Pt对Ni2P/MCM-41催化剂加氢脱硫性能的影响

以MCM-41为载体, 采用程序升温还原法制备了含有少量Pt的Ni-P/MCM-41催化剂, 并用氢气程序升温还原(H₂-TPR)、 X射线衍射(XRD)、 N₂吸附比表面积、 X射线光电子能谱(XPS)和透射电子显微镜(TEM)对催化剂的结构和性能进行了表征. 考察了P/Ni摩尔比及Pt含量对Ni-P/MCM-41催化剂催化二苯并噻吩(DBT)加氢脱硫(HDS)性能的影响. 结果表明, Pt能降低Ni₂P催化剂的还原温度, 并有助于Ni₂P相的生成, 抑制团聚现象, 提高催化剂的HDS活性. 当Pt的质量分数为0.6%, P/Ni摩尔比为2时, 催化剂具有最佳加氢脱硫活性, 在340 ℃, 3.0 MPa, 氢油体积比为500, 质量空速(WHSV)为2.0 h^-1的条件下, 二苯并噻吩转化率为100%, 且催化剂加氢脱硫活性在120 h内基本保持稳定.     

负载型磷化镍催化剂的溶剂热法制备及其加氢脱硫性能

以廉价的三苯基膦(PPh₃)为磷源,以三正辛胺(TOA)为液相反应体系,溶剂热法制备了负载型Ni₂P/MCM-41催化剂,并采用XRD、BET、CO吸附、XPS和TEM等手段对制备得到的催化剂进行了表征。该方法的合成温度为330 ℃,反应在常压下进行,比程序升温还原法(H₂-TPR)所需的还原温度至少低300 ℃,比传统的溶剂热法合成原料更廉价。以二苯并噻吩(DBT)为模型化合物,比较了所制备的Ni₂P/MCM-41催化剂与H₂-TPR法制备的催化剂结构以及加氢脱硫(HDS)性能。结果表明,溶剂热法能够降低催化剂表面上P物种的集聚,从而得到较大比表面积的Ni₂P催化剂(690 m²/g);促进小尺寸、高度分散的Ni₂P活性相的生成;制得的催化剂的HDS活性明显高于H₂-TPR法催化剂,在反应温度340 ℃,质量空速2.0 h^-1,H₂/油=500(体积比),3.0 MPa的条件下,Ni₂P/M41-R催化剂DBT转化率达到96.8%,较H₂-TPR法高10.6%。     

磷镍物质的量比对溶剂热法制备的磷化镍催化剂加氢脱硫性能的影响

以三苯基膦(PPh3)为磷源,以三正辛胺(TOA)为液相反应体系,采用溶剂热法制备了负载型Ni-P(x)/MCM-41催化剂(x为初始P/Ni物质的量比),并用X射线衍射(XRD)、N2吸附比表面积测定(BET)、CO吸附、X射线光电子能谱(XPS)和TEM对催化剂进行了结构表征。以含质量分数1%二苯并噻吩(DBT)的十氢萘溶液为原料,在连续固定床反应装置上,研究了初始P/Ni物质的量比对加氢脱硫(HDS)性能的影响。结果表明,在初始P/Ni物质的量比为0.5时,生成的磷化镍物相为以Ni12P5为主,含有少量Ni2P的混合相;初始P/Ni物质的量比大于0.5时,可得到纯Ni_2P相,且随着P/Ni物质的量比的提高,Ni2P晶粒粒径减小,分散度提高。在反应温度613 K,压力3.0 MPa,H_2/oil体积比500,质量空速2.0 h-1时,Ni-P(6)/MCM-41和Ni-P(10)/MCM-41催化剂的DBT转化率接近100%。     

柠檬酸对负载型磷化镍催化剂加氢脱硫性能的影响

采用溶胶-凝胶法制备了TiO₂-Al₂O₃复合载体,以柠檬酸(CA)为络合剂采用浸渍法制备了Ni₂P负载的TiO₂-Al₂O₃复合载体催化剂,并用 X 射线衍射(XRD)、N₂吸附比表面积(BET)测定、热重-差热分析(TG-DTA)、程序升温氢还原(H₂-TPR)和透射电子显微镜(TEM)技术对催化剂的结构和性质进行了表征,考察了加入CA对Ni₂P/TiO₂-Al₂O₃催化剂二苯并噻吩(DBT)加氢脱硫(HDS)性能的影响。结果表明,适量的CA可以丰富催化剂的孔道,提高催化剂的比表面积,使催化剂具有更好的孔结构、更高的金属活性组分分散度和更均一的活性组分尺寸。CA的引入可以减弱金属与载体之间的相互作用,显著降低Ni和P前驱体的还原温度,促进Ni-P-O活性相前驱态的生成。在360℃、3.0 MPa、氢油比500(体积比)、液时体积空速2.0 h^-1的条件下,反应4 h时二苯并噻吩转化率达到99.5%。在48 h内二苯并噻吩转化率可稳定在95.0%左右。     

