Glass formation in the CaO-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-B<Subscript>2</Subscript>O<Subscript>3</Subscript> and SrO-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-B<Subscript>2</Subscript>O<Subscript>3</Subscript> systems

A physicochemical study of glasses based on the MO-Bi₂O₃-B₂O₃ and SrO-Bi₂O₃-B₂O₃ systems was performed. Glass formation regions were found. The structural and optical properties, as well as the thermal behavior of the glasses, were studied.     

Y<Subscript>2</Subscript>O<Subscript>3</Subscript>-Ga<Subscript>2</Subscript>O<Subscript>3</Subscript> phase diagram

Phase relations in the Y₂O₃-Ga₂O₃ system were studied by the anneal-and-quench technique in air within 1000–2300°C, and a phase diagram was plotted. Three compounds were found to form: Y₃GaO₆, Y₄Ga₂O₉, and Y₃Ga₅O₁₂; the temperature and concentration bounds of stability were determined for these compounds. Indexing results for Y₃GaO₆ are given.     

Phase relations in the MgO-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript> system

Phase relations in the MgO-Bi₂O₃-B₂O₃ system have been investigated by X-ray powder diffraction analysis and DTA. No ternary compounds have been found in the system. Quasi-binary sections have been the 600°C determined and isothermal section of the system has been constructed.     

Solid solutions in the MgO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-Cr<Subscript>2</Subscript>O<Subscript>3</Subscript> system

Coexisting solid solutions with spinel and corundum structure were synthesized at 1773 K and two pressures, 1 bar and 25 kbar. Samples were analyzed by electron microprobe analysis and X-ray powder diffraction. Pressure and temperature were shown to affect the properties of the solid solutions in different ways. Pressure governs the composition of the defect spinel Mg_1−xAl₂O₄, and temperature changes the cation distribution between coexisting phases. This allows one to separate the effects of cation exchange and magnetic contribution to the heat capacity in thermodynamic modeling. The defect spinel itself can form only because γ-Al₂O₃ exists, polymorph with spinel structure.     

Synthesis and study of solid acid materials SnO<Subscript>2</Subscript>/B<Subscript>2</Subscript>O<Subscript>3</Subscript>

SnO₂/B₂O₃ samples were produced by a reaction between SnCl₄, H₃BO₃, and (NH₂)₂CO in a boiling aqueous solution. The Sn: B molar ratio in these samples was 1: 1, 1: 2, and 1: 3. The phase composition and degree of crystallinity of these materials was studied. The surface acidity of the samples was analyzed by the method based on a temperature-programmed reaction of dehydration of 2-methyl-3-butyn-2-ol. Thermal transformations of SnO₂/B₂O₃ samples were examined by means of differential-thermal analysis.     

Rational design of double-confined Mn<Subscript>2</Subscript>O<Subscript>3</Subscript>/S@Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocube cathodes for lithium-sulfur batteries

Due to the high specific capacities and environmental benignity, lithium-sulfur (Li-S) batteries have shown fascinating potential to replace the currently dominant Li-ion batteries to power portable electronics and electric vehicles. However, the shuttling effect caused by the dissolution of polysulfides seriously degrades their electrochemical performance. In this paper, Mn₂O₃ microcubes are fabricated to serve as the sulfur host, on top of which Al₂O₃ layers of 2 nm in thickness are deposited via atomic layer deposition (ALD) to form Mn₂O₃/S (MOS) @Al₂O₃ composite electrodes. The MOS@Al₂O₃ electrode delivers an excellent initial capacity of 1012.1 mAh g^?1 and a capacity retention of 78.6% after 200 cycles at 0.5 C, and its coulombic efficiency reaches nearly 99%, giving rise to much better performance than the neat MOS electrode. These findings demonstrate the double confinement effect of the composite electrode in that both the porous Mn₂O₃ structure and the atomic Al₂O₃ layer serve as the spacious host and the protection layer of sulfur active materials, respectively, for significantly improved electrochemical performance of the Li-S battery.     

Thermodynamic properties of the system MgO-B<Subscript>2</Subscript>O<Subscript>3</Subscript> melts

Vaporization processes of melts of the system MgO-B₂O₃ at 1640 K were studied by high-temperature mass spectrometry, and thermodynamic properties (activity, chemical potentials of MgO and B₂O₃, and also the corresponding excess values) were determined. Considerable negative deviations from the ideal behavior in the melts of the studied system are observed. The termodynamic properties of the system MgO-B₂O₃ can be calculated within the framework of the lattice theory of associated solutions.     

Effect of SO<Subscript>2</Subscript> on chlorination of Bi<Subscript>2</Subscript>O<Subscript>3</Subscript> + Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> mixtures

The reaction of Bi₂O₃ + Fe₂O₃ mixtures with chlorine and SO₂ at 250–700°C is studied. At 300–500°C, the degree of bismuth chloride sublimation from the oxide mixture increases in the presence of SO₂. Chemical sublimation of FeCl₃ occurs after BiCl₃ is virtually completely recovered from the solid phase.     

