Eu2+的掺杂浓度对BaAl2Si2O8:Eu2+荧光粉发光特性的影响

采用化学共沉淀法一次煅烧工艺合成了BaAl2Si2O8:Eu2+蓝色荧光粉.用X射线衍射仪和荧光分光光度计等对BaAl2Si2O8:Eu2+蓝色荧光粉的相结构、发光性能进行了测试.结果表明:化学共沉淀法一次煅烧工艺合成的BaAl2Si2O8:Eu2+蓝色荧光粉为单相;其激发光谱分布在240-410 nm的波长范围,峰值位于320 nm处,可以被InGaN管芯产生的350-410 nm辐射有效激发;在365 nm近紫外光的激发下,测得其发射光谱是位于465 nm附近的宽带峰.BaAl2Si2O8:Eu2+蓝色荧光粉的发光强度随Eu2+浓度的增大逐渐加强,当Eu2+掺杂的摩尔分数为3.5%时,发光强度达到最大值,而后随掺杂浓度的增加而减小,发生浓度猝灭;根据Dexter能量共振理论,该浓度猝灭是由于Eu2+的离子间交换相互作用引起的.     

Eu3+激活的La2Mo2O9红色荧光粉的制备与性能

利用高温固相法制备了Eu³⁺掺杂的La₂Mo₂O₉红色荧光粉,并对这种荧光粉的结构及发光性质进行了研究。XRD结果表明,实验合成了单一立方相的La₂Mo₂O₉荧光粉体。该荧光粉的激发光谱由一宽带和一系列的锐峰组成;发射光谱由一系列锐峰组成,这些都与Eu³⁺的特征跃迁⁵D_J(J=0,1)和⁷F_J(J=1~4)相对应。结果表明该荧光粉可被395nm的紫外光和470nm的可见光有效激发,并发出峰值位于620nm左右的红光,亮度可达到传统红色荧光粉Y₂O₂S:Eu³⁺的1.5倍以上,这表明它可以作为蓝+黄模式白光LED的红色补光粉,也可以作为UV-LED激发三基色荧光粉体系中的红色荧光粉。研究了Eu³⁺的掺杂浓度以及不同助熔剂对样品发光性质的影响。Eu³⁺的摩尔分数为0.3时,发光强度达到最强。质量分数为3%的NH₄Cl作为助熔剂时效果最好。     

Effects of charge compensation on red emission in CaYAl3O7:Eu3+ phosphor

Monovalent ions Li+, Na+, and K+, as charge compensators, are introduced into CaYAl3O7: M(M =Eu3+, Ce3+) in this letter. Their crystal phases and photoluminescence properties of different alkali metal ions doped in CaYAl3O7 are investigated. In addition, the influence of charge compensation ion Li+which has a more obvious role in improving luminescence intensity on CaYAl3O7: Eu3+phosphor is intentionally discussed in detail and a possible mechanism of charge compensation is given. The enhancement of red emission centered at 618 nm belonging to Eu3+is achieved by adding alkali metal ion Li+under 393-nm excitation.     

纳米棒状GdPO4:Eu3+荧光粉的合成及其发光性能的研究

采用溶解热法合成出了纳米棒状GdPO4:Eu3+荧光粉,其中不同磷源和pH值对最终产物的形成起着关键的作用.将纳米棒状和块体GdPO4:Eu3+荧光粉的发光性能进行了对比,其中与块体GdPO4:Eu3+荧光粉相比,纳米棒状GdPO4:Eu3+荧光粉的色纯度得到了改善,而在激发光谱中,纳米棒状:GdPO:Eu3+荧光粉的基质吸收和Eu-O电荷转移跃迁吸收都发生了蓝移.     

