YBO3:Eu3+纳米晶发光特性

用水热法制备了YBO₃:Eu³⁺纳米材料，通过改变其反应条件对纳米颗粒的大小和形貌进行了控制，对其发射光谱进行分析并与体材料进行了比较.在纳米材料中，很大比例的稀土离子微观环境受到表面的影响.这种影响可能使稀土离子的Judd-Ofelt参数Ω₂增大，从而使Eu³⁺的⁵D₀→⁷F₂的发射加强，红色发光材料的色纯度提高.     

Luminescent properties of Eu-activated Sr3B2SiO8: A red-emitting phosphor for white light-emitting diodes

Single-phased Sr₃B₂SiO₈:Eu³⁺ phosphor was prepared by a solid-state method at 1020 °C. The luminescence spectra showed that Sr₃B₂SiO₈:Eu³⁺ phosphor can be effectively excited by near ultraviolet light (393 nm) and blue light (464 nm). When excited at 393 or 464 nm Sr₃B₂SiO₈:Eu³⁺ exhibited the main emission peaks at 611 and 620 nm, which resulted from the supersensitive ⁵D₀→⁷F₂ transition of Eu³⁺. The luminescence intensity of Sr₃B₂SiO₈:Eu³⁺ at 611 and 620 nm reached the maximum when the doping content of Eu³⁺ was 4.5 mol%. Its chromaticity coordinates (0.646, 0.354) were very close to the NTSC standard values (0.67, 0.33). Thus, Sr₃B₂SiO₈:Eu³⁺ is considered to be an efficient red-emitting phosphor for long-UV InGaN-based light-emitting diodes.     

Synthesis of nano-size BaMgAl10O17:Eu blue phosphor by a rapid exothermic reaction

Ultrafine particles of BaMgAl₁₀O₁₇:Eu²⁺ (BAM) phosphor were synthesized by a solid-state combustion reaction in a powder bed of 0.9BaCO₃+MgO+5Al₂O₃+0.05Eu₂O₃+k(KClO₃+1.5C) composition. A large exothermic reaction of the mixture (KClO₃+1.5C) leads to a self-sustaining combustion mode. Under optimized combustion conditions, the product consisted of BAM powder and KCl was obtained. BAM ultrafine particles resulting from the combustion process were easily obtained by simply washing the salt by-product with water. Combustion-processed BAM phosphor shows a homogeneous grain size of 100-500 nm, good dispersity, regular morphology, and improved luminescence properties.     

Improved photoluminescence and afterglow in CaTiO3:Pr with addition of nanosized SiO2

Enhancement of the ¹D₂-³H₄ red emission in CaTiO₃:Pr³⁺ with addition of nanosized SiO₂ fabricated by a solid state reaction method is reported. The dynamical processes for the improvement of red emission were systematically investigated using photoluminescence (PL) and PL excitation spectra, and diffused reflectance spectra as well as time decay patterns of PL and persistent afterglow. Higher efficiency of energy transfer from CaTiO₃ host to the activator Pr³⁺ due to the improvement of crystallinity by SiO₂ addition was discussed in comparison with that of the SiO₂ free sample. The enhancement of persistent afterglow after the cessation of excitation in SiO₂ added CaTiO₃:Pr³⁺ was also analyzed by theoretically fitted results.     

Photoluminescence properties of Eu in Y(PO3)3 under VUV excitation

The photoluminescence properties of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) are investigated. The excitation spectrum of Y_0.85(PO₃)₃:0.15Eu₃⁺ shows that both the (PO₃)₃³⁻ groups and the CT bands of O²⁻-Y³⁺ can efficiently absorb the excitation energy in the region of 120-250 nm. Under 147 nm excitation, the optimal emissive intensity of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) is about 36% of the commercial phosphor (Y,Gd)BO₃:Eu³⁺, which hints that the absorbed energy by the host matrix could be efficiently transferred to Eu³⁺. We try to study the concentration quenching mechanism of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) under 147 and 172 nm excitation.     

Spherical Zn2SiO4:Eu@SiO2 phosphor particles in core-shell structure: Synthesis and characterization

Spherical SiO₂ particles have been coated with Zn₂SiO₄:Eu³⁺ phosphor layers by a Pechini sol-gel process. The microstructure and luminescent properties of the obtained Zn₂SiO₄:Eu³⁺@SiO₂ particles were well characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, and lifetime. The results demonstrate that the Zn₂SiO₄:Eu³⁺@SiO₂ particles, which have regular and uniform spherical morphology, emitted an intensive red light emission at 613 nm under excitation at 395 nm. Besides, the effects of the Eu³⁺ concentration, annealing temperature and charge compensators of Li⁺ ions on the PL emission intensities were investigated in detail.     

