Structure and properties of lithium thio-boro-germanate glasses

Structural studies of the ternary xLi₂S + (1 − x)[0.5B₂S₃ + 0.5GeS₂] glasses using IR, Raman, and ¹¹B NMR show that the Li₂S is not shared proportionately between the GeS₂ and B₂S₃ sub-networks of the glass. The IR spectra indicate that the B₂S₃ glass network is under-doped in comparison to the corresponding composition in the xLi₂S + (1 − x)B₂S₃ binary system. Additionally, the Raman spectra show that the GeS₂ glass network is over-modified. Surprisingly, however, the ¹¹Boron static NMR gives evidence that ∼80% of the boron atoms are in tetrahedral coordinated. A super macro tetrahedron, B₁₀S₁₈⁻⁶ is proposed as one of the structures in these glasses in which can account for the apparent low fraction of Li₂S present in the B₂S₃ sub-network while at the same time enabling the high fraction of tetrahedral borons in the glass.     

Optical properties of Cr ion in lithium metasilicate Li2O · SiO2 transparent glass-ceramics

The optical properties of Cr³⁺ ions in lithium metasilicate (Li₂O · SiO₂) transparent glass-ceramics were investigated. The main crystalline phase precipitated was the lithium metasilicate (Li₂O · SiO₂) crystal. The percent crystallinity and crystalline size were ranging 65-75% and 20-35 nm, respectively. The color changes drastically to deep pink from emerald green upon crystallization. New and strong absorption bands appeared and the absorption intensity increases by about 10 times that in glass. These new absorption bands are found to be derived from Cr³⁺ ions in octahedral sites in the lithium metasilicate crystal lattice. Cr³⁺ ions substitute for three Li⁺ ions and occupy the distorted octahedral site between single [SiO₄]_n chains of lithium metasilicate crystal. The ligand field parameters can be estimated: 10Dq = 13 088 cm⁻¹, B = 453 cm⁻¹, Dq/B = 2.89 and C = 2036 cm⁻¹. The near-infrared luminescence centered at 1250 nm was not detected in the deep pink glass-ceramics unlike emerald green glass.     

Thermo-optic properties of B2O3 doped Li2O-Al2O3-SiO2 glass-ceramics

Reduction in the temperature coefficient of the optical path length, dS/dT of Li₂O-Al₂O₃-SiO₂ glass-ceramics with near-zero thermal expansion coefficient was attempted using control of the temperature coefficient of electronic polarizability, ?, and the thermal expansion coefficient, α. The dS/dT value of 2.6 mol% B₂O₃-doped glass-ceramic was 12.5  × 10⁻⁶/°C, which was 0.9 ×  10⁻⁶/°C smaller than that of B₂O₃-free glass-ceramic. On the other hand, reduction in dS/dT through B₂O₃ doping was not confirmed in precursor glasses. Results showed that reduction in dS/dT of the glass-ceramic through B₂O₃ doping is caused by the reduction in ?. The reduction in ? from B₂O₃ doping was probably attributable to numerical reduction in non-bridging oxide ions with larger ? value by the concentration of boron ions in the residual glass phase. In addition, application of hydrostatic pressure during crystallization was effective to inhibit precipitation of β-spodumene solid solution, which thereby decreases dS/dT. The dS/dT value of B₂O₃-doped glass-ceramic crystallized under 196 MPa was 11.7 ×  10⁻⁶/°C. That value was slightly larger than that of silica glass. The α value of this glass-ceramic was smaller than that of silica glass.     

Structure and electrical conductivity of new Li2O-CeO2-B2O3 glasses

Fourier transformation infrared spectra, density and DC electrical conductivity of 30Li₂O · xCeO₂⋅(70 − x)B₂O₃ glasses, where x ranged between 0 and 15 mol%, have been investigated. The results suggested that CeO₂ plays the role of network modifier up to 7.5 mol%. At higher concentrations it plays a dual role; where most of ceria plays the role of network former. The density was observed to increase with increasing CeO₂ content. The effect on density of the oxides in the glasses investigated is in the succession: B₂O₃ < Li₂O < CeO₂. Most of CeO₂ content was found to be associated with B₂O₃ network to convert BO₃ into B O₄⁻ units. The contribution of Li⁺ ions in the conduction process is much more than that due to small polarons. The conductivity of the glasses is mostly controlled by the Li⁺ ions concentration rather than the activation energy for CeO₂ > 5 mol%. Lower than 5 mol% CeO₂ the conductivity is controlled by both factors. The dependence of W on BO₄⁻ content supports the idea of ionic conduction in these glasses.     