Mg5SnB2O10:Eu3+,Bi3+—一种用于发光二极管的红色荧光粉的制备及其发光性能的研究

采用高温固相法成功合成了单一相的Eu³⁺,Bi³⁺共掺的Mg₅SnB₂O₁₀红色荧光粉,并通过X射线衍射、漫反射光谱、光致发光光谱等手段对该体系的结构及其发光特性进行了测试和研究.激发光谱表明,该荧光粉在393 nm呈现Eu³⁺的⁷Fo—⁵L₆特征激发,可以与用于发光二极管的近紫外芯片很好地匹配.在393 nm激发下,其发射光谱在591,612,701 nm处呈现Eu³⁺的⁵Do—⁷F₁,⁵Do—⁷F₂,⁵D₀—⁷F₄的特征发射.并且当固定Eu³⁺的浓度时,随着Bi³⁺含量的增加,发现Bi³⁺,Eu³⁺在这一体系中存在能量传递现象,系列样品发光强度大幅度提高.通过研究系列样品在不同Bi³⁺,Eu³⁺掺杂浓度下的发光性能,得出最佳样品为Mg_4.89Eu_0.1Bi_0.01SnB₂O₁₀,其积分强度达到了商用Y₂O₂S:Eu³⁺的1.1倍.     

Effect of Eu3+ concentration on microstructure and photoluminescence of Sr2SiO4:Eu3+ phosphors prepared by microwave assisted sintering

In this paper, effect of Eu³⁺ doping concentrations on microstructure and photoluminescence of Sr₂SiO₄ phosphors was investigated. The Sr_2?xSiO₄:xEu³⁺ phosphors with x=0.05, 0.1, 0.2, 0.3 were synthesized by microwave assisted sintering at 1200 °C for 60 min in air. X-ray powder diffraction analysis confirmed the formation of pure Sr₂SiO₄ phase without second phase or phases of starting materials irrespective of the adding amount of Eu³⁺. From scanning electron microscopy image, it is found that with more Eu³⁺ ions introduced to Sr₂SiO₄, the shape of the particles is not much different from each other, but the particle size decreases significantly from 1 to 2 μm (when x=0.05) to less than 500 nm (when x=0.3). The emission spectrum was located obviously at 617 nm as the excitation spectrum at λ_ex=395 nm, and it had best emission intensity when x=0.1.     

Synthesis and luminescence properties of a broad-band red phosphor Ca3Si2O7:Eu2+ for warm white light-emitting diodes

Single-phase broad-band red-emitting Ca₃Si₂O₇:Eu²⁺ phosphors, with photoluminescence features that qualify them as candidates for white light-emitting diodes applications, were successfully synthesized via a modified solid-state reaction method that employed H₃BO₃ as a flux. The phosphors produced have an intense broad red emission band, with a peak at 603 nm, a full width at half maximum of 110 nm, and color coordinates of (0.550, 0.438). Concentration quenching occurred at 0.01 mol Eu²⁺. The discussion of the results shows that Eu²⁺ ions should be accommodated at the Ca-sites of the lattice, dipole–dipole interactions should predominantly govern the energy transfer mechanism among them, and the critical distance between them is ～31 Å.     

Dy含量对红色长余辉发光材料Sr3Al2O6:Eu2+,Dy3+性能的影响

采用溶胶凝胶法制备了Sr3Al2O6:Eu2+,Dy3+红色长余辉发光材料,利用X射线衍射仪对材料的物相进行了分析,结果表明,1200℃下制备的样品的物相为Sr3Al2O6,少量的Eu和Dy掺杂没有影响样品的相组成.采用荧光分光光度计、照度计测定了样品的发光特性.结果表明Sr3Al2O6:Eu2+和Sr3Al2O6:Eu2+,Dy3+的激发光谱均为激发峰位于473 nm的宽带谱.Sr3Al2O6:Dy3+的发射峰位于530.1 nm,对应于Dy3+代替Sr2+位置后基质中形成的施主-受主对Dy·Sr-V″Sr的重新组合.Sr3-0.02-yAl2O6:0.02Eu2+,yDy3+(0相似文献   

