Ni-Mn-Ce-K/铝土矿催化剂的制备和还原条件对水煤气变换性能的影响

以改性铝土矿为载体,采用等体积浸渍法,制备了Ni-Mn-Ce-k体系水煤气变换催化剂.通过TG、DTA、TPR和活性表征等方法,系统考察了制备和还原条件对催化剂水煤气变换性能的影响.结果表明:催化剂的优化制备工艺为:第一步浸渍组分Ni、Mn、Ce的盐溶液(其摩尔配比为8:7:4),焙烧温度500℃,第二步浸渍K的加入量为5%(W),还原最高温度为500℃,还原过程添加适量的水蒸气,制得的催化剂具有良好的催化性能和热稳定性能,优于国内外现行工业产品.     

预处理条件对Ni-Ce-P非晶态合金液相加氢活性的影响

采用真空骤冷技术制备了Ni82Ce0.31P17.7和Ni82P18非晶态合金。通过高压氢气中热处理, 使其粉化。DSC研究结果表明加入少量Ce使Ni-P非晶态合金晶化温度提高160℃。用高压反应釜考察了氧化温度和氢还原温度对Ni-De-P非晶态合金本乙烯液相加氢活性的影响, 并对比了Ni-P和Ni-Ce-P的加氢活性, 活性测试的结果表明: 氧化、还原处理过程使Ni-Ce-P加氢活性显著增加, 最佳的预处理条件是240℃氧化1h, 300℃氢气还原2h; Ni-Ce-P加氢活性是Ni-P加氢活性的3-4倍, 用AES和XPS研究了氧化、还原过程中,Ni-Ce-P表面性质的变化。     

Au/Ce1-xZrxO2催化剂的制备、表征及其在CO氧化和水煤气变换反应中的催化性能

采用共沉淀法制备了不同锆铈摩尔比的Ce1-xZrxO2(x=0,0.1,0.3,0.5,0.7,0.9和1.0)氧化物,并以改性的浸渍法制备了金担载量为1%(质量分数)的Au/Ce1-xZrxO2催化剂.考察了催化剂在低温CO氧化和水煤气变换反应中的催化性能.应用氮物理吸附、X射线衍射、透射电镜和H2程序升温还原等技术对氧化物载体及其负载金催化剂进行了表征,并与其催化性能进行了关联.结果表明,与纯CeO2和ZrO2相比,Ce1-xZrxO2的比表面积增大而孔径减小,孔分布更加集中.Zr的加入使表面Ce4 的还原更加困难,使体相Ce4 的还原更加容易.活性组分金的加入有利于铈锆氧化物的还原.ZrO2载体较大的孔径使金在载体表面分散均匀而粒子较小,因此与Au/CeO2和Au/Ce1-xZrxO2相比,Au/ZrO2具有更好的低温CO氧化活性和水煤气变换活性,而Au/CeZrO在高温下的水煤气变换反应中表现出更好的催化性能.     

铈对Fe-4%Si合金凝固特征温度的影响及机制

针对不加Ce和添加Ce的Fe-4%Si合金,采用NETZSCH STA 449C型综合热分析仪测定其示差扫描量热（DSC）曲线,探讨添加Ce对Fe-4%Si合金近平衡凝固过程中特征温度的影响。利用液态金属冷却（LMC）定向凝固技术,对添加Ce的Fe-4%Si合金试样通过定向凝固实验保留固-液界面。采用岛津EPMA-1720H电子探针（EPMA）,对添加Ce的Fe-4%Si合金定向凝固样品,进行长时间点定量分析,探索Ce在固-液界面处的富集。结果表明,添加Ce使Fe-4%Si合金近平衡凝固过程中液相线温度和固相线温度都有降低的趋势、结晶温度区间有增大的趋势。EPMA长时间点定量分析,证实了凝固过程中Ce能够以原子或夹杂物形式在固-液界面前沿的液相富集。界面处Ce的富集,可能阻碍凝固生长过程中原子的供应,进而影响Fe-4%Si合金的近平衡凝固特征温度及结晶温度区间。     

