Synthesis and characterization of a bis‐(4‐trifluoromethanesulfonyloxyphenyl)phenylamine monomer and its polymer for light‐emitting applications

This study focuses on the preparation, polymerization, characterization, and optical properties of a new bis‐(4‐trifluoromethanesulfonyloxyphenyl)phenylamine monomer. This is the first nitrogen‐containing monomer having nitrogen atoms as bridges between phenyl rings, and it was synthesized in three steps. The polymerization was carried out through the Ni(0)‐catalyzed homocoupling reaction of the bis‐(4‐trifluoromethanesulfonyloxyphenyl)phenylamine compound. The resulting polymer, polybis(paraphenyl)phenylamine, emitted an intense blue color (where λ = 415 nm) upon irradiation by ultraviolet light. The photoluminescence quantum yield was found to be 36% with a long excited‐state lifetime of 3.3 ns. Electrical conductivity data for an HCl‐doped film of the polymer were also examined. This novel polymer is of interest as an organic emitting material for electroluminescent devices. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1860–1867, 2007     

Side‐chain liquid crystalline polyacrylates containing 3,4‐disubstituted pyrrole moiety

Polymerization of liquid crystalline bifunctional monomer N‐{{ω‐{4‐[4‐(11‐acryloyloxy)undecanoxybenzoyl]biphenyleneoxy} alkyl}}‐3,4‐dimethylpyrrole gave a side‐chain liquid crystalline polyacrylate containing 3,4‐dimethylpyrrole group. Liquid crystallinity was determined by DSC and optical polarizing microscope measurements. The monomers having pentylene, hexylene, and decylene as the alkylene spacer group between the mesogenic unit and the 3,4‐dimethylpyrrole group exhibited smectic and nematic phases on the heating and cooling stages. The radically polymerized polyacrylate derivatives containing the 3,4‐dimethylpyrrole group showed nematic phases on the heating and cooling stages. These polymers are the first example of side‐chain liquid crystalline polymers containing 3,4‐dimethylpyrrole as functional group for further reaction. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1214–1221, 2000     

Synthesis and properties of soluble trifluoromethyl‐substituted polyimides containing laterally attached p‐Terphenyls

A new fluorinated diamine monomer, 2′,5′‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐p‐terphenyl, was synthesized from the chloro‐displacement of 2‐chloro‐5‐nitrobenzotrifluoride with the potassium phenolate of 2,5‐diphenylhydroquinone, followed by hydrazine palladium‐catalyzed reduction. A series of trifluoromethyl‐substituted polyimides containing flexible ether linkages and laterally attached side rods were synthesized from the diamine with various aromatic dianhydrides via a conventional two‐step process. The inherent viscosities of the poly(amic acid) precursors were 0.84–1.26 dL/g. All the polyimides afforded flexible and tough films. The use of 4,4′‐oxydiphthalic anhydride and 2,2′‐bis(3,4‐dicarboxyphenyl)hexafluoropropane dianhydride produced essentially colorless polyimide films. Most of the polyimides revealed an excellent solubility in many organic solvents. The glass‐transition temperatures of these polyimides were recorded between 254 and 299 °C by differential scanning calorimetry, and the softening temperatures of the polymer films stayed in the range of 253–300 °C according to thermomechanical analysis. The polyimides did not show significant decomposition before 500 °C in air or under nitrogen. These polyimides also showed low dielectric constants (2.83–3.34 at 1 MHz) and low moisture absorption (0.4–2.2%). For a comparative study, a series of analogous polyimides based on the nonfluorinated diamine 2′,5′‐bis(4‐aminophenoxy)‐p‐terphenyl were also prepared and characterized. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1255–1271, 2004     

High‐quality poly[2‐methoxy‐5‐(2′‐ethylhexyloxy)‐p‐phenylenevinylene] synthesized by a solid–liquid two‐phase reaction: Characterizations and electroluminescence properties

