反应物分散条件对Li1+xV3O8电化学性能的影响

以Li₂CO₃和NH₄VO₃为原料,在不同条件下合成了锂离子电池正极材料用Li_1+xV₃O₈。研究了反应物的分散条件和煅烧温度对产物晶型结构、形貌及电化学性能的影响。 XRD、IR和SEM结果表明,用超声波在无水乙醇中分散反应物得到的前驱体于550 ℃下煅烧,所得产物Li_1+xV₃O₈结晶度低、粒径小、形貌均匀。 充放电、循环伏安等结果表明,该材料在充放电过程中极化低、嵌脱锂位置多、循环稳定性好。 在0.5 C放电条件下,第2次循环放电容量达到268 mA·h/g,100次循环后容量仍保持210 mA·h/g以上。     

NO reduction with C3H8 on Co/Al2O3 catalyst. effect of O2 concentration

The selective catalytic reduction (SCR) of NO by propane in excess oxygen-containing gas mixture was studied on Co/Al₂O₃ catalyst. The oxygen concentration is very important for the reaction. The NO conversion to N₂ without oxygen is 3% at 800 K and when the O₂ concentration is raised up to 8% the NO conversion reaches its maximum value of 60% at 800 K. Characterization results by TPR and UV-Vis spectroscopy show that in the catalyst, species strongly interacting with tetrahedral and octahedral Co²⁺ ions in the support are present. This revised version was published online in June 2006 with corrections to the Cover Date.     

丙烷在Ce-Fe/Al2O3/cordierite上选择性催化还原NO

利用凝胶溶胶法和浸渍法制备了Ce-Fe/Al₂O₃/cordierite催化剂,实验研究了其催化丙烷选择性还原NO的特性。结果表明,当铈的负载量从1%增加至5%时,Ce-Fe/Al₂O₃/cordierite的C₃H₈-SCR性能先增强后减弱,3.5Ce-Fe/Al₂O₃/cordierite具有最佳的脱硝性能,在有氧条件下,600℃时可实现96.5%的脱硝效率。Ce的加入能够提升Fe/Al₂O₃/cordierite催化剂的抗硫性能。烟气中通入0.02%的SO₂后,3.5Ce-Fe/Al₂O₃/cordierite催化丙烷还原NO的转化率始终维持在93%,而没有经过Ce修饰的Fe/Al₂O₃/cordierite的NO转化率从88%下降为80%左右。利用XRD、N₂吸附-脱附、SEM、H₂-TPR、吡啶吸附红外光谱等手段研究了催化剂的物理化学性质。结果表明,加入助剂铈能与Fe形成了固溶体,增加催化剂表面Lewis酸浓度和氧化还原能力,从而提高了催化丙烷还原NO的性能。过多的铈引入会减少Fe₂O₃结晶体的形成,不利于在C₃H₈-SCR反应中形成NO₂/NO₃^-物种,从而导致NO还原效率下降。     

Two-stage catalytic system of Sn/Al2O3 and Pt/Al2O3for NO reduction by propene in lean conditions

The Pt/Al₂O₃, Sn/Al₂O₃catalysts were prepared by the single sol-gel method. The two-stage Sn/Al₂O₃and Pt/Al₂O₃catalyst in series for NO reduction with propene were investigated. The coexistance of water vapor enhanced the activity at medium temperature of 300-400^oC, and the NO conversion was above 50% at 225 to 500^oC even in the presence of water vapor and SO₂. This revised version was published online in August 2006 with corrections to the Cover Date.     

Selective catalytic reduction of NO over metal oxide or noble metal-doped In2O3/Al2O3 catalysts by propene in the presence of oxygen

The activities of metal oxide CuO, SnO₂, CoO, Ag₂O, ZnO or noble metal Pt, Pd, Rh-doped In₂O₃/Al₂O₃ catalysts for selective catalytic reduction of NO by propene were investigated. The temperature windows for NO reduction over noble metal-doped In₂O₃/Al₂O₃ catalysts were shifted and broaden slightly compared with single component catalyst alone. This revised version was published online in June 2006 with corrections to the Cover Date.     

