Mn修饰Al2O3载体负载Pd催化剂及其蒽醌加氢催化性能

以活性氧化铝(γ-Al2O3)为载体,分别以Mn(NO3)2溶液和酸性氯化钯(PdCl2)溶液为修饰组分和活性组分前体,采用分步浸渍法制备了Mn修饰Al2O3载体负载钯催化剂。将催化剂应用于蒽醌加氢反应,考察了催化剂制备方法、活性组分负载量和催化剂还原温度对反应效果的影响。用XRD、BET、XPS和TPR对催化剂进行了表征。结果表明,催化剂活性受到制备方法的影响,在对Mn修饰Al2O3载体进行焙烧,Pd负载量0.2(wt)%、还原温度300℃的条件下,催化剂蒽醌加氢活性较高,较未修饰的催化剂提高了约16%。催化剂中Mn以MnO的形式存在,影响了γ-Al2O3的组织结构,使载体与活性组分之间的作用力增强,活性组分Pd高度分散在催化剂表面,从而提高了催化剂的活性。     

CuO/Mn2O3 /γ-Al2O3催化剂的制备、表征及其在CO氧化反应中的性能研究

采用浸渍法在γ-Al2O3载体上分步负载改性剂Mn2O3和活性组分CuO,制备了一系列不同配比的CuO/Mn2O3/γ-Al2O3催化剂,并运用CO+O2模型反应、XRF、XRD、H2-TPR、in-situ FTIR等手段表征了催化剂的活性和物理化学性质。活性测试结果表明,锰氧化物对γ-Al2O3载体的改性能有效地提高CuO/γ-Al2O3催化剂在CO+O2模型反应中的催化活性。XRD结果表明,锰氧化物对γ-Al2O3载体的改性可以促进氧化铜在载体表面的分散,从而提高了分散态氧化铜的含量,不过这与活性变化的趋势并不完全一致。进一步结合H2-TPR、in-situ FTIR表征结果 ,我们发现,分散态铜、锰氧化物的还原性质也是影响其催化活性的重要因素,催化剂中分散态铜、锰物种越容易被还原,其对CO+O2模型反应的催化活性就越高。     

Na-PtSnCe/γ-Al_2O_3丙烷脱氢催化剂的制备和催化性能

以γ-Al2O3为载体,采用连续等体积浸渍法,制备了一系列不同Na含量的Na-PtSnCe/γ-Al2O3催化剂,结合XRD、Py-IR、H2-TPR和TEM等手段对催化剂进行了表征,讨论了催化剂表面酸性及负载组分与载体之间的相互作用。采用微型催化反应装置考察了碱金属Na助剂含量和焙烧温度对负载型Na-PtSnCe/γ-Al2O3催化剂的丙烷脱氢反应性能的影响。结果表明,Na-PtSnCe/γ-Al2O3催化剂丙烷脱氢性能优于PtSnCe/γ-Al2O3催化剂,最佳Na含量为0.2%;适量Na助剂的添加可以降低催化剂的表面酸,增强催化剂中活性组分与载体之间的界面作用,提高催化反应的稳定性和选择性;550℃焙烧的Na-PtSnCe/γ-Al2O3催化剂,Pt组分与各助剂及载体之间的相互作用得到增强,催化剂具有最佳反应稳定性和最高丙烯选择性。     

带双键侧链的二氧化碳三元共聚物的合成及性能研究

二氧化碳和环氧丙烷共聚物的玻璃化温度处于35～40℃,在低于20℃的环境下脆性很大.在稀土三元催化剂Y(CCl3COO)3ZnEt2甘油(glycerine)下实现了CO2、环氧丙烷(PO)和烯丙基缩水甘油醚(AGE)的三元共聚,合成了侧链带双键的二氧化碳共聚物,其玻璃化温度(Tg)为-15.4～36.1℃,大幅度拓展了二氧化碳共聚物的低温区使用范围.     

以β-环糊精为介质的高分散钯催化剂的制备及其催化性能

 以β-环糊精(β-CD)为配体制备了Pd-β-CD胶体溶液,通过紫外-可见光谱和高倍透射电镜(HRTEM)等方法对其进行了表征,考察了胶体形貌并推测其络合方式. 将此胶体负载于氧化铝载体上制备了新型高分散钯催化剂Pd-β-CD/γ-Al2O3,采用红外光谱和HRTEM等表征方法考察了其活性中心的负载情况. 考察了催化剂对2-乙基蒽醌加氢反应的催化性能,并与浸渍焙烧法制备的PdO/γ-Al2O3催化剂进行了对比. 结果表明,以β-CD为介质制得的Pd-β-CD/γ-Al2O3催化剂的活性中心钯高分散在载体上,催化剂的活性更高,其氢化效率比PdO/γ-Al2O3高15.4%.     