Synthesis,photoluminescence and thermoluminescence properties of LiNa3P2O7:Tb3+ green emitting phosphor

The alkaline phosphate based LiNa₃P₂O₇:Tb³⁺ phosphors are prepared by solid state reaction method. X-ray diffraction (XRD) analysis shows that all the powders possess orthorhombic structure. Fourier transform infrared (FTIR) spectroscopy studies suggest that the phosphor belong to the diphosphate family. The morphology of the phosphors is identified by scanning electron microscopy (SEM). Upon 378 nm excitation, the LiNa₃P₂O₇:Tb³⁺ phosphors shown emission bands at 482, 545, 588 and 620 nm corresponding to the transitions ⁵D₄→⁷F₆, ⁵D₄→⁷F₅, ⁵D₄→⁷F₄ and ⁵D₄→⁷F₃, respectively. The optimized concentration of Tb³⁺ in LiNa₃P₂O₇ phosphor is found to be 9 mol%. The concentration quenching mechanism was proved to be the exchange interaction between two nearest Tb³⁺ ions with the critical distance (R_c) of 1.18 nm. The Commission International de l'Eclairage (CIE) coordinates evidence that the phosphors emit in the green light region. Thermoluminescence properties of the prepared phosphors are studied by pre-irradiating the powders with different doses of UV irradiation. The kinetic parameters of TL glow curves are calculated using Chen's peak shape method.     

溶胶-凝胶法制备Zn2SiO4:Eu3+红色荧光粉

采用溶胶-凝胶法在Zn2SiO4基质中掺杂Eu3+,合成了红色荧光粉Zn2SiO4:Eu3+.通过样品的X射线衍射光谱、红外光谱、扫描电镜以及光致发光光谱的测试和表征,研究了Zn2SiO4:Eu3+的内部结构和发光特性.扣描电镜结果显示样品为球状荧光粉,颗粒直径为1～3μm.在395 nm激发下,样品在613 nm处发射出很强的红光.结合荧光光谱,分析了样品的退火温度,Eu3+的浓度,电荷补偿剂Li+的浓度对样品发光强度的影响.研究发现,红色荧光粉Zn2SiO4:Eu3+的发光强度随退火温度的升高而增加,发光强度随Eu3+和Li+浓度的增加先增大后减小.     

Combustion synthesis and luminescent properties of a blue-green emitting phosphor: (Ba1.95, Eu0.05)ZnSi2O7:B3+

A blue-green emitting phosphor (Ba_1.95, Eu_0.05)ZnSi₂O₇: B _x ³⁺ was prepared by combustion synthesis and an efficient blue-green emission under near-ultraviolet was observed. The luminescence, crystallinity and particle sizes were investigated by using luminescence spectrometry, X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The emission spectrum shows a single band centered at 503 nm, which corresponds to the 4f ⁶5d ¹ →4f ⁷ transition of Eu²⁺. The excitation spectrum is a broad band extending from 260 to 465 nm, which matches the emission of ultraviolet light-emitting diodes. The optical absorption spectra of the (Ba_1.95, Eu_0.05)ZnSi₂O₇: B _0.06 ³⁺ exhibited band-gap energies of 3.9 eV. The results showed that boric acid was effective in improving the luminescence intensity of (Ba_1.95, Eu_0.05)ZnSi₂O₇, and the optimum molar ratio of boric acid to zinc nitrate was about 0.06. The phosphor (Ba_1.95, Eu_0.05)ZnSi₂O₇: B_0.06³⁺ synthesized by combustion method showed 1.5 times improved emission intensity compared with that of the Ba_1.95ZnSi₂O₇: Eu_0.05²⁺ phosphor under λ _ex = 353 nm.      

