Synthesis and properties of aromatic polyamides based on non-, methyl-, and phenyl-substituted 4,4′-bis(1,4-phenylenedioxy)dibenzoic acids

4,4′-(1,4-Phenylenedioxy)dibenzoic acid (3), 4,4′-(2,5-tolylenedioxy)dibenzoic acid (Me-3), and 4,4′-(2,5-biphenylenedioxy)dibenzoic acid (Ph-3) were prepared by the nucleophilic substitution reaction of p-fluorobenzonitrile with hydroquinone, methylhydroquinone, and phenylhydroquinone, respectively, followed by alkaline hydrolysis. Several aromatic polyamides having inherent viscosities of 0.66–1.34 dL/g were directly prepared by a Yamazaki phosphorylation polyamidation technique from dicarboxylic acids 3, Me-3, and Ph-3, respectively, with aromatic diamines using triphenyl phosphite and pyridine as condensing agents. The solubility of methyl- or phenyl-substituted polyamides was remarkably enhanced when compared to that of nonsubstituted analogues. Most of the substituted polyamides revealed an amorphous nature and were readily soluble in a variety of organic solvents including N,N-dimethylacetamide (DMAc), N-methyl-2-pyrrolidone (NMP), N,N-dimethylformamide, dimethyl sulfoxide, and m-cresol. Transparent, flexible, and tough films of these polymers could be cast from the DMAc or NMP solutions. These films had tensile strength of 60–100 MPa, elongation to break of 6–11%, and tensile modulus of 1.68–2.25 GPa. The glass transition temperatures (T_g) of most polyamides could be determined by differential scanning calorimetry (DSC) and were in the range of 200–232°C. Thermogravimetric analyses established that these polymers were fairly stable up to 450°C, and the 10% weight loss temperatures were recorded in the range of 458–535°C in nitrogen and 468–528°C in air atmosphere. In general, the phenyl-substituted polyamides exhibited relatively higher T_g, thermal stability, and solubility. © 1996 John Wiley & Sons, Inc.     

Soluble aromatic poly(ether amide)s containing aryl‐, alkyl‐, and chloro‐substituted phthalazinone segments

A series of novel aromatic diamines ( 2 – 4 ) containing the alkyl‐, aryl, or chloro‐substituted group of phthalazinone segments were synthesized via two synthetic steps starting from 4‐(3‐R‐4‐hydroxyphenyl)‐2,3‐phthalazinone‐1 (R = Ph, CH₃, Cl). Three series of aromatic polyamides containing phthalazinone moieties were prepared through diamines 2 – 4 reacting with different aromatic dicarboxylic acids via a direct Yamazaki–Higashi phosphorylation polycondensation reaction. The resulting aromatic polyamides had inherent viscosities in the range of 0.40–0.76 dL/g. The thermal property of the polyamides was examined with DSC and thermogravimetric analysis. The glass‐transition temperatures of these polyamides ranged from 298 to 340 °C. The 10% mass‐loss temperature was above 405 °C under nitrogen. Structures of monomers 2 – 4 and the polymers were confirmed by Fourier transform infrared spectroscopy, ¹H NMR, and mass spectrometry. Good solubility of these polymers in polar solvents such as N‐methylpyrrolidone, dimethylformamide, dimethylacetamide (DMAc), and m‐cresol was observed, and tough, flexible films were obtained from the polymer's DMAc solutions. The effect of the substituted group on the physical property of polymers was also investigated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2026–2030, 2004     

Aromatic rigid chain copolymers. I. Synthesis,structure, and solubility of phenyl-substituted para-linked aromatic random copolyamides

