Influence of Fe_2O_3 Impurity on the Crystalline Structure of Cordierite Synthesized from Waste Aluminum Slag

1 INTRODUCTION Aluminum waste slag from aluminum factories isused as the main material to produce cordierite re-fractory material. The slag’s main composition is γ-AlOOH, which will convert into α-Al2O3 [1] at hightemperature, thus the product’s refractoriness can beimproved. Cordierite has good thermal stability andcan be widely served as high quality refractory ma-terial, electron encapsulating material, catalyst carrier,foamed ceramics, etc.[2]. Compared with th…     

Influence of Impurity Na2O on Crystalline Structure of Cordierite Synthesized from Aluminum Sludge

Waste aluminum sludge, talc powder and clay were used to synthesize cordierite in this research. The impurities, such as Fe2O3, CaO, K2O and Na2O, in the raw materials have some influence on the structures and properties of the materials. In this paper, we mainly discuss the impact of impurity Na2O on the structure of cordierite, based on which the permitted amount of Na2O was determined. The results show that Na2O with the amount less than 0.6% has little influence on the cordierite formation; while when its amount increasing from 0.6% to 0.7%, the content of cordierite decreases from 86% to 84% and the permitted amount for Na2O in the raw materials is less than 6% with the best amount less than 0.3%. X‘pert plus software analysis results show the impurity Na2O has no influence on the cordierite space group and only the lattice parameters vary slightly; but it has much influence on the structure of Mg-AI spinel and the lattice parameters are much changed.     

CaO杂质对铝型材厂工业污泥合成堇青石材料晶相结构及其含量影响

探讨原料组成对铝型材厂工业污泥合成堇青石材料的影响是非常重要的。研究目的有助于确定不同杂质在原料中允许的存在量,为选择其他原料提供可靠的依据。采用XRD法和SEM法分析各试样的晶相结构:用半定量分析方法确定各晶相的含量:用philipsX抪ertplus软件确定试样中各晶相结构参数。实验结果表明:CaO杂质含量从1.2~2.5%对合成堇青石有利:从2.5~2.8%堇青石含量开始下降:确定2.5%为CaO杂质最佳存在量,其对应的堇青石含量为91%。经plus软件确定结果:CaO杂质含量为1.2%时,其结构与单晶相同,晶胞参数变化很小:CaO含量从1.2~2.8%,其晶系由六方转变为四方结构,晶胞参数发生较大变化。镁铝尖晶石结构与晶胞参数变化较大,由单晶的立方结构转变为四方结构。     

利用铝废渣制备片状堇青石的影响因素研究

以铝厂废渣、高岭土、滑石为主要原料,采用固相法合成片状堇青石。分析了原料种类、原料配方、烧结温度、保温时间和晶核剂对合成堇青石的影响,并通过XRD、SEM进行表征。结果表明,原料的纯度越高合成的堇青石纯度越高;富含镁的配方能完全形成堇青石相;最佳烧成温度为1 380℃,保温时间为4 h,此时得到的堇青石纯度最高,且呈现片状结构,颗粒大小均匀;堇青石熟料可以起到晶核剂的作用,促进堇青石的生成。     

反应温度与时间对铝型材厂工业污泥合成堇青石材料的得率与晶相结构影响

本研究主要探讨反应温度和反应时间对铝型材厂工业污泥合成堇青石材料的得率和晶相结构的影响。该污泥系由铝型材表面处理时产生的大量废液, 经沉淀过滤所得。主要成分是一种超细的γ-AlOOH, 其中部分是晶体, 部分是无定形体, 活性很高, 有利于堇青石晶相的形成, 能降低反应温度。 实验结果表明: 堇青石含量随着反应温度升高而增加; 晶相结构和晶胞参数与反应温度有关; 确定1350℃为最佳的反应温度; 反应时间在 2~5 h的试样中,堇青石含量增加, 在5~6 h含量降低. 5 h为最佳的反应时间。     

Influence of Fe203 Impurity on the Crystalline Structure of Cordierite Synthesized from Waste Aluminum Slag

