Transport property and structural characterization studies on (1 − x)[0.75AgI:0.25AgCl]:xTiO2 conducting composite electrolyte system

Transport property and structural investigation have been carried out on newly synthesized Ag⁺ ion conducting composite electrolyte system. The composite electrolyte system (1 − x)[0.75AgI:0.25AgCl]:xTiO₂, where 0 ? x ? 0.5 (in molar weight fraction) has been synthesized by melt quenching and annealing methods. The chemical compound TiO₂ (second phase dispersoid) dispersed in different compositions in a quenched (0.75AgI:0.25AgCl) mixed system/solid solution; this solid solution was used as a first phase host salt in place of AgI. The different preparation routes were adopted for the composite electrolyte system. Composition x = 0.1 exhibited highest conductivity at room temperature. The composite system 0.9[0.75AgI:0.25AgCl]:0.1TiO₂ was synthesized at different soaking times by melt quenching method. The system exhibited optimum conductivity at 20 min soaking time (σ_rt ≈ 1.4 × 10⁻³ S/cm). The ac conductivity has been measured from Z′-Z″ (Cole-Cole) complex impedance plots using impedance spectroscopic (IS) technique. The electrical conductivity as a function of temperature and frequency has been studied, and activation energy E_a, was calculated from Arrhenius plots for all compositions (0 ? x ? 0.5). The dc conductivity value has been evaluated from Log σ vs. log f plots. Structural characterization studies were carried out by X-ray diffraction (XRD) and differential thermal analysis (DSC) techniques.     

Effects of Nb2O5 Replacement by Er2O3 on elastic and structural properties of 75TeO2-(10 − x)Nb2O5-15ZnO-(x)Er2O3 glass

Tellurite 75TeO₂-(10 − x)Nb₂O₅-15ZnO-(x)Er₂O₃; (x = 0.0-2.5 mol%) glass system with concurrent reduction of Nb₂O₅ and Er₂O₃ addition have been prepared by melt-quenching method. Elastic properties together with structural properties of the glasses were investigated by measuring both longitudinal and shear velocities using the pulse-echo-overlap technique at 5 MHz and Fourier Transform Infrared (FTIR) spectroscopy, respectively. Shear velocity, shear modulus, Young's modulus and Debye temperature were observed to initially decrease at x = 0.5 mol% but remained constant between x = 1.0 mol% to x = 2.0 mol%, before increasing back with Er₂O₃ addition at x = 2.5 mol%. The initial drop in shear velocity and related elastic moduli observed at x = 0.5 mol% were suggested to be due to weakening of glass network rigidity as a result of increase in non-bridging oxygen (NBO) ions as a consequence of Nb₂O₅ reduction. The near constant values of shear velocity, elastic moduli, Debye temperature, hardness and Poisson's ratio between x = 0.5 mol% to x = 2.0 mol% were suggested to be due to competition between bridging oxygen (BO) and NBO ions in the glass network as Er₂O₃ gradually compensated for Nb₂O₅. Further addition of Er₂O₃ (x > 2.0 mol%) seems to further reduce NBO leading to improved rigidity of the glass network causing a large increase of ultrasonic velocity (v_L and v_S) and related elastic moduli at x = 2.5 mol%. FTIR analysis on NbO₆ octahedral, TeO₄ trigonal bipyramid (tbp) and TeO₃ trigonal pyramid (tp) absorption peaks confirmed the initial formation of NBO ions at x = 0.5 mol% followed by NBO/BO competition at x = 0.5-2.0 mol%. Appearance of ZnO₄ tetrahedra and increase in intensity of TeO₄ tbp absorption peaks at x = 2.0 mol% and x = 2.5 mol% indicate increase in formation of BO.     

