Phase diagrams of the KF-K<Subscript>2</Subscript>TaF<Subscript>7</Subscript> and KF-Ta<Subscript>2</Subscript>O<Subscript>5</Subscript> systems

The phase diagrams of the systems KF-K₂TaF₇ and KF-Ta₂O₅ were determined using the thermal analysis method. The phase diagrams were described by suitable thermodynamic model. In the system KF-K₂TaF₇ eutectic points at x _KF=0.716 and t=725.4°C and at x _KF=0.214 and t=712.2°C has been calculated. It was suggested that K₂TaF₇ melts incongruently at around 743°C forming two immiscible liquids. The system KF-Ta₂O₅ have been measured up to 8 mol% of Ta₂O₅. The eutectic point was estimated to be at x _KF∼0.9 and t∼816°C. The formation of KTaO₃ and K₃TaO₂F₄ compounds has been observed in the solidified samples.     

Low temperature thermodynamic properties of Gd<Subscript>2</Subscript>SrCo<Subscript>2</Subscript>O<Subscript>7</Subscript>

Summary Thermodynamic properties of a layered perovskite oxide Gd₂SrCo₂O₇ have been studied. Powder X-ray diffraction, electric resistivity, magnetic susceptibility and heat capacity measurements were carried out. The crystal structure was determined as I4/mmm. The temperature dependence of the magnetic susceptibility was fitted to the Curie-Weiss behavior with antiferromagnetic interaction. Spin state of Co³⁺ ion was derived to be intermediate spin state configuration (t_2g⁵e_g¹). The spin ordering was observed as a broad anomaly in the heat capacity curve with a peak at 2 K. The measured entropy was 35.47 J K^-1mol^-1, which was 65% of expected value. Thus the spin ordering should not be completed at the lowest temperature 0.2 K covered in the present experiments and/or some short range ordering remains at higher temperatures.     

Phase formation in the V<Subscript>2</Subscript>O<Subscript>5</Subscript>-Ta<Subscript>2</Subscript>O<Subscript>5</Subscript>-MoO<Subscript>3</Subscript> system

Solid-phase interactions in the V₂O₅-Ta₂O₅-MoO₃ system were studied. The formation of com- pounds TaVO₅ and VTa₉O₂₅ in the V₂O₅-Ta₂O₅ binary system was verified. Tetragonal VTa₉O₂₅-base solid solutions of the general formula Ta_{5 + 4x} V_{5 − 4x} O₂₅ (x = 0.25–1) and TaVO₅-base solid solutions of the general formula Ta _x Mo_{1 − x} V_{2 − x} O_{8 − 3x} (x = 0.625–1) were found to form. Subsolidus phase equilibria in the V₂O₅-Ta₂O₅-MoO₃ were determined.     

Phase relations in the Zn<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript>-Cu<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript> system from room temperature to melting

Phase relations in the Zn₂V₂O₇-Cu₂V₂O₇ system were studied by high-temperature X-ray diffraction and differential thermal analysis. The major phase constituents of the system are solid solutions based on Zn₂V₂O₇ and Cu₂V₂O₇ polymorphs and their coexistence regions. The generation of α-Zn_{2 − 2x} Cu_2x V₂O₇ solid solution, where 0 ≤ x ≤ 0.30, leaves almost unchanged the stabilization temperature of the high-temperature zinc pyrovanadate phase. The α-Cu_{2 − 2x} Zn_2x V₂O₇ homogeneity range is 5 mol % Zn₂V₂O₇. In the range 0.050 ≤ x ≤ 0.09 from 20 to ∼ 620°C, there is the two-phase field of α-Cu₂V₂O₇ and β-Cu₂V₂O₇ base solid solutions. At still higher temperatures, β-Zn_{2 − 2x} Cu_2x V₂O₇ and α-Cu_{2 − 2x} Zn_2x V₂O₇ coexist in the mixed-phase region. β-Zn_{2 − 2x} Cu_2x V₂O₇ solid solution, where 0 ≤ x ≤ 0.30, exists above 610 ± 5°C. The extent of the β′-Cu₂V₂O₇-base solid solution is 9 to 65 mol % Zn₂V₂O₇ at 615 ± 5°C, expanding to 0 mol % Zn₂V₂O₇ with rising temperature. Original Russian Text ￠ T.I. Krasnenko, M.V. Rotermel’, S.A. Petrova, R.G. Zakharov, O.V. Sivtsova, A.N. Chvanova, 2008, published in Zhurnal Neorganicheskoi Khimii, 2008, Vol. 53, No. 10, pp. 1755–1762.     

