溶胶-凝胶法制备的Ba0.8Sr0.2TiO3薄膜的结构及铁电性质研究

采用0.05mol/L的前驱体溶液,利用溶胶-凝胶法成功制备了室温下具有优良铁电性质的Ba_0.8Sr_0.2TiO₃ (BST)薄膜.X射线衍射分析表明,制得的BST薄膜室温下呈四方相,场发射扫描电子显微观测显示BST薄膜表面平整、致密、无裂纹出现,薄膜晶粒呈柱状结构、尺寸在150nm左右.电学测量表明制备的BST薄膜室温下具有优良的铁电性能.薄膜的剩余极化P_r约为35μC/cm²,矫顽电场E关键词：     

GaS/GaAs界面电学性质研究

报道了微波放电法在GaAs表面生长GaS薄膜．用电容 电压法（C-V）、伏安法（I-V）以及深能级瞬态谱（DLTS）等测试手段对GaS/GaAs界面的电学性质进行了研究．GaS/GaAs界面的CV特性反映此处的界面特性比较好，界面态密度约为10¹²/（cm²·eV）．DLTS的测试得到了与其一致的结果．另外，从I-V曲线中漏电流的大小，估算出GaS的电阻率为10¹¹Ω·cm 关键词：     

铁电磁体Pb(Fe1/2Nb1/2)O3相变特征

借助与示差扫描量热法、磁化率测量、电子自旋共振、铁电与介电性质测量及电子衍射系统地研究了Pb(Fe_1/2Nb_1/2)O₃(PFN)的电、磁性质和相变特征．结果表明发生在380K附近的顺电－铁电转变和发生在145K附近的顺磁 反铁磁转变分别为一级相变和二级相变或弱一级相变．在室温下,PFN的剩余极化与矫顽场分别为11.5μC/cm²和3.04kV/cm.介电测量表明PFN的顺电-铁电相变为弥散型相变．其弥散指数为1.62.电子衍射表明Fe³⁺与Nb⁵⁺离子在B位置上是无序分布的,正是这种与无序分布相关联的成分涨落导致铁电相变的弥散性. 关键词：     

新型透明导电薄膜ErF3掺杂In2 O3的研制

利用电子束沉积技术首次制备了氟化铒 (ErF₃) 掺杂的氧化铟(In₂O₃)透明导电薄膜(IEFO),研究了薄膜的晶体结构、光学特性和电学特性。利用原子力显微镜测试了不同厚度薄膜的形貌,初步研究了薄膜的生长过程。研究发现:IEFO薄膜为多晶结构,Er原子的掺入改变了薄膜的优势生长方向,使薄膜在(211)、(222)、(444)3个方向上的生长趋势基本相同。 薄膜电阻率为1.265×10^-3 Ω·cm,电子迁移率为45.76 cm²·V^-1·s^-1,电子浓度为1.197×10²⁰ cm^-3,在380~780 nm范围内的可见光平均透过率为81%。     

基于旋涂法和电子束蒸发法制备的V2O5/Ag/V2O5叠层透明导电薄膜

利用溶胶-凝胶技术与电子束蒸镀相结合的方法在常温下制备了叠层V₂O₅/Ag/V₂O₅（VAV）透明导电薄膜,研究了各层薄膜厚度对叠层结构光电特性的影响。用原子力显微镜、紫外-可见光分光光度计、四探针电阻仪及开尔文探针对样品的表面形貌、光电性能及功函数等性质进行了表征。实验结果表明,该薄膜具有良好的光学和电学性质,可见光（380~780 nm）平均透过率达75%,迁移率为16.89 cm²/（V·s）,载流子浓度为－1.043×10²² cm^-3,方块电阻值为15.1 Ω/□,功函数为5.17 eV。该制备方法降低了V₂O₅薄膜的工艺制备难度,为该材料在太阳能电池中的应用创造了良好的前期基础。     

Ta2O5-PMMA复合栅绝缘层对OFETs性能的影响

选用五氧化二钽（Ta₂O₅）-聚甲基丙烯酸甲酯（PMMA）复合材料作为栅绝缘层制备了并五苯有机场效应晶体管（OFETs）。通过在Ta₂O₅表面旋涂一层PMMA可以降低栅绝缘层的表面粗糙度,增大其场效应晶体管的迁移率。研究了厚度在20~60 nm范围内的PMMA对复合绝缘层表面形貌、粗糙度以及器件电学性能的影响。结果表明,当PMMA厚度为40 nm时,器件的电学性能最佳。与单一的Ta₂O₅栅绝缘层器件相比,其场效迁移率由4.2×10^-2 cm²/（V·s）提高到0.31 cm²/（V·s）;栅电压增加到-20 V时,开关电流比由2.9×10²增大到2.9×10⁵。     

