Physical properties of polycrystalline samples of CeCu_xGa_4−x (x = 0.2–1.4), crystallizing in the tetragonal BaAl₄-type structure (space group I 4/mmm), were studied by means of X-ray powder diffraction, magnetization, specific heat, electrical resistivity and magnetoresistivity measurements in wide temperature and magnetic fields ranges. The unit-cell volume of the system was found to decrease with increasing x (in total by about 4%) but the magnetic moments of Ce³⁺ ions remain localized in the whole x-range studied. The alloys exhibit ferromagnetic order at low temperatures, which manifests itself as distinct and relatively sharp anomalies in all the temperature characteristics measured. The ordering temperature decreases with increasing the Cu content from 5.5(1) K for x = 0.2 down to 1.35(5) K for x = 1.4, and the electrical transport properties of the system show some features characteristic of Kondo lattices.     

Structure and low-temperature properties of Ba8Ni6Ge40

Structural, magnetic, heat capacity, electrical and thermal transport properties are reported on polycrystalline Ba₈Ni₆Ge₄₀. Ba₈Ni₆Ge₄₀ crystallizes in a cubic type I clathrate structure with unit cell a=10.5179 (4) Å. It is diamagnetic with susceptibility χ_dia=−1.71×10^-6 emu/g Oe. An Einstein temperature 75 K and a Debye temperature 307 K are estimated from heat capacity data. It exhibits n-type conducting behavior below 300 K. It shows high Seebeck coefficients (−111×10^-6 V/K), low thermal conductivity (2.25 W/K m), and low electrical resistivity (8.8 mΩ cm) at 300 K.     

Magnetic and electronic properties of the antiferromagnetic YbFe4Al8 compound

The magnetic, electrical and electronic properties of the tetragonal ternary YbFe₄Al₈ compound have been investigated. This compound was supposed to be an antiferromagnetic superconductor due to the negative magnetization signal appearing at a low field of the field cooling mode, however, based on the measurements of the temperature dependence of magnetization and resistivity we do not confirm the presence of superconductivity in this material and we ascribe the negative magnetization to the complicated non-collinear magnetic structure. A switch to the antiferromagnetic order at about 150 K has been visible both on the M(T) and ρ(T) curves. The valence state of the Yb ions has been studied by X-ray photoemission spectroscopy. The valence band spectrum at the Fermi level exhibits the domination of the hybridized Yb(4f) and Fe(3d) states.     

Magnetic and thermodynamic properties of DyFe2Si2 further investigated with crystal-field theory and two-ion model

We report our theoretical studies on the magnetic and thermodynamic properties of DyFe₂Si₂ using the crystal-field parameters (CFPs) proposed by Chatterji et al. recently [1]. Our calculated magnetization and magnetic specific heat curves obtained with the above CFPs based on the two-ion model we developed recently show reasonable agreement with the experimental data.     

Temperature dependence of thermoelectric properties of Ni-doped CoSb3

Temperature dependences of the Hall coefficient, Hall mobility and thermoelectric properties of Ni-doped CoSb₃ have been characterized over the temperature range from 20 to 773 K. Ni-doped CoSb₃ is an n-type semiconductor and the conduction type changes from n-type to p-type at around 450 K. The temperature for the transition from n-type to p-type increased with increasing Ni content x. The Seebeck coefficient reaches a maximum value near the transition temperature. The electrical resistivity indicates that Co_1−xNi_xSb₃ is a typical semiconductor when x≤0.03 and a degenerate semiconductor when x>0.03. Thermal conductivity analyses show that the lattice component is predominant at lower temperatures and carrier and bipolar components become large at temperatures higher than the transition temperature. The thermoelectric figure of merit reaches a maximum value close to the transition temperature and the largest value, 4.67×10⁻⁴ K⁻¹ at 600 K, was obtained for x=0.05.     

Magnetic properties for the Cu2MnSnSe4 and Cu2FeSnSe4 compounds

Magnetic susceptibility χ measurements in the range from 2 to 300 K were carried out on samples of the Cu₂FeSnSe₄ and Cu₂MnSnSe₄ compounds. It was found that Cu₂FeSnSe₄ was antiferromagnetic showing ideal Curie-Weiss behavior with a Néel temperature T_N of about 19 K and Curie-Weiss temperature θ=−200 K, while for Cu₂MnSnSe₄ the behavior was spin-glass with a freezing temperature T_f of about 22 K and Curie-Weiss temperature θ=−25 K. The spin-glass order parameter q(T), determined from the susceptibility data, was found to be in agreement with the prediction of conventional spin-glass theory.     

