焙烧及还原温度对 Co-Pt-ZrO2/γ-Al2O3催化剂费托合成反应性能的影响

采用浸渍法制备了Co-Pt-ZrO₂/γ-Al₂O₃催化剂,对其进行了BET、XRD和TPR等表征,并在浆态床反应器上考察了焙烧温度和还原温度对催化剂费托合成反应性能的影响。结果表明,焙烧温度过高,容易造成Co物种和载体间的相互作用增强,使部分氧化钴颗粒聚集或烧结,导致催化剂的F-T合成反应活性和C₅₊烃选择性降低。还原温度较低时,钴物种不能充分还原,CO加氢活性低,甲烷选择性高,重质烃选择性低;还原温度过高,则可能造成活性物种的烧结,反而降低了催化剂的活性和重质烃选择性。在原料气n(H₂)/n(CO)=2.0、483 K、2.4 MPa和空速3.6 L/(gcat·h)的条件下,31.08%Co～0.11%Pt～7.16%ZrO₂/Al₂O₃催化剂在673 K焙烧。纯H₂下653 K还原后,其费托性能最佳;CO转化率为27.0%,C₅₊的选择性为83.0%。     

浆态床中Cu/ZnO/Al2O3/ZrO2+γ-Al2O3双功能催化剂一步法合成二甲醚

采用共沉淀法,制备了纤维状CD501甲醇合成催化剂,采用SEM、TEM、XRD和BET等手段对催化剂进行了表征;并将其进一步和γ-Al₂O₃进行混合,获得了Cu/ZnO/Al₂O₃/ZrO₂+γ-Al₂O₃双功能催化剂,考察了其在浆态床中一步法合成二甲醚过程的催化特性。结果表明,相比商业催化剂(COM)和LP201催化剂,新型的CD501催化剂具有更大的比表面积和Cu/Zn分散性。对于浆态床中一步法合成二甲醚过程,采用CD501与γ-Al₂O₃双功能催化剂,相比采用COM或LP201与γ-Al₂O₃双功能催化剂,CO转化率提高了一倍,且经过270h测试,CO转化率从61%降至57%,二甲醚时空产率从0.54g/(g·h)降至0.48g/(g·h),稳定性显著优于COM催化剂。当反应温度为250℃,压力为4.0MPa,空速为3000mL/(g·h),氢碳比为1.0时,该催化剂应用在浆态床一步法合成二甲醚时,CO转化率为61%,DME时空产率达到0.54g/(g·h)。     

Ru助剂对Co/SiO2催化剂费托合成反应性能的影响

 考察了 Ru 助剂 (0.17%?9.96%) 对 Co/SiO2 催化剂结构及其费托合成反应性能的影响. 结果表明, Ru 助剂可降低 Co/SiO2 催化剂的还原温度, 从而提高其还原度. 光电子能谱和扩展 X 吸收射线精细结构研究表明, 即使 Ru 含量高达 9.96%, 在 Co/SiO2 催化剂焙烧过程中也未观察到 Ru 物种与 Co 物种作用形成的化合物. 还原后催化剂中 Ru 趋向于与 Co 物种紧密接触且分散在催化剂表面. H2 程序升温脱附结果表明, 随着 Ru 含量的增加, 位于反应温度附近的 H2 脱附峰面积增加, 即此时催化剂吸附 H2 能力提高, 因此反应活性单调增加, 但存在最佳 Ru 含量, 此时 C5+选择性最高.     

ZrO2修饰Al2O3纳米片负载钴催化剂的制备及其费托反应性能研究

通过水热法合成了Al₂O₃纳米片（Al₂O₃-CN）,采用浸渍法制备20%（质量分数）钴基催化剂,并应用于费托合成反应。制备的Al₂O₃-CN（226 m²/g）与商业氧化铝（Al₂O₃-C,249 m²/g）具有相近的比表面积,但Al₂O₃-CN孔尺寸分布更加集中。浸渍钴后,与Co/Al₂O₃-C催化剂相比,Co/Al₂O₃-CN催化剂表现出较高的还原度及更均匀的钴颗粒粒径分布。因此,Co/Al₂O₃-CN催化剂表现出更高的CO转化率和低的甲烷选择性。为了进一步提高Co/Al₂O₃-CN的催化性能,采用不同含量ZrO₂对Al₂O₃-CN进行修饰。表征结果表明,随着ZrO₂修饰量的增加,Al₂O₃-CN载体比表面积变化不明显,孔体积和孔径增大;相对应催化剂的钴颗粒粒径减小,活性位点数目增加。在相同反应条件下,经ZrO₂修饰催化剂CO转化率进一步提高,甲烷选择性降低。     

