Epitaxial growth of Sc-doped ZnO films on Si by sol-gel route

The epitaxial growth of doped ZnO films is of great technological importance. Present paper reports a detailed investigation of Sc-doped ZnO films grown on (1 0 0) silicon p-type substrates. The films were deposited by sol-gel technique using zinc acetate dihydrate as precursor, 2-methoxyethanol as solvent and monoethanolamine (MEA) as a stabilizer. Scandium was introduced as dopant in the solution by taking 0.5 wt%¹ of scandium nitrate hexahydrate. The effect of annealing on structural and photoluminescence properties of nano-textured Sc-doped films was investigated in the temperature range of 300-550 °C. Structural investigations were carried out using X-ray diffraction, scanning electron microscopy and atomic force microscopy. X-ray diffraction study revealed that highly c-axis oriented films with full-width half maximum of 0.21° are obtained at an annealing temperature of 400 °C. The SEM images of ZnO:Sc films have revealed that coalescence of ZnO grains occurs due to annealing. Ostwald ripening was found to be the dominant mass transport mechanism in the coalescence process. A surface roughness of 4.7 nm and packing density of 0.93 were observed for the films annealed at 400 °C. Room temperature photoluminescence (PL) measurements of ZnO:Sc films annealed at 400 °C showed ultraviolet peak at about (382 nm) with FWHM of 141 meV, which are comparable to those found in high-quality ZnO films. The films annealed below or above 400 °C exhibited green emission as well. The presence of green emission has been correlated with the structural changes due to annealing. Reflection high energy electron diffraction pattern confirmed the nearly epitaxial growth of the films.     

The effect of heat treatment on the physical properties of sol-gel derived ZnO thin films

Zinc oxide (ZnO) thin films were deposited on microscope glass substrates by sol-gel spin coating method. Zinc acetate (ZnAc) dehydrate was used as the starting salt material source. A homogeneous and stable solution was prepared by dissolving ZnAc in the solution of monoethanolamine (MEA). ZnO thin films were obtained after preheating the spin coated thin films at 250 °C for 5 min after each coating. The films, after the deposition of the eighth layer, were annealed in air at temperatures of 300 °C, 400 °C and 500 °C for 1 h. The effect of thermal annealing in air on the physical properties of the sol-gel derived ZnO thin films are studied. The powder and its thin film were characterized by X-ray diffractometer (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure (JCPDS 36-1451) and show the c-axis grain orientation. Increasing annealing temperature increased the c-axis orientation and the crystallite size of the film. The annealed films are highly transparent with average transmission exceeding 80% in the visible range (400-700 nm). The measured optical band gap values of the ZnO thin films were between 3.26 eV and 3.28 eV, which were in the range of band gap values of intrinsic ZnO (3.2-3.3 eV). SEM analysis of annealed thin films has shown a completely different surface morphology behavior.     

A study on the optical and electrical properties of direct-patternable ZnO films incorporated various contents of Pt nanoparticles

Platinum nanoparticles were synthesized by the methanol reduction method, and their size was controlled to 3 nm on average using PVP [poly(N-vinyl-2-pyrrolidon)] as a protecting unit. Various contents of Pt nanoparticles were incorporated into ZnO solutions which were synthesized by a sol-gel process. ZnO films with Pt nanoparticles of various content were annealed at 500 °C and 600 °C for 1 h. The crystallinity increased with the annealing temperature and also slightly with the content of Pt nanoparticles. The sheet resistance of ZnO films decreased with the incorporation of Pt nanoparticles, however the decreasing behavior was not maintained with increasing content of Pt nanoparticles. A shift of valence band maximum energy of ZnO film with Pt nanoparticles to higher energy was also observed due to electron transfer from Pt nanoparticles to ZnO film. The optical transmittance was 88 ± 2% in the visible region for all the ZnO films. Well-defined 60 μm wide direct-patterned ZnO films containing Pt nanoparticles of 0.5 atomic percent could be formed without using dry etching process.     

