The effect of flux materials on the physical and optical properties of Eu-activated yttrium oxide phosphors

A flux fusion method was used to obtain the various sizes of Eu³⁺-activated Y₂O₃ red phosphors. The flux material was selected as an independent variable to control the physical properties of phosphor particles and their effects on the morphology and size distribution of phosphors were examined by scanning electron microscopy. The concentration of the flux materials and synthetic temperature were optimized for maximal photoluminescence intensity. Fluoride-based flux materials were found to work for the crystal formation of Eu³⁺-activated Y₂O₃. In particular, when a BaF₂ flux was used during the reaction at 1450 °C for 3 h, the photoluminescence (PL) intensity of Eu³⁺-activated Y₂O₃ was 25% higher than that without a flux and spherical phosphors had a mean particle size of 4-5 μm. The morphology and size distribution of the synthesized Eu³⁺-activated Y₂O₃ phosphor were predominantly dependent upon the type and concentration of flux material and synthetic temperature.     

Thermoluminescent and stuctural properties of BaAl2O4:Eu,Nd,Gdphosphors prepared by combustion method

BaAl₂O₄:Eu²⁺,Nd³⁺,Gd³⁺ phosphors were prepared by a combustion method at different initiating temperatures (400–1200 °C), using urea as a comburent. The powders were annealed at different temperatures in the range of 400–1100 °C for 3 h. X-ray diffraction data show that the crystallinity of the BaAl₂O₄ structure greatly improved with increasing annealing temperature. Blue-green photoluminescence, with persistent/long afterglow, was observed at 498 nm. This emission was attributed to the 4f⁶5d¹–4f⁷ transitions of Eu²⁺ ions. The phosphorescence decay curves were obtained by irradiating the samples with a 365 nm UV light. The glow curves of the as-prepared and the annealed samples were investigated in this study. The thermoluminescent (TL) glow peaks of the samples prepared at 600 °C and 1200 °C were both stable at ∼72 °C suggesting that the traps responsible for the bands were fixed at this position irrespective of annealing temperature. These bands are at a similar position, which suggests that the traps responsible for these bands are similar. The rate of decay of the sample annealed at 600 °C was faster than that of the sample prepared at 1200 °C.     

Fluorescence and persistent spectral hole burning of Eu in Ge-Ga-S-KBr glasses

Fluorescence and efficient persistent spectral hole burning of Eu³⁺ at 77 K were observed in chalcohalide glasses. The depth of the hole was approximately 30% after a burning process of 1 min with 50 mW power, and it was completely erased with Ar⁺ laser irradiation. The hole survived room temperature heat treatment and showed good thermal stability. The hole-burning mechanism was most probably the photo-reduction of Eu³⁺→Eu²⁺. Fluorescence from Eu³⁺ decreased with increasing temperature and disappeared at the temperature above ∼130 K.     

Combustion synthesis and luminescence properties of NaY1−xEux(WO4)2 phosphors

The red phosphors NaY_1−xEu_x(WO₄)₂ with different concentrations of Eu³⁺ were synthesized via the combustion synthesis method. As a comparison, NaEu(WO₄)₂ was prepared by the solid-state reaction method. The phase composition and optical properties of as-synthesized samples were studied by X-ray powder diffraction and photoluminescence spectra. The results show that the red light emission intensity of the combustion synthesized samples under 394 nm excitation increases with increase in Eu³⁺ concentrations and calcination temperatures. Without Y ions doping, the emission spectra intensity of the NaEu(WO₄)₂ phosphor prepared by the combustion method fired at 900 °C is higher than that prepared by the solid-state reaction at 1100 °C. NaEu(WO₄)₂ phosphor synthesized by the combustion method at 1100 °C exhibits the strongest red emission under 394 nm excitation and appropriate CIE chromaticity coordinates (x=0.64, y=0.33) close to the NTSC standard value. Thus, its excellent luminescence properties make it a promising phosphor for near UV InGaN chip-based red-emitting LED application.     