Preparation of Li4Ti5O12 Microspheres with a Pure Cr2O3 Coating Layer and its Effect for Lithium Storage

The pure Cr₂O₃ coated Li₄Ti₅O₁₂ microspheres were prepared by a facile and cheap solutionbased method with basic chromium(III) nitrate solution (pH=11.9). And their Li-storage properties were investigated as anode materials for lithium rechargeable batteries. The pure Cr₂O₃ works as an adhesive interface to strengthen the connections between Li₄Ti₅O₁₂ particles, providing more electric conduction channels, and reduce the inter-particle resistance. Moreover, LixCr₂O₃, formed by the lithiation of Cr₂O₃, can further stabilize Li₇Ti₅O₁₂ with high electric conductivity on the surface of particles. While in the acid chromium solution (pH=3.2) modification, besides Cr₂O₃, Li₂CrO₄ and TiO₂ phases were also found in the final product. Li₂CrO₄ is toxic and the presence of TiO₂ is not welcome to improve the electrochemical performance of Li₄Ti₅O₁₂ microspheres. The reversible capacity of 1% Cr₂O₃-coated sample with the basic chromium solution modification was 180 mAh/g at 0.1 C, and 134 mAh/g at 10 C. Moreover, it was even as high as 127 mAh/g at 5 C after 600 cycles. At-20℃, its reversible specific capacity was still as high as 118 mAh/g.     

固体电解质Li4.4M0.4Si0.6O4-xLi2O(M=Al,B)的低温合成及导电性

用溶胶－凝胶法,于７００℃合成了Ｌｉ４．４Ｍ０．４Ｓｉ０．６Ｏ４－ｘＬｉ２Ｏ（Ｍ＝Ａｌ,Ｂ;ｘ＝０．００－０．５０）离子导体材料,并用ＤＴＡ－ＴＧ、ＸＲＤ、ＳＥＭ及交流阻抗等技术对样品进行了测试,结果发现：用溶胶－凝胶法可降低Ｌｉ４．４Ｍ０．４Ｓｉ０．６Ｏ４的合成温度,随Ａｌ,Ｂ的掺杂,可提高基质材料的离子导电性,同时随Ｌｉ２Ｏ的掺入可增强样品的致密性并提高了其离子的导电性能。     

273.15 K下Li2B4O7-LiCl-H2O体系热力学性质的等压研究及离子作用模型

用等压法研究了273.15 K下Li₂B₄O₇-LiCl-H₂O体系不同质量摩尔浓度分数的等压平衡浓度和水活度; 计算了LiCl和Li₂B₄O₇混合盐溶液的渗透系数等热力学性质. 用273.15 K下的实验数据对Pitzer离子相互作用模型进行了参数化研究, 拟合求取了273.15 K下Pitzer离子相互作用参数, 用获得的参数计算了LiCl和Li₂B₄O₇在Li₂B₄O₇-LiCl-H₂O体系中的活度系数. 273.15 K下由相应的Pitzer模型计算的渗透系数值与实验结果一致. 这对完善含锂、硼盐湖卤水体系的热力学模型具有重要意义.     

微乳液法制备Pt-S2O82-/ZrO2-Al2O3型固体超强酸催化剂及其异构化性能

采用微乳液法负载Pt制备了Pt-S2O82-/ZrO2-Al2O3(Pt-SZA-M)固体超强酸催化剂, 以正戊烷异构化反应为探针, 对比了微乳液法和浸渍法负载Pt制备的催化剂(Pt-SZA)的异构化性能, 并采用XRD, FTIR, BET, TG-DTA, TPR和TEM对催化剂进行了表征. 结果表明, 与Pt-SZA催化剂相比, Pt-SZA-M催化剂中Pt粒子的粒径更小(4.5 nm)且尺寸更均一; Pt-SZA-M催化剂的比表面积(109.6 m2/g)比Pt-SZA催化剂(95.0 m2/g)增加了15.4%. Pt-SZA-M催化剂的初始还原温度比Pt-SZA催化剂降低了10~20℃, 表明微乳液法负载Pt可以提高催化剂的氧化活性, 提高氢分子在催化剂上的吸附解离能力. 异构化活性实验结果表明, 与Pt-SZA催化剂相比, Pt-SZA-M催化剂的低温活性得到明显改善, 在反应压力为2.0 MPa、 氢烃摩尔比为4: 1、 质量空速为1.0 h-1的条件下, Pt-SZA-M催化剂在反应温度为230℃时活性达到60.8%, 在100 h内异戊烷的收率可稳定在58.0%左右, 选择性在95.0%以上.     

