模板合成银纳米颗粒/DNA复合物：生物硫醇的高效荧光传感平台设计

金属纳米颗粒经常被用作纳米猝灭剂构建高效荧光传感平台.在本工作中,以FAM标记的DNA为模板,通过还原Ag＋制备得到银纳米颗粒（AgNPs）.由于AgNPs与DNA间稳固的结合,模板合成AgNPs呈现出很高的猝灭效率并可用作超猝灭剂以构建生物荧光传感平台.作为一种尝试,模板合成的DNA-AgNPs复合物被用作生物硫醇荧光检测.通过形成S-Ag键,硫醇与AgNPs发生作用并将FAM标记DNA从AgNPs表面取代下来,FAM荧光恢复.由于低的荧光背景信号,该传感器具有高信背比.此外,DNA-AgNPs复合物呈现出很好的稳定性,可应用于复杂的实际样品.为验证其在实际样品中检测生物硫醇的可行性,测定了人类尿样中的硫醇含量,其结果显示人类尿样中的硫醇总含量为229μM到302μM.为验证结果的可靠性,少量Cys被额外加入到尿样中,其回收率经测定为98%～103%.     

聚苯乙烯/银纳米粒子复合微球的合成及催化性能

首先通过乳液聚合和浓硫酸酸化制备表面富含磺酸根的磺化聚苯乙烯(PS)微球(直径532 nm),再用其静电吸附[Ag(NH_3)_2]~+离子,最后采用聚乙烯吡咯烷酮还原表面吸附的[Ag(NH_3)_2]~+离子,得到了负载银纳米粒子的PS/AgNPs复合微球.采用扫描电子显微镜、透射电子显微镜、紫外-可见光谱、红外光谱和X射线衍射表征了PS/AgNPs复合微球,并考察了其对甲基蓝(MB)的催化性能.结果表明,Ag纳米粒子高度分散在磺化PS微球表面;该PS/AgNPs复合微球对催化转化MB有较高的催化活性,并可多次重复利用.本研究在催化降解有机污染物方面有一定的实用价值.     

镍氮掺杂有序大孔/介孔碳负载银纳米颗粒用于高效电催化CO2还原

多组分体系中的协同作用为设计高效的二氧化碳还原电催化剂提供了新的思路. 本工作通过双模板法和化学还原法精心设计制备了大孔/介孔镍氮掺杂碳(Ni-N-OMMC)负载银纳米颗粒复合材料(Ag/Ni-N-OMMC), 用于高效电催化还原CO₂为CO. 此复合材料表现出良好的电催化活性, 在CO₂饱和的0.1 mol•L^–1 KHCO₃电解液中, 电位为–1.0 V (相对于可逆氢电极, RHE)时CO的电流密度(J_CO)高达33.29 mA•cm^–2. 并具有较宽的工作电压范围, 在–0.7~–1.0 V (vs. RHE)下, CO的法拉第效率超过90%. 其优异的电催化性能可能归因于Ag纳米颗粒与具有丰富Ni-N _x活性位点的Ni-N-OMMC载体之间的协同效应, 以及三维互联有序大孔/介孔结构提供的高比表面积和高效的质量/电荷传输.     

