Direct observation of morphological development during the spin‐coating of polystyrene–poly(methyl methacrylate) polymer blends

We present results of the direct observation, in real‐space, of the phase separation of high molecular weight polystyrene and poly(methyl methacrylate) from ortho‐xylene using our newly developed technique of high speed stroboscopic interference microscopy. Taking a fixed concentration (3 wt % in o‐xylene) at a fixed composition (1:4 by weight) and by varying the rotational rate during the spin‐coating process, we are able to observe the formation of a range of phase separated bicontinuous morphologies of differing length‐scales. Importantly, we are able to show that the mechanism by which the final phase separated structure is formed is through domain coarsening when rich in solvent, before vitrification occurs and fixes the phase separated structure. The ability to directly observe morphological development offers a route toward controlling the length‐scale of the final morphology through process control and in situ feedback, from a single stock solution. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part B Polym. Phys. 2013, 51, 875–881     

Radiation‐induced fabrication of polymer nanoporous materials from microphase‐separated structure of diblock copolymers as a template

Polymer nanoporous materials with periodic cylindrical holes were fabricated from microphase‐separated structure of diblock copolymers consisting of a radiation‐crosslinking polymer and a radiation‐degrading polymer through simultaneous crosslinking and degradation by γ‐irradiation. A polybutadiene‐block‐poly(methyl methacrylate) (PB‐b‐PMMA) diblock copolymer film that self‐assembles into hexagonally packed poly(methyl methacrylate) cylinders in polybutadiene matrix was irradiated with γ‐rays. Solubility test, IR spectroscopy, and TEM and SEM observations for this copolymer film in comparison with a polystyrene‐block‐poly(methyl methacrylate) diblock copolymer film revealed that poly(methyl methacrylate) domains were removed by γ‐irradiation and succeeding solvent washing to form cylindrical holes within polybutadiene matrix, which was rigidified by radiation crosslinking. Thus, it was demonstrated that nanoporous materials can be prepared by γ‐irradiation, maintaining the original structure of PB‐b‐PMMA diblock copolymer film. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5916–5922, 2007     

pH‐responsive destabilization and facile bioconjugation of new hydroxyl‐terminated block copolymer micelles

New hydroxyl‐terminated amphiphilic block copolymers (HO‐ABPs) having pendant t‐butyl groups for pH‐responsiveness and terminal OH groups for bioconjugation are reported. These HO‐ABPs consist of hydrophilic poly(oligo(ethylene oxide) monomethyl ether methacrylate) and hydrophobic poly(t‐butyl methacrylate) blocks and were synthesized by a consecutive atom transfer radical polymerization in the presence of an OH‐terminated bromine initiator. Aqueous self‐assembly of HO‐ABPs resulted in colloidally stable micellar aggregates being capable of encapsulating hydrophobic guest molecules. They were nontoxic to cells and destabilized in response to low pH. A facile bioconjugation of HO‐ABP micelles for active targeting is demonstrated by conjugation with biotin (vitamin H) and competitive assay exhibiting >93% ABP chains conjugated with biotin in each micelle. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Mesogen‐controlled ion channel of star‐shaped hard–soft block copolymers for solid‐state lithium‐ion battery

Novel star‐shaped hard–soft triblock copolymers, 4‐arm poly(styrene)‐block‐poly [poly(ethylene glycol) methyl ethyl methacrylate]‐block‐poly{x‐[(4‐cyano‐4′‐biphenyl) oxy] alkyl methacrylate} (4PS‐PPEGMA‐PMAxLC) (x = 3, 10), with different mesogen spacer length are prepared by atom‐transfer radical polymerization. The star copolymers comprised three different parts: a hard polystyrene (PS) core to ensure the good mechanical property of the solid‐state polymer, and a soft, mobile poly[poly(ethylene glycol) methyl ethyl methacrylate] (PPEGMA) middle sphere responsible for the high ionic conductivity of the solid polyelectrolytes, and a poly{x‐[(4‐cyano‐4′‐biphenyl)oxy]alkyl methacrylate} with a birefringent mesogens at the end of each arm to tuning the electrolytes morphology. The star‐shaped hard–soft block copolymers fusing hard PS core with soft PPEGMA segment can form a flexible and transparent film with dimensional stability. Thermal annealing from the liquid crystalline states allows the cyanobiphenyl mesogens to induce a good assembly of hard and soft blocks, consequently obtaining uniform nanoscale microphase separation morphology, and the longer spacer is more helpful than the shorter one. There the ionic conductivity has been improved greatly by the orderly continuous channel for efficient ion transportation, especially at the elevated temperature. The copolymer 4PS‐PPEGMA‐PMA10LC shows ionic conductivity value of 1.3 × 10^?4 S cm^?1 (25 °C) after annealed from liquid crystal state, which is higher than that of 4PS‐PPEGMA electrolyte without mesogen groups. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 4341–4350     