Al2O3助剂对Co/SiC催化剂F-T反应性能的影响

分别采用沉淀法、尿素水解法制备Al₂O₃/SiC复合载体,采用等体积浸渍法制备Co/Al₂O₃-SiC催化剂。结合N₂吸附、XRD、H₂-TPR、XPS等表征手段,研究Al₂O₃助剂对钴基催化剂物相结构、还原行为以及F-T合成性能等的影响。结果表明,氧化铝加入后增强了载体与钴物种之间的相互作用,提高了钴物种的分散度,降低了钴物种的还原度。尿素水解法引入Al₂O₃后,载体与钴物种具有适中的相互作用,表现出较高的反应活性。沉淀法制备的载体负载钴物种后由于较强的金属-载体相互作用,表现出较优的稳定性。     

CoAl2O4/Al2O3载体对钴基费托催化剂反应性能影响的研究

通过浸渍和高温焙烧,制得表面附着CoAl₂O₄微晶颗粒的改性Al₂O₃载体,并采用等体积浸渍法制备负载型Co基催化剂。结合 N₂物理吸附、XRD、H₂-TPR、XPS及H₂化学吸附等表征手段,研究改性载体及其负载钴基催化剂的织构特征;采用费托合成反应评价其催化性能。结果表明,Al₂O₃改性后,表面CoAl₂O₄的存在有效减少了载体与活性组分Co的相互作用,显著提高了催化剂的还原度和催化活性。载体的改性量在20%左右达到最佳值,继续增加,催化剂还原度和活性基本不再升高。载体改性促使催化剂CH₄选择性有所降低,C₅₊选择性略有提高。     

锰助剂对F-T合成Co/Al2O3催化剂反应性能的影响

采用程序升温和原位红外技术对锰改性Co/Al2O3催化剂进行了表征，并与CO加氢反应活性和选择性进行关联.结果表明，添加适量锰能够增加反应活性，提高烃选择性，抑制甲烷及低碳烃的生成. XRD和FT IR结果表明锰助剂的添加能够促进活性相的分散，促进桥式CO吸附位数的增加. H2 TPD表明锰的加入可增加低温吸附氢量，但吸附氢量随锰含量的增加而减少.钴基催化剂的费托合成反应性能可以用锰添加导致的CO吸附态物种的变化来解释.     

微波辐射对浆态床合成甲醇CuO/ZnO/Al2O3催化剂前驱体晶相转变的影响

在微波辐射条件下,对CuO/ZnO/Al2O3催化剂的沉淀母液进行老化,通过XRD、TG、H2-TPR,FTIR、HR-TEM和XPS对前驱体及催化剂微观结构的进行表征,探讨了CuO/ZnO/Al2O3催化剂前驱体晶相转变过程中微波辐射的作用。结果表明,微波辐射有利于Cu2+取代Zn5(CO3)2(OH)6中Zn2+的同晶取代反应。微波辐射的老化过程中,首先发生Cu2+取代Zn5(CO3)2(OH)6中Zn2+生成(Cu,Zn)5(CO3)2(OH)6的同晶取代反应,并于1.0 h内基本完成;随着老化时间继续延长,主要进行Zn2+取代Cu2(CO3)(OH)2中Cu2+生成(Cu,Zn)2(CO3)(OH)2的同晶取代反应,同时(Cu,Zn)5(CO3)2(OH)6进一步结晶。与常规老化1 h制备的前驱体相比,微波辐射老化1.0 h制备的前驱体含有较多的(Cu,Zn)5(CO3)2(OH)6物相,有助于增强焙烧后CuO/ZnO/Al2O3催化剂中CuO-ZnO协同作用,提高表面铜含量,进而提高CuO/ZnO/Al2O3催化剂在浆态床合成甲醇的催化活性和稳定性,在400 h浆态床合成甲醇评价期间,甲醇时空收率最大达318.9 g.kg-1.h-1,失活率仅为0.11%.d-1。     

Mo 和 Cu 助剂对 FeK/SiO2 催化剂费托合成性能的影响

 研究了 Mo 和 Cu 助剂对 FeK/SiO₂ 催化剂的性质及费托 (F-T) 合成性能的影响. 采用 N₂ 物理吸附、H₂ 程序升温还原、X 射线衍射、穆斯堡尔谱和 X 射线光电子能谱技术对催化剂进行了表征. 结果表明, Mo 加入后与 Fe 产生了较强的相互作用, 抑制了催化剂的还原和碳化; Cu 助剂的加入促进了催化剂的还原和碳化; 当 Mo 和 Cu 共同加入后, 催化剂的还原和碳化行为与单独加入 Cu 助剂时相似. 催化剂 F-T 合成性能在固定床上于 280 ^oC, 1.5 MPa, 2 000 h^-1, H₂/CO = 2.0 的合成气中测试. 结果表明, Mo 的加入降低了催化剂活性, 但提高了重质烃 (C₅₊) 的选择性; Cu 的添加提高了催化剂的活性, 但对稳定 C₅₊选择性作用不明显. Mo 和 Cu 共同加入后, 催化剂既表现出较为稳定的 C₅₊选择性, 同时其活性也没有降低.     