Thermal analysis study of Bi<Subscript>2</Subscript>Sr<Subscript>2</Subscript>Ca<Subscript>2</Subscript>Cu<Subscript>3-x</Subscript>Er<Subscript>x</Subscript>O<Subscript>10+δ</Subscript> glass-ceramic system

Summary We have fabricated glasses in the Bi-2223 HT_c superconductor system with Bi₂Sr₂Ca₂Cu_3-xEr_xO_{10+ δ} nominal composition, where x=0.5 and 1.0, by the glass-ceramic technique. Using an analysis developed for non-isothermal crystallization studies, information on some aspects of crystallization temperature and thermal properties has been obtained. The crystallization studies were made using DTA with several uniform rates. The calculations of crystallization activation energies, E_a, and the Avrami parameters, n, were made based on the non-isothermal kinetic theory of Kissinger and the Ozawa’s equations. The DTA data of the samples showed that the first crystallization temperature, T_x1, increases and the second crystallization temperature, T_x2, decreases by increasing the Er concentration. This suggests that the Er substitution had significant effect on the glassification of the BSCCO material due to change on the surface nucleation and increased ionic activities at high temperature region. The activation energy for crystallization, E_a, of the samples was also showed an increase at high Er concentration case. However, the Avrami parameter, n, decreased from 2.5 to 1.7 for x=0.5 and 1.0 samples, respectively. This suggests that the growth mechanism is diffusion-controlled and three-dimensional parabolic growth takes place near the first crystallization temperature. The oxidization rates and the activation barrier for oxygen out-diffusion process, E, was calculated using the TG data. It was found that the total mass gain in the x=0.5 sample is comparably smaller than that of the x=1.0 sample. This shows that the oxygen absorption of the x=1.0 sample is faster than the x=0.5 sample, leading to increase in the oxidization rate in the x=1.0 material.     

Production of bscco bulk high <Emphasis Type="Italic">T</Emphasis><Subscript>c</Subscript> superconductors by sol-gel method and their characterization by ftir and XRD techniques

The production of bulk high T _c superconducting phase (2223) by EDTA-gel (ethylenediaminetetraacetic acid) techniques has been investigated. It is shown that close control of pH is necessary for the production of a well-complexed precursor which allows subsequent decomposition in two stages at 300 and 800°C. The problem of carbonate formation was investigated experimentally and solved. Precursors are characterised by Fourier transform infrared (FTIR) spectroscopy and X-ray diffraction (XRD) and the sintering behaviour was monitored by dilatometry. At least three different phases Bi₂Sr₂Ca_x−1Cu_xO_8+y (BSCCO); where x=1, 2, 3 were identified within superconducting pellets using XRD, named as Bi₂Sr₂CuO₇ (2201), Bi₂Sr₂CaCu₂O₉ (2212) and Bi₂Sr₂Ca₃O₁₀ (2223). The superconducting properties of the sintered samples were studied by vibrating sample magnetometer (VSM). Transition to a superconducting state around 80 K appeared in samples (sintered at 845°C) containing the Bi₂Sr₂Ca₁Cu₂O_y (2212) phase. Liquid phase sintering of the samples aided the formation of Bi₂Sr₂Ca₂Cu₃O_x (2223) phase at high temperature (860°C), which showed a superconducting transition temperature of 108 K.     

