr对Mn位的替代对居里温度Tc影响不明显，但是随着Cr含量的增加，电阻率和磁电阻出现双峰行为，CMR效应的温区被极大地拓宽了。体系的特殊输运行为和异常CMR效应可能是Mn^3 -O-Mn^4 和Mn^3 -O-Cr^3 两种通道共存和竞争的结果。     

La0.67Sr0.33Mn1-xCrxO3（0．00≤x≤0.30）的特殊输运行为

研究了La0.67Sr0.33Mn1-xCrxO3（0．00≤x≤0.30）体系的M-T曲线、p-T曲线和MR-T曲线。实验结果表明：Cr对Mn位的替代对居里温度Tc影响不明显，但是随着Cr含量的增加，电阻率和磁电阻出现双峰行为,CMR效应的温区被极大地拓宽了。体系的特殊输运行为和异常CMR效应可能是Mn^3＋O-Mn^4＋和Mn^3＋-O-Cr3^3＋两种通道共存和竞争的结果。     

稀土(Sm,Gd,Dy)代换镧对La0.7Sr0.3MnO3磁电性质的影响及室温CMR的增强

用固相反应法制备了La0.7-xSm,Sr0.3MnO3,La0.7-x,GdxSr0.3MnO3和La0.7-xDyxSr0.3MnO3(x=0.00,0.10,0.20,0.30)系列样品.通过M-T'曲线,ρ-T曲线,研究了用稀土离子代换La对La0.7Sr0.3MnO3磁电性质和磁电阻的影响.结果表明:稀土离子代换La引起的晶格畸变和稀土离子的额外磁性对钙钛矿锰氧化物的磁电性质影响很大;稀土离子代换La是改变钙钛矿锰氧化物居里温度和增强MR的有效途径;适量稀土离子代换La可以在室温附近产生大的磁电阻.     

K+掺杂对钙钛矿氧化物La0.7Sr0.3-xKxMnO3(0.05≤x≤0.3)的结构及磁性的影响

钙钛矿;双交换作用;居里温度;最大磁熵变     

La0.7Mg0.3(Ni1-xCox)3.5 (0≤x≤0.5)储氢合金电化学性能

近年来,具有AB2和AB5复合结构的LaNi3系和La2Ni7系储氢材料由于具有较高的储氢量而引起了人们的关注[1]. 它们可在较温和条件下快速吸放氢, 且理论吸氢量分别为LaNi5的1.25倍及1.11倍.     

Gd掺杂对La0.67 Sr0.33 CoO3、La0.67 Sr0.33 MnO3体系磁行为的影响

M~T curves and M~H curves of the systems La0.67Sr0.33CoO3, La0.67Sr0.33MnO3 (x=0.00, 0.05, 0.10, 0.20, 0.30, 0.40, 0.50, 0.60, 0.67) were studied by experiments. Experimental results show that the magnetic structure of La0.67-xGdxSr0.33CoO3 system exhibits the cluster glass state with doping Gd increasing. The M~T curves of samples x>0.10 exhibit a peculiar phenomenon that M value rises sharply at low temperature range. The magnetic structure of La0.67-xGdxSr0.33MnO3 system changes from the long rang ferromagnetic order to the cluster glass state, and anti ferromagnetic state. The M~T curves of samples x≥0.50 decline sharply at low temperature range. The different phenomena shown by the two systems come from different coupling function between Gd and Co, Mn and from spin state transition of Co.     

(La0.67Ca0.33MnO3)x/(ZrO2)1-x复合体系的磁性和传输特性

将用溶胶-凝胶法得到的La0.67Ca0.33MnO3(LCMO)微粉与ZrO2的颗粒进行复合,制备了(LCMO)x/(ZrO2)1-x渗流复合体系.当LCMO的体积分数为40%时,复合体系达到渗流阈值,此时材料在低温下的磁电阻得到显著增强.77 K时在10 mT的磁场下,(LCMO)0.4/(ZrO2)0.6的磁电阻比为7.8%,相对于LCMO增加了712%.低场磁电阻(LFMR)的增强是由于载流子在二者界面处发生的自旋相关隧穿效应.由于界面反应,不可避免地产生了Zr离子对Mn离子的B位替代,从而引起材料磁性M和居里温度Tc的下降.在x＜60%时,Tc保持在220 K附近基本不变,说明该B位替代是有限的.     

LaAlO3(100),(110)和(111)衬底上La0.7Sr0.3MnO3薄膜的输运和光诱导特性研究

采用脉冲激光沉积(PLD)的方法分别在LaAlO3(100),(110)和(111)衬底上沉积了La0.7Sr0.3MnO3(LSMO)外延薄膜,研究了不同晶面取向对薄膜输运和光诱导特性的影响。实验结果表明随着垂直膜面晶格不匹配度的增加,薄膜的相变温度向低温方向移动,而电阻率和光致电阻率变化值(Δρ)则增大,分析表明这一现象的出现可归结于晶格失配致使双交换作用减弱。     

