Heteroepitaxy of CdTe on tilting Si(2 1 1) substrates by molecular beam epitaxy

CdTe(2 1 1)B epilayers were grown on 3 in Si(2 1 1) substrates which misoriented 0–10° toward [1 1 1] by molecular beam epitaxy (MBE). The relationship of X-ray double-crystal rocking curve (XRDCRC) FWHM and deflection angle from CdTe(2 1 1) to Si(2 1 1) was studied. For 4.2–4.5 μm CdTe, the best value of FWHM 83 arcsec was achieved while deflection angle is 2.76°. A FWHM wafer mapping indicated a good crystalline uniformity of 7.4 μm CdTe on tilting Si(2 1 1), with FWHM range of 60–72 arcsec. The shear strains of these epilayers were analyzed, using reciprocal lattice points of symmetric and asymmetric reflections measured by high-resolution multi-crystal multi-reflection X-ray diffractometer (HRMCMRXD). It was found that the shear strain angle of epilayer is effectively reduced by using proper tilting Si(2 1 1) substrate. It was also proved that the lattice parameter of CdTe(2 1 1)B is affected by the shear strain and thermal strain.     

A simple method to synthesize single-crystalline β-wollastonite nanowires

The single-crystalline β-wollastonite (β-CaSiO₃) nanowires were prepared via a simple hydrothermal method, in the absence of any template or surfactant using cheap and simple inorganic salts as raw materials. Xonotlite [Ca₆(Si₆O₁₇)(OH)₂] nanowires were first obtained after hydrothermal treatment at a lower temperature of 200 °C for 24 h, and after being calcinated at 800 °C for 2 h, xonotlite nanowires completely transformed into β-wollastonite nanowires and the wire-like structure was preserved. The synthesized β-wollastonite nanowires had a diameter of 10–30 nm, and a length up to tens of micrometers, and the single-crystalline monoclinic parawollastonite structured β-wollastonite was identified by XRD with the space group of P2₁/a and cell constants of a=15.42 Å, b=7.325 Å, c=7.069 Å and β=95.38°. A possible growth mechanism of β-wollastonite nanowires was also proposed. The advantages of this method for the nanowire synthesis lie in the high yield, low temperature and mild reaction conditions, which will allow large-scale production at low cost.     

Physical properties of Ag-doped cadmium telluride thin films fabricated by closed-space sublimation technique

Cadmium telluride (CdTe) thin films were prepared by the closed-space sublimation (CSS) technique, using CdTe powder as evaporant onto substrates of water-white glass. In the next step, the annealed films at 450 °C for 30 min were dipped in AgNO₃–H₂O solution at room temperature. These films were again annealed at 450 °C for 1 h to obtain silver-doped samples. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), electrically i.e. DC electrical resistivity as well as photo resistivity by van der Pauw method at room temperature, dark conductivity, activation energy analysis as a function of temperature by two-probe method under vacuum, and spectrophotometry. The electron microprobe analyzer (EMPA) results showed an increase of Ag content composition in the samples by increasing the immersion time of films in solution. The Hall measurements indicated the increase in mobility and carrier concentrations of CdTe films by doping of Ag. A significant change in the shape and size of the CdTe grains were observed.     

Growth of NaBi(WO4)2 crystal by modified-Bridgman method

NaBi(WO₄)₂ (NBW) crystals have been grown for the first time by modified-Bridgman method. Influences of some factors on the crystal growth process are discussed. X-ray powder diffraction experiments show that the unit cell parameters of NBW crystal are a=b=0.5284 nm, c=1.1517 nm, and V=0.3215 nm³. The differential thermal analysis shows that the NBW crystal melts at 923°C.     

Synthesis and characterization of type-II textured tungsten disulfide thin films by vdWR process with Pb interfacial layer as texture promoter

The growth of type-II textured tungsten disulfide (WS₂) thin films by solid state reaction between the spray deposited WO₃ and gaseous sulfur vapors with Pb interfacial layer has been studied. X-ray diffraction (XRD) technique is used to measure the degree of preferred orientation ‘S’ and texture of WS₂ films. Scanning electron microscopy (SEM) and transmission electron microscopy techniques have been used to examine the microstructure and morphology. The electronic structure and chemical composition were studied using X-ray photoelectron spectroscopy (XPS). The use of Pb interfacial layer for the promotion of type-II texture in WS₂ thin films is successfully demonstrated. The presence of (0 0 3 l), (where l=1, 2, 3, …) family of planes in the XRD pattern indicates the strong type-II texture of WS₂ thin films. The crystallites exhibit rhombohedral (3R) structure. The large value of ‘S’ (1086) prompts the high degree of preferred orientation as well. The stratum of crystallites with their basal plane parallel to the substrate surface is seen in the SEM image. The EDS and XPS analyses confirm the tungsten to sulfur atomic ratio as 1:1.75. We purport that Pb interfacial layer enhances type-II texture of WS₂ thin films greatly.     