多壁碳纳米管负载铂的甲苯加氢脱芳催化剂

以多壁碳纳米管(CNTs)为载体制备了负载型Pt催化剂Pt/CNTs并将其用于催化甲苯加氢脱芳(HDA)反应.结果表明,在1.0%Pt/CNTs催化剂上,在0.4MPa,373K,PhCH3/H2摩尔比=6/94和GHSV=120L/(h.g)的反应条件下,甲苯转化率可达100%,比反应速率为0.0523mmol/(s.m2),分别是γ-Al2O3和AC负载各自最佳Pt负载量催化剂1.4%Pt/γ-Al2O3和2.4%Pt/AC上相应值的1.17和1.18倍.甲苯加氢产物全部为甲基环己烷,其他可能的加氢产物均在气相色谱检测限以下.催化剂的表征研究揭示,用CNTs代替γ-Al2O3或AC作为载体并不会引起所负载Pt催化剂上甲苯HDA反应的表观活化能发生明显变化.与γ-Al2O3或AC负载的相应催化剂相比,一方面,CNTs负载的Pt催化剂易于在较低温度下还原活化,并且其工作态催化剂表面催化活性Pt物种(Pt0)所占表面Pt摩尔分率有所提高;另一方面,CNTs负载的Pt催化剂对H2具有较高的吸附/活化和储存能力.这些促进效应对催化剂HDA活性的提高都有重要贡献.     

HY/MCM-41/γ-Al2O3负载的硫化态Ni-Mo-P催化剂上萘的加氢

 采用水热法合成了不同SiO2/Al2O3比的MCM-41介孔分子筛. 并分别以HY/MCM-41/γ-Al2O3, HY/γ-Al2O3和γ-Al2O3为载体,用浸渍法制备了Mo-Ni-P催化剂. 以萘为模型化合物,考察了硫化态Mo-Ni-P催化剂的加氢活性. 结果表明,不同载体负载的催化剂催化活性均随着活性组分负载量的增大而提高,其中掺杂大比表面MCM-41的HY/MCM-41/γ-Al2O3所负载的催化剂催化活性提高幅度最大. 由于MCM-41与HY分子筛在酸性和孔结构上存在互补性,因而催化剂对萘加氢存在协同作用. 提出了萘加氢的反应机理,认为反应网络包括两个平行路径: 一是萘加氢生成四氢萘后发生异构化或开环反应; 二是萘加氢生成四氢萘后进一步加氢生成十氢萘,继而发生异构化或开环反应.     

PdCl2-CuCl2/Li-Al-O对CO低压气相合成碳酸二乙酯反应的催化性能

采用Li NO3对γ-Al2O3进行改性,制备了以多孔锂铝尖晶石为载体,以Pd为活性组分的PdCl2-CuCl2/Li-Al-O负载型催化剂,并考察了催化剂对CO低压气相合成碳酸二乙酯(DEC)反应的催化性能,探讨了载体Li/Al比、改性浸渍方法、不同改性金属、Pd负载量和反应压力等因素对催化剂催化性能的影响.结果表明,当n(Li)/n(Al)=0.2,压力为0.3 MPa和温度为110℃时,DEC的时空收率可达到418 g/(L.h).用Li NO3对γ-Al2O3改性后的催化剂载体表层具有Li Al5O8尖晶石结构,不同Li/Al比的催化剂载体的晶胞参数、晶胞体积略有不同.采用双金属改性的催化剂载体表面由于结晶度较低不能形成"完全尖晶石结构",其催化活性较低.随着催化剂表面活性组分PdCl2含量的增加,可有效提高产物DEC的时空收率;锂铝尖晶石载体表面的酸性较低,有利于提高目标产物DEC的选择性.     