Mo-Ni2P/SBA-15催化剂的制备、表征及加氢脱硫催化性能

以介孔分子筛SBA-15 为载体, 通过分步浸渍硝酸镍、磷酸氢二铵、钼酸铵, 然后在H₂气流下程序升温还原(H₂-TPR), 制备了一系列不同Mo 含量的Mo-Ni₂P/SBA-15 催化剂. 采用X 射线衍射(XRD)、氮气吸脱附(BET)、透射电子显微镜(TEM)和X射线光电子能谱(XPS)对催化剂的结构进行了表征, 评价了催化剂对二苯并噻吩(DBT)的加氢脱硫(HDS)活性. 结果表明, Mo-Ni₂P/SBA-15 催化剂仍然保留有介孔结构, 催化剂的物相主要是Ni₂P. 催化剂表面的Ni 以Ni^δ+和Ni²⁺形式存在; P以P^δ-和P⁵⁺形式存在; Mo以Mo^δ+和Mo⁶⁺形式存在. Mo能促进催化性能的提高, 其中Mo含量为1% (w, 质量分数)的Mo-Ni₂P/SBA-15 催化剂具有最好的二苯并噻吩加氢脱硫催化活性, 在反应温度为380 ℃, 反应压力为3.0 MPa的条件下, 二苯并噻吩的转化率可达99.03%, 所有考察的Mo-Ni₂P/SBA-15都以直接加氢脱硫(DDS)途径为主.     

磷化镍催化剂的制备机理及其加氢脱氮性能

采用热重-质谱联用技术研究了次磷酸盐在氮气中的热分解过程,探讨了次磷酸盐热分解法制备磷化镍的反应机理:次磷酸镍中的Ni²⁺能够"催化"H₂PO₂^-低温发生歧化反应生成PH₃,继而还原Ni²⁺得到Ni₂P。制备了不同负载量的Ni₂P/SiO₂催化剂,用X射线衍射(XRD)、低温N₂吸附-脱附、高分辨透射电镜(HRTEM)等分析技术对催化剂结构进行表征。结果表明,Ni₂P活性组分在SiO₂载体上具有良好的分散性,颗粒粒径为5～8 nm。以喹啉为加氢脱氮模型化合物,在高压微型固定床反应器上对催化剂活性进行评价,在反应温度为360℃、氢气压力为2.0 MPa、液时空速为2.0 h^-1、氢油体积比为500:1时,Ni₂P(20%)/SiO₂催化剂的加氢脱氮率为41.5%。     

Ni2P和MoS2催化剂在二苯并噻吩加氢脱硫反应中的氢溢流效应

对分层装填的Ni₂P//MoS₂催化剂上的二苯并噻吩加氢脱硫反应进行了研究。结果表明,分层装填的Ni₂P/Al₂O₃和MoS₂/Al₂O₃催化剂在二苯并噻吩加氢脱硫反应中存在氢溢流效应,氢溢流有助于提高MoS₂催化剂的活性位密度和加氢脱硫反应速率。由于Ni₂P比NiS_x具有更强的氢分子解离能力,Ni₂P//MoS₂催化体系的氢溢流因子略高于NiS_x//MoS₂;相对于NiS_x,Ni₂P对MoS₂催化剂是更好的助剂。     

Ni2P和MoS2催化剂在喹啉加氢脱氮反应中的协同效应

设计实验证明了Ni₂P和MoS₂催化剂在喹啉加氢脱氮反应中存在协同效应,该协同效应能够用氢溢流遥控模型理论解释。Ni₂P//MoS₂的协同因子随反应温度升高而减小,并且略微大于相同反应条件下NiS_x//MoS₂的协同因子。Ni₂P产生的溢流氢能够提高MoS₂催化剂上加氢活性位的数量,促使Ni₂P//MoS₂催化体系增加1,2,3,4-四氢喹啉和5,6,7,8-四氢喹啉加氢生成十氢喹啉的速率,提高其脱氮活性;因此,Ni₂P对MoS₂催化剂是很好的助剂。     

