白宝石衬底上生长的MgxZn1-xO晶体薄膜的结构和光学性能

在白宝石 (sapphire)衬底上低温外延生长出了MgxZn1 -xO晶体薄膜 .x射线衍射 (XRD)及能量色散x射线 (EDX)分析表明 ,MgxZn1 -xO薄膜的晶体结构依赖于薄膜中Mg的组分x,随着Mg组分的增大 ,MgxZn1 -xO薄膜的结构从与ZnO晶体一致的六方结构转变为与MgO晶体一致的立方结构 .对MgxZn1 -xO薄膜的紫外透射光谱及紫外光致荧光谱 (UVPL)的分析表明 ,随着Mg组分的增大 ,光学吸收边产生明显的蓝移 ,表明MgxZn1 -xO晶体薄膜的带隙增大 ,且带隙连续可调 .吸收光谱和XRD测量显示 ,带隙高达 5 6 5eV的MgxZn1 -xO晶体薄膜与MgO之间的晶格失配仅为0 16 % .     

退火温度对低温生长MgxZn1-xO薄膜光学性质的影响

用射频磁控溅射法在80℃衬底温度下制备出MgxZn1-xO(x=0.16)薄膜,用X射线衍射(XRD)、光致发光(PL)和透射谱研究了退火温度对MgxZn1-xO薄膜结构和光学性质的影响.测量结果显示,MgxZn1-xO薄膜为单相六角纤锌矿结构,并且具有沿c轴的择优取向;随着退火温度的升高,(002)XRD峰强度、平均晶粒尺寸和紫外PL峰强度增大,(002)XRD峰半高宽(FWHM)减小.结果证明,用射频磁控溅射法通过适当控制退火温度可得到高质量MgxZn1-xO薄膜.     

射频磁控溅射法生长MgxZn1-xO薄膜的结构和光学特性

用射频磁控溅射法在80℃的衬底温度下制备出MgxZn1-xO(0≤x≤0.30)薄膜.x射线衍射(XRD)结果表明,MgxZn1-xO薄膜为单相六角纤锌矿结构,没有形成任何显著的MgO分离相,MgxZn1-xO薄膜的择优取向平行于与衬底垂直的c轴;c轴晶格常数随着Mg含量的增加逐渐减小.在MgxZn1-xO薄膜的光透射谱中出现锐利的吸收边,由透射谱估算出MgxZn1-xO薄膜的带隙宽度由3.32eV(x=0)线性地增加到3.96eV(x=0.30).     

MgxZn1-xO/Au/MgxZn1-xO夹层透明导电薄膜的制备及光电性质研究

采用操作简单的溶胶-凝胶法和射频磁控溅射法在石英衬底上分别制备了MgxZn1-xO薄膜和MgxZn1-xO/Au/MgxZn1-xO夹层结构的透明导电薄膜并对样品进行退火处理。利用紫外-可见分光光度计、X射线衍射仪、光致发光、霍尔效应测试对在不同退火温度下薄膜的晶体结构、光学和电学性质进行表征分析,并研究退火温度对其影响。测试结果表明:所制备的薄膜样品均具有良好的c轴(c-axis)取向并呈现出六角纤锌矿结构。Mg组分的增加使得ZnO基薄膜的光学带隙逐渐增大,PL发光谱和吸收光谱的谱线出现了明显的蓝移现象,但薄膜的电学特性有所降低。而在MgxZn1-xO/Au/MgxZn1-xO夹层结构的薄膜样品中,Au夹层的存在使薄膜的光学性质变差,在紫外区域透光率约为60%。但薄膜的电学性质得到明显改善,相比MgxZn1-xO薄膜,其电阻率和迁移率显著提高。此外通过高温退火处理可以有效提高所制备薄膜的晶体质量,进一步提高样品电学特性,其中经过500℃退火后的薄膜迁移率达到了40.9cm2·Vs-1,电阻率为0.005 7Ω·cm。但随着退火温度的进一步升高,薄膜晶体尺寸从25.1nm增大到32.4nm,从而降低了该薄膜的迁移率。因此该夹层结构的MgxZn1-xO/Au/MgxZn1-xO薄膜对于促进ZnO基透明导电薄膜在深紫外光学器件中的应用有重要作用。     