白光LED用LiBaBO3:Eu2+材料发光特性研究

采用高温固相法制备了LiBaBO₃:Eu²⁺绿色发光材料.测量了Eu²⁺浓度为1mol%时样品的激发与发射光谱,其发射光谱为双峰宽谱,主峰分别为482和507nm,与理论计算值符合很好;监测482nm发射峰时,对应激发光谱的峰值为287和365nm,监测507nm发射峰时,对应的激发峰为365和405nm.研究了Eu²⁺浓度对材料发射光谱的影响,结果显示,随Eu²⁺浓度的增大,蓝、绿发射峰均发生了     

掺杂浓度和烧结温度对CaWO4:Eu3+发光性能的影响

采用微乳液法合成掺杂浓度不同和烧结温度不同的CaWO₄:Eu³⁺系列荧光体, 这些荧光体都具有Eu³⁺离子的特征荧光发射. 在不同温度烧结后, 高浓度掺杂的样品(Eu³⁺掺杂30或50 mol%)可获得最大的发光强度, 低浓度掺杂的样品(掺杂0.5—2 mol%)在800 ℃烧结时也可获得优异的发光强度. 实验结果表明, Eu³⁺离子高浓度掺杂的CaWO₄:Eu³⁺在紫外光激发下可成为高效发光的荧光粉.     

Luminescent properties of green- or red-emitting Eu-doped Sr3Al2O6 for LED

Eu²⁺-doped Sr₃Al₂O₆ (Sr_3−xEu_xAl₂O₆) was synthesized by a solid-state reaction under either H₂ and N₂ atmosphere or CO atmosphere. When H₂ was used as the reducing agent, the phosphor exhibited green emission under near UV excitation, while CO was used as the reducing agent, the phosphor mainly showed red emission under blue light excitation. Both emissions belong to the d-f transition of Eu²⁺ ion. The relationship between the emission wavelengths and the occupation of Eu²⁺ at different crystallographic sites was studied. The preferential substitution of Eu²⁺ into different Sr²⁺ cites at different reaction periods and the substitution rates under different atmospheres were discussed. Finally, green-emitting and red-emitting LEDs were fabricated by coating the phosphor onto near UV- or blue-emitting InGaN chips.     

Luminescence spectroscopy of Eu in Ca3Sc2Si3O12

Ca₃Sc₂Si₃O₁₂ doped with 1 mol% Eu³⁺ and having a cubic garnet structure was prepared by a solid state reaction. The low temperature luminescence spectrum shows no measurable ⁵D₀→⁷F₀ band, in agreement with the location of the lanthanide dopant in a site of D₂ symmetry, i.e. with a Ca²⁺ substitution. On the other hand, the spectrum is clearly dominated by the ⁵D₀→⁷F₄ band, which is significantly stronger than that for the other transitions originating from the ⁵D₀ level. This unusual behavior is explained on the basis of a model describing the distortion of the EuO₈ coordination polyhedron from a cubic geometry to the actual D₂ one.     

Doping effects of Nb5+ on red long afterglow phosphor CaTiO3:Pr3+

A series of Nb5+ codoped red long afterglow phosphors CaTi1 xNbxO3:Pr03.+002 (0 ≤ x ≤ 0.05) is prepared by a solid state reaction method. Their photoluminescence, phosphorescence and thermoluminescence are investigated. The results indicate that codoping Nb5+ can improve the photoluminescence and phosphorescence property of CaTiO3:Pr3+ significantly. When 3-mol% Nb5+ is codoped, the emission intensity of CaTiO3:Pr3+ is enhanced twice, while the afterglow time is extended from 10 min to about 40 min. Thermoluminescence results reveal that the trapping level of CaTiO3:Pr3+ is reduced from 0.82 eV to 0.62 eV by codoping Nb5+. The effect of Nb5+ doping on enhancing the photoluminescence intensity and afterglow time of CaTiO3:Pr3+ is discussed.     