Synthesis, thermal and magnetic properties of new metal iodate: (LiFe1/3)(IO3)2

This paper reports the detail synthesis of a new kind of metal iodate, anhydrous (LiFe_1/3)(IO₃)₂, from aqueous solutions. The synthesized compound shows spinal morphology and is chemical stable up to 400°C. The iodate shows paramagnetic behavior from room temperature down to 4.2 K. At room temperature, the new compound has a hexagonal structure with the lattice parameters a=5.4632(2) Å, c=5.0895(6) Å, Z=1, space group of P6₃.     

Direct observation of sublimation process on a CdTe(1 1 1) surface using an ultrafine particle

A particle with a CdTe core and carbon mantle was produced by the advanced carbon-coating method which enables direct coverage with a carbon layer using an electron microscope. The coagulated particles containing approximately 30–200 CdTe particles produced by the gas evaporation method were covered with a carbon layer of about 7 nm thickness at 300°C. By heating these particles above 500°C, the sublimation process of a part of the CdTe particle can be directly captured by high-resolution transmission electron microscopy and recorded in real time on videotape. Sublimation on the CdTe(1 1 1) surfaces occurred in the step flow mode of two (1 1 1) layers. It was observed that two (1 1 1) zinc-blende layers changed to the (0 0 0 2) würtzite configuration unit just before sublimation. The condensation of CdTe on the sublimated particle surface and growth of CdTe in the carbon layers were also captured in the video image. These sublimation processes were discussed in terms of the existence of the polarity of II–VI compounds.     

Study on the Ce substitution effects of BiFeO3 films on ITO/glass substrates

Ce substituted Bi_1−xCe_xFeO₃ (BCFO) films with x=0–0.15 were deposited on indium tin oxide (ITO)/glass substrates by sol–gel process annealed at 500 °C. Rhombohedral phase was confirmed by XRD study and no impure phases were observed till x=0.15. Substantially enhanced ferroelectricity was observed at room temperature due to the substitution of Ce. In the films with x=0.05 and 0.10, the double remnant polarization are 75.5 and 57.7 μC/cm² at an applied field 860 kV/cm. Moreover, the breakdown field was enhanced in the films with Ce substitution.     

Mechanochemical metathesis synthesis and characterization of nano-structured MnV2O6·xH2O (x=2, 4)

A solid-state metathesis approach for the synthesis of hydrated MnV₂O₆·xH₂O (x=2, 4) materials driven by mechanochemical activation energy has been demonstrated. The metathesis pathway of forming the desired product is confirmed by the presence of high lattice energy by-product such as NaCl. The structural, optical, and chemical properties of the synthesized materials are examined by powder X-ray diffraction, X-ray photoelectron spectroscopy, thermo gravimetric analysis, scanning electron microscopy, transmission electron microscopy, and diffused reflectance measurements in the UV–vis range. The valence state of Mn and V was determined to be +2 and +5, respectively, for the title compounds and the bandgap values determined showed these materials are likely to be semiconductors.     

Hydrothermal growth of single-crystal CaV6O16·3H2O nanoribbons

CaV₆O₁₆·3H₂O nanoribbons have been prepared by the hydrothermal method in the presence of sodium dodecyl sulfate (SDS) at 160°C for 10 h. X-ray diffraction pattern indicates that the sample is monoclinic phase of CaV₆O₁₆·3H₂O with the lattice contents a=12.18 Å, b=3.598 Å, c=18.39 Å, β=118.03°. Field emission scanning electron microscopy shows that the nanoribbons have widths in the range of 150–500 nm, thicknesses of 30–60 nm and lengths of 500 mm X-ray photoelectron spectrum measurements further confirm the formation of the CaV₆O₁₆·3H₂O phase. The formation of CaV₆O₁₆·3H₂O nanoribbons is a self-assembling process, in which surfactant SDS plays the role of soft template.     

Densities of Li2O–B2O3 melts

The densities have been systematically measured in xLi₂O–(1−x)B₂O₃ melts of different compositions with Li₂O content varying from x=0 to 0.68 from their respective melting points up to about 1450 K with a modified Archimedean method. The density decreased with increasing temperature for all the melts measured in this work. When x<0.15, the plot of temperature versus density could be well fitted by a quadratic polynomial function, and when x0.15, density decreased linearly with increasing temperature. At a fixed temperature, the density of the melts increased rapidly with Li₂O content, went through a maximum at about x=0.333 (Li₂O–2B₂O₃), and then decreased slowly as Li₂O content was further increased. In addition, the volume expansion coefficient (β) was calculated based on the densities measured in this work, and it was found that a maximum value appeared in the dependence of β on the molar ratio of Li₂O at about x=0.333.     

