Spectrometric and ellipsometric studies of (1 − x)TiO2 · xLn2O3 (Ln = Nd, Sm, Gd, Er, Yb) thin films

Spectrometric and ellipsometric studies of (1 − x)TiO₂ · xLn₂O₃ (Ln = Nd, Sm, Gd, Er, Yb; x = 0.33, 0.5) thin films at room temperature were performed. The obtained dispersion dependences of refractive indices are successfully described by the optical-refractometric relation. The dependence of optical pseudogap and refractive indices on composition and molar mass of the films is investigated. The influence of compositional disordering on the energy width of the exponential absorption edge is studied.     

Glass-forming ability and crystallization of bulk metallic glass (HfxZr1−x)52.5Cu17.9Ni14.6Al10Ti5

We have produced a series of bulk metallic glasses of composition (Hf_xZr_1−x)_52.5Cu_17.9Ni_14.6Al₁₀Ti₅ (with x=0-1) by an arc melting/suction casting method. The density of these alloys increases by nearly 67% with increasing Hf content from 6.65 g/cm³ (x=0) to 11.09 g/cm³ (x=1). Over the same composition range the glass-forming ability decreases, as demonstrated by the size of the largest amorphous ingots that can be cast without crystallization. Although both the glass transition temperature and the melting temperature increase linearly with increasing Hf content, the reduced glass transition temperature (T_g/T_m) decreases, from 0.64 (x=0) to 0.62 (x=1), which suggests that the `confusion principle' correlating increased glass-forming ability with increased number of components, does not apply in this case due to the chemical similarity between Zr and Hf. A different crystallization behavior is observed for Zr-based and Hf-based glasses. The final crystalline phases are CuZr₂ and Zr₂Ni for Zr-based alloys, and Al₁₆Hf₆Ni₇ and CuHf₂ for Hf-based alloys.     

Structural and electrical properties of vapour phase grown Cd1 − xFexTe single crystals

Cd_1 − xFe_xTe single crystals were prepared by vapour phase growth method in the composition range of 0 ≤ x ≤ 0.03. Chemical analysis, surface morphology, structural investigations and electrical properties were carried out by EDAX, SEM, XRD, TEM and transport technique, respectively. Microscopic variations between the target and actual compositions were noticed. Morphology studies revealed that dislocation aided growth is active in the present crystals. TEM and XRD studies confirmed that the samples of all compositions crystallized in zinc blende structure, and the lattice parameters varied almost linearly decreases with Fe content. At room temperature, the resistivity of the Cd_1 − xFe_xTe crystals of all compositions (x = 0.01, 0.015, 0.02, 0.025 and 0.03) lies in the range of 3.5-6.5 M Ω, the activation energies lie in the range of 63-133 meV, and the samples were show the ‘p’ type conductivity.     

Thermal dissolution of Ag(Cu) in amorphous Ge(Sx Se1 − x)2 system

Thermally induced solid state reaction of Ag(Cu) into thin Ge(S_x Se_1 − x)₂ films with x = 0, 0.1, 0.4 and 1.0 was investigated using a step by step technique in order to design films with exact Ag(Cu) concentrations for applications in integrated IR optical devices. A thin film of Ag(Cu) was deposited on top of the host Ge(S_x Se_1 − x)₂ films followed by annealing in vacuum at constant temperature, which resulted in homogeneous films of good optical quality. The variation in Ag(Cu) concentration in the films ranged between 5 and 35 at.%. The kinetics of the diffusion and dissolution of metal in the host films was measured by optically monitoring the change in thickness of doped chalcogenide during consecutive thermal annealing steps. The kinetics studies revealed that the thermal dissolution rate of the Cu is greater than that of Ag. Optical UV-VIS transmission spectra of chalcogenide glass layers, undoped and thermal doped by Ag(Cu), were measured to establish the optical properties of the films. The spectra were analyzed using the technique proposed by Swanepoel and the results show that the addition of metal increases the absorption coefficient in the power-law regime and consequently the optical gap decreases and the refractive index increases. The amorphous character of the films was checked by X-ray diffraction which confirmed the amorphous structure of all Ag(Cu)GeSSe thin films.     

