外延AgCl/AgBr乳剂感光性能的研究

制备系列AgCl/AgBr八面体外延乳剂,利用EDS-STEM技术对主体乳剂AgBr八面体上氯的分布进行了测定,结果表明随AgCl/AgBr外延乳剂中AgCl含量的增大,而其分布优势始终在AgBr八面体的顶角位置,其次在边。77K时,用375nm的激发光源对外延乳剂AgCl/AgBr样品进行激发,随外延乳剂中AgCl含量的提高,AgCl的发光谱带有增大的趋势,但其峰位置基本保持在510nm左右,AgBr在600nm.AgCl和AgBr的发光峰始终以分立的形式存在,没有混晶AgBrCl的宽谱带出现,外延乳剂AgCl/AgBr的感光度随AgCl含量的提高也有一定的变化规律,当AgCl含量较低时,有明显增感作用,而当AgCl含量过高时,外延乳剂的感光度降低,但灰雾也减小。     

片状卤化银晶体的制备、结构与性能的研究——Ⅱ.pAg对片状颗粒的尺寸、纵横比、碘离子分布及离子电导率的影响

本文研究了双注法制备片状卤化银微晶时,pAg值对所形成的卤化银片状颗粒的尺寸、纵横此、碘离子分布以及离子电导率的影响。随着pAg值的升高,片状颗粒的尺寸和纵横比都相应地增大和升高,且越来越多的碘离子从颗粒中心向外层迁移,直至到达表层,这说明存在晶体的重结晶过程。表面层的溴碘原子比是用X射线光电子能谱仪(XPS)测定的,并测量了不同pAg值下制备的不同尺寸的片状卤化银乳剂的介电损耗频谱。其结果表明,片状颗粒的尺寸影响其离子电导率,表层碘含量的影响不明显。     

片状多层结构卤化银外延乳剂的光物理性质及感光性能的研究

本文利用可控双注仪设计并制备了三种系列共二十种片状多层结构溴碘化银乳剂及其外延体。用X射线能谱仪(EDS)和电镜验证所设计的碘离子多层分布和氯化银外延体的位置,研究了它们的光物理性质和感光性能,发现外延AgCl对主体微晶性质的影响随层次结构和外延位置不同有很大的变化。若主体微晶结构合理,光电子利用效率已经较高,电子与空穴分离好,外延后其乳剂的感光度提高幅度反而不大。相反,若主体微晶的结构不合理,则外延可能导致两种结果:或增加潜影形成效率,提高感光度;或造成潜影分散,降低感光度。     

单分散铁氧体纳米颗粒的生长机制与成分偏聚的透射电子显微研究

理解纳米晶的生长机制对单分散纳米晶的可控合成至关重要。本文以热分解法制备的双金属铁氧体(钴铁氧和锰铁氧)纳米颗粒为例,利用透射电子显微镜(TEM)系统研究了铁氧体纳米晶的生长机制,揭示了由此造成的成分偏聚现象。对不同时间阶段的反应产物的分析结果表明,两步加热法(即先后在相对低的温度和相对高的温度下加热反应)是制备高质量的单分散铁氧体纳米晶的关键;通过控制低温反应阶段的时间可实现纳米晶的形核阶段和生长阶段的有效分离,从而有利于单分散纳米晶的合成。利用扫描透射电子显微镜(STEM)及电子能量损失谱(EELS)谱学成像技术分析,我们进一步发现了双金属铁氧体纳米晶中的成分偏聚现象,表明双金属铁氧体纳米晶在形核阶段主要形成富Fe的核芯,而在生长阶段则形成更富Co/Mn的双金属铁氧体壳层。这些结果对制备高质量的单分散铁氧体纳米晶具有重要的指导意义,同时也有助于正确理解热分解法制备的铁氧体纳米晶的表面成分和相关表面物理化学性质。     