Growth of Na modified potassium lithium niobate crystal by the Czochralski method

Transparent Na modified potassium lithium niobate (Na_0.23K_2.60Li_1.82Nb_5.35O_15.70; NKLN) crystal was successively grown by the Czochralski method using RF induction heating from melt composition Na₂O:K₂O : Li₂O:Nb₂O₅=2:30:25:43 mol%. NKLN crystal showed a tetragonal tungsten bronze structure with lattice constants a=12.5446±0.0010 Å and c=4.0129±0.0005 Å at room temperature. The dielectric constant along the c-axis ε₃₃ showed a sharp maximum around 480 °C. Optical transmission edge was 370 nm and optical transmission spectra showed no absorption at wavelengths ranging from 380 to 800 nm. The structural and optical properties of NKLN were similar to those of the near stoichiometric KLN crystals. We believe that the growth of NKLN by the Czochralski method has an advantage for a large size and high-quality crystal.     

Profiling band structure in GaN devices by electron holography

Electron holography in a field emission gun transmission electron microscope has been used to profile the inner potential V₀ across GaN/x nm In_0.1Ga_0.9N/GaN/(0 0 0 1) sapphire samples (x=10, 40 nm) grown by molecular beam epitaxy and viewed in cross-section. Results are presented which suggest a decrease in V₀ of 3–4 V across the InGaN layer in the [0 0 0 1] direction. It is proposed that the results can be explained by charge accumulation across the InGaN layer and that the opposing contributions due to piezoelectric and polarisation fields are effectively masked by Fermi level pinning.     

Flux growth of PbMg1/3Ta2/3O3 single crystals

Single crystals of PbMg_1/3Ta_2/3O₃ (PMT) were grown by the flux method. The PbO–Pb₃O₄–B₂O₃ system was used as a solvent. Transparent and light yellow PMT single crystals of rectangular shape and dimensions up to 10×6×4 mm³ were obtained. For the applied growth conditions only, the crystals of the perovskite structure were grown. X-ray diffraction tests showed that at room temperature PMT exhibits cubic symmetry with lattice parameter a=4.042(1) Å. Dielectric studies pointed to relaxor properties of PMT. The characteristic broad and frequency-dependent maximum of dielectric permittivity was observed at 179.7 K (1 kHz).     

Density and surface tension of molten calcium fluoride

The density and the surface tension of molten calcium fluoride have been measured in the temperature range from 1690 to 1790 K by an improved Archimedian method and a ring depressing technique (J. Crystal Growth 187 (1998) 391), respectively. The ring depressing technique was demonstrated as an effective technique to measure the surface tension in comparison with the conventional ring pulling technique. The density varied with the temperature change corresponding to a linear relationship: ρ=3.767−6.94×10⁻⁴T (K). The density of the CaF₂ melt at the melting point is 2.594 g/cm³, which is equal to the result obtained by Shiraishi and Watanabe (Bull. Res. Inst. Miner. Dressing Metal, Tohoku Univ. 34 (1978) 1), but the temperature coefficient of the density is different from the results obtained by other investigators. The thermal expansion coefficient of calcium fluoride melt linearly increases with temperature heating. The surface tension of molten calcium fluoride indicates a negative linear relationship as a function of the melt temperature: γ(T)=442.4−0.0816×T(K) (mN/m). The surface tension measured using the ring depressing technique is larger than those results obtained by other techniques.     

Porous crystal structures obtained from directionally solidified eutectic precursors

Interconnecting cage-like porous structures of several halide compounds were prepared by the selective leaching of one eutectic phase method. The binary eutectic precursors were prepared by directional solidification using the Bridgman crystal growth technique. Porous NaMgF₃ (40% pore volume), CaF₂ (57% pore volume) and BaF₂ (43% pore volume) crystals were obtained after water leaching the NaF component of the directionally solidified NaF/NaMgF₃, NaF/CaF₂ and NaF/BaF₂ eutectics with the appropriate entangled microstructure. The growth conditions for eutectic-coupled growth and the morphology of the eutectics have been determined. In the coupled growth regime, the size of the eutectic phases “λ” is fairly uniform and varies with the eutectic growth rate “v” as λ²v=constant, which allows us to control the pore size within the 0.5–10 μm range. The simplicity and versatility of the eutectic growth also allows us to fabricate highly aligned porous structures at relatively high production rates.     

