Effects of Nb2O5 Replacement by Er2O3 on elastic and structural properties of 75TeO2-(10 − x)Nb2O5-15ZnO-(x)Er2O3 glass

Tellurite 75TeO₂-(10 − x)Nb₂O₅-15ZnO-(x)Er₂O₃; (x = 0.0-2.5 mol%) glass system with concurrent reduction of Nb₂O₅ and Er₂O₃ addition have been prepared by melt-quenching method. Elastic properties together with structural properties of the glasses were investigated by measuring both longitudinal and shear velocities using the pulse-echo-overlap technique at 5 MHz and Fourier Transform Infrared (FTIR) spectroscopy, respectively. Shear velocity, shear modulus, Young's modulus and Debye temperature were observed to initially decrease at x = 0.5 mol% but remained constant between x = 1.0 mol% to x = 2.0 mol%, before increasing back with Er₂O₃ addition at x = 2.5 mol%. The initial drop in shear velocity and related elastic moduli observed at x = 0.5 mol% were suggested to be due to weakening of glass network rigidity as a result of increase in non-bridging oxygen (NBO) ions as a consequence of Nb₂O₅ reduction. The near constant values of shear velocity, elastic moduli, Debye temperature, hardness and Poisson's ratio between x = 0.5 mol% to x = 2.0 mol% were suggested to be due to competition between bridging oxygen (BO) and NBO ions in the glass network as Er₂O₃ gradually compensated for Nb₂O₅. Further addition of Er₂O₃ (x > 2.0 mol%) seems to further reduce NBO leading to improved rigidity of the glass network causing a large increase of ultrasonic velocity (v_L and v_S) and related elastic moduli at x = 2.5 mol%. FTIR analysis on NbO₆ octahedral, TeO₄ trigonal bipyramid (tbp) and TeO₃ trigonal pyramid (tp) absorption peaks confirmed the initial formation of NBO ions at x = 0.5 mol% followed by NBO/BO competition at x = 0.5-2.0 mol%. Appearance of ZnO₄ tetrahedra and increase in intensity of TeO₄ tbp absorption peaks at x = 2.0 mol% and x = 2.5 mol% indicate increase in formation of BO.     

Devitrification behavior and structure of Li2O-B2O3-Al2O3 composite gels from metal alkoxides

(30 − x/2)Li₂O·(70 − x/2)B₂O₃·xAl₂O₃(x = 0, 5 and 10) composite gels have been fabricated by the sol-gel method. LiOCH₃, B(OC₄H₉)₃, and Al(OC₄H₉)₃ were used as precursor for Li₂O, B₂O₃, and Al₂O₃, respectively. B(OC₄H₉)₃ and Al(OC₄H₉)₃ were hydrolyzed separately and then mixed. The crystallization behavior and structure of the gels upon thermal treatment temperatures between 150 and 550 °C are characterized on the basis of SEM, XRD and IR analyses. Xerogel with x = 0 exhibits non-crystal features, whereas crystalline phases are found in the xerogels with x = 5 and 10. The crystalline phases are not found with increasing heat treatment temperatures from 150 to 450 °C, but crystalline phases appear present at 550 °C. The xerogel with x = 0, subject to thermal treatment below 450 °C, is found to be still amorphous, and a 550 °C heat treatment leads its structure changing from glassy to crystalline.     

Phase separation and crystallization in the system SiO2-Al2O3-P2O5-B2O3-Na2O glasses

The phase separation and crystallization behavior in the system (80 − X)SiO₂ · X(Al₂O₃ + P₂O₅) · 5B₂O₃ · 15Na₂O (mol%) glasses was investigated. Glasses with X = 20 and 30 phase separated into two phases, one of which is rich in Al₂O₃-P₂O₅-SiO₂ and forms a continuous phase. Glasses containing a larger amount of Al₂O₃-P₂O₅ (X = 40 and 50) readily crystallize and precipitates tridymite type AlPO₄ crystals. It is estimated that the phase separation occurs forming continuous Al₂O₃-P₂O₅-SiO₂ phase at first, and then tridymite type AlPO₄ crystals precipitate and grow in this phase. Highly transparent glass-ceramics comparable to glass can be successfully obtained by controlling heat treatment precisely. The crystal size and percent crystallinity of these transparent glass-ceramics are 20-30 nm and about 50%, respectively.     

