Effect of CeO2 on the catalytic performance of Ni/Al2O3 for autothermal reforming of methane

The effect of promoter Ce on the catalytic performance of Ni/Al2O3 catalyst for autothermal reforming of methane to hydrogen was investigated. The catalysts were characterized by X-ray diffraction （XRD）, temperature-programmed reduction （TPR）, and X-ray photoelectron spectroscopy （XPS）. The results indicated that the catalytic performance of the catalysts was improved with the addition of Ce. Ni/Ce30Al70Oδ showed the highest CH4 conversion in operation temperatures ranging from 650 ℃ to 850 ℃. At the same time, the decrease in H2/CO ratio with increasing reaction temperature was consistent with the fact that water-gas shift reaction was thermodynamically unfavorable at higher temperatures. The XRD result indicated that adding Ce to Ni/Al2O3 catalyst prevented the formation of NiAl2O4 and facilitated the formation of NiO. The formation of NiO increased the number of active sites, resulting in higher activity. Comparing the TPR profiles of Ni/Ce30Al70Oδ with Ni/Al2O3, it could be clearly observed that with the addition of Ce, the total reduction peak areas in the middle and low temperatures increased. It was most probably that the addition of Ce inhibited the stronger interaction between Ni and Al2O3 to form the phase of NiAl2O4, and favored the formation of the strong interaction between NiO species and CeO2. Therefore, the addition of Ce to the Ni/Al2O3 catalyst increased the active surface that promoted the activity of the catalyst.     

机械化学法制备的Al/Ce复合氧化物负载NiMo催化剂的加氢脱硫活性(英文)

将Al和/或Ce的硝酸盐与NH_4HCO_3球磨混合,采用机械化学法制备了Al_2O_3-CeO_2载体(其中Ce含量为1-10 wt%),再以杂多钼酸盐(NH_4)_4NiMo_6O_(24)为活性金属Ni和Mo的前驱体,通过浸渍法制备NiMo_6/Al_2O_3-CeO_2催化剂,并将其用于1-苯并噻吩(BT)的加氢脱硫(HDS)反应中.运用化学分析、X射线衍射、N_2吸附-脱附法、H_2程序升温还原、NH_3程序升温脱附和X射线光电子能谱对催化剂的物化性质进行了表征.结果表明,催化剂的酸性随着载体中Ce含量的增加而下降.Ce修饰的Al_2O_3载体表面的NiS/MoS原子比下降了2倍.NiMo_6/Al_2O_3催化剂表现出最高的HDS活性(以单位重量催化剂计),其酸性和表面MoO_xS_y物种的浓度(Mo~(5+)浓度)也最高;当催化剂中Ce含量逐渐增加到10 wt%以上时,其活性逐渐将为0.与浸渍法制得的参比催化剂相比,前驱体和催化剂组成相同的情况下,采用机械化学法制得的所有催化剂活性明显提高.     

Pd-Ce-B/水滑石催化液相苯酚选择性加氢制环己酮

以Al3 /(Al3 Mg2 )摩尔比为0.2的水滑石(HT)为载体,采用还原浸渍法制备了负载型Pd-Ce-B/HT催化剂,并将其应用于液相苯酚选择性加氢制环己酮.与Pd-Ce-B/Al2O3,Pd-Ce-B/MgO和Pd-Ce-B/SiO2相比,Pd-Ce-B/HT催化剂具有高活性和高环己酮选择性.5.8%Pd-Ce-B/HT上苯酚的转化率和环己酮的选择性分别达82.0%和80.3%,显示了其潜在的工业化应用前景.根据多种表征结果,初步讨论了催化剂的构效关系以及添加剂Ce3 和载体酸碱性对催化性能的促进作用.     