Ni/SiO2-Al2O3催化剂在水相加氢体系中的活性及稳定性研究

采用浸渍法制备了不同Si含量的Ni/SiO2-Al2O3催化剂,通过吡啶-原位傅里叶变换红外(Py-FTIR)、X射线衍射(XRD)、低温N2物理吸附(N2Physisorption)、H2-程序升温还原(H2-TPR)等技术对催化剂进行了表征,并考察了催化剂在水相1,4-丁炔二醇加氢反应中的活性和稳定性.结果表明:SiO2的引入覆盖了部分γ-Al2O3表面,使暴露的Al3+减少,载体表现出部分SiO2的表面性质.随Si含量的增加,Ni/SiO2-Al2O3催化剂初始活性下降,产生这一现象的原因是引入SiO2使活性组分Ni与载体之间相互作用减弱,导致活性组分Ni迁移聚集,且催化剂的孔容和孔径减小.同时,SiO2显著抑制了γ-Al2O3的水合,催化剂的使用稳定性随Si含量的增加而提高.当Si含量为3%时,催化剂的初始活性下降幅度较小,且催化剂的水热稳定性显著提高,表现出最佳的反应性能.     

负载型铈基催化剂在NH3-SCR反应中的载体效应

近年来,氨-选择催化还原(NH3-SCR)技术被公认为是控制燃煤烟气和柴油车尾气氮氧化物(NOx)排放的最有效手段之一.V2O5-WO3/TiO2和V2O5-MoO3/TiO2催化剂在300–400°C范围内表现出优异的脱硝性能和抗H2O和SO2中毒性能,因而被广泛用于NH3-SCR过程.然而,钒基催化剂存在一些缺点,如氧化SO2到SO3的活性较高、高温下将部分NH3非选择性地氧化成N2O、V2O5具有生物毒性等.因此,非钒基脱硝催化剂的研制引起人们越来越多的关注.二氧化铈(CeO2)因具有氧化还原性能优异、储/释氧能力强和Ce3+/Ce4+转换容易等优点而广泛用于NH3-SCR反应.然而,单纯CeO2的脱硝性能并不理想.研究表明,将CeO2制备成铈基复合金属氧化物催化剂和负载型铈基催化剂可显著提高其在NH3-SCR反应中的催化性能.尤其是负载型铈基催化剂由于催化性能优异、比表面积大、热稳定性高及活性组分用量少而成为研究热点.众所周知,对于负载型金属氧化物催化剂,载体并不只是惰性材料,它会显著影响表面负载组分的物理化学性质和催化性能.因此,关于载体与组分间相互作用的研究常见诸报道.但是,对于负载型铈基催化剂,具有不同晶相结构的载体对其理化性质和NH3-SCR催化性能的影响规律尚不明晰.此外,SiO2,γ-Al2O3,ZrO2和TiO2是工业上常用的四种催化剂载体,它们具有不同的晶相结构和应用场合,究竟哪一个最适合作为负载型铈基催化剂的载体用于NH3-SCR反应尚无定论.因此,为了阐明负载型铈基催化剂在NH3-SCR反应中的载体效应,筛选出最佳的催化剂载体,我们首先采用溶胶-凝胶法和沉淀法合成了SiO2,γ-Al2O3,ZrO2和TiO2四个载体,再通过浸渍法制备了一系列负载型铈基催化剂(CeO2/SiO2,CeO2/γ-Al2O3,CeO2/ZrO2和CeO2/TiO2)用于NH3-SCR反应.并借助于X射线衍射(XRD)、拉曼光谱(Raman)、比表面积测定(BET)、X射线光电子能谱(XPS)、氢气-程序升温还原(H2-TPR)以及氨气-程序升温脱附(NH3-TPD)等表征手段对上述载体和催化剂进行了较为全面的分析.研究结果表明,这些负载型铈基催化剂的理化性质和脱硝性能强烈地依赖于催化剂载体.首先,CeO2/γ-Al2O3催化剂的表面Ce3+含量明显大于CeO2/SiO2,CeO2/ZrO2和CeO2/TiO2催化剂,有利于氧空位的产生以促进NO分子的解离,进而导致优异的NH3-SCR反应性能.其次,CeO2/γ-Al2O3催化剂具有最佳的还原性能,有利于NO氧化为NO2,进而通过"快速NH3-SCR"途径提升其催化性能.再者,CeO2/γ-Al2O3催化剂表面酸性位最多,能够促进反应物NH3分子的吸附与活化,从而提高脱硝性能.最后,CeO2/γ-Al2O3催化剂在H2O和SO2存在的条件下同样表现出最佳的催化性能,表明其有望用于实际燃煤烟气脱硝.     

