对1/f噪声缺口的超巨磁电阻Pr2/3Sr1/3MnO3薄膜样品从10K到室温的热电势值进行了测量,热电势为负值,低温下随温度线性变化,表现为金属扩散热电势,在150K开始急剧减小,过渡到与温度T成反比的变化关系,与小极化子模型相符.结合在电阻极大温度附近对电阻和1/f噪声行为的讨论,对于发生在电阻极大温度附近的相变过程,结果支持源于相分离的渝渗模型.     

钙钛矿(La1-yTby)0.67Sr0.33MnO3的超巨磁电阻效应

采用固相反应烧结法制成了钙钛矿(La_1-yTb_y)_0.67Sr_0.33MnO₃(y=0—1)多晶样品.研究了样品的微观结构,常温、低温下的磁性,样品的磁电阻随温度、成分的变化关系,电阻随温度变化特性等.并在y=0.40样品中,170K附近、最大磁化场为7T时,观察到了900%的巨磁电阻. 关键词：     

La1-xCaxMnO3的巨磁电阻效应

通过测量La_2/3Ca_1/3MnO₃，La_0.6Ca_0.4MnO₃单相多晶样品的磁电阻、电阻与温度的依赖关系，发现在La_1-xCa_xMnO₃体系中随x的变化，其磁电阻峰和电阻峰都发生了位移．作者认为体系中Mn⁴⁺含量是受Ca含量调制的，正是Mn⁴⁺含量的变化，导致磁性 关键词：     

巨磁电阻材料La0.9Sr0.1MnO3与半导体Si组成的二极管的整流特性

掺杂锰氧化物La_0.9Sr_0.1MnO₃薄膜被直接沉积在n型 硅基片上，构成p-n结.这种p-n结在很宽的温度范围内都有很好的整流特性.研究结果表明， 这种p-n结的结电阻对低磁场敏感，在3×10^-2T的磁场下，磁电阻可达70％.磁 电阻的正负依赖于温度.磁电阻的大小可通过加在p-n结上的电压调节.     

热压处理对Nd0.7Sr0.3MnO3陶瓷磁电输运影响

在温度1273 K、压强9 GPa条件下对固相烧结Nd_0.7Sr_0.3MnO₃陶瓷样品进行热压处理. 结果发现, 处理后样品的晶体结构和空间群没有改变, 但晶胞参数和结构参数, 特别是样品的显微结构发生了很大变化. 这些变化对样品的磁电输运产生显著影响: 在磁性上, 热压样品的低温饱和磁矩减小并出现磁矩排列弥散特点; 在电输运方面, 当负载电流小于1.5 mA时, 与烧结样品一样, 热压样品不产生电致电阻 (ER) 效应, 并在金属-绝缘体转变点出现最大磁电阻 (MR). 但在低温下, 热压样品仍有较大MR值. 当负载电流超过1.5 mA时, 热压样品原R-T曲线中的电阻峰替变为一电阻平台, 且随负载电流增大, 平台逐渐宽化, 阻值减小, 出现ER行为. 有趣的是, 在外磁场作用下, 电阻平台随外场增大逐渐变窄、消失并又演变为一电阻峰. 这些奇特的输运行为除与热压处理导致样品晶粒绝缘化有关外, 可能还与热压导致粒间相的形成有关.     

混合场中 (Pr1－yNdy)2/3Sr1/3MnO3体系磁转变行为研究

对(Pr1-yNdy)2/3Sr1/3MnO3(y=2/8,4/8,6/8)体系在42K—300K温度范围内混合场（即交流驱动场Hac与附加直流磁场H dc的叠加）下的磁转变行为进行了系统的实验研究. 结果表明，随着外加直流磁场强 度的增大，样品的直流磁化强度增大，交流磁化率逐渐减小；在混合场作用下，磁转变温度 （居里温度）附近样品交流磁化率的实部出现一个特征的尖峰. 对于(Pr1-yNdy)2/3Sr1/3MnO3体系，随着Nd掺杂量的增加，交流磁化率实部 的相对变化 (Eχ′=Δχ′/χ′dc)的峰值对应的温度降低，这一点与该系 统的磁电阻的变化规律一致. 对锰氧化物体系在混合场中的磁转变现象进行了讨论. 关键词： 锰氧化物 混合场 磁特性     

Ag/Nd0.7Sr0.3MnO3陶瓷界面电输运性质研究

用渗银和银胶接触两种方法分别在多晶Nd_0.7Sr_0.3MnO₃陶瓷样品上制作电极,用两线和四线模式对两种接触界面的直、交流特性进行测量.结果发现:渗银电极与陶瓷样品之间具有很好的欧姆接触特性,两线、四线模式下的电阻测量值相近,并且没有电脉冲诱导电阻转变(EPIR)效应;而用银胶接触作电极时,V-I曲线表现出关于原点对称的非线性特征,并出现稳定的室温EPIR效应.两种不同方法制备的电极在交流电场下的输运也有很大差异:渗银电极阻抗 关键词： 界面 接触电阻 EPIR效应 钙钛矿结构锰氧化物     