Orbital fluctuations and orbital order in FeCr2S4

Heat-capacity investigations on the ferrimagnetic spinel FeCr₂S₄ poly- and single crystals provide experimental evidence of orbital liquid and orbital glass states. The low-temperature transition in the polycrystals at 10 K arises from orbital order and is very sensitive to the sample stoichiometry. In the single crystals the orbital order is fully suppressed resulting in an orbital glass state with the heat capacity following a strict T² dependence towards zero temperature. At elevated temperatures, FeCr₂S₄ exhibits an unexpected large linear term of about 100 mJ mol⁻¹ K⁻² as the fingerprint of the orbital liquid.     

Determination of the crystal structure of U6Fe5Al8Si9 by electron crystallography

The crystal structure of U₆Fe₅Al₈Si₉ was re-determined by electron crystallography, using selected area electron diffraction (SAED) and high resolution (HRTEM) images, taken along the [0 0 1] direction. The obtained results are very similar to those found previously by X-ray powder diffraction. The differences between the atomic positions found by SAED and HRTEM images and those found by X-ray powder diffraction were 0.11 and 0.08 Å, respectively.     

Neutron and X-ray diffraction studies on the Tb2Ni3Si5 single crystal

Neutron and X-ray diffraction studies on the Tb₂Ni₃Si₅ single crystal have been done to investigate its crystal modulation and magnetic properties. The modulated single crystal is constructed by the TbNiSi₂ (CeNiSi₂-type Cmcm) and the Tb₂Ni₃Si₅ (U₂Co₃Si₅-type Ibam) lattices. The relationship between the two lattices is described as direction of the b₁₁₂-axis coincides with the a₂₃₅-axis. The crystal modulation gives significant effects on magnetism. Each of the two lattices takes complex antiferromagnetism with multiplex propagation vectors.     

The unusual magnetic and electronic properties of Gd0.5Ba0.5CoO2.9

Magnetic and electrical properties of well-characterized Gd_0.5Ba_0.5CoO_2.9 have been studied carefully in order to compare them with those of other analogous cobaltates of the type Ln_0.5A_0.5CoO₃ (Ln=La, Nd and A=Sr, Ba) which are ferromagnetic. The results show that Gd_0.5Ba_0.5CoO_2.9, which has A-site cation ordering at room temperature, does not become a genuine ferromagnet at low temperatures, but the ferromagnetic interactions observed at 280 K give over to an antiferromagnetic (AFM) state on cooling to 230 K. The AFM state is rendered ferromagnetic on the application of high magnetic fields. The properties can be understood on the basis of phase separation induced by the large A-site cation-disorder, arising from the size mismatch.     

Antiferromagnetic phase transition in garnet-type AgCa2Co2V3O12 and AgCa2Ni2V3O12

Antiferromagnetic phase transition in two vanadium garnets AgCa₂Co₂V₃O₁₂ and AgCa₂Ni₂V₃O₁₂ has been found and investigated extensively. The heat capacity exhibits sharp peak due to the antiferromagnetic order with the Néel temperature T_N=6.39 K for AgCa₂Co₂V₃O₁₂ and 7.21 K for AgCa₂Ni₂V₃O₁₂, respectively. The magnetic susceptibilities exhibit broad maximum, and these T_N correspond to the inflection points of the magnetic susceptibility χ a little lower than T(χ_max). The magnetic entropy changes from zero to 20 K per mol Co²⁺ and Ni²⁺ ions are 5.31 J K⁻¹ mol-Co²⁺-ion⁻¹ and 6.85 J K⁻¹ mol-Ni²⁺-ion⁻¹, indicating S=1/2 for Co²⁺ ion and S=1 for Ni²⁺ ion. The magnetic susceptibility of AgCa₂Ni₂V₃O₁₂ shows the Curie-Weiss behavior between 20 and 350 K with the effective magnetic moment μ_eff=3.23 μ_B Ni²⁺-ion⁻¹ and the Weiss constant θ=−16.4 K (antiferromagnetic sign). Nevertheless, the simple Curie-Weiss law cannot be applicable for AgCa₂Co₂V₃O₁₂. The complex temperature dependence of magnetic susceptibility has been interpreted within the framework of Tanabe-Sugano energy diagram, which is analyzed on the basis of crystalline electric field. The ground state is the spin doublet state ²E(t₂⁶e) and the first excited state is spin quartet state ⁴T₁(t₂⁵e²) which locates extremely close to the ground state. The low spin state S=1/2 for Co²⁺ ion is verified experimentally at least below 20 K which is in agreement with the result of the heat capacity.     