V2O5-CeO2/TiO2催化剂上低温氨选择性催化还原NO的性能

考察了V2O5-CeO2/TiO2催化剂中V、Ce活性组分的担载量和焙烧温度对催化剂低温催化还原NO活性的影响及其在单独SO2、H2O和两者共存气氛下的抗毒化性能。结果表明,焙烧温度400℃下制备的5V30Ce/TiO2催化剂具有良好的低温催化还原NO活性,空速为10000h-1,165℃时NO转化率达99.2%;500℃以下低焙烧温度时,添加的Ce不与V相互作用,在催化剂表面主要以CeO2形式存在,有利于增大催化剂比表面积,增强V2O5在催化剂上的分散度,提高催化活性。而在500℃以上较高焙烧温度下,Ce与V会形成CeVO4,对活性提高不利。催化剂具有良好的低温抗水中毒性能,但受SO2毒化作用明显,其在SO2、H2O共存气氛下中毒程度较单独SO2下浅。     

MnOx/Al2O3/Ce0.45Zr0.45M0.10Oy （M = Mn, Y, La） catalysts used for ethanol catalytic combustion

MnOx/Al2O3/Ce0.45Zr0.45M0.10Oy (M = Mn,Y,La) catalysts were prepared by impregnation method and characterized by BET,TPR and XRD analyses.The catalytic activities toward ethanol combustion were investigated in a microreactor.The results demonstrated that the catalytic activity of MnOx/Al2O3/Ce0.50Zr0.50O2 monolithic catalyst could be improved by doping Mn,Y and La into Ce0.50Zr0.50O2.When doping Y into Ce0.50Zr0.50O2,the catalyst MnOx/Al2O3/Ce0.45Zr0.45Y0.10O1.95 showed the highest activity.The 100% conversion temperature of ethanol was 230 ℃.Furthermore,once the conversion of ethanol started,the complete conversion was quickly achieved.The doping of Mn,Y and La led to better activity for ethanol combustion and lower temperature reduction peaks in TPR profiles.The doping of Mn resulted in enhanced oxygen storage capacity (OSC),larger area of the reduction peaks,and excellent reactivity,and the doping of Y resulted in the lowest reduction temperature and the best activity.     

EFFECTS OF ALKALI AND RARE EATTH METAL OXIDES ON THE THERMAL STABILITY AND THE CARBON DEPOSITION OVER A NiO/Al_2O_3 CATALYST

采用固定床流动反应装置、ＣＯ吸附、ＴＧ、ＴＰＯ、ＸＰＳ和ＸＲＤ等手段考察了ＮｉＯ／Ａｌ２Ｏ３和ＬｉＮｉＬａＯ／Ａｌ２Ｏ３催化剂上的甲烷部分氧化反应。实验结果表明，ＬｉＮｉＬａＯ／Ａｌ２Ｏ３对甲烷部分氧化反应具有较高的反应活性。锂和镧的添加不仅改善了活性组分镍的分散度，而且提高了ＮｉＯ／Ａｌ２Ｏ３的抗积碳能力和热稳定性     

Complete Oxidation of Methane Alumina Modified with Calcium, over Palladium Supported on Lanthanum, and Cerium Ions

The activity and thermal stability of Pd/Al2O3 and Pd/（Al2O3＋MOx） （M=Ca, La, Ce） palladium catalysts in the reaction of complete oxidation of methane are presented in this study. The catalyst supports were prepared by sol-gel method and they were dried either conventionally or with supercritical carbon dioxide. Then they were impregnated with palladium nitrate solution. The catalysts with unmodified alumina had a high surface area. The activity and thermal stability of the aluminasupported catalyst was also very high. The introduction of calcium, lanthanum, or cerium oxide into alumina support caused a decrease of the surface area in the way dependent on the support precursor drying method. These modifiers decreased the activity of palladium catalysts, and they required higher temperatures for the complete oxidation of methane than unmodified Pd/Al2O3. The improvement of the palladium activity by lanthanum and cerium support modifier was observed only at low temperatures of the reaction.     

