Preparation and Photovoltaic Properties of p-Type Nano-ZnFe2O4

p-Type nano-ZnFe₂O₄ semiconductors were gained by high-prssure treatment. Surface photovoltaic spectrum(SPS) and transient photovoltaic technology(TPV) were used for studying the photogenerated charge of nano-ZnFe₂O₄. Results show that the photovoltaic behavior of nano-ZnFe₂O₄ changed as the processing pressure increased. When the processing pressure was higher than 2 GPa, both SPS response interval and peak changed significantly. XPS results show that the non-lattice oxygen entered into the lattice and the content of lattice oxygen increased with the increase of processing pressure. The material changed from oxygen vacancy type to oxygen excess type and the photoelectric properties changed from n-type to p-type when the processing pressure is higher than 2 GPa.     

TiO2/Ag2O纳米材料的制备及其对甲醛的气敏性能

采用溶胶-凝胶法制备了掺杂Ag的TiO2纳米晶粉体. 用XRD、TEM和BET方法对纳米晶的晶型﹑晶粒大小和表面性能进行了表征. 分析结果显示, 相同条件下掺杂Ag的TiO2比纯TiO2纳米材料具有更大的比表面积. 气敏性能测试结果表明, 掺杂Ag的TiO2传感器对甲醛有较好的灵敏度和更高的选择性.当焙烧温度为500 ℃, 掺杂Ag的摩尔比为5%(n(AgNO3)/n(Ti(OC4H9)4)=5%)时, TiO2对甲醛气体敏感性能最好. 在最佳工作电流124 mA下, 该元件对10 μL·L-1 HCHO的灵敏度S 接近4, 它的响应时间不超过1 s, 恢复时间为9 s.     

负载型纳米TiO2／Al2O3复合载体负载SO4^2-催化剂的制备与催化性能研究

分别采用沉淀法,水解法和溶胶凝胶法制备了负载型纳米TiO2/Al2O3复合载体,同时在复合载体表面负载SO42-制成SO42-/TiO2/Al2O3固体酸催化剂,并将此催化剂用于α-蒎烯异构化反应中.用XRD、FTIR,TPD等手段对催化剂的晶相结构、比表面积、孔径分布、表面酸性等进行了表征.结果表明,三种方法所制备的催化剂均为纳米级且拥有着丰富而规则的孔结构,水解法制备的SO42-/TiO2/Al2O3催化剂中TiO2的平均粒径(10.0 nm)较小,比表面积(172.88 m2/g)较大,平均孔径为3.926 nm,表面酸中心数和酸强度均高于沉淀法和溶胶凝胶法制备的催化剂,在α-蒎烯催化异化反应中的具有较高的活性,α-蒎烯转化率为82.76%.     

Preparation and characterization of CoFe_2O_4/TiO_2 magnetic composite films

CoFe2O4/TiO2 magnetic composite films were prepared using the sol-gel method with tetrabutyltitanate and metallic chlorates as starting materials. The effects of heat treatment temperatures on micro- structures and on magnetic properties were studied. The microstructure and properties of the samples at different heat treatment temperatures were characterized by X-ray diffraction, Raman spectrum, scanning electron microscopy, polarized microscopy and vibrating sample magnetometry. The results show that crystals of different substances grow up independently. Cobalt ferrite is evenly embedded into the titanium dioxide matrix in the prepared composite films. The magnetism of the composite films is enhanced with an increase of the heat temperature.     

Fe3O4／TiO2磁性催化剂的制备及在污水治理中的应用

以纳米Fe3O4为载体,以钛酸四丁酯为前躯体,用溶胶-凝胶法在Fe3O4表面包覆TiO2层,制备Fe3O4／TiO2光催化材料．透射电镜（TEM）、X射线衍射（XRD）、X射线光电子能谱（XPS）和红外光谱（IR）分析表明,TiO2在纳米Fe3O4颗粒表面形成很好的包覆层．用Fe3O4／TiO2光催化材料对工业上难处理...     