Optical Properties of Bi2O3-TeO2-B2O3 Glasses

Glasses of the Bi₂O₃-TeO₂-B₂O₃ ternary system were developed and their linear and nonlinear optical properties were investigated. The absorption edges of these glasses were found to be 367-384 nm with a good transmittance in visible wavelength, although they exhibit the refractive indices as high as 1.98-2.12 at 633 nm. The absorption edges are quite steep and they are analyzed by the Urbach theory. The obtained Urbach energies of these glasses are 73-79 meV which are comparable to silica glasses. The high refractive index and its glass composition dependency are discussed according to the basics of the electronic polarizability and optical basicity. The high third order nonlinear susceptibility χ⁽³⁾ = 2.0 × 10^− 12 esu at 800 nm was also obtained in the 36Bi₂O₃-18TeO₂-46B₂O₃ glass.     

Development of optical nonlinearity, high dielectric constant and ferromagnetic behavior in a silicate glass nanocomposite by suitable heat treatment

We have explored the development of multifunctionalities viz, optical nonlinearity, high dielectric constant and ferromagnetic behavior in a nanostructured silica based glass of 14.0Na₂O, 26.0BaO, 26.0TiO₂, 16.0B₂O₃, 17.0SiO₂, 1.0NiO (mol%) composition. A heat treatment at 863 K for 4 h led to nonlinear refractive index and absorption coefficients at wavelength 800 nm of 0.11 × 10⁻¹⁹ m²/W and 1.15 × 10⁻³ cm/GW, respectively. A heat treatment at 1073 K for 2 h followed by 1113 K for 3 h increased the dielectric constant from 11 to 50, apparently due to the formation of nanocrystals of BaTiO₃ within the glass medium. Glass samples reduced at 923 K for 1 h exhibited ferromagnetic behavior due to the presence of nickel nanoparticles.     

Influence of alkali and alkali-earth metal oxide substitutions on the properties of lithium-iron-phosphate glasses

The influences of different alkali and alkali-earth oxide substitutions on the properties of lithium-iron-phosphate (LIP) glasses have been studied. Na₂O, K₂O, MgO, CaO and BaO were used to substitute Li₂O to prepare LIP glasses with molar compositions of (20 − x)Li₂O − xR₂O(RO) − 30Fe₂O₃ − 50P₂O₅ (x = 2.4, 4, 5.6 and 7.2). The glass transition temperature (T_g) was determined by the differential thermal analysis technique. The density and chemical durability of the prepared glasses were measured based on the Archimedes principle and the weight losses after the glasses were boiled in water. The results show that T_g decreases with the initial substitutions, whereas the density and chemical durability increase. The diminution of the aggregation effect of Li⁺ ions on the glass structure due to the decrease in Li⁺ concentration, the larger molecule weights of the substitutes, the mixed-alkali and depressing effects as well the slower mobility of substitute ions mainly contribute to the initial changes in T_g, density and chemical durability of the LIP glasses, respectively. Further increasing the amounts of substitutes brings about increasing diminution of the aggregation effect of Li⁺ ions and breakage of the glass network on the one hand and increasing amounts of substitutes with larger molecule weights and ion radii on the other hand. Both aspects influence the glass properties oppositely and consequently non-monotonic variations in the properties of LIP glasses with the substitutions are observed.     

Glass formation and structure of glasses in B2O3―Bi2O3―MoO3 system

The purpose of this paper is to study the glass formation tendency in the ternary system B₂O₃―Bi₂O₃―MoO₃ and to define the main structural units building the amorphous network. A wide glass formation area was determined which is situated near the Bi₂O₃―B₂O₃ side. A liquid phase separation region was observed near the MoO₃―B₂O₃ side for compositions containing below 25 mol% Bi₂O₃ and their microheterogeneous structure was observed by SEM. The phase formation was characterized by X-ray diffraction (XRD). By DTA was established the glass transition temperature (T_g) in the range of 380-420 °C and crystallization temperature (T_x) vary between 420 and 540 °C. The main building units forming the amorphous network are BO₃ (1270 and 1200 cm^− 1), BO₄ (930-880, 1050-1040 cm^− 1), MoO₄ (840-760 cm^− 1) and BiO₆ (470 cm^− 1). It was proved that Bi₂O₃ favors the BO₃ → BO₄ transformations while MoO₃ preserves BO₃ units in the amorphous network.     

