InAs wetting layer evolution on GaAs(0 0 1)

The evolution of two-dimensional (2D) strained InAs wetting layers on GaAs(0 0 1), grown at different temperatures by molecular beam epitaxy, was studied by in situ high-resolution scanning tunneling microscopy. At low growth temperature (400 °C), the substrate exhibits a well-defined GaAs(0 0 1)-c(4 × 4) structure. For a disorientation of 0.7°, InAs grows in the step-flow mode and forms an unalloyed wetting layer mainly along steps, but also in part on the terrace. The wetting layer displays some local c(4 × 6) reconstruction, for which a model is proposed. 1.2 monolayer (ML) InAs deposition induces the formation of 3D islands. At a higher temperature (460 °C), the wetting layer is obviously alloyed even at low InAs coverage. The critical thickness of the wetting layer for the 2D-to-3D transition is shifted to 1.50 ML in this case presumably since the strain is reduced by alloying.     

C-induced Ge dots: enhanced light-output from Si-based nanostructures

Pre-deposition of a fraction of a monolayer of C on an Si (0 0 1) substrate causes the formation of extremely small islands after the growth of only 2 monolayers (ML) of Ge. We demonstrate that these CGe dots exhibit particularly intense photoluminescence (PL) compared to a variety of different but comparable structures. Although grown at low temperatures (460°C), the CGe islands show a ten times more intense PL signal than conventionally grown self-assembled Ge islands, grown at 700°C. We show that the initial stage of CGe dot formation is likely to be governed by strain compensation effects. In a series of samples, where we have kept the total C and Ge amounts constant but varied the deposition sequence, we show that the specific CGe dot growth order of pre-grown low surface mobility C, followed by high surface mobility Ge leads to a distinct nanostructure within the SiGeC material system, exhibiting typical ‘dot-like' and intense PL. An almost strain compensated 50 layer stack of CGe dots is shown to emit intense PL at 0.99 eV.     

Large scale atomic ordering on uncovered GaAs(0 0 1) after InAs monolayer capping: Atomic structure of the (12 × 6) reconstruction

A well ordered c(8 × 2)-InAs monolayer is grown by molecular beam epitaxy (MBE) on a GaAs(0 0 1) substrate. After slow sublimation of this monolayer up to 560 °C, a homogeneously (n × 6) reconstructed GaAs surface is obtained. This surface is studied by scanning tunneling microscopy (STM) in UHV. This shows that it is well-ordered on a large scale with 200 nm long As dimer rows along and is also locally (12 × 6) reconstructed, the cell structure is proposed. We believe that this surface organization results from the specific As/Ga (0.7) surface atomic ratio obtained after the InAs monolayer growth and sublimation cycle.     

A novel (8 × 4) superstructure as precursor to the c(4 × 4) phase during Sb/Si(0 0 1) desorption

The role of kinetics in the superstructure formation of the Sb/Si(0 0 1) system is studied using in situ surface sensitive techniques such as low energy electron diffraction, Auger electron spectroscopy and electron energy loss spectroscopy. Sb adsorbs epitaxially at room-temperature on a double-domain (DD) 2 × 1 reconstructed Si(0 0 1) surface at a flux rate of 0.06 ML/min. During desorption, multilayer Sb agglomerates on a stable Sb monolayer (ML) in a DD (2 × 1) phase before desorbing. The stable monolayer desorbs in the 600–850 °C temperature range, yielding DD (2 × 1), (8 × 4), c(4 × 4), DD (2 × 1) phases before retrieving the clean Si(0 0 1)-DD (2 × 1) surface. The stable 0.6-ML (8 × 4) phase here is a precursor phase to the recently reported 0.25-ML c(4 × 4) surface phase, and is reported for the first time.     