The influence of Fe203 impurity on the crystalline structure of cordierite synthesized from waste aluminum slag is discussed. XRD and SEM techniques were employed to characterize the crystalline structure and microstructure of each specimen. Philips X‘pert plus software was used to determine the lattice parameters of each specimen. The results show that the Fe2O3 content of 0.8-1.6wt% is beneficial to the formation of cordierite, with the cordierite amount reaching 90wt%. So 0.8-1.6wt% is considered as the allowable Fe2O3 content in the specimens and 0.8wt% is determined to be the best after overall analysis. Plus software analysis shows that the cordierite in each specimen has the same symmetrical hexagonal structure as the single crystal, and the lattice parameters as well as the lattice dimensions change slightly.     

Influence of Fe2O3 and V2O5 on Crystalline Structure of Mg-Al Spinel Synthesized by Waste Aluminum Slag

Mg-Al spinel is synthesized by using industrial waste-residue and basic magnesium carbonate in the aluminum factory as the main raw materials. The influence of V2O5 and Fe2O3 mineralizers on the structure, cell parameters and microscopic morphology of synthesized Mg-Al spinel has been discussed. The Mg-Al spinel is characterized by using XRD, SEM and relevant analytical software, such as Philips plus, Rietveld quantification and so on. The experimental results show that certain amounts of V2O5 and Fe2O3 are beneficial to the formation of Mg-Al spinel, and the optimum addition of V2O5 and Fe2O3 is respectively 2wt% and 3wt%. V2O5 has few effects on cell parameters of Mg-Al spinel; but Fe2O3 can form solid solution with Mg-Al spinel in which Mg-Fe spinel can also dissolve to form continuous solid solution. Therefore, with the increase of Fe2O3 content, the cell parameters of Mg-Al approximately present linear increase.     

菱镁矿风化石与叶腊石合成堇青石的结构表征

采用菱镁矿风化石、叶腊石、二氧化硅微粉为主要原料,研究分析烧成温度对合成堇青石结晶度、晶粒尺寸、晶相组成和显微结构来确定适宜的合成温度。用X′ Pert plus软件对X射线衍射图进行拟合,分析试样的结晶度,用半定量(semi-quantification)法对试样结晶相中晶相组成进行计算,用Scherrer公式计算试样中堇青石、方石英晶粒的粒径大小。结果表明：采用菱镁矿风化石与叶腊石为原料合成堇青石,当温度由1 350 ℃增加到1 400 ℃,试样的结晶度增加,堇青石晶粒尺寸和堇青石相量增加,在1 400 ℃时,试样结晶度最高,晶粒尺寸最大。晶相组成中堇青石相占67%,方石英相占33%。当温度大于1 400 ℃,试样结晶度降低,堇青石和方石英晶粒尺寸减小,当温度在1 500 ℃时,堇青石相消失,促进了方石英相析出。采用菱镁矿风化石与叶腊石为原料合成堇青石的最佳烧成温度为1 400 ℃。     

Studies on the Influence of Sintering Temperature on Crystalline Structures of Mg-Al Spinel Synthesized by Waste Aluminum Slag

Mg-Al spinel is synthesized by using industrial waste-residue and basic mag- nesium carbonate in the aluminum factory as the main raw materials. The influence of sintering temperature on crystalline structure and microstructure of Mg-Al spinel has been mainly discussed. The crystalline structure of sample is characterized by using XRD, SEM and relevant analytical software. The experimental results show that compared to the conventional synthetic method, the application of waste aluminum slag as the raw material can greatly decrease the synthetic tem- perature. The content of Mg-Al spinel first increases and then decreases with the rise of sintering temperature, and its purity can reach as high as 96wt% at 1550 ℃, which is therefore determined to be the optimum synthetic temperature. SEM observations demonstrate that as the rise of sintering temperature, the grain of Mg-Al spinel grows up obviously with typical octahedral characteristic appearance.     

