Highly Active Electrocatalysis of the Hydrogen Evolution Reaction by Cobalt Phosphide Nanoparticles

Nanoparticles of cobalt phosphide, CoP, have been prepared and evaluated as electrocatalysts for the hydrogen evolution reaction (HER) under strongly acidic conditions (0.50 M H₂SO₄, pH 0.3). Uniform, multi‐faceted CoP nanoparticles were synthesized by reacting Co nanoparticles with trioctylphosphine. Electrodes comprised of CoP nanoparticles on a Ti support (2 mg cm^?2 mass loading) produced a cathodic current density of 20 mA cm^?2 at an overpotential of ?85 mV. The CoP/Ti electrodes were stable over 24 h of sustained hydrogen production in 0.50 M H₂SO₄. The activity was essentially unchanged after 400 cyclic voltammetric sweeps, suggesting long‐term viability under operating conditions. CoP is therefore amongst the most active, acid‐stable, earth‐abundant HER electrocatalysts reported to date.     

Channel‐Rich RuCu Nanosheets for pH‐Universal Overall Water Splitting Electrocatalysis

Channel‐rich RuCu snowflake‐like nanosheets (NSs) composed of crystallized Ru and amorphous Cu were used as efficient electrocatalysts for oxygen evolution reaction (OER), hydrogen evolution reaction (HER), and overall water splitting in pH‐universal electrolytes. The optimized RuCu NSs/C‐350 °C and RuCu NSs/C‐250 °C show attractive activities of OER and HER with low overpotentials and small Tafel slopes, respectively. When applied to overall water splitting, the optimized RuCu NSs/C can reach 10 mA cm^?2 at cell voltages of only 1.49, 1.55, 1.49 and 1.50 V in 1 m KOH, 0.1 m KOH, 0.5 m H₂SO₄ and 0.05 m H₂SO₄, respectively, much lower than those of commercial Ir/C∥Pt/C. The optimized electrolyzer exhibits superior durability with small potential change after up to 45 h in 1 m KOH, showing a class of efficient functional electrocatalysts for overall water splitting.     

Hierarchical Architectures Based on Ru Nanoparticles/Oxygen-Rich-Carbon Nanotubes for Efficient Hydrogen Evolution

Highly active and durable electrocatalysts are essential for producing hydrogen fuel through the hydrogen evolution reaction (HER). Here, a uniform deposition of Ru nanoparticles strongly interacting with oxygen-rich carbon nanotube architectures (Ru-OCNT) through ozonation and hydrothermal approaches has been designed. The hierarchical structure of Ru-OCNT is made by self-assembly of oxygen functionalities of OCNT. Ru nanoparticles interact strongly with OCNT at the Ru/OCNT interface to give excellent catalytic activity and stability of the Ru-OCNT, as further confirmed by density functional theory. Owing to the hierarchical structure and adjusted surface chemistry, Ru-OCNT has an overpotential of 34 mV at 10 mA cm⁻² with a Tafel slope of 27.8 mV dec⁻¹ in 1 M KOH, and an overpotential of 55 mV with Tafel slope of 33 mV dec⁻¹ in 0.5 M H₂SO₄. The smaller Tafel slope of Ru-OCNT than Ru-CNT and commercial Pt/C in both alkaline and acidic electrolytes indicates high catalytic activity and fast charge transfer kinetics. The as-proposed chemistry provides the rational design of hierarchically structured CNT/nanoparticle electrocatalysts for HER to produce hydrogen fuel.     

Fe–N/C nanofiber electrocatalysts with improved activity and stability for oxygen reduction in alkaline and acid solutions

Fe–N/C nanofiber (Fe–N/CNF) electrocatalysts were prepared by impregnating electrospun polyacrylonitrile nanofibers with iron nitrate (Fe(NO₃)₃) solution and subsequent heat treatment, exhibiting improved activity and stability during oxygen reduction reaction (ORR) both in 0.1 M KOH (pH?=?13) and 0.5 M H₂SO₄ (pH?=?0) electrolyte solutions. Higher treatment temperature and NH₃ atmosphere were preferred by the Fe–N/CNF catalysts, and especially the concentration of Fe(NO₃)₃ solution exerted great effects on the surface morphology, structure, and thus electrocatalytic performance of the catalysts. The Fe–N/CNFs prepared using 0.5 wt% Fe(NO₃)₃ solution showed relatively higher ORR activity in alkaline and acid solutions and better stability especially in 0.5 M H₂SO₄ solution than the catalyst without Fe, probably because Fe could promote the graphitization of the polymer-converted carbon species, enhancing the resistance to electrochemical oxidation and thus the stability of the Fe–N/CNF catalysts.     