Four 2,5-biphenylene based difunctional condensation monomers, such as 2,5-diphenyldicar-boxylic acid or phenylterephthalic acid (PTA), 2,5-bis(carbonylimino-4-benzoic acid)biphenyl (2,5-BCIBABP), 2,5-diaminobiphenyl hydrochloride (2,5-DABP.HCl) and 2,5-bis(iminocarbonyl-4-benzoic acid)biphenyl (2,5-BICBABP), have been synthesized and characterized. These monomers were polymerized in combination with terephthalic acid (TA) and p-phenylenediamine (PPD) via the phosphorylation reaction to prepare a series of phenyl-substituted random copolyamides having all amide groups attached to para-positions of the benzene rings. All the copolyamides have been characterized by solubility, solution viscosity, and by differential scanning calorimetry (DSC). Some of these copolyamides have unusual solubility in organic solvents such as N,N-dimethylacetamide (DMAc) and N-methyl-2-pyrrolidinone (NMP) containing dissolved lithium chloride. A few copolyamides were tested for lyotropic behavior and found to form anisotropic solutions at critical concentrations in organic solvents. A randomly distributed unsymmetrical phenyl substituent on the benzene ring of para-oriented wholly aromatic polyamides dramatically changes the solubility and melting point. The phenyl substituent on a terephthalic acid unit is more efficient in decreasing melting point and increasing solubility in organic solvents of aromatic polyamides than the one on a p-phenylenediamine unit. However, the former also introduces a more flexible link in the extended polyamide chain.     

Synthesis and properties of polyurethanes and polyureas containing 2,5-thiophenylene linkage

A novel diisocyanate monomer, thiophene-2,5-diisocyanate (ThDI) was prepared from readily available adipic acid via the intermediate formation of thiophene-2,5-dicarboxylic acid chloride (ThDAC) and thiophene-2,5-dicarboxylic acid azide (ThDAA) which was subjected to a Curtius rearrangement. Polyurethanes and polyureas containing 2,5-thiophenylene linkage were synthesized by the polycondensation of thiophene-2,5-diisocyanate with various diols and diamines, respectively, in N,N-dimethylformamide. Polymerization conditions were optimized and the high yields of polymers were obtained. The identity of ThDI, model compounds, and the resulting polymers was confirmed by elemental analysis and spectroscopic methods. These polyurethanes and polyureas were found to have inherent viscosities in the range of 0.33–0.68 dL/g. Some physical properties of these polymers were also investigated.     

N-methyl-substituted aromatic polyamides

A series of N-methyl-substituted aromatic polyamides derived from the secondary aromatic diamines 4,4′-bis(methylamino)diphenylmethane, 3,3′-bis(methylamino)diphenylmethane, 4,4′-bis(methylamino)benzophenone or 3,3′-bis(methylamino)benzophenone and isophthaloyl dichloride, and terephthaloyl dichloride or 3,3′-diphenylmethane dicarboxylic acid dichloride was prepared by high-temperature solution polymerization in s-tetrachloroethane. Compared with analogous unsubstituted and partly N-methylated aromatic polyamides, the full N-methylated polyamides exhibited significantly lower glass transition temperatures (T_g), reduced crystallinity, improved thermal stability, and good solubility in chlorinated solvents.     

Synthesis and characterization of N‐benzoylated wholly aromatic polyamides from 4,4′‐oxydianilinobis(benzimidoyl) chloride and aromatic dicarboxylic acids

A novel type of polyamides, N‐benzoylated wholly aromatic polyamides, were synthesized by low‐temperature solution polycondensation of a new aromatic bis(imidoyl) chloride, 4,4′‐oxydianilinobis(benzimidoyl) chloride, with aromatic dicarboxylic acids, 4,4′‐oxydibenzoic acid and isophthalic acid. Compared with the conventional all aromatic polyamides and also N‐phenylated wholly aromatic polyamides, these N‐benzoylated aramides exhibit better solubility in organic solvents, lower glass transition temperatures and thermal stability.     

Synthesis and characterization of aromatic polymers containing pendant silyl groups. II. Aromatic polyamides

In order to improve the solubility of aromatic polyamides without significant loss of thermal stability, synthesis of aromatic polyamides containing pendant silyl groups was carried out by direct polycondensation of silylated aromatic diacids such as 2-trimethylsilylterephthalic acid (TSTA), 2,5-bis (trimethylsilyl) terephthalic acid (BTSTA), 5-trimethylsilylisophthalic acid (TSIA), 5-dimethylphenylsilylisophthalic acid (DMSIA), and 5-triphenylsilylisophthalic acid (TPSIA) with various aromatic diamines. The resulting polyamides had inherent viscosities in the range of 0.18–1.10 dL/g and showed improved solubilities toward aprotic polar solvents such as NMP, DMF, DMSO, etc. The prepared aromatic polyamides exhibited fairly good thermal stabilities, which were almost comparable to those of corresponding nonsubstituted aromatic polyamides. That is, thermogravimetric analysis (TGA) data revealed 10% weight losses at 358–500°C and residual weights at 700°C were 46–67% under nitrogen atmosphere. © 1992 John Wiley & Sons, Inc.     