Structure and properties of Ni60(Nb100−xTax)34Sn6 bulk metallic glass alloys

Refractory bulk metallic glasses and bulk metallic glass composites are formed in quaternary Ni-Nb-Ta-Sn alloy system. Alloys of composition Ni₆₀(Nb_100−xTa_x)₃₄Sn₆ (x = 20, 40, 60, 80) alloys were prepared by injection-casting the molten alloys into copper molds. Glassy alloys are formed in the thickness of half mm strips. With thicker strips (e.g., 1 mm), Nb₂O₅ and Ni₃Sn phases and the amorphous phase form an in situ composite. Glass transition temperatures, crystallization temperatures, and ΔT_x, defined as T_x1 − T_g (T_x1: first crystallization temperature, T_g: glass transition temperature) of the alloys increase dramatically with increasing Ta contents. These refractory bulk amorphous alloys exhibit high Young’s modulus (155-170 GPa), shear modulus (56-63 GPa), and estimated yield strength (3-3.6 GPa).     

Insulator-like electrical transport in structurally ordered Al65Cu20+xRu15−x (x = 1.5, 1.0, 0.5, 0.0 and −0.5) icosahedral quasicrystals

Low-temperature resistivities, in zero-field and 8 T field, and magnetoresistance have been measured down to 1.4-300 K for stable icosahedral quasicrystals Al₆₅Cu_20+xRu_15−x (x = 1.5, 1.0, 0.5, 0.0 and −0.5). The analysis of the magnetoresistance data shows an overwhelming presence of anti weak-localization effect (τ_so ∼ 10⁻¹² s). But the sample with x = −0.5 shows anomalous magnetoresistance and the anti weak-localization effect breaks down (τ_so to be 10⁻¹⁵ s). The in-field σ-T between 5 K and 20 K, for x = 1.0, 0.5, 0.0 and −0.5 samples, and between 1.4 K and 40 K for x = 1.5 sample, follow a power-law behavior with an exponent of 0.5 and above ∼30 K the exponent ranges from 1.17 to 1.58. The observed power-laws basically characterize the presence of critical regime of the metal-insulator (MI) transition, dominated by electron-electron and electron-phonon inelastic scattering events respectively. In samples with x = 1.0, 0.5, 0.0 and −0.5 the in field σ-T has been found to follow ln σ-vs-T^1/4 below 5 K, which indicates the presence of variable range hopping. The observed transport features indicate the occurrence of proximity of metal-insulator transition in these Al-Cu-Ru quasicrystal samples.     

Crystallization kinetics of Fe73.5−xMnxCu1Nb3Si13.5B9 (x = 0, 1, 3, 5, 7) amorphous alloys

In this study, we have investigated the effect of substituting Mn for Fe on the crystallization kinetics of amorphous Fe_73.5−xMn_xCu₁Nb₃Si_13.5B₉ (x = 1, 3, 5, 7) alloys. The samples were annealed at 550 °C and 600 °C for 1 h under an argon atmosphere. The X-ray diffraction analyses showed only a crystalline peak belonging to the α-Fe(Si) phase, with the grain size ranging from 12.2 nm for x = 0 to 16.7 nm for x = 7. The activation energies of the alloys were calculated using Kissinger, Ozawa and Augis-Bennett models based on differential thermal analysis data. The Avrami exponent n was calculated from the Johnson-Mehl-Avrami equation. The activation energy increased up to x = 3, then decreased with increasing Mn content. The values of the Avrami exponent showed that the crystallization is typical diffusion-controlled three-dimensional growth at a constant nucleation rate.     