Materials for the preparation of polymer pen lithography tip arrays and a comparison of their printing properties

Polymer Pen Lithography (PPL) uses an array of polymeric tips, typically composed of poly(dimethyl siloxane), to transfer ink onto a surface and create patterns of soft molecules with micrometer to nanometer feature dimensions. In this study, tip arrays were fabricated from poly(methyl methacrylate), poly([methyl methacrylate]‐co‐[butyl methacrylate]), and poly(3‐mercaptopropylmethylsiloxane), and used to pattern 1‐mercaptohexadecanoic acid onto Au surfaces to determine the fidelity of pattern transfer by PPL as a function of the mechanical properties of the materials. It was found that the dependence between the applied force and feature edge length correlates directly to the mechanical properties of each of the polymers used to fabricate the tip arrays, where stiffer polymers have a reduced dependence between the applied force and feature size. This study demonstrates that PPL tip arrays can be composed of a wide variety of materials whose choice is determined by the desired printing application. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Cationic methacrylate copolymers containing primary and tertiary amino side groups: Controlled synthesis via RAFT polymerization,DNA condensation,and in vitro gene transfection

A versatile family of cationic methacrylate copolymers containing varying amounts of primary and tertiary amino side groups were synthesized and investigated for in vitro gene transfection. Two different types of methacrylate copolymers, poly(2‐(dimethylamino)ethyl methacrylate)/aminoethyl methacrylate [P(DMAEMA/AEMA)] and poly(2‐(dimethylamino)ethyl methacrylate)/aminohexyl methacrylate [P(DMAEMA/AHMA)], were obtained by reversible addition‐fragmentation chain transfer (RAFT) copolymerization of dimethylaminoethyl methacrylate (DMAEMA) with N‐(tert‐butoxycarbonyl)aminoethyl methacrylate (Boc‐AEMA) or N‐(tert‐butoxycarbonyl)aminohexyl methacrylate (Boc‐AHMA) followed by acid deprotection. Gel permeation chromatography (GPC) measurements revealed that Boc‐protected methacrylate copolymers had M_n in the range of 16.1–23.0 kDa and low polydispersities of 1.12–1.26. The copolymer compositions were well controlled by monomer feed ratios. Dynamic light scattering and agarose gel electrophoresis measurements demonstrated that these PDMAEMA copolymers had better DNA condensation than PDMAEMA homopolymer. The polyplexes of these copolymers revealed low cytotoxicity at an N/P ratio of 3/1. The in vitro transfection in COS‐7 cells in serum free medium demonstrated significantly enhanced (up to 24‐fold) transfection efficiencies of PDMAEMA copolymer polyplexes as compared with PDMAEMA control. In the presence of 10% serum, P(DMAEMA/AEMA) and P(DMAEMA/AHMA) displayed a high transfection activity comparable with or better than 25 kDa PEI. These results suggest that cationic methacrylate copolymers are highly promising for development of safe and efficient nonviral gene transfer agents. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2869–2877, 2010     

