Growth of ZnTe layers on (111) GaAs substrates by metalorganic vapor phase epitaxy

ZnTe layers were grown on (111) GaAs substrates by metalorganic vapor phase epitaxy using dimethylzinc and diethyltelluride as the source materials. X-ray diffraction analysis revealed that epitaxial ZnTe layers can be obtained on (111) GaAs substrates. X-ray rocking curves, Raman spectroscopy, and photoluminescence measurements showed that the crystal quality of ZnTe layers depends on the substrate temperature during the growth. A high-crystalline quality (111) ZnTe heteroepitaxial layer with strong near-band-edge emission at 550 nm was obtained at a substrate temperature of 440 °C.     

Growth and characterization of GaN and AlN films on (1 1 1) and (0 0 1) Si substrates

GaN and AlN films were grown on (1 1 1) and (0 0 1) Si substrates by separate admittances of trimethylgallium (or trimethylaluminum) and ammonia (NH₃) at 1000°C. A high temperature (HT) or low temperature (LT) grown AlN thin layer was employed as the buffer layer between HT GaN (or HT AlN) film and Si substrate. Experimental results show that HT AlN and HT GaN films grown on the HT AlN-coated Si substrates exhibit better crystalline quality than those deposited on the LT AlN-coated Si substrates. Transmission electron microscopy (TEM) of the HT GaN/HT AlN buffer layer/(1 1 1)Si samples shows a particular orientation relationship between the (0 0 0 1) planes of GaN film and the (1 1 1) planes of Si substrate. High quality HT GaN films were achieved on (1 1 1) Si substrates using a 200 Å thick HT AlN buffer layer. Room temperature photoluminescence spectra of the high quality HT GaN films show strong near band edge luminescence at 3.41 eV with an emission linewidth of ∼110 meV and weak yellow luminescence.     

Structural,electrical and optical properties of in-situ phosphorous-doped Ge layers

We have studied the impact of temperature and pressure on the structural and electronic properties of Ge:P layers grown with GeH₄+PH₃ on thick Ge buffers, themselves on Si(0 0 1). The maximum phosphorous atomic concentration [P] exponentially decreased as the growth temperature increased, irrespective of pressure (20 Torr, 100 Torr or 250 Torr). The highest values were however achieved at 100 Torr (3.6×10²⁰ cm^?3 at 400 °C, 2.5×10¹⁹ cm^?3 at 600 °C and 10¹⁹ cm^?3 at 750 °C). P atomic depth profiles, “box-like” at 400 °C, became trapezoidal at 600 °C and 750 °C, most likely because of surface segregation. The increase at 100 Torr of [P] with the PH₃ mass-flow, almost linear at 400 °C, saturated quite rapidly at much lower values at 600 °C and 750 °C. Adding PH₃ had however almost no impact on the Ge growth rate (be it at 400 °C or 750 °C). A growth temperature of 400 °C yielded Ge:P layers tensily-strained on the Ge buffers underneath, with a very high concentration of substitutional P atoms (5.4×10²⁰ cm^?3). Such layers were however rough and of rather low crystalline quality in X-ray Diffraction. Ge:P layers grown at 600 °C and 750 °C had the same lattice parameter and smooth surface morphology as the Ge:B buffers underneath, most likely because of lower P atomic concentrations (2.5×10¹⁹ cm^?3 and 10¹⁹ cm^?3, respectively). Four point probe measurements showed that almost all P atoms were electrically active at 600 °C and 750 °C (1/4th at 400 °C). Finally, room temperature photoluminescence measurements confirmed that high temperature Ge:P layers were of high optical quality, with a direct bandgap peak either slightly less intense (750 °C) or more intense (600 °C) than similar thickness intrinsic Ge layers. In contrast, highly phosphorous-doped Ge layers grown at 400 °C were of poor optical quality, in line with structural and electrical results.     