Bioactive glasses in the system CaO-B2O3-P2O5: Preparation, structural study and in vitro evaluation

Glasses in the system x B₂O₃(1 − x) [y CaO P₂O₅], (x = 0, 0.1, 0.2, 0.3, y = 2, 2.6, 3, 4, 5) have been prepared by fast quenching of high temperature melts. The presence of B₂O₃ affected the glass forming ability, allowing the preparation of calcium phosphate glasses with y ? 2.6. The structure of glasses was analyzed by μ-Raman and infrared spectroscopy. The analysis indicated that the glass network is dominated by highly charged species from phosphate tetrahedra with 3 (pyro) or 4 (ortho) NBOs, while the boron atoms are incorporated mainly in 3 coordinated sites in the form of B∅₃ or B∅₂O⁻ units. A small fraction of units was also evident from the spectra analysis of glasses with high CaO content. All calcium borophosphate glasses exhibited bioactivity after soaking in SBF solution within a few days. This was observed by μ-Raman and SEM microscopy, while XRD patterns clearly revealed growth of hydroxyapatite phase. The presence of boron in the glass network has a catalytic effect at favoring bioactivity of the otherwise bioinert calcium phosphate glasses.     

Structure and growth morphology of Gd2O3-doped CeO2 thin films

Gd₂O₃-doped CeO₂ (Gd_0.1Ce_0.9O_1.95, GDC) thin films were synthesized on (1 0 0) Si single crystal substrates by a reactive radio frequency magnetron sputtering technique. Structures and surface morphologies were characterized by X-ray diffraction (XRD), Atomic Force Microscopy (AFM) and one-dimensional power spectral density (1DPSD) analysis. The XRD patterns indicated that, in the temperature range of 200–700 °C, f.c.c. structured GDC thin films were formed with growth orientations varying with temperature—random growth at 200 °C, (2 2 0) textures at 300–600 °C and (1 1 1) texture at 700 °C. GDC film synthesized at 200 °C had the smoothest surface with roughness of R_rms=0.973 nm. Its 1DPSD plot was characterized with a constant part at the low frequencies and a part at the high frequencies that could be fitted by the f^−2.4 power law decay. Such surface feature and scaling behavior were probably caused by the high deposition rate and random growth in the GDC film at this temperature. At higher temperatures (300–700 °C), however, an intermediate frequency slope (−γ₂≈−2) appeared in the 1DPSD plots between the low frequency constant part and the high frequency part fitted by f⁻⁴ power law decay, which indicated a roughing mechanism dominated by crystallographic orientation growth that caused much rougher surfaces in GDC films (R_rms>4 nm).     

Temperature-assisted electrical poling of TeO2-Bi2O3-ZnO glasses for non-linear optical applications

The suitability for effective thermal poling of the ternary tellurite glasses with the compositions (100 − 2x)TeO₂-xBi₂O₃-xZnO (x = 5, 10 and 15, in molar percentage) for the second harmonic generation (SHG) was analyzed. The glass transitions and crystallization temperatures were studied via differential thermal analysis. The structural properties of the annealed glasses and furtherly heat-treated samples were probed by extended X-ray absorption fine structure (EXAFS) spectroscopy. Thermal poling of the glasses was undertaken conventionally at various temperatures close to the glass transition temperature under high vacuum and the second harmonic generated signals were compared. A new technique of two stage poling was tested for comparison. The non-linear second harmonic signal of the poled glasses was analyzed using the Maker-fringe technique and it was found that the two stage poling enhanced the non-linear efficiency when compared to the conventionally poled samples.     

EPR study of RLi2O.V2O5, RNa2O.V2O5, RCaO.V2O5, and RBaO.V2O5 modified vanadate glass systems

