油分散性氧化锌纳米微粒的制备及表征

采用直接沉淀法制备了异丁酸修饰纳米氧化锌微粒，用XRD、TEM、XPS、IR、UV-Vis、PL等检测手段对样品进行结构表征。结果表明：所制的样品为纤锌矿结构的氧化锌颗粒，粒度约为20 nm，异丁酸分子与表面锌原子以双齿螯合的形式结合。 Zn(II)2p_3/2的结合能与Zn的标准峰位相比，向低结合能方向移动了1.5 eV，其在可见光区比紫外区的荧光发射显著增强。分散性实验表明，样品在有机溶剂中有良好的分散性。     

纳米ZnO改性锌电极的性能

纳米ZnO改性锌电极的性能;纳米ZnO;锌电极;循环可逆性;放电容量     

CMC辅助纳米ZnO粒子的制备及表征

以离子型纤维素醚羧甲基纤维素(CMC)的水溶液为反应介质,制备[Zn4CO3(OH)6]CMC水凝胶,洗涤、干燥后经不同温度煅烧前驱物得到ZnO纳米粒子。通过XRD、SEM、TEM、TG-DSC及FT-IR等测试技术对产物的组成、粒径及形态进行表征,研究了CMC对前驱物及ZnO形态和尺寸的影响。结果表明,由于CMC加入对煅烧前驱物产生的空间位阻作用,所制得纳米ZnO粒子粒度分布均匀、分散性好、不易团聚、粒子的平均粒径<20 nm。利用UV-V is测试了纳米ZnO的光吸收性能,所得的纳米ZnO在200~400 nm具有较强的吸收性。     

ZnO纳米颗粒锚定的亚微米碳纤维的制备及其吸波性能

使用静电纺丝技术结合水热法制备了表面锚定ZnO纳米颗粒的亚微米碳纤维（ZnO/SDCFs）复合物,并详细研究了反应溶液的pH值对复合物的结构、组成、电磁特性和吸波性能的影响。结果显示,随着pH值的升高,ZnO的含量增加,介电常数、介电损耗以及电磁衰减能力均下降,但阻抗匹配程度提高。相比于纯碳纤维,所有ZnO/SDCFs复合物的吸波性能均得到不同程度的加强。其中,pH值等于8时所制备的ZnO/SDCFs-8复合物拥有最好的吸波性能,主要归因于电磁衰减能力和阻抗匹配间的更好平衡。当ZnO/SDCFs-8的填充量仅为2.5%（质量分数）、厚度为1.7 mm时,相应吸波涂层的最小反射损耗达到-44.1 dB,低于-10 dB的有效吸收带宽为6.1 GHz,频率范围为11.9~18 GHz;当厚度为3.0 mm时,有效吸收带宽可提高到11.8 GHz（6.2~18 GHz）。     

超声振荡直接沉淀法制备纳米ZnO的工艺研究

在超声振荡下直接沉淀法制备纳米ZnO的关键是控制硝酸锌的浓度、氨水和硝酸锌的配比,以及前驱化合物的焙烧温度、表面活性剂的种类以及加入时间。实验结果表明,用该法制备纳米ZnO,硝酸锌的初始浓度在0.7～1.0 mol/L,氨水和硝酸锌配比为1.0～1.2,在反应10 min后加入表面活性剂油酸钠,15 min后加入聚乙二醇1000,可制备得到30～60 nm的纳米ZnO。     

和频光谱研究油酸包覆的Fe3 O4 纳米颗粒

采用红外-可见和频振动光谱研究了表面包覆油酸分子的Fe3O4纳米颗粒, 得到了2种实验构型(构型1: 可见光入射角63°, 红外光入射角55°; 构型2: 可见光入射角45°, 红外光入射角55°)和3种偏振组合(ssp, ppp, sps)下的和频振动光谱, 比较了2种实验构型下和频光谱的特征, 通过偏振分析方法对各个光谱峰进行了归属.     