Potential-induced structure transitions in self-assembled monolayers: ethanethiol on Au(1 0 0)

We have characterized the structural behaviour of ethanethiol self-assembled monolayers (SAMs) on Au(1 0 0) in 0.1 M H₂SO₄ as a function of electrode potential, using in-situ scanning tunneling microscopy (STM). After modification of the Au(1 0 0) electrode in an ethanolic solution of ethanethiol, STM images in air reveal a disordered thiol adlayer and a surface that is covered by 25% of monoatomic high gold islands, which originate from lifting of the (hex) reconstruction during thiol adsorption. In contrast to alkanethiol SAMs on Au(1 1 1), no vacancy islands are seen on the Au(1 0 0) surface. After contact of the SAM-covered Au(1 0 0) electrode with 0.1 M H₂SO₄ under potential control, two different structures are observed, depending on the potential range positive or negative of +0.3 V vs. SCE. In both cases the emerging ordered structures are quadratic, their unit cells being rotated by 45° with respect to the main crystallographic axes of the substrate. However, the ordered structure at negative potentials is more densely packed than the one at positive potentials, and in addition the surface reveals an almost 50% coverage of monoatomic high gold islands. The structure of the SAM changes reversibly with the electrode potential, the long range order gradually decreasing with each transition. Concomittant with this structure transition monoatomic deep holes are created when the potential is stepped from the cathodic to the anodic region. The experimental observations are rationalized by a high mobility of the gold thiolate moiety, causing the surface density of the SAM-covered gold to change drastically with potential.     

Surface deformation phenomena induced by electron-beam irradiation in strained InGaAs/AlGaAs layers on GaAs (1 0 0) and (3 1 1)B substrates

The strained InGaAs/AlGaAs layer structures have been grown on GaAs ( 10 0) and (3 1 1)B substrates in a horizontal low-pressure metalorganic vapor-phase epitaxy system at a temperature of 800°C. In the surface observation using a high-resolution scanning electron microscope, we have found that surface deformation phenomena induced by electron-beam irradiation in strained In_0.36Ga_0.64As,/Al_0.3Ga_0.7As layers on GaAs (1 0 0) and (3 1 1)B substrates. The change of the surface morphology was observed in real time on the display of SEM with the accelerating voltage of 30 kV and the irradiated time of 60–120 s. The surface deformation through mass transport seems to be the cause of the residual strain relaxation due to electron-beam irradiation.     

Local Au coverage as driving force for Au induced faceting of vicinal Si(0 0 1): a LEEM and XPEEM study

Adsorption of Au at 850°C on a regular stepped 4° vicinal Si(0 0 1) surface results in a dramatic change of the step morphology: the surface decomposes into areas which are perfectly flat with a (0 0 1) orientation and (1 1 9) facets. Low energy electron microscopy shows the dynamics of the faceting process in real space while X-ray photoemission electron microscopy (XPEEM) allows a spatially resolved determination of the Au coverage at different stages of the faceting process. At a critical Au coverage of ≈1/3 ML (0 0 1) terraces are formed which extend anisotropically along the step edges of the surface. The steps in between the terraces bunch and form step bands in order to conserve the macroscopic miscut of the sample. Driving force for this morphological transformation is a complex (5×3.2) reconstruction formed on the (0 0 1) terraces. XPEEM shows this phase separation also for the Au coverage: on the (0 0 1) terraces the Au coverage is up to 40% higher compared to the step bands. With further increasing Au coverage the width of the Au rich terraces increases while the step bands become steeper. In a second step Au adsorbs on the step bands transforming them into well defined and smooth (1 1 9) facets.     

Enhanced dispersion and stability of gold nanoparticles on stoichiometric and reduced TiO2(1 1 0) surface in the presence of molybdenum

Mo, Au and their coadsorbed layers were produced on nearly stoichiometric and oxygen-deficient titania surfaces by physical vapor deposition (PVD) and characterized by low energy ion scattering (LEIS), X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES) and scanning tunnelling microscopy (STM). The behavior of Au/Mo bimetallic layers was studied at different relative metal coverages and sample temperatures.