一种侧链共轭聚噻吩衍生物薄膜的三阶非线性光学响应

合成了一种侧链共轭的聚噻吩衍生物聚3-（5′辛基-噻吩乙烯基）噻吩（POTVTh）,并通过溶液旋涂制备了聚合物薄膜.吸收光谱显示该聚合物薄膜具有较小的禁带宽度和宽的光谱响应.采用Z扫描技术在800 nm下用飞秒激光器研究了该聚合物薄膜的三阶非线性光学特性,非线性吸收系数为5.63×10^-7cm/W,非线性折射率为-6.38×10^-11 cm²/W,三阶非线性极化率为4.21×10^-9esu,比侧链未共轭的 关键词： 聚噻吩衍生物 侧链共轭 三阶非线性极化率 非线性折射率     

旋涂法制备氧化锆介质层及其在薄膜晶体管中的应用

采用旋涂法制备了氧化锆介质层薄膜,重点讨论了退火温度以及旋涂转速对薄膜性能的影响及作用机制。研究发现高温后退火一方面使得氧化锆水合物脱水形成氧化锆,另一方面促使氧化锆薄膜结晶。此外,转速较高时,其变化对薄膜厚度及粗糙度无显著影响。当转速为5 000 r/min、退火温度为300℃时,制备的绝缘层厚度具有良好的厚度均匀性,粗糙度为0.7 nm,漏电流为3.13×10^-5 A/cm²（电场强度1 MV/cm）。最终,利用ZrO₂薄膜作为栅极绝缘层,在玻璃基板上制备了铟镓锌氧化物-薄膜晶体管（IGZO-TFT）,其迁移率为6.5 cm²/（V·s）,开关比为2×10⁴。     

Sol-gel法制备Bi0.85Nd0.15FeO3多铁性薄膜

利用sol-gel法在Pt/Ti/SiO₂/Si衬底上制备出Bi_0.85Nd_0.15FeO₃薄膜.研究退火温度对其晶相形成的影响,发现在450 ℃退火时,Bi_0.85Nd_0.15FeO₃晶相开始形成,但是结晶较差,而且存在杂相;在500—600 ℃退火可以获得单相Bi_0.85Nd_0.15FeO₃薄膜,退火温度升高有利于其结晶.对600 ℃退火的Bi_0.85Nd_0.15FeO₃薄膜的介电、铁电和电磁性能进行了测试.在测试频率为1 MHz时,其介电常数和介电损耗分别为145,0.032;饱和磁化强度大约为44.8 emu/cm³;剩余极化值(2P_r)大约是16.6 μC/cm². 关键词： sol-gel法 0.85Nd_0.15FeO₃薄膜')" href="#">Bi_0.85Nd_0.15FeO₃薄膜 铁电性能 铁磁性能     

(111)取向(Pb,La)TiO3铁电薄膜中90°纳米带状畴与热释电性能的研究

采用射频磁控溅射技术在Pt/Ti/SiO₂/Si(100)衬底上生长了掺镧钛酸铅(PLT)铁电薄膜.用X射线衍射技术(XRD)研究了PLT薄膜结晶性能，结果表明PLT薄膜为 (111)择优取向钙钛矿相织构.使用原子力显微镜(AFM)和压电响应力显微镜(PFM) 分别观察了PLT薄膜的表面形貌和对应区域的电畴结构.PFM观察显示PLT薄膜中存在90°纳米带状畴，电畴的极化为首尾相接的低能量的排列方式，带状畴的宽度为20—60nm.研究了PLT10铁电薄膜的制备条件与性能之间的关系.发现在优化条件下制备的PLT10铁电薄膜的介电常数ε_r为365、介电损耗tgδ为0.02，热释电系数γ为2.18×10^-8C·(cm²·K)^-1，可以满足制备非制冷红外探测器的需要. 关键词： PLT薄膜 电畴 PFM 极化     

溶胶-凝胶法制备Sr2Bi4Ti5O18薄膜及其铁电性能研究

采用溶胶-凝胶法,在氧气氛中和层层晶化的工艺条件下,成功地制备了沉积在Pt/Ti/SiO₂/Si(100)衬底上的铁电性能优良的Sr₂Bi₄Ti₅O₁₈ (SBTi)薄膜,并研究了SBTi薄膜的微结构、表面形貌、铁电性能和疲劳特性.研究表明：薄膜具有单一的层状钙钛矿结构，且为随机取向；薄膜表面光滑，无裂纹，厚度约为725nm；铁电性能测试显示较饱和、方形的电滞回线，当外电场强度为275kV/cm时 关键词： 溶胶-凝胶法 铁电薄膜 2Bi₄Ti₅O₁₈')" href="#">Sr₂Bi₄Ti₅O₁₈     