还原-氧化预处理对Co_3O_4催化分解N_2O性能的影响

采用液相沉淀法制备了Co_3O_4催化剂,并对其进行还原-氧化预处理制得Co_3O_4-RO。通过XRD、N_2-physisorption、Raman、H_2-TPR、XPS和O_2-TPD等技术对催化剂进行表征,在连续流动微反应装置上考察了催化剂催化分解N_2O性能。结果表明,经过还原-氧化预处理,与Co_3O_4催化剂相比,Co_3O_4-RO结晶度变差,晶粒粒径减小,尤其是尖晶石结构重构过程削弱了Co-O键,增强了催化剂表面的氧物种脱附能力,降低了催化分解N_2O反应的活化能,因而显著提高了催化剂的催化活性。同时,Co_3O_4-RO对原料气中的O_22%(体积分数)和H_2O 2. 3%(体积分数)表现出较强的耐受性。     

Pt-Al2O3 catalyst and discharge plasma pre-treatment techniques for enhancing selective catalytic reduction of nitrogen oxides: a comparative study

Summary This paper reports the effect of pretreatment of the gas stream by two different oxidation techniques, viz. by a noble metal catalyst and electric discharge plasma on selective catalytic reduction of nitrogen oxides.     

放电温度对LiNi3/8Co2/8Mn3/8O2电化学性能的影响

采用X射线衍射（XRD）、X射线光电子能谱（XPS）、恒流充放电、循环伏安及交流阻抗法，研究了放电温度对LiNi3/8Co2/8Mn3/8O2的倍率特性、锂离子扩散及电荷传递的影响.结果表明， 提高放电温度可显著改善LiNi3/8Co2/8Mn3/8O2的放电容量与倍率放电性能.尽管温度升高使电荷传递活性与锂离子扩散速度都增加，但电荷传递活化能比锂离子扩散活化能大一倍多，表明电荷传递步骤是其电化学反应控制步骤.温度对其电荷传递的影响大于对锂离子扩散的影响.温度升高，电荷传递速率加快，电化学嵌入-迁出反应加速，是其放电容量与倍率放电特性显著改善的主要原因.     

掺加Nd和K改性对Co3O4催化分解N2O活性的影响

用水热法和共沉淀法分别制备了Nd-Co₃O₄催化剂,催化分解N₂O。其中,水热法制备的Nd-Co₃O₄催化活性较高。在不同组成的Nd-Co₃O₄中,优化出了较高活性的0.01Nd-Co₃O₄催化剂,在其表面浸渍K₂CO₃溶液制备K改性催化剂（K/Nd-Co₃O₄）。用X射线衍射（XRD）、N₂物理吸附、扫描电镜（SEM）、X射线光电子谱（XPS）、程序升温还原（H₂-TPR）、O₂程序升温脱附（O₂-TPD）等技术表征催化剂结构。结果表明,Nd-Co₃O₄和K改性催化剂均为尖晶石结构;K改性弱化了催化剂表面Co-O键,有利于表面氧的脱除,提高了催化剂活性。有氧有水气氛350 ℃连续反应40 h,K/Nd-Co₃O₄催化剂上的N₂O分解率超过90%,稳定性较好。     