Thermodynamics of the Cu/Cu-redox equilibrium in soda-silicate and soda-lime-silicate melts

The thermodynamics of the redox equilibrium of Cu⁺/Cu²⁺ were determined by square-wave voltammetry in glass melts with the base mol% compositions x Na₂O · (100 − x) SiO₂ (x = 15, 20, 26 and 33) and (26 − x) Na₂O · x CaO · 74 SiO₂ (x = 0, 5, 10 and 15) doped with 1 mol% CuO in the temperature range from 850 to 1150 °C. All recorded voltammograms showed two maxima attributed to the reductions of Cu²⁺ to Cu⁺ and Cu⁺ to metallic copper. Both peaks are shifted to smaller potentials with decreasing temperature. With increasing melt basicity, the [Cu⁺]/[Cu²⁺]-ratio first increases, and remains constant for optical basicities >0.56. The effect of composition on the redox equilibrium is explained by the incorporation of both Cu⁺ and Cu²⁺ in octahedral coordination into the melt structure.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Studies of some mechanical and optical properties of: (70 − x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Specimens of the glassy system: (70 − x)TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by the melt-quenching. An ultrasonic pulse-echo technique was employed, at 5 MHz, for measuring: the ultrasonic attenuation, longitudinal and shear wave velocities, elastic moduli, Poisson ratio, Debye temperature and hardness of the present glasses. It is found that the gradual replacement of TeO₂ by Li₂O in the glass matrix up to 30 mol% leads to decrease the average crosslink density and rigidity of prepared samples which affects the properties, i.e., the hardness, ultrasonic wave velocities and elastic moduli are decreased, while the Poisson ratio and the ultrasonic attenuation are increased. Also, optical absorption spectra were recorded in the range, 200-800 nm for these glasses. The obtained results showed that a gradual shift in the fundamental absorption edge toward longer wavelengths occurred. Values of both of the optical energy gap, E_opt, and width tails, ΔE, are determined. It is observed that E_opt is decreased and ΔE increased with the increase of Li₂O in the glass matrix up to 30 mol%. The compositional dependences of the above properties are discussed and correlated to the structure of tested glasses.     

Crystallization behavior and microstructure of powdered and bulk ZnO-Al2O3-SiO2 glass-ceramics

The crystallization behavior of glass with the composition: 55.6 mol% SiO₂, 22.8 mol% Al₂O₃, 17.7 mol% ZnO and 3.84 mol% of TiO₂ as nucleating agent and with different particle sizes has been studied by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and tranmission electron microscopy (TEM). In glass powders two crystalline phases: zinc-aluminosilicate s.s. with high-quartz structure, Zn_x/2Al_xSi_3−xO₆, (x varies dependent on heat-treatment temperature) and gahnite are formed. The ratio of these phases depends on particle sizes. In bulk glass, however, gahnite is the sole crystalline phase. The composition of initially formed zinc-aluminosilicate s.s. was determined by Rietveld refinement of XRD patterns to be Zn_0.69Al_1.38Si_1.62O₆. With temperature increase, the amount of zinc-aluminosilicate s.s decreased with simultaneous reduce of zinc and aluminum incorporated in the structure. Eventually at 1423 K almost pure high-quartz structure was formed. The activation energies of zinc-aluminosilicate s.s. and gahnite crystallization were determined by non-isothermal method to be 510 ± 18 and 344 ± 17 kJ mol⁻¹, respectively. The latter value matches well with those cited in literature for crystal growth of gahnite in similar glasses. That is attributed to the fact that the high-quartz structure acts as a precursor for gahnite crystallization.     

The effect of composition on the structure of sodium borophosphate glasses

Glasses in the system 40(P₂O₅)-x(B₂O₃)-(60 − x)(Na₂O) (10 ? x ? 30 mol%) have been prepared by the melt-quenching technique. Thermal properties were studied using differential thermal analysis and the relationship between composition and thermal stability was obtained. Structural characterization was achieved by a combination of experimental data (infrared and Raman spectroscopy, ¹¹B and ³¹P solid state NMR). In particular, variations in the phosphate network structure upon addition of B₂O₃ and Na₂O were investigated. Analysis of the data indicates that with increasing B₂O₃ content and decreasing Na₂O, the glass network shows increasing levels of cross-linking between phosphate and borate units. Evidence of direct B-O-P bonds was observed. In the compositional range investigated, borate groups contain boron almost exclusively in four-fold coordination.     

Planar waveguides by ion exchange in Er-doped tellurite glass

This work reports the preparation of planar waveguides by Ag⁺ → Na⁺ ion exchange in Er³⁺-doped tellurite glass with a composition of 75TeO₂-2GeO₂-10Na₂O-12ZnO-1Er₂O₃ (mol%). The metric, of T_x − T_g, indicates that the glass has good thermal stability. Measurments of refractive index, absorption spectrum, luminescence and lifetime were made. The glass was chemically stable during the ion exchange process. Monomode and multimode planar waveguides in the tellurite glasses have been prepared. We determined the depth of the guides, effective diffusion coefficient and the activation energy. The depths of the waveguides could be controlled by varying ion exchange temperatures and times (250-280 °C, and 3-12 h were used).     