STM data indicated clearly that the deposition of Au on the Mo-covered stoichiometric TiO₂(1 1 0) surface results in an enhanced dispersion of gold at 300 K. The mean size of the Au nanoparticles formed at 300 K on the Mo-covered TiO₂(1 1 0) was significantly less than on the Mo-free titania surface (2 ± 0.5 nm and 4 ± 1 nm, respectively). Interestingly, the deposition of Mo at 300 K onto the stoichiometric TiO₂(1 1 0) surface covered by Au nanoparticles of 3–4 nm (0.5 ML) also resulted in an increased dispersity of gold. The driving force for the enhanced wetting at 300 K is that the Au–Mo bond energy is larger than the Au–Au bond energy in 3D gold particles formed on stoichiometric titania. In contrast, 2D gold nanoparticles produced on ion-sputtered titania were not disrupted in the presence of Mo at 300 K, indicating a considerable kinetic hindrance for breaking of the strong Au-TiO_x bond.

The annealing of the coadsorbed layer formed on a strongly reduced surface to 740 K did not cause a decrease in the wetting of titania surface by gold. The preserved dispersion of Au at higher temperatures is attributed to the presence of the oxygen-deficient sites of titania, which were retained through the reaction of molybdenum with the substrate. Our results suggest that using a Mo-load to titania, Au nanoparticles can be produced with high dispersion and high thermal stability, which offers the fabrication of an effective Au catalyst.     

Well-ordered (1 0 0) InAs surfaces using wet chemical treatments

Atomic ordering of HCl-isopropanol (HCl-iPA) treated and vacuum annealed (1 0 0) InAs surfaces was studied by scanning tunneling microscopy (STM), low-energy electron diffraction (LEED), and reflectance anisotropy spectroscopy (RAS). On the as-treated surface, a diffused (1 × 1) pattern is observed, which successively evolves to the β₂(2 × 4)/c(2 × 8) and (4 × 2)/c(8 × 2) ones after annealing to 330 °C and 410 °C, respectively. At the intermediate temperature of 370 °C, an ₂(2 × 4)/(4 × 2) mixed reconstruction is observed. Reflectance anisotropy spectra are compared with those of the corresponding reconstructions observed after As-decapping and found to be quite similar. Therefore we conclude that high-quality (1 0 0) InAs surfaces can be obtained by wet chemical treatment in an easy, inexpensive and practical way.     

Effects of growth conditions on the formation of self-assembled InAs quantum dots grown on (1 1 5)A GaAs substrate

Effects of growth conditions on the formation of InAs quantum dots (QDs) grown on GaAs (1 1 5)A substrate were investigated by using the reflection high-energy electron diffraction (RHEED) and photoluminescence spectroscopy (PL). An anomalous evolution of wetting layer was observed when increasing the As/In flux ratio. This is attributed to a change in the surface reconstruction. PL measurements show that QDs emission was strongly affected by the InAs deposited amount. No obvious signature of PL emission QDs appears for sample with 2.2 ML InAs coverage. Furthermore, carrier tunneling from the dots to the non-radiative centers via the inclination continuum band is found to be the dominant mechanism for the InAs amount deposition up to 4.2 MLs.     

Heteroepitaxial growth of thin InAs layers on GaAs(1 0 0) misoriented substrates: A structural and morphological comparison

Thin InAs epilayers were grown on GaAs(1 0 0) substrates exactly oriented and misoriented toward [1 1 1]A direction by atmospheric pressure metalorganic vapor phase epitaxy. InAs growth was monitored by in situ spectral reflectivity. Structural quality of InAs layers were studied by using high-resolution X-ray diffraction. No crystallographic tilting of the layers with respect to any kind of these substrates was found for all thicknesses. This result is discussed in terms of In-rich growth environment. InAs layers grown on 2° misoriented substrate provide an improved crystalline quality. Surface roughness of InAs layers depend on layer thickness and substrate misorientation.     

Energetics of the growth mode transition in InAs/GaAs(0 0 1) small quantum dot formation: A first-principles study

Based on first-principles density-functional pseudopotential calculations, the growth of InAs on the GaAs(0 0 1) surface has been studied. By analyzing the free energies of the surfaces with different thicknesses of the InAs coverages, the critical thickness of the layer-by-layer (2D) to island (3D) growth mode transition is predicted to be around 1.5 ML. Comparing the total energy differences between layer-by-layer growth models and 3D island models, the mechanism of the 2D-3D growth mode transition near the critical thickness (θ_crit) is studied which indicates that at the initial stage of InAs quantum dots formation, small 3D islands are formed randomly.     