Effects of Nb2O5 Replacement by Er2O3 on elastic and structural properties of 75TeO2-(10 − x)Nb2O5-15ZnO-(x)Er2O3 glass

Tellurite 75TeO₂-(10 − x)Nb₂O₅-15ZnO-(x)Er₂O₃; (x = 0.0-2.5 mol%) glass system with concurrent reduction of Nb₂O₅ and Er₂O₃ addition have been prepared by melt-quenching method. Elastic properties together with structural properties of the glasses were investigated by measuring both longitudinal and shear velocities using the pulse-echo-overlap technique at 5 MHz and Fourier Transform Infrared (FTIR) spectroscopy, respectively. Shear velocity, shear modulus, Young's modulus and Debye temperature were observed to initially decrease at x = 0.5 mol% but remained constant between x = 1.0 mol% to x = 2.0 mol%, before increasing back with Er₂O₃ addition at x = 2.5 mol%. The initial drop in shear velocity and related elastic moduli observed at x = 0.5 mol% were suggested to be due to weakening of glass network rigidity as a result of increase in non-bridging oxygen (NBO) ions as a consequence of Nb₂O₅ reduction. The near constant values of shear velocity, elastic moduli, Debye temperature, hardness and Poisson's ratio between x = 0.5 mol% to x = 2.0 mol% were suggested to be due to competition between bridging oxygen (BO) and NBO ions in the glass network as Er₂O₃ gradually compensated for Nb₂O₅. Further addition of Er₂O₃ (x > 2.0 mol%) seems to further reduce NBO leading to improved rigidity of the glass network causing a large increase of ultrasonic velocity (v_L and v_S) and related elastic moduli at x = 2.5 mol%. FTIR analysis on NbO₆ octahedral, TeO₄ trigonal bipyramid (tbp) and TeO₃ trigonal pyramid (tp) absorption peaks confirmed the initial formation of NBO ions at x = 0.5 mol% followed by NBO/BO competition at x = 0.5-2.0 mol%. Appearance of ZnO₄ tetrahedra and increase in intensity of TeO₄ tbp absorption peaks at x = 2.0 mol% and x = 2.5 mol% indicate increase in formation of BO.     

Preparation, phase transformation and microstructure of ZrxTi1−xO2 (x = 0.1-0.9) fine fibers

Zr_xTi_1−xO₂ (x = 0.1-0.9) fibers were prepared by the sol-gel dry-spinning method. Polyacetylacetonatozirconium (PAZ) and tetrabutyl titanate (C₁₆H₃₆O₄Ti) were used as raw materials. The green fibers were obtained from the amorphous spinnable solution and then heat-treated to convert into polycrystalline fibers. The main phase changes from TiO₂ to zirconium titanate (ZT) and then tetragonal ZrO₂ with increasing ZrO₂ content. The crystallization temperature varied with the molar ratio of Zr:Ti. The heat-treated fibers at 1050 °C have few pores and no cracks with diameters of 10-20μm and lengths of 1-5 cm.     

Boron content dependance of magnetoimpedance in Fe91−xZr5BxNb4 alloys

A systematic investigation of the influence of B content on the magnetoimpedance (MI) effect in melt-spun Fe_91−xZr₅B_xNb₄ (FZBN, 0 ? x ? 30) ribbons has been performed within a frequency range, f ∼ 310-1110 kHz and under a varying dc magnetic field (H_dc) up to 70 Oe. The MI effect is not observed in the sample with x ? 5 but within the range 8 ? x ? 30. A distinct MI effect has been observed with a maximum change of 180% at around 1.1 MHz in the sample with x = 20, coincident with a saturation magnetic field of 66 Oe and a field sensitivity of about 7%/Oe. Magnetic measurements reveal that the MI effect and B content dependence of the effect are closely related to coercivity of the FZBN alloy series, except for the sample with 20 at.%. The drastic MI ratio observed in the sample with x = 20 is ascribed to its special microstructure. The mechanism of the MI effect in FZBN alloys and of the significant MI value appearing at a B content of x = 20 is discussed in this paper.     