Influence of Cr2O3 on the Structure and Property of Mg-Al Spinel Synthesized by Waste Slag in Aluminum Factory

Via the solid phase reaction, Mg-Al spinel has been synthesized by using industrial waste slag from aluminum factory, basic magnesium carbonate and a little amount of clay as the main raw materials. The influences of Cr2O3 mineralizer on crystalline structure, micro-morphology and properties of synthesized Mg-Al spinel are discussed. The synthesized product was characterized by using XRD and SEM, and the relative contents of each crystalline phase are calculated by relevant analytical software such as Philips plus, Rietveld quantification and so on. The experimental results show that a certain amount of Cr2O3 is helpful to the formation of Mg-Al spinel, and when the addition of Cr2O3 is 2.0%, Mg-Al spinel in the system exists in the form of solid solution (Mg0.68Al0.32)(Al0.84Mg0.16)2O4 whose content is the highest reaching 91%. Then the corresponding indexes of each property are as follows: water absorption 3.0%, apparent porosity 9.8%, bulk density 3.36 g·cm-3, and flexural strength 83.32 MPa. Therefore, we can confirm that the optimum addition of Cr2O3 mineralizer is 2.0%.     

Influence of MnO_2 Mineralizer on the Crystal Structure,Properties of SiC Kiln Furniture Bonded with Fine Silicon Powder

lINTRODUCTIONSiCkilnfllrniturepossessesgoodhigh-temperaturepropertiesandsmoothness.Itishighlyresistanttowarddeforming,slaggingandthermalshock.Thefurniturecanpracticallyresultinimprovingqualityandproductionofceramicsandiswidelyusedovertheworld.However,SiChassinteringtemperatureofupto2OOO:Ct13landitisdifficulttosinterasproductbyusingcommonkilnfurnace.Toserveashigh-temperaturerefractorykilnfurniture,itmustbemixedwithabonder.Thisworkus-esfinesiliconpowderasabonder,whichisadustproducedfroms…     

铝厂污泥在不同煅烧温度的晶相结构研究

铝厂污泥主要成分是-AlOOH,其中部分是晶体,部分是无定形体。将此污泥分别于450,600,800,1000,1050,1200和1300 ℃进行了煅烧,探讨污泥在不同温度下的晶相变化,为污泥的综合利用提供可靠的数据。采用XRD法和SEM法表征了污泥在不同温度下的晶相结构和显微结构。实验结果表明:随着煅烧温度的提高,污泥发生如下变化过程: 这与常规转化规律不同。在450,600,800,1000和1100 ℃的试样中均形成了-Al2O3和无定形体结构的微晶,随着温度的升高,-Al2O3含量增加而无定形体结构的微晶含量降低。当煅烧温度上升至1200和1300 ℃时, - Al2O3和无定形体结构的微晶全部转变为 - Al2O3。 -Al2O3是介稳态,高活性,-Al2O3是稳定态,低能态。     

液相合成超薄TiO2纳米片微结构影响因素研究

二维纳米结构二氧化钛由于表面活性位点剧增可带来光催化活性的显著提高.本文通过液相法在低温条件下合成大尺寸TiO₂纳米片,重点研究溶液中硝酸浓度、熟化温度和反应物浓度对其二维结构形成过程的影响.采用透射电子显微镜（TEM）表征样品的微观形态,并结合紫外-可见吸收光谱、X射线衍射谱（XRD）、X射线光电子能谱（XPS）和傅立叶变换红外光谱分析样品的微结构性质.采用光催化还原Cr （VI）作为指示反应,评估各制备参数对二氧化钛光催化性能的影响.结果表明,硝酸浓度为0.0217~0.0721 mol·L^-1的样品在0~4℃条件下胶溶及熟化时可得到具有显著量子尺寸效应的超薄锐钛矿型TiO₂纳米片;硝酸浓度过高引起样品晶型和形态的转变,过低导致胶溶时间延长;熟化温度超过4℃会破坏二维结构的形成;提高反应物中乙醇的用量有助于分散水解产物,促进胶溶和二维结构的形成进程.     