Experimental EPR spectra in several modified vanadate glass systems reveal hyperfine structure (hfs) lines whose widths vary with the molar ratio of modifier to vanadium pentoxide, R. In the RNa₂O.V₂O₅ system, for example, hfs lines show no resolution at low R values (near 0.1); by contrast, these lines exhibit dramatic narrowing as R approaches 0.5. In the model proposed here, this narrowing is due to an increase in hopping time for small polarons associated with V⁴⁺ ions in these systems. Increases in polaron hopping times are accompanied by increases in electron spin-spin relaxation times T₂'s, and, an associated narrowing of EPR linewidths. Experiments confirm that spectral widths are limited by electron T₂'s due to the fact that EPR linewidths do not vary with temperature down to 4.2 K. Resolved spectra in RNa₂O.V₂O₅ at R = 0.5 reveal a hyperfine coupling parameter of 0.0177 ± 0.0008 T, corresponding to an upper-limit polaron hopping frequency of 487 ± 20 MHz. By similar analyses, the systems of RCaO.V₂O₅, RBaO.V₂O₅, and RLi₂O.V₂O₅ exhibit comparable polaron hopping frequencies limits of 480 ± 20 MHz, 469 ± 20 MHz, and 468 ± 20 MHz, respectively, when R is near 1.0. In addition to the relaxation effects discussed here, results of modeling of resolved spectra to obtain hyperfine coupling constants A_|| and A_┴, and g_┴ values g_|| and g_┴ are presented and discussed.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Spectral properties of PbO-P2O5 glasses

The optical absorption spectra of xPbO-(100 − x) P₂O₅ glasses where x = 5, 10, 15, 20, 25, and 30 is reported. The spectral absorption of these glasses was measured in the spectral range 300-900 nm at room temperature. Optical absorption spectra show that the absorption edge has a tail extending towards lower energies. The edge shifts nearly linearly towards higher energies with increasing PbO content. The degree of the edge shift was found to depend on the PbO content and is mostly related to the structural rearrangement and the relative concentrations of the glass basic units. The optical energy gap increases, from 2.55 to 3.05 eV by increasing PbO content from 5 to 30 mol%. The width of the localized states is decreased by increasing PbO content.     

The effect of alumina on the Sn/Sn redox equilibrium and the incorporation of tin in Na2O/Al2O3/SiO2 melts

Glasses with the basic compositions 10Na₂O · 10CaO · xAl₂O₃ · (80 − x)SiO₂ (x=0, 5, 15, 25) and 16Na₂O · 10CaO · xAl₂O₃ · (74 − x)SiO₂ (x=0, 5, 10, 15, 20) doped with 0.25-0.5 mol% SnO₂ were studied using square-wave-voltammetry at temperatures in the range from 1000 to 1600 °C. The voltammograms exhibit a maximum which increases linearly with increasing temperature. With increasing alumina concentration and decreasing Na₂O concentration the peak potentials get more negative. Mössbauer spectra showed two signals attributed to Sn²⁺ and Sn⁴⁺. Increasing alumina concentrations did not affect the isomer shift of Sn²⁺; however, they led to increasing quadrupole splitting, while in the case of Sn⁴⁺ both isomer shift and quadrupole splitting increased. A structural model is proposed which explains the effect of the composition on both the peak potentials and the Mössbauer parameters.     

Electron spin resonance and magnetic studies on CaO-SiO2-P2O5-Na2O-Fe2O3 glasses

Room temperature electron spin resonance (ESR) spectra and temperature dependent magnetic susceptibility measurements have been performed to investigate the effect of iron ions in 41CaO · (52 − x)SiO₂ · 4P₂O₅ · xFe₂O₃ · 3Na₂O (2 ? x ? 10 mol%) glasses. The ESR spectra of the glass exhibited the absorptions centered at g ≈ 2.1 and g ≈ 4.3. The variation of the intensity and linewidth of these absorption lines with composition has been interpreted in terms of variation in the concentration of the Fe²⁺ and Fe³⁺ in the glass and the interaction between the iron ions. The magnetic susceptibility data were used to obtain information on the relative concentration and interaction between the iron ions in the glass.     

Synthesis and physical properties of glasses in the Sb2O3-PbCl2-MoO3 system

Lead chloroantimonite glasses form stable binary glasses that may accommodate numerous oxides or halides as a third component. Molybdenum trioxide is a glass progenitor leading to molybdate glasses. Ternary glasses have been synthesized and studied in the Sb₂O₃-PbCl₂-MoO₃ system. Compositional limits of glass formation are reported and two series of glass samples have been prepared corresponding to the general formulas: (90 − x)Sb₂O₃-xPbCl₂-10MoO₃ and (90 − x)Sb₂O₃-xMoO₃-10PbCl₂. Glass transition temperature is close to 290 °C at high Sb₂O₃ content and decreases as antimony oxide is substituted by MoO₃ or PbCl₂. Position, width and intensity of crystallization peak suggest that devitrification rate is small in some composition ranges. The evolution of density, thermal expansion, refractive index and microhardness has been studied as a function of composition parameter x. Deviations from linearity are observed. They suggest structural changes in the case of the MoO₃/Sb₂O₃ substitution while it appears that molar volume increases linearly versus lead content in the other series of glasses. Refractive index is close to 2.04. Optical transmission ranges from 550 nm in the visible spectrum to 5.5 μm in the infrared. It is limited by extrinsic absorption bands arising from hydroxyls and silicon impurities. Young's, bulk and shear moduli have been measured for the two series of samples.     