Transmission electron microscopy investigation of AlN growth on Si(111)

AlN layers with a thickness of 250 nm were grown by plasma-assisted gas source molecular-beam epitaxy on Si(111) at substrate temperatures between 600 °C and 900 °C. The surface morphology and microstructure of the AlN layers were analyzed by scanning and transmission electron microscopy. Different defect types are observed in the AlN layers and at the AlN/Si(111) interfaces as a function of the temperature: inclusions of pure Al in the Si-substrate, crystallites of the cubic AlN phase, dislocations, stacking faults and inversion domain boundaries. The formation and concentration of the defects depends strongly on the substrate temperature during the growth. X-ray diffraction rocking curves for the (0002) reflection yield minimum full width at half maximum values for the sample grown at the 900 °C under Al-rich conditions indicating optimum structural quality. However, the discussion of the entity of defects will show that a more differentiated view is required to assess the overall quality of the AlN layers.     

The preferential orientation of the directionally solidified Si–TaSi2 eutectic in situ composite

The Si–TaSi₂ eutectic in situ composite is a favorable field emission material due to relatively low work function, good electron conductivity, and three-dimensional array of Schottky junctions grown in the composite spontaneously. The preferential orientation during directional solidification is determined by the growth anisotropy. In order to obtain the preferential direction of the steady-state crystal growth, the transmission electron microscopy (TEM) is used for analysis. It is found that the preferential orientation of the Si-TaSi₂ eutectic in situ composite prepared by Czochralski (CZ) technique is [3 3¯ 2¯] Si∥[0 0 0 1] TaSi₂, (2 2 0)Si∥(2 2¯ 0 0) TaSi₂. Whereas the preferential orientation of the Si–TaSi₂ eutectic in situ composite prepared by electron beam floating zone melting (EBFZM) technique is [0 1¯ 1¯ ]] Si∥[0 0 0 1] TaSi₂,(0 1¯ 1) Si∥(0 1¯ 1 1)TaSi₂. The preferential directions of the Si-TaSi₂ eutectic in situ composites prepared by two kinds of crystal growth techniques are distinctly different from each other, which results from different solid–liquid interface temperatures on account of the different crystal growth conditions, e.g. different solidification rate, different temperature gradient, different solid–liquid interface curvature and different kinetic undercooling.     

Low temperature epitaxial growth of Ge on CaF2 buffered cube-textured Ni

Quasi-single crystal Ge films were grown on cube textured Ni substrate at a temperature of 350 °C using an insulating buffer layer of CaF₂. A direct deposition of Ge on Ni at 350 °C was shown to alloy with Ni. From x-ray pole figure analysis, it was shown that Ge grew epitaxially with the same orientation as CaF₂ and the dispersions in the out-of-plane and in-plane directions were found to be 1.7±0.1° and 6±1°, respectively. In the out-of-plane direction, Ge[111]6CaF₂[111]6Ni[001]. In addition, the Ge consisted of four equivalent in-plane oriented domains such that two mutually orthogonal directions: Ge〈2?11〉 and Ge〈01?1〉 are parallel to mutually orthogonal directions: Ni〈1?10〉 and Ni〈1?1?0〉, respectively, of the Ni(001) surface. This was shown to originate from the four equivalent in-plane oriented domains of CaF₂ created to minimize the mismatch strain between CaF₂ and Ni in those directions.     