ZnO纳米粒子的表面光电压谱和光催化性能

采用焙烧前驱物碱式碳酸锌的方法制备了不同粒径的ZnO纳米粒子，而用粒径 最小的作为光催化剂，通过光还原过程分别得了贵金属质量分数为0.5%和0.75%的 Pd/ZnO或Ag/ZnO复合纳米粒子。利用XRD，TEM，XPS，SPS和EFISPS等测试技术对样 品进行了表征，并通过光催化氧化气相正庚烷评估了样品的光催化活性，考察了微 晶尺寸和贵金属Pd或Ag的沉积对ZnO纳米粒子表面光电压信号以及光催化活性的影 响，探讨了样品表面光电压谱与其光催化活性的关系，说明了可以通过表面光电压 谱的测试来初步地评估纳米粒子的光催化活性。结果表明：随着ZnO纳米微晶尺寸 的减小，其SPS信号强度逐渐变弱，而光催化活性逐渐升高；沉积适量的贵金属Pd 或Ag后，ZnO纳米粒子的SPS信号强度明显下降，而其光催化活性却有所升高。此外 ，对ZnO纳米粒子光催化剂的失活机理进行了分析。     

溶剂热法制备六角锥形ZnO及其光致发光性能

通过乙酸锌和醇溶液反应得到了六角锥形纳米ZnO颗粒, 反应过程中不使用碱溶液和表面活性剂. 利用透射电子显微镜(TEM)、选区电子衍射(SAED)及扫描电子显微镜(SEM)对其形貌和结构进行了表征分析. 结果表明, 此方法制备的ZnO颗粒为单晶, 而且六角锥形ZnO的室温光致发光谱(PL)在378 nm处显示出了单纯的紫外发射峰, 而不是通常报道的可见光区发射, 这也预示着这种特殊结构的纳米ZnO将会成为一种具有良好应用前景的光学材料.     

纳米银的电解质效应

向2种不同电性的纳米银溶胶中分别加入KCl、KBr、KI、KNO3、Mg(NO3)2、Al(NO3)3、K2CO3、K2SO4、KOH和HNO3电解质溶液,利用透射电子显微镜、紫外-可见分光光度计等研究电解质对纳米银的显微结构和光谱学性质的影响。结果表明,不同电解质离子在纳米银胶体表面吸附程度以及导致纳米银胶体聚集和生长程度不同,从而对纳米银胶体的分散状态和表面电势产生不同影响。这种影响的结果导致其对相同电性纳米银粒子和不同电性纳米银粒子的显微结构和光谱学性质影响不同。     

三氟乙酸修饰TiO_2纳米微粒的制备及磨擦学性能

采用化学法制备一种粒径约50nm的三氟乙酸修饰TiO2纳米微粒,并用高分辨透射电镜(HRTEM)、傅立叶红外(FTIR)和热分析(TG、DTA)、X射线粉末衍射(XRD)等手段对该纳米微粒进行了表征,用MRS 10A型四球磨擦试验机考察了该纳米微粒在液体石蜡中的磨擦学性能 结果表明:三氟乙酸修饰TiO2纳米微粒能分散于液体石蜡中且具有较好的抗磨性能,能极大地提高液体石腊的抗磨性和承载能力,降低了磨擦系数     

纳米氧化锌的制备及其在太阳光下的光催化性能

本文以醋酸锌、浓氨水为原料,采用均匀沉淀法,制备了在太阳光下具有优良光催化性能的纳米氧化锌粉体,并利用透射电镜(TEM)、UV-Vis、X射线衍射(XRD)和ξ电位对所得样品进行了表征;以亚甲基蓝(MB)溶液的光催化脱色降解为模型反应,考察了煅烧温度对其结构与催化性能的影响。研究结果表明:在150℃下煅烧4h得到了具有良好分散性和结晶性能的纳米氧化锌粒子,粒径分布均匀、平均粒径约10nm;该纳米材料在太阳光下具有高的光催化活性和稳定性,照射2h可以使MB溶液的脱色率达100%,且重复使用5次时染料的脱色率仍在95%以上;所得样品的ξ电位均为负值,样品表面过剩的负电荷源自于样品的结构缺陷,即Zn2+空位或O2-过剩,且表面电荷量随煅烧温度的不同而不同;结构缺陷是其光谱响应范围的拓展和在太阳光条件下具有良好催化性能等的重要原因。     

