Synthesis and magnetic properties of single-crystalline BaFe12O19 nanoparticles

Rod-like and platelet-like nanoparticles of simple-crystalline barium hexaferrite (BaFe₁₂O₁₉) have been synthesized by the molten salt method. Both particle size and morphology change with the reaction temperature and time. The easy magnetization direction (0 0 l) of the BaFe₁₂O₁₉ nanoparticles has been observed directly by performing X-ray diffraction on powders aligned at 0.5 T magnetic field. The magnetic properties of the BaFe₁₂O₁₉ magnet were investigated with various sintering temperatures. The maximum values of saturation magnetization (σ_s=65.8 emu/g), remanent magnetization (σ_r=56 emu/g) and coercivity field (H_ic=5251 Oe) of the aligned samples occurred at the sintering temperatures of 1100 °C. These results indicate that BaFe₁₂O₁₉ nanoparticles synthesized by the molten salt method should enable detailed investigation of the size-dependent evolution of magnetism, microwave absorption, and realization of a nanodevice of magnetic media.     

Simple recipe to synthesize single-domain BaFe12O19 with high saturation magnetization

We report a new synthesis route for preparation of single-domain barium hexaferrite (BaFe₁₂O₁₉) particles with high saturation magnetization. Nitric acid, known as a good oxidizer, is used as a mixing medium during the synthesis. It is shown that formation of BaFe₁₂O₁₉ phase starts at 800 °C, which is considerably lower than the typical ceramic process and develops with increasing temperature. Both magnetization measurements and scanning electron microscope micrographs reveal that the particles are single domain up to 1000 °C at which the highest coercive field of 3.6 kOe was obtained. The best saturation magnetization of ≈60 emu/g at 1.5 T was achieved by sintering for 2 h at 1200 °C. Annealing at temperatures higher than 1000 °C increased the saturation magnetization, on the other hand, decreased the coercive field which was due to the formation of multi-domain particles with larger grain sizes. It is shown that the best sintering to obtain fine particles of BaFe₁₂O₁₉ occurs at temperatures 900-1000 °C. Finally, magnetic interactions between the hard BaFe₁₂O₁₉ phase and impurity phases were investigated using the Stoner-Wohlfarth model.     

Preparation and magnetic properties of BaFe12O19/Ni0.8Zn0.2Fe2O4 nanocomposite ferrite

Nanocomposite of hard (BaFe₁₂O₁₉)/soft ferrite (Ni_0.8Zn_0.2Fe₂O₄) have been prepared by the sol–gel process. The nanocomposite ferrite are formed when the calcining temperature is above 800 °C. It is found that the magnetic properties strongly depend on the presintering treatment and calcining temperature. The “bee waist” type hysteresis loops for samples disappear when the presintering temperature is 400 °C and the calcination temperature reaches 1100 °C owing to the exchange-coupling interaction. The remanence of BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite with the mass ratio of 5:1 is higher than a single phase ferrite. The specific saturation magnetization, remanence magnetization and coercivity are 63 emu/g, 36 emu/g and 2750 G, respectively. The exchange-coupling interaction in the BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite is discussed.     

Magnetic and electrical properties of bulk BaTiO3+MgFe2O4 composite

BaTiO₃+MgFe₂O₄ material system was synthesized by hybrid chemical process using chlorides and nitrates of barium, titanium, iron, and magnesium. Magnetic properties of the composite samples measured as a function of annealing conditions indicated soft magnetic behavior. Saturation specific magnetization from 8 21 emu/g was observed for samples annealed at temperature between 950 and 1150 °C. Variation of specific saturation magnetization with respect to annealing temperature was related with the distribution of Fe cations in the tetrahedral and octahedral sites of MgFe₂O₄. Electrical properties of the samples annealed at different temperatures were measured to analyze the coexistence of ferroelectric phase. Dielectric constant varying from 15 to 200 with respect to frequency was observed for samples annealed from 950 to 1150 °C.     