磁性纳米TiO_2/SiO_2/NiFe_2O_4的制备及其催化性能

采用溶胶凝胶法制备了核壳结构磁性纳米TiO2/SiO2/NiFe2O4催化剂.利用XRD、TEM、VSM等手段对样品的粒径、晶体结构、磁性和光催化性能进行了研究.结果表明:SiO2/NiFe2O4的加入抑制了TiO2纳米粒子的生长,使晶粒尺寸减小,促进了锐钛矿相向金红石相的转变,催化剂的回收率和光催化性能均得到提高.光催化实验结果表明,当SiO2/NiFe2O4的负载量为15%时,焙烧温度为500℃时对亚甲基兰的脱色率最高.     

Pr2O3/TiO2纳米粒子的制备及其US/UV协同催化降解苯酚的研究

以钛酸丁酯为原料,用溶胶-凝胶(Sol-gel)法制备了Pr2O3/TiO2纳米粒子.采用X光衍射仪对粉体的物相进行了表征.样品经500 ℃焙烧2 h后,0.5%(摩尔分数)Pr3 TiO2纳米粉末为单一的锐钛型结构.研究了US(超声波)/UV(紫外光)协同催化氧化水中苯酚的降解效果,考察了超声波声强、溶液pH值、反应温度和催化剂投加量对苯酚降解速率的影响.研究结果表明:US/UV协同催化氧化要比单独超声波或光化学处理效果显著,证实了声光联合技术具有明显的协同效应.     

染料敏化La~(3+)掺杂的TiO_2纳晶薄膜制备及其光电性能

采用溶胶-凝胶法制备出La3+掺杂的TiO2纳米粉体材料,通过料浆喷涂工艺制得掺杂La3+的TiO2薄膜并将其以N719染料敏化制成染料敏化太阳能电池(DSSC)。以X射线衍射(XRD)、扫描电镜(SEM)和DSSC测试系统对制得的La3+掺杂的TiO2纳米粉体材料、相应的La3+掺杂的TiO2薄膜以及制成的DSSC分别进行测试表征,研究了La3+掺杂对TiO2晶型和染料敏化太阳能电池性能的影响。XRD测试结果表明,La3+的掺杂改善了TiO2的颗粒分布;电池的测试结果说明,La3+掺杂量为0.5%,煅烧温度为450℃时制备的纳米TiO2膜DSSC电池性能最佳,光电转换效率达1.926%。     

固体超强酸催化剂SO2-4/TiO2-WO3的制备及其催化性能研究

制备了固体超强酸催化剂SO2-4/TiO2-WO3,并以丁酸丁酯的合成作为探针反应,系统考察了WO3的含量、硫酸浸渍浓度、焙烧温度等制备条件对SO2-4/TiO2-WO3催化活性的影响.实验表明:制备催化剂的适宜条件为m(H2WO4)=12.5%,硫酸浸渍浓度为1.0 mol·L-1,焙烧温度为580℃,活化时间3 h.利用优化条件下制备的催化剂SO2-4/TiO2-WO3催化合成缩醛(酮),在醛/酮与二元醇(乙二醇,1,2-丙二醇)的投料摩尔比为1:1.5,催化剂的用量占反应物总投料质量的0.5%,反应时间为l h条件下,2-甲基-2-乙氧羰甲基-1,3-二氧环戊烷的收率为78.7%,2,4-二甲基-2-乙氧羰甲基-1,3-二氧环戊烷的收率为83.0%,环己酮-乙二醇缩酮的收率为85.9%,环己酮-1,2-丙二醇缩酮的收率为84.6%,丁酮-乙二醇缩酮的收率为70.7%,丁酮-1,2-丙二醇缩酮的收率为88.3%,2-丙基-1,3-二氧环戊烷的收率为80.6%,4-甲基-2-丙基-1,3-二氧环戊烷的收率为79.6%,2-异丙基-1,3-二氧环戊烷的收率为64.2%,4-甲基-2-异丙基-1,3-二氧环戊烷的收率为83.3%,2-苯基-l,3-二氧环戊烷的收率为75.3%,4-甲基-2-苯基-1,3-二氧环戊烷的收率为95.1%.     