高效 CeO2-MnOx-Al2O3催化剂的制备、表征及催化消除 NO性能

机动车在给人类生活带来便利的同时,也造成了严重的大气污染.其尾气净化成为人们关注的焦点.一氧化氮(NO)、一氧化碳(CO)和碳氢化合物(HCs)是机动车尾气中的三大典型污染物,主要通过三效催化(TWC)技术进行脱除. TWC技术涉及几个重要的催化反应,其中 CO催化还原 NO由于能够同时消除 CO和 NO两种污染物而引起研究者的极大关注.研究表明,负载型贵金属催化剂在该反应中显示出优异的催化性能,但存在资源匮乏、价格昂贵以及热稳定性欠佳等不足.因此,低价、高效的过渡金属氧化物催化剂成为近年研究重点.稀土金属氧化物 CeO2由于具有良好的氧化还原性能、较高的储释氧容量以及丰富的表面氧空位而被广泛用于 CO催化还原 NO反应.研究表明,对 CeO2进行离子掺杂可进一步增大其比表面积,改善其氧化还原性能和储释氧容量.并且,我们在先前的研究中还发现,将具有多种可变价态的钛离子或锡离子掺入 CeO2晶格由于掺杂离子能与 Ce4+/Ce3+发生电子转移而更有利于改善 CeO2的理化性质.此外,锰氧化物(MnOx)在氧化还原气氛中容易实现不同价态之间的切换,从而在一些重要的氧化还原反应中表现出优异的催化性能.近年来,有研究者将 CeO2与 MnOx相结合制备了 CeO2-MnOx催化剂用于 NO消除、碳烟燃烧和挥发性有机物(VOCs)氧化等反应,并取得一些有意义的结果.然而,对于实际应用来说, CeO2-MnOx催化剂存在比表面积偏小等不足.众所周知,γ-Al2O3是一种常用的具有高比表面积和高热稳定性的催化剂载体材料,可有效增大催化剂比表面积.我们前期研究结果表明,通过共沉淀法将 Al3+掺入铈基复合氧化物的晶格相比于以γ-Al2O3为载体更有利于改善铈基复合氧化物的理化性质和催化性能.因此,我们通过简单的氨水反滴加共沉淀法制备了一系列 CeO2-MnOx-Al2O3(Ce：Mn：Al摩尔比=6：4：x,x =0.25,0.5,1,2)复合氧化物催化剂用于 CO催化还原 NO反应.并运用 X射线衍射、拉曼光谱、氮气物理吸附、氢气程序升温还原、X射线光电子能谱以及原位漫反射红外光谱等表征技术对上述催化剂进行了系统分析.重点考察了 Al3+掺杂量对 CeO2-MnOx-Al2O3复合氧化物催化剂理化性质和催化性能的影响.结果表明,在 CeO2-MnOx复合氧化物中掺入少量 Al3+会导致其晶粒尺寸减小,从而增大其比表面积和孔体积,并增加 Ce3+和 Mn4+的含量.比表面积和孔体积增大有助于催化剂与反应物分子之间充分接触; Ce3+和 Mn4+含量增加能分别促进 CO物种吸附以及吸附态 NO物种脱附、转化和解离.这些变化有利于提高 CeO2-MnOx复合氧化物在 CO催化还原 NO反应中的催化性能.最后,基于催化剂的理化性质表征及其催化性能评价,我们尝试提出了一个可能的催化反应机理,以进一步理解 CeO2-MnOx-Al2O3复合氧化物催化剂在 CO催化还原 NO反应中的优异性能.     

Effect of Transition Metals (Cu, Co and Fe) on the Autothermal Reforming of Methane over Ni/Ce0.2Zr0.1Al0.7Oδ Catalyst

