A study of growth and morphological features of TiOxNy thin films prepared by MOCVD

The growth and morphological features of MOCVD TiO_xN_y films have been characterized to evaluate the effect of various process parameters on film growth. XRD analysis of the films deposited at 600°C on Si(1 1 1) and mica show a TiN(1 1 1) peak at 2θ=36.6°, but only anatase peaks are detected below 550°C. Above 650°C, both anatase and rutile peaks are detected. The presence of ammonia is not effective below 550°C as the deposited film is mostly TiO₂. Also, ammonia does not play any role in homogeneous nucleation in the gas phase, as evident by the deposition of anatase/rutile particles above 650°C. The following changes in the morphological features are observed by varying process parameters. By increasing the ratio of titanium-isopropoxide to ammonia flow, the cluster shape changes from angular to rounded; dilution of the flow results in larger elongated clusters; increase in flow rate at constant precursor to ammonia ratios, changes the cluster shape from rounded to elongated and the cluster size deceases. Deposition at higher temperatures results in finer clusters with a slower growth rate and eventually results in a very thin film with particle deposition at 650°C and above.     

Electrical and optical properties of Cd1−xZnxS (0x0.18) grown by chemical bath deposition

Cd_1−xZn_xS films with 0x0.18 were grown by chemical bath deposition technique on glass substrates from an aqueous solution containing cadmium and zinc sulfate, ammonia and thiourea. Microstructural features, obtained from X-ray diffraction and scanning electron microscopy (SEM) measurements, reveal a predominance of Wurtzite structure and an homogenous microstructure formed by densely microcrystallines for all the samples studied. Cd_1−xZn_xS semiconductor was found to be resistive and of n-type. Also, the electron density decreases with increased x and the mobility reaches a maximum around x=0.12. Which means that the Cd_1−xZn_xS films at this composition are of high crystalline quality, i.e. having reduced intrinsic defect concentrations.     

XPS and electroluminescence studies on SrS1−xSex and ZnS1−xSex thin films deposited by atomic layer deposition technique

SrS_1−xSe_x and ZnS_1−xSe_x thin films were deposited by the atomic layer deposition (ALD) technique using elemental selenium as the Se source, thus avoiding use of H₂Se or organometallic selenium compounds. X-ray diffraction (XRD) analysis showed that the films were solid solutions and X-ray photoelectron spectroscopy (XPS) data showed that the surface of both ZnS_1−xSe_x and SrS_1−xSe_x were covered with an oxide and carbon-containing contaminants from exposure to air. The oxidation of SrS_1−xSe_x extended into the film and peak shifts from sulfate were found on the surface. Luminance measurements showed that emission intensity of the ZnS_1−xSe_x:Mn alternating current thin film electroluminescent (ACTFEL) devices at fixed voltage was almost the same as that of the ZnS:Mn device, while emission intensity of the SrS_1−xSe_x:Ce devices decreased markedly as compared to the SrS:Ce device. Emission colors of the devices were altered only slightly due to selenium addition.     

Photocurrent measurements on GaAs1−xNx epilayers grown by metalorganic chemical vapor deposition

GaAs_1−xN_x epilayers were grown on a GaAs(0 0 1) substrate by metalorganic chemical vapor deposition. Composition was determined by high resolution X-ray diffraction. Band gap was measured from 77 to 400 K by using photocurrent measurements. The photocurrent spectra show clear near-band-edge peak and their peak energies drastically decrease with increasing nitrogen composition due to band gap bowing in the GaAs_1−xN_x epilayers. Those red shifts were particularly notable for low nitrogen compositions. However, the shifts tended to saturate when the nitrogen composition become higher than 0.98%. When the nitrogen composition is in the range 1.68–3.11%, the measured temperature dependence of the energy band gap was nicely fitted. However, the properties for the nitrogen composition range 0.31–0.98% could not be fitted with a single fitting model. This result indicates that the bowing parameter reaches 25.39 eV for low nitrogen incorporation (x=0.31%), and decreases with increasing nitrogen composition.     