A new phosphor with flower-like structure and luminescent properties of Sr<Subscript>2</Subscript>MgSi<Subscript>2</Subscript>O<Subscript>7</Subscript>: Eu<Superscript>2+</Superscript>, Dy<Superscript>3+</Superscript> long afterglow materials by sol–gel method

The flower-like phosphors of Sr₂MgSi₂O₇: Eu²⁺, Dy³⁺ with high brightness and long afterglow were obtained by sol–gel method. X-ray diffraction pattern (XRD) shows that single-phased Sr₂MgSi₂O₇ phosphor is prepared by sol–gel method under 1250 °C. Scanning electron microscope (SEM) indicates that the phosphor consists of nano-sized whiskers which are detected for the first time in Eu²⁺ and Dy³⁺ co-doped long-lasting phosphorescence silicates. Furthermore, the investigation on the mechanism indicates that the internal structure and gas, liquid and solid phase effect play important roles in the formation of flower-like Sr₂MgSi₂O₇: Eu²⁺, Dy³⁺ nanostructure. Finally, the optical properties of flower-like Sr₂MgSi₂O₇ nanostructure have been characterized by photoluminescence (PL) spectra.     

Structures and phase transitions in (K<Subscript>1-x</Subscript>Rb<Subscript>x</Subscript>)<Subscript>2</Subscript>SeO<Subscript>4</Subscript>

Summary The phase diagram of the mixed crystal (K_1-xRb_x)₂SeO₄ was determined by means of thermal analysis and neutron scattering experiments. The hexagonal to orthorhombic phase transition line exists for any x. The normal-incommensurate phase transition temperature decreases continuously with increasing Rb content. However, the incommensurate-commensurate phase transition was not observed except for K₂SeO₄. According to the clear softening of the Σ₂- Σ ₃ phonon branches and the finite frequency at 0 K for x>0.34, an existence of the hypothetical phase transition was confirmed.     

Heat capacities and absolute entropies of UTi<Subscript>2</Subscript>O<Subscript>6</Subscript> and CeTi<Subscript>2</Subscript>O<Subscript>6</Subscript>

Summary As part of a larger study of the physical properties of potential ceramic hosts for nuclear wastes, we report the molar heat capacity of brannerite (UTi₂O₆) and its cerium analog (CeTi₂O₆) from 10 to 400 K using an adiabatic calorimeter. At 298.15 K the standard molar heat capacities are (179.46±0.18) J K^-1 mol^-1 for UTi₂O₆ and (172.78±0.17) J K^-1 mol^-1 for CeTi₂O₆. Entropies were calculated from smooth fits of the experimental data and were found to be (175.56±0.35) J K^-1 mol^-1 and (171.63±0.34) J K^-1 mol^-1 for UTi₂O₆ and CeTi₂O₆, respectively. Using these entropies and enthalpy of formation data reported in the literature, Gibb’s free energies of formation from the elements and constituent oxides were calculated. Standard free energies of formation from the elements are (-2814.7±5.6) kJ mol^-1 for UTi₂O₆ and (-2786.3±5.6) kJ mol^-1 for CeTi₂O₆. The free energy of formation from the oxides at T=298.15 K are (-5.31±0.01) kJ mol^-1 and (15.88±0.03) kJ mol^-1 for UTi₂O₆ and CeTi₂O₆, respectively.     

Electrical conductivity studies in the system Li<Subscript>2</Subscript>TiO<Subscript>3</Subscript>-Li<Subscript>1.33</Subscript>Ti<Subscript>1.67</Subscript>O<Subscript>4</Subscript>

Electrical conductivity in the monoclinic Li₂TiO₃, cubic Li_1.33Ti_1.67O₄, and in their mixture has been studied by impedance spectroscopy in the temperature range 20–730 °C. Li₂TiO₃ shows low lithium ion conductivity, σ₃₀₀≈10^–6 S/cm at 300 °C, whereas Li_1.33Ti_1.67O₄ has 3×10^–8 at 20 °C and 3×10^–4 S/cm at 300 °C. Structural properties are used to discuss the observed conductivity features. The conductivity dependences on temperature in the coordinates of 1000/T versus log_e(σT) are not linear, as the conductivity mechanism changes. Extrinsic and intrinsic conductivity regions are observed. The change in the conductivity mechanism in Li₂TiO₃ at around 500–600 °C is observed and considered as an effect of the first-order phase transition, not reported before. Formation of solid solutions of Li_{2– x} Ti_{1+ x} O₃ above 900 °C significantly increases the conductivity. Irradiation by high-energy (5 MeV) electrons causes defects and the conductivity in Li₂TiO₃ increases exponentially. A dose of 144 MGy yields an increase in conductivity of about 100 times at room temperature. Electronic Publication     