稀土三元催化体系ZnO/SiO2负载化及季铵盐催化CO2与环氧丙烷合成高分子量聚碳酸酯

由环氧丙烷(PO)和CO2交替共聚合成脂肪族聚碳酸亚丙酯,CO2利用率高, 所得产物具有一定的力学性能和生物降解性能, 具有广泛应用前景. 目前, 用于CO2和环氧化合物共聚的催化体系主要包含锌、钴、镉、铬、铝和稀土等金属活性中心, 结构、活性各异的催化剂体系, 其催化性能和产物性能也各具特色. 其中, 稀土三元催化剂(ZnEt2-甘油-三氯乙酸钇)因合成聚碳酸酯产物的分子量高、碳酸酯单元含量高、聚醚及环碳酸酯副产物少的特点而受到关注. 但是由于催化剂催化效率低, 聚合时间长, 产品成本高, 使得工业化规模生产受到限制.本文基于稀土三元催化体系, 将催化剂负载于硅胶及锌改性硅胶, 优化了其制备条件, 同时考察了添加季铵盐对催化CO2/环氧丙烷共聚合成聚碳酸酯性能的影响. 结果表明, 在1 L聚合釜中, 于3.5 MPa和70 oC反应条件下, ZnO担载量及ZnO/SiO2添加量对反应性能均有影响. 当3 wt% ZnO/SiO2的添加量为5 g时, 稀土三元催化体系的活性为4845.2 g/molZn..所得聚合物经过多次纯化处理后, 能够有效提高材料的热学性能, 即有效除去产物中的ZnO对聚合物的热稳定性有重要作用. 添加含有不同阴离子(F- , Cl- 和Br- )的季铵盐可显著影响稀土三元催化剂的活性. 其中, 仅四甲基氟化铵可以明显提高反应活性乃至聚合物分子量. 在3 wt% ZnO/SiO2载体和四甲基氟化铵的协同作用下, 稀土三元催化体系的共聚性能明显提 升, 活性最高可达5223.0 g/molZn. 聚合物结构分析表明, 在载体和四甲基氟化铵存在下, 聚合物分子量明显提高, 可达到20万以上, 分子量分布明显变窄, 且聚合物结构如碳酸酯的单元含量、副产物含量以及聚合物产品玻璃化温度基本不变, 后者均保持在40-41 ?C. 基于此, 我们提出了在ZnO改性硅胶载体及四甲基氟化铵存在下稀土三元催化体系催化CO2/环氧丙烷共聚的反应机理: ZnO/SiO2载体有利于稀土三元催化体系的分散, 而四甲基氟化铵则有利于吸附在ZnEt2上的环氧丙烷开环.     

Copolymerization of carbon dioxide and propylene oxide under inorganic oxide supported rare earth ternary catalyst

Recently, rare earth ternary coordination catalyst represented as Y(CCl₃OO)₃‐Glycerin‐ZnEt₂ has been used for producing poly(propylene carbonate) (PPC, an alternating copolymer of carbon dioxide and propylene oxide) in industry scale, but its catalytic activity needs further improvement. One reason for the relatively low catalytic activity lied in that only 11.7% of active center was efficient due to possible embedding of active center in the heterogeneous catalyst. In this report, supporting strategy was developed, where Y(CCl₃OO)₃‐Glycerin‐ZnEt₂ was supported on various inorganic oxides. Two supporting methods were carried out. One way was to mix Y(CCl₃OO)₃‐Glycerin with inorganic oxide first and then ZnEt₂ was dropped to form the supported catalyst, and the other was to make Y(CCl₃OO)₃‐Glycerin‐ZnEt₂ at first and then mixing with inorganic oxides. The former showed decreasing catalytic activity compared with corresponding unsupported rare earth ternary catalyst, while an improvement of 16–36% in catalytic activity was realized in the latter. PPC with an average number molecular weight (M_n) of over 100 kg/mol and carbonate unit (CU) content of higher than 96% was prepared by both supported catalysts. The catalytic activity of the supported catalyst depended significantly on the supports, which increased in the following order: α‐Al₂O₃ < MgO < ZnO ≈ SiO₂ <γ‐Al₂O₃. γ‐Al₂O₃ was the best support for rare earth ternary catalyst, which showed a remarkable 36% increase in catalytic activity, corresponding to the utilization of 17% of active center. Although MgO supported catalyst gave only an 8% increase in catalytic activity, the M_n and CU content of PPC were raised to about 143 kg/mol and 99%, whereas the PPC from common rare earth ternary catalyst was about 108 kg/mol and 97%, respectively. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Ni2+在γ-Al2O3上的分散状态及负载型Ni/γ-Al2O3催化剂的α-蒎烯加氢活性