钯纳米颗粒负载在聚苯胺材料上制得催化Suzuki-Miyaura偶联反应的高效催化剂

在最近的几十年里,金属钯催化的Suzuki-Miyaura偶联反应已经得到了越来越多的关注,被广泛应用于药物、天然产物以及新材料的合成.与此同时均相催化剂发展迅速,高效的配体和大量的设计被用于Suzuki-Miyaura偶联反应中,但是钯催化剂的配体通常很昂贵和难以合成,因此钯催化剂系统的回收是非常有价值的,不仅是经济上的原因,同时也避免了产品的污染,所以发展非均相催化剂是必要的.近年来,研究学者们致力于设计非均相的钯催化剂,如将钯纳米颗粒负载到金属有机骨架、介孔分子筛以及活性炭等多种材料上得到的非均相钯催化剂并应用于Suzuki-Miyaura偶联反应中.我们主要介绍了钯纳米颗粒被负载在含磷配体的交联的聚苯胺材料上制得负载的钯催化剂,首先通过钯催化的三(4-碘苯基)胺与金刚烷基膦的C–P偶联,再由钯催化三(4-碘苯基)胺与对苯二胺的C–N偶联,进而得到钯纳米颗粒负载在含金刚烷基膦的聚苯胺材料上的催化剂Pd@PAN-Ad-0.5(钯含量为0.58 wt%),同时我们对催化剂进行了一些表征,如TEM,SEM,XRD,EDX,XPS,FT-IR,ICP等.通过TEM分析,我们发现钯纳米颗粒在聚合物表面分布均匀,并且金属钯的平均粒径为2–3 nm;EDX检测显示催化剂含有C,N,P,Pd,I元素,说明钯负载到含金刚烷基膦的聚苯胺材料上的催化剂Pd@PAN-Ad-0.5已经形成,并被用于Suzuki-Miyaura偶联反应.我们对反应体系中的各种影响因素进行了优化,包括溶剂、碱、反应时间、催化剂加入量以及不同的催化剂的优化,最终确定了最佳反应条件;对于带有不同取代基(如腈基、甲氧基、醛基、酮基以及硝基)的氯代芳烃和溴代芳烃与苯硼酸的Suzuki-Miyaura反应,以较少的催化剂使用量(0.075 mol%Pd)就能获得较高的相应的联苯产物收率.此外,催化剂Pd@PAN-Ad-0.5在偶联反应中具有较高的反应活性的同时,还具有较好的回收使用能力(至少能够回收使用5次),循环使用4次以后还具有较高的催化活性.为了探索催化剂Pd@PAN-Ad-0.5在工业上的应用,由于4'-氯-2-硝基-1,1'-联苯是合成啶酰菌胺药物的重要中间体,因此我们使用催化剂Pd@PAN-Ad-0.5催化2-硝基氯苯与4-氯苯硼酸的偶联反应,目标产物4'-氯-2-硝基-1,1'-联苯的收率高达96%.我们相信这类催化剂应用于实验室或工业上合成联苯化学品具有较大的潜力.     

Au/Ag2O与Ag掺杂的Au粉催化剂上CO氧化反应：Au-Ag双金属催化剂活性位

有关用于各种氧化反应中Au-Ag双金属催化剂存在显著协同效应的来源有两种观点：(1) AgOx块与体相Au表面的接触界面起重要作用,体相Au的表面是催化活性位;(2) Au-Ag双金属催化剂中形成的Au-Ag合金中电荷从Ag转移到Au上,可能对催化剂活性起作用。因此,确定Au表面上Ag是以氧化物还是以金属合金形式存在可能是深度理解该协同效应的关键。
　　为了检测和验证催化剂活性的增加是由于Ag2O与Au纳米粒子的紧密接触,在密闭循环反应体系中比较研究了Au/Ag2O和Ag2O催化剂上CO氧化反应。将CO/O2摩尔比为2的混合气通入到这二个催化剂上来跟踪压力降低的速率。因而检测了气体的消耗量和CO2的生成量。结果发现,在稳态下Au/Ag2O和Ag2O催化剂的压力降低的速率不存在差别。这两个催化剂上压力的降低是由于Ag2O中表面晶格氧被混合气中CO的还原所致。 Au/Ag2O催化剂上得到的结果与以前研究的具有氧化表面的Ag掺杂的Au粉末(Ag/Au-b)上的一致,也表明AgOx块与体相Au表面界面周边不大可能是CO氧化反应催化活性位。基于具有稳态表面的Ag/Au-b样品上的研究结果,我们认为AgOx物种被还原为0价态Ag而形成的Ag-Au合金很可能是催化活性位。     

一种家蚕茧衍生具有蜂窝状结构的钴-锰共掺杂碳材料双功能电解水催化剂

通过一步碳化石墨化过程,由家蚕茧制得了一种具有蜂窝状结构的氮钴锰共掺杂碳材料。该材料具有蜂窝状结构和高比表面积,同时由于暴露的钴-锰活性位点以及富含的吡啶氮和石墨氮,3%钴-锰/蚕茧的碳材料(3%Co-Mn/SCC)显示了高析氢反应活性,其初始电位和10 m A·cm~(-2)过电位分别只有121和155 m V,Tafel斜率为130 m V·dec~(-1),并且在酸性条件下具有很好的稳定性。与此同时,2%Co-Mn/SCC在碱性条件下表现出优异的析氧反应催化性能,具有较低的初始电位,Tafel斜率为143 m V·dec~(-1)。     