Synthesis of (Mg0.476Mn0.448Zn0.007)(Fe1.997Ti0.002)O4 powder and sintered ferrites by high energy ball-milling process

(Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder prepared by high energy ball-milling process were consolidated by microwave and conventional sintering processes. Phases, microstructure and magnetic properties of the ferrites prepared by different processes were investigated. The (Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder could be prepared by high energy ball-milling process of raw Fe₃O₄, MnO₂, ZnO, TiO₂ and MgO powders. Prefired and microwave sintered ferrites could achieve the maximum density (4.86 g/cm⁻³), the average grain size (15 μm) was larger than that (10 μm) prepared by prefired and conventionally sintered ferrites with pure ferrite phase, and the saturation magnetization (66.77 emu/g) was lower than that of prefired and conventionally sintered ferrites (88.25 emu/g), the remanent magnetization (0.7367 emu/g) was higher than that of prefired and conventionally sintered ferrites (0.0731 emu/g). Although the microwave sintering process could increase the density of ferrites, the saturation magnetization of ferrites was decreased and the remanent magnetization of ferrites was also increased.     

Improvement of the magnetic properties of barium hexaferrite nanopowders using modified co-precipitation method

Barium hexaferrite BaFe₁₂O₁₉ powders have been synthesized using the modified co-precipitation method. Modification was performed via the ultrasonication of the precipitated precursors at room temperature for 1 h and the additions of the 2% KNO₃, surface active agents and oxalic acid. The results revealed that single phase magnetic barium hexaferrite was formed at a low annealing temperature of 800 °C for 2 h with the Fe³⁺/Ba²⁺ molar ratio 8. The microstructure of the powders appeared as a homogeneous hexagonal platelet-like structure using 2% KNO₃ as the crystal modifier. A saturation magnetization (60.4 emu/g) was achieved for the BaFe₁₂O₁₉ phase formed at 1000 °C for 2 h with Fe³⁺/Ba²⁺ molar ratio 8 using 5 M NaOH solution at pH 10 in the presence of 2% KNO₃. Moreover, the saturation magnetization was 52.2 emu/g for the precipitated precursor at Fe³⁺/Ba²⁺ molar ratio 12 in was achieved for the precipitated precursor ultrasonicated for 1 h and then annealed at 1200 °C for 2 h. Coercivities from 956.9 to 4558 Oe were obtained at different synthesis conditions.     

Monodispersed nanocrystalline Co1–xZnxFe2O4 particles by forced hydrolysis: Synthesis and characterization

Zinc-substituted cobalt ferrites, Co_1–xZn_xFe₂O₄, were for the first time successfully prepared by forced hydrolysis method. The obtained materials are single phase, monodispersed nanocrystalline with an average grain size of about 3 nm. These materials are superparamagnetic at room temperature and ferrimagnetic at temperature lower than the blocking temperature. When the zinc substitution increases from x=0 to 0.4, at 4.2 K, the saturation magnetization increases from 72.1 to 99.7 emu/g. The high saturation magnetization of these samples suggests that this method is suitable for preparing high-quality nanocrystalline magnetic ferrites for practical applications.     

Effect of synthesis conditions on the preparation of YIG powders via co-precipitation method

Yttrium iron garnet (YIG) (Y₃Fe₅O₁₂) powders have been synthesized through a co-precipitation method in the presence of sodium bis(2-ethylhexylsulfosuccinate), AOT as an anionic surfactant. The garnet precursors produced were obtained from aqueous iron and yttrium nitrates mixtures using 5 M sodium hydroxide at pH 10. A statistical Box–Behnken experimental design was used to investigate the effect of the main parameters (i.e. AOT surfactant concentration, annealing time and temperature) on YIG powder formation, crystallite size, morphology and magnetic properties. YIG particles were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometer. XRD revealed that the formation of single cubic phase of YIG was temperature dependent and increased by increasing the annealing temperature from 800 to 1200 °C. SEM micrographs showed that the addition of AOT surfactant promoted the microstructure of YIG in crystalline cubic-like structure. The magnetic properties were sensitive to the synthesis variables of annealing temperature, time and AOT surfactant concentration. The maximum saturation magnetization (28.13 emu/g), remanence magnetization (21.57 emu/g) and coercive force (703 Oe) were achieved at an annealing temperature of 1200 °C, time 2 h and 500 ppm of AOT surfactant concentration.     