NaCl-CsCl熔盐中Ce(Ⅲ)离子的阴极过程研究

以钨微盘为研究电极采用循环伏安法和方波伏安法研究了温度为873K的NaCl-CsCl熔盐中Ce3 离子的阴极行为.结果表明,摩尔比为1:2的NaCl-CsCl熔盐体系中Ce3 离子分两步还原,其电化学反应历程为:Ce3 e=Ce2 ,Ce2 2e-=Ce.进一步计算得到熔盐体系中Ce3 离子的扩散系数(D).     

CeO2-TiO2混合氧化物及Pd/CeO2-TiO2催化剂的氧化还原性能

 以溶胶-凝胶-超临界流体干燥法制备了CeO2-TiO2混合氧化物(n(Ce)/n(Ti)=0.05～0.40),以其为载体,通过等体积浸渍法制备了Pd/CeO2-TiO2催化剂. XRD分析结果表明,在低Ce/Ti比的CeO2-TiO2混合氧化物中,CeO2高度分散于TiO2上; Ce/Ti比高于0.10时,大晶粒锐钛矿相TiO2和TiO2-CeO2固溶体或其前驱体无定形相共存. 采用H2-TPR对所合成材料的氧化还原性能进行了研究. H2-TPR谱中500 ℃附近的耗氢峰对应于CeO2-TiO2中CeO2的还原,还原过程中不存在表面晶格氧与体相晶格氧的差别. 由于TiO2与CeO2的协同作用,混合氧化物中形成了丰富的结构缺陷,提高了CeO2的氧化还原性能,其中Ce/Ti比为0.20时TiO2与CeO2的协同作用最显著. 负载上Pd后,载体中CeO2的还原温度(＜150 ℃)大大降低,同时随着Ce/Ti比的增大,PdO与载体间的相互作用增强,导致PdO难于还原,相应的H2-TPR还原峰向高温方向移动.     

镧、铈对Pt, In/Al2O3催化剂选择性还原NO性能的影响

采用溶胶-凝胶法(SG)制备了掺杂少量La或Ce的Pt/Al2O3贵金属催化剂和In2O3/Al2O3氧化物催化剂, 并考察了La或Ce对催化剂的比表面和晶相结构和丙烯在这些催化剂上选择性还原NO的活性. 结果表明, 掺杂少量的La或Ce, 可以改变催化剂的热稳定性, 富氧条件下丙烯选择性催化还原NO的反应中, La或Ce的掺杂对催化活性和催化活性温度窗口没有明显改善.     

氯化物熔体中铈离子在铁阴极上的电还原

用循环伏安法、充电曲线和衰减曲线研究了在700～850°CNaCl-KCl-CeCl_3熔体中铈离子在铁电极上的还原过程。Ce(Ⅲ)还原时,首先形成金属间化合物,然后析出纯金属铈。用铁阴极电解制取了含83wt％Ce的Ce-Fe合金,其物相为CeFe_2和Ce。     

Ce4+/Ce3+-V2+/V3+氧化还原流动电池的可行性研究(Ⅱ)--旋转圆盘(RDE)与旋转环盘(RRDE)法对Ce4+/Ce3+氧化还原体系的研究

用RDE与REDE法研究了Ce4+/Ce3+-V2+/V3+氧化还原流动电池中Ce4+/Ce3+体系的电化学动力学参数,以说明组成该新型氧化还原流动电池的可能性.用RDE法得出在铂电极表面与玻碳电极上均会生成一层氧化膜,对Ce3+的氧化反应产生阻碍作用.但在铂上的氧化膜对Ce4+的还原反应却有催化作用.用Rrde法得出Ce3+在玻碳电极上的氧化与析氧之间存在着竞争,为得到较高的Ce3+氧化效率,应控制氧化电流在2～8 mA@cm-2之间.     