ZIF-67/石墨烯复合物衍生的氮掺杂碳限域Co纳米颗粒用于高效电催化氧还原

燃料电池阴极氧还原(ORR)催化剂目前主要以商业Pt/C为主, 其高成本和稀缺性极大地限制了燃料电池的广泛应用. 为了替代Pt/C催化剂, 廉价高效的非贵金属催化剂目前受到了广泛的研究和关注. 利用氧化石墨烯(GO)为诱导模板, 借助表面丰富的含氧官能团, 实现了Co基金属有机框架材料(MOF) (ZIF-67)在GO表面的原位生长, 构筑了ZIF-67/GO层状复合材料. 热解过程中, 石墨烯的存在有效抑制了Co纳米颗粒的团聚, 并且很好地维持了原始的层状结构. 最终获得的Co@N-C/rGO复合催化剂材料实现了活性位的高度分散, 并且具有丰富的孔结构和优异的导电性能. 在电化学性能测试中Co@N-C/rGO表现出优异的ORR性能, 其起始电位为0.96 V, 半波电位0.83 V, 远优于ZIF-67直接热解得到的Co@N-C材料, 且性能与商业Pt/C催化剂相当. 此外, Co@N-C/rGO复合催化剂还表现出良好的催化稳定性和甲醇耐受性, 显示出该材料作为燃料电池氧还原催化剂的重要潜力.     

MoSe2纳米片耦合Pt纳米颗粒用于高效双功能催化甲醇辅助水电解制氢(英文)

化石燃料的大量消耗所带来的全球性挑战推动人们大力发展清洁和可持续的能源.氢能作为一种绿色、无污染的能源载体,是能源向绿色经济转换的关键,而利用可再生能源进行的电解水制氢被认为是实现绿色制氢的最佳选择.然而由于析氧反应(OER)的氧化电位(1.23 V)较高,动力学缓慢,实际水电解需要更多的能量输入.具有低氧化电位的甲醇辅助水电解(0.016 V)可以匹配可再生能源实现低能耗电解制氢,受到了广泛关注.开发高效的用于催化甲醇氧化(MOR)和析氢反应(HER)的双功能催化剂是实现这一愿景的前提.传统的Pt基催化剂容易受到阳极侧MOR过程中产生的CO中间体毒化,严重影响甲醇辅助水电解制氢的效率.为了提升Pt基催化剂的催化活性和稳定性,一种有效的策略是引入合适的功能组分来促进催化反应.例如,贵金属颗粒和亲氧化成分(如过渡金属氧化物和磷化物)之间的金属-载体相互作用可以有效提高Pt基催化剂的抗CO中毒能力.过渡金属硒化物由于其优良的金属性和亲氧性作为催化促进剂受到越来越多的关注.硒化钼(MoSe₂)具有良好的稳定性和导电性并且其2H相中的不饱和边缘具有水活化和解离活性,同时其...     