γ-Al2O3对SCR脱硝催化剂V2O5-WO3/TiO2的改性研究

采用溶胶凝胶法制备了不同γ-Al₂O₃含量的钛铝复合载体,以此为载体采用浸渍法负载V₂O₅和WO₃制备了一系列催化剂。采用X射线衍射(XRD)、比表面积测定(BET)、程序升温还原(H₂-TPR)、高分辨率透射电子显微镜(HRTEM)等表征技术对催化剂表面形态进行分析,同时在模拟氨气选择性催化还原NO(NH₃-SCR)的反应条件下,对催化剂的脱硝反应活性和SO₂抗中毒进行考察。结果发现,TiO₂和γ-Al₂O₃之间的协同作用使得V₂O₅-WO₃/TiO₂-γ-Al₂O₃催化剂的脱硝效率及活性窗口明显优于单一载体制备的催化剂,表现出了良好的热稳定性和抗SO₂毒化能力,特别是V₂O₅-WO₃/TiO₂-15% γ-Al₂O₃在310~460 ℃,NO的转化率均在80%以上,反应窗口最宽。各种表征结果表明,TiO₂-γ-Al₂O₃复合载体中γ-Al₂O₃高度分散在TiO₂上,复合载体具有较大的比表面积,同时具有较强的还原能力。     

298.15 K Li2B4O7-MgCl2-H2O体系热力学性质的电动势法测定及离子相互作用模型的研究

测定了298.15 K下, 无液接电池Li-ISE│Li₂B₄O₇ (m_A)(aq.), MgCl₂(m_B)(aq.)│AgCl/Ag的电动势, 利用测定结果计算了Li₂B₄O₇-MgCl₂-H₂O体系离子强度在0.05～3 mol•kg^－1范围内, 不同MgCl₂离子强度分数的溶液中LiCl的平均活度系数, 并给出了其随离子强度I, B₄O₇^2－和Mg^2＋浓度的变化规律. 结合以往关于该体系和Li₂B₄O₇-LiCl-H₂O, Li₂B₄O₇-H₂O体系的等压研究结果, 用迭代和多元线性回归方法对Li^＋-Mg^2＋-Cl^－-B₄O₇^2－-H₂O体系的离子相互作用模型进行了研究. 具体方法为考虑了该体系在不同的总硼浓度范围H₃BO₃, B(OH)₄^－, B₃O₃(OH)₄^－和B₄O₅(OH)₄^2－四种含硼化合物的存在以及各硼化合物间的化学平衡, 以修正了的Pitzer渗透系数方程和活度系数方程为基础, 对该体系的等压法和电动势法研究结果进行最小二乘拟合, 拟合的标准偏差为0.0167, 用该模型计算的该体系的渗透系数、活度系数与实验值基本一致.     

尖晶石结构材料Li_2MgTi_3O_8的制备及其电化学性能

以Li2CO3、MgO和TiO2为原料,采用高温固相法合成了具有尖晶石结构材料Li2MgTi3O8。采用X射线衍射(XRD)、傅里叶红外光谱(FTIR)等手段对材料的晶体结构进行了表征,材料的电化学性能通过恒流充放电、循环伏安(CV)进行测试。结果表明,材料具有优异的循环稳定性和良好的库伦效率。在室温下,充放电倍率为0.5C时,Li2MgTi3O8首次放电比容量为215.6mAh·g-1,100周循环后保持在225mAh·g-1。     

商业V_2O_5-WO_3/TiO_2烟气SCR脱硝催化剂CaSO_4中毒机理研究

基于商业V_2O_5-WO_3/Ti O_2脱硝催化剂,设计了两种模拟Ca SO_4中毒的方法,通过比表面积测定(BET)、X射线衍射(XRD)、程序升温还原(H_2-TPR)、扫描电子显微镜(SEM)、原位漫反射傅里叶变换红外光谱(in situ DRIFTS)等表征技术并结合固定床脱硝性能测试平台,对中毒前后催化剂的微观结构、氧化还原能力及表面性质的变化与脱硝活性进行了对比研究,探索硫酸钙中毒机理。研究表明,Ca SO_4会堵塞催化剂孔径,孔径小于2.7 nm和孔径大于17.8 nm时Ca SO_4的影响更大,从而使催化剂的比表面积和孔体积变小;Ca SO_4中毒会导致Brnsted酸位数量和强度的降低,同时Lewis酸强度也会减弱,从而阻碍了NH_3的吸附,Ca SO_4引起催化剂氧化还原能力的降低。     