Growth kinetics and boron doping of very high Ge content SiGe for source/drain engineering

We have studied the in-situ boron doping of high Ge content Si_1?xGe_x layers (x=0.3, 0.4 and 0.5). These layers have been grown at low pressure (20 Torr) and low temperature (600–650 °C) with a heavily chlorinated chemistry on blanket Si(0 0 1) substrates. Such a chemistry yields a full selectivity versus SiO₂ (isolation) and Si₃N₄ (sidewall spacers) on patterned wafers with gate stacks. We have quantified the impact of the diborane flow on the SiGe layer crystalline quality, its resistivity, the SiGe:B growth rate and the apparent Ge concentration. Resistivity values lower than 1 mΩ cm are easily achieved, all the more so for high Ge content layers. The SiGe growth rate increases and the apparent Ge concentration (from X-ray diffraction) decreases as the diborane flow increases. B atoms (much smaller than Si or Ge) indeed partially compensate the compressive strain in the SiGe:B layers. We have also probed the in-situ boron and phosphorus doping of Si at 750 °C, 20 Torr with a heavily chlorinated chemistry. The B ions concentration increases linearly with the diborane flow, then saturates at a value close to 4×10¹⁹ cm^?3. By contrast, the P ions concentration increases sub-linearly with the phosphine flow, with a maximum value close to 9×10¹⁸ cm^?3. Adding diborane (phosphine) to the gaseous mixture leads to a sharp increase (decrease) of the Si:B (the Si:P) growth rates, which has to be taken into account in device layers. All the know-how acquired will be most handy for the formation of in-situ doped recessed or raised sources and drains in metal-oxide semiconductor devices.     

Deposition of microcrystalline Ge films using hot-wire technique without toxic gases

To investigate the deposition of Ge films without toxic gas such as germane, we have studied the Ge films prepared by the hot-wire technique, which utilize the reaction between a Ge target and hydrogen atoms generated by the hot-wire decomposition of H₂ gas. The films deposited on Si substrate were microcrystalline Ge films and the mean crystallite size of the films increased from 13.3 to 24.8 nm with increasing the substrate temperature from 300 to 500 °C. Moreover, the deposition rate of Ge films deposited on Si substrate was higher than that of Ge films deposited on Corning 1737 substrate. It was found that the substrate temperature and the kind of substrate are key parameters for the preparation of microcrystalline Ge films by the hot-wire technique.     

Microcrystalline silicon–germanium alloys for solar cell application: Growth and material properties

Microcrystalline silicon–germanium (μc-Si_1−xGe_x:H) alloy films have been grown by 100-MHz glow-discharge of a SiH₄/GeH₄/H₂ gas mixture. Alloys over a full range of compositions were prepared to gain a comprehensive understanding of their growth and material properties. With increasing GeH₄ concentration in the gas-phase, we observed a preferential Ge incorporation behavior in the solid. Growth rate studies revealed that the Ge incorporation efficiency from source gas to solid is about five times greater than for Si at growth temperature of 200 °C, which accounts for the variation of alloy composition. With increasing Ge incorporation in the solid, on the other hand, we find a monotonic decrease in photoconductivity, followed by an electrical transition from weak n-type to strong p-type conduction at x > 0.7. At x ≈ 0.4, however, we obtained relatively high photoconductivity gains by a factor of 20 and strong infrared response in the solar cell structure. The Ge incorporation behavior and its effect on charge carrier transport are discussed.     

Optical investigations of germanium nanoclusters – Rich SiO2 layers produced by ion beam synthesis

In this work, refractive index and extinction coefficient spectra of germanium nanoclusters – rich SiO₂ layers have been determined using variable angle spectroscopic ellipsometry (VASE) in the 250–1000 nm range. The samples were produced by Ge⁺ ion implantation into SiO₂ layers on Si substrates and subsequent annealing at temperatures from 700 to 1100 °C. It is known from previous investigations of similar samples that the Ge nanoclusterization process starts already at 800 °C and spherical Ge nanocrystallites 5–8 nm in diameter are observed in the SiO₂ layers after annealing for 1 h at even higher temperatures of 1000–1100 °C. Rutherford backscattering spectrometry (RBS) was employed to measure the Ge atom concentration depth profiles in the studied samples. The RBS results helped us choose realistic models for the VASE analysis which were necessary for a proper interpretation of the VASE data. It has been found that the refraction index value for the SiO₂/Si layer increases after Ge implantation. This effect can be explained by a defect-dependent compaction of ion-bombarded layers. A band’s tail in the extinction coefficient spectra for all the samples is observed which originates from a strong ultraviolet absorption band at 6.8 eV due to a Germanium Oxygen-Deficiency Center (GeODC) and/or a Ge-E’center in SiO₂. The annealing process results in the emergence of weaker extinction coefficient bands in the 400–600 nm region, associated with direct band-to-band transitions in Ge nanostructures. Transformation of these bands, including their blue-shift with the increasing annealing temperature could be explained via a quantum-confinement mechanism, by size and structural changes in Ge nanostructures.     

