Synthesis and luminescence properties of Gd6MoO12:Yb3+, Er3+ phosphor with enhanced photoluminescence by Li+ doping

Yb³⁺/Er³⁺ co-doped Gd₆MoO₁₂ and Yb³⁺/Er³⁺/Li⁺ tri-doped Gd₆MoO₁₂ phosphors were prepared by adjusting the annealing temperature via the high temperature solid-state method. Under the excitation of 980 nm semiconductor, the upconversion luminescence properties were investigated and discussed. In the experimental process, we get the optimum Yb³⁺ concentration and the concentration quench effect will happen while the concentration extends the given region. According to the Yb³⁺ concentration quenching effects, the critical distance between Yb³⁺ ions had been calculated. The measured UC luminescence exhibited a strong red emission near 660 nm and green emission at 530 nm and 550 nm, which are due to the transitions of Er³⁺(⁴F_9/2, ²H_11/2, ⁴S_3/2) → Er³⁺(⁴I_15/2). Then the effect of excitation power density in different regions on the upconversion mechanisms was investigated and the calculated results demonstrate that the green and red upconversion is a two-photon process. A possible mechanism was discussed. After Li⁺ ions mixing, the upconversion emission enhanced largely, and the optimum Li⁺ concentration was obtained while fixed the Yb³⁺ and Er³⁺ on the above optimum concentration. This enhancement owns to the decrease of the local symmetry around Er³⁺ after Li⁺ ions doping into the system. This result indicates that Li⁺ is a promising candidate for improving luminescence in some case.     

Erbium-doped lead silicate glass for near-infrared emission and temperature-dependent up-conversion applications

Erbium-doped lead silicate glass has been investigated for near-infrared emission and up-conversion applications. Near-infrared emission due to ⁴I_13/2 → ⁴I_15/2 transition of Er³⁺ is relatively broad (70.5 nm) and long-lived (3.7 ms). Also, up-conversion luminescence spectra of Er³⁺ ions in lead silicate glass have been examined as a function of temperature. The relative intensities of luminescence bands corresponding to ²H_11/2 → ⁴I_15/2 and ⁴S_3/2 → ⁴I_15/2 transitions of Er³⁺ were determined with temperature. The fluorescence intensity ratio and temperature sensitivity were calculated. The maximum sensitivity for Er³⁺ doped lead silicate glass is close to 26.4 × 10^?4 K^?1 at T = 590 K.     

Upconversion luminescence in Tm3+/Yb3+co-doped lead tungstate tellurite glasses

This work reports the upconversion luminescence properties of Tm³⁺/Yb³⁺ ions in lead tungstate tellurite (LTT) glasses. Judd–Oflet intensity parameters have been obtained from the absorption band intensities of Tm³⁺ singly-doped and Tm³⁺/Yb³⁺ co-doped LTT glasses. The spontaneous emission probabilities, radiative lifetimes and branching ratios for ¹G₄ and ³H₄ emission levels of Tm³⁺ have been determined. Upconversion luminescence has been observed by exciting the samples at 980 nm (Yb³⁺:²F_7/2→²F_5/2) at room temperature. Four upconversion emission bands corresponding to the ¹G₄→³H₆ (477 nm), ¹G₄→³F₄ (651 nm), ¹G₄→³H₅ (702 nm) and ³H₄→³H₆ (810 nm) transitions have been identified. The relative variation in the intensities of upconversion bands, the different channels responsible for upconversion spectra and the effect of Yb³⁺ ions concentration on the upconversion luminescence of Tm³⁺ ions have also been discussed.     

Quasi-one dimensional Er3+–Yb3+ codoped single-crystal MoO3 ribbons: Synthesis,characterization and up-conversion luminescence

The quasi-one dimensional (Q1D) Er³⁺–Yb³⁺ codoped single-crystal MoO₃ ribbons with width range from 1 to 5 μm, and maximum length about 30 μm have been synthesized by the vapor transport method. The samples were characterized using X-ray diffraction, scanning electron microscopy, transmission electron microscope, and luminescence spectra. By a 975 nm laser diode (LD) as excitation source, the blue, green and red emission bands centered at about 408, 532, 553 and 657 nm were detected, which attributed to the ²H_9/2 → ⁴I_15/2, ²H_11/2, ⁴S_3/2 → ⁴I_15/2 and ⁴F_9/2 → ⁴I_15/2 transitions of Er³⁺, respectively. The three-, and two-photon process was responsible for the blue, green and red up-conversion emissions mechanism for the Q1D Er³⁺–Yb³⁺ codoped single-crystal MoO₃ ribbons, respectively. The results suggested that the Q1D Er³⁺–Yb³⁺ codoped single-crystal MoO₃ ribbons will have potential applications in remote bio-imaging and surface enhanced Raman scattering.     