CeO_2-ZrO_2-Al_2O_3材料的制备及其单钯催化剂性能的研究

采用水热晶化法制备了Ce O2-Zr O2-Al2O3储氧材料,详细考察了制备过程中水热时间和温度对储氧材料结构和性能的影响。X射线衍射(XRD)、N2物理吸附、H2程序升温还原(H2-TPR)和热重分析技术(TG)表征结果表明,当水热温度为100℃,水热时间为12 h时,制备的Ce O2-Zr O2-Al2O3材料具有优异的结构性能、织构性能、还原性能和储氧性能。分别以较优水热条件下制备的Ce O2-Zr O2-Al2O3储氧材料和商用的铈锆铝储氧材料为载体,制备Pd/Ce O2-Zr O2-Al2O3催化剂,考察了其对汽车尾气中碳氢化合物的催化转化能力。     

预硫化处理对Ce-TiO2催化剂NH3-SCR反应活性影响及其反应机理研究

通过对Ce-TiO2催化剂进行SO2+O2气氛下的不同时间的预硫化处理并用于NH3-SCR反应,研究了Ce-TiO2催化剂物化特性随预硫化时间的演变规律,以及预硫化对中低温活性及NH3-SCR反应路径的影响。结果表明Ce-TiO2催化剂表面氧化铈的硫酸化相当迅速,在预硫化处理0.5h后,几乎所有的表面氧化铈都被硫酸盐化形成硫酸铈,随着硫酸化时间的增加到1h和1.5h,Ce-TiO2催化剂上沉积的硫缓慢增加。活性测试表明预硫化后的催化剂对SCR活性的抑制作用随着反应温度的提高而减弱,结合NO-DRIFT、NH3-DRIFT等多种原位表征,结果表明预硫化后低温NH3-SCR活性大幅降低是由于生成硫酸铈后催化剂氧化还原能力大幅削弱,E-R反应路径严重受阻。随着反应温度的升高,SCR活性逐渐不受硫酸铈沉积的影响,一方面,氧化还原性能的提高导致E-R反应路径逐渐恢复;另一方面,硫酸铈的生成促进了NO的活化,增强了L-H反应路径,两者共同导致了预硫化后较高的中温NH3-SCR活性。     

Preparation of mesoporous carbon from commercial activated carbon with steam activation in the presence of cerium oxide

Mesoporous carbon was prepared from the commercial activated carbon by steam activation with cerium oxide as catalyst. Steam activation with a catalyst loading of 0.5-2.0 wt% at 680-870 degrees C was examined. The surface area and pore size were evaluated by nitrogen adsorption at 77 K, and the structure of cerium oxide was characterized by XRD, XPS, and TEM. The results showed that the catalyst promoted the development of a mesopore at lower temperature (680-740 degrees C), and the mesopore was concentrated around 4-10 nm. The noncatalytic activation was advantageous in mesopore development and the catalyst would restrict the formation of mesopores at high temperature (800-870 degrees C). Higher loading of cerium oxide and higher activation temperature caused the aggregation of cerium oxide and then resulted in scattered pore size distribution.     

NO选择性催化还原Ce-Mn-Ti-O催化剂铈组分助催化作用

用NH3程序升温脱附(NH3-TPD)、X射线衍射(XRD)、X射线光电子能谱(XPS)、H2程序升温还原(H2-TPR)和BET表面积测试结合NO选择性催化还原(SCR)微型反应评价等方法,研究了溶胶-凝胶法制备的Ce-Mn-Ti-O复合氧化物催化剂中铈组分的助催化作用.结果表明随铈含量增加,NO转化率大幅度增加,在Ce/Mn摩尔比约0.08时达极大值,其后随铈含量进一步增加,NO转化率又逐渐下降.适量铈组分的加入对Mn-Ti-O催化剂表面酸性影响不大,但增加了催化剂活性组分Mn物种的表面浓度,提高了Mn4+物种的相对含量和Mn物种的可还原性,从而提高催化剂低温SCR活性.当Ce/Mn摩尔比超过0.08,催化剂表面的Mn组分与Ce组分可能形成无定型结构的多层聚集的Ce-O-Mn物种,导致催化剂Mn/Ti摩尔比下降和Mn物种可还原性下降,从而导致催化剂SCR活性的下降.     