Magnetic properties of FexCo1−x/CoyFe1−yFe2O4 composite under hydrothermal condition

The metal–ferrite composites Fe_xCo_1−x/Co_yFe_1−yFe₂O₄ are synthesized by using disproportion of Fe (II) and reduction of Co (II) by Fe⁰ under hydrothermal condition. The size of the particles of the composites decreases as the [KOH] decreasing. The composites are measured by TEM and it can be deduced that when [KOH] = 0.1, the size of the alloy body-centered cubic (BCC) in composites is 20 ± 7 nm, the size of the Cobalt ferrite (spinel) is 170 ± 50 nm. The maximal value of the saturation magnetization (Ms) of the composite is about 100.14 emu/g, which is synthesized under Co (II)/Fe (II) = 0.05, [KOH] = 1 N, T = 150 °C and t = 3 h. The value of Hc of the composite synthesized under Co (II)/Fe (II) = 0.5, t = 3 h, T = 150 °C and [KOH] = 10.2 mol/L is about 2878.19 Oe. The Fe–Co alloy is synthesized through a reduction reaction of the composites in a flowing gaseous mixture. There is a maximal value (302.9 emu/g) of the Ms for the alloys generated at 1000 °C, which is the Co_0.412Fe_0.588 alloy.     

Microwave-assisted synthesis of SrFe12O19 hexaferrites

Ultra-fine and homogeneous SrFe₁₂O₁₉ hexaferrites were synthesized by a microwave-assisted calcination route. The calcined precursors were prepared by a sol-gel auto-combustion method using Fe(NO₃)₃·9H₂O, Sr(NO₃)₂ and citric acid as starting materials. The structures, powder morphology and magnetic properties of the products were characterized by X-ray diffraction, scanning electron microscope and vibrating sample magnetometer. The results showed that microwaves are helpful to reduce the calcination temperature and shorten the calcination time. The ferrites with saturation magnetization, remanence and intrinsic coercivity of 54.80 emu/g, 29.52 emu/g and 5261 Oe, respectively, were obtained in samples calcined at 800 °C for 80 min.     

Preparation, characterization and magnetic properties of the doped barium hexaferrites BaFe12−2xCox/2Znx/2SnxO19, x=0.0-2.0

A series of powders of M-typed barium hexaferrites doped with Co, Zn and Sn of general formula BaFe_12-2xCo_x/2Zn_x/2Sn_xO₁₉ (x=0-2.0) were prepared by the co-precipitation/molten salt method. The structures, particle morphology and magnetic properties of the products were characterized by X-ray powder diffraction, vibrating sample magnetometer and ESEM/EDX. The results show that the crystallinity of the samples decreases with increase in the doping amount x. When x is less than 0.6, it is possible to obtain perfectly crystallized hexagonal BaFe_12-2xCo_x/2Zn_x/2Sn_xO₁₉, where the diameters of the particles are around 500 nm. The saturation magnetization of pure barium ferrite BaFe₁₂O₁₉ produced with this method is 71.9 A m² kg⁻¹ at room temperature and the intrinsic coercivity (H_c) is 367.8 kA m⁻¹. The doped barium hexaferrite powder obtained when x is between 0.3 and 0.4 exhibits high saturation magnetization and a temperature dependence of coercivity close to zero.     

BaCO3 mediated modifications in structural and magnetic properties of natural nanoferrites

Preparing M-type barium hexaferrite and improving the magnetic response of natural ferrites by incorporating barium carbonate (BaCO₃) is ever-demanding. Series of barium carbonate doped ferrites with composition (100−x)Fe₃O₄·xBaCO₃ (x=0, 10, 20, 30 wt%) are prepared through solid state reaction method and sintered gradually at temperatures of 800 and 1000 °C. Nanoparticles of natural ferrite and commercial BaCO₃ are used as raw materials. Impacts of BaCO3 on structural and magnetic properties of these synthesized ferrites are inspected. The obtained ferrites are characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD) and vibrating sample magnetometer (VSM) at room temperature. Uniform barium hexaferrite particles in terms of both morphology and size are not achieved. The average crystallite size of BaFe₁₂O₁₉ is observed to be within 30–600 nm. The sintering process results phase transformation from Fe₃O₄ (magnetite) to α-Fe₂O₃ (hematite) and the formation of hexagonal barium ferrite crystals. The occurrence of barium crystal is found to enhance with the increase of BaCO₃ concentrations up to 20 wt% and suddenly drop at 30 wt%. Saturation and remanent magnetization of the doped ferrites are significantly augmented up to 16.37 and 8.92 emu g⁻¹, respectively compared to their pure counterpart. Furthermore, the coercivity field is slightly decreased as BaCO₃ concentrations are increased. BaCO₃ mediated improvements in the magnetic response of natural ferrites are demonstrated.     