均一形貌的ZnO纳米棒的制备及其光催化性能研究

ZnO nanorods were synthesized from high purity Zn granule by a vapor phase deposition in the Ar + O₂ gas. The products were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The ZnO nanorods were typically 1～2 μm in length and 20～30 nm in diameter with an aspect ratio as high as 20. The UV absorption properties were detected and the results show that the ZnO nanorods have an extremely strong absorption at 200～380 nm wavelength. The results were good when the ZnO nanorods were used as photocatalyst.     

Novel Uric Acid Sensor Based on Enzyme Electrode Modified by ZnO Nanoparticles and Multiwall Carbon Nanotubes

Abstract

In this work, we report the development of a highly sensitive and stable uric acid sensor based on the synergic action of multiwalled carbon nanotubes (MWNTs) and ZnO nanoparticles. MWNTs were first cast on pyrolytic graphite (PG) wafers. ZnO nanoparticles were then decorated onto the negatively charged MWNTs via the Vapor Liquid Solid (VLS) growth. Uricase was immobilized on the ZnO nanoparticles surface because of their large differences in the isoelectric point (IEP). Last, a cationic polydiallyldimethylammonium chloride (PDDA) layer was coated onto the uricase-contained ZnO nanoparticle layer and resulted in the PDDA/uricase/ZnO/MWNTs multilayer structure. The unique multilayer structure provides a favorable microenvironment to keep the bioactivity of uricase, which led to rapid amperometric response toward uric acid. Amperometric detection of uric acid was carried out at 320 mV (vs. SCE) in 0.05 mol/L (M) phosphate buffer solution (pH 6.8). For the sensor, a wide linear response range of 5.0 µM to 1 mM with a linear sensitivity of 393 mA cm^?2M^?1, a detection limit of 2.0 µM (3σ), and a long-term stability of 160 days can be obtained by using differential pulse voltammetry (DPV). Testing results in human urine obtained from the sensors were also compared with the data obtained by spectrometry. For five samples with different concentrations of urine, the relative deviations between them were smaller than 3.8%. The recovery was between 96.5 and 104.0%.     

ZnO纳米粒子的表面光电压谱和光催化性能

采用焙烧前驱物碱式碳酸锌的方法制备了不同粒径的ZnO纳米粒子，而用粒径 最小的作为光催化剂，通过光还原过程分别得了贵金属质量分数为0.5%和0.75%的 Pd/ZnO或Ag/ZnO复合纳米粒子。利用XRD，TEM，XPS，SPS和EFISPS等测试技术对样 品进行了表征，并通过光催化氧化气相正庚烷评估了样品的光催化活性，考察了微 晶尺寸和贵金属Pd或Ag的沉积对ZnO纳米粒子表面光电压信号以及光催化活性的影 响，探讨了样品表面光电压谱与其光催化活性的关系，说明了可以通过表面光电压 谱的测试来初步地评估纳米粒子的光催化活性。结果表明：随着ZnO纳米微晶尺寸 的减小，其SPS信号强度逐渐变弱，而光催化活性逐渐升高；沉积适量的贵金属Pd 或Ag后，ZnO纳米粒子的SPS信号强度明显下降，而其光催化活性却有所升高。此外 ，对ZnO纳米粒子光催化剂的失活机理进行了分析。     

单分散氧气锌纳米粒子的制备及表征

用羟丙基甲基纤维素(HPMC)为空间分散剂,制备了前驱物[Zn2(OH)2CO3*HPMC],焙烧后得到的纳米ZnO同不加HPMC制备的ZnO相比较,产物粒度小、分散均匀、不易团聚.通过XRD, TEM及FT-IR对产物的组成、粒径及形貌进行了表征.利用UV-Vis测试了产物的光吸收性能,结果表明,所得的产物在200nm～400nm具有较强的吸收.     