利用P-MBE制备高质量MgxZn1-xO的结构和光学特性

利用等离子体辅助分子束外延(P-MBE)的方法,在c平面的蓝宝石衬底上制备了高质量的MgxZn1-xO合金薄膜。通过改变Mg源的温度,得到了不同Mg组份的MgxZn1-xO合金薄膜;通过引入ZnO的低温缓冲层,有效地提高了MgxZn1-xO合金薄膜的结晶质量。随着Mg组份的增加,MgxZn1-xO的X射线衍射的(002)衍射峰逐渐向大角度方向移动。对样品进行光致发光(PL)谱的测量,在室温下观察到了较强的紫外发光。随Mg浓度的增加,紫外发光峰向高能侧移动,并且发光峰逐渐展宽。通过对x=0.15的样品进行变温光谱的测量研究了紫外发光峰起因,得到了MgxZn1-xO的发光是来自于自由激子的发光。自由激子束缚能为54meV。     

MgxZn1-xO单晶薄膜的结构和光学性质

用等离子辅助分子束外延(P-MBE)的方法,在蓝宝石c平面上外延生长了MgxZn1-xO合金薄膜。在0≤x≤0．2范围内薄膜保持着ZnO的纤锌矿结构不变。X射线双晶衍射谱的结果表明生长的样品是单晶薄膜。据布喇格衍射公式计算得到,随着Mg含量的增加,薄膜的品格常数C由0．5205nm减小到0．5185nm。室温光致发光谱出现很强的紫外近带发射(NBE)峰,没有观察到深能级(DL)发射,且随着Mg的掺入量的增加,紫外发射峰有明显的蓝移。透射光谱的结果表明,合金薄膜的吸收边随着Mg离子的掺入逐渐向高能侧移动,这与室温下光致发光的结果是相吻合的,并计算出随着x值增加,带隙宽度从3．338eV逐渐展宽到3．682eV。通过研究Mg0.12Zn0.88O样品的变温光谱,将紫外发射归结为束缚在施主能级上的束缚激子发射。并详细地研究了在整个温度变化过程中,束缚激子的两个不同的猝灭过程以及谱线的半峰全宽与温度变化的关系。     

Au/SiO2纳米复合型材料的光吸收性质

在室温下用离子束溅射沉积工艺在石英基材上生成Au-SiO2复合薄膜。把生成薄膜从500~900℃(分别保温5 min)分五个不同温度进行退火处理。用X光衍射方法(XRD)对薄膜结构进行了测试,得到Au-SiO2纳米复合薄膜未退火(as-dep)和退火后的X射线衍射谱;透射电子显微镜(TEM)观察了经过700℃退火处理复合薄膜中Au粒子在薄膜中分布状态和颗粒大小。用分光计测试薄膜光吸收特性,吸收光谱范围为190~1000 nm,发现退火温度从500~700℃,光谱吸收峰有明显红移存在,而在更高温度吸收峰的位置和强度几乎都不变。这与X射线衍射检测吻合。并用德鲁特(Drude)模型给于理论解释。     

射频磁控共溅射GaAs/SiO2纳米颗粒镶嵌薄膜的光学性质

应用射频磁控共溅射方法和真空退火方法制备了GaAsSiO2纳米颗粒镶嵌薄膜.X射线衍射实验结果表明,经高温退火的薄膜中形成了面心立方闪锌矿结构的GaAs纳米晶粒,晶粒平均直径为1.5—3.2nm.吸收光谱展示了由于强量子限域引起的1.5—2eV的吸收边蓝移.室温光致荧光(PL)光谱显示了电子重空穴激子与电子劈裂空穴激子的近紫外和紫外双PL谱峰以及深俘获态的PL谱峰.对实验吸收边蓝移量与有效质量模型的蓝移量的悬殊差别、俘获态PL谱的形成以及PL谱线的特征作了解释.应用激光Z扫描技术测量了退火温度为500℃的复合膜在非共振条件下的光学非线性,结果表明,复合膜的非线性折射率系数和非线性吸收系数都比块材GaAs相应的系数增大了5个数量级.光学非线性系数增大主要起因于强量子限域效应 关键词： 射频磁控共溅射 GaAsSiO2纳米颗粒镶嵌薄膜 光谱 激光Z扫描     