介孔TiO2-ZnO复合薄膜的制备与表征

以三嵌段聚合物P123为模板剂, 以钛酸异丙酯和二水乙酸锌为无机前驱体, 利用溶胶-凝胶法和旋涂法成功地制备了不同ZnO含量的介孔TiO2-ZnO复合薄膜. 在ZnO前驱体摩尔分数为0~50％范围内获得薄膜质量较高的介孔TiO2-ZnO复合薄膜. 用小角XRD、扫描电子显微镜(SEM)、高分辨透射电子显微镜(HRTEM)、能谱仪(EDS)、紫外-可见吸收光谱(UV-Vis)及X射线光电子能谱(XPS)对所得的复合薄膜进行了表征和分析. EDS和XPS等研究证明介孔薄膜为TiO2和ZnO的复合体系, 且ZnO前驱体含量的增加仍能保持TiO2-ZnO复合薄膜的均匀性. UV-Vis研究结果表明, 介孔复合薄膜的光学带隙宽度为3.45-3.58 eV, 随着ZnO含量的增加, 复合薄膜的紫外吸收蓝移.     

二氧化钛/聚乙烯吡咯烷酮纳米复合薄膜的制备与表征

采用溶胶-凝胶法(so1 gel)制备了TiO2/聚乙烯吡咯烷酮(PVP)有机 无机纳米复合薄膜.采用扫描电子显微镜、接触角测定仪、红外光谱仪、紫外 可见吸收光谱仪和静 动摩擦系数测定仪对所制备的TiO2/PVP纳米复合薄膜进行了结构表征和性能研究.结果表明:所制备的TiO2/PVP纳米复合薄膜表面平整光滑、无裂纹、具有一定的疏水性、良好的透明性、防紫外线性能和减摩抗磨性能.     

纤维状TiO2／Bi2O3光催化剂的制备及其光催化性能

研究了SrCo0．7Fe0．2Mo0．103-δ（SCFM）材料的相组成、微观结构、热膨胀系数、氧渗透性能和化学稳定性,其结果和文献中的SrCo0．8Fe0.2O3-δ（SCF）做了对比．通过EDTA-citric混合方法成功获得了纯相SCFM材料．SCFM材料在500-1050℃显示出比SCF材料更低的热膨胀系数（24×10^-6-29×10^-6／K）,表明其具有一种更稳定的结构,尽管由于Mo掺杂造成其透氧率比SCF材料低,但是SCFM的透氧率仍然维持在一个较高水平．证实SCF中的Mo掺杂能够阻止晶格中的有序-无序转变,提高了其在CO2下的化学稳定性．     

Effect of Magnetic Carrier NiFe2O4 Nanoparticles on Physicochemical and Catalytic Properties of Magnetically Separable Photocatalyst TiO2/NiFe2O4

A series of magnetically separable photocatalyst TiO₂/NiFe₂O₄(TN) with different mass ratios of NiFe₂O₄ to TiO₂ was prepared by sol-gel method. The X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), transmission electron microscopy(TEM), ultraviolet-visible spectroscopy(UV-Vis), Brunauer-Emmett-Teller(BET) surface analysis and photoluminescence spectroscopy(PL) were used to characterize the photocatalyst TN. The XRD patterns of TN indicate that adulterating a smidgen of NiFe₂O₄ into TiO₂(about 0.1%, mass ratio) can promote the phase transformation of TiO₂, however, when the doped amount of NiFe₂O₄ surpasses 1%, the introduction of NiFe₂O₄ can inhibit the growth of TiO₂ crystal grain and reduce the size of TiO₂ crystal grain. The XPS results of TN indicate that some Fe³⁺ replace Ti⁴⁺ of the TiO₂ lattice forming Fe―O―Ti bonds. The PL analysis of TN shows that the NiFe₂O₄ nanoparticles in photocatalyst TN play the role of the effective recombination centre of the photogenerated electrons and holes, leading to the decrease in photocatalytic activity.     

