Structure and magnetism of NaRu2O4 and Na2.7Ru4O9

The structures of NaRu₂O₄ and Na_2.7Ru₄O₉ are refined using neutron diffraction. NaRu₂O₄ is a stoichiometric compound consisting of double chains of edge sharing RuO₆ octahedra. Na_2.7Ru₄O₉ is a non-stoichiometric compound with partial occupancy of the Na sublattice. The structure is a mixture of single, double and triple chains of edge-shared RuO₆ octahedra. NaRu₂O₄ displays temperature independent paramagnetism with . Na_2.7Ru₄O₉ is paramagnetic, χ₀= with and a Curie constant of 0.0119 emu/mol Oe K. Specific heat measurements reveal a small upturn at low temperatures, similar to the upturn observed in La₄Ru₆O₁₉. The electronic contribution to the specific heat (γ) for Na_2.7Ru₄O₉ was determined to be15 mJ/mole_Ru K².     

The crystal structure determinations and refinements of K2S2O7, KNaS2O7 and Na2S2O7 from X-ray powder and single crystal diffraction data

The crystal structures of K₂S₂O₇, KNaS₂O₇ and Na₂S₂O₇ have been solved and/or refined from X-ray synchrotron powder diffraction data and conventional single-crystal data. K₂S₂O₇: From powder diffraction data, monoclinic C2/c, Z=4, a=12.3653(2), b=7.3122(1), , β=93.0792(7)°, R_Bragg=0.096. KNaS₂O₇: From powder diffraction data; triclinic , Z=2, a=5.90476(9), b=7.2008(1), , α=101.7074(9), β=90.6960(7), γ=94.2403(9)°, R_Bragg=0.075. Na₂S₂O₇: From single-crystal data; triclinic , Z=2, a=6.7702(9), b=6.7975(10), , α=116.779(2), β=96.089(3), γ=84.000(3)°, R_F=0.033. The disulphate anions are essentially eclipsed. All three structures can be described as dichromate-like, where the alkali cations coordinate oxygens of the isolated disulphate groups in three-dimensional networks. The K-O and Na-O coordinations were determined from electron density topology and coordination geometry. The three structures have a cation-disulphate chain in common. In K₂S₂O₇ and Na₂S₂O₇ the neighbouring chains are antiparallel, while in KNaS₂O₇ the chains are parallel. The differences between the K₂S₂O₇ and Na₂S₂O₇ structures, with double-, respectively single-sided chain connections and straight, respectively, corrugated structural layers can be understood in terms of the differences in size and coordinating ability of the cations.     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Syntheses, structures, and magnetic and optical properties of the compounds [Hg3Te2][UCl6] and [Hg4As2][UCl6]

Two new quaternary salts, [Hg₃Te₂][UCl₆] and [Hg₄As₂][UCl₆], have been synthesized and their structures determined by single-crystal X-ray diffraction analysis. [Hg₃Te₂][UCl₆] is the product of a reaction involving UCl₄, HgCl₂, and HgTe at 873 K. The compound crystallizes in space group P2₁/c of the monoclinic system. [Hg₄As₂][UCl₆] results from the reaction of U, Hg₂Cl₂, and As at 788 K. It crystallizes in space group Pbca of the orthorhombic system. [Hg₃Te₂][UCl₆] has a two-dimensional framework of layers, whereas [Hg₄As₂][UCl₆] has a three-dimensional framework of layers interconnected by Hg atoms linearly bonded to As atoms. Both framework structures contain discrete [UCl₆]²⁻ anions between the layers. [Hg₃Te₂][UCl₆] exhibits temperature-independent paramagnetism. The optical absorption spectra of these compounds display f-f transitions.     

Multianvil high-pressure/high-temperature preparation, crystal structure, and properties of the new oxoborates Dy4B6O14(OH)2 and Ho4B6O14(OH)2

This paper reports about two new hydrogen-containing rare-earth oxoborates RE₄B₆O₁₄(OH)₂ (RE=Dy, Ho) synthesized under high-pressure/high-temperature conditions from the corresponding rare-earth oxides, boron oxide, and water using a Walker-type multianvil equipment at 8 GPa and 880 °C. The single crystal structure determination of Dy₄B₆O₁₄(OH)₂ showed: Pbcn, a=1292.7(2), b=437.1(2), , Z=2, R1=0.0190, and wR2=0.0349 (all data). The isotypic holmium species revealed: Pbcn, a=1292.8(2), b=436.2(2), , Z=2, R1=0.0206, and wR2=0.0406 (all data). The compounds exhibit a new type of structure, which is built up from layers of condensed BO₄-tetrahedra. Between the layers, the rare-earth cations are coordinated by 7+2 oxygen atoms. Furthermore, we report about temperature-resolved in situ powder diffraction measurements, DTA/TG, and IR-spectroscopic investigations into RE₄B₆O₁₄(OH)₂ (RE=Dy, Ho).     

