Synthesis of a New Polyoxometalate Loaded Stearic Acid Nanoparticles

The stearic acid nanoparticles loaded polyoxometalate K6[γ-(CpTi)2SiW10O38][(CpTi)2SiW10] have been prepared and structurally characterized by elemental analysis, IR spectra.The particle size was estimated by transition electron microscope and zatesizer instrument. The result showed that the polyoxometalate retained the parent structure after encapsulation by stearic acid nanoparticles.     

Ionothermal Synthesis and Characterization of Two Polyoxometalate-based Supramolecules

Two novel 3D supramolecular architectures with hexamolybdate and phosphotungstate anions were synthesized under ionothermal conditions. The structures were named as[Cu^I(L1)₂]₂L2[Mo₆O₁₉](1) and[Cu^I(L3)₂]_2.5· H_0.5[PW₁₂O₄₀]·H₂O(2)(L1=2,2'-bipyridine, L2=4,4'-bipyridine, L3=2,2'-biimidazole) and characterized via Fourier transform infrared spectroscopy(FTIR) and FT-Raman spectroscopy analyses. Single-crystal X-ray diffraction analysis revealed that the two compounds crystallized in the space group P and were constructed through hydrogen bonding.     

溶剂热法制备无皂PMMA纳米粒子

用溶剂热法制备无皂聚甲基丙烯酸甲酯(PMMA)纳米粒子,讨论了温度和丙酮含量对粒子粒径和分散度的影响,用DTA,^1HNMR,TEM,GPC等对产物进行了表征。结果表明无皂PMMA纳米粒子的粒径约60衄,分子量分布较好、以间同结构为主;随着反应温度增高,PMMA的玻璃化温度增加,间同结构含量有所增大,纳米粒子的粒径逐渐减小,粒径分布变差;溶剂中丙酮含量增加时,粒径逐渐减小,粒径的分布变差。     

轮型多金属氧酸盐复合物膜的制备及在检测亚硝酸盐中的应用

利用自组装和电沉积交替的方法制备了基于磷钨酸盐K₂₈Li₅H₇P₈W₄₈O₁₈₄·92H₂O(P₈W₄₈)、 碳纳米管和Ni纳米颗粒的复合膜电极, 用于NO₂^- 的检测. 由于复合膜中P₈W₄₈, CNTs和Ni纳米颗粒3种活性成分的协同作用, 所制备的传感器表现出低的检出限、 宽的线性范围和较高的选择性. 将该传感器用于检测果汁中的NO₂^- , 所得到的回收率在允许的误差范围内. 这种复合膜电极传感器有望在实际应用中高度灵敏地检测NO₂^- .     

Polyoxometalate-based eight-connected self-catenated network and fivefold interpenetrating framework

Two entangled compounds [(bpy)₆Cu^I₆Cl₃(Mo^VW₅O₁₉)] (1) and [(bpy)₇Cu^I₇Cl₂(BW₁₂O₄₀)]·H₂O (2) (bpy=4,4′-bipyridine), have been successfully synthesized under hydrothermal conditions and characterized by element analysis, IR spectroscopy, thermal gravimetric analysis, X-ray photoelectron spectroscopy, and single crystal X-ray diffraction analyses. Compound 1 represents the first eight-connected self-penetrating network constructed from cuprous chloride clusters [Cu₆Cl₃] and Lindquist-type polyoxoanions. Compound 2 exhibits an interesting fivefold interpenetrating network consisting of Keggin polyoxoanions and Cu⁺-metal-organic framework. Crystal data of the two compounds are following: 1, triclinic, , a=11.502(2) Å, b=13.069(3) Å, c=13.296(3) Å, α=90.55(3)°, β=113.74(3)°, γ=110.48(3)°, Z=1; 2, triclinic, , a=12.341(3) Å, b=13.119(3) Å, c=15.367(3) Å, α=99.12(3)°, β=90.53(3)°, γ=104.49(3)°, Z=1.     