Effect of ethylene carbonate in poly (methyl methacrylate)-lithium tetraborate based polymer electrolytes

Thin films composed of poly (methyl methacrylate) (PMMA), lithium tetraborate (Li₂B₄O₇) and ethylene carbonate (EC) were prepared by solution casting method. The highest ionic conductivity at room temperature was achieved for the composition PMMA:Li₂B₄O₇:EC (42:18:40) with the value 1.29 × 10⁻⁵ S cm⁻¹. The presence of plasticizer in the polymer complex is crucial in improving the ionic conductivity by increasing the concentration of free mobile ions through the structural conversion from crystalline to amorphous phase. This conversion lowers the viscosity of the polymer complex. Conductivity-temperature plots were found to obey Williams-Landel-Ferry (WLF) mechanism. Dielectric data was analyzed using the dielectric permittivity (ε′) and dielectric modulus (M′) of the samples. Fourier transform infrared (FTIR) studies confirmed that complexation occurs between PMMA, Li₂B₄O₇ and EC. Thermal stability of the polymer complex, which decreases with the addition of plasticizer (EC), was determined using thermal gravimetric analysis (TGA).     

Spectroscopic properties of Er-doped Na2O-Sb2O3-B2O3-SiO2 glasses

Spectroscopic properties of Er³⁺-doped Na₂O-Sb₂O₃-B₂O₃-SiO₂ glasses have been investigated for developing 1.5-μm broadband fiber amplifiers. An intense 1.5-μm near infrared emission with a broad full width at half maximum (FWHM) of 88 nm has been obtained for Er³⁺-doped 5Na₂O-20Sb₂O₃-35B₂O₃-40SiO₂ glass upon excitation with a 980 nm laser diode. The obtained emission cross-section of the ⁴I_13/2 → ⁴I_15/2 transition and the lifetime of the ⁴I_13/2 level of Er³⁺ ions are 6.8 × 10⁻²¹ cm² and 0.36 ms, respectively. It is noted that the product of the emission cross-section and the FWHM of the glass, σ_e × FWHM, is as great as 598.4 × 10⁻²¹ cm² nm, which is comparable or higher than that of Er³⁺-doped bismuth-based and tellurite-based glasses. These special optical properties encourage in identifying them as important materials for potential applications in high performance optics and optical communication networks.     

Investigation of near constant loss contribution to conductivity in lithium bismo-silicate glasses

Glasses having compositions 20Li₂O · (80 − x)Bi₂O₃ · xSiO₂ (x = 55, 60, 65, 70 mol%) were investigated using impedance spectroscopy in the frequency range from 20 Hz to 1 MHz and in the temperature range from 543 to 663 K. The ac and dc conductivities, activation energy of the dc conductivity and relaxation frequency are extracted from the impedance spectra. The increase in conductivity with increase in SiO₂ content is attributed to the change in the structural units of bismuth. Both electric modulus and the conductivity formalism have been employed to study the relaxation dynamics of charge carriers in these glasses. A single ‘master curve’ for normalized plots of all the modulus isotherms observed for a given composition indicates the temperature independence of the dynamic processes for ions in these glasses. Similar values of activation energy for dc conduction and for conductivity relaxation time indicates that the ions overcome same energy barrier while conducting and relaxing. The observed conductivity spectra follows power law with exponent ‘s’ which increases regularly with frequency and approaches unity at higher frequencies. Near constant losses (NCL) characterize this linearly dependent region of conductivity spectra. A deviation from ‘super curve’ for various isotherms of conductivity spectra was also observed in high frequency region and at low temperatures, which supports the existence of different dynamic processes like NCL in addition to the ion hopping processes in the investigated glass system.     

The effect of composition on UV-vis-NIR spectra of iron doped glasses in the systems Na2O/MgO/SiO2 and Na2O/MgO/Al2O3/SiO2

Glasses with the compositions xNa₂O · 10MgO · (90 − x)SiO₂, 10Na₂O · xMgO · (90 − x)SiO₂, 5Na₂O · 15MgO · xAl₂O₃ · (80 − x)SiO₂, xNa₂O · 10MgO · 10Al₂O₃ · (80 − x)SiO₂, 10Na₂O · 10MgO · xAl₂O₃ · (80 − x)SiO₂, 10Na₂O · 5MgO · 10Al₂O₃ · (80 − x)SiO₂ were melted and studied using UV-vis-NIR spectroscopy in the wavenumber range from 5000 to 30 000 cm⁻¹. At [Al₂O₃] > [Na₂O], the UV-cut off is strongly shifted to smaller wavenumbers and the NIR peak at around 10 000 cm⁻¹ attributed to Fe²⁺ in sixfold coordination gets narrower. Furthermore, the intensity of the NIR peak at 5500 cm⁻¹ increases. This is explained by the incorporation of iron in the respective glass structures.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Electrical transport properties of 0.5Li2O-0.5M2O-2B2O3 (M = Li, Na and K) glasses