Synthesis and liquid crystal properties of bipyridine-containing aromatic polyamides

A series of novel aromatic polyamides containing 2,2′-bipyridine moiety were synthesized by polycondensation of 2,2′-bipyridine-5,5′-dicarboxylic acid ( 2 ) with various aromatic diamines in hexamethylphosphoramide (HMPA) containing lithium chloride. The resulting polyamide solutions in 98% sulfuric acid and in HMPA-LiCl exhibited lyotropic liquid crystal phases. The phase transition behaviors were studied by polarizing microscopy and X-ray diffraction. The polyamides also formed metal complexes with cis-dichlorobis(bipyridine)ruthenium dihydrate [cis-Ru(bpy)₂Cl₂ · 2H₂O] which was supported by changes in electronic spectra.     

Synthesis and properties of aromatic polyamides based on 4,4′-(2,7-naphthalenedioxy)dibenzoic acid

4,4′-(2,7-Naphthalenedioxy)dibenzoic acid, a new aromatic dicarboxylic acid monomer, was prepared starting from 2,7-dihydroxynaphthalene and p-fluorobenzonitrile in three steps. Using triphenyl phosphite (TPP) and pyridine as condensing agents, a series of novel aromatic polyamides were synthesized by the direct polycondensation of the diacid monomer and aromatic diamines in N-methyl-2-pyrrolidone (NMP) solution containing dissolved calcium chloride. The resulting polyamides had inherent viscosities ranging from 0.48 to 0.67 dL/g. Most of these polyamides were readily soluble in polar solvents, such as NMP and N,N-dimethylacetamide (DMAc). Transparent, flexible, and tough films were cast from their DMAc solutions. They had tensile strengths of 65–70 MPa, elongations to break of 5–7%, and initial moduli of 1.4–1.6 GPa. Most of these polymers proved to be amorphous, with glass transition temperatures in the range between 143–227°C. Thermogravimetric analysis (TG) showed that all the polyamides were stable up to 450°C in both air and nitrogen atmospheres. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 1469–1478, 1997     

Novel two-step synthesis of polybenzothiazoles via precursor polyamides from 2,5-bis(isopropylthio)-1,4-phenylenediamine and aromatic dicarboxylic acid chlorides

A novel two-step method for the synthesis of polybenzothiazoles has been developed starting from 2,5-bis(isoprophylthio)-1,4-phenylenediamine and aromatic dicarboxylic acid chlorides. The low-temperature solution polycondensation of these monomer pairs in N-methyl-2-pyrrolidone afforded the aromatic polyamides with pendant isopropylthio groups having inherent viscosities in the range of 0.8 and 2.4 dL/g. The soluble precursor polyamides were subjected to thermal cyclization to the corresponding polybenzothiazoles along with the elimination of propylene and water. The resulting polymers were also characterized.     

Preparation of phosphorus-containing polymers. XXV. Polyamide-imides that contain phenoxaphosphine rings

New phenoxaphosphine-containing polyamide-imides were prepared by cyclodehydration of the polyamide-amic acids obtained from 8-chloroformyl-10-phenylphenoxaphosphine-2,3-dicarboxylic anhydride 10-oxide and diamines by a low-temperature solution polycondensation. Polymers with reduced viscosities of 0.10–0.59 dl/g in DMA or concentrated H₂SO₄ at 30°C were obtained in 64–97% yields. All the polyamide-imides were soluble in m-cresol, concentrated H₂SO₄, and dichloroacetic acid and some of them were soluble in DMF, DMA, and DMSO; the polyamide-imides had better solubility in organic solvents than phenoxaphosphine-containing polyimides. The phenoxaphosphine-containing polyamide-imides derived from aromatic diamines exhibited excellent thermal properties and little degradation below about 400°C, whereas the polymers from aliphatic diamines began to lose weight at about 250°C. They appeared to have thermal stability between phenoxaphosphine-containing polyimides and polyamides. These polyamide-imides exhibited self-extinguishing behavior.     