基于水溶性多金属氧酸盐的光催化燃料电池

以水溶性多金属氧酸盐作为光催化剂和电子载体构建了一种新型光催化燃料电池.该光催化燃料电池发生燃料的均相光催化降解反应,可实现在无光照情况下的持续放电.使用生物柴油副产物甘油作为燃料时,该光催化燃料电池的输出功率达0.24 m W/cm~2.在持续光照条件下,电池可长时间运转近50 h,电流稳定在0.75 m A/cm~2以上.甘油在电池中可持续循环放电,根据实际的反应程度可被转化为醛和酸,进一步氧化得到COx.对多种有机燃料的应用表明该光催化燃料电池具有广泛的适用性.     

PhO2阳极在硫酸铬电解氧化制备重铬酸时的电极行为

二氧化铅电极;PhO2阳极在硫酸铬电解氧化制备重铬酸时的电极行为     

Preparation of Gold Nanoparticles Protected with Polyelectrolyte

Gold nanoparticles were synthesized through the reduction of tetrachlorauric acid (HAuCh) by NaBH4, with polyethyleneimine(PEI) as stabilizer. The nanoparticles were characterized by UV-vis spectroscopy and atomic force microscopy(AFM).     

纳米氧化镍的固相合成

纳米氧化镍的固相合成;NiO;纳米粒子;固相反应;合成机理     

ATO纳米粉体的燃烧合成研究

锑掺杂氧化锡(Antimony鄄dopedtinoxideATO)是一种新型多功能材料,具有耐高温、耐腐蚀、机械稳定性好的特点而被广泛应用。作为新型导电填料,可用于材料的抗静电,其效果优于传统的碳黑、金属粉体,表面活性剂等,性价比高于最近提出的碳纳米管导电材料。用于电致变色材料可以替代     

W/O型微乳液中不同形貌PbS纳米粒子的制备及其形成机理的探讨

用聚乙二醇辛基苯基醚(OP)/异辛醇/环己烷/水溶液所形成的微乳液体系控制合成出了PbS纳米粒子，考察了微乳液中水与表面活性剂的物质的量的比(ω₀)、反应物浓度及浓度比、陈化时间等条件对产物形貌的影响。采用透射电子显微镜(TEM)、X-射线衍射(XRD)分别对产物的结构、粒度和形貌进行了表征。结果表明，在微乳液体系中，控制不同的实验条件，可以成功地合成球形、梭形、针状和棒状的PbS纳米粒子，并且粒径分布集中，无团聚现象。论文还对不同形貌PbS纳米粒子的形成机理进行了探讨。     

A New Method for the Synthesis of Selenium Nanoparticles and the Application to Construction of H_2O_2 Biosensor

To date the most popular biosensor reported in the literature are those employing redox enzymes coupled with amperometric detection. For the construction of this kind of biosensors, a general, broadly applicable method for enzyme immobilization still needs to be discovered. One of recent trends is based on the use of new carriers, such as nanosized particles1,2. Amorphous selenium nanoparticles (SN) are demonstrated not only unique photoelectric, semiconducting and X-ray-sensing properties,…     

用聚丙烯酰胺微波高压合成金纳米粒子

金纳米粒子;光谱性质;用聚丙烯酰胺微波高压合成金纳米粒子     

油溶性Cu纳米颗粒的两相法制备

在四氢呋喃-饱和氯化钠水溶液的两相体系中利用两相法化学合成了双正十六烷氧基二硫代磷酸(DDP)表面修饰的Cu纳米颗粒. 系统探讨了不同因素对制备Cu纳米颗粒的影响, 并采用透射电子显微镜(TEM)比较分析不同还原剂的用量、Cu^2＋浓度、修饰剂双正十六烷氧基二硫代磷酸铵盐(ADDP)和Cu^2＋的物质的量之比对Cu纳米颗粒粒径及分布的影响; 通过红外光谱仪(IR)、X射线粉末衍射仪(XRD)、X射线光电子能谱仪(XPS)等测试技术对优化条件下所合成的铜纳米颗粒进行了结构表征. 结果表明, 合成粒径细小、分布均匀的铜纳米颗粒的工艺条件为pH值在12左右, 反应温度高于30 ℃, 铜离子浓度小于0.05 mol•L^－1, NaBH₄与Cu^2＋的物质的量之比在8∶1到12∶1之间, ADDP和Cu^2＋的物质的量之比为2∶1和2.5∶1; 所制备的铜纳米颗粒是由无定形的金属Cu无机纳米核及通过化学键键合在其表面的DDP分子所组成, 并且修饰剂在反应前后结构没发生变化.     