Controlled block glycopolymers able to bind specific proteins

The syntheses of a variety of amphiphilic block glycopolymers based on 2‐{[(D ‐glucosamin‐2‐N‐yl)carbonyl]oxy}ethyl acrylate and n‐butyl acrylate or methyl methacrylate by single‐electron transfer‐living radical polymerization (SET‐LRP) are described. In a first step, the homopolymerization of unprotected acrylic glycomonomer to obtain well‐controlled glycopolymers is studied. Posterior and based on these studies, di‐ and triblock glycopolymers were synthesized via SET‐LRP of the glycomonomer from different hydrophobic blocks, varying the hydrophilic block lengths. All the copolymers are characterized by nuclear magnetic resonance spectroscopy and GPC. Moreover, their water solution behavior by dynamic light scattering and their capacity of interaction with Concanavalin A lectin by turbidimetry are analyzed. The effect on the block glycopolymers behavior of hydrophobic block nature and the length of glycopolymer segments is evaluated. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Preparation of amphiphilic statistical copolymers of 2‐hydroxyethyl methacrylate with 2‐diethylaminoethyl methacrylate,precursors of water‐soluble copolymers

Statistical copolymers of 2‐hydroxyethyl methacrylate (HEMA) and 2‐diethylaminoethyl methacrylate (DEA) were synthesized at 50 °C by free‐radical copolymerization in bulk and in a 3 mol L^?1 N,N′‐dimethylformamide solution with 2,2′‐azobisisobutyronitrile as an initiator. The solvent effect on the apparent monomer reactivity ratios was attributed to the different aggregation states of HEMA monomer in the different solvents. The copolymers obtained were water‐insoluble at a neutral pH but soluble in an acidic medium when the molar fraction of the DEA content was higher than 0.5. The quaternization of DEA residues increased the hydrophilic character of the copolymers, and they became water‐soluble at a neutral pH when the HEMA content was lower than 0.25. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2427–2434, 2002     

Solvent effect on the free‐radical copolymerization of 2‐hydroxyethyl methacrylate with t‐butyl acrylate

The free‐radical copolymerization of 2‐hydroxyethyl methacrylate with t‐butyl acrylate was carried out at 50 °C in bulk and in 3 mol · L^?1 1,4‐dioxane and N,N′‐dimethylformamide solutions. Differences between the apparent reactivity ratios determined in this work indicated a noticeable solvent effect. This is explained with a qualitative bootstrap effect. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2043–2048, 2001     

Multifunctional linear methacrylate copolymer polyenes having pendant vinyl groups: Synthesis and photoinduced thiol–ene crosslinking polyaddition

UV‐induced thiol‐ene crosslinked films composed of linear methacrylate copolymers having pendant enes (MCPenes) are reported. An approach involving a combination of controlled radical polymerization to synthesize well‐controlled pendant hydroxyl containing copolymers (MCP_OHs) with the following facile carbodiimide coupling of the formed MCP_OHs with enes allows for the synthesis of well‐controlled MCPenes with narrow molecular weight distribution. The density of the pendant enes in MCPenes are easily modulated by varying monomer ratios in the feed. Under UV irradiation, the resulting MCPenes undergo thiol‐ene polyaddition reactions with polythiols to form crosslinked films with a uniform network. The results from thermal and mechanical analysis suggest these properties are tuned by adjusting the densities of pendant enes in MCPenes and the amount of thiols in the reactive mixtures. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 572–581     

Optimal estimation of reactivity ratios for acrylamide/acrylic acid copolymerization

Reactivity ratios for the important acrylamide (AAm)/acrylic acid (AAc) copolymerization system exhibit considerable scatter in previously published literature, and therefore, there is a need for more definitive values for these reactivity ratios. An appropriate methodology, based on the error‐in‐variables‐model (EVM) framework along with a direct numerical integration procedure, is applied in order to determine reliable reactivity ratios. The reliability of the results is confirmed with extensive and independent replication. Furthermore, via an EVM‐based criterion for the design of experiments using mechanistic models, optimal feed compositions are calculated, and from these optimal reactivity ratios are estimated for the first time (r_AAm = 1.33 and r_AAc = 0.23) based on information from the full conversion range. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 4819–4827     

Statistical copolymers of methyl methacrylate and 2‐methacryloyloxyethyl ferrocenecarboxylate: Monomer reactivity ratios,thermal and electrochemical properties