Subsolidus phase relations in the Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-Li<Subscript>2</Subscript>O-Ta<Subscript>2</Subscript>O<Subscript>5</Subscript> (Nb<Subscript>2</Subscript>O<Subscript>5</Subscript>) systems

The phase composition has been studied and an equilibrium phase diagram has been designed for the Al₂O₃-Li₂O-R₂O₅ (R = Ta or Nb) systems in the subsolidus region up to 1000°C and 85 mol % Li₂O. New phases with the composition Li_1+x Al_1?x O_2?x , where x = 0–0.67, have been found.     

Towards high-performance cathode materials for lithium-ion batteries: Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-coated LiNi<Subscript>0.8</Subscript>Co<Subscript>0.15</Subscript>Zn<Subscript>0.05</Subscript>O<Subscript>2</Subscript>

Zn-doped LiNi_0.8Co_0.2O₂ exhibits impressive electrochemical performance but suffers limited cycling stability due to the relative large size of irregular and bare particle which is prepared by conventional solid-state method usually requiring high calcination temperature and prolonged calcination time. Here, submicron LiNi_0.8Co_0.15Zn_0.05O₂ as cathode material for lithium-ion batteries is synthesized by a facile sol-gel method, which followed by coating Al₂O₃ layer of about 15 nm to enhance its electrochemistry performance. The as-prepared Al₂O₃-coated LiNi_0.8Co_0.15Zn_0.05O₂ cathode delivers a highly reversible capacity of 182 mA h g^?1 and 94% capacity retention after 100 cycles at a current rate of 0.5 C, which is much superior to that of bare LiNi_0.8Co_0.15Zn_0.05O₂ cathode. The enhanced electrochemistry performance can be attributed to the Al₂O₃-coated protective layer, which prevents the direct contact between the LiNi_0.8Co_0.15Zn_0.05O₂ and electrolyte. The escalating trend of Li-ion diffusion coefficient estimated form electrochemical impedance spectroscopic (EIS) also indicate the enhanced structural stability of Al₂O₃-coated LiNi_0.8Co_0.15Zn_0.05O₂, which rationally illuminates the protection mechanism of the Al₂O₃-coated layer.     

Changes in the heat capacity of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-Cr<Subscript>2</Subscript>O<Subscript>3</Subscript> solid solutions near the point of antiferromagnetic phase transition in Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>

Al₂O₃-Cr₂O₃ solid solutions with 0, 4, 7, 10 and 20 mol% of corundum were synthesized using a high-pressure/high-temperature apparatus and characterized by X-ray powder diffraction. Calorimetric measurements were carried out using DSC-111 (Setaram). Heat capacity was measured by the enthalpy method in a temperature range of 260–340 K, near magnetic phase transition in pure Cr₂O₃ (305 K). Magnetic contribution into the heat capacity was derived and found to change irregularly with the composition.     

Mass spectrometric investigation of vaporization in the Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> system

The thermodynamics of vaporization in the Bi₂O₃-Fe₂O₃ quasibinary system was studied by high-temperature mass-spectrometry. The partial pressures of the constituents of a saturated vapor over the system at 1100 K were determined. Based on the experimental data, the following parameters were calculated: the activities of the components of the Bi₂O₃-Fe₂O₃ system condensed phase, the standard enthalpies of some heterogeneous reactions, and standard enthalpies of formation and enthalpies of formation for crystalline BiFeO₃ and Bi₂Fe₄O₉ from individual oxides. An optimal temperature for the solid-phase synthesis of bismuth ferrites from simple oxides is recommended.     

A comparative study of Ir/Ga<Subscript>2</Subscript>O<Subscript>3</Subscript>, Pt/Ga<Subscript>2</Subscript>O<Subscript>3</Subscript>, and Ru/Ga<Subscript>2</Subscript>O<Subscript>3</Subscript> catalysts in selective hydrogenation of crotonaldehyde

Catalytic performance of gallia-supported iridium catalysts in the reaction of selective hydrogenation of crotonaldehyde in the gas phase was studied and compared to that of platinum and ruthenium catalysts. The best catalytic properties in terms of the selectivity to crotyl alcohol are shown by 5 wt % Pt/α-Ga₂O₃ and 5 wt % Ir/α-Ga₂O₃ catalysts prepared from nonchlorine precursors: Pt(acac)₂ and Ir(acac)₃, but for the 5 wt % Pt/α-Ga₂O₃ a very high selectivity of 75% at the high conversion (ca. 60%) is observed. A high selectivity of galia-supported iridium and platinum catalysts was explained by the surface reducibility of gallium oxide leading to covering (decoration) of platinum and iridium by gallium suboxides and the promoting effect of gallium.     

Thermochemical properties of MnNb<Subscript>2</Subscript>O<Subscript>6</Subscript>

Homogeneous manganocolumbite (MnNb₂O₆) was synthesized from Nb₂O₅ and MnO oxides. Powder sample was orthorhombic with unit cell parameters: α = 0.5766 nm, b = 1.4439 nm, c = 0.5085 nm and V = 0.4234 nm³. Heat capacity over the temperature range of 313–1253 K was measured in an inert atmosphere with combined thermogravimetry and calorimetry using NETZSCH STA 449C Jupiter thermoanalyzer. Melting point was 1767 ± 3 K, enthalpy of melting was 144 ± 4 kJ mol⁻¹. Experimental heat capacity of MnNb₂O₆ is fitted to polynomial C _pm = 221.46 + 3.03 · 10⁻³ T + −39.79 · 10⁵ T ⁻² + 40.59 · 10⁻⁶ T ².     