Preparation and luminescence properties of SrTiO3:Pr,Al phosphor from the glycolate method

Spherical SrTiO₃:Pr³⁺,Al³⁺ phosphor with high crystallinity and uniform particle size distribution was formed from the glycolate precursor. The glycolate precursor was obtained by heating the mixed solution of metallic nitrates and titanium oxychloride in ethylene glycol up to 200 °C. The thermal decomposition of the glycolate precursor proceeded through three major stages, i.e., (i) evolution of glycols (∼200 °C), (ii) decomposition of glycolate precursor, and (iii) decomposition of strontium carbonate and crystallization of SrTiO₃:Pr³⁺,Al³⁺ phosphor.SrTiO₃:Pr³⁺,Al³⁺ phosphor exhibited a strong red emission, peaking at about 617 nm. SrTiO₃:Pr³⁺,Al³⁺ phosphor obtained from the glycolate complex has higher luminescent properties than the conventional solid state reaction and the Pechini method in terms of photoluminescence (PL) and cathodoluminescence (CL). High crystallinity, low residual carbon content and small grain size with uniform shape would enhance the luminescence intensity of phosphor by the glycolate method due to high surface area per unit volume and low organic content compared with the Pechini method. Also, Al³⁺ ion is more effective than Ga³⁺ ion to enhance PL intensity of SrTiO₃:Pr³⁺,Al³⁺ phosphor because of smaller Al³⁺ ion radius. Therefore, the glycolate method has been demonstrated to be a convenient and unique process for the production of muticomponent oxide with smaller grain size and higher crystallinity compared with the conventional mixed oxide reaction and the polymer precursor method.     

Synthesis and properties of submicron range CaSO4:Eu particles

CaSO₄:Eu with particle size in submicron range was synthesized. Radiation induced Eu³⁺↔Eu²⁺ conversion as well as thermal conversion was studied. The samples showed thermal conversion above 400 °C. However, no radiation induced conversion in submicron range particles was observed. Particles heated above 400 °C coalesce and when heated at 925 °C bigger particles of 20 μm size were formed. Optical microscopy of these particles reveals red inclusion of about 5 μm inside CaSO₄ particle. It is speculated that the red inclusion is CaS:Eu²⁺.     

A white light emitting phosphor Sr1.5Ca0.5SiO4:Eu, Tb, Eu for LED-based near-UV chip: Preparation, characterization and luminescent mechanism

In this work, we report preparation, characterization and luminescent mechanism of a phosphor Sr_1.5Ca_0.5SiO₄:Eu³⁺,Tb³⁺,Eu²⁺ (SCS:ETE) for white-light emitting diode (W-LED)-based near-UV chip. Co-doped rare earth cations Eu³⁺, Tb³⁺ and Eu²⁺ as aggregated luminescent centers within the orthosilicate host in a controlled manner resulted in the white-light phosphors with tunable emission properties. Under the excitation of near-UV light (394 nm), the emission spectra of these phosphors exhibited three emission bands: one broad band in the blue area, a second band with sharp lines peaked in green (about 548 nm) and the third band in the orange-red region (588-720 nm). These bands originated from Eu²⁺ 5d→4f, Tb³⁺⁵D₄→⁷F_J and Eu³⁺⁵D₀→⁷F_J transitions, respectively, with comparable intensities, which in return resulted in white light emission. With anincrease of Tb³⁺ content, both broad Eu²⁺ emission and sharp Eu³⁺ emission increase. The former may be understood by the reduction mechanism due to the charge transfer process from Eu³⁺ to Tb³⁺, whereas the latter is attributed to the energy transfer process from Eu²⁺ to Tb³⁺. Tunable white-light emission resulted from the system of SCS:ETE as a result of the competition between these two processes when the Tb³⁺ concentration varies. It was found that the nominal composition Sr_1.5Ca_0.5SiO₄:1.0%Eu³⁺, 0.07%Tb³⁺ is the optimal composition for single-phased white-light phosphor. The CIE chromaticity calculation demonstrated its potential as white LED-based near-UV chip.     

Enhanced luminescent properties of long-persistent Sr2MgSi2O7:Eu, Dy phosphor prepared by the co-precipitation method

Sr₂MgSi₂O₇:Eu²⁺, Dy³⁺ phosphors were prepared by the (aminopropyl)-triethoxysilane (APTES) co-precipitation method. Effects of synthesis temperature on the crystal characteristics, luminescent properties and afterglow performance of Sr₂MgSi₂O₇:Eu²⁺, Dy³⁺ phosphors have been discussed in detail and compared with the corresponding commercial product. The experimental results indicated that the sample could be synthesized at a relatively lower temperature and had better performance on the above-mentioned properties using the co-precipitation method.     

Preparation and luminescence properties of Tb doped ZrO2 and BaZrO3 phosphors

ZrO₂:Tb³⁺ and BaZrO₃:Tb³⁺ powders are prepared by combustion synthesis method and the samples were further heated to 500, 700 and 1000 °C to improve the crystallinity of the materials. The structure and morphology of materials have been examined by X-ray diffraction, Raman spectra and scanning electron microscopy. It is remarkable that all the samples of ZrO₂:Tb³⁺ and BaZrO₃:Tb³⁺ have similar morphology. These images exhibited homogeneous aggregates of varying shapes and sizes, which are composed of a large number of small cuboids and broken cuboids. The cuboids and broken cuboids size of all the samples are less than 0.5 μm. Photoluminescence for both materials increases with increase of temperature and found maximum for the samples heated to 1000 °C with 5 mole% doping of Tb³⁺ ions. Luminescence is almost double for the zirconia compared to that of barium-zirconate.     