MBE growth of cubic AlyGa1−yN/GaN heterostructures—structural, vibrational and optical properties

Cubic Al_yGa_1−yN/GaN heterostructures on GaAs(0 0 1) substrates were grown by radio-frequency plasma-assisted molecular beam epitaxy. High resolution X-ray diffraction, micro-Raman, spectroscopic ellipsometry, and cathodoluminescence measurements were used to characterize the structural, optical and vibrational properties of the Al_yGa_1−yN epilayers. The AlN mole fraction y of the alloy was varied between 0.07<y<0.20. X-ray diffraction reciprocal space maps demonstrate the good crystal quality of the cubic Al_yGa_1−yN films. The measured Raman shift of the phonon modes of the Al_yGa_1−yN alloy was in excellent agreement with theoretical calculations. Both SE and CL of the Al_yGa_1−yN epilayer showed a linear increase of the band gap with increasing Al-content.     

High-resolution electron microscopy of microstructure of SrTiO3/BaZrO3 bilayer thin films on MgO substrates

SrTiO₃/BaZrO₃ heterofilms as buffer layers are deposited on (0 0 1) MgO substrates by an RF-sputtering technique. The atomic structure and the defect configuration at the interfaces are investigated by means of aberration-corrected high-resolution transmission electron microscopy. At the BaZrO₃/MgO interface, two types of interfacial structures, MgO/ZrO₂-type and MgO/BaO-type, are observed. Antiphase boundaries and dislocations are found at the BaZrO₃/MgO interface. The formation of these lattice defects is discussed in terms of film growth and structural imperfections of the substrate surface. At the SrTiO₃/BaZrO₃ interface, a high density of misfit dislocations is observed with different configurations. The formation of these dislocations contributes both to the relaxation of the large misfit strain and to stopping of the further propagation of lattice defects which are formed in the BaZrO₃ layer into the SrTiO₃ layer.     

Mechanochemical metathesis synthesis and characterization of nano-structured MnV2O6·xH2O (x=2, 4)

A solid-state metathesis approach for the synthesis of hydrated MnV₂O₆·xH₂O (x=2, 4) materials driven by mechanochemical activation energy has been demonstrated. The metathesis pathway of forming the desired product is confirmed by the presence of high lattice energy by-product such as NaCl. The structural, optical, and chemical properties of the synthesized materials are examined by powder X-ray diffraction, X-ray photoelectron spectroscopy, thermo gravimetric analysis, scanning electron microscopy, transmission electron microscopy, and diffused reflectance measurements in the UV–vis range. The valence state of Mn and V was determined to be +2 and +5, respectively, for the title compounds and the bandgap values determined showed these materials are likely to be semiconductors.     

The growth and spectroscopic characteristics of Ca3Y2(BO3)4:Er laser crystal

The Ca₃Y₂(BO₃)₄:Er³⁺ crystal with a size up to 20 mm×30 mm was grown by the Czochralski method. The absorption spectrum was measured and its absorption peaks were assigned to the corresponding transitions between the Er³⁺ energy levels. A broad emission spectrum from 1429.4 to 1662.8 nm was exhibited from 530 nm wavelength pumping. This crystal is promising as a tunable infrared laser crystal.     

Growth and shape control of orthorhombic Fe5(PO4)4(OH)3·2H2O single crystalline dendrites

Orthorhombic Fe₅(PO₄)₄(OH)₃·2H₂O single crystalline dendritic nanostructures have been synthesized by a facile and reproducible hydrothermal method without the aid of any surfactants. The influences of synthetic parameters, such as reaction time, temperature, the amount of H₂O₂ solution, pH values, and types of iron precursors, on the crystal structures and morphologies of the resulting products have been investigated. The formation process of Fe₅(PO₄)₄(OH)₃·2H₂O dendritic nanostructures is time dependent: amorphous FePO₄·nH₂O nanoparticles are formed firstly, and then Fe₅(PO₄)₄(OH)₃·2H₂O dendrites are assembled via a crystallization-orientation attachment process, accompanying a color change from yellow to green. The shapes and sizes of Fe₅(PO₄)₄(OH)₃·2H₂O products can be controlled by adjusting the amount of H₂O₂ solution, pH values, and types of iron precursors in the reaction system.     