Poly[2‐methoxy‐5‐(2′‐ethylhexyloxy)‐p‐phenylenevinylene] (MEH‐PPV) with a molar mass of 26–47 × 10⁴ g mol^?1 and a polydispersity of 2.5–3.2 was synthesized by a liquid–solid two‐phase reaction. The liquid phase was tetrahydrofuran (THF) containing 1,4‐bis(chloromethyl)‐2‐methoxy‐5‐(2′‐ethylhexyloxy)benzene as the monomer and a certain amount of tetrabutylammonium bromide as a phase‐transfer catalyst. The solid phase consisted of potassium hydroxide particles with diameters smaller than 0.5 mm. The reaction was carried out at a low temperature of 0 °C and under nitrogen protection. No gelation was observed during the polymerization process, and the polymer was soluble in the usual organic solvents, such as chloroform, toluene, THF, and xylene. A polymer light‐emitting diode was fabricated with MEH‐PPV as an active luminescent layer. The device had an indium tin oxide/poly(3,4‐ethylenedioxylthiophene) (PEDOT)/MEH‐PPV/Ba/Al configuration. It showed a turn‐on voltage of 3.3 V, a luminescence intensity at 6.1 V of 550 cd/m², a luminescence efficiency of 0.43 cd/A, and a quantum efficiency of 0.57%. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3049–3054, 2004     

Aromatic oxadiazole‐based conjugated polymers with excited‐state intramolecular proton transfer: Their synthesis and sensing ability for explosive nitroaromatic compounds

Aromatic polyoxadiazole derivatives containing 9,9′‐dioctylfluorene were successfully synthesized via the Suzuki coupling reaction. The oxadiazole moiety in the polymer backbone was linked with the bis(hydroxyphenyl) group in its 2‐position to exhibit a large Stokes shift in the emission spectrum due to the excited‐state intramolecular proton transfer. To prepare the polymer via the Suzuki cross‐coupling reaction, the hydroxyl group in the monomer was protected with the t‐butoxycarbonyl group before polymerization and removed after polymerization to a desirable extent. The polymer with the free hydroxyl group showed a considerable sensitivity for nitroaromatic compounds, exhibiting fluorescence quenching in a chloroform solution. The interaction between the electron‐donating OH group and electron‐deficient nitroaromatic compounds seemed to play a decisive role in fluorescence quenching. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2059–2068, 2006     

Synthesis and properties of ortho‐linked aromatic polyimides based on 1,2‐bis(4‐aminophenoxy)‐4‐tert‐butylbenzene

A bis(ether amine) containing the ortho‐substituted phenylene unit and pendant tert‐butyl group, 1,2‐bis(4‐aminophenoxy)‐4‐tert‐butylbenzene, was synthesized and used as a monomer to prepare polyimides with six commercial dianhydrides via a conventional two‐stage procedure. The intermediate poly(amic acid)s had inherent viscosities of 0.78–1.44 dL/g, and most of them could be thermally converted into transparent, flexible, and tough polyimide films. The inherent viscosities of the resulting polyimides were in the range of 0.46–0.87 dL/g. All polyimides were noncrystalline, and most of them showed excellent solubility in polar organic solvents. The glass‐transition temperatures of these polyimides were in the range of 222–259 °C in differential scanning calorimetry and 212–282 °C in thermomechanicl analysis. These polyimides showed no appreciable decomposition up to 500 °C in thermogravimetric analysis in air or nitrogen. A comparative study of the properties with the corresponding polyimides without pendant tert‐butyl groups derived from 1,2‐bis(4‐aminophenoxy)benzene is also presented. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1551–1559, 2000     

Synthesis of a new class of triphenylamine‐containing poly(ether‐imide)s for electrochromic applications

A novel triphenylamine (TPA)‐containing bis(ether anhydride) monomer, namely 4,4′‐bis(3,4‐dicarboxyphenoxy)triphenylamine dianhydride, was synthesized and reacted with various aromatic diamines leading to a series of new poly(ether‐imide)s (PEI). Most of these PEIs were soluble in organic solvents and could be easily solution cast into flexible and strong films. The polymer films exhibited good thermal stability with glass‐transition temperatures in the range 211–299 °C. The polymer films exhibited reversible electrochemical processes and stable color changes (from transparent to navy blue) with high coloration efficiency and contrast ratio upon electro‐oxidation. During the electrochemical oxidation process, a crosslinked polymer structure was developed due to the coupling reaction between the TPA radical cation moieties in the polymer chains. These polymers can be used to fabricate electrochromic devices with high coloration efficiency, high redox stability, and fast response time. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 825–838     