Statistical copolymers of methyl methacrylate (MMA) with 2‐methacryloyloxyethyl ferrocenecarboxylate (MAEFC) were prepared by free radical polymerization. The reactivity ratios were estimated using the Fineman‐Ross, inverted Fineman‐Ross, Kelen‐Tüdos, and extended Kelen‐Tüdos graphical methods. Structural parameters of the copolymers were obtained by calculating the dyad monomer sequence fractions and the mean sequence length. The glass‐transition temperature (T_g) values of the copolymers were measured and examined by means of several theoretical equations, allowing the prediction of these T_g values. The thermal degradation behavior of the copolymers was also studied and compared with the respective homopolymers. Cyclic voltammetry was employed to study the electrochemical properties of the copolymers. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Fast switching immobilized photochromic dyes

A novel photochromic dye conjugate architecture is described, which allows both covalent tethering to a polymeric host matrix and fast photochromic switching. The new conjugates consist of a photochromic dye covalently bound to two different substituents via a Y‐branching linker (hetero Y‐branching), one being a polymerizable methacrylate moiety and the other a soft (low T_g) poly(dimethylsiloxane) oligomer. The novel conjugates gave faster photochromic decoloration in the host lens matrix compared with the electronically equivalent nonmatrix‐bound and unconjugated parent control dyes. In addition, further acceleration of fade speed kinetics was observed with a longer linker between photochromic dye and methacrylate moiety. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis of nitroxide‐containing block copolymers for the formation of organic cathodes

This contribution describes the polymerization of 2,2,6,6‐tetramethylpiperidin‐4‐yl methacrylate by atom transfer radical polymerization (ATRP). Different catalytic systems are compared. The CuCl/4,4′‐dinonyl‐2,2′‐dipyridyl catalytic system allows a good control over the polymerization and provides polymers with a polydispersity index below 1.2. The successful polymerization of styrene from PTMPM‐Cl macroinitiators by ATRP is then demonstrated. Successful quantitative oxidation of PTMPM‐b‐PS block copolymers leads to poly(2,2,6,6‐tetramethylpiperidinyloxy‐4‐yl‐methacrylate)‐b‐poly(styrene) (PTMA‐b‐PS). The cyclic voltammogram of PTMA‐b‐PS indicates a reversible redox reaction at 3.6 V (vs. Li⁺/Li). Such block copolymers open new opportunities for the formation of functional organic cathode materials. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

A facile strategy for synthesis of α,α′‐heterobifunctionalized poly (ε‐caprolactones) and poly (methyl methacrylate)s containing “clickable” aldehyde and allyloxy functional groups using initiator approach

Two new initiators, namely, 4‐(4‐(2‐(4‐(allyloxy) phenyl)‐5‐hydroxypentane 2‐yl) phenoxy)benzaldehyde and 4‐(4‐(allyloxy) phenyl)‐4‐(4‐(4‐formylphenoxy) phenyl) pentyl 2‐bromo‐2‐methyl propanoate containing “clickable” hetero‐functionalities namely aldehyde and allyloxy were synthesized starting from commercially available 4,4′‐bis(4‐hydroxyphenyl) pentanoic acid. These initiators were utilized, respectively, for ring opening polymerization of ε‐caprolactone and atom transfer radical polymerization of methyl methacrylate. Well‐defined α‐aldehyde, α′‐allyloxy heterobifunctionalized poly(ε‐caprolactones) (M_n,GPC: 5900–29,000, PDI: 1.26–1.43) and poly(methyl methacrylate)s (M_n,GPC: 5300–28800, PDI: 1.19–1.25) were synthesized. The kinetic study of methyl methacrylate polymerization demonstrated controlled polymerization behavior. The presence of aldehyde and allyloxy functionality on polymers was confirmed by ¹H NMR spectroscopy. Aldehyde‐aminooxy and thiol‐ene metal‐free double click strategy was used to demonstrate reactivity of functional groups on polymers. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Kinetic study of the stable free‐radical copolymerization of styrene with butyl methacrylate