Effects of buffer layer annealing temperature on the structural and optical properties of hydrothermal grown ZnO

ZnO was deposited on bare Si(1 0 0), as-deposited, and annealed ZnO/Si(1 0 0) substrates by hydrothermal synthesis. The effects of a ZnO buffer layer and its thermal annealing on the properties of the ZnO deposited by hydrothermal synthesis were studied. The grain size and root mean square (RMS) roughness values of the ZnO buffer layer increased after thermal annealing of the buffer layer. The effect of buffer layer annealing temperature on the structural and optical properties was investigated by photoluminescence, X-ray diffraction, atomic force microscopy, and scanning electron microscopy. Hydrothermal grown ZnO deposited on ZnO/Si(1 0 0) annealed at 750 °C with the concentration of 0.3 M exhibits the best structural and optical properties.     

Influence of CH3COO on the room temperature photoluminescence of ZnO films prepared by CVD

ZnO films with strong c-axis-preferred orientation have been prepared by a single source chemical vapor deposition technique using zinc acetate as source material at the growth temperature of 230 °C. The strong UV and blue emissions were observed in the photoluminescence spectra of as-grown films. A small quantity of residual zinc acetate was reserved on the surface of as-grown ZnO films and the emission mechanism of blue luminescence was nearly related to the CH₃COO^- of unidentate type. The blue emission disappeared and the green emission appeared after annealing treatment. The green emission is related to the singly ionized oxygen vacancies.     

Investigation of p-type behavior in Ag-doped ZnO thin films by E-beam evaporation

Ag-doped ZnO (ZnO:Ag) thin films were grown on glass substrates by E-beam evaporation technique. The structural, electrical and optical properties of the films were investigated as a function of annealing temperature. The films were subjected to post annealing at different temperatures in the range of 350-650 °C in an air ambient. All the as grown and annealed films at temperature of 350 °C showed p-type conduction. The films lost p-type conduction after post annealing treatment temperature of above 350 °C, suggesting a narrow post annealing temperature window for the fabrication of p-type ZnO:Ag films. ZnO:Ag film annealed at 350 °C revealed lowest resistivity of 7.25 × 10⁻² Ω cm with hole concentration and mobility of 5.09 × 10¹⁹ cm⁻³ and 1.69 cm²/V s, respectively. Observation of a free-to-neutral-acceptor (e,A^o) and donor-acceptor-pair (DAP) emissions in the low temperature photoluminescence measurement confirms p-type conduction in the ZnO:Ag films.     

Effect of annealing temperature on photocatalytic activity of ZnO thin films prepared by sol-gel method

Zinc oxide thin films are deposited on Si and quartz substrates using the sol-gel method. The thin films, annealed at 400, 600 and 800 °C respectively, are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), ultraviolet-visible spectrophotometer (UV-Vis), fluorescence spectrometer (FL) and the photocatalytic activity is tested by the decomposition of methyl orange dye under UV illumination. The results show that the mean grain size, surface-to-volume ratio, rms roughness and degradation efficiency of the thin films increases with increasing annealing temperature. In particular, ZnO thin film annealed at 800 °C exhibits the highest photocatalytic activity, degrading methyl orange by almost 88% in 180 min. Photocatalytic reaction mechanism of the ZnO thin films is discussed in detail, and the oxygen defects are proposed to be the active sites of the ZnO photocatalyst.     

The structural and optical properties of ZnO/Si thin films by RTA treatments

ZnO/Si thin films were prepared by rf magnetron sputtering method and some of the samples were treated by rapid thermal annealing (RTA) process at different temperatures ranging from 400 to 800 °C. The effects of RTA treatment on the structural properties were studied by using X-ray diffraction and atomic force microscopy while optical properties were studied by the photoluminescence measurements. It is observed that the ZnO film annealed at 600 °C reveals the strongest UV emission intensity and narrowest full width at half maximum among the temperature ranges studied. The enhanced UV emission from the film annealed at 600 °C is attributed to the improved crystalline quality of ZnO film due to the effective relaxation of residual compressive stress and achieving maximum grain size.     