Poly(arylene thioether) synthesis via nitro‐displacement reaction

High molecular weight poly(arylene thioether)s containing trifluoromethyl groups were prepared through the aromatic nucleophilic nitro‐displacement reaction of a dinitro monomer with aromatic dithiols. The high reactivity of the monomer, 4,4′‐dinitro‐3,3′‐bis(trifluoromethyl)biphenyl(1), activated by o‐trifluoromethyl groups and complete exclusion of oxygen was critical for the successful polymerization without any disulfide formation. The resulting trifluoromethylated poly(arylene thioether)s ( P1 and P2 ) were amorphous, dissolved in common organic solvents, and showed superior thermal properties compared to commercial poly(phenylene sulfide). © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2440–2447, 2006     

Kinetics,polymer molecular weights,and microstructure in zirconocene‐catalyzed 1‐hexene polymerization

1‐Hexene was polymerized by rac‐(dimethylsilyl)bis(4,5,6,7‐tetrahydro‐1‐indenyl)zirconium dichloride catalyst and methylaluminoxane cocatalyst over the temperature range 0–100 °C. The polymerization rate, polymer molecular weight, and polymer microstructure (stereospecificity and regiospecificity) were studied as a function of the temperature and the concentrations of monomer, catalyst, and cocatalyst. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 3802–3811, 2000     

Synthesis and properties of new aromatic poly‐(ether benzoxazole)s from 2,2′‐bis(4‐amino‐3‐hydroxyphenoxy)biphenyl and aromatic dicarboxylic acid chlorides

A new bis(o‐aminophenol) with a crank and twisted noncoplanar structure and ether linkages, 2,2′‐bis(4‐amino‐3‐hydroxyphenoxy)biphenyl, was synthesized by the reaction of 2‐benzyloxy‐4‐fluoronitrobenzene with biphenyl‐2,2′‐diol, followed by reduction. Biphenyl‐2,2′‐diyl‐containing aromatic poly(ether benzoxazole)s with inherent viscosities of 0.52–1.01 dL/g were obtained by a conventional two‐step procedure involving the polycondensation of the bis(o‐aminophenol) monomer with various aromatic dicarboxylic acid chlorides, yielding precursor poly(ether o‐hydroxyamide)s, and subsequent thermal cyclodehydration. These new aromatic poly(ether benzoxazole)s were soluble in methanesulfonic acid, and some of them dissolved in m‐cresol. The aromatic poly(ether benzoxazole)s had glass‐transition temperatures of 190–251 °C and were stable up to 380 °C in nitrogen, with 10% weight losses being recorded above 520 °C. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2656–2662, 2002     

Syntheses and properties of organosoluble poly(ether imide)s from 1,1‐bis[4‐(3,4‐dicarboxyphenoxy)phenyl]cyclohexane dianhydride and aromatic diamines

A bis(ether anhydride) monomer, 1,1‐bis[4‐(3,4‐dicarboxyphenoxy)phenyl]cyclohexane dianhydride ( IV‐A ), was synthesized from the nitro displacement of 4‐nitrophthalodinitrile by the phenoxide ion of 1,1‐bis(4‐hydroxyphenyl)cyclohexane ( I‐A ), followed by alkaline hydrolysis of the intermediate bis(ether dinitrile) and dehydration of the resulting bis(ether acid). A novel series of organosoluble poly(ether imide)s ( VI _a–i )(PEIs) bearing cyclohexylidene cardo groups was prepared from the bis(ether anhydride) IV‐A with various aromatic diamines V _a–i via a conventional two‐stage process. The PEIs had inherent viscosities in the range of 0.48–1.02 dL/g and afforded flexible and tough films by solution‐casting because of their good solubilities in organic solvents. Most PEIs showed yield points in the range of 89–102 MPa at stress‐strain curves and had tensile strengths of 78–103 MPa, elongations at breaks of 8–62%, and initial moduli of 1.8–2.2 GPa. The glass‐transition temperatures (T_g's) of these PEIs were recorded between 200–234 °C. Decomposition temperatures of 10% weight loss all occurred above 490 °C in both air and nitrogen atmospheres, and their residues were more than 43% at 800 °C in nitrogen atmosphere. The cyclohexane cardo‐based PEIs exhibited relatively higher T_g's, better solubilities in organic solvents, and better tensile properties as compared with the corresponding Ultem® PEI system. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 788–799, 2001     