A General Route to Prepare Low‐Ruthenium‐Content Bimetallic Electrocatalysts for pH‐Universal Hydrogen Evolution Reaction by Using Carbon Quantum Dots

A challenging but pressing task to design and synthesize novel, efficient, and robust pH‐universal hydrogen evolution reaction (HER) electrocatalysts for scalable and sustainable hydrogen production through electrochemical water splitting. Herein, we report a facile method to prepare an efficient and robust Ru‐M (M=Ni, Mn, Cu) bimetal nanoparticle and carbon quantum dot hybrid (RuM/CQDs) for pH‐universal HER. The RuNi/CQDs catalysts exhibit outstanding HER performance at all pH levels. The unexpected low overpotentials of 13, 58, and 18 mV shown by RuNi/CQDs allow a current density of 10 mA cm^?2 in 1 m KOH, 0.5 m H₂SO₄, and 1 m PBS, respectively, for Ru loading at 5.93 μgRu cm^?2. This performance is among the best catalytic activities reported for any platinum‐free electrocatalyst. Theoretical studies reveal that Ni doping results in a moderate weakening of the hydrogen bonding energy of nearby surface Ru atoms, which plays a critical role in improving the HER activity.     

β‐AgVO3 Nanorods as Peroxidase Mimetic for Colorimetric Determination of Glucose

β‐AgVO₃ nanorods have been demonstrated to exhibit intrinsic peroxidase‐like activity. The oxidation of glucose can be catalyzed by glucose oxidase (GOx ) to generate H₂O₂ in the presence of O₂ . The β‐AgVO₃ nanorods can catalytically oxidize peroxidase substrates including o‐phenylenediamine (OPD ), 3,3′,5,5′‐tetramethylbenzidine (TMB ), and diammonium 2,2′‐azino‐bis(3‐ethylbenzothiazoline‐6‐sulfonate) (ABTS ) by H₂O₂ to produce typical color reactions: OPD from colorless to orange, TMB from colorless to blue, and ABTS from colorless to green. The catalyzed reaction by the β‐AgVO₃ nanorods was found to follow the characteristic Michaelis–Menten kinetics. Compared with horseradish peroxidase and AgVO₃ nanobelts, β‐AgVO₃ nanorods showed a higher affinity for TMB with a lower Michaelis–Menten constant (K _m) value (0.04118 mM ) at the optimal condition. Taking advantage of their high catalytic activity, the as‐synthesized β‐AgVO₃ nanorods were utilized to develop a colorimetric sensor for the determination of glucose. The linear range for glucose was 1.25–60 μM with the lower detection limit of 0.5 μM . The simple and sensitive GOx ‐β–AgVO₃ nanorods–TMB sensing system shows great promise for applications in the pharmaceutical, clinical, and biosensor detection of glucose.     

WO_3纳米棒/石墨烯复合材料的制备及电化学储锂性能

以氯化钨和氧化石墨烯(GO)为原料,乙醇为溶剂,一步合成了WO3纳米棒/石墨烯纳米复合材料(WO3/RGO).将WO3/RGO纳米复合材料用于锂离子电池负极,并通过充放电测试、循环伏安(CV)和电化学阻抗谱(EIS)技术综合考察了该材料的储锂性能.结果显示,在0.1C(1C=638 mA?g-1)倍率下,复合物的首次放电比容量达到761.4 mAh?g-1,100次循环后可逆容量仍保持在635 mAh?g-1,保持率为83.4%.即使在5C倍率下容量仍高达460 mAh?g-1.由此说明,WO3/RGO纳米复合物具有优异的循环稳定性及倍率性能,可望用于高性能锂离子电池.     