Crystallization and glass transition kinetics in Cu ion substituted Cux-Ag1 − xI-Ag2O-V2O5 superionic glasses

Crystallization kinetics and thermal properties in superionic glasses Cu_xAg_1 − xI-Ag₂O-V₂O₅ for x = 0.1-0.3 have been thoroughly investigated. X-ray diffraction and differential scanning calorimetry measurements confirm the precipitation of at least three compounds during crystallization, viz. AgI, Ag₄V₂O₇ and Ag₈I₄V₂O₇. The activation energies for structural relaxation (E_s) and crystallization (E_c) obtained using Moynihan and Kissinger formulation exhibit interesting trends with CuI substitution. The E_s value decreases with CuI substitution in the system. Further, the E_c values corresponding to precipitation of Ag₄V₂O₇ and Ag₈I₄V₂O₇ exhibit increasing trend, whereas, for that of AgI precipitation a decreasing trend with CuI content. The Avrami parameter calculated from Augis-Bennett method and Ozawa equation suggests predominantly surface crystallization in the glassy system. The electrical conductivity-temperature (σ-T) cycles interestingly demonstrate increasing precipitation of AgI with CuI content in the glass matrix.     

Sodium tracer diffusion in glasses of the type (Na2O)0.2[(BO1.5)x(SiO2)1 − x]0.8

Sodium tracer diffusion coefficients, D_Na*, have been measured in sodium borosilicate glasses of the type (Na₂O)_0.2[(BO_1.5)_x(SiO₂)_1 − x]_0.8 as a function of temperature and the composition parameter x. In these glasses, which can alternatively also be described by using the formula Na₂O·(2B₂O₃)_x·(4SiO₂)_1 − x, one network former unit, SiO₂, is replaced by another one, BO_1.5, while keeping the sodium concentration constant. At constant temperature, the tracer diffusion coefficient of sodium as a function of x has a shallow minimum at about x = 0.7. At temperatures below about 310 °C the temperature dependences of the measured tracer diffusion coefficients are of Arrhenius-type; at higher temperatures one observes an increase in the temperature dependence with increasing temperature. The activation energy derived from sodium tracer diffusion data for temperatures up to about 310 °C increases about linearly with increasing x from about 70 to 80 kJ/mol. The pre-exponential factor as a function of x varies by about one order of magnitude and has a minimum at about x = 0.4. Values derived for the Haven-ratio are smaller than one and show a shallow minimum as a function of x at around x = 0.75. Furthermore, it was investigated whether there is a significant, directly measurable uptake of water during annealing in moist atmospheres and whether water taken up from moist atmospheres can influence the diffusion of sodium.     

Electrical properties of AsxSe1−x (x ≤ 0.05) Mott-barriers

We have experimentally measured the current-voltage and capacitance-voltage characteristics of Au/amorphous As_xSe_1 − x (x ≤ 0.05)/Zr trilayer structures at temperatures from 4 to 295 K. The observed capacitance of structures with an amorphous As_xSe_1 − x (a-As_xSe_1 − x) thickness of ~ 0.4 to ~ 2.8 μm does not significantly change over the entire range of applied bias (− 5 V to 5 V), indicating that the a-As_xSe_1 − x films are fully depleted and thus the structures are Mott barriers. The current-voltage (I-V) characteristics of the a-As_0.03Se_0.97 device at low (< 3000 V/cm) to moderate fields (3000 V/cm-10000 V/cm) follow the predictions of trap limited space charge conduction theory, as they exhibit Ohmic behavior at low fields and trap limited space charge current at moderate fields. According to the trap limited space charge current model of Lampert, the a-As_0.03Se_0.97 film has an effective hole mobility, Θμ (with Θ < 1), of ~ 5 × 10^− 7 cm²/V-sec at 295 K. This value is similar to, but consistently lower than previously reported mobilities inferred from time of flight measurements. The current at high fields (> 10⁴ V/cm) increases rapidly with applied field as a result of carrier emission from localized states and is consistent with transport by the Poole-Frenkel mechanism. A permanent transition to a high conductance state (~ 10^− 3 S) is observed after exposure to very high electric fields (~ 4 × 10⁵V/cm).     