Observation of triangular terraces and triangular craters of CaF2 film on Si(1 1 1) substrate

We have investigated the growth mode and surface morphology of CaF₂ film on Si(1 1 1)7×7 substrate by reflection high-energy electron diffraction (RHEED) using very weak electron beam and atomic force microscopy (AFM). It was found by RHEED intensity oscillation measurements and AFM observations that three-dimensional (3D) islands grow at RT; however, rather flat surface appears with two-dimensional (2D) islands around 300 °C. Especially, at high temperature of 700 °C, characteristic equilateral triangular terraces (or islands) with flat and wide shape grow with the tops directed toward [1 1 −2] of substrate Si(1 1 1). On the other hand, the desorption process of the CaF₂ film due to electron stimulated desorption (ESD) was also examined. It was found that the ESD process at 300 °C forms characteristic equilateral triangular craters on the film surface with the tops (or corners) directed toward [−1 −1 2] of substrate Si(1 1 1), provided that the film was grown at 700 °C.     

Fabrication of p-Si/β-FeSi2 balls/n-si structures by MBE and their electrical and optical properties

We report on the formation technique of single-crystalline β-FeSi₂ balls (<100 nm) embedded in a Si p–n junction region by Si molecular beam epitaxy (MBE). β-FeSi₂ films grown on Si (0 0 1) by reactive deposition epitaxy (RDE) aggregated into islands after annealing at 850°C in ultrahigh vacuum. The islands of β-FeSi₂ aggregated further into a ball shape by following the Si MBE overgrowth at 750°C. It was found from X-ray diffraction (XRD) patterns that the epitaxial relationship between the two materials, and single-crystalline nature were preserved even after the annealing and the Si overgrowth. Capacitance–voltage (C–V) characteristics and transmission electron microscope (TEM) images revealed that a lot of defects were introduced around the embedded β-FeSi₂ balls with an increase of embedded β-FeSi₂ quantity.     

Growth mechanism of the Pd(100)-p(2×2)-p4g-Al surface alloy

We have studied the growth mechanism of a Pd(100)-p(2×2)-p4g-Al surface alloy by scanning tunneling microscopy (STM). The surface alloy has a bilayer structure and is formed by annealing at 450–700 K (depending on the initial aluminum coverage) after the deposition of aluminum on Pd(100) at room temperature. The ratio of the surface-alloy coverage to the initial aluminum coverage is found to be constant (0.44) irrespective of the initial aluminum coverage from 0.5 monolayers (ML) up to 2 ML. The growth mechanism of the surface alloy is proposed on the basis of the STM measurements at various annealing temperatures. Upon annealing at 450 K, some of the surface aluminum atoms migrate into the bulk and, instead, palladium atoms come out to the surface. These palladium atoms react with aluminum atoms remaining on the surface to form a surface alloy. When the initial aluminum coverage is less than 1 ML, bilayer-high islands of the surface alloy with an average area of 100 nm² are formed at 450–500 K, which diffuse on the terrace at 500–700 K and coalesce to form larger islands. A possible role of the percolation transition of aluminum islands in the formation of the surface alloy is discussed.     

Molecular beam epitaxy growth and characterization of self-assembled InAs quantum dots on (1 0 0) InAlAs/InP substrates

Self-assembled InAs quantum dots (QDs) on In_0.52Al_0.48As layer lattice matched to (1 0 0) InP substrates have been grown by molecular beam epitaxy (MBE) and evaluated by transmission electron microscopy (TEM) and photoluminescence (PL). TEM observations indicate that defect-free InAs QDs can be grown to obtain emissions over the technologically important 1.3–1.55 μm region. The PL peak positions for the QDs shift to low energy as the InAs coverage increases, corresponding to increase in QD size. The room temperature PL peak at 1.58 μm was observed from defect-free InAs QDs with average dot height of 3.6 nm.     

