环氧-丙烯酸酯混杂光固化体系的研究

研究环氧－丙烯酸酯混杂光固化体系中引发剂的协同作用，证实混杂光固化过程中自由基引发剂对阳离子引发剂二苯基碘Weng盐的增感作用，混杂光固化膜具有优良的机械性能，其抗冲击性能，抗弯曲性能及硬度优于单纯的阳离子体系固化膜，与自由基体系固化膜性能接近。混杂光固化膜的玻璃化转变温度高于自由基体系固化膜；它的耐溶剂性能优异，耐丙酮擦拭次数比自由基固化膜高25倍以上，比阳离子固化膜高3．5倍。这可能是由于混杂光固化过程中形成的IPN结构造成的，动态粘弹谱和扫描电镜的实验结果证实了这一结论。     

有机硅改性丙烯酸环氧单酯光-热混杂固化体系的表面性能

以有机硅改性丙烯酸环氧单酯为树脂配制了一系列紫外光-热混杂固化体系.通过FTIR表征了光-热固化过程双键和环氧特征吸收峰的变化.研究了不同的稀释剂对光固化和光-热混杂固化膜的凝胶率、吸水率、表面水接触角等性能的影响,并用能谱仪(EDS)测试了固化膜表面硅元素的含量.结果表明:光固化膜的凝胶率低于86.5%,而光-热混杂固化膜的凝胶率在97.0%左右.与丙烯酸环氧单酯光-热固化体系相比,有机硅改性丙烯酸环氧单酯光-热固化膜的表面水接触角有显著提高,由62.53°提高到99.27°,EDS测试也表明有机硅有富集于固化膜表面的特性.     

自由基-阳离子混杂光固化环氧/丙烯酸酯协同效应的研究

采用可见光引发自由基-阳离子混杂光固化体系,固化环氧/丙烯酸酯制备的复合树脂,重点研究了自由基光引发剂樟脑醌和阳离子光引发剂二苯基碘鎓六氟磷酸盐质量比对固化时间、固化深度、线尺寸变化率及树脂性能的影响。结果表明:在可见光的照射下,当樟脑醌在混合引发剂中的质量分数为0.75时,固化时间为6s,光固化深度为7.86mm,线尺寸变化率为0.2%,固化复合树脂的综合性能优良;很好地证明了自由基-阳离子混杂光固化体系结合了自由基聚合和阳离子聚合的优点,表现出较好的协同效应。     

甲基丙烯酸环氧丙酯共聚物乳液的研究

研究了以甲基丙烯酸环氧丙酯作为活性单体，采用种子乳液聚合制备四元体系的核—壳结构共聚物乳液，用透射电子显微镜观察了乳胶粒的微观形态，并对其稳定性、流变性等进行了测试，考察了甲基丙烯酸环氧丙酯及其含量对乳液性能的影响．     

环氧丙烯酸酯的紫外光固化

制备了适于配制紫外光固化涂料的环氧丙烯酸酯，研究了反应温度、阻聚剂、催化剂等因素对环氧树脂与丙烯酸反应的影响；讨论了反应机理和动力学；并利用红外光谱观察了产物的紫外光固化行为。季铵盐能有效地催化环氧树脂和丙烯酸的反应，当其用量为０．６％～１．２％时，在９０～１１０℃反应４．５～８小时后，环氧基转化率大于９７％。由此配制的光固化涂料经紫外光辐照能快速固化。     

用FTIR研究环氧化天然橡胶的热老化

与天然橡胶（ＮＲ）相比,环氧化天然橡胶（ＥＮＲ）具有良好的耐油性和气密性［１,２］,并由于环氧基团而有一定的极性,同其它高聚物的相容性较好．通过环氧基团的二次反应,ＥＮＲ分子链可接上其它的功能团,满足一些特殊的用途［３,４］．对于ＥＮＲ的力学性能、共...     