Interface of GaN grown on Ge(1 1 1) by plasma assisted molecular beam epitaxy

Early efforts to grow GaN layers on germanium substrates by plasma assisted molecular beam epitaxy led to GaN domains, rotated by 8° relative to each other. Increased insight in the growth of GaN on germanium resulted in the suppression of these domain and consequently high quality layers. In this study the interface of these improved layers is investigated with transmission electron microscopy. The GaN layers show high crystal quality and an atomically abrupt interface with the Ge substrate. A thin, single crystalline Ge₃N₄ layer is observed in between the GaN layer and Ge substrate. This Ge₃N₄ layer remains present even at growth temperatures (850 °C) far above the decomposition temperature of Ge₃N₄ in vacuum (600 °C). Triangular voids in the Ge substrate are observed after growth. Reducing the Ga flux at the onset of GaN growth helps to reduce the triangular defect size. This indicates that the formation of voids in the Ge substrate strongly depends on the presence of Ga atoms at the onset of growth. However complete elimination was not achieved. The formation of voids in the germanium substrate leads to diffusion of Ge into the GaN layer. Therefore we examined the diffusion of Ge atoms into the GaN layer and Ga atoms into the Ge substrate. It was found that the diffusion of Ge into the GaN layer and Ga into the Ge substrate can be influenced by the growth temperature but cannot be completely suppressed. Our results suggest that Ga atoms diffuse through small imperfections in the Ge₃N₄ interlayer and locally etch the Ge substrate, leading to the diffusion of Ga and Ge atoms.     

Aluminum induced formation of SiGe alloy in Ge/Si/Al thin film structure

In this work, a study of aluminum induced crystallization (AIC) of thin film germanium/silicon/aluminum (Ge/Si/Al) structure on oxidized silicon is presented. The Ge/Si/Al trilayer structure was prepared in three consecutive thin film deposition processes. The AIC was performed in nitrogen at 500 °C within time duration between 1 and 9 h. The progress of crystallization was monitored by optical microscopy, Raman spectroscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM) combined with energy dispersive X-ray spectroscopy (EDS). It was found that in Ge/Si/Al structure the AIC can lead to formation of SiGe alloy at temperature of 500 °C. This presents an alternative low-temperature formation method of SiGe which is suitable for integration with the conventional Si technology in electronic device fabrication.     

InAs nanowire growth on oxide-masked 〈111〉 silicon

Here we investigate the growth of InAs nanowires on 〈111〉 Si substrates masked by SiO_x using metal–organic chemical vapor deposition. We study 〈111〉 (axial) and 〈1?10〉 (radial) growth of InAs NWs by varying growth duration, temperature, group-III molar flows, V/III ratio, mask material, mask opening size, and inter-wire distance. We find that growth takes place without an In droplet and the process evolves through three successive phases: nucleation of an InAs cluster, followed by two distinct nanowire growth phases. These two growth phases have different axial and radial growth rates, which originate in a transition from having In supply dominated by the open Si area in the first phase towards an In supply from the vapor/oxide mask in the second growth phase. The linear relation found between nanowire length and diameter vs. time in the last growth phase indicates that 〈111〉 growth is not surface diffusion limited as is usually the case for catalyzed growth. A high yield of vertical nanowires is obtained if group-III flow is above and V/III ratio below threshold values, in addition to having an arsenic-terminated Si surface. Furthermore, we observe that 〈111〉 and 〈1?10〉 growth is surface kinetically limited below 520 °C and 540 °C, respectively, with activation energies of 20 and 6.5 kcal/mol. This difference in activation energies limits the selectivity of the 〈111〉 to 〈1?10〉 growth to 25:1 under optimized conditions, which must be considered when fabricating axially modulated structures. However, we find that by placing wires in large arrays it is possible to completely stop the 〈1?10〉 growth rate in favor of the 〈111〉 growth rate.     