碳膜包覆的氧化铁纳米颗粒:一种高效的芳硝基化合物加氢催化剂

铁是地球上最丰富的元素之一,它在生命反应中起到至关重要的作用.目前,铁基催化剂广泛应用于合成氨、费托合成、NOx的选择性催化还原等.最近,铁因其含量丰富、价格低廉、无毒等优势而在多相催化方面引起了重点关注.最新研究发现,铁基催化剂在甲烷直接偶联制乙烯、氧还原以及芳硝基化合物的选择性加氢等领域具有突出表现,其中芳硝基化合物选择性加氢是一类具有重要应用前景的反应,这是因为苯胺(AN)是一种重要的精细化学品和有机中间体,广泛用于医药、染料、农药等行业,苯胺的年产量超过了400万吨,目前使用的催化剂主要有Raney Ni、负载镍、Ru/SnO2及少量铂碳、钯碳催化剂.但是,在Ni基催化剂上,硝基苯加氢主要经过间接缩合途径,同时会伴有氧化偶氮苯(AOB)、偶氮苯(AB)和氢化偶氮苯(HAB)等副产物生成,这些高沸点的副产物会带来一系列问题,如产物分离困难、产品纯度较低以及催化剂失活等.在这种情况下,为了加速苯胺生成,工业上一般采用过量的Raney Ni催化剂.贵金属(如Pt,Pd和Ru等)对催化芳硝基化合物加氢具有极高的活性,且苯胺的生成主要经过直接加氢途径.然而,由于成本过高,贵金属催化剂的大规模应用还存在一定的困难.本文采用简易的方法制备了一种铁基催化剂,在这个催化剂中氧化铁纳米颗粒被碳膜包覆并嵌入至平板碳中(Fe2O3@G-C).该催化剂由活性炭、苯胺及醋酸亚铁热解所得.通过扫描电镜(SEM)、拉曼光谱(Raman)及X射线衍射(XRD)分析,我们证实在原始碳颗粒上形成了新的碳膜.同时高倍透射电镜图也清楚地揭示了氧化铁纳米颗粒被碳膜包覆的结构.实验发现,Fe2O3@G-C-900催化剂(900oC热解所得)在芳硝基化合物选择性加氢反应中具有很高的活性.在2 MPa H2,70oC条件下反应2 h,硝基苯(NB)转化率达到95.4%,苯胺选择性达到99.1%,远远高于其他载体(活性炭、SiO2、Al2O3和MgO)负载的铁基催化剂.表征结果发现,Fe2O3@G-C-900催化剂的高活性可能与其具有较大的比表面积(573.7 m2/g)、孔体积(0.22 cm3/g,孔径小于2 nm)、高度分散的氧化铁纳米颗粒以及氧化铁纳米颗粒和其表面碳膜的协同作用密切相关.此外,催化剂中引入的氮原子不仅可以在包覆的碳膜上形成缺陷,也能进一步增强包覆在氧化铁纳米颗粒表面的碳膜的催化活性.通过对Fe2O3@G-C-900催化剂在硝基苯加氢反应中的循环使用活性的考察,发现该催化剂在循环使用5次后,仍具有良好的活性.更重要的是,在Fe2O3@G-C-900催化剂上硝基苯的加氢主要是直接途径,反应中没有高沸点AOB,AB和HAB等副产物生成.鉴于Fe2O3@G-C-900催化剂对NB加氢具有优异的活性,我们还进行了一系列含有不同取代基团的芳硝基化合物的加氢实验,发现对位取代的底物相对于间位及邻位的底物更容易发生加氢还原反应,这应归因于该催化剂的孔径较小(0.52 nm).这些研究方法可以扩展至其他金属催化剂的制备,以促进高效益和可持续的工业生产的发展.     

银纳米颗粒/聚(乙撑二氧噻吩)修饰的硅纳米线阵列的合成及可见光催化性能研究

硅纳米线阵列由于其较强的光吸收能力及硅材料的丰富储量,被认为是最具大规模应用潜力的可见光光催化剂.针对硅材料在水相环境中不稳定这一瓶颈问题,本文提出了对硅纳米线阵列"先稳定、再活化"的修饰策略.通过在硅纳米线表面修饰聚(乙撑二氧噻吩)使其稳定,之后再修饰银纳米颗粒以提高光催化效率,得到了高效、稳定的可见光光催化剂.并通过研究聚(乙撑二氧噻吩)的厚度及银纳米颗粒的担载量对光催化剂性能的影响,得到了最佳的修饰条件.     