Magnetic and transport properties of SmCoAsO1−xFx

A series of SmCoAsO_1−xF_x (with x=0, 0.05, 0.1, and 0.2) samples have been prepared by solid state reactions. X-ray powder diffraction proved that all samples can be indexed as a tetragonal ZrCuSiAs-type structure. A clear shrinkage of the lattice constants a and c with increasing F content indicated that F has been doped into the lattice. The magnetic and transport properties of the samples have been investigated. Parent SmCoAsO compound exhibited complicated magnetism including antiferromagnetism, ferromagnetism, and ferrimagnetism. For the fluorine doped samples, the antiferromagnetic Néel temperatures were almost independent of the F content and metamagnetic transitions were observed below antiferromagnetic Néel temperatures. With increasing F content, high temperature (below 142 K) ferrimagnetic state gradually changed to ferromagnetic state. In the resistivity result, metallic conduction in the region of 2-300 K and Fermi liquid behavior at low temperatures were shown in all samples. Transport properties at applied magnetic fields showed anomalies at low temperatures.     

Preparation and study of silver added La0.67Ca0.33MnO3 film

La_0.67Ca_0.33MnO₃ (LCMO) and Ag admixed La_0.67Ca_0.33MnO₃ (Ag-LCMO) polycrystalline films have been prepared on SrTiO₃ single crystal (100) substrates by ultrasonic spray pyrolysis technique. These films are characterized using XRD, SEM, and temperature dependence of resistivity (ρ-T) and ac susceptibility (χ-T). The films are having cubic structure with lattice parameters as 3.890 and 3.885 Å for LCMO and Ag-LCMO films, respectively. The peek in ρ-T curve (T_p) and the ferromagnetic transition temperature (T_C) for the Ag-LCMO film is higher than that of LCMO film. The stability of both the films was tested by repeated measurements of its characteristics over a period of one week after several thermal cycling from room temperature to 77 K. In the LCMO film, the peak in the ρ-T curve (T_p) is found to shift towards lower value and conduction noise of the film increases in the subsequent measurements. In the case of Ag-LCMO the value of T_p, T_C and conduction noise of the film did not change even after several measurements. Silver segregating at the grain boundaries in Ag-LCMO polycrystalline film seems to be responsible for improving the characteristics of Ag-LCMO films.     

Magnetic contribution to heat capacity and entropy of nickel ferrite (NiFe2O4)

The heat capacity of nickel ferrite was measured as a function of temperature from 50 to 1200 °C using a differential scanning calorimeter. A thermal anomaly was observed at 584.9 °C, the expected Curie temperature, T_C. The observed behavior was interpreted by recognizing the sum of three contributions: (1) lattice (vibrational), (2) a spin wave (magnetic) component and (3) a λ-transition (antiferromagnetic-paramagnetic transition) at the Curie temperature. The first was modeled using vibrational frequencies derived from an experimentally-based IR absorption spectrum, while the second was modeled using a spin wave analysis that provided a T^3/2 dependency in the low-temperature limit, but incorporated an exchange interaction between cation spins in the octahedral and tetrahedral sites at elevated temperatures, as first suggested by Grimes [15]. The λ-transition was fitted to an Inden-type model which consisted of two truncated power law series in dimensionless temperature (T/T_C). Exponential equality (m=n=7) was observed below and above T_C, indicating symmetry about the Curie temperature. Application of the methodology to existing heat capacity data for other transition metal ferrites (AFe₂O₄, A=Fe, Co) revealed nearly the same exponential equality, i.e., m=n=5.     

The effects of elements doping on transport and thermoelectric properties of Sr3Ti2O7

The Ruddlesden–Popper (RP) phase compounds (Sr_0.95R_0.05)₃Ti₂O₇ (R=Er, Y, Dy, Gd, Eu, Sm, Nd and La) were prepared, and their transport and thermoelectric properties were investigated. The results indicate that high-T electrical resistivity ρ (300 K<T<1000 K) increases monotonically with temperature and basically has a relation ρ∝T^M, with M varying from 0.91 to 1.92 at temperatures T>~650 K, suggesting acoustic phonon scattering is dominant. At low temperatures (5 K<T<300 K), ρ for (Sr_0.95R_0.05)₃Ti₂O₇ (R=Nd and La) decreases monotonously with decreasing temperature, whereas ρ for (Sr_0.95R_0.05)₃Ti₂O₇ (R=Er, Y, Dy, Gd, Eu and Sm) decreases first, and then increases instead as T decreases to a critical temperature T_c. Moreover, electrical conductivity σ∝T^1/2 holds at lower temperatures, indicating that the electron–electron interaction caused by the presence of disorder dominates the transport process at the low temperatures. Besides, experiments show that at T<~400 K the lattice thermal conductivity of the doped compounds basically decreases with increase of the atomic mass of dopants. Generally, the figure of merit (ZT) at 1000 K increases first, and then decreases with the increase of the dopants' ionic radius, and the largest ZT is achieved in (Sr_0.95Gd_0.05)₃Ti₂O₇ mainly owing to its lower lattice thermal conductivity.     