石英玻璃衬底上纤锌矿Mg0.25Zn0.75O薄膜的结构及光学性能

MgxZn1-xO材料是一种新型光电功能材料.采用溶胶凝胶法在石英玻璃上制备了Mg0.25Zn0.75O薄膜,理论结合实验研究了Mg0.25Zn0.75O薄膜的结构和光学性能.研究表明,石英玻璃衬底上Mg0.25Zn0.75O薄膜呈六方纤锌矿结构,薄膜均匀,平均粒径约为20 nm.吸收光谱表明吸收带边始于360 nm,相应的禁带宽度为3.83 eV.发光光谱包含三个发射峰,分别位于384.9 nm(3.23 eV),444.8 nm(2.79 eV)和533.6 nm(2.32 eV),激发光谱峰位于378 nm.由于Mg离子的间隙缺陷导致Mg0.25Zn0.75O薄膜晶格增大,禁带宽度变宽,紫外、蓝光和绿光发射分别红移59,14和12.6 nm.     

MgxZn1-xO薄膜的光致发光性能研究

用溶胶-凝胶旋涂的方法在Si(100)衬底上成功制备了MgxZn1-xO薄膜.通过对样品的X射线衍射花样进行分析,发现制得的样品都有明显的C轴取向.掺入Mg后C轴参数逐渐变小,这表明Mg离子进入了ZnO晶格.随着镁的掺入,其光致发光谱中的紫外发射峰的峰位发生明显蓝移,从3.28eV线性地变化到3.45eV.值得注意的是,掺入镁离子后,薄膜的紫外发光和可见发光的强度都显著高于ZnO.     

Guided-Wave Two-Dimensional Acousto-Optic Scanner Using Proton-Exchanged Lithium Niobate Waveguide

Two-dimensional scanning of a 0.6328 mum guided-light beam has been realized using noncolinear acousto-optic (AO) coplanar Bragg diffraction together with colinear AO guided-mode to substrate radiation-mode conversion in a Z-cut Xpropagation LiNbO3 proton-exchanged (PE) waveguide. The two surface acoustic (SAW) waves utilized are at the center frequencies of 500 and 200 MHz, propagating in the Y and X axes, respectively. Two-dimensional scanning of approximately 720 resolvable light beam spots, namely, 18 40 (horizontal vertical) scanning, has been demonstrated using a light beam of 1.0 mm aperture. The total number of resolvable beam spots can be greatly increased from 720 by simply utilizing SAW transducers of larger bandwidth and a light beam of greater aperture. It should also be possible to significantly increase the diffraction efficiency from 3 % by optimizing the parameters of the PE waveguide and the SAWs.     

Effect ofγ-radiation on the spectral luminescence characteristics of impure cadmium tungstate crystals

Results of a study of the effect of γ-radiation on the spectral luminescence properties of cadmium tungstate crystals doped with silver, bismuth, and molybdenum cations are presented. Spectral characteristics of the nondnnnoped crystals are briefly described. Absorption and photo and X-ray luminescence spectra of the crystals taken before and after exposure to γ-radiation (5.5·10⁴ Gy) are compared. It is found that the spectral characteristics of the crystals doped with silver, bismuth, and molybdenum cations do not change markedly after the exposure. The relation between the type of impurity-induced defects, individual characteristics of the impurity cations, and the character of the effect of γ-radiation on the spectral luminescence properties of impure crystals is analyzed (preliminarily). Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 64, No. 1, pp. 55–60, January–February, 1997.     

Femtosecond Transform-Limited Pulse Generation by Compensating for the Linear Chirp of SPM Spectra in Dispersion Shifted Fibers

A simple technique of pulse compression, based on the linear chirp compensation of self-phase modulation (SPM) spectra in dispersion shifted fibers, is demonstrated. The optimization procedure is carried out, for a short span of a single-mode fiber, using a parabolic law, which describes the behavior of the squared output pulse width versus the pump peak power in the case of Gaussian pulses. The experimental results give a minimum pulse duration of 233 fs, which is in good agreement with the model. Shorter and coherent pulses, down to 90 fs, have been obtained by inserting an interference filter at the optical output.     