费托合成铁基催化剂中Fe3O4含量对CO2选择性的影响

本研究以共沉淀法制备的α-Fe₂O₃催化剂为前驱体,通过调变碳化温度和碳化时间制备了不同物相组成的系列催化剂,采用XRD、M?ssbauer谱、XPS和Raman光谱等技术考察了催化剂体相和表面物相组成,在此基础上研究了不同条件下(不同CO转化率和H₂O分压)催化剂的物相组成与催化剂性能之间的关系,重点探究了费托合成条件下CO₂生成的活性相。结果表明,升高碳化温度和延长碳化时间有利于Fe₃O₄向碳化铁转变。在典型的费托合成条件下,催化剂的活性受到碳化铁含量和积炭程度的共同影响。当H₂O分压较低时,动力学因素限制了水煤气变换(WGS)反应的进行,CO₂选择性仅受CO转化率的影响,Fe₃O₄含量变化对CO₂选择性无明显影响;而在较高的H₂O分压下,随着催化剂中Fe₃O₄含量增加,CO     

Effect of Al2O3 Binder on the Precipitated Iron-Based Catalysts for Fischer-Tropsch Synthesis

A series of iron-based Fischer-Tropsch synthesis (FTS) catalysts incorporated with Al2O3 binder were prepared by the combination of co-precipitation and spray drying technology. The catalyst samples were characterized by using N2 physical adsorption, temperature-programmed reduc-tion/desorption (TPR/TPD) and Mossbauer effect spectroscopy (MES) methods. The characterization results indicated that the BET surface area increases with increasing Al2O3 content and passes through a maximum at the Al2O3/Fe ratio of 10/100 (weight basis). After the point, it decreases with further increase in Al2O3 content. The incorporation of AI2O3 binder was found to weaken the surface basicity and suppress the reduction and carburization of iron-based catalysts probably due to the strong K-Al2O3 and Fe-Al2O3 interactions. Furthermore, the H2 adsorption ability of the catalysts is enhanced with increasing Al2O3 content. The FTS performances of the catalysts were tested in a slurry-phase continuously stirred tank reactor (CSTR) under the reaction conditions of 260℃, 1.5 MPa, 1000 h-1 and molar ratio of H2/CO 0.67 for 200 h. The results showed that the addition of small amounts of Al2O3 affects the activity of iron-based catalysts to a little extent. However, with further increase of Al2O3 content, the FTS activity and water gas shift reaction (WGS) activity are decreased severely. The addition of appropriate Al2O3 do not affect the product selectivity, but the catalysts incorporated with large amounts of Al2O3 have higher selectivity for light hydrocarbons and lower selectivity for heavy hydrocarbons.     

Effect of barium on reducibility and activity for cobalt-based Fischer-Tropsch synthesis catalysts

Barium modified Co/Al2O3 catalysts were prepared by incipient wetness impregnation. The catalysts were characterized by XRD, TPD and DRIFTS. The catalytic activity for Fischer-Tropsch synthesis was measured in a continuously stirred tank reactor. It was found that small amounts of BaO (≤ 2 wt%) improved the cobalt reducibility, which led to more cobalt active sites on the catalyst surface, and then resulted in higher CO conversion and C5+ selectivity. However, for the catalysts with high BaO loadings negative effects on the catalytic activity and selectivity for high hydrocarbons were observed because of low cobalt reducibility.     

Fischer-Tropsch synthesis over Ru/Al2O3 catalysts

Fischer-Tropsch syntheses (FTS) were carried out in a slurry phase over Ru/Al₂O₃ catalysts using hexadecane as a solvent. The outcome of the FTS was dependent on the oxide support, calcination temperature, synthesis gas composition and sulfur content. The addition of Mn/Na to Ru/Al₂O₃ was effective in raising the initial activity and C5+ selectivity, but after 20 hours, the performance of the modified catalyst was similar to that of the unmodified catalyst. An additional investigation involving the use of fresh vs used catalysts demonstrated that an agglomeration of the metallic Ru, at least in part, does occur during the reaction.     