The crystal chemistry of L-Ta2O5 and related structures

Single crystals of a new form of L-Ta₂O₅ with a 19×b superstructure have been synthesised by flux growth. The phase is most likely stabilised by the incorporation of a small amount of lithium (0.14 wt% Li) from the flux. The phase has C-centred monoclinic symmetry with , (), , γ=90.00(1)°. The structure was refined in space group C112/m to R₁=0.044 for 814 unique reflections with F>4σ(F). The structure can be described as comprising chains of edge-shared TaO₇ pentagonal bipyramids that are regularly folded at (010) planes to give sinusoidal chains along [010]. These chains are interconnected along [100] and [001] by corner sharing, creating inter-chain regions that are occupied by isolated TaO₆ octahedra and pairs of corner-shared octahedra. A comparison with published data for high-quality refinements of related structures has led to the development of a general model that can explain the structural chemistry variations in the known L-Ta₂O₅-related structures. A shorthand notation is presented for representing the structures, based on the sequence along [010] of the interchain octahedra.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

Synthesis, crystal and magnetic structure of a novel brownmillerite-type compound Ca2Co1.6Ga0.4O5

The novel compound Ca₂Co_1.6Ga_0.4O₅ with brownmillerite (BM) structure has been prepared from citrates at 950 °C. The crystal structure of Ca₂Co_1.6Ga_0.4O₅ was refined, from neutron powder diffraction (NPD) data, in space group Pnma, , , , χ²=1.798, , R_wp=0.0378 and R_p=0.0292. On the basis of the NPD refinement the compound was found to be a G-type antiferromagnet (space group Pn^′m^′a) at room temperature, with the magnetic moments of cobalt atoms directed along chains of tetrahedra in the BM structure. Electron diffraction and electron microscopy studies revealed disorder in the crystallites, which can be interpreted as the presence of slabs with BM-type structure of Pnma and I2mb symmetry.     

Composition-induced phase transition in Ca14Zn6−xGa10+xO35+x/2 (x=0.0 and 0.5)

Novel complex oxides Ca₁₄Zn₆Ga₁₀O₃₅ and Ca₁₄Zn_5.5Ga_10.5O_35.25 were prepared in air at 1200 °C, 72 h. Refinements of their crystal structures using X-ray powder diffraction data showed that Ca₁₄Zn₆Ga₁₀O₃₅ is ordered (S.G. F23, =0.0458, R_p=0.0485, R_wp=0.0659, χ²=1.88) and Ca₁₄Zn_5.5Ga_10.5O_35.25 disordered (S.G. F432, =0.0346, R_p=0.0601, R_wp=0.0794, χ²=2.82) variants of the crystal structure of Ca₁₄Zn₆Al₁₀O₃₅. In the crystal structure of Ca₁₄Zn₆Ga₁₀O₃₅, there are large empty voids, which could be partially occupied by additional oxygen atoms upon substitution of Zn²⁺ by Ga³⁺ as in Ca₁₄Zn_5.5Ga_10.5O_35.25. These oxygen atoms are introduced into the crystal structure of Ca₁₄Zn_5.5Ga_10.5O_35.25 only as a part of four tetrahedra (Zn, Ga)O₄ groups sharing common vertex. This creates a situation where even a minor change in the chemical composition leads to considerable anion and cation disordering resulting in a change of space group from F23 (no. 196) to F432 (no. 209).     

Structure and Ionic Conductivity of Bi6Cr2O15, a New Structure Type Containing (Bi12O14)n Columns and CrO4 Tetrahedra

Powder samples of the Cr⁶⁺-containing compound Bi₆Cr₂O₁₅ were prepared by solid state reaction of Bi₂O₃ and Cr₂O₃ in air at 650°C. The structure was solved and refined using high-resolution neutron powder diffraction data in space group Ccc2, with anisotropic thermal displacement parameters a=12.30184(5), b=19.87492(7), and c=5.88162(2) Å, V=1438.0 ų, and 126 variables to R_F=1.8%. Bi₆Cr₂O₁₅ exhibits a new structure type that contains (Bi₁₂O₁₄)⁸ⁿ⁺_n columns, of the kind previously found only for phases isotypic with Bi₁₃Mo₄VO₃₄. Each column is surrounded by eight CrO²⁻₄ tetrahedra. The ionic conductivity of Bi₆Cr₂O₁₅ was determined by impedance measurements to be 3.5×10⁻⁵ (Ω cm)⁻¹ at 600°C.     