用X-射线衍射(XRD)、紫外-可见漫散射光谱(UV-Vis DRS)、程序升温还原(TPR)、CO化学吸附和微反测试等方法研究了Ni²⁺在γ-Al₂O₃上的分散状态和负载型Ni/γ-Al₂O₃催化剂的α-蒎烯加氢催化活性。结果表明，当Ni²⁺负载量远低于其在γ-Al₂O₃载体表面分散容量时，Ni²⁺优先嵌入载体表面四面体空位，随着Ni²⁺负载量的增加，嵌入载体表面八面体空位Ni²⁺的比例增大。由于八面体Ni²⁺易被还原为金属态Ni⁰，NiO/γ-Al₂O₃样品的还原度随Ni²⁺负载量的增加而大幅度地增加，经氢还原所得Ni/γ-Al₂O₃催化剂的CO吸附量和α-蒎烯加氢催化活性大幅度增加。对La₂O₃助剂的作用进行了研究，结果表明分散在γ-Al₂O₃上的La³⁺物种可阻止Ni²⁺嵌入γ-Al₂O₃表面四面体空位，增大了八面体Ni²⁺物种所占比例，提高了催化剂的还原度，故Ni-La₂O₃/γ-Al₂O₃催化剂催化活性高于Ni/γ-Al₂O₃催化剂。     

改性Ag/α-Al_2O_3催化丙烯气相环氧化反应

制备了以分子氧为氧化剂,对丙烯气相环氧化具有较好催化性能的改性负载银催化剂,并利用氧气程序升温脱附(O2-TPD)技术研究了氧在其表面上的脱附行为.实验结果表明:Ag/α-Al2O3催化剂只能使丙烯完全氧化成二氧化碳和水;当该催化剂用K2O改性后,可获得少量的环氧丙烷;Y2O3改性的Ag/α-Al2O3催化剂,可获得极少量的丙醛和丙酮;将0.1%(w)Y2O3添加到Ag-K2O/α-Al2O3后,可以显著提高催化剂的丙烯环氧化性能.在0.1MPa、245℃、20%C3H6/8%O2/72%N2和气体空速2000h-1的反应条件下,通过20%(w)Ag-0.1%Y2O3-0.1%K2O/α-Al2O3催化剂时,丙烯转化率为4.0%,环氧丙烷的选择性为46.8%.O2-TPD研究表明,少量的Y2O3、K2O或Y2O3-K2O作为助剂添加到20%Ag/α-Al2O3催化剂中时,减少了高温区与丙烯完全氧化有关的吸附氧物种的量,低温区余下的吸附氧物种量不变,有利于丙烯环氧化反应,提高了环氧丙烷的选择性.     

0.1%Pt-0.02%Pd/不锈钢整体催化剂上丙酮氧化性能及稳定性(英文)

制备了0.1%Pt-0.02%Pd/不锈钢整体催化剂。选取不锈钢为该催化剂的载体,可克服传统γ-Al2O3和堇青石蜂窝载体热稳定性差的缺点。采用阳极氧化技术在不锈钢上自生长了结构致密的多孔阳极氧化膜,并在其上负载Pt和Pd制备得到挥发性有机物(VOCs)净化催化剂。结果表明,经500、800和1000℃不同温度焙烧后,该催化剂完全氧化丙酮的温度分别为160、160和200℃。该催化剂表现出以下优点:(a)高温稳定性能好;(b)低温催化活性高;(c)贵金属负载量低。通过SEM和EDX等技术对该催化剂的结构及活性组分分散情况进行了表征。     

Support effects on the chemical property and catalytic activity of Co-Mo HDS catalyst in sulfur recovery

Effects of carbon nanotubes (CNT) and alumina (γ-Al2O3) supports on the catalytic activities of hydrodesulfurization (HDS) process over CoMo catalyst have been studied. XRD results indicated that the main active phases in CNT and γ-Al2O3 supported Co-Mo catalysts are MoO2 and MoO3, respectively. The TPR results reveal that the reduction peak temperatures of the active species on CNT supported Co-Mo catalyst is lower than those on alumina supported Co-Mo catalyst, indicating that the CNT supports favor the r...     