以氨基化的聚苯乙烯微球为模板制备电致变色性能优良的单层有序多孔PBTB薄膜

以氯化钨和氧化石墨烯(GO)为原料,乙醇为溶剂,一步合成了WO₃纳米棒/石墨烯纳米复合材料(WO₃/RGO). 将WO₃/RGO纳米复合材料用于锂离子电池负极,并通过充放电测试、循环伏安(CV)和电化学阻抗谱(EIS)技术综合考察了该材料的储锂性能. 结果显示,在0.1C (1C=638 mA·g^-1)倍率下,复合物的首次放电比容量达到761.4 mAh·g^-1,100次循环后可逆容量仍保持在635 mAh·g^-1,保持率为83.4%. 即使在5C倍率下容量仍高达460 mAh·g^-1. 由此说明,WO₃/RGO纳米复合物具有优异的循环稳定性及倍率性能,可望用于高性能锂离子电池.     

Voltammetric Determination of BHT Antioxidant at Gold Electrode in Biodiesel

The voltammetric determination of synthetic antioxidant 2,6‐di‐tert‐butyl‐4‐methylphenole (BHT) was studied using linear‐sweep voltammetry (LSV) and cyclic voltammetry (CV) with a gold electrode and performed in isopropanol media containing either 0.1 mol L^?1 H₂SO₄ or 0.1 mol L^?1 LiClO₄ as supporting electrolyte. The results obtained have revealed that the most reliable detection was acquired in acidic media (isopropanol–H₂SO₄) whereas the use of isopropanol? LiClO₄ solution exhibited poorer reproducibility due to possible passivation of the electrode. Real samples of biodiesel mixture were analyzed without any special sample treatment or separation and results were compared with those obtained by FTIR‐spectroscopy.     

Co@Co3O4 Encapsulated in Carbon Nanotube‐Grafted Nitrogen‐Doped Carbon Polyhedra as an Advanced Bifunctional Oxygen Electrode

Efficient reversible oxygen electrodes for both the oxygen reduction reaction (ORR) and the oxygen evolution reaction (OER) are vitally important for various energy conversion devices, such as regenerative fuel cells and metal–air batteries. However, realization of such electrodes is impeded by insufficient activity and instability of electrocatalysts for both water splitting and oxygen reduction. We report highly active bifunctional electrocatalysts for oxygen electrodes comprising core–shell Co@Co₃O₄ nanoparticles embedded in CNT‐grafted N‐doped carbon‐polyhedra obtained by the pyrolysis of cobalt metal–organic framework (ZIF‐67) in a reductive H₂ atmosphere and subsequent controlled oxidative calcination. The catalysts afford 0.85 V reversible overvoltage in 0.1 m KOH, surpassing Pt/C, IrO₂, and RuO₂ and thus ranking them among one of the best non‐precious‐metal electrocatalysts for reversible oxygen electrodes.     

Formation of Eu2O3 Nanorods through Solvothermal Routes by Surfactant Assistance

Eu₂O₃nanorods were synthesized and characterized. The crystallites of Eu₂O(CO₃)₂·H₂O nanorods and Eu₂O₃ nanorods were obtained by means of surfactant assistance, with aqueous butanol solution as the solvent and hexamethylene tetramine as the base. The characteristics of the nanorods were analyzed by transmission electron microscopy, high‐resolution transmission electron microscopy, scanning electron microscopy and X‐ray diffraction. The Eu₂O₃ nanorod is about 80–300 nm in diameter and 1–5 µm in length. The formation mechanism of the 1D products was also proposed.     

Amorphous Mo-doped NiS0.5Se0.5 Nanosheets@Crystalline NiS0.5Se0.5 Nanorods for High Current-density Electrocatalytic Water Splitting in Neutral Media

It is vitally important to develop highly active, robust and low-cost transition metal-based electrocatalysts for overall water splitting in neutral solution especially at large current density. In this work, amorphous Mo-doped NiS_0.5Se_0.5 nanosheets@crystalline NiS_0.5Se_0.5 nanorods (Am−Mo−NiS_0.5Se_0.5) was synthesized using a facil one-step strategy. In phosphate buffer saline solution, the Am−Mo−NiS_0.5Se_0.5 shows tiny overpotentials of 48 and 209 mV for hydrogen evolution reaction (HER), 238 and 514 mV for oxygen evolution reaction (OER) at 10 and 1000 mA cm⁻², respectively. Moreover, Am−Mo−NiS_0.5Se_0.5 delivers excellent stability for at least 300 h without obvious degradation. Theoretical calculations revealed that the Ni sites in the defect-rich amorphous structure of Am−Mo−NiS_0.5Se_0.5 owns higher electron state density and strengthened the binding energy of H₂O, which will optimize H adsorption/desorption energy barriers and reduce the adsorption energy of OER determining step.     