负载酞菁铁的氮掺杂中空碳球的电催化氧还原性能（英文）

开发低成本、高性能的氧还原反应（ORR）催化剂是当前的研究热点.虽然酞菁铁（FePc）在几十年前就被证明能高效地电催化氧还原反应,但由于其电子传导性和稳定性较差,无法取代商用的Pt/C催化剂.氮掺杂碳材料不仅化学性质稳定、电子传导性好,还有一定的氧还原催化活性.本文首先制备了聚苯乙烯@聚多巴胺球前驱体,经过高温碳化后制得了氮掺杂中空碳球,进而负载酞菁铁后制备了负载酞菁铁的氮掺杂中空碳球复合材料（FePc-NHCS）.通过调整煅烧温度和酞菁铁的负载量,可进一步调控FePc-NHCS的多孔结构、石墨化程度、氮掺杂的种类与含量及酞菁铁的负载状态.优化后的FePc-NHCS在碱性电解质中显示出优异的ORR催化活性,其半波电位和稳定性均高于商用Pt/C催化剂.研究结果表明,掺杂与复合是增强单项催化组分活性的有效途径.此外,通过调控催化剂的结构和组分也能有效地优化催化剂的氧化还原性能.     

Pressureless and Low-Pressure Synthesis of Microporous Carbon Spheres Applied to CO2 Adsorption

In this work, low-pressure synthesis of carbon spheres from resorcinol and formaldehyde using an autoclave is presented. The influence of reaction time and process temperature as well as the effect of potassium oxalate, an activator, on the morphology and CO₂ adsorption properties was studied. The properties of materials produced at pressureless (atmospheric) conditions were compared with those synthesized under higher pressures. The results of this work show that enhanced pressure treatment is not necessary to produce high-quality carbon spheres, and the morphology and porosity of the spheres produced without an activation step at pressureless conditions are not significantly different from those obtained at higher pressures. In addition, CO₂ uptake was not affected by elevated pressure synthesis. It was also demonstrated that addition of the activator (potassium oxalate) had much more effect on key properties than the applied pressure treatment. The use of potassium oxalate as an activator caused non-uniform size distribution of spherical particles. Simultaneously higher values of surface area and total pore volumes were reached. A pressure treatment of the carbon materials in the autoclave significantly enhanced the CO₂ uptake at 25 °C, but had no effect on it at 0 °C.     

CO2 Adsorption Study of Potassium-Based Activation of Carbon Spheres

The adsorption properties of microporous spherical carbon materials obtained from the resorcinol-formaldehyde resin, treated in a solvothermal reactor heated with microwaves and then subjected to carbonization, are presented. The potassium-based activation of carbon spheres was carried out in two ways: solution-based and solid-based methods. The effect of various factors, such as chemical agent selection, chemical activating agent content, and the temperature or time of activation, was investigated. The influence of microwave treatment on the adsorption properties was also investigated and described. The adsorption performance of carbon spheres was evaluated in detail by examining CO₂ adsorption from the gas phase.     

Comparative Adsorption of Crystal Violet and Congo Red onto ZnCl2 Activated Carbon

In this study, the adsorption characteristics of crystal violet (CV) and Congo red (CR) dyes from the aqueous solution onto prepared activated carbon were examined. The activated carbon was prepared from wood apple shell by chemical activation with ZnCl₂. The parameters studied were the effect of contact time, initial dyes concentration, and pH of solution. The experimental equilibrium data were analyzed and fitted to Langmuir, Freundlich, and Temkin isotherms. The maximum monolayer adsorption capacities of CV and CR dyes were found to be 142.85 and 83.33 mg per gram of prepared activated carbon at 298 K. The kinetic data obtained at different concentrations were analyzed using pseudo-first-order, pseudo-second-order, and intra-particle diffusion models. Batch adsorption kinetic studies showed that the adsorption of dyes followed pseudo-second-order kinetics and at four different concentrations of both dyes, indicating that chemisorption is the rate-limiting step. Thermodynamic studies reveal that the removal of dyes from aqueous solution onto activated carbon was a spontaneous, feasible, and endothermic process at a temperature greater than standard equilibrium temperature.     