Sorting of bending magnets for the SSRF booster

The Shanghai Synchrotron Radiation Facility(SSRF)booster ring,a full energy injector for the storage ring,is deigned to accelerate the electron beam energy from 150MeV to 3.5GeV that demands high extraction efficiency at the extraction energy with low beam loss rate when electrons are ramping.Closed orbit distortion(COD)caused by bending magnet field uniformity errors which affects the machine performance harmfully could be effectively reduced by bending magnet location sorting.Considering the affections of random errors in measurement,both ideal sorting and realistic sorting are studied based on measured bending magnet field uniformity errors and one reasonable combination of bending magnets which can reduce the horizontal COD by a factor of 5is given as the final installation sequence of the booster bending magnets in this paper.     

Measurement of nonlinear coefficient of optical fiber based on small chirped soliton transmission

We measure the waveform and phase curves of short optical pulses before and after transmission over different lengths of fibers by use of the pulse analyzer with the frequency-resolved optical gating (FROG),and numerically simulate pulse evolution under the experimental conditions.The nonlinear coefficient of the fiber is given by comparing the experimental results with the numerical ones.Difference between the experiment and numerical simulation is analyzed.     

Resonance scattering of canonical elastic shells in absorbing fluid medium

Resonance scattering of elastic spherical shell and cylindrical shell while the surrounding fluid medium has absorption is studied. The normal mode solution derived using exact elastic theory and the separation of variables is still applicable. However, the scattering form function has to be modified for the absorbing medium, otherwise the unreasonable result would be obtained. The backscattering form function in the absorbing medium is redefined, and the form function of elastic spherical and cylindrical shell with vacuum or solid matter filled is calculated in various absorption conditions. The results show that the absorption of surrounding fluid leads to notable attenuation of the coincidence resonances in the mid-frequency, but it has a little influence on the low-frequency resonance scattering induced by the filler inside the shell.     

Single-beam self-referenced phase-sensitive surface plasmon resonance sensor with high detection resolution

A versatile and low-cost single-beam self-referenced phase-sensitive surface plasmon resonance(SPR)sensing system with ultra-high resolution performance is presented.The system exhibits a root-mean-square phase fluctuation of ±0.0028.over a period of 45 min.i.e.a resolution of±5.2×10-9 refractive index units.The enhanced performance has been achieved through the incorporation of three design elements:a true single-beam configuration enabling complete self-referencing so that only the phase change associated with SPR gets detected,a differential measurement scheme to eliminate spurious signals not related to the sensor response,and the elimination of retardation drifts by incorporating temperature stabilization in the liquid crystal phase modulato .Our design should bring the detection sensitivity of non-labeling SPR biosensing closer to that achievable by conventional fluorescence-based techniques.     

Influences of SiO2 protective layers and annealing on the laser-induced damage threshold of Ta2O5 films

Ta2O5 films are prepared on BK7 substrates with conventional electron beam evaporation deposition.The effects of SiO2 protective layers and annealing on the laser-induced damage threshold (LIDT) of the films are investigated.The results show that SiO2 protective layers exert little influence on the electric field intensity(EFI)distribution,microstructure and microdefect density but increase the absorption slightly.Annealing iS effective on decreasing the microdefect density and the absorption of the films.Both SiO2 protective layers and annealing are beneficial to the damage resistance of the films and the latter is more effective to improve the LIDT.Moreover,the maximal LIDT of Ta2O5 films is achieved by the combination of SiO2 protective layers and annealing.     

A stereo matching algorithm using multi-peak candidate matches and geometric constraints

Gray cross correlation matching technique is adopted to extract candidate matches with gray cross correla- tion coefficients less than some certain range of maximal correlation coefficient called multi-peak candidate matches. Multi-peak candidates are extracted corresponding to three closest feature points at first. The corresponding multi-peak candidate matches are used to construct the model polygon. Correspondence is determined based on the local geometric relations between the three feature points and the multi-peak candidates. The disparity test and the global consistency checkout are applied to eliminate the remaining ambiguous matches that are not removed by the local geometric relational test. Experimental results show that the proposed algorithm is feasible and accurate.