金属助剂对Ni/SiO2催化剂苯甲醚加氢脱氧性能的影响

采用等体积浸渍法制备了Ni/SiO₂及Ni与金属助剂M（M=Fe、Co、Cu、Zn及Ga）物质的量比为30的Ni基双金属催化剂（记作Ni₃₀M/SiO₂）,利用H₂-TPR、XRD、H₂化学吸附、NH₃-TPD以及N₂物理吸附-脱附等手段对催化剂进行了结构表征,研究了不同助剂对催化剂结构与苯甲醚加氢脱氧性能影响。结果发现,金属助剂影响了催化剂前驱体中镍物种的还原性能,表明金属助剂及镍之间存在一定相互作用。Ni₃₀M/SiO₂中Ni-M双金属晶粒粒径和Ni/SiO₂中金属Ni晶粒粒径相近。由于表面张力较低的金属会在双金属晶粒表面富集,Ni₃₀M/SiO₂的H₂化学吸附量不同程度地低于Ni/SiO₂。另外,Ni₃₀M/SiO₂催化剂的酸量（尤其较弱酸中心酸量）高于Ni/SiO₂。在300℃、常压、苯甲醚质量空速1.0 h^-1及H₂与苯甲醚物质的量比为25：1条件下考察了各催化剂苯甲醚的加氢脱氧性能。Ni₃₀M/SiO₂上苯甲醚转化率不同程度低于Ni/SiO₂,原因在于Ni₃₀M/SiO₂催化剂H₂化学吸附量较低。Ga及Zn改性催化剂上三苯（包括苯、甲苯及二甲苯）选择性分别为81.7%和76.8%,高于Ni/SiO₂（71.5%）,且Ni₃₀Ga/SiO₂及Ni₃₀Zn/SiO₂上三苯收率（分别为65.0%及63.8%）高于或接近于Ni/SiO₂（63.7%）。Ni/SiO₂及Ni₃₀M/SiO₂催化剂中,Ni₃₀Zn/SiO₂具有较高甲基转移能力及较低C-C键氢解活性。从提高碳收率、降低耗氢量角度而言,Ni₃₀Zn/SiO₂具有较佳的加氢脱氧性能,与Ni和Zn之间作用及Zn亲氧性高于Ni有关。     

Ni2P负载量对Ni2P/Ce-Al2O3催化剂结构及萘加氢性能的影响

采用程序升温还原法制备了一系列Ni₂P/Ce-Al₂O₃催化剂,考察了制备过程中Ni₂P负载量对催化剂结构及萘加氢饱和性能的影响。结果表明,Ni₂P负载量可调控活性组分Ni₂P与载体Ce-Al₂O₃之间的相互作用,进而调变催化剂的比表面积、Ni₂P粒径及催化剂活性位点数量。当Ni₂P负载量（质量分数）为17%时,催化剂具有较大的比表面积（40 m²/g）、较小的Ni₂P粒径（26.3 nm）和最多的活性位点数量（26.7 μmol/g）;同时,该催化剂萘转化率为95%,十氢萘选择性为76%,且活性稳定性良好,这主要归因于催化剂大的比表面积和高的活性位点数量为反应提供了更多的场所。     

Ni_2P/TiO_2-Al_2O_3催化剂的制备及其加氢脱硫、脱氮性能

采用溶胶-凝胶法制备了TiO2-Al2O3复合载体,采用浸渍法制备了Ni2P/TiO2-Al2O3催化剂,并用X射线衍射(XRD)、N2吸附比表面积(BET)测定、热重-差热分析(TG-DTA)、X射线光电子能谱(XPS)等技术对催化剂的结构和性质进行了表征.催化剂加氢脱硫(HDS)和脱氮(HDN)活性评价在实验室固定床连续反应装置上,以噻吩和吡啶为模型反应物进行.考察了不同载体、Ni2P负载量、标称Ni/P摩尔比、催化剂焙烧温度对Ni2P/TiO2-Al2O3催化剂上同时进行的噻吩加氢脱硫和吡啶加氢脱氮性能的影响.结果表明,TiO2含量为80%(w)的TiO2-Al2O3复合氧化物为载体,Ni2P负载量为30.0%(w),标称Ni/P摩尔比为1/2,催化剂焙烧温度为500℃时,Ni2P/TiO2-Al2O3催化剂加氢脱硫脱氮活性最高.在360℃,3.0MPa,氢油比800(V/V),液时体积空速1.5h-1的条件下,噻吩HDS和吡啶HDN转化率分别为61.32%和64.43%.     