单分散聚苯乙烯胶体颗粒的界面电性质研究

以过硫酸钾(KPS)为引发剂,以水为反应介质,采用无皂乳液聚合工艺,制备出粒径在500nm左右单分散(分散系数<5%)聚苯乙烯微球。所制备的聚苯乙烯微球为光滑的球形颗粒。研究发现:由无皂乳液聚合法制备的胶体颗粒其ζ电势在不同的离子强度下随pH的变化曲线均出现平台pH6～10.5,说明在一定的离子强度和pH条件下,聚苯乙烯胶乳的ζ电势具有良好的稳定性。聚苯乙烯胶乳有望作为具有一定电势值的标准颗粒。     

银纳米线的制备及电催化还原氧性能研究

分别以聚乙烯基吡咯烷酮(PVP),乙二醇作为软模板和还原剂,采用不同晶种(AgCl、Ag)快速合成了银纳米线.通过SEM和TEM表征,证明合成银纳米线材料形貌均一,颗粒含量很少.并且发现以AgCl为晶种合成的银纳米线长径比为200左右(SNWH),而以Ag为晶种合成的长径比为30左右(SNWL).以银纳米线作为电催化氧...     

两种基于硫醇配体的银(Ⅰ)配合物的合成、表征和晶体结构（英文）

通过AgCl、PPh_3和MBT以1∶2∶1的物质的量之比反应得到2种不同的配合物[AgCl(PPh_3)_2(BTZT)]·CH_3OH(1)和[AgCl(PPh_3)_2(BTZT)]_2(2)(PPh3=三苯基膦;MBT=2-巯基苯并噻唑;BTZT=苯并噻唑-2-硫酮)(其中2已报道)。配合物[AgBr(PPh_3)_2(BTZT)]·CH_3OH(3)和[AgBr(PPh_3)_2(BTZT)]_2(4)改用AgBr以相似的反应获得(其中4已报道)。通过红外光谱、元素分析、核磁共振氢谱、X射线单晶衍射、荧光光谱对配合物1和3进行了分析和表征。我们发现在不同的化学环境中,MBT配体可以转化为BTZT配体,原因是其具有化学活性基团。荧光光谱表明1和3的发射峰均源于配体中的π-π*跃迁。     

掺杂正八面体AgBr乳剂介电频谱的研究——Cd2+、Br-离子的影响

测定了单分散正八面体AgBr乳剂中加入不同量CdBr₂和KBr以后的介电吸收频谱。发现Cd²⁺离子的表面掺杂使正八面体AgBr乳剂的介电吸收峰向低频方向位移。这种变化在CdBr₂的加入量为0—2×10^-2mol/mol AgBr范围内尤为明显。说明掺杂Cd²⁺使正八面体AgBr乳剂中AgBr微晶的介电电导率σ₂显著下降。能进入AgBr微晶表面层晶格中的Cd²⁺离子的数量不仅与乳剂中Cd²⁺离子的浓度有关,而且与乳剂中的Br^-离子浓度有关。通过简单的水洗,可以将掺杂的Cd²⁺大部分除去。水洗后,样品的介电吸收峰又向高频方向回移。在本实验条件下,Cd²⁺离子掺杂的这种“可逆性”表明进入AgBr微晶中的Cd²⁺离子主要是处在AgBr微晶的表面层内。样品介电吸收峰频率位置的这种可逆变化表明:非均匀电介质中的界面极化效应在保持连续相不变时,受分散相颗粒表面层物质的组成和结构的影响很大。     

某些稳定剂对卤化银乳剂微晶体的离子电导率的影响

利用Maxwell-Wagner效应,采用介电损耗测定法,在10kHz—3MHz的频率范围内,研究了苯亚磺酸钠(sodium benzosulfinate,简称BSI),1-苯基-5-巯基四氮唑(1-phenyl-5-mercaptotrazole,简称PMT)和5-甲基-7-羟基-1,3,4-三氮吲(口乃木)利嗪(5-methyl-7-hydroxyl-1,3,4-triazaindolizine,简称TAI)对卤化银乳剂微晶体的离子电导率的影响。加入BSI(4.76—19.07g/M AgBr)并不引起离子电导率的降低,而加入PMT和TAI(只是0.93g/M AgBr)却使离子电导率降低2个对数单位,升高了卤化银乳剂微晶体的离子电导活化能△E和表面电位eφ_s(约升高0.12eV)。进一步的研究表明:在乳剂微晶体中所含的碘,对于TAI吸附在微晶体上所引起的离子电导率的降低具有很强的抑制作用。文中对稳定剂对于离子电导性质影响的根据进行了讨论。     