Growth and photoluminescence properties of vertically aligned SnO2 nanowires

Vertically aligned SnO₂ nanowires (NWs) were grown for the first time by a vapor–liquid–solid method on c-sapphire with gold as a catalyst under Ar gas flow. Electron backscatter diffraction analysis indicated the NWs are single crystalline having the rutile structure, grow vertically along the [1 0 0] direction, and exhibit a consistent epitaxial relationship where lattice mismatch is estimated to be 0.3% along the SnO₂ [0 1 0] direction. The growth of these NWs is sensitive to many parameters, including growth duration, substrate type, source vapor concentration, and the thickness of the catalyst layer. Photoluminescence measurements at room temperature showed that the vertically aligned NWs exhibit an intense transition at 3.64 eV, a near band-edge transition which is rarely observed in SnO₂.     

Three-dimensional Bi2Se3 nanopattern films self-assembled with ultrathin nanosheets on the surface of Se nanotubes

Regular three-dimensional (3D) rose-like Bi₂Se₃ nanopattern film is fabricated through a simple chemical route. This nanopattern film is self-assembled with ultrathin Bi₂Se₃ nanosheets having thicknesses of less than 8 nm. The Bi₂Se₃ nanosheets were formed on the surface of Se nanotubes, and the Se nanotubes were used as both the Se resource and the substrate to support the growth of the Bi₂Se₃ nanopattern film. Since several length scales are involved in this confined 3D structure, which are developed at different time, during the formation of the micro-structure, a careful control of these length scales is expected to provide new opportunities for engineering the boundary scattering of phonons of different wavelengths and developing new thermoelectric materials with novel properties.     

Atomic modelling of crystal/complex fluid/crystal contacts—Part II. Simulating AFM tests via the GenMol code for investigating the impact of CO2 storage on kaolinite/brine/kaolinite adhesion

GenMol^TM code is used to simulate Atomic Force Microscopy (AFM) tests at a kaolinite/brine/kaolinite contact, the confined fluid in sub-nanometre interspaces being in equilibrium with an external multi-species solution. The attraction/repulsion effort, i.e. the derivative versus the interspace aperture h of the interaction energy between both kaolinite faces, is computed versus the variable composition of the confined fluid (see for the method Part I of this work). Two external solutions are tested. Solution S1 is a neutral brine (pH=7.5) leading to a possible attraction for apertures lower than 7 Å. Solution S2 is an acidified brine (pH=3.2) leading to repulsion whatever may be the aperture h. These two AFM simulations prove the existence of a critical pH value (3.2<pH_crit<7.5) of the external solution, below which the acidification of a natural brine in a CO₂ confinement inhibits adhesion between kaolinite aggregates.     

Study of effects of polishing and etching processes on Cd1−xZnxTe surface quality

The effect of surface preparation on CdZnTe properties was investigated. Surface etching using bromine solutions enhances Te elemental composition, resulting in a Te rich surface layer that is prone to oxidize. This oxidation degrades the performance of the fabricated CZT gamma detector. Roughness results were identical for samples polished with 1 and 3 μm and subsequently etched in 2% Br-MeOH. The optimal concentration of etching was 2% Br-MeOH.     

Thermal-induced phase transition and assembly of hexagonal metastable In2O3 nanocrystals: A new approach to In2O3 functional materials

This paper reports on the thermal-induced performance of hexagonal metastable In₂O₃ nanocrystals involving in phase transition and assembly, with particular emphasis on the assembly for the preparation of functional materials. For In₂O₃ nanocrystals, the metastable phase was found to be thermally unstable and transform to cubic phase when temperature was higher than 600 °C, accompanied by assembly as well as evolution of optical properties, but the two polymorphs coexisted at the temperature ranging from 600 to 900 °C, during which the content of product phase and crystal size gradually increased upon increasing temperature. The assembly of In₂O₃ nanocrystals can be developed to fabricate In₂O₃ functional materials, such as various ceramic materials, or even desired nano- or micro-structures, by using metastable In₂O₃ nanocrystals as precursors or building blocks. The electrical resistivity of In₂O₃ conductive film fabricated by a hot-pressing route was as low as 3.72×10⁻³ Ω cm, close to that of In₂O₃ single crystal, which is important for In₂O₃ that is always used as conductive materials. The findings should be of importance for both the wide applications of In₂O₃ in optical and electronic devices and theoretical investigations on crystal structures.     