Enhancing the Hydrogen Evolution Reaction Activity of Platinum Electrodes in Alkaline Media Using Nickel–Iron Clusters

Herein, we demonstrate an easy way to improve the hydrogen evolution reaction (HER) activity of Pt electrodes in alkaline media by introducing Ni–Fe clusters. As a result, the overpotential needed to achieve a current density of 10 mA cm^?2 in H₂‐saturated 0.1 m KOH is reduced for the model single‐crystal electrodes down to about 70 mV. To our knowledge, these modified electrodes outperform any other reported electrocatalysts tested under similar conditions. Moreover, the influence of 1) Ni to Fe ratio, 2) cluster coverage, and 3) the nature of the alkali‐metal cations present in the electrolyte on the HER activity has been investigated. The observed catalytic performance likely originates from both the improved water dissociation at the Ni–Fe clusters and the subsequent optimal hydrogen adsorption and recombination at Pt atoms present at the Ni–Fe/Pt boundary.     

CoP‐Doped MOF‐Based Electrocatalyst for pH‐Universal Hydrogen Evolution Reaction

Although electrocatalysts based on transition metal phosphides (TMPs) with cationic/anionic doping have been widely studied for hydrogen evolution reaction (HER), the origin of performance enhancement still remains elusive mainly due to the random dispersion of dopants. Herein, we report a controllable partial phosphorization strategy to generate CoP species within the Co‐based metal‐organic framework (Co‐MOF). Density functional theory calculations and experimental results reveal that the electron transfer from CoP to Co‐MOF through N‐P/N‐Co bonds could lead to the optimized adsorption energy of H₂O (ΔG ) and hydrogen (ΔG_H*), which, together with the unique porous structure of Co‐MOF, contributes to the remarkable HER performance with an overpotential of 49 mV at a current density of 10 mA cm^?2 in 1 m phosphate buffer solution (PBS, pH 7.0). The excellent catalytic performance exceeds almost all the documented TMP‐based and non‐noble‐metal‐based electrocatalysts. In addition, the CoP/Co‐MOF hybrid also displays Pt‐like performance in 0.5 m H₂SO₄ and 1 m KOH, with the overpotentials of 27 and 34 mV, respectively, at a current density of 10 mA cm^?2.     

Electrochemical Overoxidation of Polyindole and Its Cation‐Permselective Behavior

Polyindole films prepared by potentiostatic growth in dichloromethane solution were subjected to overoxidation studies in aqueous media. Overoxidation at potentials greater than 1.1 V (vs. SCE) in 0.1 M KNO₃ or 0.1 M H₂SO₄ was possible. Overoxidation in 0.1 M NaOH resulted in mechanically unstable films which were not adherent to the electrode surface. The overoxidation process in 0.1 M KNO₃ involved removal of one electron per four indole monomer moieties in the polymer film. Nucleophilic attack led to introduction of carboxylate functionality and to cation permselective behavior, as tested by cyclic voltammetry and hydrodynamic voltammetry of hexamminoruthenium(III) and hexacyanoferrate(III). Such films may be useful in various electrochemical sensor applications.     

A General Route to Prepare Low-Ruthenium-Content Bimetallic Electrocatalysts for pH-Universal Hydrogen Evolution Reaction by Using Carbon Quantum Dots

A challenging but pressing task to design and synthesize novel, efficient, and robust pH-universal hydrogen evolution reaction (HER) electrocatalysts for scalable and sustainable hydrogen production through electrochemical water splitting. Herein, we report a facile method to prepare an efficient and robust Ru-M (M=Ni, Mn, Cu) bimetal nanoparticle and carbon quantum dot hybrid (RuM/CQDs) for pH-universal HER. The RuNi/CQDs catalysts exhibit outstanding HER performance at all pH levels. The unexpected low overpotentials of 13, 58, and 18 mV shown by RuNi/CQDs allow a current density of 10 mA cm⁻² in 1 m KOH, 0.5 m H₂SO₄, and 1 m PBS, respectively, for Ru loading at 5.93 μgRu cm⁻². This performance is among the best catalytic activities reported for any platinum-free electrocatalyst. Theoretical studies reveal that Ni doping results in a moderate weakening of the hydrogen bonding energy of nearby surface Ru atoms, which plays a critical role in improving the HER activity.     