内灰化八面体核壳乳剂的制备方法对微晶结构与性能的影响

应用双注仪制备了碘含量1.5%的AgBrI乳剂,在一定温度,pAg和pH下将乳剂成熟到一定程度(D₀>5.0).用此乳剂做为核,采用二次乳化法包壳。本文主要研究了包壳时pH值,壳的组成,厚度对乳剂颗粒大小、形状、显影密度及离子电导的影响。结果表明:(1)当壳的组成为AgBrI时,随氯含量增加(分别为0、2.5、5、10%mol),核壳乳剂表显密度变化不大而内显密度上升;(2)包壳时随pH由低到高(pH为2、4、6、8),乳剂颗粒由小变大。颗粒形状由规整八面体变得棱角模糊,均匀度下降,表显密度由小变大,而内显密度由大变小;(3)在相同pH下包壳,随壳厚度的增加(壳与核卤化银的摩尔数比为:1:0.5,1:1,1:2,1:3)表显密度急剧下降,内显密度变化不大;(4)随包壳时pH增加,卤化银微晶的离子电导增大.     

Composite Silver Bromide Based T-Crystals of Epitaxial Type

The process was studied in which heterocontact microcrystals based on silver bromide are obtained in bulk crystallization. The influence exerted by parameters of the crystallization process on the epitaxial growth was revealed. The conditions were determined for obtaining the AgBr/AgCl and AgBr/AgSCN epitaxial systems with the use of substrate-type tabular AgBr microcrystals (T-crystals of AgBr).     

Mechanism of halide conversion process of colloidal AgCl microcrystals by Br ions : I. Observation of the dynamic changes in shape, structure, and composition

The mechanism of the halide conversion process in suspension of AgCl microcrystals by bromide ions was studied by electron microscopy, X-ray diffractometry, and electron-beam diffractometry. The typical conversion process after the introduction of Br⁻ was found to consist of more than three distinctive steps. The first step was an almost instantaneous reaction within a few seconds for a surface conversion without apparent morphological change of the original particles. The second step was a very rapid epitaxial growth process of virtually pure AgBr crystals on every corner and partly on the edges of the AgCl cubic microcrystals with dissolution of their own {100} faces, which was finished in about 1 min at 25°C. The third step was a much slower process of about 2 h at 25°C (ca. 5 min at 45°C) for the formation of an AgCl_0.5Br_0.5 solid solution developing from the joints of AgBr guest and AgCl host by simultaneous dissolution of the guests and the hosts. After the complete dissolution of the AgBr guests, a further recrystallization process that formed a solid solution richer in chloride content followed. Finally, the conversion virtually stopped midway to yield double-structured particles of Ag(Cl, Br) shell/AgCl core. However, when the initial molar ratio of [Br⁻]₀/[AgCl]₀ was so high as to exceed unity, the original AgCl particles were totally decomposed into about eightfold AgBr particles in number. In this case the steps later than the second one were missing. Also, it was suggested from the subsidiary study on open systems, where bromide ions were added continuously, that the kinetics was basically controlled by the deposition rate of the solute of the AgBr component of the growing parts, though it was switched to being limited by the dissolution rate of the host AgCl crystals when their open surface area for dissolution was extremely diminished.     