Thermodynamic properties of melts of the system CaO-B<Subscript>2</Subscript>O<Subscript>3</Subscript>

Activities, chemical potentials, Gibbs energies, and also the corresponding excess values for CaO and B₂O₃ in the homogeneity region of melts of the CaO-V₂O₃ system at 1600 K were determined. These parameters were also calculated in terms of the generalized lattice theory of associated solutions. Considerable negative deviations from the ideal behavior are observed in the melts studied.     

Thermodynamic properties of silicate glasses and melts: V. Systems CaB<Subscript>2</Subscript>O<Subscript>4</Subscript>-CaSiO<Subscript>3</Subscript> and Ca<Subscript>2</Subscript>B<Subscript>2</Subscript>O<Subscript>5</Subscript>-CaSiO<Subscript>3</Subscript>

Thermodynamic properties of melts of the CaB₂O₄-CaSiO₃ and Ca₂B₂O₅-CaSiO₃ systems were determined by the method of high-temperature mass-spectrometry. The melts of these systems are characterized by negative deviations from the ideal behavior at 1800 K.     

Phase relations in the CaO-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-B<Subscript>2</Subscript>O<Subscript>3</Subscript> system in the subsolidus region

Phase relations in the CaO-Bi₂O₃-B₂O₃ system have been investigated by X-ray powder diffraction and differential thermal analyses, and the isothermal section at 600°C has been constructed. The formation of ternary compounds at the component ratios 1CaO: 1Bi₂O₃: 1B₂O₃ (CaBi₂B₂O₇) and 1CaO: 1Bi₂O₃: 2B₂O₃ (CaBi₂B₄O₁₀) has been established X-ray diffraction characteristics of these phases are presented.     

Surface chemistry of nanoscale Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> dispersed in magnetic fluids

The interaction between stabilizers and nanoparticles is one of the important factors to prepare stable magnetic fluids. The magnetic nano-size Fe₃O₄ core with single domain and the average grain size around 8–12 nm were prepared by chemical precipitation method. The O/Fe molar ratio of the particle surface was measured by X-ray photoelectron spectroscopy (XPS). The heat effects of stabilizers adsorption on nanoparticles were measured by solution calorimetry. The excess amount of oxygen was possibly the result of the hydroxygen formed on the surface of the nanoparticles. The heat effects showed that compounds containing carboxyl groups can be adsorbed chemically on magnetite by forming chemical bonds. The other stabilizers involving NH-groups, such as polyethylene-imine, can be adsorbed physically. The exothermic value is about half of the former case. Supported by the National Natural Science Foundation of China (Grant No. 50476039), and Guangdong Provincial Department of Science and Technology (Grant No. 2004A10-703001)     

Comparison of the Solubility of ZnFe<Subscript>2</Subscript>O<Subscript>4</Subscript>, Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> and Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> in High Temperature Water

As the solubility is a direct measure of stability, this study compares the solubilities of ZnFe₂O₄, Fe₃O₄ and Fe₂O₃ in high temperature water. Through literature analysis and formula derivation, it is shown that it is reasonable to assume ZnFe₂O₄ and Fe(OH)₃ coexist when ZnFe₂O₄ is dissolved in water. Results indicated that the solubility of ZnFe₂O₄ is much lower than that of Fe₂O₃ or Fe₃O₄. The low solubility of ZnFe₂O₄ indicates that it is more protectively stable as an anticorrosion phase. Moreover, the gap between the solubility of ZnFe₂O₄ and that of Fe₃O₄ or Fe₂O₃ was enlarged with an increase of temperature. This means that ZnFe₂O₄ is more protective at higher temperatures. Further analysis indicated that with the increase of temperature, the solubility of ZnFe₂O₄ changed little while those of Fe₂O₃ or Fe₃O₄ changed a lot. Little change of the solubility of ZnFe₂O₄ with increase of temperature showed that ZnFe₂O₄ is stable. The very low and constant solubility of ZnFe₂O₄ suggests that it is more protective than Fe₂O₃ and Fe₃O₄, especially in water at higher temperature.     

Synthesis processes and transport properties of solid solutions in the Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-GeO<Subscript>2</Subscript>-V<Subscript>2</Subscript>O<Subscript>5</Subscript> system

The results of studies of solid solutions with the overall composition of Bi₄V_{2 ? x} Ge _x O_{11 ? δ} and Bi₄Ge_{3 ? x} V _x O_{12 + δ} are presented. The process of phase formation are studied during the synthesis of solid solution using the ceramic method and through liquid precursors. Crystallochemical parameters of the obtained compounds are determined. The size distribution of the particles is studied. Conductivity of annealed of polycrystalline samples as a function of temperature and composition is studied using the impedance spectroscopy method. The shape of impedance complex plane plots of the samples obtained in different ways is studied and analyzed.