Synthesis and characterization of soluble polyimides derived from 2,2′‐Bis(3,4‐dicarboxyphenoxy)‐9,9′‐spirobifluorene dianhydride

The synthesis of aromatic poly(ether imide)s containing spirobifluorene units in the polymer backbone is described. 2,2′‐Bis(3,4‐dicarboxyphenoxy)‐9,9′‐spirobifluorene dianhydride, which was used as a new monomer, was synthesized with 2,2′‐dihydroxy‐9,9′‐spirobifluorene as the starting material. In the spiro‐segment, the rings of the connected bifluorene were orthogonally arranged. This bis(ether anhydride) monomer was employed in reactions with a variety of aromatic diamines to furnish poly(ether imide)s, involving an initial ring‐opening polycondensation and subsequent chemically induced cyclodehydration. Excellent solubility in common organic solvents at room temperature, good optical transparency, and high thermal stability are the prominent characteristic features of these new polymers, which can be attributed to the presence of spiro‐fused orthogonal bifluorene segments along the polymer chain. The glass‐transition temperatures of the polyimides were 240–293 °C, and the 5% weight‐loss temperatures were greater than 500 °C. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 262–268, 2002     

Synthesis of hydrophilic sorbents from N‐vinylimidazole/divinylbenzene and the evaluation of their sorption properties in the solid‐phase extraction of polar compounds

This article reports the synthesis of N‐vinylimidazole/divinylbenzene resins by suspension polymerization. Several polymerization conditions were tested to achieve a quantitative incorporation of the N‐vinylimidazole monomer into the final polymer while a high specific surface area was maintained. The retention properties of several copolymers with different nitrogen contents were evaluated with the solid‐phase extraction of polar compounds from water samples, and the best results were obtained for a polymer containing 6.3% N with a surface area of 627 m² g^?1. The sorption properties of the resins were compared to those of styrene–divinylbenzene and other copolymers containing nitrogen, and the results were best for the new sorbents with N‐vinylimidazole as the polar monomer. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2019–2025, 2004     

Synthesis,one‐ and two‐photon properties of poly[9,10‐bis(3,4‐bis(2‐ethylhexyl‐oxy)phenyl)‐2,6‐anthracenevinylene‐alt‐N‐octyl‐3,6‐/2,7‐carbazolevinylene]

The synthesis, one‐ and two‐photon absorption (TPA) and emission properties of two novel 2,6‐anthracenevinylene‐based copolymers, poly[9,10‐bis(3,4‐bis(2‐ethylhexyloxy)phenyl)‐2,6‐anthracenevinylene‐alt‐N‐octyl‐3,6‐carbazolevinyl‐ene] ( P1 ) and poly[9,10‐bis(3,4‐bis(2‐ethylhexyloxy)phenyl)‐2,6‐anthracenevinyl‐ene‐alt‐N‐octyl‐2,7‐carbazolevinylene] ( P2 ) were reported. The as‐synthesized polymers have the number‐average molecular weights of 1.56 × 10⁴ for P1 and 1.85 × 10⁴ g mol^?1 for P2 and are readily soluble in common organic solvents. They emit strong bluish‐green one‐ and two‐photon excitation fluorescence in dilute toluene solution (? _P1 = 0.85, ? _P2 = 0.78, λ_em( P1 ) = 491 nm, λ_em( P2 ) = 483 nm). The maximal TPA cross‐sections of P1 and P2 measured by the two‐photon‐induced fluorescence method using femtosecond laser pulses in toluene are 840 and 490 GM per repeating unit, respectively, which are obviously larger than that (210 GM) of poly[9,10‐bis‐(3,4‐bis(2‐ethylhexyloxy) phenyl)‐2,6‐anthracenevinylene], indicating that the poly(2,6‐anthracenevinylene) derivatives with large TPA cross‐sections can be obtained by inserting electron‐donating moieties into the polymer backbone. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 463–470, 2010     