Synthesis of cubic Ag@AgCl and Ag@AgBr plasmonic photocatalysts and comparison of their photocatalytic activity for degradation of methyl orange and 2,4-dichlorophenol

Uniform cubic Ag@AgCl and Ag@AgBr plasmonic photocatalysts with side length of 0.7 µm were synthesized by a facile green route, in which a controllable double-jet precipitation technique was employed to fabricate homogeneous cubic AgCl and AgBr grains while a photoreduction process was used to produce Ag nanoparticles (NPs) on the surface of AgCl and AgBr grains. The synthesized samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) analysis, X-ray photoelectron spectroscopy (XPS), and ultraviolet–visible (UV–Vis) diffuse reflectance spectroscopy (DRS). The photocatalytic activities of Ag@AgCl and Ag@AgBr were compared using degradation of methyl orange (MO) dye and 2,4-dichlorophenol (2,4-DCP) under visible-light irradiation. Ag@AgBr showed higher photocatalytic activity for MO degradation but weaker activity for 2,4-DCP decomposition. Possible degradation mechanisms are proposed to interpret these contrary paradoxical experimental results.     

卤化银乳剂微晶体的结构与性能研究 Ⅴ.八面体核壳复合结构乳剂的电性质与感光性能

本工作应用双注法制备了一系列不同碘含量的八面体核壳孔剂。测定了它们的光吸收,离子电导(介电损耗法)、光电导(微波光导法)和感光性能。结果表明:乳剂微晶体的光吸收和离子电导随着碘含量的增加而显著上升,光电导也随着碘含量的增加而增大,其光电子表减过程遵循二级反应动力学过程,光电子半衰期在碘含量为5mol%时为最大。在相同的化学敏化条件下,乳剂的感光度随碘含量增加而上升(碘含量0-12.5mol%)。     

冠醚化合物对乳剂晶体外延生长的调变作用

本工作研究了冠醚化合物在外延乳剂生长过程中的调变作用。结果表明,1,4,7,10,13,16-六氧杂环十八烷对AgBr八面体乳剂无侵蚀作用,对非同晶系晶体之间的外延不起调变作用。1,7,10,16-四氟-4,13-二氮代杂环十八烷均使AgBr八面体乳剂的棱角产生了不同程度的侵蚀,可充当不同晶系晶体外延生长的调变剂,对晶体的溶解侵蚀能力依2S-18-C-6,2N-18-C-6,18-C-6的次序降低。这与它们同Ag⁺络合能力的强弱一致。2S-18-C-6,2N-18-C-6仅对非同晶系晶体之间的外延起调度作用,而对同晶系晶体的外延不起调查作用。冠醚化合物对晶体外延生长的调变作用与冠醚化合物对晶体的络合溶解作用有关。     

硫氰酸钾在外延卤化银乳剂制备中的作用

外延卤化银乳剂一般都是在有机调变剂作用下制备出来的,而有机调变剂会给乳剂体系带来一些不利因素。本文中用无机酸盐KSCN作外延乳剂调变剂制备出了一系列外延乳剂,并利用电子透射显微技术研究了硫氰酸钾对主体乳剂颗粒的浸蚀作用和浸蚀部位,指出了浸蚀部位和外延生长位置间的关系,对八面体及薄片颗粒外延乳剂的形貌和晶态进行了研究和描述,对不同外延成份的薄片颗粒外延乳剂的形貌也进行了描述,证明了无机酸盐KSCN可以用作外延调变剂。     

AgBrⅠ核壳乳剂的还原敏化与硫加金敏化的协同增感效应

使用微机控制的双注仪和二次乳化方法制备了一系列在AgBrⅠ核内进行不同程度还原增感的溴碘化银/溴化银核壳乳剂.对这些乳剂感光性能的研究表明:1)颗粒内部经还原敏化或Ag₂掺杂的乳剂表现出明显的增感效应,颗粒内碘离子的存在并不影响Ag₂的增感作用;2)在对乳剂进行了颗粒表面的硫加金增感以后,在一定的DMAB用量下,观察到显著的颗粒内部还原增感和表面硫加金增感的协同增感效应,使乳剂的感光度有了成倍的增长.以上协同增感效应的结果再次说明,颗粒内部的还原敏化中心与颗粒表面的硫加金敏化中心具有两种不同的增感机理,前者捕获空穴,后者捕获电子,两者都有利于提高潜影的形成效率.