热处理中Pr0.5Sr0.5MnO3薄膜的电学性能变化和应力弛豫

我们用脉冲激光法在(001)LaAlO3衬底上制备了Pr0.5Sr0.5MnO3薄膜,在900℃的空气中进行后退火处理,研究了退火前后薄膜的电磁性能和晶格结构变化.随着温度降低原位生长薄膜在低温段电阻率迅速上升,表现为绝缘体性质.磁化强度-温度曲线表明薄膜具有顺磁-铁磁-反铁磁的相变,并且存在相分离现象.相比之下,退火后薄膜随着温度降低只出现了顺磁绝缘体-铁磁金属相变,在低温区域一直表现为铁磁金属性.x光衍射实验发现退火使得薄膜在垂直于衬底表面方向的晶格伸长量明显减小,表明退火过程中发生了应力弛豫.为了搞清楚后退火中氧含量和应力弛豫的不同作用,我们进行了(110)SrTiO3衬底上Pr0.5Sr0.5MnO3薄膜的后退火对比实验,结果表明退火中的应力弛豫是导致退火前后薄膜电磁性质差异的主要原因.     

(La1-xCex)2/3Ca1/3MnO3体系的结构和输运性质研究

关键词：     

新型超导体MgCNi3的输运性质研究

测量了新型超导体MgCNi3(Tc=8K)的电阻率、正常态Hall效应和热电势等输运性质.电阻率温度曲线表明,在高于70K的温区可以用电声子散射的BlochGr櫣ｎｅｉｓｅｎ公式拟合.Hall系数RH和热电势S在Tc以上的整个温度范围都为负值,强烈表明MgCNi3的载流子类型为电子型.RH在从Tc到140K的温区内基本不随温度变化,但在140K到室温范围,RH随温度升高其绝对值减小,对RH的这种温度依赖关系进行了讨论.S在150K以上近似与温度成线性关系,而在150K以下显示非线性,用电声子相互作用的重整 关键词： 电阻率 热电势 Hall效应     

Magnetic and magnetocaloric properties of perovskite manganite Pr0.55Sr0.45MnO3

In this paper, we have studied the magnetic and magnetocaloric properties of the perovskite manganite Pr_0.55Sr_0.45MnO₃. It shows a sharp paramagnetic-ferromagnetic phase transition at 291 K and possesses a moderate magnetic entropy change near room temperature. In addition, a large relative cooling power (143.64 J/kg) and a wide temperature range (84 K) have been found in this material. Compare with the Landau model, we find that the itinerant electrons mainly contribute the larger magnetic entropy change at paramagnetic region.     

Magnetotransport properties of La0.67Ca0.33MnO3//La0.67Sr0.33MnO3 bilayers

The perovskite bilayers La0.67Ca0.33MnO3 （LCMO） （100 nm） / La0.67Sr0.33MnO3（LSMO） （100 nm） and LSMO （100 nm） / LCMO （100 nm） are fabricated by a facing-target sputtering technique. Their transport and magnetic properties are investigated. It is found that the transport properties between them are different obviously due to distinguishable structures, and the different lattice strains in both films result in the difference of metal-to-insulator transition. Only single-step magnetization loop appears in our bilayers from 5K to 320K, and the coercive force of LSMO/LCMO varies irregularly with a minimum ～ 2387A/m which is lower than that of LCMO and LSMO single layer films. The behaviour is explained by some magnetic coupling.     

The unusual magnetotransport properties of La0.67Sr0.33MnO3 with Nb2O5 addition

Enhancements of the low-field (LFMR) and high-field magnetoresistance (HFMR) were observed in the manganite system prepared by doping Nb₂O₅ into La_0.67Sr_0.33MnO₃ powders. The maximum MR ratios at 77 K with H=1 T and 1 kOe are 30% and 20% for the 0.07 molar ratio doped sample, which are 1.7 times and 1.6 times as large as that for LSMO, respectively. An MR effect up to 6.5% was also found for the sample with x=0.03 at room temperature (RT). The spin-dependent tunneling and scattering at the interfaces of grain boundaries are responsible for the LFMR while the HFMR originates from a noncollinear spin structure in the surface layer. With increasing x, the Curie temperature (T_C) decreases monotonically from 364 to 154 K while the temperature T_P related to the peak resistivity decreases firstly to a minimum of 204 K (x=0.06) and then rises up to 240 K (x=0.1). There is a maximum resistivity ρ for the sample with x=0.06, which is higher than that for LSMO by five orders of magnitude. It is due to the enhancement of spin-dependent and independent scattering and tunneling effects on the interfaces of grain boundaries and inside the grains.     