Preparation and properties of polyamides from 2,8-phenoxathiin-bis-(γ-ketobutyric acid), 2,7-thianthrene-bis(γ-ketobutyric acid), and aromatic diamines

Aromatic-aliphatic polyamides containing phenoxathiin and thianthrene heterocyclic units were prepared by the direct polycondensation of 2,8-phenoxathiin-bis(γ-ketobutyric acid) ( I ) or 2,7-thianthrene-bis(γ-ketobutyric acid) (II) with various aromatic diamines in a triphenylphosphite-pyridine system. Prior to polymer synthesis two model diamides were prepared by condensing γ-keto acid I or II with p-toluidine. The model diamides and polyamides were characterized by spectral methods and elemental analysis. The polyamides, obtained in 56–90% yields, had inherent viscosities in the 0.82–1.1 dL/g range in concentrated H₂SO₄ at 30°C. The effect of heterocyclic units on polymer properties, such as solubility, crystallinity, and thermal stability has been discussed.     

Polyamides from perchloro-4,4′-dichloroformylbiphenyl

New thermally stable polyamides were prepared by low-temperature polycondensation in N,N-dimethylacetamide from perchloro-4,4′-dichloroformylbiphenyl and various aromatic and aliphatic diamines. The polymers were characterized by infrared spectroscopy, elemental analysis, TGA, and DSC and found to show higher thermal stability than other nonchlorinated polyamides.     

Preparation and properties of fluorine-containing aromatic polyamides from tetrafluorophthaloyl chlorides and aromatic diamines

New fluorine-containing aromatic polyamides with inherent viscosities of 0.4–1.8 dL/g were prepared by the low temperature solution polycondensation of tetrafluoroisophthaloyl and tetrafluoroterephthaloyl chlorides with N,N′-bis(trimethylsilyl)-substituted aromatic diamines. The aromatic polyperfluoroisophthalamides were amorphous polymers with glass transition temperatures around 280°C, whereas the polyperfluoroterephthalamides were crystalline. Most of these aromatic polyamides were soluble in organic solvents, and began to decompose around 330°C in air or nitrogen atmosphere.     

Aromatic polyisophthalamides with N-benzylidene pendant groups

A new series of modified polyisophthalamides bearing N-benzylidene pendant groups was prepared by reacting various aromatic diamines with 5-(N-benzylidene) isophthalic acid. The latter was synthesized from the reaction of 5-aminoisophthalic acid with benzaldehyde and characterized by IR and ¹H-NMR spectroscopy. Triphenyl phosphite and pyridine was used as condensing agents for preparing polyamides. In addition, the corresponding unsubstituted polyisophthalamides were prepared under identical experimental conditions for comparative purposes. Characterization of modified polyamides was accomplished by IR as well as inherent viscosity measurements. They showed a slightly lower solubility in various media than the corresponding unsubstituted polyamides. The cured modified polyamides displayed significantly higher thermal stability than the cured unsubstituted polyamides. They were stable up to 355–308°C in N₂ or air and afforded anaerobic char yield of 66–61% at 800°C. © 1992 John Wiley & Sons, Inc.     

Synthesis and properties of new poly(ether sulfone)amides

High molecular-weight aromatic polyamides were obtained from 1,5- and 2,6-bis-(4′-carboxy-4-phenylenoxy-sulfonyl)naphthalene by direct polycondensation reaction in N-methyl-2-pyrrolidone with various aromatic diamines, using triphenyl phosphite and pyridine as condensing agents. The polymers were characterized by elemental analysis, thermogravimetric analysis, differential scanning calorimetry, and infrared analysis. The polyamides, obtained in quantitative yield, possessed inherent viscosities in the range 0.42–1.70 dL/g, glass transition temperatures between 245–310°C, and 10% weight loss temperatures in nitrogen and air above 435 and 424°C, respectively. Most of the polymers were soluble in aprotic solvents. The effect of the structure on properties, such as solubility, T_g, and thermal behavior, were also studied. © 1996 John Wiley & Sons, Inc.     