Synthesis and characterization of soluble polyimides derived from 2′,5′‐bis(3,4‐dicarboxyphenoxy)‐p‐terphenyl dianhydride

A novel bis(ether anhydride) monomer, 2′,5′‐bis(3,4‐dicarboxyphenoxy)‐p‐terphenyl dianhydride, was synthesized from the nitro displacement of 4‐nitrophthalonitrile by the phenoxide ion of 2′,5′‐dihydroxy‐p‐terphenyl, followed by alkaline hydrolysis of the intermediate bis(ether dinitrile) and cyclodehydration of the resulting bis(ether diacid). A series of new poly(ether imide)s bearing laterally attached p‐terphenyl groups were prepared from the bis(ether anhydride) with various aromatic diamines via a conventional two‐stage process that included ring‐opening polyaddition to form the poly(amic acid)s followed by thermal or chemical imidization to the poly(ether imide)s. The inherent viscosities of the poly(amic acid) precursors were in the range of 0.62–1.26 dL/g. Most of the poly(ether imide)s obtained from both routes were soluble in polar organic solvents, such as N,N‐dimethylacetamide. All the poly(ether imide)s could afford transparent, flexible, and strong films with high tensile strengths. The glass‐transition temperatures of these poly(ether imide)s were recorded as between 214 and 276 °C by DSC. The softening temperatures of all the poly(ether imide) films stayed in the 207–265 °C range according to thermomechanical analysis. For all the polymers significant decomposition did not occur below 500 °C in nitrogen or air atmosphere. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1008–1017, 2004     

Donor–acceptor‐structured naphtodithiophene‐based copolymers for organic thin‐film transistors

New donor–acceptor (D‐A) polymers, poly(4,5‐bis(2‐octyldodecyloxy)naphto[2,1‐b:3,4‐b']dithiophenebenzo[c][1,2,5]thiadiazole) (PNDT‐B) and poly(4,5‐bis(2‐octyldodecyloxy)naphto [2,1‐b:3,4‐b′]dithiophene‐4,7‐di(thiophen‐2‐yl)benzo[c][1,2,5]thiadiazole) (PNDT‐TBT), with the extended π‐electron delocalization of naphtho[2,1‐b:3,4‐b']dithiophene, were successfully synthesized by Suzuki and Stille coupling reactions. The structure and physical properties of polymers were characterized by DFT calculation, UV–vis absorption, cyclovoltammetry, TGA and DSC analyses. X‐ray diffraction studies indicated a relatively highly ordered intermolecular structure in PNDT‐TBT after annealing. This high degree of molecular order resulted from the crystallinity and increasing planarity, provided by the thiophene linker groups and the interdigitation of the long alkoxy side chains. The new D‐A polymer, PNDT‐TBT, exhibited a p‐type carrier mobility of 0.028 cm²/Vs and an on/off ratio of 5.9 × 10³. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 525–531     

Design,synthesis, and characterization of main‐chain,aromatic polyesters based on 3,4‐ethylenedioxythiophene

A series of new thermoplastic polyesters based on 3,4‐ethylenedioxythiophene (EDOT) with flexible aliphatic spacers have been synthesized and characterized for the first time. The thermal properties of these polyesters based on EDOT are comparable to those of conventional polyesters based on the 1,4‐phenyl unit, indicating that EDOT is a viable replacement for the phenyl units. The glass‐transition and melting‐transition temperatures decrease monotonically with an increase in the spacer length. Theoretical calculations have revealed that the core angle for EDOT is comparable to that of unsubstituted thiophene and hence should be compatible with the formation of the mesophase. This has been confirmed experimentally by the synthesis of a main‐chain, thermotropic, liquid‐crystalline polyester based on EDOT that exhibits fluid birefringence. In fact, this is the first report in which a main‐chain, liquid‐crystalline polymer based on 3,4‐disubstituted thiophene has been successfully designed and synthesized. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3479–3486, 2006     

