Optical spectroscopy of Yb/Er codoped NaY(WO4)2 crystal

Erbium and ytterbium codoped double tungstates NaY(WO₄)₂ crystals were prepared by using Czochralski (CZ) pulling method. The absorption spectra in the region 290-2000 nm have been recorded at room temperature. The Judd-Ofelt theory was applied to the measured values of absorption line strengths to evaluate the spontaneous emission probabilities and stimulated emission cross sections of Er³⁺ ions in NaY(WO₄)₂ crystals. Intensive green and red lights were measured when the sample were pumped by a 974 nm laser diode (LD), especially, the intensities of green upconversion luminescence are very strong. The mechanism of energy transfer from Yb³⁺ to Er³⁺ ions was analyzed. Energy transfer and nonradiative relaxation played an important role in the upconversion process. Photoexcited luminescence experiments are also fulfilled to help analyzing the transit processes of the energy levels.     

Growth, spectroscopic characteristics and laser potential of Yb3+:Ca3La2(BO3)4 crystal

Crystal of Yb³⁺-doped Ca₃La₂(BO₃)₄ has been grown by the Czochralski technique. The room temperature absorption and fluorescence spectra of the crystal have been investigated. The result showed that this crystal exhibits broad absorption and emission with the FWHM of 11 nm at 978 nm and 66 nm FWHM at 1025 nm, respectively. The stimulated emission cross-section of Yb³⁺ ions were calculated using the reciprocity method and Fuchtbauer-Ladenburg method, respectively. The room temperature fluorescence decay curves of ² F _5/2 manifold of Yb³⁺ ions were recorded for both crystal and powder samples. The effect of radiation tapping on the spectroscopic properties is discussed. The result that the lifetime of the powder sample is shorter than that of the bulk sample demonstrates the existence of radiation trapping effect. The laser potentiality was also evaluated and the results show that this crystal is a good candidate for tunable and ultrashort pulse lasers.     

Spectroscopic characteristics of Pr<Superscript>3+</Superscript> in biaxial La<Subscript>2</Subscript>(WO<Subscript>4</Subscript>)<Subscript>3</Subscript> crystal

A Pr³⁺-doped La₂(WO₄)₃ crystal grown by the Czochralski method has been investigated as a promising laser material. The principal axes of the optical indicatrix and Pr³⁺ concentration of the crystal were determined. The polarized absorption, fluorescence spectra and fluorescence decay curves of the main emission multiplets of the crystal were measured at room temperature. The spectroscopic parameters were obtained by the modified Judd–Ofelt theory combined with the normalized method. The peak stimulated emission cross-sections of the major emission lines were estimated. The good spectroscopic properties imply that the Pr³⁺:La₂(WO₄)₃ crystal is a potential laser gain medium for solid-state laser and self-stimulated Raman laser applications. PACS 78.20.-e; 42.70.Hj     

Polarized spectroscopic properties of Nd-doped KGd(WO4)2 single crystal

The polarized absorption spectra, infrared fluorescence spectra, upconversion visible fluorescence spectra, and fluorescence decay curve of orientated Nd³⁺:KGd(WO₄)₂ crystal were measured at room-temperature. Some important spectroscopic parameters were investigated in detail in the framework of the Judd-Ofelt theory and the Fuchtbauer-Ladenburg formula. The effect of the crystal structure on the spectroscopic properties of the Nd³⁺ ions was analyzed. The relation among the spectroscopic parameters and the laser performances of the Nd³⁺:KGd(WO₄)₂ crystal was discussed.     

Growth and spectroscopic properties of Yb-doped Li6Y(BO3)3 single crystal

The spectroscopic properties of high-quality Czochralski grown 20% Yb³⁺-doped Li₆Y(BO₃)₃ single crystal as new promising laser material are presented. The crystal was seeded-grown in the 〈0 1 0〉 direction and its crystallinity was measured using X-ray rocking curve analysis. Low temperature transmission spectrum exhibits broad bands in a short range of wavelengths and two sharp lines at 972.5 and 978 nm, interpreted as two zero-lines of two nonequivalent Yb³⁺ centers inside the lattice. The fluorescence lifetimes associated to these two intense lines are different: 0.867 and 1.33 ms. An attempt of determination of the Stark sublevels energies of the ⁴F_5/2 and ⁴F_7/2 manifolds of the two Yb³⁺ nonequivalent ions is given. The polarized absorption and emission spectra were also recorded at room temperature and we conclude that the most favorable emission line for laser application could be around 1042 nm in n_g polarization.     