Synthesis and luminescence properties of nanocrystalline Gd2O3:Eu by combustion process

The nanocrystalline Gd₂O₃:Eu³⁺ powders with cubic phase were prepared by a combustion method in the presence of urea and glycol. The effects of the annealing temperature on the crystallization and luminescence properties were studied. The results of XRD show pure phase can be obtained, the average crystallite size could be calculated as 7, 8, 15, and 23 nm for the precursor and samples annealed at 600, 700 and 800 °C, respectively, which coincided with the results from TEM images. The emission intensity, host absorption and charge transfer band intensity increased with increasing the temperature. The slightly broad emission peak at 610 nm for smaller particles can be observed. The ratio of host absorption to O²⁻-Eu³⁺ charge transfer band of smaller nanoparticles is much stronger compared with that for larger nanoparticles, furthermore, the luminescence lifetimes of nanoparticles increased with increasing particles size. The effects of doping concentration of Eu³⁺ on luminescence lifetimes and intensities were also discussed. The samples exhibited a higher quenching concentration of Eu³⁺, and luminescence lifetimes of nanoparticles are related to annealing temperature of samples and the doping concentration of Eu³⁺ ions.     

Synthesis and luminescent properties of nanoparticles GdCaAl3O7:RE (RE=Eu, Tb) via the sol-gel method

By using metal nitrates as starting materials and citric acid as complexing agent, GdCaAl₃O₇:Eu³⁺ and GdCaAl₃O₇:Tb³⁺ powder phosphors were prepared by a citrate-gel method. Thermal analysis (TG-DTG), X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM), photoluminescence excitation and emission, as well as kinetic decays were employed to characterize the resulting samples. The results of the XRD indicated the precursor samples began to crystallize at 800 °C and the crystallinity increased with elevation the annealing temperature. TEM images showed that the phosphor particles were basically of spherical shape, with good dispersion about a particle size of around 40-70 nm. Upon excitation with UV irradiation, it is shown that there is a strong emission at around 617 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺, and at around 543 nm corresponding to the ⁵D₄-⁷F₅ transition of Tb³⁺. The dependence of photoluminescence intensity on Eu³⁺ (or Tb³⁺) concentration and annealing temperature were also studied in detail.     

Preparation and photoluminescence characteristics of Eu-doped MgAl1.8Y0.2O4 nanocrystals

A simple combustion route was employed for the preparation of Eu³⁺-doped MgAl_1.8Y_0.2−xO₄ nanocrystals using metal nitrates as precursors and urea as a fuel in a preheated furnace at 500 °C. The powders thus obtained were then fired at 1000 °C for 3 h to get better luminescent properties. The incorporation of Eu³⁺ activator in these nanocrystals was checked by luminescence characteristics. These nanocrystals displayed bright red color on excitation under 254 nm UV source. The main emission peak was assigned to the transition [⁵D₀→⁷F₂] at 615 nm. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) studies were carried out to understand surface morphological features and the particle size. Crystal structures of the nanocrystals were investigated by the X-ray diffraction (XRD) technique. The crystallite size of the as-prepared nanocrystals was around 29 nm, which was evaluated from the broad XRD peaks. The crystallite size increased to ∼45 nm on further heat treatment at 1000 °C.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

Spherical Zn2SiO4:Eu@SiO2 phosphor particles in core-shell structure: Synthesis and characterization

Spherical SiO₂ particles have been coated with Zn₂SiO₄:Eu³⁺ phosphor layers by a Pechini sol-gel process. The microstructure and luminescent properties of the obtained Zn₂SiO₄:Eu³⁺@SiO₂ particles were well characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, and lifetime. The results demonstrate that the Zn₂SiO₄:Eu³⁺@SiO₂ particles, which have regular and uniform spherical morphology, emitted an intensive red light emission at 613 nm under excitation at 395 nm. Besides, the effects of the Eu³⁺ concentration, annealing temperature and charge compensators of Li⁺ ions on the PL emission intensities were investigated in detail.     

Highly luminescent red light phosphor CaTiO3:Eu under near-ultraviolet excitation

The Eu-doped CaTiO₃ particles with a good crystallinity were prepared via sol-gel method. The phosphors showed a strong red emission corresponding to ⁵D₀→⁷F₂ (618 nm) of Eu³⁺ under the near-ultraviolet excitation (400 nm). X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM), photoluminescent (PL) analysis and Brunauer-Emmett-Teller (BET) specific surface area measurement were utilized to characterize the CaTiO₃:Eu³⁺ particles. The concentration quenching and thermal quenching of the samples were discussed as well. The optimal concentration and the calcination temperature were 16 mol% of Eu³⁺ and 1400 °C for these phosphors, and the possible reason was discussed as well. CaTiO₃:Eu³⁺ is a promising red phosphor under near-ultraviolet excitation for various applications.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).     