The transition metals (Cu, Co, and Fe) were applied to modify Ni/Ce0.2Zr0.1Al0.7Oδ catalyst.The effects of transition metals on the catalytic properties of Ni/Ce0.2Zr0.1Al0.7Oδ autothermal reforming of methane were investigated. The Ni-supported catalysts were characterized by XRD, TPR and XPS.Tests in autothermal reforming of methane to hydrogen showed that the addition of transition metals (Cu and Co) significantly increased the activity of catalyst under the conditions of lower reaction temperature,and Ni/Cu0.05Ce0.2Zr0.1Al0.65Oδ was found to have the highest conversion of CH4 among all catalysts in the operation temperatures ranging from 923 K to 1023 K. TPR, XRD and XPS measurements indicated that the cubic phases of CexZr1-xO2 solid solution were formed in the preparation process of catalysts.Strong interaction was found to exist between NiO and CexZr1-xO2 solid solution. The addition of Cu improved the dispersion of NiO, inhibited the formation of NiAl2O4, and thus significantly promoted the activity of the catalyst Ni/Cu0.05Ce0.2Zr0.1Al0.65Oδ.     

铈镁铝混合氧化物催化剂的脱NOx性能

 用共沉淀法制得Mg-Al水滑石和二氧化铈的混合物,经750 ℃热活化,得到铈镁铝混合氧化物催化剂. 考察了催化剂的组成、反应温度、反应体系中氧含量、水蒸气及二氧化硫的存在对NO和CO反应活性的影响. 结果表明,铈镁铝混合氧化物催化剂具有较高的脱NOx活性,并具有优异的水热稳定性和一定的抗氧性及抗二氧化硫毒化的能力.     

Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟

以CexZr1-xO2固溶体做载体,制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂(x=1,0.75,0.5,0.25,0).应用Brunauer-Emmet-Teller(BET)比表面积分析、X射线衍射(XRD)和H2程序升温还原(H2-TPR)等手段对催化剂进行相关表征,并系统研究了催化剂在饮食油烟催化燃烧中的催化活性.BET结果表叫催化剂的比表面积随Ce/Zr摩尔比的减小而减小.XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上.H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好.催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧,降低了反应温度.随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化,催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2＞Pt/γ-Al2O3/Ce0.25Zr0.75O2＞Pt/γ-Al2O3/Ce0.75Zr0.25O2＞Pt/γ-Al2O3/CeO2＞Pt/γ-Al2O3/ZrO2.     

表面Mo修饰提高CeTiO_x催化剂低温脱硝性能（英文）

近年来,以雾霾为代表的大气污染问题严重影响到经济社会的可持续发展.其中,氮氧化物(NOx)的大量排放是导致雾霾天气的重要原因之一.氨选择性催化还原(NH3-SCR)是目前消除氮氧化物的主流技术,低温NH3-SCR更是广泛应用于钢铁、焦化、水泥、玻璃、陶瓷和垃圾焚烧等行业的烟气排放治理.传统的V2O5-WO3/Ti O2催化剂活性温度高(300–400 oC)且钒具有生物毒性,因此亟待开发环境友好的低温非钒基脱硝催化剂.最近, Ce Ti Ox基催化剂由于在中高温段(250–400 oC)表现出优异的脱硝性能而得到广泛关注.然而,该催化剂仍面临低温活性差及抗硫性能差的问题,制约了其工业化应用.研究显示,添加过渡金属可提高Ce Ti Ox基催化剂的脱硝活性和抗硫中毒性能,这主要是因为过渡金属的添加可以有效改善催化剂的氧化还原性能和表面酸性.Mo O3作为一种可以提供大量酸性位的氧化物,常被用作助剂改善钒钨钛催化剂的活性.研究显示, Mo O3的引入可以促进催化剂中钒物种的分散度以及提高表面酸性.基于此,我们制备了一系列不同Mo含量的Mo O3/Ce Ti Ox催化剂,以期提高Ce Ti Ox催化剂的低温脱硝性能及抗SO2中毒能力,并着重研究表面Mo的修饰对Ce Ti Ox催化剂物理化学性质的影响.研究发现,表面Mo修饰可以显著提高Ce Ti Ox的低温催化活性,其脱硝效率在150 oC即可达到80%,同时抗SO2中毒能力也得到增强.进一步借助X射线衍射、比表面积测定、氢气程序升温还原、氨气程序升温脱附和X射线光电子能谱等方法对催化剂进行了全面表征分析.结果显示,表面Mo修饰对Ce Ti Ox催化剂物理化学性质的影响与其脱硝性能有着密不可分的关系.首先,钼物种主要是以Mo O3的形式存在于Ce Ti Ox表面,其最佳的负载量为4wt.%.其次,表面Mo的沉积显著提高了催化剂的表面酸量,尤其是Br?nsted酸位的数量,而表面酸位的增加有利于催化剂吸附与活化反应物种NH3;同时,表面Mo修饰还减弱了硝酸盐在催化剂表面的吸附,进一步促使NH3-SCR反应按照Eley-Rideal机理顺利进行.最后,该催化剂在H2O和SO2存在的条件下仍具有最佳的脱硝性能,因而有望用于实际含SO2的低温烟气脱硝.     