High-quality silicon/insulator heteroepitaxial structures formed by molecular beam epitaxy using Al2O3 and Si

Heteroepitaxial growth of γ-Al₂O₃ films on a Si substrate and the growth of Si films on the γ-Al₂O₃/Si structures by molecular beam epitaxy have been investigated. It has been found from AFM and RHEED observations that, γ-Al₂O₃ films with an atomically smooth surface with an RMS values of ∼3 Å and high crystalline quality can be grown on Si (1 1 1) substrates at substrate temperatures of 650–750°C. Al₂O₃ films grown at higher temperatures above 800°C, did not show good surface morphology due to etching of a Si surface by N₂O gas in the initial growth stage. It has also been found that it is possible to grow high-quality Si layers by the predeposition of Al layer followed by thermal treatment prior to the Si molecular beam epitaxy. Cross-sectional TEM observations have shown that the epitaxial Si had significantly improved crystalline quality and surface morphology when the Al predeposition layer thickness was 10 Å and the thermal treatment temperature was 900°C. The resulting improved crystalline quality of Si films grown on Al₂O₃ is believed to be due to the Al₂O₃ surface modification.     

Insights into effects of annealing on microstructure from SnO2 thin films prepared by pulsed delivery

Tin dioxide thin films were prepared by pulsed laser deposition techniques on clean glass substrates, and the thin films were then annealed for 30 min from 50 to 550 °C with a step of 50 °C, respectively. The influence of the annealing temperature on the microstructural and morphological properties of the tin dioxide thin films was investigated using X-ray diffraction, scanning electron microscopy, transmission electron microscopy and selected area electron diffraction. The experimental results showed that the amorphous microstructure almost transformed into a polycrystalline tin dioxide phase exhibiting a preferred orientation related to the (1 1 0), (1 0 1) and (2 1 1) crystal planes with increased temperatures. The thin film annealed at 200 °C demonstrated the best crystalline properties, viz. optimum growth conditions. However, the thin film annealed at 100 °C revealed the minimum average root-mean-square roughness of 20.6 nm with average grain size of 26.6 nm. These findings indicate that the annealing temperature is very important parameter to determining the thin film quality, which involves the phase formation, microstructure and preferred orientation of the thin films.     

Growth of germanium sulfide by hot wire chemical vapor deposition for nonvolatile memory applications

The growth of amorphous germanium sulfide (Ge–S) thin films using the hot wire chemical vapor deposition method has been performed at deposition temperatures in the range of 22–450 °C and pressures between 100 and 1800 Pa. Tetraallylgermanium and propylene sulfide were used as precursors for germanium and sulfur, respectively. The growth rate varies in the range of 1 and 100 nm/min and increases with increasing pressure and decreasing temperature. However, only the films deposited with lower growth rate exhibit conformal filling and good step coverage that could be observed at a growth rate of approximately 20 nm/min. Higher temperatures yield higher Ge content in the Ge–S films. In addition, the typical resistive switching behavior (three or four orders of magnitude) indicated that those films are suitable for nonvolatile memory applications.     