ZnO/SAPO-34组装体的制备及发光性质研究

以微孔分子筛SAPO-34为主体，采用锌盐浸渍-灼烧的方法，在SAPO-34的菱沸石笼中制备出ZnO纳米粒子，并对不同温度下灼烧后得到的ZnO/SAPO-34组装体的发光性质进行了研究。由于SAPO-34菱沸石笼的尺寸所限，制备出来的ZnO粒子粒径小于1 nm。量子尺寸效应使得SAPO-34笼中的ZnO纳米粒子的荧光光谱在近紫外区的发射谱峰有明显的蓝移。     

基于低分子量聚乙烯亚胺和油酸的负电性基因载体

构建负电性的基因载体、发展基于低分子量聚乙烯亚胺(PEI)的基因载体对基因传递研究具有重要意义. 本文基于低分子量聚乙烯亚胺(2 kDa)和油酸构建了负电性的基因载体. 它通过混合聚乙烯亚胺(2 kDa)、dsDNA和油酸胶束而自发形成. 该基因载体在血清中很稳定,细胞毒性非常低,可包封80%以上DNA. 通过1,2-二硬脂酰-sn-甘油-3-磷酸乙醇胺-N-[甲氧基(聚乙二醇2000)]铵盐(DSPE-PEG)对其表面进行修饰,发现多达90%的基因可被细胞摄取.     

Sb2S3纳米粒子修饰ZnO纳米片微纳分级结构的光电化学性能

采用恒电位方法,选择氯化钾和乙二胺(EDA)为添加剂,在氧化铟锡(ITO)导电玻璃上制备了高度有序的ZnO纳米片阵列,通过二次电沉积得到了ZnO纳米片上生长纳米棒的微纳分级结构.利用化学浴沉积法在ZnO基底上沉积Sb₂S₃纳米粒子制备出了Sb₂S₃/ZnO纳米片壳核结构和Sb₂S₃/ZnO微纳分级壳核结构.利用扫描电子显微镜(SEM)、X射线衍射(XRD)、紫外-可见(UV-Vis)吸收光谱、瞬态光电流等对其形貌、结构组成和光电化学性能进行了表征和分析.结果表明, Sb₂S₃/ZnO纳米片上生长纳米棒分级壳核结构的光电流明显高于Sb₂S₃/ZnO纳米片壳核结构.在Sb₂S₃/ZnO纳米片壳核结构和Sb₂S₃/ZnO微纳分级壳核结构的基础上旋涂一层P3HT薄膜形成P3HT/Sb₂S₃/ZnO复合结构,以上述复合结构薄膜为光活性层组装成杂化太阳电池,其中, P3HT/Sb₂S₃/ZnO分级壳核结构杂化太阳电池的能量转换效率最高,达到了0.81%.     

纳米氧化锌的机械力化学表面改性

采用机械力化学表面改性工艺,以硬脂酸为改性剂,在气流粉碎机中对纳米氧化锌进行解团聚和表面改性,并借助SEM、XRD、FF—IR和XPS对改性前后的氧化锌粉体进行结构表征．结果表明：硬脂酸分子化学键合在氧化锌表面．改性前后氧化锌的晶体结构相同,其颗粒的团聚性降低,二次粒径明显减小．通过测定改性样品的活化指数和亲油化度,选择最佳的改性剂用量为氧化锌质量的10％,氧化锌表面亲油疏水,在有机溶剂中有较好的分散性．     

纳米ZnO的制备及其光催化性能研究

本文以羟丙基纤维素(HPC)作为分散剂,运用沉淀法制备出了粒径均匀的ZnO颗粒.通过透射电子显微镜(TEM),X射线衍射(XRD),紫外可见光吸收光谱,光致发光谱(PL)对ZnO进行了性能表征,并探讨了其形成机理及制备中的影响因素.利用纳米ZnO作为光催化剂对有机染料罗丹明B进行了光降解实验,实验结果表明,此方法制备的ZnO具有良好的光催化性能,有望在治理环境污染等领域具有良好的应用.