Ag/TiO2中空纳米纤维光催化材料的制备及表征

以棉花纤维为模板制备了银掺杂的TiO₂中空纳米纤维光催化材料, 利用热重分析(TG)、扫描电子显微镜(SEM)、X光电子能谱(XPS)、X射线衍射(XRD)、Zeta电位、紫外-可见光谱(UV-Vis)和傅立叶变换红外光谱(FT-IR)等技术对该材料的形貌、晶体结构、银的状态等特性进行了表征. 以亚甲基蓝(MB)的脱色降解为模型反应, 考察了银掺杂的样品Ag/TiO₂在不同光源下的光催化性能. 结果表明, 所制得的Ag/TiO₂材料保留了棉花纤维的形貌, 且表面带有大量的负电荷|该Ag/TiO₂材料在太阳光条件下的光催化性能显著高于同条件下TiO₂和同材料在紫外光条件下的, 如Ag/TiO₂在太阳光下1.5 h可使MB溶液的脱色降解率在95%以上, 在TiO₂上2.5 h时不足60%, 低于Ag/TiO₂上0.5 h的结果|在紫外光条件下Ag/TiO₂ 3 h时脱色降解率仅为35%. 连续重复使用5次时Ag/TiO₂仍能保证MB溶液的脱色降解率在90%以上|该纤维光催化材料易于离心分离去除、再利用. 因此, 以棉花为模板制备的Ag/TiO₂中空纳米纤维催化材料是一种无能耗、无污染、高活性的绿色环保型光催化材料.     

SO2-4/TiO2光催化氧化邻硝基苯酚

采用不同浓度的硫酸溶液浸渍处理TiO2,制得不同SO2-4含量的SO2-4/TiO2光催化剂.考察了光催化剂对邻硝基苯酚溶液的光催化行为.发现SO2-4/TiO2的光催化活性高于TiO2的光催化活性,浸渍液中H2SO4的浓度和焙烧温度对SO2-4/TiO2的催化活性有一定的影响,最佳浸渍H2SO4浓度为0.5 mol·L-1,最佳焙烧温度为500℃.     

Mo掺杂TiO2/AC负载膜的制备及光催化活性

溶胶-凝胶法;Mo掺杂TiO2/AC负载膜的制备及光催化活性     

纳米复合固体超强酸S2O2-8/CoFe2O4催化合成癸二酸二乙酯

催化酯化反应;纳米复合固体超强酸S2O2-8/CoFe2O4催化合成癸二酸二乙酯     

Preparation of CoFe2O4/sawdust and NiFe2O4/sawdust magnetic nanocomposites for removal of oil from the water surface

In this study, CoFe₂O₄/Sawdust and NiFe₂O₄/Sawdust magnetic nanocomposites were synthesized using a hydrothermal method, and then characterized using X-ray powder diffraction, Infrared, scanning electron microscopy, Brunauer–Emmett–Teller/Barrett–Joyner–Halenda, and vibrating-sample magnetometer techniques. In this study, unmodified sawdust (US), modified sawdust (MS), unmodified CoFe₂O₄/sawdust (UCS), modified CoFe₂O₄/sawdust (MCS), unmodified NiFe₂O₄/sawdust (UNS), and modified NiFe₂O₄/Sawdust (MNS) magnetic nanocomposites, which are inexpensive, economical, environmentally friendly absorbents, and have a high selective hydrophobic, were used for the removal of oil from the water surface. The results show that the UCS, MCS, UNS, and MNS magnetic nanocomposites can selectively absorb the oil spreading on the water surface, due to its superhydrophobicity and superoleophilicity, and can be easily collected from water under the influence of a magnetic field. In addition, the results showed that the absorbents reach their equilibrium at the 30-min mark. Among all the absorbents, the MNS magnetic nanocomposite showed the maximum absorption capacity (18.172 g/g) at the 40-min mark. The results of the kinetic studies showed that the second-order kinetic equation with the highest correlation coefficient had the best fit with the experimental results.     

低含量铁掺杂纳米TiO2薄膜的制备及其抗菌机理研究