Structural, microstructural and magnetic properties of NiFe2O4, CoFe2O4 and MnFe2O4 nanoferrite thin films

The structural, microstructural and magnetic properties of nanoferrite NiFe₂O₄ (NF), CoFe₂O₄ (CF) and MnFe₂O₄ (MF) thin films have been studied. The coating solution of these ferrite films was prepared by a chemical synthesis route called sol-gel combined metallo-organic decomposition method. The solution was coated on Si substrate by spin coating and annealed at 700 °C for 3 h. X-ray diffraction pattern has been used to analyze the phase structure and lattice parameters. The scanning electron microscopy (SEM) and atomic force microscopy (AFM) have been used to show the nanostructural behavior of these ferrites. The values of average grain's size from SEM are 44, 60 and 74 nm, and from AFM are 46, 61 and 75 nm, respectively, measured for NF, CF and MF ferrites. At room temperature, the values of saturation magnetization, M_s∼50.60, 33.52 and 5.40 emu/cc, and remanent magnetization, M_r∼14.33, 15.50 and 1.10 emu/cc, respectively, are observed for NF, CF and MF. At low temperature measurements of 10 K, the anisotropy of ferromagnetism is observed in these ferrite films. The superparamagnetic/paramagnetic behavior is also confirmed by χ′(T) curves of AC susceptibility by applying DC magnetizing field of 3 Oe. The temperature dependent magnetization measurements show the magnetic phase transition temperature.     

Effects of annealing temperature on structure and magnetic properties of CoAl0.2Fe1.8O4/SiO2 nanocomposites

CoAl_0.2Fe_1.8O₄/SiO₂ nanocomposites were prepared by sol–gel method. The effects of annealing temperature on the structure and magnetic properties of the samples were studied by X-ray diffraction, transmission electron microscopy, vibrating sample magnetometer and Mössbauer spectroscopy. The results show that the CoAl_0.2Fe_1.8O₄ in the samples exhibits a spinel structure after being annealed. As annealing temperature increases from 800 to 1200 °C, the average grain size of CoAl_0.2Fe_1.8O₄ in the nanocomposites increases from 5 to 41 nm while the lattice constant decreases from 0.8397 to 0.8391 nm, the saturation magnetization increases from 21.96 to 41.53 emu/g. Coercivity reaches a maximum of 1082 Oe for the sample annealed at 1100 °C, and thereafter decreases with further increasing annealing temperature. Mössbauer spectra show that the isomer shift decreases, hyperfine field increases and the samples transfer from mixed state of superparamagnetic and magnetic order to the completely magnetic order with annealing temperature increasing from 800 to 1200 °C.     

Preparation of substituted barium ferrite BaFe12−x(Ti0.5Co0.5)xO19 by citrate precursor method and compositional dependence of their magnetic properties

As a possible candidate for the left-handed metamaterial with negative permeability, a series of Ti, Co-substituted M-type barium hexaferrite BaFe_12−x(Ti_0.5Co_0.5)_xO₁₉ (x=0, 1, 2, 3, 4 and 5) was prepared by citrate precursor method. The formation processes of the substituted barium hexaferrite compounds from the precursors were followed by the measurements of powder X-ray diffraction (XRD), Infrared absorption spectra (FT-IR), and thermogravimetry and differential thermal analysis (TG/DTA) coupled with mass spectroscopy (MS). In the case of the non-substituted sample, the formation of the barium hexaferrite is regulated by the thermal decomposition of BaCO₃ and the solid-state reactions of BaO and Fe₂O₃ in the temperature range from 800 to 1100 K. The formation temperature of the substituted BaFe_12−x(Ti_0.5Co_0.5)_xO₁₉ is higher than that for the non-substituted sample and increases with the value of x, due to the effects of carbonate ions incorporated by the partial substitution of Fe³⁺ by (Ti_0.5Co_0.5)³⁺. On heating up to ca. 1200 K, all the substituted samples transform into the magenetoplumbite phase as is the non-substituted sample. The compositional dependence of the magnetic properties of the substituted barium hexaferrite was investigated by the magnetization measurement. The decrease in the magnetic anisotropy was confirmed by the change in the magnetization curve and coercivity H_C with the composition x. A negative permeability spectrum was observed in the BaFe₉(Ti_0.5Co_0.5)₃O₁₉ in the frequency range from 2 to 4 GHz.     