Catalytic wastewater treatment from chemical container cleansing

The catalytic wet oxidation method was used for treatment of wastewater from chemical containers contaminated with various highly toxic pollutants. A heterogeneous catalyst containing Cu²⁺ ions on active carbon as an active component was proposed. The influence of the Cu2+ concentration, temperature, and calcination duration on the efficiency of the copper- containing catalyst was studied. The optimal results were obtained from the catalyst heated for 3 h at 573 K upon the impregnation with 6% Cu²⁺. The study of the copper catalyst doped with cerium showed that the optimal content of the promoter was 6%. The copper and cerium catalysts were characterized by thermal analysis, scanning electron microscopy, and X-ray diffraction analysis. The catalyst lifetime and the resistance of cerium to removal were studied. The introduction of cerium increases the activity and life of the catalyst and decreases the concentration of Cu²⁺ ions removed from the surface to 15 mg L^-1. The treatment parameter estimated by a decrease in the chemical oxygen demand increased from 89.7 to 94.8%.     

Influence du cérium dans l'hydrogénation sélective du cinnamaldéhyde en présence de catalyseurs cobalt supportés

The study of the cinnamaldehyde hydrogenation over supported cobalt catalysts shows that the addition of cerium to cobalt increases the selectivity to unsaturated alcohol without decrease of the activity. Moreover the support has an important effect over the catalytic properties of the mixed cobalt-cerium system; active carbons clearly lead to the most active catalysts. If the calcination step does not modify the catalytic properties, the reduction step has a decisive effect, i.e. after a reduction with hydrogen at low temperature, a selectivity to unsaturated alcohol of 95 % is obtained at a conversion of 90 %. The preparation method, especially the order of addition of the elements (cobalt and cerium) to the support (C_L2S) also has an important effect, both on the activity and the selectivity. The first step of ceria dispersion on the support leads to the most efficient catalyst. The study of the catalysts reducibility and the electron microscopy micrographs show that in that case, the cobalt and cerium dispersion are much more important than that observed with another preparation.     

铈源对甲醇水蒸气重整制氢CuO/CeO2催化剂的影响

采用沉淀法合成了CeO_2载体,再经浸渍法负载活性组分得到CuO/CeO_2催化材料,探究了铈源(Ce(NO_3)_3·6H_2O、Ce Cl_3·6H_2O、Ce(NH_4)_2(NO_3)_6、Ce(SO_4)_2·4H_2O)对CuO/CeO_2催化性能的影响。通过采用XRD、SEM、N_2O滴定、BET和H_2-TPR等表征手段对催化材料的结构和性质研究发现,四种铈源合成的CuO/CeO_2催化材料在Cu比表面积、还原性能以及活性组分和载体间的相互作用方面存在着明显差别。其中,由Ce(NO_3)_3·6H_2O合成的CuO/CeO_2催化材料的Cu比表面积较大,CuO还原温度较低,CeO_2载体与CuO之间相互作用较强,在甲醇水蒸气重整反应过程中,表现出较佳的催化活性,在反应温度为553 K,水醇比n(H_2O)/n(MeOH)为1.2,甲醇水蒸气气体空速(GHSV)为1760 h~(-1)时,甲醇的转化率为100%,重整气中CO摩尔含量为0.84%。     

介孔Co_3O_4-CeO_2复合氧化物的制备及在CO选择性氧化中的应用

以硝酸钴和硝酸铈为前驱物,SBA-15为硬模板,利用双溶剂法制备了Co3O4-CeO2介孔复合氧化物,通过X-射线衍射、N2吸脱附测试、程序升温还原和透射电子显微镜等技术对活性组分及载体进行了表征,并且与浸渍法和共沉淀法所制备的催化剂进行了对比分析.结果表明,相比于浸渍法和共沉淀法,采用双溶剂法制备的介孔Co3O4-C...     