三氧化二铝含量对Ni／Zr0.4Ce0.6O2—Al2O3催化剂的CH4—CO2重整反应性能影响

采用水热合成法,制备了不同Al2O3含量的Ni/Zr0.4Ce0.6O2-Al2O3催化剂,采用X－射线衍射（XRD）和扩展X光吸收精细结构（EXAFS）,对催化剂样品进行结构表征;考察了Al2O3的加入对催化剂结构和CH4－CO2重整反应活性的影响。结构表征和活性测试表明,催化剂中存在的主要晶相是Zr0.4Ce0.6O2.Al2O3的加入,使催化剂颗粒度变小,镍的分散度提高,并使反应活性有明显改进;而过量Al2O3的加入,却容易导致积炭。     

掺杂助剂Ce和Zr的Ni/Al2O3催化剂的X光电子能谱分析

以Na2CO3为沉淀剂,在pH 9.0的沉淀条件下,采用并流沉淀法制备了Ni/Al2O3、Ni/CeO2-Al2O3、Ni/ZrO2-Al2O3和Ni/ZrO2-CeO2-Al2O34种催化剂,催化剂中Ni负载量(质量分数)为10%。采用XPS表征手段及常压固定床反应器对催化剂进行活性评价,考察了助剂Ce和Zr及二者的协同作用对Ni基催化剂表面物种结合能的影响以及对甲烷自热重整制氢反应性能的影响。结果表明,助剂Ce和Zr的添加及二者的协同作用对Ni基催化剂表面各物种的结合能均有一定的影响,结合评价结果可知,Ce和Zr二者的协同作用对Ni基催化剂的催化性能提高最大。     

添加钒对Pd/Al2O3-TiO2 催化剂上醇醛催化氧化性能及表面特性的影响

采用浸渍法分别制备了Pd/Al₂O₃-TiO₂、V/Al₂O₃-TiO₂和不同钒含量的V-Pd/Al₂O₃-TiO₂催化剂,并对乙醇、乙醛的完全催化氧化性能进行了测试。结果表明,添加适量的钒组分(1%~3%)能够有效地提高催化剂的深度氧化活性。采用XRD、NH₃-TPD、N₂吸附等技术分析研究催化剂的表面特性与催化活性之间的关系,发现Pd/Al₂O₃-TiO₂催化剂添加适量钒组分后,调变了催化剂的表面酸性、比表面积和孔容,使得V组分和Pd组分与载体之间产生较强的相互作用,双金属组分的协同效应提高了催化剂对乙醇、乙醛的深度氧化活性。     