ANALYSIS OF LASING PERFORMANCES OF Yb3+-DOPED YAG, FAP, KYW CRYSTALS

The Yb³⁺ laser emitting at a 1.03μm wavelength has been evoking strong interest recently due to its advantages of long fluorescence lifetime, broad absorption band and the fact that it never shows concentration quenching. On the other hand, as a laser of three-level system it has, in general, a relatively high threshold power, which makes it important to seek some suitable host crystals to reduce this. Here, we present a comparison of the lasing performances of Yb³⁺-doped YAG [Y₃Al₅O₁₂], FAP [Ca₅(PO₄)₃F] and KYW [KY(WO₄)₂] crystals, including threshold power and slope efficiency, with those of the Nd:YAG laser based on the threshold formula of three-and four-level systems deduced by the authors. The results show that the Yb³⁺ laser can output a power larger than the Nd:YAG laser does in the case of comparably higher pumping power, if the length of the lasing rod and the concentration of the active ions satisfy some conditions. The theoretical results are also close to the experimental results reported.     

Up-conversion emission in triply-doped Ho/Yb/Tm KGd(WO4)2 single crystals

Detailed spectroscopic studies of the triply doped KGd(WO₄)₂:Ho³⁺/Yb³⁺/Tm³⁺ single crystals (which exhibit multicolor up-conversion fluorescence) are reported for the first time. The absorption spectra of crystals were measured at 10 and 300 K; the room temperature luminescence spectra were excited at 980 nm wavelength. The dependence of the intensity of luminescence on the excitation power for three different concentration of Ho³⁺, Yb³⁺ and Tm³⁺ ions was investigated. Efficient green and red up-converted luminescence of Ho³⁺ ions and weak blue up-conversion luminescence of Tm³⁺ ions were observed in spectra. The red emission of Ho³⁺ ions is more intensive than their green emission. Dependence of the up-conversion luminescence intensity on the excitation power and impurities concentration was also studied; the number of phonon needed for efficient up-conversion was determined for each case. All possible energy transfer processes between different pairs of the impurity ions' energy levels are also discussed.     

Synthesis process and the luminescence properties of rare earth doped NaLa(WO4)2 nanoparticles

Rare earth doped NaLa(WO₄)₂ nanoparticles have been prepared by a simply hydrothermal synthesis procedure. The X-ray diffraction (XRD) pattern shows that the Eu³⁺-doped NaLa(WO₄)₂ nanoparticles with an average size of 10-30 nm can be obtained via hydrothermal treatment for different time at 180 °C. The luminescence intensity of Eu³⁺-doped NaLa(WO₄)₂ nanoparticles depended on the size of the nanoparticles. The bright upconversion luminescence of the 2 mol% Er³⁺ and 20 mol% Yb³⁺ codoped NaLa(WO₄)₂ nanoparticles under 980 nm excitation could also be observed. The Yb³⁺-Er³⁺ codoped NaLa(WO₄)₂ nanoparticles prepared by the hydrothermal treatment at 180 °C and then heated at 600 °C shows a 20 times stronger upconversion luminescence than those prepared by hydrothermal treatment at 180 °C or by hydrothermal treatment at 180 °C and then heated at 400 °C.     

EPR and optical properties of KYb(WO4)2 and KTb0.2Yb0.8(WO4)2 single crystals

Well oriented KYb(WO₄)₂ and KTb_0.2Yb_0.8(WO₄)₂ single crystals have been investigated for their magnetic and optical properties using the Raman and EPR techniques. The registered EPR signal is dominated by three lines ascribed to ytterbium ions: one main and two satellites. Tb ions, although non-paramagnetic, distinctly modify magnetic properties of the KYb(WO₄)₂ single crystal. Basic parameters of the spin Hamiltonian, including Zeeman and hyperfine terms (g and A matrices) as well the spatial orientation between principal and crystallographic axes systems were determined for both crystals.     

Spectroscopic properties of Pr:KY(MoO4)2 crystal as a visible laser gain medium

A Pr³⁺-doped KY(MoO₄)₂ single crystal was grown by the Czochralski method. The polarized absorption and fluorescence spectra of the Pr³⁺:KY(MoO₄)₂ crystal were measured at room temperature. The stimulated emission cross-sections for the transitions from the ³P₀ multiplet were estimated from the fluorescence spectra. The fluorescence lifetime of the ³P₀ multiplet was estimated from the fluorescence decay curve at room temperature. The analysis of spectral properties shows that the Pr³⁺:KY(MoO₄)₂ crystal is a promising gain medium for visible lasers.     