Phosphorescent and thermoluminescent properties of SrAl2O4:Eu,Dy phosphors prepared by solid state reaction method

Long persistent SrAl₂O₄:Eu²⁺ phosphors co-doped with Dy³⁺ were prepared by the solid state reaction method. The main diffraction peaks of the monoclinic structure of SrAl₂O₄ were observed in all the samples. The broad band emission spectra at 497 nm for SrAl₂O₄:Eu²⁺, Dy³⁺ were observed and the emission is attributed to the 4f⁶5d¹ to 4f⁷ transition of Eu²⁺ ions. The samples annealed at 1100–1200 °C showed similar broad TL glow curves centered at 120 °C. The similar TL glow curves suggest that the traps responsible for them are similar. The long afterglow displayed by the phosphors annealed at different temperatures, may be attributed to the Dy³⁺ ions acting as the hole trap levels, which play an important role in prolonging the duration of luminescence.     

Optical properties of annealed Mn-doped ZnS nanoparticles

Cysteine stabilized ZnS and Mn²⁺-doped ZnS nanoparticles were synthesized by a wet chemical route. Using the ZnS:Mn²⁺ nanoparticles as seeds, silica-coated ZnS (ZnS@Si) and ZnS:Mn²⁺ (ZnS:Mn²⁺@Si) nanocomposites were formed in water by hydrolysis and condensation of tetramethoxyorthosilicate (TMOS). The influence of annealing in air, formier gas, and argon at 200-1000 °C on the chemical stability of ZnS@Si and ZnS:Mn²⁺@Si nanoparticles with and without silica shell was examined. Silica-coated nanoparticles showed an improved thermal stability over uncoated particles, which underwent a thermal combustion at 400 °C. The emission of the ZnS@Si and ZnS:Mn²⁺@Si passed through a minimum in photoluminescence intensity when annealed at 600 °C. Upon annealing at higher temperatures, ZnS@Si conserved the typical emission centered at 450 nm (blue). ZnS:Mn²⁺@Si yielded different high intensity emissions when heated to 800 °C depending on the gas employed. Emissions due to the Mn²⁺ at 530 nm (green; Zn₂SiO₄:Mn²⁺), 580 nm (orange; ZnS:Mn²⁺@Si), and 630 nm (red; ZnS:Mn²⁺@Si) were obtained. Therefore, with a single starting product a set of different colors was produced by adjusting the atmosphere wherein the powder is heated.     

Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Luminescent properties of Eu-activated Sr3B2SiO8: A red-emitting phosphor for white light-emitting diodes

Single-phased Sr₃B₂SiO₈:Eu³⁺ phosphor was prepared by a solid-state method at 1020 °C. The luminescence spectra showed that Sr₃B₂SiO₈:Eu³⁺ phosphor can be effectively excited by near ultraviolet light (393 nm) and blue light (464 nm). When excited at 393 or 464 nm Sr₃B₂SiO₈:Eu³⁺ exhibited the main emission peaks at 611 and 620 nm, which resulted from the supersensitive ⁵D₀→⁷F₂ transition of Eu³⁺. The luminescence intensity of Sr₃B₂SiO₈:Eu³⁺ at 611 and 620 nm reached the maximum when the doping content of Eu³⁺ was 4.5 mol%. Its chromaticity coordinates (0.646, 0.354) were very close to the NTSC standard values (0.67, 0.33). Thus, Sr₃B₂SiO₈:Eu³⁺ is considered to be an efficient red-emitting phosphor for long-UV InGaN-based light-emitting diodes.     

Abnormally enhanced Eu emission in Y2O2SO4:Eu inherited from their precursory dodecylsulfate-templated concentric-layered nanostructure

A new nanostructure-mediated approach was demonstrated to synthesize Eu³⁺-doped yttrium oxysulfates Y₂O₂SO₄:Eu³⁺ giving rise to abnormally enhanced Eu³⁺ emission. Yttrium and europium salts, sodium dodecylsulfate (SDS), and urea at various Eu³⁺ concentrations were reacted in aqueous solution at 80, 85, and 87 °C to yield Eu³⁺-doped dodecylsulfate-templated yttrium oxide mesophases with straight-layered (S-type), concentric-layered (C-type) and layer-to-hexagonal transient-layered (T-type) structures, respectively. On calcination at 1000 °C, all of these mesophases were converted into Y₂O₂SO₄:Eu³⁺ to exhibit luminescence bands including the ⁵D₀-⁷F₂ transition with a tendency in intensity to saturate or reach a maximum at 10-12 mol% Eu doping. The Eu³⁺ emissions for Y₂O₂SO₄:Eu³⁺ mediated by the T- and C-type mesophases were enhanced in intensity by a factor of about two and three times, respectively, stronger than those for not only compositionally the same sulfate Y₂O₂SO₄:Eu³⁺ obtained from yttrium-based sulfates but also Y₂O₃:Eu³⁺ obtained in the SDS-free system. In contrast, the emission intensities for the S-type-mesophase-mediated Y₂O₂SO₄:Eu³⁺ were close to those for the latter sulfates. The abnormally enhanced emission is likely based on specific deformation of sulfate groups induced through the conversion of concentric dodecylsulfate-layers to straight sulfate-layers in the oxysulfate framework upon calcination.     