Influence of pH on characteristics of BaFe12O19 powder prepared by sol–gel auto-combustion

BaFe₁₂O₁₉ powders with nanocrystalline sizes were produced by sol–gel auto-combustion. Fe³⁺ and Ba²⁺, in a molar ratio of 11.5, were chelated by citric acid ions at different pH. After dehydration, auto-combustion and calcinations, BaFe₁₂O₁₉ powders were formed. TG/DSC indicated the action to form BaFe₁₂O₁₉ first occurred at about 800. XRD patterns of the annealed powders showed that the well-crystalline powder was produced when pH=10. In addition, the data from XRD showed the lattice parameters a and c, and the unit-cell volume V had a little decrease and the density went up with the increasing pH. The data from PPMS exhibited that pH in the starting solution had an important influence on magnetic properties. In this case, BaFe₁₂O₁₉ powder, of maximum magnetization M(3 T)≈60 A m²/kg, the remanent magnetization M_r≈33 A m²/kg and the intrinsic coercive H_c≈432 kA/m, was produced under the molar ratio of citric acid to the metal nitrate of 1.5 when pH=10.     

Influence of annealing temperature on morphological and magnetic properties of La0.9Sr0.1MnO3

The nanocrystalline samples of La_0.9Sr_0.1MnO₃ (LSMO) have been prepared by the combustion method. The thermo gravimetric analysis of precursor was carried out. The X-ray diffraction study confirms the rhombohedral crystal structure without any other impurity phases. The morphology and magnetic properties change with annealing temperature. The saturation magnetization increases linearly and coercivity of the nanoparticles varies significantly as annealing temperature increases. The maximum saturation magnetization and lower coercivity found for the sample heat treated at 1200 °C are 52.5 emu/g and 10.7 Oe respectively.     

Pulsed laser deposition of oriented barium ferrite (BaFe<Subscript>12</Subscript>O<Subscript>19</Subscript>) thin films

Barium ferrite (BaFe₁₂O₁₉) thin films have been deposited by pulsed laser deposition at 900 °C in 250 mTorr oxygen on Si substrates with Pt(111) underlayers. The barium ferrite films contained platelet grains and a small amount of acicular grains, with sizes of 300 nm and 80×300 nm, respectively, and had a surface roughness of 11 nm. Vibrating-sample magnetometer measurements indicated that the BaFe₁₂O₁₉ films have some perpendicular orientation, with a perpendicular squareness of 0.64 and an in-plane squareness of 0.28. The saturation magnetization is about 190 emu/cc. The perpendicular and in-plane coercivities are 2.1 kOe and 1.6 kOe, respectively. PACS 75.50.Ss; 75.60.Ej; 75.70.Ak; 68.55.Ik     

Influence of annealing temperature on structural, optical and magnetic properties of Zn0.95Cu0.02Cr0.03O powders

Zn_0.95Cu_0.02Cr_0.03O powders have been synthesized by the sol-gel method and sintered in argon atmosphere under different temperatures. The structural, optical and magnetic properties of the powders were investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), photoluminescence (PL) and vibrating sample magnetometer (VSM). The XRD results demonstrated that Cr and Cu ions are incorporated into ZnO successfully when annealing temperatures were 600 and 700 °C. But when the samples were annealed at 500 °C, the crystallinity of the samples was not very good. However, when the annealing temperature was increased to 800 °C, the secondary phase of Cu and ZnCr₂O₄ appeared in the samples. The PL spectra revealed that the position of the ultraviolet (UV) emission peak of the samples showed a blue shift and the green emission peak enhanced significantly with the annealing temperature increasing from 600 to 700 °C. Magnetic measurements indicated that the room temperature ferromagnetism of Zn_0.95Cu_0.02Cr_0.03O was intrinsic in nature. In addition, the saturation magnetization (Ms) increased from 0.0078 to 0.0088 emu/g with the annealing temperature increased from 600 to 700 °C.     

Annealing effect on the optical properties in Si delta-doped Al0.24Ga0.76As/In0.15Ga0.85As/GaAs pseudomorphic high electron mobility transistor structures

The optical properties of Si delta-doped Al_0.24Ga_0.76As/In_0.15Ga_0.85As/GaAs pseudomorphic high electron mobility transistor structure (PHEMTs) are estimated after the process of rapid thermal annealing (RTA) in the temperature range 500–750°C. After layer intermixing and decrease of 2DEG densities of PHEMTs just occurs around the annealing temperature of 650°C, the 12H transition peak at 1.354 eV above the annealing temperature of 650°C is newly observed from the photoluminescence (PL) and photoreflectance (PR) spectra. From the results of PL and PR measurements in the annealed PHEMTs, it is found that remarkable modification of band profile in InGaAs QW occur at annealing temperature above 650°C.