Thermal behaviour and properties of Na<Subscript>2</Subscript>O-TiO<Subscript>2</Subscript>-P<Subscript>2</Subscript>O<Subscript>5</Subscript> glasses

Differential scanning calorimetry (DSC) and thermomechanical analysis (TMA) were used to study the thermal behaviour of (50-x)Na₂O-xTiO₂-50P₂O₅ and 45Na₂O-yTiO₂-(55-y)P₂O₅ glasses. The addition of TiO₂ to the starting glasses (x=0 and y=5 mol% TiO₂) resulted in a nonlinear increase of glass transition temperature and dilatation softening temperature, whereas the thermal expansion coefficient decreased. All prepared glasses crystallize under heating within the temperature range of 300–610°C. The contribution of the surface crystallization mechanism over the internal one increases with increasing TiO₂ content. With increasing TiO₂ content the temperature of maximum nucleation rate is also gradually shifted from a value close to the glass transition temperature towards the crystallization temperature. X-ray diffraction measurements showed that the major compounds formed by glass crystallization were NaPO₃, TiP₂O₇ and NaTi₂(PO₄)₃. The chemical durability of the glasses without titanium oxide is very poor, but with the replacement of Na₂O or P₂O₅ by TiO₂, it increases sharply.     

High-temperature heat capacity of stannates Er<Subscript>2</Subscript>Sn<Subscript>2</Subscript>O<Subscript>7</Subscript> and Tm<Subscript>2</Subscript>Sn<Subscript>2</Subscript>O<Subscript>7</Subscript>

Erbium stannate Er₂Sn₂O₇ and thulium stannate Tm₂Sn₂O₇ with a pyrochlore-type structure were produced by solid-phase synthesis by calcining stoichiometric mixtures of the respective oxides in air at 1473 K for 240 and 200 h. The high-temperature heat capacity of Er2Sn2O7 and Tm₂Sn₂O₇ was studied by differential thermal calorimetry at 353–1000 K. From the experimental dependences C _P = f(T), the thermodynamic functions (enthalpy change, entropy change, and reduced Gibbs free energy) of oxide compounds were calculated.     

Mechanism and kinetics of formation of La<Subscript>2</Subscript>SrFe<Subscript>2</Subscript>O<Subscript>7</Subscript> and Nb<Subscript>2</Subscript>SrFe<Subscript>2</Subscript>O<Subscript>7</Subscript>

Phase formation processes in the systems Ln₂O₃-SrO-Fe₂O₃ (Ln = La, Nd) in air in the temperature range 1200–1500°C were studied. The synthesis of the complex ferrites La₂SrFe₂O₇ and Nb₂SrFe₂O₇ involves the formation of the intermediate compounds LnFeO₃ and LnSrFeO₄ and occurs by the same mechanism as the synthesis of the corresponding aluminates, but much faster.     

Changes in the heat capacity of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-Cr<Subscript>2</Subscript>O<Subscript>3</Subscript> solid solutions near the point of antiferromagnetic phase transition in Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>

Al₂O₃-Cr₂O₃ solid solutions with 0, 4, 7, 10 and 20 mol% of corundum were synthesized using a high-pressure/high-temperature apparatus and characterized by X-ray powder diffraction. Calorimetric measurements were carried out using DSC-111 (Setaram). Heat capacity was measured by the enthalpy method in a temperature range of 260–340 K, near magnetic phase transition in pure Cr₂O₃ (305 K). Magnetic contribution into the heat capacity was derived and found to change irregularly with the composition.     

Synthesis and magnetic properties of the complex oxide La<Subscript>1.5</Subscript>Sr<Subscript>1.5</Subscript>CuMnO<Subscript>6.67</Subscript>

A new oxide phase, La_1.5Sr_1.5CuMnO_6.67, related to the Ruddlesden-Popper homologous series A _{n + 1}B _n O_{3n + 1} (n = 2) was synthesized. The magnetic susceptibility of the obtained compound obeys the Curie-Weiss law above 114 K. At 14 K, a magnetic anomaly related to the transition to the spin-glass state was detected.     