稀土锰氧化物La0.7Ca0.3Mn1-xCuxO3低场磁电阻及电传输特性研究

采用溶胶-凝胶法制备了系列多晶CMR材料La0.7Ca0.3Mn1-xCuxO3（x=0%,1%,5%,10%,15%,20%）。在77-350 K温度范围内测量了样品的电阻率及磁电阻大小。实验结果发现：系列样品TC随掺杂量增加而递减;系列样品的电阻率峰及磁电阻峰在整个测温范围内随掺杂量的增加均依次被展宽直至消失,当掺杂量为x≥10%时,电阻率随温度的变化在整个测温范围内呈现绝缘相行为;同时还发现,掺杂量为x≥10%时,样品的磁电阻在整个测温区内基本表现为隧穿磁电阻。基于我们采用蒙特卡罗模拟方法提出的逾渗模型及隧穿磁电阻模型,对样品的磁电阻行为进行了很好的解释。对系列样品的ρ-T曲线进行lnρ-T^-（1/4）系拟合,发现掺杂量为x=10%样品在整个温区内的lnρ-T^-（1/4）系基本呈线性。     

微观结构对溶胶-凝胶法合成的La0.67Sr0.33MnO3电磁性能影响

采用溶胶-凝胶法制备了不同烧结温度的钙钛矿类锰氧化物La0.67Sr0.33MnO3样品。实验结果表明,在1573 K以上烧结的样品,晶粒出现异常长大,晶界效应明显。随着烧结温度的提高,磁化强度逐渐增大,但样品的居里温度基本不变。此外,在1173和1573 K温度下烧结的样品,均出现了低于居里温度的金属-半导体导电行为转变。在合适的烧结条件下,可以观察到隧道磁电阻(TMR)和超大磁电阻(CMR)2种磁电阻效应。实验表明,自旋电子的输运,不仅与样品平均粒径的大小和密度有关,而且与晶界的微观结构有密切关系。     

稀土空位庞磁电阻材料La(1-x)2/3Ca1/3MnO3的结构变化和输运性质

利用标准的固相反应法制备了La（1-x）2/3Ca（1/3）MnO3（x〈0.1）系列具有稀土La空位的庞磁电阻锰氧化物多晶样品.X射线粉末衍射（XRD）测量分析表明所有的样品均为单相,单胞具有正交对称性（Pnma）.分析了不同浓度的La空位对磁电输运性质的影响： 随着空位浓度的增大,绝缘体-金属的转变温度（TMI）几乎不变（约为267 K）,这表明少量的稀土空位不会破坏双交换作用;但当La空位浓度x〉0.04时,零场电阻率增大,但磁电阻（MR）值减小;在x=0.04时MR值在转变温度TMI处达到最大值约为220%（8 T）.     

（100），（110）和（111）生长方向的La0.7Sr0.3MnO3薄膜结构及性能研究

利用磁控溅射方法，在（100），（110）和（111）LaAlO3（LAO）衬底上制备得到了不同生长方向的La0.7Sr0.3MnO3（LSMO）薄膜并对其晶体结构及磁电学性能进行了系统研究。AFM图揭示出（100），（110）和（111）生长方向的LSMO薄膜分别具有圆形、长条形和点状的表面晶粒形貌。磁电学测试结果表明不同生长方向的LSMO薄膜磁电学性能与其应变程度有关。（111）生长方向的LSMO薄膜由于按最密排面生长，晶格畸变很小，从而具有相对最大的磁饱和强度值和最低的电阻。     

钙钛矿锰氧化物(La_(1-x)Gd_x)_(0.5)Sr_(0.5)MnO_3的磁电阻效应

采用传统的高温固相法制备了多晶样品(La1-xGdx)0.5Sr0.5MnO3(x=0,0.1,0.2,0.3,0.4),利用X射线衍射仪(XRD)、超导量子磁强计(SQUID)、标准四端引线法分别对样品结构、磁性、电性以及磁电阻效应进行了研究。研究表明:Gd的少量替代并没有引起结构变化;随着Gd含量的增加,所有样品的居里温度TC和金属-绝缘体转变温度Tp都降低了;在TC附近发现了磁电阻效应,同时在低温下发现了更大的磁电阻;并且Gd的少量替代可使磁电阻MR增大。     

(La1-xDyx)0.67Ca0.33MnO3的磁性和磁电阻特性

在La0.67Ca0.33MnO3中用Dy对La进行了部分替代.结果表明, 随替代量增加, 材料的居里温度和相变温度单调下降, 磁电阻比急剧增大.这些变化可以用稀土离子平均直径的减小和自旋团簇模型来解释.掺Dy使材料中形成大量无序自旋团簇, 外加磁场使自旋团簇取向一致, 从而增加了电子在团簇之间跳跃时的迁移率, 产生了磁场所致的庞磁电阻效应.     

(La0.57Ce0.1)Sr0.03MnO3纳米材料的低温合成及其磁热效应研究

采用聚合物前驱体方法,以H5DTPA为配位剂,低温下合成出(La0.57Ce0.1)Sr0.03MnO3纳米颗粒.用TGA-DTA对凝胶前驱体的热分解历程进行分析,采用XRD,高分辨透射显微镜(HRTEM)对凝胶前驱体不同温度下烧结所得粉体的相组成和微观结构进行研究.采用PPMS对(La0.57Ce0.1)Sr0.03MnO3纳米颗粒的磁性能进行了测量.结果表明:凝胶前驱体经600℃烧结2 h可以得到纯钙钛矿型(La0.57Ce0.1)Sr0.03MnO3纳米粉体,平均粒径为40～50 nm;(La0.57Ce0.1)Sr0.03MnO3纳米粉体的居里温度TC为368 K.