Photoelectrochemical properties of tungsten trioxide thin film electrodes prepared from facet-controlled rectangular platelets

The control of anisotropic crystal growth is critical for directing the orientation of crystal lattice planes, and it plays a key role towards understanding the effects of different planes on chemical reactions. Here, we report on the photoelectrochemical properties of plate-structured tungsten trioxide (WO₃) thin films prepared from facet-controlled rectangular platelets of hydrotungstite (WO₃·2H₂O) and tungstite (WO₃·H₂O), which are directly grown on tungsten substrates. The WO₃ thin films, prepared via WO₃·2H₂O platelets, show relatively stable current for photoelectrochemical water splitting and methanol oxidation. On the other hand, the photocurrent of the WO₃ thin films prepared via WO₃·H₂O platelets was significantly decreased during the photoelectrochemical oxidation of water, which is likely due to the accumulation of partially oxidized intermediates such as peroxo species on the surface. These results indicate that the surface nanostructures of WO₃ may have a significant influence on photoelectrode efficiency and selectivity for the catalytic oxygen evolution reaction.     

Glucose-derived carbon sphere supported CoP as efficient and stable electrocatalysts for hydrogen evolution reaction

Glucose-derived carbon sphere supported cobalt phosphide nanoparticles(Co P/C) were synthesized via a concise two-step method. The electrochemical measurement results indicate that the Co P/C prepared at 900 ℃ presents excellent electrocatalytic performance for hydrogen evolution reaction(HER). The overpotential at a current density of 10 m A cm~(-2) is 108 and 163 mV in 0.5 M H_2SO_4 and 1 M KOH, respectively, and maintains its electrocatalytic durability for at least 10 h. This work supplies a new field to challenge the construction of electrocatalysts for HER through using cost-effective carbon supported transition metal phosphides.     

Ultrathin,Porous and Oxygen Vacancies‐Enriched Ag/WO3−x Heterostructures for Electrocatalytic Hydrogen Evolution

Exploring advanced electrocatalysts for electrocatalytic hydrogen evolution is highly desired but remains a challenge due to the lack of an efficient preparation method and reasonable structural design. Herein, we deliberately designed novel Ag/WO_3?x heterostructures through a supercritical CO₂‐assisted exfoliation‐oxidation route and the subsequent loading of Ag nanoparticles. The ultrathin and oxygen vacancies‐enriched WO_3?x nanosheets are ideal substrates for loading Ag nanoparticles, which can largely increase the active site density and improve electron transport. Besides, the resultant WO_3?x nanosheets with porous structure can form during the electrochemical cycling process induced by an electric field. As a result, the exquisite Ag/WO_3?x heterostructures show an enhanced hydrogen evolution reaction (HER) activity with a low onset overpotential of ≈30 mV, a small Tafel slope of ≈40 mV dec^?1 at 10 mA cm^?2, and as well as long‐term durability. This work sheds light on material design and preparation, and even opens up an avenue for the development of high‐efficiency electrocatalysts.     

微波固相合成氧化锌纳米棒

通过前驱体的微波固相热分解法快速合成了氧化锌纳米棒, 其直径在60～385 nm之间, 长可达数微米. 前驱体则通过一步室温固相反应制备. 用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、能量色散X射线分析(EDX)和透射电子显微镜(TEM)对产物的结构和形貌进行了表征. 同时, 对氧化锌纳米棒的光致发光(PL)性能作了测试, 结果表明在355 nm处有一个明显的近带隙发射峰. 另外, 对比实验表明, 微波辐射在氧化锌纳米棒的形成过程中起了关键性作用, 并对其形成机理进行了初步探讨.