双金属氰化物/稀土配合物催化二氧化碳和环氧丙烷的共聚合

使用双金属氰化物/稀土配合物复合催化剂催化二氧化碳和环氧丙烷共聚合,其催化效率比双金属氰化物催化剂有显著提高,得到了数均相对分子质量大于1.0×105的聚合物。研究了复合催化剂的组成(如稀土的种类、稀土与锌的比例(Ln/Zn)、稀土配合物中酸根离子的酸性等)对共聚反应的影响,同时研究了反应体系的压力及反应时间对催化活性的影响。采用Y(CCl3COO)3稀土金属配合物有利于共聚反应的进行。当n(Y)/n(Zn)=6、聚合4 h后,其催化活性比单纯的双金属氰化物提高了31.5%,聚合物的相对分子质量则没有太大变化,而副产物碳酸丙烯酯的质量分数低于2%,而在该温度下单独采用稀土三元催化剂时副产物碳酸丙烯酯的生成量通常在10%以上。聚合物中碳酸酯含量低于双金属氰化物的催化产物,说明稀土配合物只是起到活化金属与环氧丙烷配位的作用,没有提高共聚物的碳酸酯含量,整个共聚合反应依然遵循双金属氰化物催化的共聚反应机理。     

负载金属催化剂Ir(γ-Al2O3)对阿维菌素选择加氢反应研究

分别采用氢气、NaBH₄、醇水混合溶剂还原, PVP(聚乙烯吡咯烷酮)保护和微乳液法制备了γ-Al₂O₃负载的Ir金属催化剂, 通过XPS、XRD、TEM对催化剂的结构进行了表征, 考察了催化剂对阿维菌素选择加氢制备伊维菌素的性能, 探讨了催化剂制备方法对催化剂活性和选择性的影响. 实验结果表明, 在不同金属催化剂Ru/γ-Al₂O₃、Pd/γ-Al₂O₃、Pt/γ-Al₂O₃、Ir/γ-Al₂O₃中, Ir/γ-Al₂O₃的活性和选择性最好. 用PVP保护的Ir/γ-Al₂O₃, 其催化活性和选择性比没有PVP保护的催化剂有显著提高; 采用微乳液法制备的Ir/γ-Al₂O₃催化剂显示出最好的活性, 但反应选择性比PVP保护的催化剂差.     

The Role of Vanadia for the Selective Oxidation of Benzyl Alcohol over Heteropolymolybdate Supported on Alumina

A series of 12-molybdophosphoric acid (MPA) supported on V2O5 dispersed γ-Al2O3 catalysts with different vanadia loadings were prepared by impregnation and characterized by N2 adsorption-desorption,X-ray diffraction,temperature-programmed reduction,in situ laser Raman spectroscopy,UV-Vis diffused reflectance spectroscopy,scanning electron microscopy,and temperature-programmed desorption of NH3 techniques.Their catalytic activities were evaluated for the vapor phase aerobic oxidation of benzyl alcohol.The catalysts exhibited high catalytic activity and the conversion of benzyl alcohol depended on the vanadia content while the catalyst with 15 wt％ V2O5 content showed optimum activity.The characterization results suggest the presence of well-dispersed V2O5 and partially disintegrated Keggin ions of MPA on the support.In situ Raman studies showed a reduced Mo(IV) species when the catalysts were calcined at high temperatures.The high oxidation activity of the catalysts is related to the synergistic effect between MPA and V2O5.     

BaTiO3-BaAl2O4-Al2O3复合载体的制备、表征及其Ni基催化剂催化CH4/CO2重整反应性能

以十六烷基三甲基溴化胺为结构导向剂,采用溶胶-凝胶法制备了BaTiO3-BaAl2O4-Al2O3复合载体,采用X射线衍射、红外光谱、N2吸附-脱附、透射电子显微镜和H2程序升温还原等技术对复合载体进行了表征,并以CH4/CO2重整制合成气为探针反应,考察了不同Ni/BaTiO3-BaAl2O4-Al2O3催化剂的性能.结果表明,BaTiO3-BaAl2O4-Al2O3复合载体具有多孔织构特性和较高的比表面积,BaTiO3和BaAl2O4以晶粒状态分布在复合载体的内外表面,晶粒尺寸在20～50nm的范围,复合载体孔径为10～20nm.复合载体上BaTiO3和BaAl2O4的引入,适度削弱了Ni/BaTiO3-BaAl2O4-Al2O3催化剂中Ni物种与γ-Al2O3间的强相互作用,抑止了NiAl2O4尖晶石的生成;当载体中Ba(Ti)含量为17.33%时,其负载的Ni催化剂上CH4/CO2重整制合成气反应的活性和稳定性最高.