KF/Al2O3催化合成2-甲基-3-(3,4-亚甲二氧基苯基)丙烯醛

缩合;催化剂;洋茉莉醛;KF/Al2O3催化合成2-甲基-3-(3;4-亚甲二氧基苯基)丙烯醛     

氨法选择性还原氮氧化物 V2O5/TiO2-PILC催化剂的抗硫性能

选择性催化还原(SCR)是目前去除氮氧化物最有效的方法之一. V2O5/TiO2催化剂被广泛应用于氨法选择性还原氮氧化物(NH3-SCR)反应,但该催化剂存在工作温度高(300–400oC)及 SO2氧化率高引起设备腐蚀和管路堵塞等问题,开发低温 SCR催化剂具有重要意义.过渡金属氧化物(如 Fe2O3, MnOx和 CuO等)催化剂用于低温SCR先后见诸文献报道,但这些催化剂在 SO2和 H2O存在下易失活.近年来柱撑黏土(PILC)引起科学家广泛关注, Yang等首次将 V2O5/TiO2-PILC催化剂应用于 NH3-SCR反应,发现其催化活性高于传统 V2O5/TiO2催化剂.柱撑黏土基催化剂在 NH3-SCR反应中也显示出良好抗硫性能,但 V2O5/TiO2-PILC催化剂的抗硫机理至今尚未见深入研究.因此我们制备了一系列 V2O5/TiO2-PILC催化剂,采用原位漫反射红外等方法详细研究了其抗硫性能较好的原因.
　　首先采用离子交换法制备出 TiO2-PILC载体,之后采用浸渍法制备了不同钒含量(质量分数x/%=0,3,4,5)的xV2O5/TiO2-PILC催化剂.同时,制备了传统 V2O5/TiO2和 V2O5-MoO3/TiO2催化剂作为对比.活性评价结果显示,4V/TiO2-PILC催化剂具有最高的催化活性,其催化性能与传统钒钛催化剂相当.在160oC时, NO转化率可达80%以上.同时,4V/TiO2-PILC催化剂还具有较宽的反应温度窗口,在260–500oC范围内, NO转化率保持在90%以上.向反应体系中加入0.05% SO2和10% H2O后,在低温(160oC以下)时所有催化剂的反应活性都有一定提高,可能是由于 SO2的加入提高了催化剂的表面酸性.继续升高温度,4V/TiO2和4V6Mo/TiO2催化剂活性均明显下降,而4V/TiO2-PILC催化剂的活性则未出现明显下降.原位漫反射红外光谱结果显示, SO2在三种催化剂表面的吸附以表面硫酸盐或亚硫酸盐物种以及离子态 SO42–物种形式存在,而在4V/TiO2-PILC催化剂表面离子态 SO42–物种的量最少. X射线光电子能谱及 O2程序升温脱附结果显示,在4V/TiO2-PILC催化剂上,表面吸附氧(Oads)的量最少.综合上述分析可以得出,在 SO2气氛下,离子态 SO42–物种在 SCR催化剂表面的累积可能是导致其失活的主要原因,而离子态 SO42–物种的形成可能与催化剂表面吸附氧的量有关.     

CeO2和Pd在Ni/γ-Al2O3催化剂中的助剂作用

采用脉冲微反技术研究了添加n型半导体氧化物CeO2及贵金属Pd对Ni/γ Al2O3催化剂上CH4积炭/CO2消炭反应性能的影响,并运用BET、TPR、CO2 TPSR及氢吸附等技术对催化剂进行了表征.结果表明, n型半导体氧化物CeO2的添加可以降低Ni/γ Al2O3催化剂上CH4裂解积炭活性,提高CO2消炭活性,添加少量贵金属Pd可以进一步改变载体Al2O3、助剂CeO2和活性组分Ni之间的相互作用,从而改善Ni/γ Al2O3催化剂的抗积炭性能.通过Ni Ce Pd/γ Al2O3催化剂上CH4积炭/CO2消炭模型对上述作用机制作出了新的解释.     