Synthesis and luminescence properties of nanocrystalline Gd2O3:Eu by combustion process

The nanocrystalline Gd₂O₃:Eu³⁺ powders with cubic phase were prepared by a combustion method in the presence of urea and glycol. The effects of the annealing temperature on the crystallization and luminescence properties were studied. The results of XRD show pure phase can be obtained, the average crystallite size could be calculated as 7, 8, 15, and 23 nm for the precursor and samples annealed at 600, 700 and 800 °C, respectively, which coincided with the results from TEM images. The emission intensity, host absorption and charge transfer band intensity increased with increasing the temperature. The slightly broad emission peak at 610 nm for smaller particles can be observed. The ratio of host absorption to O²⁻-Eu³⁺ charge transfer band of smaller nanoparticles is much stronger compared with that for larger nanoparticles, furthermore, the luminescence lifetimes of nanoparticles increased with increasing particles size. The effects of doping concentration of Eu³⁺ on luminescence lifetimes and intensities were also discussed. The samples exhibited a higher quenching concentration of Eu³⁺, and luminescence lifetimes of nanoparticles are related to annealing temperature of samples and the doping concentration of Eu³⁺ ions.     

超声喷雾共沉淀法制备的Lu3Al5O12∶Eu3+ 纳米粉体发光特性

采用新型超声喷雾共沉淀法技术,以Lu₂O₃、Eu₂O₃、Al(NO₃)₃·9H₂O为原料,制备了不同浓度Eu³⁺离子掺杂的Lu₃Al₅O₁₂纳米粉体.用X射线粉末衍射表征了获得纳米粉体的相,用扫描电镜观察了纳米粒子的形貌.测定了粉体的激发光谱、⁷F₀-⁵D₂声子边带谱与发射光谱.研究了不同高温烧结温度与Eu³⁺掺杂浓度对纳米粒子的发光强度与粒子形貌的影响规律.研究表明,当烧结温度高于900 ℃时,粉体发光强度明显增强,并且随着煅烧温度的增加,发光强度有所增强.Eu³⁺离子的最佳掺杂浓度为5~7 mol%.根据稀土离子Eu³⁺光学跃起矩阵元的特点,从发射光谱获得Eu³⁺光学跃起的J-O参量Ω₂与Ω₄.在Eu³⁺掺杂浓度均为5 mol%时,其强度参量达最小,电-声子耦合最强.然后随着掺杂浓度的进一步提高,强度参量略有增加,电-声子耦合减弱.说明Eu-O键强增加,共价性增强,Eu³⁺的局域环境对称性降低.Ω₂值低于Eu³⁺在玻璃与晶体基质中的情况,这是由于纳米粒子中存在着大量的缺陷以及晶体的结构畸变导致纳米粒子的对称性下降所致.     

发光二极管用SrWO4:Eu3+红光荧光粉激发谱强度的调控

采用化学共沉淀法制备了Eu³⁺掺杂摩尔分数不同、煅烧温度不同的SrWO₄:Eu³⁺系列发光粉体, 所制备的粉体均具有Eu³⁺特征的强室温红光荧光发射. 通过调节煅烧温度和掺杂摩尔分数来调控近紫外和蓝光吸收强度, 进而调控用395 nm的近紫外光和465 nm的蓝光激发样品所得红光发光强度. 研究结果表明, 所制备的SrWO₄:Eu³⁺红光荧光粉可以被紫外和蓝光发光二极管有效激 关键词： 稀土掺杂 4:Eu³⁺')" href="#">SrWO₄:Eu³⁺ 光致发光 白光发光二极管     

A red oxide phosphor, Sr2ScAlO5:Eu2+ with perovskite-type structure, for white light-emitting diodes

Sr2ScAlO5:Eu2+,a red oxide phosphor with a perovskite-type structure,has been synthesized through a solid-state reaction and its luminescence properties have been investigated.An absorption band centering at 450 nm is observed from the diffuse reflection spectra and the excitation spectra,indicating that the phosphor can match perfectly with the blue light of InGaN light-emitting diodes.A broad red emission band at 620 nm is found from the emission spectra,originating from the 4f 6 5d-4f 7 transition of the Eu 2+ ions.The best doping content of Eu in this material is about 5%.Sr2ScAlO5:Eu2+is a highly promising red phosphor for use in white light-emitting diodes.