An efficient method for dephosphorylation of phosphopeptides by cerium oxide

In this article, an effective method for dephosphorylation of phosphopeptides by cerium oxide is described. The dephosphorylation activity of cerium oxide was evaluated by two standard phosphopeptides and the phosphopeptides in digests of phosphoprotein alpha-casein and beta-casein. Results showed that the dephosphorylation of all the phosphopeptides was completed in 10 min, and temperature had little effect on the dephosphorylation, the dephosphorylation could be carried out at 0 degrees C, room temperature and 37 degrees C. The dephosphorylation mediated by cerium oxide can be attributed to Lewis acid and nucleophile activations. Advantages of using cerium oxide as catalyst for the dephosphorylation include: safe, simple, high catalytic activity, and no precise control of the treatment temperature. The method is valid for the phosphorylation of Ser, Thr and Tyr, and can be used for phosphoprotein analysis.     

碱金属沉积对Mn-Ce/TiO_2低温SCR催化剂性能影响

采用溶胶凝胶法制备了Mn-Ce/TiO_2低温SCR催化剂,考察了碱金属浓度与种类对催化剂活性的影响,探究了不同反应条件下钠盐沉积对活性保留分率的影响,利用SEM、BET、XRD和FT-IR对催化剂碱金属中毒原因进行了分析。结果表明,碱金属毒化后催化剂脱硝活性下降,钾中毒催化剂失活程度高于钠中毒的催化剂,2%钾中毒催化剂在160℃时NO去除率为62.0%,较新鲜催化剂下降29.2%。这主要因为碱金属毒化造成催化剂比表面积明显减小,且催化剂载体锐钛矿型TiO_2部分转化为金红石型,BET和SEM表征均说明碱金属沉积堵塞了催化剂表面的微孔。碱金属对Mn-Ce/TiO_2催化剂活性保留分率的影响表明,催化剂的颗粒粒径对其活性保留分率影响不大,碱金属含量减小、温度升高,Mn-Ce/TiO_2催化剂的活性保留分率增加,Na_2SO_4和NaCl对Mn-Ce/TiO_2催化剂的脱硝活性抑制作用大于KNO_3。     

CeO2/NaY催化剂的氧合及其催化氧化脱硫性能

采用等体积浸渍法制备了一系列CeO₂/NaY催化剂,重点考察了焙烧温度和铈负载量对催化剂活性组分结构及性能的影响。通过拉曼（Raman）光谱、X射线衍射（XRD）、低温N₂吸附-脱附（BET）、高分辨透射电子显微镜（HR-TEM）以及氢气程序升温还原（H₂-TPR）等技术对催化剂的结构、形貌和化学性能进行了表征分析。结果表明,焙烧温度与铈负载量对于铈物种在分子筛载体表面及孔道内的分散形态和与载体的相互作用有着重要影响,进而影响催化剂中铈物种的氧合性能与氧化脱硫性能。在常温常压下的氧合性能测试,催化剂最大储氧量为每克催化剂1.44 mmol O₂。在反应温度100 ℃,催化剂用量0.20 g,以正辛烷为溶剂二苯并噻吩初始浓度为500 μg·g^-1的模拟油样20 mL,氧气流量为50 mL·min^-1的条件下,反应240 min二苯并噻吩转化率可达90.10%,二苯并噻吩被氧化为二苯并噻吩砜。因此,发展稀土改性分子筛催化剂,应用于以分子氧为氧化剂的油品氧化深度脱硫,对探究绿色高效的油品氧化脱硫技术具有积极意义。