Transparent glasses in the system 0.5Li₂O-0.5M₂O-2B₂O₃ (M = Li, Na and K) were fabricated via the conventional melt quenching technique. The amorphous and glassy nature of the samples was confirmed via the X-ray powder diffraction and the differential scanning calorimetry, respectively. The frequency and temperature dependent characteristics of the dielectric relaxation and the electrical conductivity were investigated in the 100 Hz-10 MHz frequency range. The imaginary part of the electric modulus spectra was modeled using an approximate solution of Kohrausch-Williams-Watts relation. The stretching exponent, β, was found to be temperature independent for 0.5Li₂O-0.5Na₂O-2B₂O₃ (LNBO) glasses. The activation energy associated with DC conduction was found to be higher (1.25 eV) for 0.5Li₂O-0.5K₂O-2B₂O₃ (LKBO) glasses than that of the other glass systems under study. This is attributed to the mixed cation effect.     

Phase separation and crystallization in the system SiO2-Al2O3-P2O5-B2O3-Na2O glasses

The phase separation and crystallization behavior in the system (80 − X)SiO₂ · X(Al₂O₃ + P₂O₅) · 5B₂O₃ · 15Na₂O (mol%) glasses was investigated. Glasses with X = 20 and 30 phase separated into two phases, one of which is rich in Al₂O₃-P₂O₅-SiO₂ and forms a continuous phase. Glasses containing a larger amount of Al₂O₃-P₂O₅ (X = 40 and 50) readily crystallize and precipitates tridymite type AlPO₄ crystals. It is estimated that the phase separation occurs forming continuous Al₂O₃-P₂O₅-SiO₂ phase at first, and then tridymite type AlPO₄ crystals precipitate and grow in this phase. Highly transparent glass-ceramics comparable to glass can be successfully obtained by controlling heat treatment precisely. The crystal size and percent crystallinity of these transparent glass-ceramics are 20-30 nm and about 50%, respectively.     

Crystallization processes of Li2O-Ga2O3-SiO2-NiO system glasses

Crystallization processes of Li₂O-Ga₂O₃-SiO₂-NiO system glasses have been studied by X-ray diffraction, differential calorimetry and optical absorption. Transparent glass-ceramic containing LiGa₅O₈:Ni²⁺ as the sole crystalline phase has been obtained from glass with the composition of 13Li₂O-23Ga₂O₃-64SiO₂-0.1NiO (in mol%) by the heat treatment in the temperature range from 923 to 953 K. It was revealed that the specific surface area of samples enhances crystallization of LiGaSi₂O₆ but obstructed that of LiGa₅O₈. LiGa₅O₈ grew to nano-sized crystallites dispersed in the glass matrices and did not affect the transparency seriously. In contrast, LiGaSi₂O₆ grew to crystallites with diameters more than 100 nm on the surface and made the glasses opaque. Optical absorption measurements revealed that doped Ni²⁺ occupied five-folded trigonal bipyramidal sites in the as-quenched glass matrices but six-folded octahedral sites of precipitated LiGa₅O₈ in the glass-ceramics. It was confirmed that transparent glass-ceramic containing Ni²⁺:LiGa₅O₈ was effectively obtained by the heat treatment at a temperature of 953 K for 10 h.     

The comparative structure, properties, and ionic conductivity of LiI + Li2S + GeS2 glasses doped with Ga2S3 and La2S3

The well known and characterized fast ion conducting (FIC) LiI + Li₂S + GeS₂ glass-forming system has been further optimized for higher ionic conductivity and improved thermal and chemical stability required for next generation solid electrolyte applications by doping with Ga₂S₃ and La₂S₃. These trivalent dopants are expected to eliminate terminal and non-bridging sulfur (NBS) anions thereby increasing the network connectivity while at the same time increasing the Li⁺ ion conductivity by creating lower basicity [(Ga or La)S_4/2]⁻ anion sites. Consistent with the finding that the glass-forming range for the Ga₂S₃ doped compositions is larger than that for the La₂S₃ compositions, the addition of Ga₂S₃ is found to eliminate NBS units to create bridging sulfur (BS) units that not only gives an improvement to the thermal stability, but also maintains and in some cases increases the ionic conductivity. The compositions with the highest Ga₂S₃ content showed the highest T_gs of ∼325 °C. The addition of La₂S₃ to the base glasses, by comparison, is found to create NBS by forming high coordination octahedral LaS₆³⁻ sites, but yet still improved the chemical stability of the glass in dry air and retained its high ionic conductivity and thermal stability. Significantly, at comparable concentrations of Li₂S and Ga₂S₃ or La₂S₃, the La₂S₃-doped glasses showed the higher conductivities. The addition of the LiI to the glass compositions not only improved the glass-forming ability of the compositions, but also increased the ionic conductivity glasses. LiI concentrations from 0 to 40 mol% improved the conductivities of the Ga₂S₃ glasses from ∼10⁻⁵ to ∼10⁻³ (Ω cm)⁻¹ and of the La₂S₃ glasses from ∼10⁻⁴ to ∼10⁻³ (Ω cm)⁻¹ at room temperature. A maximum conductivity of ∼10⁻³ (Ω cm)⁻¹ at room temperature was observed for all of the glasses and this value is comparable to some of the best Li ion conductors in a sulfide glass system. Yet these new compositions are markedly more thermally and chemically stable than most Li⁺ ion conducting sulfide glasses. LiI additions decreased the T_gs and T_cs of the glasses, but increased the stability towards crystallization (T_c − T_g).     