CoFe2O4纳米阵列催化剂的费托合成性能研究

通过可控的水热生长方法和钴铁碳酸根氢氧根水合物的焙烧在泡沫铁上制备了CoFe₂O₄纳米阵列催化剂。通过粉末X射线衍射,扫描电镜和电感耦合等离子体发射光谱表征了CoFe₂O₄纳米阵列的晶相,结构和组成。制备的催化剂被用于费托合成性能研究。CoFe₂O₄纳米阵列催化剂在5L/（g·h）的空速下具有69%的转化率,并且其性能优于粉体催化剂。     

TiO2对Ni/Al2O3催化剂CO甲烷化性能的影响

采用溶胶凝胶法制备了一系列不同TiO₂含量的TiO₂-Al₂O₃复合载体,并通过浸渍法制备了NiO/TiO₂-Al₂O₃催化剂。分别考察了不同TiO₂含量的NiO/TiO₂-Al₂O₃催化剂及反应温度对CO甲烷化催化性能的影响。实验结果表明,当复合载体中TiO₂质量分数为30%,反应温度为350～450 ℃时,催化剂催化活性较高。利用N₂吸附-脱附(BET)、X射线衍射(XRD)及H₂程序升温还原(H₂-TPR)等手段对催化剂物化性能进行了表征。结果表明,加入适量的TiO₂能抑制镍铝尖晶石NiAl₂O₄物种的生成,改善NiO的表面分散性能,避免大晶粒NiO的形成,也改善了催化剂的还原性能,从而提高催化剂的CO甲烷化活性。     

NO reduction with C3H8 on Co/Al2O3 catalyst. effect of O2 concentration

The selective catalytic reduction (SCR) of NO by propane in excess oxygen-containing gas mixture was studied on Co/Al₂O₃ catalyst. The oxygen concentration is very important for the reaction. The NO conversion to N₂ without oxygen is 3% at 800 K and when the O₂ concentration is raised up to 8% the NO conversion reaches its maximum value of 60% at 800 K. Characterization results by TPR and UV-Vis spectroscopy show that in the catalyst, species strongly interacting with tetrahedral and octahedral Co²⁺ ions in the support are present. This revised version was published online in June 2006 with corrections to the Cover Date.     

氧化铝载体硫酸化对锰铈催化剂SCR脱硝性能的影响

分别以硫酸改性前后的氧化铝为载体,采用浸渍法制备了锰铈催化剂,对其NH_3-SCR脱硝性能进行评价,并采用XRD、BET、NH_3-TPD、H_2-TPR以及FT-IR对催化剂进行了表征。结果表明,改性降低了金属的分散性和氧化性,增加了酸量,特别是B酸量;催化剂的最佳脱硝温度窗口向高温扩展,活性温度窗口范围变宽,并且,改性液浓度越大变化幅度越大。当反应温度在200-250℃时,未改性催化剂与采用0.2 mol/L硫酸改性的催化剂具有接近的催化活性,但改性后的催化剂具有更高的抗水抗硫活性,250℃时脱硝率可达70%。     

Preparation and characterization of MgO/Al2O3 mixed oxides support for hydrotreating catalysts

The characteristics of pure MgO, Al₂O₃ and three binary mixtures of MgO-Al₂O₃ were studied by determining their BET surface areas, micropore surface area, total pore volume, adsorption-desorption isotherms, the x-ray diffractogram, surface acidity and catalytic functionality for cumene cracking.The XRD results show that the incorporation of alumina into the magnesia beyond 50% renders it amorphous. Furthermore, the mixed oxide containing 50% magnesia and 50% alumina had the highest BET surface area of 200 m²/g and is the only mixed oxide with bimodal pores.The results of the acidity measurements and cumene cracking functionality indicates that strong acid sites are found only in mixed oxides containing more than 50% alumina.     

焙烧温度对二甲醚水蒸气重整制氢 Cu/ZnO/Al2O3/Cr2O3+H-ZSM-5双功能催化剂性能的影响

采用共沉淀耦合机械混合法制备了Cu/ZnO/Al₂O₃/Cr₂O₃+H-ZSM-5双功能催化剂,并用于二甲醚水蒸气重整制氢反应,结合热重、傅里叶红外光谱、XRD、BET、H₂-TPR表征,考察了焙烧温度对Cu/ZnO/Al₂O₃/Cr₂O₃催化剂物理化学性质及双功能催化剂催化性能的影响。研究结果表明,400℃焙烧时,析出CuO粒子的同时伴有尖晶石相,进而在反应过程中对金属铜粒子起到良好的隔离作用。而焙烧温度较低时,催化剂分解不完全,催化剂活性位较少。焙烧温度大于500℃时,CuO粒子发生二次团聚,同时尖晶石相大量生成,造成催化剂活性位减少,活性较低。合适的焙烧温度为400℃,此时二甲醚转化率为92.9%,氢气收率可达到76.5%,具有较好的反应效果。