K改性的Pt/Al2O3催化剂上CO氧化反应：反应动力学和红外光谱研究

CO氧化不仅具有重要的实用价值,而且在基础研究中被用于考察反应机理及催化剂结构敏感性等一些重要问题,因此,该反应在催化领域中具有重要意义. Pt基催化剂被广泛应用于CO氧化反应.其催化活性取决于催化剂的制备方法.其中,碱金属如Na、K等助剂的添加可有效促进催化活性,红外光谱证据表明,其促进作用在于碱金属的添加可降低CO与表面Pt原子的相互作用.尽管如此,催化剂上反应动力学证据却十分缺乏.反应动力学的研究可以提供一些本证反应信息如反应基元步骤、反应速率表达式以及反应机理等.通过对比不同催化剂之间的反应动力学行为,可以进一步解释碱金属对催化剂结构以及反应行为的影响.因此在本工作中,我们制备了一系列以K为助剂的Pt/Al2O3催化剂,并进行了CO氧化的反应动力学研究,考察了助剂对CO反应级数和反应活化能的影响.结合原位红外光谱表征,进一步揭示了助剂在反应中的作用.通过对比不同Pt和K含量的催化剂上CO氧化反应活性,我们发现, K的添加能促进反应活性,且随着催化剂中K含量的增加,促进程度越明显.例如,0.42K-2Pt/Al2O3上T50温度比对应的2Pt/Al2O3降低了30oC.不同催化剂上CO氧化的反应动力学实验表明,反应速率随着CO的分压的增加而降低;但随着O2分压的增加而增大.幂函数反应速率表达式推导得到的反应级数发现,对于含K的催化剂其CO的反应级数(约为–0.2)明显比不含K的催化剂(约为–0.5)中高,说明K的添加减弱了CO与表面Pt原子之间的吸附能力.但对O2的反应级数影响较小.例如：在0.42K-2.0Pt/Al2O3上反应速率表达式为r =6.55′10–7pco–0.22po20.63;而在2.0Pt/Al2O3上为r =2.56′10–7pco–0.53po20.70.表观反应活化能的计算表明,含K的催化剂上表观反应活化能较低,进一步说明K的添加有利于反应进行.根据反应速率表达式,我们进行了基元步骤的推导,并计算了反应动力学参数.结果发现,与不含K的催化剂相比,含K的催化剂中本征反应速率常数明显增加,而CO吸附平衡常数降低了一半,表明K的存在使CO在Pt表面上的覆盖度降低.我们还通过原位红外光谱对比了催化剂上CO吸附行为的差异.数据表明,与不含K的催化剂相比, K的添加一方面降低了CO在催化剂表面的吸附量(峰面积变小);另一方面显著降低了CO在Pt表面上的脱附温度,说明两者之间的相互作用力减弱.综上所述,通过反应动力学和红外光谱实验,我们认为K助剂与表面Pt原子相互作用后生成了较为稳定的Pt–O–K物种.尽管该物种的具体结构目前还不明确,但我们的实验证据表明,该物种的存在可以有效减弱CO与表面Pt原子之间的相互作用,降低CO的表面覆盖度并有利于O2在Pt表面的竞争吸附,从而降低了表面吸附的CO与O2之间反应的能垒,促进了反应性能.     

甲烷部分氧化制合成气反应Pt/Al_2O_3和Pt/CeO2/Al_2O_3催化剂的研究(英文)

研究了Ｐｔ／Ａｌ２Ｏ３和Ｐｔ／ＣｅＯ２／Ａｌ２Ｏ３催化剂对甲烷部分氧化制合成气反应的催化活性，发现Ｐｔ／ＣｅＯ２／Ａｌ２Ｏ３显示了比Ｐｔ／Ａｌ２Ｏ３更高的甲烷转化率和合成气选择性。用Ｈ２ＴＰＲ，Ｈ２ＴＰＤ，ＳＥＭ和ＸＲＤ等手段和技术对催化剂进行了表征。ＣｅＯ２与Ｐｔ之间存在较强的相互作用（ＳＭＳＩ），这种作用促进了Ｐｔ在催化剂表面的分散，抑制了Ｐｔ在催化剂表面的迁移，大大降低了催化剂在反应中的完全燃烧活性，提高了催化剂的部分氧化活性和选择性，避免了因催化剂床层局部温度过高而导致催化剂活性下降或失活，提高了催化剂的稳定性。同时，在反应过程中，ＣｅＯ２通过促进水蒸气变换反应（ＷＧＳＲ）的进行使反应体系迅速达到平衡，提高了催化剂对Ｈ２的选择性。