A PdO(1 0 1) thin film grown on Pd(1 1 1) in ultrahigh vacuum

We present experimental results demonstrating that a high quality PdO(1 0 1) thin film can be grown on Pd(1 1 1) in ultrahigh vacuum by oxidizing the metal at 500 K using an oxygen atom beam, followed by annealing to 675 K. Low energy electron diffraction (LEED) images show that the [0 1 0] direction of the PdO(1 0 1) thin film aligns with the [−1 1 0] direction of the Pd(1 1 1) substrate, and that the PdO film grows in three degenerate domains, rotated 120° relative to one another. Based on excellent agreement between the experimental and simulated LEED patterns, we conclude that the surface structure of the PdO thin film deviates minimally from bulk-terminated PdO(1 0 1). Recent temperature programmed desorption (TPD) experiments also provide evidence that the PdO(1 0 1) thin film on Pd(1 1 1) is terminated by the stoichiometric surface in which half of the Pd atoms are coordinatively unsaturated (cus), corresponding to a cus-Pd atom density equal to about 35% of the surface density of Pd(1 1 1). The ability to generate a well-defined PdO(1 0 1) surface in ultrahigh vacuum should provide new opportunities for conducting model surface science studies of PdO, particularly studies aimed at elucidating the reactivity of PdO(1 0 1) toward species important in commercial applications of Pd catalysis.     

Heteroepitaxial growth of thin InAs layers on GaAs(1 0 0) misoriented substrates: A structural and morphological comparison

Thin InAs epilayers were grown on GaAs(1 0 0) substrates exactly oriented and misoriented toward [1 1 1]A direction by atmospheric pressure metalorganic vapor phase epitaxy. InAs growth was monitored by in situ spectral reflectivity. Structural quality of InAs layers were studied by using high-resolution X-ray diffraction. No crystallographic tilting of the layers with respect to any kind of these substrates was found for all thicknesses. This result is discussed in terms of In-rich growth environment. InAs layers grown on 2° misoriented substrate provide an improved crystalline quality. Surface roughness of InAs layers depend on layer thickness and substrate misorientation.     

Femtosecond pulsed laser deposition of Ge quantum dot growth on Si(1 0 0)-(2 × 1)

Ge quantum dots were grown on Si(1 0 0)-(2 × 1) by femtosecond pulsed laser deposition at various substrate temperatures using a femtosecond Ti:sapphire laser. In situ reflection high-energy electron diffraction and ex situ atomic force microscopy were used to analyze the film structure and morphology. The morphology of germanium islands on silicon was studied at different coverages. The results show that femtosecond pulsed laser deposition reduces the minimum temperature for epitaxial growth of Ge quantum dots to ∼280 °C, which is 120 °C lower than previously observed in nanosecond pulsed laser deposition and more than 200 °C lower than that reported for molecular beam epitaxy and chemical vapor deposition.     

Nanowedge island formation on Mo(1 1 0)

The deposition of ultrathin Fe films on the Mo(1 1 0) surface at elevated temperatures results in the formation of distinctive nanowedge islands. The model of island formation presented in this work is based on both experiment and DFT calculations of Fe adatom hopping barriers. Also, a number of classical molecular dynamics simulations were carried out to illustrate fragments of the model. The islands are formed during a transition from a nanostripe morphology at around 2 ML coverage through a Bales-Zangwill type instability. Islands nucleate when the meandering step fronts are sufficiently roughened to produce a substantial overlap between adjacent steps. The islands propagate along the substrate [0 0 1] direction due to anisotropic diffusion/capture processes along the island edges. It was found that the substrate steps limit adatom diffusion and provide heterogeneous nucleation sites, resulting in a higher density of islands on a vicinal surface. As the islands can be several layers thick at their thinnest end, we propose that adatoms entering the islands undertake a so-called “vertical climb” along the sides of the island. This is facilitated by the presence of mismatch-induced dislocations that thread to the sides of the islands and produce local maxima of compressive strain. Dislocation lines also trigger initial nucleation on the surface with 2-3 ML Fe coverage. The sides of the nanowedge islands typically form along low-index crystallographic directions but can also form along dislocation lines or the substrate miscut direction.