Structure and properties of the CaFe2O4-type cobalt oxide CaCo2O4

The calcium cobalt oxide CaCo₂O₄ was synthesized for the first time and characterized from a powder X-ray diffraction study, measuring magnetic susceptibility, specific heat, electrical resistivity, and thermoelectric power. CaCo₂O₄ crystallizes in the CaFe₂O₄ (calcium ferrite)-type structure, consisting of an edge- and corner-shared CoO₆ octahedral network. The structure of CaCo₂O₄ belongs to an orthorhombic system (space group: Pnma) with lattice parameters, a=8.789(2) Å, b=2.9006(7) Å and c=10.282(3) Å. Curie-Weiss-like behavior in magnetic susceptibility with the nearly trivalent cobalt low-spin state (Co³⁺, 3d, S=0), semiconductor-like temperature dependence of resistivity (ρ=3×10⁻¹ Ω cm at 380 K) with dominant hopping conduction at low temperature, metallic-temperature-dependent large thermoelectric power (Seebeck coefficient: S=+147 μV/K at 380 K), and Schottky-type specific heat with a small Sommerfeld constant (γ=4.48(7) mJ/Co mol K²), were observed. These results suggest that the compound possesses a metallic electronic state with a small density of states at the Fermi level. The doped holes are localized at low temperatures due to disorder in the crystal. The carriers probably originate from slight off-stoichiometry of the phase. It was also found that S tends to increase even more beyond 380 K. The large S is possibly attributed to residual spin entropy and orbital degeneracy coupled with charges by strong electron correlation in the cobalt oxides.     

Superstructure of a phosphor material Ba3MgSi2O8 determined by neutron diffraction data

Ba₃MgSi₂O₈, a phosphor host examined for use in white-light devices and plant-growth lamps, was synthesized at 1225 °C in air. Its crystal structure has been determined and refined by a combined powder X-ray and neutron Rietveld method (, Z=3, a=9.72411(3) Å, c=7.27647(3) Å, V=595.870(5) Å³; R_p/R_wp=3.79%/5.03%, χ²=4.20). Superstructure reflections, observed only in the neutron diffraction data, provided the means to establish the true unit cell and a chemically reasonable structure. The structure contains three crystallographically distinct Ba atoms—Ba1 resides in a distorted octahedral site with S₆ () symmetry, Ba2 in a nine-coordinate site with C₃ (3) symmetry, and Ba3 in a ten-coordinate site with C₁ (1) symmetry. The Mg atoms occupy distorted octahedral sites, and the Si atom occupies a distorted tetrahedral site.     

The crystal chemistry of Bi6TP2O15+x, T=Fe, Ni, Zn: Isomorphism and polymorphism, structural relationship to Bi6TiP2O16

The crystal structures of compounds with nominal compositions Bi₆FeP₂O_15+x (I), Bi₆NiP₂O_15+x (II) and Bi₆ZnP₂O_15+x (III) were determined from single-crystal X-ray diffraction data. They are monoclinic, space group I2, Z=2. The lattice parameters for (I) are a=11.2644(7), b=5.4380(3), c=11.1440(5) Å, β=96.154(4)°; for (II) a=11.259(7), b=5.461(4), c=11.109(7) Å, β=96.65(1)°; for (III) a=19.7271(5), b=5.4376(2), c=16.9730(6) Å, β=131.932(1)°. Least squares refinements on F² converged for (I) to R1=0.0554, wR₂=0.1408; for (II) R₁=0.0647, wR₂=0.1697; for (III) R₁=0.0385, wR₂=0.1023. The crystals are complexly twinned by 2-fold rotation about , by inversion and by mirror reflection. The structures consist of edge-sharing articulations of OBi₄ tetrahedra forming layers in the a-c plane that then continue by edge-sharing parallel to the b-axis. The three-dimensional networks are bridged by Fe and Ni octahedra in (I) and (II) and by Zn trigonal bipyramids in (III) as well as by oxygen atoms of the PO₄ moieties. Bi also randomly occupies the octahedral sites. Oxygen vacancies exist in the structures of the three compounds due to required charge balances and they occur in the octahedral coordination polyhedron of the transition metal. In compound (III), no positional disorder in atomic sites is present. The Bi-O coordination polyhedra are trigonal prisms with one, two or three faces capped. Magnetic susceptibility data for compound (I) were obtained between 4.2 and 350 K. Between 4.2 and 250 K it is paramagnetic, μ_eff=6.1 μ_B; a magnetic transition occurs above 250 K.     