Co/Fe/Al2O3/cordierite催化C3H6选择性还原NO的实验研究

采用溶胶凝胶法和浸渍法制备了负载于蜂窝陶瓷上的Co/Fe/Al₂O₃/cordierite催化剂,在陶瓷管流动反应器上对其催化C₃H₆选择性还原NO的性能进行了测试。结果表明,该催化剂表现出最优脱硝性能,在模拟烟气条件下,当反应温度为550 ℃时可实现97%的脱硝效率。Co的引入可显著增强Fe/Al₂O₃/cordierite催化剂抗SO₂和H₂O的能力。在模拟烟气中同时引入0.02% SO₂和3% H₂O后,1.5Co/Fe/Al₂O₃/cordierite的脱硝性能受影响甚微,当反应温度高于500 ℃时1.5Co/Fe/Al₂O₃/cordierite催化C₃H₆还原NO的效率均可达到90%以上;相比之下,未经Co修饰的催化剂Fe/Al₂O₃/cordierite脱硝性能受到了严重的抑制,在整个反应温度区间（200-700 ℃）内,其催化C₃H₆还原NO的效率最高不足50%。XRD和SEM表征结果表明,经过适量的Co修饰后的1.5Co/Fe/Al₂O₃/cordierite表面变得更疏松,且形成了以钴铁和钴铝双金属氧化物为主要成分的球状晶粒。H₂-TPR结果表明,相比于Fe/Al₂O₃/cordierite,1.5Co/Fe/Al₂O₃/cordierite有更好的低温还原性能。Py-FTIR结果表明,Co的引入可使催化剂表面的Lewis酸明显增加,且生成了Brønsted酸。N₂吸附-脱附表征结果表明,Co可增大催化剂的比表面积。     

SO_4~(2-)功能化处理对Fe_2O_3催化剂上氨选择性催化还原NO_x性能的促进机理研究

采用沉淀法制备了Fe(OH)_3和Fe_2O_3。通过硫酸化处理得到SO_4~(2-)/Fe(OH)_3和SO_4~(2-)/Fe_2O_3两种催化剂,并将其应用于氨选择性催化还原NO_x(NH_3-SCR)反应,研究了SO_4~(2-)功能化处理对Fe_2O_3催化剂上NH_3-SCR脱硝性能的促进机理。结果表明,与纯的Fe_2O_3相比,硫酸化处理得到的催化剂上SCR活性得到显著提升;其中,SO_4~(2-)/Fe(OH)_3表现出更加优异的催化性能,在250-450℃时NO_x转化率高于80%,且具有优异的稳定性和抗H_2O+SO_2性能。XRD、Raman、TG、FT-IR、H_2-TPR、NH_3-TPD和in situ DRIFTS等表征结果显示,硫酸功能化处理能抑制Fe_2O_3的晶粒生长,同时SO_4~(2-)与Fe~(3+)结合形成硫酸盐复合物,提高了催化剂表面酸性位点的数量和酸强度,抑制了Fe_2O_3上的氨氧化反应,从而提高了其脱硝催化性能。     

燃煤烟气中砷对V_2O_5-WO_3/TiO_2 SCR脱硝催化剂性能的影响

通过将商业V_2O_5-WO_3/TiO_2脱硝催化剂暴露于含As_2O_3烟气中,制备了砷中毒催化剂,并运用X射线衍射(XRD)、比表面积(BET)、NH3化学吸附、傅里叶变换红外光谱(FT-IR)、X射线光电子能谱等技术表征分析了砷对催化剂性能的影响,并提出了催化剂砷中毒机理。结果表明,砷对催化剂具有严重的毒害作用,As_2O_3会吸附在催化剂表面,并被催化剂氧化形成As_2O_5覆盖层,减小催化剂比表面积,减少催化剂V活性位,阻止催化剂对NH3的吸附,造成催化剂失活。