Synthesis and luminescence properties of Na2Ba2Si2O7:Eu2+ phosphor

Green-emitting phosphor Na₂Ba₂Si₂O₇:Eu²⁺ has been synthesized by a conventional high-temperature solid-state reaction. The phase structure and luminescence properties are characterized by the X-ray powder diffraction, diffuse reflectance spectra, photoluminescence excitation and emission spectra, temperature-dependent emission spectra, respectively. It can be efficiently excited in the wavelength range of 325–400 nm and consists of a strong broad green band centered at about 501 nm, which is ascribed to 4f⁶6s⁰5d¹ → 4f⁷6s²5d⁰ transition of Eu²⁺. The critical quenching concentration of Eu²⁺ in the Na₂Ba₂Si₂O₇ host is about 0.8 mol % and corresponding quenching behavior is ascribed to be electric dipole–dipole interaction. Furthermore, the phosphor has good thermal stability property, and the activation energy for thermal quenching is calculated as 0.34 eV.     

Crystal structure and photoluminescence correlations in white emitting nanocrystalline ZrO2:Eu3+ phosphor: Effect of doping and annealing

White emitting nanocrystalline ZrO₂:Eu³⁺ phosphors were synthesized by a simple precipitation route without using a capping agent. X-ray diffraction (XRD) study of ZrO₂ and ZrO₂:Eu³⁺samples revealed the presence of monoclinic and tetragonal phases. The monoclinic phase increases with increase in the annealing temperature while the tetragonal phase increases with increase in the concentration of Eu³⁺. This can be attributed to the presence of oxygen vacancy evolved when Zr⁴⁺ is replaced by Eu³⁺. Photoluminescence (PL) emission peaks of Eu³⁺ are observed at 591, 596, 606 and 613 nm on monitoring excitation wavelengths at 250, 286, 394 and 470 nm. The peaks at 591 and 606 nm were found to correlate with the tetragonal phase and those at 596 and 613 nm with the monoclinic phase. Intensities of these peaks are found to change as the crystal structure changes. The lifetime value corresponding to 591 nm peak increases with Eu³⁺ concentration at a particular heating temperature indicating increase of tetragonal phase with respect to monoclinic phase. The CIE co-ordinates of the doped samples were found to be close to that of white color (0.33, 0.33). The changes in the crystal structure of the doped samples due to doping and annealing did not affect the white color emission.     

Synthesis and optical properties of red emitting Eu doped CaZrO3 phosphor

Eu³⁺ activated Ca_1−xEu_xZrO₃ (x = 0.01–0.05) phosphor with perovskite structure has been synthesized by sol–gel combustion method. The structure, morphology and optical properties of materials were characterized by X-ray diffraction, scanning electron microscopy and fluorescence spectrometry. The XRD results indicate that crystals of CaZrO₃:Eu³⁺ belongs to orthorhombic perovskite structure. The phosphors can be effectively excited by UV light and the emission spectra results indicate that red luminescence of CaZrO₃:Eu³⁺ due to electric dipole transition ⁵D₀ → ⁷F₂ at 616 nm is dominant. Thus, these prepared phosphors show remarkable luminescent properties which find applications in display devices.     

A potential red emitting K4Ca(PO4)2: Eu3+ phosphor for white light emitting diodes

Europium (III) ions doped red phosphors K₄Ca(PO₄)₂ were prepared first time by high temperature solid state reaction method. The prepared phosphors structure was examined by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS) analyses. The thermal properties of the synthesized phosphor were investigated by differential scanning calorimetry (DSC) analysis. Photoluminescence (PL) spectra of K₄Ca(PO₄)₂:Eu³⁺ phosphors have shown strong red emission at 618 nm (⁵D₀→⁷F₂) with near UV an excitation wavelength of λ_exc=394 nm (⁷F₀→⁵L₆). In addition, the decay curves and CIE color coordinate measurements are also carried out. Hence, emission and excitation characterization of synthesized phosphors shows that the phosphors may be a promising red component for the application in the white light emitting diodes (WLEDs).     