Effects of vanadium doping on structure and electrical properties of SrBi4Ti4O15 thin films

The effects of vanadium(V) doping into SrBi₄Ti₄O₁₅ (SBTi) thin films on the structure, ferroelectric, leakage current, dielectric, and fatigue properties have been studied. X-ray diffraction result showed that the crystal structure of the SBTi thin films with and without vanadium is the same. Enhanced ferroelectricity was observed in the V-doped SrBi₄Ti₄O₁₅ (SrBi_4−x/3Ti_4−xV_xO₁₅, SBTiV-x (x = 0.03, 0.06, and 0.09)) thin films compared to the pure SrBi₄Ti₄O₁₅ thin film. The values of remnant polarization (2P_r) and coercive field (2E_c) of the SBTiV-0.09 thin film capacitor were 40.9 μC/cm² and 105.6 kV/cm at an applied electric field of 187.5 kV/cm, respectively. The 2P_r value is over five times larger than that of the pure SBTi thin film capacitor. At 100 kHz, the values of dielectric constant and dielectric loss were 449 and 0.04, and 214 and 0.06 for the SBTiV-0.09 and the pure SBTi thin film capacitors, respectively. The leakage current density of the SBTiV-0.09 thin film capacitor measured at 100 kV/cm was 6.8 × 10⁻⁹ A/cm², which is more than two and a half orders of magnitude lower than that of the pure SBTi thin film capacitor. Furthermore, the SBTiV-0.09 thin film exhibited good fatigue endurance up to 10¹⁰ switching cycles. The improved electrical properties may be related to the reduction of internal defects such as bismuth and oxygen vacancies with changes in the grain size by doping of vanadium into SBTi.     

Effects of co-substitution on the electrical properties of BiFeO3 thin films prepared by chemical solution deposition

Ferroelectric BiFeO₃ thin films with Nd-Cr (or Sm-Cr) co-substitution (denoted by BNdFCr and BSmFCr, respectively) were deposited on the Pt(2 0 0)/TiO₂/SiO₂/Si(1 0 0) substrates by a chemical solution deposition method. X-ray diffraction patterns revealed the formation of BNdFCr and BSmFCr thin films without any secondary phases. The co-substituted BNdFCr (or BSmFCr) thin films, which were annealed at 550 °C for 30 min in N₂ atmosphere, exhibited enhanced electrical properties compared to BFO thin films with the remanent polarization (2P_r) and coercive electric field (2E_c) of 196, 188 μC/cm² and 600, 570 kV/cm with the electric field of 800 kV/cm, respectively. The leakage current densities of BNdFCr and BSmFCr thin films measured at room temperature were approximately three orders of magnitude lower than that of BFO thin film, and the leakage current at room temperature of the thin films exhibited three distinctive conduction behaviors. Furthermore, the values of pulse polarizations [i.e., +(P*-P^{^}) or −(P*-P^{^})] of BNdFCr and BSmFCr thin films were reasonably unchanged up to 1.4 × 10¹⁰ switching cycles.     

Ferroelectric properties of neodymium-doped Sr2Bi4Ti5O18 thin film prepared by solgel route

Sr₂Bi₄Ti₅O₁₈ (SBTi) and Nd-modified SBTi (SBNT) thin films were deposited on Pt/Ti/SiO₂/Si (1 0 0) substrates using a sol-gel method. Structure, morphology and electric properties were investigated systematically. These films were randomly oriented and composed of rod-like grains. The remanent polarization (2P_r) and coercive field (E_c) of SBNT films were 30 μC/cm² and 55 kV/cm, respectively. This value of 2P_r was much higher than the reported value of SBTi prepared by pulsed-laser deposition. More importantly, the SBNT films showed high fatigue resistance against continuous switching up to 3×10⁹ cycles and excellent charge-retaining ability up to 3×10⁴ s.     

Enhanced ferroelectric property of (Pb0.95Ca0.05)(Nb0.02Zr0.80Ti0.20)O3 thin films prepared by RF magnetron sputtering

(Pb_0.95Ca_0.05)(Nb_0.02Zr_0.80Ti_0.20)O₃ [PCNZT] thin films were deposited on the Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates by RF magnetron sputtering with and without a LaNiO₃ [LNO] buffer layer. Ca and Nb elements in PZT films enhance the ferroelectric property, LaNiO₃ buffer layer improves the crystal quality of the PCNZT thin films. PCNZT thin films possess better ferroelectric property than that of PZT films for Ca and Nb ion substitution, moreover, PCNZT thin films with a LNO buffer layer possess (1 0 0) orientation and good ferroelectric properties with high remnant polarization (P_r = 38.1 μC/cm²), and low coercive field (E_c = 65 kV/cm), which is also better than that of PCNZT thin films without a LNO buffer layer (P_r = 27.9 μC/cm², E_c = 74 kV/cm). The result shows that enhanced ferroelectric property of PZT films can be obtained by ion substitution and buffer layer.     