Potentiodynamic polarization studies on amorphous Zr46.75Ti8.25Cu7.5Ni10Be27.5, Zr65Cu17.5Ni10Al7.5, Zr67Ni33 and Ti60Ni40 in aqueous HNO3 solutions

Potentiodynamic polarization studies were carried out on virgin specimens of Zr-based bulk amorphous alloys Zr_46.75Ti_8.25Cu_7.5Ni₁₀Be_27.5 and Zr₆₅Cu_17.5Ni₁₀Al_7.5, and conventional-type binary amorphous alloys Zr₆₇Ni₃₃ and Ti₆₀Ni₄₀ in solutions of 0.2 M, 0.5 M and 1.0 M HNO₃ at room temperature. The values of the corrosion current density (I_corr) for the bulk amorphous alloy Zr_46.75Ti_8.25Cu_7.5Ni₁₀Be_27.5 were found to be comparable with those of Zr₆₅Cu_17.5Ni₁₀Al_7.5 in 0.2 M and 0.5 M HNO₃, but the value of I_corr for the former was almost three times more than that of the latter in 1.0 M HNO₃. In the case of conventional binary amorphous alloys, Ti₆₀Ni₄₀ showed lower value of I_corr as compared to Zr₆₇Ni₃₃ in 0.5 M and 1.0 M HNO₃ and a comparable value of I_corr in 0.2 M HNO₃. In general, the binary Ti₆₀Ni₄₀ displayed the best corrosion resistance among all the alloys in all the cases and the corrosion current density (I_corr) for all the alloys was found to increase with the increasing concentration of nitric acid. It is noticed that the bulk amorphous alloys do not possess superior corrosion resistance as compared to conventional binary amorphous alloys in aqueous HNO₃ solutions. The observed differences in their corrosion behavior are attributed to different alloy constituents and composition of the alloys investigated.     

Glass formation ability and mechanical properties of Ti40Cu40Zr10Ni10 alloy

Melt-spun ribbon and bulk samples in cylindrical rod form with diameter ranging from 2 mm to 4 mm of Ti₄₀Cu₄₀Zr₁₀Ni₁₀ alloy were prepared by melt-spinning technique and copper mould casting method, respectively. The microstructure, thermal stability and mechanical properties of the bulk samples were investigated. A completely glassy single phase is formed in the 2 mm rod sample. Increasing the diameter of the rod samples resulted in the formation of CuTi crystalline phase in the 3 mm and 4 mm rod samples. The 2 mm single glassy rod sample exhibited a large supercooled liquid region ΔT_x = 58 K and γ = T_x/(T_g + T_l) is 0.390, which indicated that the alloy possessed a good glass-forming ability. The bulk samples also exhibited good mechanical properties. The 2 mm rod sample showed the highest yield strength of about 2086 MPa. The 3 mm rod sample not only showed high yield strength of about 2000 MPa, but also enhanced plastic strain of about 0.71%.     

Transport property and structural characterization studies on (1 − x)[0.75AgI:0.25AgCl]:xTiO2 conducting composite electrolyte system

Transport property and structural investigation have been carried out on newly synthesized Ag⁺ ion conducting composite electrolyte system. The composite electrolyte system (1 − x)[0.75AgI:0.25AgCl]:xTiO₂, where 0 ? x ? 0.5 (in molar weight fraction) has been synthesized by melt quenching and annealing methods. The chemical compound TiO₂ (second phase dispersoid) dispersed in different compositions in a quenched (0.75AgI:0.25AgCl) mixed system/solid solution; this solid solution was used as a first phase host salt in place of AgI. The different preparation routes were adopted for the composite electrolyte system. Composition x = 0.1 exhibited highest conductivity at room temperature. The composite system 0.9[0.75AgI:0.25AgCl]:0.1TiO₂ was synthesized at different soaking times by melt quenching method. The system exhibited optimum conductivity at 20 min soaking time (σ_rt ≈ 1.4 × 10⁻³ S/cm). The ac conductivity has been measured from Z′-Z″ (Cole-Cole) complex impedance plots using impedance spectroscopic (IS) technique. The electrical conductivity as a function of temperature and frequency has been studied, and activation energy E_a, was calculated from Arrhenius plots for all compositions (0 ? x ? 0.5). The dc conductivity value has been evaluated from Log σ vs. log f plots. Structural characterization studies were carried out by X-ray diffraction (XRD) and differential thermal analysis (DSC) techniques.     