Spectral properties of Nd-doped Sr3Ga2Ge4O14 crystal

Neodymium doped strontium gallogermanate crystals were grown successfully by the Bridgman technique. The linear thermal expansion coefficients for the c- and a-axes were measured as 5.8 × 10⁻⁶ °C⁻¹ and 6.5 × 10⁻⁶ °C⁻¹. Absorption spectra, and fluorescence spectra, as well as fluorescence decay curves of Nd³⁺-doped Sr₃Ga₂Ge₄O₁₄ crystal, have been recorded at room temperature and used to calculate the absorption and stimulated emission cross-sections. Based on the Judd-Ofelt theory, three intensity parameters were obtained. The luminescent quantum efficiency of the ⁴F_3/2 level was determined to be approximately 73.8% for this material. Compared with other Nd³⁺-doped laser crystals, Nd³⁺-doped Sr₃Ga₂Ge₄O₁₄ crystal displays special laser properties due to its disorder structure.     

Spectral performance and intensive green upconversion luminescence in Er/Yb-codoped NaY(WO4)2 crystal

Using Czochralski (CZ) pulling method, an Er³⁺/Yb³⁺-codoped NaY(WO₄)₂ crystal was prepared. Absorption spectra, emission spectra and excitation spectra of this crystal were measured at room temperature. Some optical parameters, such as intensity parameters, spontaneous emission probabilities and lifetimes, were calculated from absorption spectra with Judd-Ofelt (J-O) theory. Upconversion luminescence excited by a 970 nm diode laser was studied. In this crystal, green upconversion luminescence is particularly intensive. Energy transfer mechanisms that play an important role in upconversion processes were analyzed. Two cross-relaxation processes: ⁴G_11/2 + ⁴I_9/2 → ²H_11/2 (or ⁴S_3/2) + ²H_11/2 (or ⁴S_3/2), and ⁴G_11/2 + ⁴I_15/2 → ²H_11/2 (or ⁴S_3/2) + ²I_13/2, which contribute to the intensive green luminescence under 378 nm excitation, were put forward. Background energy transfer ⁴G_11/2(Er³⁺) + ²F_7/2(Yb³⁺) → ⁴F_9/2(Er³⁺) + ²F_5/2(Yb³⁺) was also demonstrated.     

The optical properties of Dy-doped NaY(MoO4)2 crystal

The Dy³⁺-doped NaY(MoO₄)₂ single crystals were grown successfully by the Czochralski technique. The main spectroscopic properties (absorption, luminescence, decay curve) of Dy³⁺-doped NaY(MoO₄)₂ have been determined for both the σ and π polarizations. By using the Judd-Ofelt theory, the measured room temperature absorption spectra were applied to determine the intensity parameters, spontaneous transition probabilities, branching ratios, and radiative lifetimes of Dy³⁺ transitions. The results show that the Dy³⁺-doped NaY(MoO₄)₂ crystal may realize the yellow laser operation.     

Yb3+掺杂KY(WO4)2激光晶体生长、结构与光谱分析

采用顶部籽晶提拉法(TSSG)生长出Yb:KY(WO₄)₂(Yb:KYW)激光晶体.对预烧后的原料及晶体进行了XRD分析，结果表明，分别在920℃和600℃预烧8h后的熔质和助熔剂基本上形成一相，抑止了实验中的挥发问题；所生长的晶体为β-Yb:KYW，计算其晶格常数为a=1.063nm，b=1.034nm，c=0.755nm，β=130.75°.测得不同厚度样品的吸收光谱，结果表明样品在933nm和981nm有较强的吸收峰，计算出主峰981nm的吸收截面σ关键词： Yb:KYW TSSG法 晶体结构 光谱参数     

EPR studies of Gd3+-doped Ce2(SO4)3.8H2O and La2(SO4)3.9H2O single crystals

EPR spectra of Gd³⁺-doped Ce₂(SO₄)₃.8H₂O and La₂(SO₄)₃.9H₂O single crystals have been measured with an X-band spectrometer at room and low temperatures. The absolute signs of spin Hamiltonian parameters have been determined for the La₂(SO₄)₃.9H₂O host from intensities of lines at liquid helium temperature; for the Ce₂(SO₄).8H₂O host the lines broaden considerably below 60 K, not permitting the determination of absolute signs of spin Hamiltonian parameters. The data are analysed using a rigourous least-squares procedure, fitting simultaneously all lines obtained for several orientations of the external magnetic field. The zero-field splittings have been computed for both the hosts. The characteristics of EPR spectra of Gd³⁺ in these hosts are compared with those obtained in other rare-earth trisulphate octahydrate hosts.     