980 nm激发下Er3+/Yb3+共掺杂ZrO2-Al2O3粉末的上转换发光特性

通过固相反应法制备了Er³⁺/Yb³⁺共掺杂ZrO₂-Al₂O₃粉末的样品，并对样品在980nm激光激发下的上转换发光特性进行了研究.从发射光谱可以发现，在可见光范围内有3个强的发光带，一个位于654nm附近的红光带和两个分别位于545nm、525nm附近的绿光带，分别对应于Er³⁺离子的以下辐射跃迁：⁴F_9/2→⁴I_15/2、⁴S_3/2→⁴I_15/2、 ²H_11/2→⁴I_15/2.其中又以Er³⁺离子的⁴F_9/2→⁴I_15/2跃迁产生的红色荧光辐射最强.对其上转换发光机制进行了分析，发现这三个发光过程都是双光子过程.对样品粉末进行了XRD检测，发现ZrO₂主要以立方相为主，并且计算得到了这种立方结构的晶格常数.Al₂O₃固溶于ZrO₂中，Al³⁺嵌入ZrO₂后产生氧空位，导致ZrO₂晶体的对称性降低，这种结构变化更有利于提高上转换效率，即上转换发光强度增强. 关键词： 3+/Yb³⁺')" href="#">Er³⁺/Yb³⁺ 上转换 2-Al₂O₃')" href="#">ZrO₂-Al₂O₃ 荧光 稀土     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Photoluminescence investigations of Li2SiO3:Ln (Ln=Er3+, Eu3+, Dy3+, Sm3+) phosphors

In this study, we report a comprehensive structural and photoluminescence (PL) study on lithium metasilicate (Li₂SiO₃) phosphor ceramics doped with four rare earth (RE) ions. X-ray diffraction (XRD) patterns show a dominant phase, characteristic of the orthorhombic structure Li₂SiO₃ compound and the presence of dopants has no effect on the basic crystal structure of the material. The first excited state Er³⁺ luminescence at 1.54 μm arises from a sharp atomic-like radiative transition between the ⁴I_13/2 state and the ⁴I_15/2 state (ground level) under a 532 nm line of an Ar ion laser excitation. Sm doped samples showed Sm³⁺ emission characteristics corresponding to the some ⁴G_5/2→⁶H_j (j=5/2,9/2,11/2) transitions indicating a strong crystal-field effect. PL spectra of Eu doped material exhibited peaks corresponding to the ⁵D₀→⁷F_j (j=0,1,2,3 and 4) transitions under 405 nm excitation. The dominant red color emission at 612 nm from the hypersensitive (⁵D₀→⁷F₂) transition of Eu³⁺ indicates the inversion antisymmetry crystal field around Eu³⁺ ion, which is favorable to improve the red color purity. Dy doped samples showed the Dy³⁺ emission characteristic due to the ⁴F_9/2→⁶H_13/2 transition. Their relative intensity ratios also suggested the presence of a symmetric environment around the metal ion. We suggest that lithium metasilicate has enough potential candidates to be a phosphor material.     

Positive influence of Tm3+ on effective Er3+: 3 μm emission in fluoride glass under 980 nm excitation

Er³⁺ and Tm³⁺ singly doped and codoped new fluoride glasses were prepared by traditional melt-quenching method. Efficient 3 μm emission was obtained under 980 nm laser excitation. It is worthy to notice that one of the two ions can be the sensitizer to the other one by depressing the Er³⁺: 1.5 μm emission through the energy transfer process from Er³⁺:⁴I_13/2 level to Tm³⁺:³F₄ level. On the basis of measured absorption spectra, the Judd-Ofelt intensity parameters and radiation emission probability were calculated to evaluate the spectroscopic properties. Additionally, the micro-parameters together with the phonon assistance of Er³⁺:⁴I_13/2 → Tm³⁺:³F₄ and Er³⁺:⁴I_11/2 → Tm³⁺:³H₅ processes were quantitatively analyzed by using Dexter model. The theoretical micro-parameters results meet well with the experiments which indicates that Er³⁺/Tm³⁺ codoped fluoride glass is a potential kind laser glass for 3 μm laser.     