Sodium tracer diffusion in glasses of the type (Na2O)0.2(B2O3)y(SiO2)0.8 − y

Sodium tracer diffusion coefficients, D^?_Na, have been measured in sodium borosilicate glasses of the type (Na₂O)_0.2(B₂O₃)_y(SiO₂)_0.8−y as a function of temperature and the composition parameter y. At constant temperature, the tracer diffusion coefficient of sodium decreases as y increases. The activation enthalpy derived from sodium tracer diffusion data for temperatures up to about 350 °C increases about linearly with increasing values of y from about 70 to 100 kJ/mol. The pre-exponential factor of the sodium tracer diffusion coefficient as a function of y varies by about one order of magnitude and has a minimum at near y = 0.3.     

Three-dimensional structure of fast ion conducting 0.5Li2S + 0.5[(1 − x)GeS2 + xGeO2] glasses from high-energy X-ray diffraction and reverse Monte Carlo simulations

A high-energy X-ray diffraction study has been carried out on a series of 0.5Li₂S + 0.5[(1 − x)GeS₂ + xGeO₂] glasses with x = 0.0, 0.1, 0.2, 0.4, 0.6 and 0.8. Structure factors were measured to wave vectors as high as 30 Å⁻¹ resulting in atomic pair distribution functions with high real space resolution. The three dimensional atomic-scale structure of the glasses was modeled by reverse Monte Carlo simulations based on the diffraction data. Results from the simulations show that at the atomic-scale 0.5Li₂S + 0.5[(1 − x)GeS₂ + xGeO₂] glasses may be viewed as an assembly of independent chains of (Li^+-S)₂GeS_2/2 and (Li^+-O)₂GeO_2/2 tetrahedra as repeat units, where the Li ions occupy the open space between the chains. The new structure data may help understand the reasons for the sharp maximum in the Li⁺ ion conductivity at x ∼ 0.2.     

Effect of carbon on the microstructural evolution of Zr66.7−xNi33.3Cx (x = 0, 1, 3) alloys during mechanical alloying

In the present paper, the effect of carbon on the microstructural evolution of Zr_66.7−xNi_33.3C_x (x = 0, 1, 3) alloys during mechanical alloying has been investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that these three alloys undergo similar amorphization and crystallization processes, and the final milling product is a metastable fcc-Zr_66.7−xNi_33.3C_x phase. The carbon addition can shorten the milling time for the complete amorphization reaction and enhance the stability of the formed amorphous alloy, which can suppress the mechanically induced amorphous-crystalline phase transformation with further increasing milling time.     

Studies of some mechanical and optical properties of: (70 − x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Specimens of the glassy system: (70 − x)TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by the melt-quenching. An ultrasonic pulse-echo technique was employed, at 5 MHz, for measuring: the ultrasonic attenuation, longitudinal and shear wave velocities, elastic moduli, Poisson ratio, Debye temperature and hardness of the present glasses. It is found that the gradual replacement of TeO₂ by Li₂O in the glass matrix up to 30 mol% leads to decrease the average crosslink density and rigidity of prepared samples which affects the properties, i.e., the hardness, ultrasonic wave velocities and elastic moduli are decreased, while the Poisson ratio and the ultrasonic attenuation are increased. Also, optical absorption spectra were recorded in the range, 200-800 nm for these glasses. The obtained results showed that a gradual shift in the fundamental absorption edge toward longer wavelengths occurred. Values of both of the optical energy gap, E_opt, and width tails, ΔE, are determined. It is observed that E_opt is decreased and ΔE increased with the increase of Li₂O in the glass matrix up to 30 mol%. The compositional dependences of the above properties are discussed and correlated to the structure of tested glasses.