ZnO growth on Si with low-temperature ZnO buffer layers by ECR-assisted MBE

High-quality ZnO films were grown on Si(1 0 0) substrates with low-temperature (LT) ZnO buffer layers by an electron cyclotron resonance (ECR)-assisted molecular-beam epitaxy (MBE). In order to investigate the optimized buffer layer temperature, ZnO buffer layers of about 1.1 μm were grown at different growth temperatures of 350, 450 and 550 °C, followed by identical high-temperature (HT) ZnO films with the thickness of 0.7 μm at 550 °C. A ZnO buffer layer with a growth temperature of 450 °C (450 °C-buffer sample) was found to greatly enhance the crystalline quality of the top ZnO film compared to others. The root mean square (RMS) roughness (3.3 nm) of its surface is the smallest, compared to the 350 °C-buffer sample (6.7 nm), the 550 °C-buffer sample (7.4 nm), and the sample without a buffer layer (6.8 nm). X-ray diffraction (XRD), photoluminescence (PL) and Raman scattering measurements were carried out on these samples at room temperature (RT) in order to characterize the crystalline quality of ZnO films. The preferential c-axis orientations of (0 0 2) ZnO were observed in the XRD spectra. The full-width at half-maximum (FWHM) value of the 450 °C-buffer sample was the narrowest as 0.209°, which indicated that the ZnO film with a buffer layer grown at this temperature was better for the subsequent ZnO growth at elevated temperature of 550 °C. Consistent with these results, the 450 °C-buffer sample exhibits the highest intensity and the smallest FWHM (130 meV) of the ultraviolet (UV) emission at 375 nm in the PL spectrum. The ZnO characteristic peak at 438.6 cm⁻¹ was found in Raman scattering spectra for all films with buffers, which is corresponding to the E₂ mode.     

Ultra-thin polycrystalline Si layers on glass prepared by aluminum-induced layer exchange

In this work, we present studies of ultra-thin polycrystalline silicon layers (5–100 nm) prepared by the aluminum-induced layer exchange process. Here, a substrate/Al/oxide/amorphous Si layer stack is annealed at temperatures below the eutectic temperature of the Al/Si system of 577 °C, leading to a layer exchange and the crystallization of the amorphous Si. We have studied the process dynamics and grain growth, as well as structural properties of the obtained polycrystalline Si thin films. Furthermore, we derive a theoretical estimate of the grain density and examine characteristic thermal activation energies of the process. The structural properties have been investigated by Raman spectroscopy. A good crystalline quality down to a layer thickness of 10 nm has been observed.     

High-quality AlN layers grown by hot-wall MOCVD at reduced temperatures

We report on a growth of AlN at reduced temperatures of 1100 °C and 1200 °C in a horizontal-tube hot-wall metalorganic chemical vapor deposition reactor configured for operation at temperatures of up to 1500–1600 °C and using a joint delivery of precursors. We present a simple route—as viewed in the context of the elaborate multilayer growth approaches with pulsed ammonia supply—for the AlN growth process on SiC substrates at the reduced temperature of 1200 °C. The established growth conditions in conjunction with the particular in-situ intervening SiC substrate treatment are considered pertinent to the accomplishment of crystalline, relatively thin, ～700 nm, single AlN layers of high-quality. The feedback is obtained from surface morphology, cathodoluminescence and secondary ion mass spectrometry characterization.     

Characterizations of pulsed laser deposited SiC thin films

Thin films of silicon carbide (SiC) were prepared using pulsed laser deposition (PLD) on Si(1 0 0) substrates at a temperature of 370 °C. Various structural characterizations showed the development of short-range SiC precipitates in the films. These films were annealed isochronally at temperatures of 800 °C, 1000 °C and 1200 °C for 2 h under an inert environment. Thermally induced crystalline ordering of SiC into β-SiC phase was investigated by X-ray diffraction (XRD), Raman spectroscopy and Fourier transforms infrared (FTIR) spectroscopic measurements. In addition to the crystallization of SiC films, high temperature annealing resulted in the dissolution of carbon clusters found in the as-grown films.