Electrical conductivity and dielectric properties of Bi2O3-GeO2-PbO-MoO3 glasses

Glasses having compositions 40Bi₂O₃-20GeO₂-(40−x)PbO-xMoO₃ (where x = 3, 6, 9, 12 and 15 mol%) were prepared by normal melt quenching technique. The density (d) decreases gradually with the increase of the MoO₃ content in such glasses. This may be due to the lower molecular weight MoO₃ is substituted by a higher molecular weight PbO. The dc conductivity decreases while the activation energy increases with the increase of the MoO₃ content. The dc conductivity in the present glasses is electronic depends strongly upon the average distance, R, between the Mo ions. Analysis of the electrical properties has been made in the light of small polaron hopping model. The parameters obtained from the fits of the experimental data to this model are reasonable and consistent with glass composition. The conduction is attributed to non-adiabatic hopping of small polaron. Dielectric properties (constant ε, loss tan δ, ac conductivity σ_ac, over a range of frequency 0.12-100 kHz and temperature 325-650 K and frequency exponent s) of these glasses have been studied.     

Crystal growth and characterization of two-leg spin ladder compounds: Sr14Cu24O41 and Sr2Ca12Cu24O41

Single crystals of Sr_14−xCa_xCu₂₄O₄₁ (x=0 and 12) are grown by the travelling solvent floating zone technique using an image furnace. The grown crystals are characterized for their single crystallinity by the X-ray and Neutron Laue method. The magnetic susceptibility measurements in Sr₁₄Cu₂₄O₄₁ show considerable anisotropy along the main crystallographic axes. Low-temperature specific heat measurement and DC susceptibility measurement in Ca-doped crystal showed antiferromagnetic ordering at 2.8 K at ambient pressure. High-pressure AC susceptibility measurement on Ca-doped crystal showed a sharp superconducting transition at 2 K under 40 kbars. T_c onset reached a maximum value of 9.9 K at 54 kbars. The bulk superconductivity of the sample is confirmed by the high-pressure AC calorimetry with T_c max=9.4 K and T_N=5 K at 56 kbars.     

Studies of some mechanical and optical properties of: (70 − x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Specimens of the glassy system: (70 − x)TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by the melt-quenching. An ultrasonic pulse-echo technique was employed, at 5 MHz, for measuring: the ultrasonic attenuation, longitudinal and shear wave velocities, elastic moduli, Poisson ratio, Debye temperature and hardness of the present glasses. It is found that the gradual replacement of TeO₂ by Li₂O in the glass matrix up to 30 mol% leads to decrease the average crosslink density and rigidity of prepared samples which affects the properties, i.e., the hardness, ultrasonic wave velocities and elastic moduli are decreased, while the Poisson ratio and the ultrasonic attenuation are increased. Also, optical absorption spectra were recorded in the range, 200-800 nm for these glasses. The obtained results showed that a gradual shift in the fundamental absorption edge toward longer wavelengths occurred. Values of both of the optical energy gap, E_opt, and width tails, ΔE, are determined. It is observed that E_opt is decreased and ΔE increased with the increase of Li₂O in the glass matrix up to 30 mol%. The compositional dependences of the above properties are discussed and correlated to the structure of tested glasses.     