Temporal dynamics of upconversion luminescence in Er3+, Yb3+ co-doped crystalline KY(WO4)2 thin films

Crystalline Er³⁺ and Yb³⁺ singly and doubly doped KY(WO₄)₂ thin films were grown by low-temperature liquid-phase epitaxy. Absorption, luminescence, excitation and temporal evolution measurements were carried out for both Er³⁺ and Yb³⁺ transitions from 10 K to room temperature. Green Er³⁺ upconversion luminescence was observed after Yb³⁺ and Er³⁺ excitation. The mechanisms responsible for the upconversion phenomena detected in each case were identified.     

Microwave sol–gel derived NaCaGd(MoO4)3:Er3+/Yb3+ phosphors and their upconversion photoluminescence properties

Ternary molybdate NaCaGd_1−x(MoO₄)₃:Er³⁺/Yb³⁺ phosphors with the proper doping concentrations of Er³⁺ and Yb³⁺ (x = Er³⁺ + Yb³⁺, Er³⁺ = 0, 0.05, 0.1, 0.2 and Yb³⁺ = 0, 0.2, 0.45) were successfully synthesized by microwave sol–gel method for the first time. Well-crystallized particles formed after heat-treatment at 900 °C for 16 h showed a fine and homogeneous morphology with particle sizes of 3–5 μm. The optical properties were examined comparatively using photoluminescence emission and Raman spectroscopy. Under excitation at 980 nm, the doped particles exhibited a strong 525-nm emission band, a weak 550-nm emission band in the green region, which correspond to the ²H_11/2 → ⁴I_15/2 and ⁴S_3/2 → ⁴I_15/2 transitions, and a very weak 655-nm emission band in the red region, which corresponds to the ⁴F_9/2 → ⁴I_15/2 transition. The optimal Yb³⁺:Er³⁺ ratio was obtained to be 9:1, as indicated by the composition-dependent quenching effect of Er³⁺ ions. The pump power dependence of upconversion emission intensity and Commission Internationale de L’Eclairage chromaticity coordinates of the phosphors were evaluated in detail.     

Visible luminescence of nanocrystalline AlN:Er thin film by co-deposition of AlN,Er, and SiO2

We report a visible luminescence of Er³⁺ ions in an amorphous-nanocrystalline AlN:Er thin film prepared by co-deposition using AlN, Er, and SiO₂ targets. A PL emission spectrum of Er³⁺ in the AlN:Er film annealed at 750 °C showed a strong bluish green emission of Er³⁺ in the amorphous-nanocrystalline AlN:Er thin film, which is attributed to the intra-4fEr³⁺ transitions of ²H_11/2 → ⁴I_15/2 and ⁴F_7/2 → ⁴I_15/2. It was found that crystallite diameters were between 3 and 5 nm by high-resolution transmission electron microscopy. The occurrence of the strong Er³⁺ emission in the annealed AlN:Er thin film with a mixture of amorphous and nanocrystalline phases may be contributed to an increase in the number of excitation Er³⁺ centers and a presence of oxygen related to Er³⁺ excitation and recombination process in the AlN:Er thin film.     

Upconversion mechanisms and thermal effects of Er3+ in Er3+ doped yttria nanocrystals

Efficient Er³⁺:Y₂O₃ phosphor is synthesized by the sol–gel method. Rate equations for Er³⁺ energy level populations are used to investigate pump power and temperature dependences of upconversion intensity as well as the fluorescence decay profiles. Excited state absorption cross section of Er^{3+ 4}I_13/2 of 6.8×10^?27 m² and cross relaxation rate of 6200 s^?1 are determined from comparison between theoretical predictions and experimental data. In addition, it is found that effect of temperature on the phonon-assistant absorption cannot be neglected. This work provides references for the prediction of the upconversion behavior in Er³⁺ singly doped matrix.     