Influence of annealing temperature on structural and optical properties of ZnO: In thin films prepared by ultrasonic spray technique

Transparent conducting indium doped zinc oxide was deposited on glass substrate by ultrasonic spray method. The In doped ZnO samples with indium concentration of 3 wt.% were deposited at 300, 350 and 400 °C with 2 min of deposition time. The effects of substrate temperature and annealing temperature on the structural, electrical and optical properties were examined. The DRX analyses indicated that In doped ZnO films have polycrystalline nature and hexagonal wurtzite structure with (0 0 2) preferential orientation and the maximum average crystallite size of ZnO: In before and annealed at 500 °C were 45.78 and 55.47 nm at a substrate temperature of 350 °C. The crystallinity of the thin films increased by increasing the substrate temperature up 350 °C, the crystallinity improved after annealing temperature at 500 °C. The film annealed at 500 °C and deposited at 350 °C show lower absorption within the visible wavelength region. The band gap energy increased from E_g = 3.25 to 3.36 eV for without annealing and annealed films at 500 °C, respectively, indicating that the increase in the transition tail width. This is due to the increase in the electrical conductivity of the films after annealing temperature.     

Photoluminescence of ZnO nanowires dependent on O2 and Ar annealing

High-purity ZnO nanowires have been synthesized on Si substrates without the presence of a catalyst at 600 °C by a simple thermal vapor technique. Photoluminescence (PL) spectra of the annealed samples at 900 °C under oxygen and argon gases have been investigated. After O₂ or Ar annealing, the PL visible-emission intensity that is related to intrinsic defects (oxygen vacancies) is greatly reduced compared with as-grown ZnO nanowires because the oxygen-gas ions or oxygen interstitials diffuse into the oxygen vacancies during annealing process. The blue-band peak of the O₂- or Ar-annealed ZnO naonowires is also smaller than the green-band peak in the visible broadband because of the reduction of oxygen vacancies. Therefore, the main intrinsic defects (oxygen vacancies) of as-grown ZnO nanowires can be reduced by O₂ or Ar annealing, which is an important procedure for the development of advanced optoelectronic ZnO nanowire devices.     

Effects of thermal annealing temperature and duration on hydrothermally grown ZnO nanorod arrays

In this study, the effects of thermal annealing temperature and duration on ZnO nanorod arrays fabricated by hydrothermal method were investigated. The annealed ZnO/Si(1 1 1) substrate was used for ZnO nanorod array growth. The effects of annealing treatment on the structural and optical properties were investigated by scanning electron microscopy, X-ray diffraction, and room-temperature photoluminescence measurements. With the annealing temperature of 750 °C and the annealing duration of 10 min, both the structural and optical properties of the ZnO nanorod arrays improved significantly, as indicated in the X-ray diffraction and photoluminescence measurement.     

Unidirectional variation of lattice constants of Al-N-codoped ZnO films by RF magnetron sputtering

Al-N-codoped ZnO films were fabricated by RF magnetron sputtering in the ambient of N₂ and O₂ on silicon (1 0 0) and homo-buffer layer, subsequently, annealed in O₂ at low pressure. X-ray diffraction (XRD) spectra show that as-grown and 600 °C annealed films grown by codoping method are prolonged along crystal c-axis. However, they are not prolonged in (0 0 1) plane vertical to c-axis. The films annealed at 800 °C are not prolonged in any directions. Codoping makes ZnO films unidirectional variation. X-ray photoelectron spectroscopy (XPS) shows that Al content hardly varies and N escapes with increasing annealing temperature from 600 °C to 800 °C.     