Effect of Bi2O3 proportion on physical, structural and electrical properties of zinc bismuth phosphate glasses

The variation in physical, structural and electrical properties has been studied as a function of Bi₂O₃ content in 20ZnF₂-(10 + x) Bi₂O₃-(70-x) P₂O₅, 0 ≤ x ≤ 10 mol% glasses, which were prepared by melt quenching technique and characterized by differential thermal analysis (DTA). Colorless samples, which have no absorption peaks, are obtained for 10 and 12 mol% of Bi₂O₃ and the glasses are slowly becoming brownish from 15 to 20 mol% of Bi₂O₃ which exhibit two absorption peaks at ~ 370 nm, ~ 450 nm correspond to Bi° transitions ⁴S_3/2 → ²P_3/2 and ⁴S_3/2 → ²P_1/2 respectively. The decrease in ³P₁ → ¹S₀ transition of Bi³⁺ photo luminescence emission for 18 and 20 mol% of Bi₂O₃ and increase in optical absorption area shows the reduction of Bi³⁺ to Bi°. From FTIR studies it is observed that an addition of Bi₂O₃ decreases the P―O―P covalent bond by forming P―O―Bi bonds due to high polarizing nature of Bi³⁺ ions. Dielectric parameters like ε', tan δ and a.c. conductivity σ_ac are found to increase and activation energy for a.c. conduction is found to decrease with the increase in the concentration of Bi₂O₃. Density of defect energy states is found to increase for higher concentration of Bi₂O₃ and is discussed according to quantum mechanical tunneling (QMT) model.     

Preparation and characterization of new fluorotellurite glasses for photonics application

Glasses based on (85 − x)TeO₂-xZnF₂-12PbO-3Nb₂O₅ (x = 0-40) system have been studied for the first time for fabricating mid-infrared optical fiber lasers. The thermal and optical properties including UV-Vis, Raman as well as FTIR spectra are reported. It is demonstrated that increasing the ZnF₂ concentration to 30 mol% significantly increased the thermal stability of the glass. Adding ZnF₂ also reduced the hydroxyl (OH) content of the glass resulting in lower optical absorption in the mid-infrared region, which is crucial for infrared laser applications. The glass absorption cut-off edge near 400 nm blue-shifts with increasing ZnF₂ addition. Raman spectra show a depolymerization of the glass network with increasing transformation of TeO₃₊₁ to TeO₃ structures.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Structure and electrical conductivity of new Li2O-CeO2-B2O3 glasses

Fourier transformation infrared spectra, density and DC electrical conductivity of 30Li₂O · xCeO₂⋅(70 − x)B₂O₃ glasses, where x ranged between 0 and 15 mol%, have been investigated. The results suggested that CeO₂ plays the role of network modifier up to 7.5 mol%. At higher concentrations it plays a dual role; where most of ceria plays the role of network former. The density was observed to increase with increasing CeO₂ content. The effect on density of the oxides in the glasses investigated is in the succession: B₂O₃ < Li₂O < CeO₂. Most of CeO₂ content was found to be associated with B₂O₃ network to convert BO₃ into B O₄⁻ units. The contribution of Li⁺ ions in the conduction process is much more than that due to small polarons. The conductivity of the glasses is mostly controlled by the Li⁺ ions concentration rather than the activation energy for CeO₂ > 5 mol%. Lower than 5 mol% CeO₂ the conductivity is controlled by both factors. The dependence of W on BO₄⁻ content supports the idea of ionic conduction in these glasses.     