Deep-UV Raman spectroscopic analysis of structure and dissolution rates of silica-rich sodium borosilicate glasses

As part of ongoing studies to evaluate relationships between structure and rates of dissolution of silicate glasses in aqueous media, sodium borosilicate glasses of composition Na₂O·xB₂O₃·(3 − x)SiO₂, with x ≤ 1 (Na₂O/B₂O₃ ratio ≥ 1), were analyzed using deep-UV Raman spectroscopy. Results were quantified in terms of the fraction of SiO₄ tetrahedra with one non-bridging oxygen (Q³) and then correlated with Na₂O and B₂O₃ content. The Q³ fraction was found to increase with increasing Na₂O content, in agreement with studies on related glasses, and, as long as the value of x was not too high, this contributed to higher rates of dissolution in single pass flow-through testing. In contrast, dissolution rates were less strongly determined by the Q³ fraction when the value of x was near unity, and appeared to grow larger upon further reduction of the Q³ fraction. Results were interpreted to indicate the increasingly important role of network hydrolysis in the glass dissolution mechanism as the BO₄ tetrahedron replaces the Q³ unit as the charge-compensating structure for Na⁺ ions. Finally, the use of deep-UV Raman spectroscopy was found to be advantageous in studying finely powdered glasses in cases where visible Raman spectroscopy suffered from weak Raman scattering and fluorescence interference.     

Effect of boron addition on the structure and properties of iron phosphate glasses

Effects of boron addition on the glass forming characteristics, structure and properties of iron phosphate glasses with nominal compositions of xB₂O₃-(40−x)Fe₂O₃-60P₂O₅ (x = 2-20, mol%) and xB₂O₃-(100−x)[Fe₂O₃-60P₂O₅] (x = 2-20, mol%) have been investigated by DTA, XRD, IR and Mössbauer spectroscopy. Although there were some weak local surface crystallizations on especially most of the glasses in group B, all of the compositions formed glass. DTA spectra showed two exothermic peaks corresponding to crystallizations along with an endothermic glass transition peak. T_g increased with increasing B₂O₃ content for the glasses in the first series which indicates that the addition of B₂O₃ increases the thermal stability of glasses in this series while the opposite is observed in the second series. The dissolution rates of boron containing bulk glasses were found to be around 10⁻⁹ gr/cm² min which are comparable to that of the base iron phosphate glass. When the B₂O₃ content was above 14%, new bands related to BO₄ tetrahedral groups have been observed in the IR spectra. The Mössbauer isomer shift values of boron doped glasses were found to be a little lower than that of base glass but both iron ions had distorted octahedral coordination in all glasses. The fraction of Fe²⁺ ions in glasses (Fe²⁺/∑(Fe²⁺ + Fe³⁺)) was found to be 23% for the base glass while it was 10-22% for the boron doped glasses.     

Nano- and micro-indentation studies on lithium borate-barium bismuth niobate glasses

The structure and mechanical properties of multifunctional lithium tetra-borate based glasses and glass-ceramics of the system (100 − x) Li₂B₄O₇₋x(BaO-Bi₂O₃-Nb₂O₅) with x = 10, 20 and 30 in molar ratio, have been characterized. Nano- and micro-indentation techniques were employed to evaluate the elastic modulus, hardness and toughness of the as-cast and annealed glasses. These were complemented with detailed structural investigations using X-ray diffraction, microscopy (optical, scanning electron and high resolution transmission electron microscopies) and nuclear magnetic resonance spectroscopy. These investigations reveal a smooth variation of the mechanical properties with composition except for the composition corresponding to x = 20. This deviation has been attributed to subtle changes in the glass-structure due to amorphous phase-separation and heat-treatment-assisted nano-crystallization.