Facile Preparation of Porous Carbon Derived from Pomelo Peel for Efficient Adsorption of Methylene Blue

Pomelo peel waste-derived porous carbon (PPPC) was prepared by a facile one-step ZnCl₂ activation method. The preparation parameters of PPPC were the mass ratio of ZnCl₂ to pomelo peel of 2:1, carbonization temperature of 500 °C, and carbonization time of 1 h. This obtained PPPC possessed abundant macro-,meso-, and micro-porous structures, and a large specific surface area of 939.4 m² g⁻¹. Surprisingly, it had excellent adsorption ability for methylene blue, including a high adsorption capacity of 602.4 mg g⁻¹ and good reusability. The adsorption isotherm and kinetic fitted with Langmuir and pseudo-second order kinetic models. This work provides a novel strategy for pomelo peel waste utilization and a potential adsorbent for treating dye wastewater.     

吸附法制备金属/碳催化剂用于5-羟基甲基糠醛高效电催化氧化的研究

以介孔中空碳球(HC)为载体,通过简单的吸附法吸附Ni2+/Fe3+金属离子,获得了在碱性电解液中具有高效5-羟基甲基糠醛(HMF)电催化氧化性能的Nix Fe1-x/HC催化剂.通过X射线衍射(XRD)、场发射扫描电子显微镜(SEM)和X射线光电子能谱(XPS)等手段对Nix Fe1-x/HC的物相、形貌结构及电子结构进行了表征,并通过线性扫描伏安和计时电位等方法测试了Nix Fe1-x/HC的HMF电催化氧化性能．结果显示, Nix Fe1-x/HC材料催化HMF氧化的活性随Fe引入量的增加先升高后降低, Ni0.7Fe0.3/HC拥有最优的催化活性, HMF的转化率为100%,2,5-呋喃二甲酸(FDCA)的选择性为90.5%,法拉第效率为90.2%,经历10次循环后,催化活性仅略微降低,表现出优良的催化稳定性.     

Characterization of Microporous Activated Carbon Electrodes for Electric Double-layer Capacitors

IntroductionElectric double layer capacitors( EDLCs) witha high power density can be used as memory back-up devices or electric vehicles.EDLCs store energyin the electric double layer by charge accumulationon the interface between the electrode and the elec-trolyte. In order to obtain reasonable energies andpower densities,the more suitable material forEDLCs musthave a high surface area with a signif-icant value of specific double layer capacitance,better pore size distribution and electro…     

Comparative Study for the Removal of Oxadiazon from Aqueous Solutions by Adsorption on Chitosan and Activated Carbon

Abstract

In the present investigation, chitosan and activated carbon are used as adsorbents for the removal of oxadiazon from aqueous solutions. The analyzing system was a gas chromatograph equipped with mass selective detector. The equilibrium studies are systematically carried out in a batch process, covering various process parameters that include agitation time, adsorbent dosage, and pH of the aqueous solution. Also, the relationship between extraction of oxadiazon and volume of aqueous/organic phase as well as the effect of inorganic salt were investigated. Adsorption behavior was found to follow Freundlich and Langmuir isotherms. The adsorption mechanism is described by a pseudo-second-order kinetics.     

One-Pot Synthesis of N-Rich Porous Carbon for Efficient CO2 Adsorption Performance

N-enriched porous carbons have played an important part in CO₂ adsorption application thanks to their abundant porosity, high stability and tailorable surface properties while still suffering from a non-efficient and high-cost synthesis method. Herein, a series of N-doped porous carbons were prepared by a facile one-pot KOH activating strategy from commercial urea formaldehyde resin (UF). The textural properties and nitrogen content of the N-doped carbons were carefully controlled by the activating temperature and KOH/UF mass ratios. As-prepared N-doped carbons show 3D block-shaped morphology, the BET surface area of up to 980 m²/g together with a pore volume of 0.52 cm³/g and N content of 23.51 wt%. The optimal adsorbent (UFK-600-0.2) presents a high CO₂ uptake capacity of 4.03 mmol/g at 0 °C and 1 bar. Moreover, as-prepared N-doped carbon adsorbents show moderate isosteric heat of adsorption (43–53 kJ/mol), acceptable ideal adsorption solution theory (IAST) selectivity of 35 and outstanding recycling performance. It has been pointed out that while the CO₂ uptake was mostly dependent on the textural feature, the N content of carbon also plays a critical role to define the CO₂ adsorption performance. The present study delivers favorable N-doped carbon for CO₂ uptake and provides a promising strategy for the design and synthesis of the carbon adsorbents.