Structural and spectroscopic studies on concentration dependent Er3+ doped boro-tellurite glasses

Er³⁺ doped boro-tellurite glasses have been prepared by the conventional melt quenching technique with the chemical composition (39?x) B₂O₃+30TeO₂+15MgO+15K₂O+xEr₂O₃ (where x=0.01, 0.1, 1, 2 and 3 wt%). The structural analysis of the glasses were made through XRD, FTIR spectral measurements and the optical absorption, luminescence measurements were made to analyze the optical behavior of the prepared glasses. The bonding parameters were determined from the optical absorption spectra and were found to be ionic in nature. The experimental oscillator strengths were determined from the absorption spectra have been used to determine the Judd–Ofelt parameters. The Judd?Ofelt parameters were used to explore the important radiative parameters such as transition probability (A), stimulated emission cross-section (σ_P^E) and branching ratios (β_R) of the emission transitions ²H_9/2→⁴I_15/2 and ²H_11/2 and ⁴S_3/2→⁴I_15/2 of the trivalent erbium ions. The optical band gap energy (E_opt) values corresponding to the direct and indirect allowed transitions and the Urbach energy values of the prepared Er³⁺ doped boro-tellurite glasses have been calculated and discussed with similar studies. The spectroscopic behavior of the Er³⁺ boro-tellurite glasses have been studied by varying the trivalent erbium ion content and the results were discussed and compared with similar studies.     

Excited states dynamics of Er3+ in Sc2O3 ceramic

The spectral characteristics of Er³⁺ in Sc₂O₃ transparent ceramics are presented. The Er³⁺ visible spectra in the ceramics, prepared by solid-state synthesis, show only lines that could be assigned to C₂ sites. The Stark energy levels, cross-sections and emission kinetics of levels involved in the green upconversion emission under infrared excitation in the 800 nm range were determined. The green upconversion emission (²H_11/2, ⁴S_3/2)→⁴I_15/2 characteristics under excitation with a pulsed Ti:sapphire laser in (⁴I_15/2→⁴I_9/2) absorption were analyzed. The emission kinetics reveal a competition of two-step (⁴I_15/2→⁴I_9/2)+(⁴I_9/2→²H_9/2) excited state absorption (ESA) and (⁴I_11/2, ⁴I_15/2)→(⁴I_11/2, ⁴F_7/2) energy transfer upconversion (ETU) processes function on the excitation wavelength.     

Comparative study of the spectroscopic properties of Yb3+/Er3+ codoped tellurite glasses modified with R2O (R=Li,Na and K)

Spectroscopic characterization of Yb³⁺/Er³⁺ codoped TeO₂–R₂O–ZnO–Ln₂O₃ glasses as a function of network modifiers (R=Li, Na and K) has been investigated. The Judd–Ofelt parameters (Ω_t), quantum efficiency in near infrared (1.55 μm) and visible up-conversion (546 and 660 nm) and quality factor spectroscopy (χ) were calculated. Three up-conversion emission bands centered at 525, 546 and 660 nm were observed as maxima for glasses containing potassium. The measured lifetime of ⁴I_13/2, ⁴F_9/2 and ⁴S_3/2 from Er³⁺ and ⁴F_5/2 from Yb³⁺ levels increased when potassium (K) replaced lithium (Li) and Na. The maximum emission cross-section (ECS) for ⁴I_13/2→⁴I_15/2 transition of Er³⁺ was calculated to be 1.02×10^?20 cm² for TeO₂–Li₂O–ZnO–Ln₂O₃ glasses. The energy transfer efficiency (ET) from Yb³⁺ to Er³⁺, (⁴F_5/2)+(⁴I_15/2)→(⁴F_7/2)+(⁴I_13/2), was calculated using the measured lifetimes of Yb³⁺ with and without the presence of acceptor (Er³⁺). The maximum calculated ET was 58% for 0.25 mol% of Er³⁺ and 3 mol% of Yb³⁺ for TeO₂–K₂O–ZnO–Ln₂O₃ glass composition.     

Structural and luminescence properties of Nd3+-doped PbO–B2O3–TiO2–AlF3 glass for 1.07 μm laser applications

Trivalent neodymium doped multi-component lead borate titanate aluminumfluoride (LBTAFNd) glasses were prepared and characterized as a function of Nd³⁺ ions concentration through optical absorption, NIR luminescence and decay measurements. The intensity (Ω_2,4,6) and other radiative parameters were determined within the frame work of Judd–Ofelt theory. The intensities of absorption bands were expressed in terms of experimental oscillator strengths. Reasonably small root mean square deviation of ±0.384×10^?6 obtained between the experimental and calculated oscillator strengths indicates the validity of intensity parameters. Upon 805 nm laser excitation, the NIR emissions at 0.92 μm (⁴F_3/2→⁴I_9/2), 1.07 μm (⁴F_3/2→⁴I_11/2) and 1.35 μm (⁴F_3/2→⁴I_13/2) were observed. The spectroscopic quality factor has been determined from the Ω₄ and Ω₆ intensity parameters as well as the intensities of emission bands centered at 1.07 and 1.35 μm. The decay curves of the ⁴F_3/2 excited state were recorded by monitoring the emission and excitation wavelengths at 1.07 μm and 805 nm, respectively. The decay curves exhibit single exponential behavior for all the glasses. The laser characteristic parameters of ⁴F_3/2→⁴I_11/2 (1.07 μm) transition were determined and compared with other reported glasses.     