Post-annealing influence on properties of N-In codoped ZnO thin films prepared by ion beam enhanced deposition method

N-In codoped ZnO thin films were prepared by ion beam enhanced deposition method (IBED) and were annealed in nitrogen and oxygen ambient after deposition. The influence of post-annealing on structure, electrical and optical properties of thin films were investigated. As-deposited and all post-annealed samples showed preferential orientation along (0 0 2) plane. Electrical property studies indicated that the as-deposited ZnO film showed p-type with a sheet resistance of 67.5 kΩ. For ZnO films annealed in nitrogen with the annealing temperature increasing from 400 to 800 °C, the conduction type of the ZnO film changed from p-type to n-type. However, for samples annealed in oxygen the resistance increased sharply even at a low annealing temperature of 400 °C and the conduction type did not change. Room temperature PL spectra of samples annealed in N₂ and in O₂ showed UV peak located at 381 and 356 nm, respectively.     

Microstructural and surface property variations due to the amorphous region formed by thermal annealing in Al-doped ZnO thin films grown on n-Si (1 0 0) substrates

X-ray diffraction (XRD) patterns revealed that the as-grown and annealed Al-doped ZnO (AZO) films grown on the n-Si (1 0 0) substrates were polycrystalline. Transmission electron microscopy (TEM) images showed that bright-contrast regions existed in the grain boundary, and high-resolution TEM (HRTEM) images showed that the bright-contrast regions with an amorphous phase were embedded in the ZnO grains. While the surface roughness of the AZO film annealed at 800 °C became smoother, those of the AZO films annealed at 900 and 1000 °C became rougher. XRD patterns, TEM images, selected-area electron diffraction patterns, HRTEM images, and atomic force microscopy (AFM) images showed that the crystallinity in the AZO thin films grown on the n-Si (1 0 0) substrates was enhanced resulting from the release in the strain energy for the AZO thin films due to thermal annealing at 800 °C. XRD patterns and AFM images show that the crystallinity of the AZO thin films annealed at 1000 °C deteriorated due to the formation of the amorphous phase in the ZnO thin films.     

Rapid thermal annealing induced changes on the contact of Ni/Au to N-doped ZnO

N-doped p-type ZnO (p ∼ 10¹⁸cm^-3) was grown on sapphire(0 0 0 1) substrate by metal-organic chemical vapor deposition method. Ni/Au metal was evaporated on the ZnO film to form contacts. As-deposited contacts were rectifying while ohmic behavior was achieved after thermally annealing the contacts in nitrogen environment. Specific contact resistance was determined by circular transmission line method and a minimum specific contact resistance of 8 × 10⁻⁴ Ω cm² was obtained for the sample annealed at 650 °C for 30 s. However, Hall effect measurements indicate that, as the rapid thermal annealing temperature increased up to 550 °C or higher the samples’ conductive type have changed from p-type to n-type, which may be due to the instability nature of the present-day p-type N-doped ZnO or the dissociation of ZnO caused by annealing process in N₂ ambient. Evolution of the sample's electric characteristics and the increment of metal/semiconductor interface states induced by rapid thermal annealing process are supposed to be responsible for the improvement of electrical properties of Au/Ni/ZnO.     

The Al-doping and post-annealing treatment effects on the structural and optical properties of ZnO:Al thin films deposited on Si substrate

Al-doped ZnO (ZnO:Al) thin films with different Al contents were deposited on Si substrates using the radio frequency reactive magnetron sputtering technique. X-ray diffraction (XRD) measurements showed that the crystallinity of the films was promoted by appropriate Al content (0.75 wt.%). Then the ZnO:Al film with Al content of 0.75 wt.% was annealed in vacuum at different temperatures. XRD patterns revealed that the residual compressive stress decreased at higher annealing temperatures. While the surface roughness of the ZnO:Al film annealed at 300 °C became smoother, those of the ZnO:Al films annealed at 600 and 750 °C became rougher. The photoluminescence (PL) measurements at room temperature revealed a violet, two blue and a green emission. The origin of these emissions was discussed and the mechanism of violet and blue emission of ZnO:Al thin films were suggested. We concluded that the defect centers are mainly ascribed to antisite oxygen and interstitial Zn in annealed (in vacuum) ZnO:Al films.     