TiO2柱撑海泡石负载Ni2P的噻吩加氢脱硫性能

以氢氧化镍为镍源, 亚磷酸为磷源, TiO₂柱撑海泡石(Ti-Sep)为载体, 采用浸渍法制备了含磷化镍前驱体的样品, 然后采用程序升温还原法制备了Ni质量分数(w)为5%-25%的Ni₂P/Ti-Sep催化剂, 并考察了其噻吩加氢脱硫性能. 采用X射线衍射(XRD)、N₂吸附-脱附、热重分析(TGA)、透射电子显微镜(TEM)和傅里叶变换红外(FTIR)光谱对催化剂样品进行了表征. 结果表明, 海泡石经TiO₂柱撑之后层间距增大, 比表面积和孔容都明显变大, 热稳定性增强, 活性组分Ni₂P能很好地分散在海泡石层间及表面, 并且没有破坏海泡石的层状结构. 上述原因导致Ni₂P/Ti-Sep催化剂的噻吩加氢脱硫活性明显优于Ni₂P/Na-Sep(NaCl改性海泡石)和Ni₂P/HCl-Sep(HCl改性海泡石)催化剂. 当Ni负载量为15% (w)时, Ni₂P/Ti-Sep催化剂具有最好的噻吩加氢脱硫性能; 在反应温度为400℃时, 噻吩转化率达100%.     

Preparation of MnCo/MCM-41 catalysts with high performance for chlorobenzene combustion

MCM-41 was synthesized by a soft template technique. The specific surface area and pore volume of the MCM-41 were 805.9 m²/g and 0.795 cm³/g, respectively. MCM-41-supported manganese and cobalt oxide catalysts were prepared by an impregnation method. The energy dispersive X-ray spectroscopy clearly confirmed the existence of Mn, Co, and O, which indicated the successful loading of the active components on the surface of MCM-41. The structure and function of the catalysts were changed by modulating the molar ratio of manganese to cobalt. The 10%MnCo(6:1)/MCM-41 (Mn/Co molar ratio is 6:1) catalyst displayed the best catalytic activity according to the activity evaluation experiments, and chlorobenzene (1000 ppm) was totally decomposed at 270 °C. The high activity correlated with a high dispersion of the oxides and was attributed to the exposure of more active sites, which was demonstrated by X-ray diffraction and high-resolution transmission electron microscopy. The strong interactions between MnO₂, Co₃O₄, MnCoO_x, and MCM-41 indicated that cobalt promoted the redox cycles of the manganese system. The bimetal-oxide-based catalyst showed better catalytic activity than that of the single metal oxide catalysts, which was further confirmed by H₂ temperature-programmed reduction. Chlorobenzene temperature-programmed desorption results showed that 10%MnCo(6:1)/MCM-41 had higher adsorption strength for chlorobenzene than that of single metal catalysts. And stronger adsorption was beneficial for combustion of chlorobenzene. Furthermore, 10%MnCo(6:1)/MCM-41 was not deactivated during a continuous reaction for 1000 h at 260 °C and displayed good resistance to water and benzene, which indicated that the catalyst could be used in a wide range of applications.     

Preparation,characterization and hydrodesulfurization performances of Co-Ni_2P/SBA-15 catalysts

A series of Co-Ni2P/SBA-15 catalysts with various Co contents, Ni2P contents and P/Ni molar ratios were prepared by impregnating nickel nitrate, diammonium hydrogen phosphate, and then cobalt nitrate into SBA-15 support followed by temperature-programmed reduction in a H2 flow. The catalyst structure was characterized by X-ray diffraction(XRD), high resolution-transmission electron microscopy(HR-TEM)and N2adsorption-desorption techniques and their catalytic performance of the hydrodesulfurization(HDS) of dibenzothiophene(DBT) was evaluated. The effects of Co contents, Ni2 P contents and P/Ni molar ratios on the catalyst structure and HDS of DBT over the Co-Ni2P/SBA-15 catalyst were investigated. The results indicated that the mesoporous structure was mainly maintained and the nickel phosphides were well dispersed in all of the characterized catalysts. The 4Co-25Ni2P/SBA-15(P/Ni = 0.8) catalyst with the Co and Ni2 P contents of 4 wt% and25 wt%, respectively, and the P/Ni molar ratio of 0.8 showed the highest catalytic performance for HDS of DBT. Under the reaction conditions of 380?C and 3.0 MPa, the DBT conversion can reach 99.62%. The HDS of DBT proceeded mainly via the direct desulfurization(DDS)pathway with biphenyl(BP) as the dominant product on all of the catalysts and the BP selectivity was slightly enhanced after the introduction of Co promoters.     