Preparation and luminescence properties of Tb doped ZrO2 and BaZrO3 phosphors

ZrO₂:Tb³⁺ and BaZrO₃:Tb³⁺ powders are prepared by combustion synthesis method and the samples were further heated to 500, 700 and 1000 °C to improve the crystallinity of the materials. The structure and morphology of materials have been examined by X-ray diffraction, Raman spectra and scanning electron microscopy. It is remarkable that all the samples of ZrO₂:Tb³⁺ and BaZrO₃:Tb³⁺ have similar morphology. These images exhibited homogeneous aggregates of varying shapes and sizes, which are composed of a large number of small cuboids and broken cuboids. The cuboids and broken cuboids size of all the samples are less than 0.5 μm. Photoluminescence for both materials increases with increase of temperature and found maximum for the samples heated to 1000 °C with 5 mole% doping of Tb³⁺ ions. Luminescence is almost double for the zirconia compared to that of barium-zirconate.     

Low-voltage cathodoluminescence property of Li-doped Gd2−xYxO3:Eu

Cathodoluminescent (CL) spectra of Li-doped Gd_2−xY_xO₃:Eu³⁺ solid-solution (0.0?x?0.8) were investigated at low voltages (300 V-1 kV). The CL intensity is maximum for the composition of x=0.2 and gradually reduces with increasing the amount of substituted Y content. In particular, small (∼100 nm) particles of Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ are obtained by firing the citrate precursors at only 650°C for 18 h. Relative red-emission intensity at 300 V of this phosphor is close to 180% in comparison with that of commercial red phosphor Y₂O₃:Eu³⁺. An increase of firing temperature to 900°C results in 400-600 nm sized spherical particles. At low voltages (300-800 V), the CL emission of 100 nm sized particles is much stronger than that of 400-600 nm sized ones. In contrast, the larger particles exhibit the higher CL emission intensity at high voltages (1-10 kV). Taking into consideration small spherical morphology and effective CL emission, Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ appears to be an efficient phosphor material for low voltage field emission display.     

Influence of high hydrostatic pressure on Eu-luminescence in KMgF3:Eu crystal

Spectroscopic investigations are presented of KMgF₃:Eu²⁺ crystal under high hydrostatic pressure from ambient to 310 kbar. The sample was excited by 30 ps pulses generated by optical parametric generator (OPG) system with wavelength controlled between 210 and 325 nm. The Grüneisen parameters of individual phonons are obtained from the pressure shift of the Eu²⁺ emission related to the ⁶P_7/2→⁸S_7/2 transition accompanied by phonon sideband. The luminescence decays exponentially for the pressure below 135 kbar with lifetime of 3.30 ms and slightly nonexponential above 135 kbar, while the average decay time is nearly independent of the pressure. The results obtained for KMgF₃:Eu²⁺ are compared with those for LiBaF₃:Eu²⁺ in which the ⁶P_7/2→⁸S_7/2 emission is replaced by the broadband emission of the 4f⁶5d¹→4f⁷ transition at high hydrostatic pressure.     

Investigation of crystallographic sites of Eu in La2BaZnO5 by site-selective laser-excitation spectroscopy

La₂BaZnO₅:Eu³⁺ (0.05 mol%) was prepared by a solid-state reaction at high temperature. X-ray powder diffraction analysis confirmed the formation of single phase La₂BaZnO₅. Luminescence properties of La₂BaZnO₅:Eu³⁺ are investigated by site-selective laser-excitation and emission spectroscopy at 18 K. Two different crystallographic sites for Eu³⁺ corresponding to the La³⁺ and Ba²⁺ sites are identified from the ⁷F₀→⁵D₀ excitation spectra obtained by monitoring the ⁵D₀→⁷F_J (J=1, 2, …, 6) emissions. It is found that Eu³⁺ substituted for the Ba²⁺ ion experiences stronger crystal-field strength than Eu³⁺ substituted for the La³⁺ ion. Energy transfer between the two crystallographic Eu³⁺ centers is investigated by luminescence decay curves at 18 K.