Structure and crystallization of potassium titanium phosphate glasses containing B2O3 and SiO2

Transparent glasses composition of which can be expressed by the formula: (100−x) · (K₂O · 2TiO₂ · P₂O₅) · x(K₂O · 2B₂O₃ · 7SiO₂), where x=5, 10, 15 and 20 mol% (KTP-xKBS), were obtained by melt quenching technique. The structure and crystallization behavior of these glasses have been examined by Fourier transform infrared spectroscopy, differential thermal analysis and X-ray diffraction. In spite of their nominal composition, the studied glasses exhibit a similar oxygen polyhedra distribution. However, significant differences were found in the trigonal BO₃ units amount. During DTA runs all the examined glasses devitrify in two steps. In the former, very small crystals of an unknown crystalline phase are produced. In KTP-5KBS and KTP-10KBS glasses anatase phase was also detected. Attempts were made in order to identify the unknown phase (UTP) for which a AB₃(XO₄)₂(OH)₆ Crandallite-type structure was proposed where the A, B and X sites were occupied by K, Ti and/or Al, and P, respectively. In the second devitrification step the crystallization of the KTiOPO₄ phase occurs while the UTP phase previously formed disappears. Isothermal heat treatments performed at temperature just above T_g have allowed one to obtain transparent crystal-glass nanocomposites, formed by crystalline nanostructure of the UTP phase uniformly dispersed in the amorphous matrix.     

Copper redox behavior, structure and properties of copper lead borate glasses

Copper oxidation states, structure and properties of xCuO · (50-x)PbO · 50B₂O₃ glasses were investigated. Both infrared (IR) and ¹¹B magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopies were employed to determine the tetrahedral BO₄ fraction in the glasses as a function of CuO content. IR study indicates that the replacement of Pb²⁺ by Cu²⁺ ions increases the BO₃ units by converting BO₄- containing groups into ring type metaborate groups. The oxidation states of copper ions in the glasses have been studied using both X-ray photoelectron spectroscopy (XPS) and the wet chemical method. For high CuO containing (?30 mol%) glasses, high Cu⁺ ion concentrations (Cu⁺/Cu_tot.>0.3) result in a relatively slow disproportionation of B⁴-containing groups because of the small coordination number of Cu⁺ compared to Cu²⁺ ions. Effects of both glass structure and redox states of copper ions on glass properties including density, Vickers’ hardness, coefficient of thermal expansion, and chemical durability have been discussed.     

Erbium doped fluoride glass-ceramics waveguides fabricated by PVD

Transparent amorphous and glass-ceramics waveguides in the system ZrF₄-LaF₃-ErF₃-AlF₃ (ZELA) have been fabricated by physical vapor deposition (PVD). The ceramming process was studied by means of X-ray diffraction and transmission electron microscopy for different deposition temperatures. With increasing deposition temperature, formation of La_xEr_1−xF₃ nanocrystals with x ∼ 0.3 was observed. The decay curves of the ⁴I_13/2 level in the glass-ceramics with 14.5 mol% Er³⁺ gave evidence of the presence of erbium both in the amorphous matrix (τ = 8.6 ms) and in the crystal phase (τ = 2.2 ms). The decrease of lifetime was due to clustering of erbium incorporated in LaF₃ crystal lattice. No significant increase of attenuation loss was detected after waveguide cerammization (1.3 dB/cm at 1304 nm).     

Structural and optical properties of the gadolinium-lead-germanate glasses

Glasses in the system xGd₂O₃(100 − x)[7GeO₂·3PbO] with 0 ≤ x ≤ 40 mol% have been prepared from melt quenching method. The influence of gadolinium ions on structural behavior in lead-germanate glasses has been investigated using FTIR, UV-VIS and EPR spectroscopy. The structural changes have been analyzed with increasing rare earth concentration.FTIR data suggest that the glass network modifications has taken place mainly in the germanate part whereas the lead part remained unmodified and its network consists mainly from the [GeO₄], [GeO₆], [Ge₂O₇] structural units and with interconnected through Ge-O-Ge bridges in [GeO₄] structural units. The changes in amplitude and bandwidth of the UV-VIS bands ranging from 200 nm to 350 nm depend on the content of Gd₂O₃.By increasing the Gd₂O₃ content in the glass matrix, the optical band gap energy increases, indicating changes of the lattice parameters and that no non-bridging-oxygens form upon the addition of gadolinium oxide. The decreasing trend has been observed both in optical gap band energy and refractive index of oxide glasses at x = 10 mol% Gd₂O₃ indicating breaks up the [GeO₄] tetrahedral units bonds and create of non-bridging oxygen atoms. For sample with x ≥ 20 mol%, the gadolinium ions having a behavior of network formers (g ≈ 4.8) will coordinate more with the excess of oxygen. Accordingly, the gadolinium ions are generally suspected to improve their environment of network formers.     