Influence of oxygen, hydrogen, helium, argon and vacuum on the surface behavior of molten InSb, other semiconductors, and metals on silica

Sessile drop experiments were performed on molten indium antimonide on clean quartz (fused silica) surfaces. A cell was constructed through which argon, helium, oxygen, hydrogen or a mixture of these was flowed at 600 °C. Some of the InSb was doped with 0.1% Ga. The surface tension σ of oxide-free molten InSb was smaller in Ar than in He, may have increased with increasing O₂ in the gas, and was not influenced by Ga or H₂. The contact angle θ on silica was higher in the presence of Ar, was lowered by O₂, and was not influenced by H₂ or Ga. The work of adhesion W and the surface energy σ_sv of the silica were higher in He than in Ar. The surface remained free of solid oxide only in flowing gas containing 0.8 ppm O₂. This behavior is attributed to reaction of O₂ at the surface of the melt to form In₂O gas. When solid oxide formed on Ga-doped material, it was strongly enriched in Ga, with the Ga/In ratio increasing with the concentration of O₂ in the gas.

Examination of published sessile-drop results for liquid metals and semiconductors on silica revealed that W and σ_sv were highest for reactive melts, in which SiO₂ dissolves. For non-reactive melts, W and σ_sv were lower and θ higher in a gas than in a vacuum, regardless of whether the experiments had been carried out in sealed ampoules, a flowing gas, or dynamic vacuum. The implication is that the surface of silica was different in a vacuum than in a gas at 1 bar.     

Synthesis and spectrum stability of high quality CdTe quantum dots capped with stearate groups in N-oleoylmorpholine solvent

The stearate-capped CdTe quantum dots (QDs) have been first prepared via direct reaction of cadmium stearate with Te powder in N-oleoylmorpholine solvent, which was a kind of clean, air-stable and conveniently synthesized acylamide, and can readily dissolve precursors cadmium stearate and Te powder at a relative low temperature. The as-prepared CdTe QDs exhibited size-dependent optical properties, steep absorbance edge and narrow photoluminescence full width at half maximum. The high-resolution transmission electron microscopy images and X-ray diffraction revealed that the highly monodisperse CdTe QDs were of regular spherical morphology with zinc blende crystal structure displaying mean sizes of about 4 nm. The energy dispersed spectrometry measurement indicated the presence of Cd and Te, with the Cd:Te ratio being close to 1:1. Fourier transform infrared transmission spectra confirmed the existence of stearate on the CdTe QDs surfaces. The experimental results also demonstrated that the stearate-capped CdTe QDs had an unexpected good stability.     

A study of the degree of relaxation of AlGaN epilayers on GaN template

The strain state of 570 nm Al_xGa_1−xN layers grown on 600 nm GaN template by metal organic chemical vapor deposition was studied using Rutherford backscattering (RBS)/channeling and triple-axis X-ray diffraction measurements. The results showed that the degree of relaxation (R) of Al_xGa_1−xN layers increased almost linearly when x0.42 and reached to 70% when x=0.42. Above 0.42, the value of R varied slowly and Al_xGa_1−xN layers almost full relaxed when x=1 (AlN). In this work the underlying GaN layer was in compressive strain, which resulted in the reduction of lattice misfit between GaN and Al_xGa_1−xN, and a 570 nm Al_xGa_1−xN layer with the composition of about 0.16 might be grown on GaN coherently from the extrapolation. The different shape of (0 0 0 4) diffraction peak was discussed to be related to the relaxation.     

Synthesis of Y2O3:Eu phosphors by bicontinuous cubic phase process

A novel approach for preparation of red-emitting europium-doped yttrium oxide phosphor (Y₂O₃:Eu) by using the bicontinuous cubic phase (BCP) process was reported in this paper. The BCP system was composed of anionic surfactant sodium bis(2-ethylhexyl)sulfosuccinate (AOT) and aqueous yttrium nitrate/europium nitrate solution. Energy dispersive spectrometer analysis revealed the homogeneous precipitation occurred in the BCP structure. Thermogravimetric analysis measurements indicated the precursor powder was europium-doped yttrium hydroxide, Y_1−xEu_x(OH)₃. Scanning electron microscopy micrographs showed the precursor powder had a primary size about 30 nm and narrow size distribution. After heat treatment in furnace above 700 °C for 4 h, high crystallinity Y₂O₃:Eu phosphors was obtained. However, the primary size of particles grew to 50–200 nm and the dense agglomerates with a size below 1 μm were formed. X-ray diffraction patterns indicated the crystal structure of precursor powders and Y₂O₃:Eu phosphors were amorphous and body-centered cubic structure, respectively. The photoluminescence analysis showed that the obtained Y₂O₃:Eu phosphor had a strong red emitting at 612 nm and the quenching started at a Eu concentration of 10 mol%. This study indicated that the BCP process could be used to prepare the highly efficient oxide-based phosphors.