Decrease in dielectric loss of CaCu3Ti4O12 by the addition of TeO2

CaCu₃Ti₄O₁₂ (CCTO) has challenged for the last few years the scientific community due to its large dielectric constant, which is almost temperature and frequency independent, from 100 K to 400 K and from 1 kHz to 1 MHz, respectively. This makes the material desirable for many electronic applications. However, the dissipation factor is very large, with tan δ values, at room temperature and 1 kHz, higher than 0.1.In our work we report how the addition of TeO₂ lowers the dielectric loss and, although there is a decrease of dielectric constant of doped samples relatively to the undoped one, high dielectric constant values are still being reached. The sample of doped CCTO with 1.5% of TeO₂ by weight, presents, at room temperature and 60 kHz, a large dielectric constant, over 3000, and a dissipation factor around 0.09, which represents a decrease on tan δ over 30% relatively to the CCTO undoped sample. Two relaxation processes were identified for all the samples, one at MHz region and the other one at low frequency region (< 1 kHz). DC bias voltage was applied up to 40 V and a strong dc bias influence on the low frequency region was observed both at dielectric and impedance responses of the undoped sample, which was much weaker than the dc bias effects on the 4% Te doped sample.Dielectric measurements will be discussed and correlated with the samples' microstructure, supported on internal barrier layer capacitance (IBLC) and surface barrier layer capacitance (SBLC) models.     

Spectrometric and ellipsometric studies of (1 − x)TiO2 · xLn2O3 (Ln = Nd, Sm, Gd, Er, Yb) thin films

Spectrometric and ellipsometric studies of (1 − x)TiO₂ · xLn₂O₃ (Ln = Nd, Sm, Gd, Er, Yb; x = 0.33, 0.5) thin films at room temperature were performed. The obtained dispersion dependences of refractive indices are successfully described by the optical-refractometric relation. The dependence of optical pseudogap and refractive indices on composition and molar mass of the films is investigated. The influence of compositional disordering on the energy width of the exponential absorption edge is studied.     

Spectroscopic and magnetic behavior of xNd2O3(1−x)(3Bi2O3 · PbO) glasses

Glasses of the xNd₂O₃(1−x)(3Bi₂O₃ · PbO) system with 0?x?0.30 were obtained and studied by IR spectroscopy, X-ray photoelectron spectroscopy (XPS), density and magnetic susceptibility measurements. IR and density measurements show that the addition of neodymium ions produces structural changes and the neodymium ions play a network modifier role in the host glass matrix. XPS investigation permitted following the evolution of the structural disorder, of the degree of polymerization of bismuthate chains and of the fraction of bridging oxygens with respect to the neodymium ion concentration of the studied glasses. Magnetic susceptibility data show that the Nd³⁺ ions are present as isolated species for x?0.05 and as both isolated and exchange coupled species for higher x values.     

Crystallization kinetics of Fe73.5−xMnxCu1Nb3Si13.5B9 (x = 0, 1, 3, 5, 7) amorphous alloys

In this study, we have investigated the effect of substituting Mn for Fe on the crystallization kinetics of amorphous Fe_73.5−xMn_xCu₁Nb₃Si_13.5B₉ (x = 1, 3, 5, 7) alloys. The samples were annealed at 550 °C and 600 °C for 1 h under an argon atmosphere. The X-ray diffraction analyses showed only a crystalline peak belonging to the α-Fe(Si) phase, with the grain size ranging from 12.2 nm for x = 0 to 16.7 nm for x = 7. The activation energies of the alloys were calculated using Kissinger, Ozawa and Augis-Bennett models based on differential thermal analysis data. The Avrami exponent n was calculated from the Johnson-Mehl-Avrami equation. The activation energy increased up to x = 3, then decreased with increasing Mn content. The values of the Avrami exponent showed that the crystallization is typical diffusion-controlled three-dimensional growth at a constant nucleation rate.     

Compositional dependence of the optical properties of amorphous Sb2Se3−xSx thin films

Thin films of Sb₂Se_3−xS_x solid solutions (x = 0, 1, 2, and 3) were deposited by thermal evaporation of presynthesized materials on glass substrates held at room temperature. The films compositions were confirmed by using energy dispersive analysis of X-rays (EDAX). X-ray diffraction studies revealed that all the as-deposited films as well as those annealed at T_a < 423 K have amorphous phase. The optical constants (n, k) and the thickness (t) of the films were determined from optical transmittance data, in the spectral range 500-2500 nm, using the Swanepoel method. The dispersion parameters were determined from the analysis of the refractive index. An analysis of the optical absorption spectra revealed an Urbach’s tail in the low absorption region, while in the high absorption region an indirect band gap characterizes the films with different compositions. It was found that the optical band gap energy increases quadratically as the S content increases.