New materials for optical cooling

Well-characterized solid-state laser materials are evaluated for performance in optical refrigeration as well as radiation-balanced laser systems. New figures-of-merit are developed and applied to ytterbium-doped materials. Superior performance is predicted for high-cross-section tungstate materials. Photothermal deflection experiments on samples of Yb³⁺-doped KGd(WO₄)₂ confirm anti-Stokes fluorescence cooling. This is the first observation of optical cooling in a crystal. Received: 1 February 2000 / Revised version: 15 June 2000 / Published online: 13 September 2000     

Optical amplification properties of Dy3+-doped Gd2SiO4, Lu2SiO5 and YAl3(BO3)4 single crystals

Comparative investigation of the optical amplification properties of dysprosium doped Gd₂SiO₅, Lu₂SiO₅ and YAl₃(BO₃)₄ single crystals was performed in a pump-and-probe experiment. High power laser pulses at 475 nm were used as the pump source in order to strongly populate the ⁴F_9/2 level of the Dy³⁺ ions due to ground state absorption. Low signal beam cw radiation at 574 nm was used as the probe beam to stimulate the emission associated with the ⁴F_9/2→⁶H_13/2 electronic transition of the Dy³⁺ ions. The process was modelled as a three levels system, and their populations were analysed and simulated in order to study the gain dynamics. Positive optical gain was observed and compared in these crystals. These results confirmed that among the systems studied the Dy³⁺-doped YAl₃(BO₃)₄ single crystal can be considered as a good candidate to develop an optical amplifier employing the ⁴F_9/2→⁶H_13/2 transition at around 574 nm which is the first step to consider as laser active media.     

Spectroscopic characteristics of Yb3+-doped Li3Ba2Y3(WO4)8 crystal

This paper reports the spectroscopic properties of Yb³⁺:Li₃Ba₂Y₃(WO₄)₈ crystal. The polarized spectral properties of Yb³⁺:Li₃Ba₂Y₃(WO₄)₈ crystal were investigated. The laser performance parameters β_min, I_sat and I_min of Yb³⁺:Li₃Ba₂Y₃(WO₄)₈ crystals have been also established. Yb³⁺:Li₃Ba₂Y₃(WO₄)₈ crystal has a broad FWHM of the gain cross-section and larger absorption and emission cross-sections. These results may regard the Yb³⁺:Li₃Ba₂Y₃(WO₄)₈ crystal as a tunable laser material.     

The Yb to Er energy transfer in YAl3(BO3)4 crystal

The Yb³⁺ to Er³⁺ energy transfer in yttrium aluminum borate (YAB) crystal is investigated with the rate equation without considering the back energy transfer. The energy transfer coefficients (W₂₅) in the crystals with different Yb³⁺ concentrations are determined and compared with those in other crystals. The transfer efficiencies and the micro-parameters of energy transfer and migration are also determined. The results show that the energy transfer from Yb³⁺ to Er³⁺ in YAB crystal is very efficient and the Yb³⁺–Er³⁺ co-doped YAB crystal may be a good candidate for the 1.55 μm laser media.     

Origin of green luminescence in PbWO4 crystals

Characteristics of two green emission bands, G(I) and G(II), and their origin were investigated within 0.4-300 K under photoexcitation in the 3.4-6.0 eV energy range for undoped and Mo⁶⁺-, Mo⁶⁺ , Y³⁺-, Mo⁶⁺, Nb⁵⁺-, Mo⁶⁺, Ce³⁺-, Cr⁶⁺-, La³⁺-, Ba²⁺- and Cd²⁺-doped PbWO₄ crystals with different concentrations of impurity and intrinsic defects, grown by different methods and annealed at different conditions. The G(I) emission band, observed at low temperatures, located around 2.3-2.4 eV and excited around 3.9 eV, is usually a superposition of many closely positioned bands. The G(I) emission of undoped crystals is assumed to arise from the WO₄²⁻ groups located in the crystal regions of lead-deficient structure. In Mo⁶⁺-doped crystals, this emission arises mainly from the MoO₄²⁻ groups themselves. The G(II) emission band located at 2.5 eV is observed only in the crystals, containing the isolated oxygen vacancies — WO₃ groups. This emission appears at T>160 K under excitation around 4.07 eV as a result of the photo-thermally stimulated disintegration of localized exciton states and subsequent recombination of the produced electron and hole centres near WO₃ groups. The G(II) emission accompanies also thermally stimulated recombination processes in PbWO₄ crystals above 150 K. Mainly the G(II) emission is responsible for the slow decay of the green luminescence in PbWO₄ crystals.