Influence of Pore-expansion Agent on the Structure and Performance of Activated Alumina Synthesized from Waste Aluminum Sludge

1 INTRODUCTION The reactivity of activated alumina adsorbent is closely related to its specific surface area: the larger the specific surface area, the better its activity and adsorbent capability are. However, in reality, the prac- tically available specific surface area or effective spe- cific area has relationship with its pore structure[1]. Since many reactant molecules are difficult to enter the pores to react with whose radius is shorter than certain critical value, the increase of p…     

Study on the In-situ Synthesis of Aluminum Titanate Sintered by Waste Aluminum Slag

Aluminum titanate was in-situ synthesized by using industrial waste-residue in the aluminum factory and TiO2 as the main raw materials and the influence of different reaction temperatures on the purity and microstructures of synthesized products were mainly discussed. The obtained Al2TiO5 was characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and relevant analytical software. The results show that elevating the sintering temperature can increase the content of aluminum titanate; and at 1420 ℃, it reaches the highest in the synthesized ceramic. When the sintering temperature continues to increase, the produced aluminum titanate will decompose resulting in the drop of its content. Therefore, the optimum sintering temperature of in-situ synthesis of aluminum titanate is determined as 1420 ℃, at which the grains of aluminum titanate grow completely, the purity of aluminum titanate is 89.3wt%., the highest density is 2.75 g/cm^3, and the porosity is 9%.     

堇青石窑具多晶结构与性能研究

利用X-射线衍射分析和电子显微镜分析的结果，确定堇青石窑具的多晶结构和各晶相的含量；结合窑具性能的研究，确定堇青石窑具具有优良性能的适宜配方。     

NaA,MAP和MAX高铝沸石的结构定向及其转晶

本文根据不同沸石的结构特点及其在晶化动力学上的差异,由化学组成相近的硅铝凝胶混合物(投料Si/Al比约为1)定向合成出具有不同骨架结构的高铝沸石—NaA,MAP和MAX。考察了沸石晶化过程中晶化导向剂、晶种以及金属阳离子在合成高铝沸石的结构导向作用以及上述三种高铝沸石间的转晶规律。同时本文首次发现了MAP沸石的“室温固相转晶”现象。     

溶胶-凝胶-水热法制备Ce-Si/TiO2及其可见光催化性能

以钛酸四正丁酯、正硅酸乙酯、六水硝酸铈为原料,在140℃下通过溶胶-凝胶-水热法水解制备Ce-Si/TiO2.所得样品用X射线衍射、氮吸附、透射电镜、紫外漫反射、傅里叶变换红外光谱、X射线光电子能谱等测试手段分析,结果显示400-600℃条件下焙烧所有样品均为锐钛矿,样品具有较大的比表而积,Si和Ce均被引入到TiO2中.在可见光照射下,以脱色降解罗丹明B为探针反应,研究其可见光催化性能,结果表明,与末掺杂和单一组分掺杂的二氧化钛相比较,共掺杂的二氧化钛具有更高的催化性能,当Ce/Ti和Si/Ti的物质的量比分别为0.010和0.10时,可见光催化性能最好.     

K_2O矿化剂对硅微粉结合SiC窑具析晶结构,性能与氧化动力学影响的研究

在硅微粉结合SiC窑具中添加适量的K2O矿化剂，能使体积效应大的a-方石英转化成体积效应小的α-鳞石英，其矿化能力与MnO2相当[1]，但比MnO2矿化剂更有适用价值。采用XRD法确定析晶结构及其含量，探讨析晶结构对窑具性能的影响，从中确定最佳的K2O添加量为1．5％。     

Thermal stability of anatase TiO2 aerogels

Titanium dioxide (TiO₂) aerogels were prepared with sol–gel ambient pressure drying method by using titanium tetrachloride (TiCl₄) as precursor and tetraethoxysilane as modifier, calcinated at different temperature and characterized by X‐ray diffraction, transmission electron microscopy and small angle X‐ray scattering. The results showed that the TiO₂ aerogels remained amorphous under 500 °C, changed to anatase from 600 °C and further changed to rutile from 900 °C. Between 60 °C and 500 °C, the primary particles within the samples concentrated mainly upon small sizes, enlarged and diverged remarkably above 600 °C. The crystalline grains grew and agglomerated with the rise of the calcination temperature. The TiO₂ aerogels at a temperature higher than 800 °C have better stability than anatase because of the formation of partial Ti―O―Si bonds. Copyright © 2016 John Wiley & Sons, Ltd.