共查询到20条相似文献,搜索用时 125 毫秒
1.
采用脉冲激光沉积(PLD)工艺,制备了以Bi4Ti3O12(BIT)为过渡阻挡层的Au/PZT/BIT/p-Si异质结.研究了BIT铁电层对Pb(Zr0.52Ti0.48)O3(PZT)薄膜晶相结构、铁电及介电性能的影响,对Au/PZT/BIT/p-Si异质结的导电机制进行了讨论.氧气氛530℃淀积的PZT为多晶铁电薄膜,与直接淀积在Si基片上相比,加入BIT铁电层后PZT铁
关键词:
铁电薄膜
异质结构
脉冲激光沉积(PLD) 相似文献
2.
3.
采用热力学非线性理论,研究了外加电场对立方基底Pb(Zr0.3Ti0.7)O3(PZT)铁电薄膜相变的影响.通过数值计算,得到了"失配应变-外加电场"相图,及外加电场与极化强度的关系.当外加电场达到186 kV/cm时,能使生长在SrTiO3 基底上PZT铁电薄膜从单斜r相转变为c相.在实验上,采用扫描探针显微镜通过对PZT薄膜施加不同的极化电场来研究了它的电畴翻转.从得到的压电响应相图可以看出,绝大多数的电畴是清晰可
关键词:
铁电薄膜
相变
扫描探针显微镜
失配应变 相似文献
4.
" 在Pt/Ti/SiO2/Si基片上用溶胶-凝胶法与快速退火工艺制备了300 nm厚的锆钛酸铅Pb(Zr0:95Ti0:05)O3 (PZT95/5)反铁电薄膜.结果显示600~700 ℃晶化处理的钙钛矿PZT95/5薄膜具有高度(111)取向生长特性.薄膜的电性能测量采用金属-铁电-金属电容器结构.在20 V电压作用下,600~700 ℃晶化处理的PZT95/5薄膜显示出饱和电滞回线.在1 kHz下,600、650和700 ℃晶化的薄膜介电常数与损耗分别为519与0.028、677与0.029、987 相似文献
5.
用Sol-Gel法制备了Pb(1 x)TiO3/PbZr0.3Ti0.7O3/Pb(1 x)TiO3(PT/PZT/PT)夹心结构及PZT铁电薄膜,为了获得高质量的PT/PZT/PT夹心结构铁电薄膜,使用不同过量Pb配比(x)的PbTiO3 (PT)层进行制备,以获得优化的PT子晶层.X射线衍射和原子力显微镜分析结果表明PT层中过量Pb配比(x)对薄膜的微结构影响很大,只有PT层中Pb过量配比x=0.10-0.15的薄膜为表面晶粒大小均匀致密的纯钙钛矿结构.X射线电子能谱对薄膜微区进行元素成分分析表明,对x=0.00的薄膜,在表面和界面处Pb明显的缺乏;而x=0.20时的薄膜,Pb则明显的过量.薄膜的铁电性能、疲劳特性和漏电流特性等电学性能与PT层中过量Pb配比(x)没有明显的变化趋势,但与薄膜的结晶性能密切相关.结晶性能较好的薄膜,其电学性能也较好.说明PT层中过量Pb配比(x)是通过影响PT子晶层自身的结晶,而影响整个薄膜的结晶行为,并进一步影响到整个薄膜的电学性能.因此,在其他工艺参数都相同时,PT层中合适的过量Pb配比应为x=0.10-0.15.优化的子晶层不仅能获得结晶性能较好的薄膜,而且薄膜的电学性能也好. 相似文献
6.