油分散性氧化锌纳米微粒的制备及表征

采用直接沉淀法制备了异丁酸修饰纳米氧化锌微粒，用XRD、TEM、XPS、IR、UV-Vis、PL等检测手段对样品进行结构表征。结果表明：所制的样品为纤锌矿结构的氧化锌颗粒，粒度约为20 nm，异丁酸分子与表面锌原子以双齿螯合的形式结合。 Zn(II)2p_3/2的结合能与Zn的标准峰位相比，向低结合能方向移动了1.5 eV，其在可见光区比紫外区的荧光发射显著增强。分散性实验表明，样品在有机溶剂中有良好的分散性。     

超声辐射法制备与表征DDP修饰锡纳米微粒

金属纳米微粒因自身特殊的光、电、磁和热力学等性能而在催化、光电装置、信息存储以及润滑等领域中有着广阔的应用前景[1~5],因而制备具有特定性能的金属纳米微粒一直是纳米技术领域中的一个研究热点[6~8]。目前制备金属纳米微粒常用的方法主要包括物理法(机械粉碎[9]、气相沉     

纳米晶氧化锡的水热合成与表征

以水热法合成了高比表面积的纳米晶SnO_2粉体，运用FT-IR，XRD，BET，TEM 等手段对粉体的晶化过程进行了分析表征。FT-IR显示120 ℃水热得到的粉体即实 现水合锡化合物的晶化。XRD分析表明所得粉体均匀数纳米，且随水热温度的提高 ，晶粒长大。水热粉体均具有很高的比表面积。TEM显示粉体呈单分散状态。将水 热粉体进行热处理，粉体则长大较快，比表面积降低，分散性能出现反常改善。     

超声分散法制备Sn-Cd纳米微粒

用超声分散法制备了Sn-Cd纳米微粒,用XRD和TG/DTA研究了样品的晶型与结构,用TEM观察了样品的形貌,考察了超声功率对纳米颗粒粒径的影响,并在四球机上研究了样品的摩擦学性能.     

利用水引发固相反应方法合成氮化铝纳米粉

以AlCl3和Li3N为前驱物,利用过量Li3N与水反应大量放热现象,引发两种前驱物之间的固相反应合成了AlN纳米粉．X射线衍射分析、红外吸收光谱、透射电子显微镜以及X射线光电子能谱测试结果表明,利用这种新的合成方法制备的氮化铝主要是六方相,而且颗粒细小．另外,这种方法反应迅速、操作过程简便,有利于降低制备成本和扩大制备规模．     

脉冲激光制备发光碳纳米颗粒

利用毫秒脉冲激光辐照石墨悬浮液制备了超细碳纳米颗粒, 经过有机聚合物PEG 2000N的表面修饰, 碳纳米颗粒发出了较强的可见光, 并具有双光子激发的特征. 利用硫酸奎宁作参比, 测得碳纳米颗粒的荧光量子产率为6.3%. 石墨颗粒通过吸收激光能量快速升温并升华, 形成了大量的碳蒸气; 在周围液体介质的冷却下, 通过凝聚形成了碳纳米颗粒. 由于尺寸量子限制效应, 经过有机聚合物修饰后, 碳纳米颗粒表面产生了能量势阱, 导致了碳纳米颗粒的可见光发射. 发光的碳纳米颗粒具有无毒、化学惰性和良好的生物相容性, 在生物医药领域具有重要的应用价值.