Photoluminescence of Er-doped Si-SiO2 and Al–Si-SiO2 sputtered thin films

Er-doped Si-SiO₂ and Al–Si-SiO₂ films have been deposited by rf-sputtering being annealed afterwards. Annealing behavior of the Er³⁺: ⁴I_13/2→⁴I_15/2 emission of Er-doped Si-SiO₂ yields a maximum intensity for annealing at 700–800 °C. ⁴I_13/2→⁴I_15/2 peak emission for Er-doped Al–Si-SiO₂ at 1525 nm is shifted from that for Er-doped Si-SiO₂ at 1530 nm and the bandwidth increases from 29 to 42 nm. ⁴I_13/2→⁴I_15/2 emission decays present a fast decaying component related to Er ions coupled to Si nanoparticles, defects, or other ions, and a slow decaying component related to isolated Er ions. Excitation wavelength dependence and excitation power dependence for the ⁴I_13/2→⁴I_15/2 emission correspond with energy transfer from Si nanoparticles. Populating of the ⁴I_11/2 level in Er-doped Si-SiO₂ involves branching and energy transfer upconversion involving two or more Er ions. Addition of Al reduces the populating of this level to an energy transfer upconversion involving two ions.     

Thermal stability and spectroscopic properties of erbium-doped niobic-tungsten–tellurite glasses for laser and amplifier devices

Er³⁺ doped niobic-tungsten–tellurite glasses doped with concentration of Er³⁺ ion up to 3 wt% were fabricated. The effect of Er³⁺ doping concentration on thermal stability and optical properties was investigated in order to obtain the most suitable rare earth content for developing 1.5 μm compact fiber amplifier pumped with a commercial telecom 980 nm laser diode. The maximum doping concentration allowed was found to be around 1.77×10²⁰ ions/cm³, for which a broad 1.5 μm emission spectra of 65 nm FWHM and a lifetime of 3.4 ms for the ⁴I_13/2 level was measured.     

Tailoring red-green-blue emission from Er3+, Eu3+ and Tb3+ doped Y2O3 nanocrystals produced via PVA-assisted sol-gel route

Y₂O₃ luminescent nanoparticles were synthesized via PVA-assisted sol-gel method and their structural and optical properties were investigated. Effects of rare earth (Er³⁺, Eu³⁺ and Tb³⁺) doping on luminescence properties of the produced nanophosphors have been investigated under NIR (800 nm) and UV (240–300 nm) excitation. Intense infrared to red and green emissions were observed and a weak blue upconverted luminescence was also detected. Moreover, it was observed that changing the doping ions, the color emitted by the samples could be modified and different combinations of UV excitation and doping produced effective white light emissions. The obtained results demonstrate that PVA-assisted sol-gel is an effective methodology for the synthesis of rare-earth doped Y₂O₃ nanophosphors.     

Synthesis of TiO2 nanoparticles and spectroscopic upconversion luminescence of Nd3+-doped TiO2–SiO2 composite glass

Nd³⁺-doped TiO₂–SiO₂ composites were prepared by sol–gel method. Optical properties such as radiative life-time (τ), stimulated emission cross-section (σ_p) and branching ratio (β) were calculated using Judd–Ofelt theory. Violet to blue upconversion emissions at 380 nm (⁴D_3/2→⁴I_11/2), 399 nm (²P_3/2→⁴I_11/2), 420 nm (²D_5/2→⁴I_9/2) and 452 nm (²P_3/2→⁴I_13/2) were obtained under 578 nm xenon-lamp excitation. The choice of 578 nm is justified by the absorption spectra of the same samples, which shows a strong absorption peak at 578 nm. This 578 nm excitation pump produces upconversion in Nd³⁺ by a sequential two-photon absorption process.