Hydride-assisted growth of GaN nanowires on Au/Si(0 0 1) via the reaction of Ga with NH3 and H2

High quality, straight GaN nanowires (NWs) with diameters of 50 nm and lengths up to 3 μm have been grown on Si(0 0 1) using Au as a catalyst and the direct reaction of Ga with NH₃ and N₂:H₂ at 900 °C. These exhibited intense, near band edge photoluminescence at 3.42 eV in comparison to GaN NWs with non-uniform diameters obtained under a flow of Ar:NH₃, which showed much weaker band edge emission due to strong non-radiative recombination. A significantly higher yield of β-Ga₂O₃ NWs with diameters of ≤50 nm and lengths up to 10 μm were obtained, however, via the reaction of Ga with residual O₂ under a flow of Ar alone. The growth of GaN NWs depends critically on the temperature, pressure and flows in decreasing order of importance but also the availability of reactive species of Ga and N. A growth mechanism is proposed whereby H₂ dissociates on the Au nanoparticles and reacts with Ga giving Ga_xH_y thereby promoting one-dimensional (1D) growth via its reaction with dissociated NH₃ near or at the top of the GaN NWs while suppressing at the same time the formation of an underlying amorphous layer. The higher yield and longer β-Ga₂O₃ NWs grow by the vapor liquid solid mechanism that occurs much more efficiently than nitridation.     

In-situ visualization of a super-accelerated synthesis of zinc oxide nanostructures through CO2 laser heating

A simple growth technique capable of growing a variety of zinc oxide (ZnO) nanostructures with record growth rates of 25 μm/s is demonstrated. Visible lengths of ZnO nanowires, nanotubes, comb-like and pencil-like nanostructures could be grown by employing a focused CO₂ laser-assisted heating of a sintered ZnO rod in ambient air, in few seconds. For the first time, the growth process of nanowires was videographed, in-situ, on an optical microscope. It showed that ZnO was evaporated and presumably decomposed into Zn and oxygen by laser heating, reforming ZnO nanostructures at places with suitable growth temperatures. Analysis on the representative nanowires shows a rectangular cross-section, with a [0 0 0 1] growth direction. With CO₂ laser heating replacing furnace heating used conventionally, and using different reactants and forming gases, this method could be easily adopted for other semiconducting inorganic nanostructures in addition to ZnO.     

Cs2LiGdCl6 (Ce): New scintillation material

We investigated the scintillation properties of Cs₂LiGdCl₆:Ce³⁺ as a function of the Ce concentration. X-ray excited luminescence spectra of the scintillation material showed broad emission bands between 360 and 460 nm, with two overlapping peaks, due to the d→f transitions on Ce³⁺ ions. The samples provide good scintillation results. The energy resolution was found to be 5.0% (FWHM) at 662 keV for 10% Ce sample. Under γ-ray excitation, Cs₂LiGdCl₆:Ce³⁺ showed three exponential decay time components of about 130–200 ns decay time constant. The light output of the investigated samples was 20,000 photons/MeV for a 10% Ce concentration. The light output deviation from the linear response is within 7% between the energy range of 31 and 1333 keV. Overall, the scintillation properties confirm that Cs₂LiGdCl₆:Ce³⁺ single crystal is a promising candidate for medical imaging and radiation detection.     

Bi20TiO32 nanocones prepared from Bi–Ti–O mixture by metalorganic decomposition method

Bi₂₀TiO₃₂ in the form of nanocones are reported for the first time, which have been found during the formation of Bi₂Ti₂O₇ nanocrystals. Bi₂₀TiO₃₂ nanocones were prepared by metalorganic decomposition technique. From X-ray patterns, it was found that Bi₂₀TiO₃₂ is a metastable phase, and can transform gradually into Bi₂Ti₂O₇ phase with the annealing time increasing at a temperature of 550°C. The image of field emission scanning electron microscopy shows that the lengths of the nanocones are up to several micrometers and the diameters of cusps range from 20 to 200 nm. The studies of transmission electron microscopy show that the nanocones are crystalline Bi₂₀TiO₃₂. The growth mechanism of Bi₂₀TiO₃₂ nanocones has been proposed, which is similar to the vapor–liquid–solid growth mechanism.