Structural investigation of bismuth borate glasses and crystalline phases

Glasses of the system: xBi₂O₃-(100−x)B₂O₃ (x = 20 to 66 mol%) were prepared and characterized by density, DSC, UV-visible absorption and ¹¹B MAS-NMR spectroscopy. Glass molar volume increases while the glass transition temperature decreases with Bi₂O₃ concentration. Densities of some bismuth borate glasses are found to be greater or very close to those of single crystal phases with equal composition. B¹¹ MAS-NMR studies determined that the fraction of tetrahedrally coordinated borons (N₄) is maximum at 42 mol% of Bi₂O₃ and that there is a local maxima in N₄ at Bi₂O₃ concentration of 50 mol%. Glasses containing Bi₂O₃ concentration of 33 mol% and higher show an unusual, intense absorption band just below the optical band gap. Two crystalline phases: Bi₃B₅O₁₂ and Bi₄B₂O₉ were prepared by devitrification of glasses and characterized by X-ray diffraction, FTIR and ¹¹B MAS-NMR studies. Both crystalline phases contained significantly lower N₄ than glasses with equal composition.     

Thermal, chemical, optical properties and structure of Er-doped and Er/Yb-codoped P2O5-Al2O3-ZnO glasses

This study was explored in series of the optical, thermal, and structure properties based on 60P₂O₅-10Al₂O₃-30ZnO (PAZ) glasses system that doped with varied rare-earth (RE) elements Yb₂O₃/Er₂O₃. The glass transition temperature, softening temperature and chemical durability were increased with RE-doping concentrations increasing, whereas thermal expansion coefficient was decreased. In the optical properties, the absorption and emission intensities also increase with RE-doping concentrations increasing, When Er₂O₃ and Yb₂O₃ concentrations are over than 3 mol% in the Er³⁺-doped PAZ system and Yb³⁺-doped concentration is over than 3 mol% for Er³⁺/Yb³⁺-codoped PAZ system, the emission intensity significantly decreases presumably due to concentration quenching, formation of the ions clustering, and OH⁻ groups in the glasses network. It is suggested that the maximum emission cross-section (σ_e) is 7.64 × 10^− 21 cm² at 1535 nm is observed for 3 mol% Er³⁺-doped PAZ glasses. Moreover, the maximum σ_e × full-width-at-half-maximum is 327.8 for 5 mol% Er³⁺-doped PAZ glasses.     

Crystallization of monoclinic WO3 in tungstate fluorophosphate glasses

Tungstate fluorophosphate glass compositions with high WO₃ concentration were prepared in the ternary system (80−0.8x)NaPO₃-(20−0.2x)BaF₂-xWO₃ with x = 40,50 and 60 mol%. Transparency decreases as WO₃ concentration increases but can be improved by addition of oxidizing systems such as CeO₂ or Sb₂O₃/NaNO₃. Characterizations by thermal analysis (DSC) point out that an increase in the amount of WO₃ results in a higher glass transition temperature. In addition, such compositions are very stable against devitrification since samples containing 40% and 50% of WO₃ donot even exhibit the expected crystallization event. In these samples, the stability against crystallization decreases with the WO₃ content and vitreous sample containing 60% of WO₃ exhibits an endothermic event around 620 °C due to crystallization of monoclinic WO₃ phase. In these glasses, it was shown that the nucleation stage can be induced by thermal-treatment when external nucleating agents such as Ti or Sb are used. Finally, gold-doped samples exhibit a higher crystallization tendency and monoclinic WO₃ phase can be grown in such glasses.     

Electrical conductivity of NbN-SiO2 films obtained by ammonolysis of Nb2O5-SiO2 sol-gel derived coatings

The studies of electrical conductivity of NbN-SiO₂ films are reported. To obtain these films, sol-gel derived xNb₂O₅-(100 − x)SiO₂ (where x = 100, 90, 80, 70, 60, 50 mol%) coatings were nitrided at 1200 °C. The nitridation process leads to the formation of some disordered structures, with NbN metallic grains dispersed in insulating SiO₂ matrix. The structure of the samples was studied using X-ray diffraction (XRD) and atomic force microscopy (AFM). The electrical conductivity was measured with the conventional four-terminal method in the temperature range from 5 to 280 K. The superconducting transition was not observed even for the sample that does not contain silica. All the samples exhibit negative temperature coefficient of resistivity. The results of conductivity versus temperature may be described on the grounds of a model proposed for a weakly disordered system.