采用Sol-Gel工艺低温制备了Si基Bi3.25La0.75Ti3O12铁电薄膜.研究了退火温度对薄膜微观结构、介电特性与铁电性能的影响.500℃退火处理的Bi3.25La0.75Ti3O12薄膜未能充分晶化,晶粒细小且有非晶团聚,介电与铁电性能均较差.高于550℃退火处理的Bi3.25La0.75Ti3O12薄膜表面平整无裂纹,晶粒均匀,无焦碌石相或其他杂相,薄膜为多晶生长,具有较好的介电与铁电性能,4V电压下的漏电流密度低于2×10-8A/cm2.随退火温度升高,晶化程度的提升和晶粒尺寸的增大使薄膜的剩余极化增大而矫顽电场降低.600℃退火处理的Bi3.25La0.75Ti3O12薄膜显示了优于Bi4Ti3O12薄膜的铁电性能,其剩余极化Pr和矫顽电场Ec分别达到17.5μC/cm2和102kV/cm. 相似文献
7.
通过MOD法在Si(100)和Pt(111)/Ti/SiO2/Si基片上制备出LaNiO3 ( LNO)薄膜.再通过修 正的Sol-gel法,在Pt(111)/Ti/SiO2/Si,LNO/Si(100)和LNO/Pt/Ti/SiO2< /sub>/Si三种衬底上 制备出具有择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜. 经XRD分析表明,L NO薄膜具有(100)择优取向的类钙钛矿结构;PZT薄膜均具有钙钛矿结构,且在Pt(111)/Ti/S iO2/Si衬底上的薄膜以(110)择优取向,在LNO/Pt/Ti/SiO2/Si和LN O/Si(100)衬底上的 薄膜以(100)择优取向.经场发射SEM分析和介电、铁电性能测试表明,在LNO/Si和LNO/Pt/Ti /SiO2/Si衬底上的PZT薄膜的平均粒径、介电常数以及剩余极化强度均比以Pt/T i/SiO2/Si为衬底的薄膜大.
关键词:
3薄膜')" href="#">LaNiO3薄膜
PZT铁电薄膜
择优取向
剩余极化强度 相似文献
8.
利用扫描力显微术中压电响应模式原位研究了(111)择优取向的PZT60/40铁电薄膜的纳米尺度畴结构及其极化反转行为.铁电畴图像复杂的畴衬度与晶粒中的畴排列和晶粒的取向密切相关.直接观察到极化反转期间所形成的小至30nm宽的台阶结构,该台阶结构揭示了(111)取向的PZT60/40铁电薄膜在极化反转期间其畴成核与生长机理主要表现为铁电畴的纵向生长机理.
关键词:
畴结构
反转机理
PZT薄膜
扫描力显微术 相似文献
9.
10.
通过MOD法在Si(100)和Pt(111)/Ti/SiO2/Si基片上制备出LaNiO3 (LNO)薄膜.再通过修正的Sol-gel法,在Pt(111)/Ti/SiO2/Si,LNO/Si(100)和LNO/Pt/Ti/SiO2/Si三种衬底上制备出具有择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜.经XRD分析表明,LNO薄膜具有(100)择优取向的类钙钛矿结构;PZT薄膜均具有钙钛矿结构,且在Pt(111)/Ti/SiO2/Si衬底上的薄膜以(110)择优取向,在LNO/Pt/Ti/SiO2/Si和LNO/Si(100)衬底上的薄膜以(100)择优取向.经场发射SEM分析和介电、铁电性能测试表明,在LNO/Si和LNO/Pt/Ti/SiO2/Si衬底上的PZT薄膜的平均粒径、介电常数以及剩余极化强度均比以Pt/Ti/SiO2/Si为衬底的薄膜大. 相似文献
11.
根据薄膜沉积过程等离子体对光学薄膜膜蒸气分子或原子的作用,建立低压等离子体离子镀设备,并对常规光学薄膜、如硫化物、氧化物薄膜以及多层膜器件进行了系统的研究,对所制备薄膜样品的透射光谱、吸收、散射以及膜层的聚集密度等进行了全面的测试分析。实验研究表明,低压等离子体离子镀可大大提高常规光学薄膜的光机性能。 相似文献
12.