Investigation on FR(LT)–FR(HT) phase transition and pyroelectric properties of pulsed laser deposited Pb(Zr0.93Ti0.07)O3 thin films

The preparation process, crystallinity and electrical properties of pulse laser deposited Pb(Zr_xTi_1−x)O₃ (PZT) thin films were investigated in this paper. PZT (x = 0.93) thin film samples deposited at different substrate temperatures were prepared. Si (1 1 0) was the substrate; Ag and YBCO were the top electrode and the bottom electrode respectively. The bottom electrode YBCO was deposited on the Si substrate by pulsed laser deposition (PLD), and then PZT was epitaxially deposited on YBCO also by PLD. After annealing, the top electrode Ag was prepared on PZT by thermal evaporation, and then the Ag/PZT/YBCO/Si structured thin films were obtained. The XRD and the analysis of their electrical characters showed that, when the substrate temperature was elevated from 600 °C to 800 °C, the crystallinity and electrical properties of PZT thin films became better and better, and the F_R(LT)–F_R(HT) phase transition of PZT (x = 0.93) thin films occurred at 62 °C. The PZT film deposited at 800 °C had the best pyroelectric properties, and when the F_R(LT)–F_R(HT) phase transition of this film occurred, the peak value of pyroelectric coefficient (p) was obtained, with a value of 1.96 × 10⁻⁶ C/(cm² K). The PZT film deposited at 800 °C had the highest remnant polarization (P_r) and the lowest coercive field (E_c), with the values of 34.3 μC/cm² and 41.7 kV/cm respectively.     

基于VO2薄膜非致冷红外探测器光电响应研究

VO₂薄膜是非致冷微测辐射热红外探测器热敏电阻材料.研究中应用微电子工艺制备了VO₂溅射薄膜红外探测器,在296K的环境中测试了该探测器在不同的直流偏置、光调制频率下对873K标准黑体源8—12μm红外辐射的光电响应以及器件的噪声电压,在10和30Hz的调制频率下其响应率分别大于17kV/W和接近10kV/W.该探测器实现了探测率D大于1.0×10⁸cm (Hz)^1/2/W,热时间常量为0.011s的8—12μm非致冷 关键词： 非致冷测辐射热探测器 红外探测器 二氧化钒 薄膜     

Ferroelectric properties of Pr6O11-doped Bi4Ti3O12

Praseodymium doped Bi₄Ti₃O₁₂ (BIT) ceramics with composition Bi_2.9Pr_0.9Ti₃O₁₂ (BPT) were prepared by solid state reaction. These samples have polycrystalline Bi-layered perovskite structure without preferred orientation, and consist of well-developed plate-like grains with random orientation. Pr doping into BIT causes a large shift of the Curie temperature (T_C) of the BIT from 675 to 398 °C. At an electric field of 87 kV/cm, the remanent polarization and the coercive field of the BPT ceramics are 30 μC/cm² and 52 kV/cm, respectively. Furthermore, the dielectric permittivity and the dissipation factor of the BPT ceramics are 300 and 0.003 at 1 MHz, 1 V, and room temperature. Ferroelectric properties of the BPT ceramics are superior to V-doped Bi₄Ti₃O₁₂ (∼20 μC/cm² and 80 kV/cm) and (Sr, Ta)-doped Bi₄Ti₃O₁₂ (∼12 μC/cm² and 71 kV/cm) ceramics. In addition, the dense ceramics of praseodymium-doped B₄Ti₃O₁₂ were obtained by sintering at 1100 °C, about 100-200 °C lower than those of the SrBi₂Ta₂O₉ system.     

Si基Bi3.25La0.75Ti3O12铁电薄膜的制备与特性研究

采用Sol-Gel工艺低温制备了Si基Bi_3.25La_0.75Ti₃O₁₂铁电薄膜.研究了退火温度对薄膜微观结构、介电特性与铁电性能的影响.500℃退火处理的Bi_3.25La_0.75Ti₃O₁₂薄膜未能充分晶化，晶粒细小且有非晶团聚，介电与铁电性能均较差.高于550℃退火处理的Bi_3.25La_{0.75 关键词： 铁电薄膜 3.25}La_0.75Ti₃O₁₂')" href="#">Bi_3.25La_0.75Ti₃O₁₂ Sol-Gel工艺