磷化镍/介孔TiO_2催化剂的制备及其催化加氢脱硫性能

以介孔TiO2(m-TiO2)为载体,采用程序升温还原法制备了Ni2P/m-TiO2催化剂,考察了不同起始Ni/P摩尔比及活性组分负载量对该催化剂结构及其催化加氢脱硫(HDS)性能的影响.结果表明,当Ni/P摩尔比为1.25时,活性组分以Ni2P为主,催化剂的最佳Ni负载量为10%.采用X射线衍射、低温N2吸附-脱附、场发射扫描电镜和程序升温还原等技术表征了m-TiO2及其它不同载体负载的Ni2P催化剂.结果表明,高结晶度m-TiO2载体使Ni和P物种的还原温度大幅度降低,在450～600oC还原制得的Ni2P/m-TiO2催化剂的结构参数基本一致,比表面积均为90m2/g左右,具有很高的热稳定性和对二苯并噻吩的HDS催化性能.在相同的反应条件下,m-TiO2负载的Ni2P催化剂HDS性能最好,各载体负载的Ni2P催化剂活性大小顺序为Ni2P/m-TiO2Ni2P/SiO2Ni2P/P25.     

Al-Ni2P/SBA-15催化剂的制备、表征及加氢脱硫催化性能

以磷酸氢二铵为磷源,硝酸镍为镍源,硝酸铝为助剂铝源,制备了n_P/n_Ni=0.8,Al含量为1.06wt%~6.35wt%的一系列Al-Ni₂P/SBA-15催化剂。采用XRD、TEM和N₂吸脱附等技术对催化剂的结构进行了表征研究,以二苯并噻吩(DBT)作为模型化合物,在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价。结果表明,Al修饰的Al-Ni₂P/SBA-15催化剂仍然保持介孔结构,当Al含量低于5.29wt%时,催化剂的物相主要是Ni₂P,当Al含量在5.29wt%-6.35wt%之间时,催化剂的物相为Ni₂P和Ni₁₂P₅。Al含量为4.24wt%的3-Al-Ni₂P/SBA-15催化剂具有最好的二苯并噻吩加氢脱硫催化活性,在反应温度为360 ℃,反应压力为3.0 MP的条件下,3-Al-Ni₂P/SBA-15催化剂对二苯并噻吩的转化率可达99.0%。     

Synthesis of an Ni<Subscript>2</Subscript>P catalyst supported on Na-MCM-41 with highly activity for dibenzothiophene HDS under mild conditions

A novel and simple method to synthesize supported Ni₂P/Na(x)-MCM-41 catalysts (where x is the mass fraction of Na-to-MCM-41 in terms of percentage) at a lower reduction temperature by incorporation of Na was described. The catalysts were characterized by H₂ temperature-programmed reduction (H₂-TPR), X-ray diffraction (XRD), N₂ adsorption–desorption, CO uptake, X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). The effect of Na on the structure of catalysts and catalytic properties for the dibenzothiophene (DBT) hydrodesulfurization (HDS) was investigated, which confirmed that a suitable amount of Na can promote highly dispersed Ni₂P particles. The Na preferentially interacts with phosphate to generate the sodium phosphate and therefore suppresses the formation of stronger P–O–P bonds, which enables the phosphide catalyst to be easily formed at a lower reduction temperature. Compared with conventional phosphate (973–1273 K), the reduction temperature of Ni₂P/Na(x)-MCM-41 catalyst was relatively low (773 K). The Ni₂P/Na(x)-MCM-41 catalyst with x?=?1.0 showed the maximum DBT conversion of 91.6%, which is higher than that of Ni₂P/M41 without Na (80.3%).     

柠檬酸络合法制备Ni2P/SBA-15催化剂及加氢脱硫性能

以介孔分子筛SBA-15为载体,Ni组分采用柠檬酸(CA)配合法,制备了Ni2P质量含量为25%～45%、P/Ni为0.8、CA/Ni为0～1.5的一系列CA-Ni2P/SBA-15催化剂.利用XRD和N2吸脱附表征了催化剂结构,以二苯并噻吩(DBT)为模型硫合物,对催化剂加氢脱硫(HDS)性能进行了评价,考察了CA/Ni比对催化剂结构和反应性能的影响.结果表明,催化剂仍然保持有介孔结构,催化活性物相为Ni2P.反应温度为300～340℃时,Ni2P含量和CA/Ni比都对催化剂的性能有一定的影响,反应温度在360℃以上时,Ni2P含量和CA/Ni比对催化剂性能的影响不明显.Ni2P含量为35%、CA/Ni比为1.0的催化剂具有最好的HDS活性,DBT的转化率可达98%.