Positron annihilation lifetime and Doppler broadening of annihilation line techniques have been used to obtain information about the small pore structure and size of porous SiO2 thin film produced by sputtered Al-Si thin film and etched Al-Si thin film. The film is prepared by an Al/Si 75:25 at.-% (A175Si25) target with the radiofrequency (RF) power of 66 W at room temperature. A 5 wt.-% phosphoric acid solution is used to etch the Al cylinders. All the A1 cylinders dissolved in the solution after 15 h at room temperature, and the sample is subsequently rinsed in pure water. In this way, the porous SiO2 on the Si substrate is produced. From our results, the values of all lifetime components in the spectra of Al-Si thin film are less than 1 ns, but the value of one of the lifetime components in the spectra of porous SiO2 thin film is τ = 7.80 ns. With these values of lifetime, RTE (Rectangular Pore Extension) model has been used to analyze the pore size. 相似文献
13.
14.
X.T Zhang Y.C LiuZ.Z Zhi J.Y ZhangY.M Lu D.Z ShenW Xu X.W FanX.G Kong 《Journal of luminescence》2002,99(2):149-154
The properties of the excitonic luminescence for nanocrystalline ZnO thin films are investigated by using the dependence of excitonic photoluminescence (PL) spectra on temperature. The ZnO thin films are prepared by thermal oxidation of ZnS films prepared by low-pressure metalorganic chemical vapor deposition (LP-MOCVD) technique. The X-ray diffraction (XRD) indicates that ZnO thin films have a polycrystalline hexagonal wurtzite structure with a preferred (0 0 2) orientation. A strong ultraviolet (UV) emission peak at 3.26 eV is observed, while the deep-level emission band is barely observable at room temperature. The strength of the exciton-longitudinal-optical (LO) phonon coupling is deduced from the temperature dependence of the full-width at half-maximum (FWHM) of the fundamental excitonic peak, decrease in exciton-longitudinal-optical (LO) phonon coupling strength is due to the quantum confinement effect. 相似文献
15.
16.
17.
18.
19.
ZHANG Zhe QIN Xiu-Bo WANG Dan-Ni YU Run-Sheng WANG Qiao-Zhan MA Yan-Yun WANG Bao-Yi 《中国物理C(英文版)》2009,33(2)
Positron annihilation lifetime and Doppler broadening of annihilation line techniques have been used to obtain information about the small pore structure and size of porous SiO2 thin film produced by sputtered A1-Si thin film and etched Al-Si thin film. The film is prepared by an Al/Si 75:25 at.-% (A175Si25) target with the radiofrequency (RF) power of 66 W at room temperature. A 5 wt.-% phosphoric acid solution is used to etch the A1 cylinders. All the Al cylinders dissolved in the solution after 15 h at room temperature, and the sample is subsequently rinsed in pure water. In this way, the porous SiO2 on the Si substrate is produced. From our results, the values of all lifetime components in the spectra of Al-Si thin film are less than 1 ns, but the value of one of the lifetime components in the spectra of porous SiO2 thin film is T = 7.80 ns. With these values of lifetime, RTE (Rectangular Pore Extension) model has been used to analyze the pore size. 相似文献
20.
借助于原子力显微镜研究了离子束溅射沉积工艺中入射离子能量对制备的Ti薄膜表面形貌的影响。对薄膜表面高度数据进行相关运算,发现在此工艺条件下制备的薄膜具有典型的分形特征,利用分形表面高度—高度相关函数的唯象表达形式对不同能量下制备Ti薄膜表面的高度相关函数进行拟合。得到了薄膜表面的分形维数、水平相关长度、标准偏差粗糙度等参量。研究发现,入射Ar离子能量在300—700eV之间薄膜表面的粗糙度随着沉积粒子的能量增加而增大,分形维数随着入射离子能量的增加而减少。另外,在得到的分形维数基础上对不同溅射电压下Ti薄膜的生长机制进行了初步研究。 相似文献