Structure and properties of ZnO films grown on Si substrates with low temperature buffer layers

Zinc oxide (ZnO) thin films were grown on Si (1 0 0) substrates by pulsed laser deposition (PLD) using two-step epitaxial growth method. Low temperature buffer layer (LTBL) was initially deposited in order to obtain high quality ZnO thin film; the as-deposited films were then annealed in air at 700 °C. The effects of LTBL and annealing treatment on the structural and luminescent properties of ZnO thin film were investigated. It was found that tensile strain was remarkably relaxed by employing LTBL and the band-gap redshifted, correspondingly. The shift value was larger than that calculated from band-gap theories. After annealing treatment, it was found that the annealing temperature with 700 °C has little influence on strains of ZnO films with LTBLs other than directly deposited film in our experiments. Interestingly, the different behaviors in terms of the shift of ultraviolet (UV) emission after annealing between films with and without buffer were observed, and a tentative explanation was given in this paper.     

Influence of annealing temperature on the structural, optical and mechanical properties of ALD-derived ZnO thin films

ZnO thin films grown on Si(1 1 1) substrates by using atomic layer deposition (ALD) were annealed at the temperatures ranging from 300 to 500 °C. The X-ray diffraction (XRD) results show that the annealed ZnO thin films are highly (0 0 2)-oriented, indicating a well ordered microstructure. The film surface examined by the atomic force microscopy (AFM), however, indicated that the roughness increases with increasing annealing temperature. The photoluminescence (PL) spectrum showed that the intensity of UV emission was strongest for films annealed at 500 °C. The mechanical properties of the resultant ZnO thin films investigated by nanoindentation reveal that the hardness decreases from 9.2 GPa to 7.2 GPa for films annealed at 300 °C and 500 °C, respectively. On the other hand, the Young's modulus for the former is 168.6 GPa as compared to a value of 139.5 GPa for the latter. Moreover, the relationship between the hardness and film grain size appear to follow closely with the Hall-Petch equation.     

Fuel additives and heat treatment effects on nanocrystalline zinc ferrite phase composition

Nanocrystalline ZnFe₂O₄ powder was prepared by the auto-combustion method using citric acid, acetic acid, carbamide and acrylic acid as fuel additives. Pure spinel zinc ferrite with the crystallite size of about 15 nm can be obtained by using acrylic acid as fuel additive. Samples prepared using other fuel additives contain ZnO impurities. In order to eliminate ZnO impurities, the sample prepared with citric acid as fuel additive was annealed at different temperatures up to 1000 °C in air and in argon. Annealed powders have pure ZnFe₂O₄ phase when annealing temperature is higher than 650 °C in air. Sample annealed at 650 °C in air is paramagnetic. However, annealed powders become a mixture of Fe₃O₄ and FeO after annealing at 1000 °C in argon atmosphere due to Zn volatility and the reduction reaction.     

Observation of ferromagnetism at room temperature for Cr ions implanted ZnO thin films

Single crystalline ZnO films were grown on c-plane GaN/sapphire (0 0 0 1) substrates by molecular beam epitaxy. Cr⁺ ions were implanted into the ZnO films with three different doses, i.e., 1 × 10¹⁴, 5 × 10¹⁵, and 3 × 10¹⁶ cm⁻². The implantation energy was 150 keV. Thermal treatment was carried out at 800 °C for 30 s in a rapid thermal annealing oven in flowing nitrogen. X-ray diffraction (XRD), atomic force microscopy, Raman measurements, transmission electron microscopy and superconducting quantum interference device were used to characterize the ZnO films. The results showed that thermal annealing relaxed the stress in the Cr⁺ ions implanted samples and the implantation-induced damage was partly recovered by means of the proper annealing treatment. Transmission electron microscopy measurements indicated that the first five monolayers of ZnO rotated an angle off the [0 0 0 1]-axis of the GaN in the interfacial layer. The magnetic-field dependence of magnetization of annealed ZnO:Cr showed ferromagnetic behavior at room temperature.