Nonradiative energy transfer from Mn2+ to Eu3+ in K2CaP2O7:Mn2+,Eu3+ phosphor

A series of color tunable phosphors K₂Ca_1?x?yP₂O₇:xMn²⁺, yEu³⁺ are synthesized by solid state reaction method. The energy transfer phenomenon from Mn²⁺ to Eu³⁺ has been observed in the Mn²⁺/Eu³⁺ codoped non-magnetic K₂CaP₂O₇ host, which was confirmed by PL spectra and decay curves. The Mn²⁺→Eu³⁺ energy transfer is controlled by quadrupole–quadrupole interaction between sensitizer and activator. The maximum efficiency of energy transfer is estimated to be 33% with x=0.125 and y=0.03 in K₂Ca_1?x?yP₂O₇:xMn²⁺, yEu³⁺ phosphor. The phosphors can emit light from green to yellow and eventually to orange under 400 nm excitation by changing the Mn²⁺/Eu³⁺ content ratio, indicating that K₂CaP₂O₇: Mn²⁺, Eu³⁺ would be potential candidates for use in lighting and displays applications.     

发光二极管用红色荧光粉SrMoO4:Eu3+的制备和发射性质

采用化学共沉淀法制备了适合于紫外、近紫外、蓝光发光二极管(LED)激发的红色荧光粉SrMoO4:Eu3+.研究了样品的晶体结构和发光性质.结果表明:化学共沉淀法合成的SrMoO4:Eu3+荧光粉为四方纯相,其激发光谱包括一个宽带峰和一系列尖峰,峰值位于280nm(宽带峰中心),395nm,465nm,可以被紫外LED和蓝光LED有效激发.在395nm的激发下,测得发射光谱的强发射峰位于613nm,对应Eu3+离子的5D0→7F2跃迁.Eu3+离子掺杂浓度的改变对基质的晶格常数、Eu3+离子在晶体中对称性及发光性能有较大影响.通过对比不同掺杂浓度Eu3+离子的发射谱,发现在SrMoO4基质中Eu3+离子掺杂存在浓度猝灭现象,其最佳掺杂浓度为15%.     

Synthesis and luminescence properties of red long-lasting phosphor Y2O2S:Eu3+, Zn2+, Ti4+ nanotubes via hydrothermal method

Red long-lasting phosphor Y₂O₂S:Eu³⁺, Zn²⁺, Ti⁴⁺ nanotubes were prepared by hydrothermal method. Powder X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence and thermoluminescence spectra (TL) were used to characterize the long-lasting phosphor. XRD investigation revealed that the product synthesised under 750 °C for 6 h was a pure phase of Y₂O₂S. SEM observation showed that the sulfuretted phosphor inherited the tube-like shape from the precursor. Under 325 nm UV excitation, the result indicated the strongest red-emission lines at 627 nm, corresponded to the transition from ⁵D₀ to ⁷F₂ level of Eu³⁺ ion. Both the afterglow decay curves and TL curves revealed that the phosphor had efficient luminescent and excellent long-lasting properties.     

Luminescence properties of a new green emitting Eu2+-doped barium chlorosilicate phosphor

A new intense green light-emitting phosphor, the Eu²⁺-doped (BaO–BaCl₂–SiO₂) phosphor system, was synthesized at 800°C by the conventional high-temperature solid-state reaction. Its structure and luminescence properties were investigated by using thermogravimetry-differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), diffuse reflection spectra, photoluminescence (PL) and photoluminescence excitation (PLE) spectra. The photoluminescence spectrum reveals that this phosphor can be efficiently excited by near-ultraviolet (UV) light and blue light in the wavelength region covering 280 and 480 nm, which perfectly matches the emission wavelength of near-UV light-emitting diodes (LEDs). It emits an intense green light peaking at 502 nm, which is promising to develop possible applications for white LEDs.