Synthesis and characterization of main‐chain NLO oligomers and polymer that contain 4‐dialkylamino‐ 4′‐(alkylsulfonyl)azobenzene chromophores

An ω‐amino carboxylic acid monomer that contained a nonlinear optical (NLO) chromophore was prepared by a convergent synthesis. Strategies for selective protection/deprotection of the amino and carboxylic acid functionalities were developed. The protected monomer, 4‐[N‐(4‐benzyloxycarbonyl)butyl‐N‐methylamino]‐4′‐[2″,5″‐bis(decyloxy)‐4″‐(phthalimidomethyl)benzylsulfonyl]azobenzene, could be deprotected selectively or sequentially to give HOOC‐monomer‐N‐phthaloyl, benzyl‐OOC‐monomer‐NH₂, or HOOC‐monomer‐NH₂. Sequential synthesis was performed to yield main‐chain NLO dimers and tetramers. This was accomplished by selective deprotection and dicyclohexylcarbodiimide coupling. The HOOC‐monomer‐NH₂ was polymerized by treatment with diphenylphosphoryl azide to give a main‐chain NLO polyamide. The monomer, dimer, tetramer, and polymer NLO materials were characterized by ¹H, ¹³C, IR, and UV–visible spectroscopy as well as by gel permeation chromatography, differential scanning calorimetry, and elemental analysis. The NLO properties of these materials were measured. Thin films of the oligomers and polymer were prepared by spin casting on indium‐tin oxide coated glass. The second‐order NLO properties of the oligomers and polymer thin films were studied by in situ corona poling/second‐harmonic generation and attenuated total reflection methods. The optimal poling temperatures were significantly lower than the melting temperatures or glass‐transition temperatures of the oligomers and polymer. The poling efficiency increased in the following order: monomer, oligomers, and polymer. An electro‐optic coefficient of 4 pm/V at 1.06 μm was obtained for the polymer. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 546–559, 2000     

Synthesis of comb‐like polystyrene with poly(N‐phenyl maleimide‐alt‐p‐chloromethyl styrene) as macroinitiator

The copolymerization of N‐phenyl maleimide and p‐chloromethyl styrene via reversible addition–fragmentation chain transfer (RAFT) process with AIBN as initiator and 2‐(ethoxycarbonyl)prop‐2‐yl dithiobenzoate as RAFT agent produced copolymers with alternating structure, controlled molecular weights, and narrow molecular weight distributions. Using poly(N‐phenyl maleimide‐alt‐p‐chloromethyl styrene) as the macroinitiator for atom transfer radical polymerization of styrene in the presence of CuCl/2,2′‐bipyridine, well‐defined comb‐like polymers with one graft chain for every two monomer units of backbone polymer were obtained. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2069–2075, 2006     

Synthesis and characterization of aromatic cyclolinear phosphazene polyetherketones containing bis‐Spiro‐substituted cyclotriphosphazene unit

A novel monomer, 2,2‐bis‐(4′‐fluorobenzoylphenoxy)‐4,4,6,6‐bis[spiro‐(2′,2″‐dioxy‐1′, 1′‐biphenylyl)] cyclotriphosphazene, was synthesized and polymerized with 4,4′‐difluorobenzophenone as a comonomer and 4,4′‐isopropylidenediphenol or 4,4′‐(hexafluoroisopropylidene) diphenol in N,N‐dimethylacetamide at 162 °C for 4 h to give two series of aromatic cyclolinear phosphazene polyetherketones containing bis‐spiro‐substituted cyclotriphosphazene groups. The structure of the monomer was confirmed by ¹H, ¹³C, and ³¹P NMR. The effect of the incorporation of the bis‐spiro‐substituted cyclotriphosphazene group on the thermal properties of these polymers was investigated by DSC and thermogravimetric analysis. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2993–2997, 2001