光固化环氧丙烯酸酯/SiO2杂化材料的研究

用FTIR、SEM、DSC和TGA表征了光固化环氧丙烯酸酯／SiO2杂化材料[(EA-TMSPM)／SiO2]，研究了盐酸、γ-甲基丙烯酰氧丙基三甲氧基硅烷(TMSPM)和无机物浓度对(EA-TMSPM)／SiO2结构与性能的影响。结果表明，无机物浓度高的(EA-TMSPM)／SiO2杂化体系中SiO2粒子尺寸略大于无机物浓度低的体系；盐酸和无机物浓度的增加，都可以增强杂化材料的耐磨性。     

苯乙烯-间戊二烯交替共聚物环氧化研究

苯乙烯(ST)-间戊二烯(PD)通过阴离子聚合可以合成交替序列共聚物SP,基于此序列的嵌段共聚物在抗冲击高透明树脂、增韧树脂等领域有极大应用价值，同时极性化改性聚烯烃材料对提升产品相容性、耐氧化、耐热性及透明性有重要意义。本文以间氯过氧化苯甲酸(m-CPBA)为环氧化试剂对SP进行环氧化改性研究，考察了反应温度、溶剂、SP分子量及环氧化剂类型对环氧化反应的影响。通过核磁氢谱(¹H-NMR)和傅里叶红外光谱(FTIR)对环氧化SP产物(eSP)进行了结构表征。同时建立了不同环氧度eSP的定量分析方法，并通过正交实验确定了本实验所采用实验条件的最优反应条件：四氢呋喃(THF)/环己烷(CH)混合溶剂、温度343 K、C—C/m-CPBA摩尔比为1∶1.25、反应时间60 min,可以实现SP的完全环氧化。最后利用示差扫描热量仪(DSC)分析了不同环氧度eSP的玻璃化转变温度(T_g),证明环氧化改性改善产品极性的同时也能显著提升聚烯烃使用温度。     

新型光交联互穿网络体系的合成与非线性光学性能

设计合成了侧链上接有肉桂酸酯基团功能化聚合物(E51-DO3-C)和侧链同时含有环氧基团和偶氮苯生色团的功能化低聚物(PPGF-DO3-50),这两种功能化聚合物可分别以环加成反应和阳离子光引发机制进行交联反应形成先交联IPN体系,研究了E51-DO3-C、PPGFDO3-50体系和光IPN体系的极化交联后材料的二阶非线性光学(NLO)性能。研究含DO3生色团的酚醛环氧甘油醚低聚体在BDS·2PF_6阳离子光引发下的光交联过程以及NLO性能,非线性光学系数d_(33)值稳定性较差。利用这两种体系的相容性,设计获得了复合物E51-DO3-C/PPGF-DO3-50,其d_(33)值稳定性有显著提高,室温下30天后d_(33)值保持初值的80％左右。     

乙丙共聚物熔融接枝甲基丙烯酸环氧丙酯

乙丙共聚物熔融接枝甲基丙烯酸环氧丙酯张晓民，尹志辉，殷敬华（中国科学院长春应用化学研究所高分子物理开放实验室长春１３００２２）关键词乙丙共聚物，甲基丙烯酸环氧丙酯，接枝共聚接枝共聚物可作为不相容共混体系的增容剂［１，２］，反应加工法制备乙丙共聚物（Ｅ...     

电子束辐射固化环氧树脂的反应过程分析

对双酚A型环氧树脂的电子束辐射固化反应过程进行了分析.考察了引发剂、稀释剂对树脂体系辐射反应的影响,以环氧丙烷作为模型化合物,研究了环氧丙烷-碘盐体系的电子束辐射反应机理,证实了在电子束辐射下,碘盐分解产生质子酸,引发环氧树脂阳离子开环聚合的反应过程.观测环氧树脂辐射固化区域发现,电子束穿过样品时发生强烈的散射,在辐射方向以及周围一定区域内引发固化反应,固化反应从活性中心开始向体系内部层层扩展,整个固化区域由很多的层状结构组成.     

Monitoring of visible light photopolymerization of an epoxy/dimethacrylate hybrid system by Raman and near-infrared spectroscopies

Hybrid systems formulated with epoxy and methacrylate monomers at mass fraction either 50:50 or 75:25 were studied. The individual monomer conversions during photopolymerization with visible light were monitored by Raman and near-infrared spectroscopies. The rate of polymerization and final degree of conversion of the methacrylate groups were raised when the epoxy monomer was present. This is attributed to enhancement of the mobility of the reactive species caused by the presence of the epoxy monomer. Conversely, the earlier vitrification of the system due to the faster polymerizing methacrylate network resulted in reduced conversion of epoxy rings.     