多晶La0.7Sr0.3MnO3的低温输运性质和磁电阻效应

详细研究了由纳米晶粒组成的块体多晶La_0.7Sr_0.3MnO₃(LSM)的电阻率和磁电阻效应,以及它们的温度依赖性.随着温度从室温降低,电阻率(ρ)在250K附近存在一最大值,低于该温度后,样品表现为金属导电特性,随后在50K附近存在一极小值.也就是说在低于50K的温度范围内,随着温度降低ρ反而升高,表现为绝缘体性的导电特性.经研究发现,这种随温度降低ρ反而增加的现象与隧穿效应的理论模型(lnρ∝T^-1/2)符合得很好 关键词： 0.7Sr_0.3MnO₃')" href="#">多晶La_0.7Sr_0.3MnO₃ 隧道效应 隧道磁电阻效应     

Structure,magnetic and magnetoresistance properties of Pr0.67Sr0.33MnO3 manganite oxide prepared by ball milling method

A sample of Pr_0.67Sr_0.33MnO₃ nanoparticles was synthesized by the ball milling method. X-ray diffraction pattern of the sample showed orthorhombic system with Pnma space group. The average crystallite size of 110 nm was obtained by both Scanning Electron Microscopy and X-ray diffraction. Magnetic measurements showed para-to-ferromagnetic transition with a Curie temperature of T_C=269 K. Electrical investigations showed that all our samples exhibit a semi-conducting behavior above T_C and a metallic-like one at lower temperatures. The sample exhibited a large magnetoresistance of 30% at room temperature in an applied magnetic field of 2 T. The transport and the magnetic properties were interpreted in terms of the existence of magnetic polarons in the sample.     

Nd0.7Sr0.3MnO3中显微结构相关电致电阻效应

用固相反应和高能球磨合成后续热处理两种方法分别得到钙钛矿结构Nd_0.7Sr_0.3MnO₃氧化物.两种不同方法得到的多晶样品,虽然晶体结构相同,化学成分和晶粒大小相近,但它们电输运性质却表现出很大差异.用固相反应法制得的样品的电阻几乎不随负载电流的变化而变化,即不表现电致电阻行为;而通过高能球磨合成后续热处理方法得到的样品电阻随外加电流增大而急剧减小,出现显著电致电阻效应.产生这种截然不同电输运特性的原因可能与样品的显微结构和界面性质有关. 关键词： 电致电阻效应 显微结构 钙钛矿结构锰氧化物 界面电阻     

Giant magnetoimpedance and colossal ac magnetoresistance of a Cu coil wound on La0.67Sr0.33MnO3

We observed the giant magnetoimpedance and colossal ac magnetoresistance for a Cu coil wound on La_0.67Sr_0.33MnO₃ under low dc magnetic fields. Even though the dc magnetoresistance for La_0.67Sr_0.33MnO₃ plate is only −2.4% under H=12 kOe, a Cu coil wound on La_0.67Sr_0.33MnO₃ plate exhibits a colossal ac magnetoresistance of −93% at 10 MHz and a giant magnetoimpedance of −59% in a wide frequency range of 500 kHz-10 MHz under a longitudinal field . The transverse magnetoimpedance is weaker than the longitudinal one. The giant magnetoimpedance and colossal ac magnetoresistance for a Cu coil wound on La_0.67Sr_0.33MnO₃ are connected with the variation of permeability induced by dc magnetic field.     

Nd0.7Sr0.3MnO3陶瓷中界面“陷阱态”相关电阻转变行为

通过固相烧结和高能球磨后热处理两种方法分别得到不具晶(相)界和具有明显晶(相)界的两种Nd_0.7Sr_0.3MnO₃陶瓷样品, 并用两线法和四线法分别对这两种样品的电极-块体接触界面和晶(相)界界面的I-V和电脉冲诱导电阻转变效应(EPIR)进行研究. 结果发现, 在两线法测试下, 电极-块体界面具有回滞的非线性I-V特征, 并能产生稳定的EPIR效应, EPIR的稳定性随温度的升高逐渐减弱并消失; 而对具有明显晶(相)界的陶瓷样品, 四线法测试结果表明, 虽然其I-V行为也具有非线性和回滞性特点, 但不能产生EPIR 效应. 这些奇特的界面输运行为与界面中的各种缺陷充当“陷阱”并实现对载流子的捕捉和释放过程密切相关. 而大量的晶(相)界界面及其复杂的连接方式导致较大的漏导则是晶(相)界不能出现EPIR效应的主要原因.