Chemical composition-structure-properties relations in a series of Sr<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Ba<Subscript>1-<Emphasis Type="Italic">x</Emphasis></Subscript>Nb<Subscript>2</Subscript>O<Subscript>6</Subscript> compounds

Based on structural studies of Sr _x Ba_1-x Nb₂O₆ crystals with different concentrations of strontium and barium, the structural causality of optical nonlinearity of these crystalline materials is established. YAG:Nd laser radiation of the crystals results in a monotonic decrease in the second harmonic intensity with increasing strontium concentration in a sample. Fine details of the structure responsible for this effect are determined.     

Synthesis and magnetic properties of quasi-unidimensional oxide Sr<Subscript>6.3</Subscript>Rh<Subscript>2.35</Subscript>Mn<Subscript>2.35</Subscript>O<Subscript>15</Subscript>

Attempts of the synthesis in air of complex oxides Sr₃RhMnO_x and Sr₄Rh_1.5Mn_1.5O_x resulted in revealing formation of a new oxide phase Sr_6.3Rh_2.35Mn_2.35O₉ related to quasi-unidimensional family A_3n+3m A′ _n B_3m+n O_9m+6n at n = 1 and m = 1. Its structural characteristics and magnetic properties are studied. X-ray data of the obtained phase is indicated on the basis of trigonal cell (spatial group P321) with the parameters: a 9.6239(4) Å; c ₁ 4.1130(4) Å, c ₂ 2.4946(2) Å. Manganese and rhodium exist in the compound as the cations Mn⁴⁺, Rh³⁺ and Rh⁴⁺, as follows from the data of measuring of magnetic susceptibility in the range 2–300 K.     

New phase in the system FeVO<Subscript>4</Subscript>-Cd<Subscript>4</Subscript>V<Subscript>2</Subscript>O<Subscript>9</Subscript>

A new phase Cd₄Fe_7+xV_9+xO_37+4x, where −0.5<x<1.5, has been obtained in the solid-state in the FeVO₄−Cd₄V₂O₉ system. The temperature of incongruent melting and the unit cell volume of this phase decrease with decreasing the content of cadmium. The IR spectrum and SEM image of the new phase are presented.     

Osmotic Coefficients of the Li<Subscript>2</Subscript>B<Subscript>4</Subscript>O<Subscript>7</Subscript>+LiCl + H<Subscript>2</Subscript>O System at <Emphasis Type="Italic">T</Emphasis>=273.15 K

Osmotic coefficients and water activities for the Li₂B₄O₇+LiCl+H₂O system have been measured at T=273.15 K by the isopiestic method, using an improved apparatus. Two types of osmotic coefficients, φ _S and φ _E, were determined. φ _S is based on the stoichiometric molalities of the solute Li₂B₄O₇(aq), and φ _E is based on equilibrium molalities from consideration of the equilibrium speciation into H₃BO₃,B(OH)₄⁻ and B₃O₃(OH)₄⁻. The stoichiometric equilibrium constants K _m for the aqueous speciation reactions were estimated. Two types of representations of the osmotic coefficients for the Li₂B₄O₇+LiCl+H₂O system are presented with ion-interaction models based on Pitzer’s equations with minor modifications: model (I) represents the φ _S data with six parameters based on considering the ion-interactions between three ionic species of Li⁺, Cl⁻, and B₄O₇²⁻, and model (II) for represents the φ _E data based on considering the equilibrium speciation. The parameters of models (I) and (II) are presented. The standard deviations for the two models are 0.0152 and 0.0298, respectively. Model (I) was more satisfactory than model (II) for representing the isopiestic data.     

High-temperature heat capacity and thermodynamic properties of pyrovanadate Pb<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript> and orthovanadate Pb<Subscript>3</Subscript>(VO<Subscript>4</Subscript>)<Subscript>2</Subscript>

The heat capacities of Pb₂V₂O₇ and Pb₃(VO₄)₂ as a function of temperature in the range 350–965 K have been studied by the differential scanning calorimetry method. The C_P = f(T) curve for Pb₂V₂O₇ is described by the equation C_p = (230.76 ± 0.51) + (73.60 ± 0.50)×10^-3T ? (18.38 ± 0.54)×10⁵T^-2 in the entire temperature range. For Pb₃(VO₄)₂, there is a well-pronounced extreme point in the C_P = f(T) curve at T = 371.5 K, which is caused by the existence of a structural phase transition. The thermodynamic properties of the oxide compounds have been calculated.