The radical copolymerization of styrene and n‐butyl methacrylate mediated by 1‐phenyl‐1‐(2′,2′,6′,6′‐tetramethyl‐1′‐piperidinyl‐oxy)ethane in bulk at 125 °C has been analyzed over a wide range of conversions and monomer feed compositions. Monomer reactivity ratios have been determined, and the Mayo–Lewis terminal model provides excellent predictions for the variations of the intermolecular structure over the entire conversion range. The kinetic analysis of this copolymerization system indicates an apparent propagation rate coefficient independent of the monomer feed composition as well as a limiting conversion that decreases as the styrene monomer feed decreases. This fact is attributed to side reactions leading to unsaturated end groups and the accumulation of nonactive adducts of n‐butyl methacrylate. The number‐average molecular weights linearly increase with conversion, and the copolymers present narrow molecular weight distributions. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2750–2758, 2002     

Relationship between lens properties and director orientation in a liquid crystal lens

Lenses with a homogeneously aligned liquid crystal having a Fresnel structure have been prepared by using a nematic with a positive dielectric anisotropy. Their focal length can be varied continuously from the value f_e for an extraordinary ray to f _o for an ordinary ray by applying an electric field across the lens cell. The effective refractive index of the lens where the director is aligned perpendicular to the grooves of the Fresnel structure becomes smaller than when the director is aligned parallel to the grooves. Then the liquid crystal lens has a characteristic aberration which could not be observed in a conventional glass lens; that is, the focal length of the lens becomes different according to the incidence of rays on the different parts of the lens. The properties of the liquid crystal lens can be improved by making the director orientation axially symmetric, in the form of a concentric circle, but the polarization component rotated 90° from the incident extraordinary ray appears when the voltage is applied across the lens cell. This phenomenon is discussed in relation to the optical properties and the director orientation in a liquid crystal prism cell.     

Epoxy functionalized polymethacrylates based on various multifunctional d‐glucopyranoside acetals

The synthesis of acetal‐derived d ‐glucopyranosides with a various number of hydroxyl groups (the first step, acetalization) and their modified forms with bromoester groups (the second step, esterification) are presented here. The latter, due to the type of functional groups, can be used to initiate the controlled atom transfer radical polymerization. The copolymerizations of equimolar feed of methacrylate monomers, namely, methyl methacrylate and glycidyl methacrylate, were initiated by prepared new glycoinitiators, based on methyl α‐d ‐glucopyranoside (Meαd Glu) or 2‐(hydroxymethyl)phenyl‐β‐d ‐glucopyranoside (salicin), in the presence of the catalyst system CuCl/dNbpy in anisole at 30 °C. The conditions were sufficient for successful synthesis of well‐defined copolymers with sugar cores sheltered by two‐, three‐, four‐, or six‐polymethacrylate segments with various polymerization degrees (DP_arm = 15 – 70) and low dispersity indices (Ð = 1.15–1.30). Because of the presence of oxirane groups, the star‐copolymers can be functionalized in further steps by biologically active compounds or modified to amphipilics. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 2483–2494     

Electroactive methacrylate‐based triblock copolymer elastomer for actuator application

A series of ABA triblock copolymers of methyl methacrylate (MMA) and dodecyl methacrylate (DMA) [poly(MMA‐b‐DMA‐b‐MMA)] (PMDM) were synthesized by Ru‐based sequential living radical polymerization. For this, DMA was first polymerized from a difunctional initiator, ethane‐1,2‐diyl bis(2‐chloro‐2‐phenylacetate) with combination of RuCl₂(PPh₃)₃ catalyst and nBu₃N additive in toluene at 80 °C. As the conversion of DMA reached over about 90%, MMA was directly added into the reaction solution to give PMDM with controlled molecular weight (M_w/M_n ≤ 1.2). These triblock copolymers showed well‐organized morphologies such as body centered cubic, hexagonal cylinder, and lamella structures both in bulk and in thin film by self‐assembly phenomenon with different poly(methyl methacrylate) (PMMA) weight fractions. Obtained PMDMs with 20–40 wt % of the PMMA segments showed excellent electroactive actuation behaviors at relatively low voltages, which was much superior compared to conventional styrene‐ethylene‐butylene‐styrene triblock copolymer systems due to its higher polarity derived from the methacrylate backbone and lower modulus. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013