Selected properties of EuCo2(Si1−xGex)2 alloys

EuCo₂(Si_1−xGe_x)₂, x=0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1 samples were synthesised by induction melting followed by annealing at 900 °C and rapid quenching. X-ray powder diffraction and Auger electron spectroscopy studies revealed that solid solutions are formed only for x?0.2 and x?0.7. Magnetic susceptibility investigations for the solid solutions revealed a dominant divalent europium valence state in the germanium-rich samples and a dominant trivalent europium component in the silicon-rich samples. In the germanium-rich samples, a long-range antiferromagnetic ordering was observed. In all samples studied, additional magnetic transitions at various temperatures were detected, which could be attributed to small clusters containing different europium chemical surrounding from that in the predominant phase.     

Study of magnetotransport in double-layered La1.4Ca1.6Mn2O7 manganite: Presence of nano-ferromagnetic domains in paramagnetic matrix

Double-layered manganite La_1.4Ca_1.6Mn₂O₇ has been synthesized using the solid-state reaction method. It had a metal-to-insulator transition at temperature T_M1≈127 K. The temperature dependence of ac susceptibility showed a broad ferromagnetic transition. The two-dimensional (2D)-ferromagnetic ordering temperature (T_C2) was observed as ≈245 K. The temperature dependence of its low-field magnetoresistance has been studied. The low-field magnetoresistance of double-layered manganite, in the temperature regions between T_M1 and T_C2, has been found to follow 1/T⁵. The observed behaviour of temperature dependence of resistivity and low-field magnetoresistance has been explained in terms of two-phase model where ferromagnetic domains exist in the matrix of paramagnetic regions in which spin-dependent tunneling of charge carriers occurs between the ferromagnetic correlated regions. Based on the two-phase model, the dimension of these ferromagnetic domains inside the paramagnetic matrix has been estimated as ∼12 Å.     

On the power-law behavior of the AC conductivity of the mixed crystal (NH4)3H(SO4)1.42(SeO4)0.58

A power law used to describe the AC conductivity from 299 to 393 K of the mixed crystal (NH₄)₃H(SO₄)_1.42(SeO₄)_0.58 led to fractional exponent values ranging from 1.08 to 0.91, depending on structural changes induced on temperature variation [B. Louati, M. Gargouri, K. Guidara and T. Mhiri, J. Phys. Chem. Solids 66 (2005) 762]. In the present note, we suggest that the fractional law exhibits features of lattice relaxation. Despite the structural changes, the parameters of the power law are mutually interconnected to yield a temperature independent phenomenon. Such behavior is probably of general validity and characterizes the universal fractional dispersion of the AC conductivity, as it was also observed in glasses of different composition.     

Study of the structural, dielectric and magnetic properties of Bi2O3 and PbO addition on BiFeO3 ceramic matrix

In this paper we studied the effects of Bi₂O₃ and PbO addition on BiFeO₃ (BFO) ceramic matrix. The structural, dielectric and magnetic properties of fifteen BFO samples were discussed in view of possible applications in RF and microwave devices. The present work also reports the preparation of the samples. Polyvinyl alcohol (PVA) and tetraethyl orthosilicate (TEOS) were also added as a binder in the fabrication procedure. The samples have been studied by X-ray powder diffraction (XRD), scanning electron microscopy (SEM) and magnetic hysteresis measurements. Further, a study based on impedance spectroscopy also has been done. Dielectric permittivity (ε′) and dielectric loss (tan δ) were measured at room temperature in the frequency range 100 Hz-10 MHz, as well as a.c. conductivity. The -Im[Z(f)] versus Re[Z(f)] plot has been obtained. The samples were investigated in view of possible applications like miniaturized filters, diplexers and dielectric resonator antennas (DRA). In the RF and MW frequency region, the application of magneto-dielectric and multiferroic perovskite composite materials is desirable for the miniaturization of components.     

Kondo behaviour of the solid solution (Ce1−xLax)PtGa

The solid solution (Ce_1−xLa_x)PtGa has been studied through X-ray diffraction, magnetization (σ(B)), magnetic susceptibility (χ(T)), electrical resistivity (ρ(T)), magnetoresistivity (MR) and heat capacity (C_P(T)) measurements. The Néel temperature (T_N=3.3 K) for CePtGa is lowered upon La substitution as observed from χ(T) and ρ(T) measurements. The Kondo temperature T_K as calculated from MR measurements is comparable to T_N and also decreases with La substitution. The volume dependence of T_K is in accordance with the compressible Kondo lattice model and a Doniach diagram of the results is presented. C_P(T) measurements are presented for CePtGa, Ce_0.2La_0.8PtGa and LaPtGa and the results are discussed in terms of the electronic and magnetic properties. Other features of interest are anomalies in ρ(T) and C_P(T) due to crystalline electric field effects and metamagnetism as observed in σ(B) studies for samples with 0≤x≤ 0.3.