含环氧基聚硅氧烷的研究进展

含环氧基聚硅氧烷作为一类新型的功能高人子近年来受到了人们的关注。着重介绍含环氧基聚硅烷的种类、制备方法、性能特点等。     

Epoxy resins. New results and developments

In a survey the development of epoxy resin systems is described. During the past years countless formulations based on known structures were used, but only a relative small number of new epoxies and curing agents were investigated and only very few new compounds came on the market. A choice of these products will be discussed, also new latent accelerators and curing agents. By improvement of technical processes purer epoxies can be offered and toxicological risks could be strongly reduced. Especially new results in the fast growing field of photocrosslinking will be described. Besides iodonium, sulfonium and phosphonium compounds new arene iron salts and their behaviour will be presented. Generally, the trend in the epoxy field is to better heat resistant structures for new formulations in the field of adhesives and fibre-reinforced materials, and to new photocrosslinking systems.     

环氧树脂水性化体系研究进展

系统地介绍了目前国内外环氧树脂水性化的研究进展,总结了环氧树脂水性化体系的特点与应用,并提出一种水性环氧树脂乳液制备的新方法。     

阻燃型含磷环氧树脂体系的研究进展

将磷导入环氧树脂体系而赋予其阻燃性能是目前热门的研究课题。本文简述了含磷阻燃剂的阻燃机理，详细讨论了含磷阻燃环氧的类型及固化物的阻燃特性，以及磷和氮、硅等元素的协同效应。     

环氧树脂共混物相结构的调控方法研究

研究了环氧树脂(E51)/聚砜(PSF)共混物相结构的控制方法.通过抑制相分离、控制预固化的反应程度控制环氧树脂的分子量,固化后可获得不同的共混物相结构.依据红外测定的固化反应程度设定固化程序,可有效控制共混物的相结构.加入促进剂三氟化硼-乙基胺(BTF-EA)可提高固化反应速度,使相分离结构在早期被抑制,以获得小微区的相结构.     

Epoxy resin particles. I. Spontaneous particle formation by the polymerization reaction of epoxy resin in a stationary system using polyethers as organic media

 A thermosetting epoxy resin was found to form polymer particles spontaneously in a stationary reaction system using polyethers as solvents. Poly(oxypropylene) and its copolymer with poly(oxyethylene) were effectively used as reaction media. The diameter of the resultant particles depended on the structure of the amines used as hardeners as well as on the molecular weight and composition of the polyether media. The glass-transition temperatures of the particles revealed that a small amount of polyether used as the medium was incorporated in the epoxy resin particles during the polymerization. Received: 8 September 1999 Accepted: 7 December 1999     

端噁唑啉聚醚对环氧树脂的固化与增韧作用的研究

用IR、DSC等分析方法研究了端2-噁唑啉聚环氧丙烷(活性聚醚)与环氧树脂的固化反应,对固化机理作了讨论。并考察了不同分子量活性聚醚对环氧树脂的增韧作用。结果表明,此活性聚醚对环氧树脂增韧效果明显,固化树脂综合性能较好。     

舰船用无溶剂环氧涂料常温释放物及高温热解物分析与评价

涂料作为舰船舱室及其部件的内部防护装饰材料已广泛地应用于舰船舱室,科技的发展使得涂料更新换代的步伐加快。舰船舱室经常处于全封闭状态,为减少舱室空气污染对船员的身心健康和战术技术发挥的不良影响,故对舰船舱室大气环境质量提出了更高更新的要求,因此舰船用涂料的筛选尤为重要。涂料作为常用的一种非金属材料其挥发物具有一定的毒性,尤其是对一些新的、毒性不明的涂料,必须先对其进行使用条件下的安全性评价,以便确定其可否应用于舰船舱室之中。本实验根据有关标准对舰船用低毒无溶剂环氧涂料常温释放物及高温热解物进行分析,并对其作卫生学评价,从而为舰船设计、建造部门在筛选艇用涂料方面提供可靠的科学依据。