Preparation and properties of aromatic polymides from 2,2′-bibenzoic acid and aromatic diamines

Aromatic polyamides having inherent viscosities up to 1.8 dL/g were synthesized either by the direct polycondensation of 2,2′-bibenzoic acid with various aromatic diamines or by the low temperature solution polycondensation of 2,2′-bibenzoyl chloride with aromatic diamines. All the aromatic polyamides were amorphous and soluble in a variety of organic solvents including N,N-dimethylacetamide (DMAc), N-methyl-2-pyrrolidone, dimethyl sulfoxide, m-cresol, and pyridine. Transparent and flexible films of these polymers could be cast from the DMAc solutions. These aromatic polymides had glass transition temperatures in the range of 226-306deg;C and began to lose weight around 350°C in air.     

Synthesis and characterization of aromatic polyamides from 1,1-bis(4-aminophenyl)-2,2-diphenylethylene and aromatic diacid chlorides

Novel, soluble aromatic polyamides and copolyamides containing tetraphenylethylene units were prepared by the low temperature solution polycondensation of 1,1-bis(4-aminophenyl)-2,2-diphenylethylene and aromatic diamines with various aromatic diacid chlorides. Highmolecular-weight polyamides having inherent viscosities of 0.6–1.5 dL/g and number-average molecular weight above 21000 were obtained quantitatively. These polymers were readily soluble in various solvents such as N-methyl-2-pyrrolidone, N,N-dimethylacetamide (DMAc), and dimethyl sulfoxide and gave pale yellow, transparent, flexible films by casting from DMAc solution. The polymers had glass transition temperatures between 290 and 340°C, and started to lose weight around 400°C, with 10% weight loss being recorded at about 470°C in air.     

Polyamides containing arylene sulfone ether linkages

Polyamides containing arylene sulfone ether linkages were synthesized from 4,4′-[sulfonylbis(p-phenyleneoxy)] dibenzoyl chloride (SPCI), 3,3′-[sulfonylbis(p-phenyleneoxy)] dibenzoyl chloride (SMCl), and arylene sulfone ether diamines (SED), by solution and interfacial polymerization techniques. In solution polymerization, the effect of various acid acceptors such as propylene oxide (PO), lithium chloride (LiCl)/lithium hydroxide (LiOH), and triethylamine (TEA) on molecular weight of the polyamides was studied. The effect of methyl substituted and unsubstituted aromatic sulfone ether diamines on molecular weight and thermal properties of polyamides was also studied. The polyamides prepared were characterized by solution viscosity, elemental analysis, thermal gravimetric analysis, differential scanning calorimetry, and x-ray diffraction. Physical and thermal properties of polyamides prepared from SPCl and SED were compared with the polyamides prepared from SMCl and SED.     

Synthesis and characterization of new soluble polyamides containing phthalimide pendent group

A dicarboxylic acid monomer, 5-phthalimidoisophthalic acid, containing a phthalimide pendent group was prepared by the condensation of 5-aminoisophthalic acid and phthalic anhydride in glacial acetic anhydride. The monomer was reacted with various aromatic diamines to produce polyamides using triphenyl phosphite and pyridine as condensing agents. These polyamides were produced with inherent viscosities of 0.64–1.14 dL · g⁻¹. All the polymers, characterized by wide-angle X-ray diffraction, revealed an amorphous nature resulting from the presence of the bulky pendent group. These polyamides exhibited excellent solubility in a variety of solvents such as N- methyl-2-pyrrolidinone, N,N-dimethylacetamide (DMAc), N,N-dimethylformamide, dimethyl sulfoxide, pyridine, and cyclohexanone. These polyamides showed glass-transition temperatures (T_g's) between 247 and 273 °C (by DSC) and 248 and 337 °C (by a dynamic mechanical analyzer). The thermogravimetric analytic measurement revealed the decomposition temperature at 10% weight-loss temperatures (Td₁₀) ranging from 442 to 530 °C in nitrogen. The polyamides containing phthalimide groups exhibited higher T_g and Td₁₀ values than those having no phthalimide groups. Transparent, tough, and flexible films of these polyamides could be cast from the DMAc solutions. These casting films had tensile strengths ranging from 81 to 126 MPa, elongations at break ranging from 7 to 13%, and tensile moduli ranging from 2.0 to 2.9 GPa. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 1557–1563, 2001