Crystal growth, structural characterization and magnetic properties of Ca3CuRhO6, Ca3Co1.34Rh0.66O6 and Ca3FeRhO6

Single crystals of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ were synthesized by high temperature flux growth in molten K₂CO₃ and structurally characterized by single crystal X-ray diffraction. While Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ crystallize with trigonal (rhombohedral) symmetry in the space group , Z=6: Ca₃Co_1.34Rh_0.66O₆a=9.161(1) Å, c=10.601(2) Å; Ca₃FeRhO₆a=9.1884(3) Å, c=10.7750(4) Å; Ca₃CuRhO₆ adopts a monoclinic distortion of the K₄CdCl₆ structure in the space group C2/c, Z=4: a=9.004(2) Å, b=9.218(2) Å, c=6.453(1) Å, β=91.672(5). All crystals of Ca₃CuRhO₆ examined were twinned by pseudo-merohedry. Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are structurally related and contain infinite one-dimensional chains of alternating face-sharing RhO₆ octahedra and MO₆ trigonal prisms. In the monoclinic modification, the copper atoms are displaced from the center of the trigonal prism toward one of the rectangular faces adopting a pseudo-square planar configuration. The magnetic properties of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are discussed.     

Structures of the reduced niobium oxides Nb12O29 and Nb22O54

The crystal structure of Nb₂₂O₅₄ is reported for the first time, and the structure of orthorhombic Nb₁₂O₂₉ is reexamined, resolving previous ambiguities. Single crystal X-ray and electron diffraction were employed. These compounds were found to crystallize in the space groups P2/m (, , , β=102.029(3)^°) and Cmcm (, , ), respectively and share a common structural unit, a 4×3 block of corner sharing NbO₆ octahedra. Despite different constraints imposed by symmetry these blocks are very similar in both compounds. Within a block, it is found that the niobium atoms are not located in the centers of the oxygen octahedra, but rather are displaced inward toward the center of the block forming an apparent antiferroelectric state. Bond valence sums and bond lengths do not show the presence of charge ordering, suggesting that all 4d electrons are delocalized in these compounds at the temperature studied, T=200 K.     

Syntheses, crystal structures and Raman spectra of Ba(BF4)(PF6), Ba(BF4)(AsF6) and Ba2(BF4)2(AsF6)(H3F4); the first examples of metal salts containing simultaneously tetrahedral BF4 and octahedral AF6 anions

In the system BaF₂/BF₃/PF₅/anhydrous hydrogen fluoride (aHF) a compound Ba(BF₄)(PF₆) was isolated and characterized by Raman spectroscopy and X-ray diffraction on the single crystal. Ba(BF₄)(PF₆) crystallizes in a hexagonal space group with a=10.2251(4) Å, c=6.1535(4) Å, V=557.17(5) Å³ at 200 K, and Z=3. Both crystallographically independent Ba atoms possess coordination polyhedra in the shape of tri-capped trigonal prisms, which include F atoms from BF₄⁻ and PF₆⁻ anions. In the analogous system with AsF₅ instead of PF₅ the compound Ba(BF₄)(AsF₆) was isolated and characterized. It crystallizes in an orthorhombic Pnma space group with a=10.415(2) Å, b=6.325(3) Å, c=11.8297(17) Å, V=779.3(4) Å³ at 200 K, and Z=4. The coordination around Ba atom is in the shape of slightly distorted tri-capped trigonal prism which includes five F atoms from AsF₆⁻ and four F atoms from BF₄⁻ anions. When the system BaF₂/BF₃/AsF₅/aHF is made basic with an extra addition of BaF₂, the compound Ba₂(BF₄)₂(AsF₆)(H₃F₄) was obtained. It crystallizes in a hexagonal P6₃/mmc space group with a=6.8709(9) Å, c=17.327(8) Å, V=708.4(4) Å³ at 200 K, and Z=2. The barium environment in the shape of tetra-capped distorted trigonal prism involves 10 F atoms from four BF₄⁻, three AsF₆⁻ and three H₃F₄⁻ anions. All F atoms, except the central atom in H₃F₄ moiety, act as μ₂-bridges yielding a complex 3-D structural network.     

Sr4PbPt4O11, the first platinum oxide containing Pt2 ions

We report the synthesis and crystal structure of the new compound Sr₄PbPt₄O₁₁, containing platinum in highly unusual square pyramidal coordination. The crystals were obtained in molten lead oxide. The structure was solved by X-ray single crystal diffraction techniques on a twinned sample, the final R factors are R=0.0260 and wR=0.0262. The symmetry is triclinic, space group P1¯, with , , , α=90.421(3)°, β=89.773(8)°, γ=90.140(9)° and Z=2. The structure is built from dumbell-shaped Pt₂O₉ entities formed by a dinuclear metal-metal bonded Pt₂⁶⁺ ion with asymmetric environments of the two Pt atoms, classical PtO₄ square plane and unusual PtO₅ square pyramid. Successive Pt₂O₉ entities deduced from 90° rotations are connected through the oxygens of the PtO₄ basal squares to form [Pt₄O₁₀⁸⁻]_∞ columns further connected through Pb²⁺ and Sr²⁺ ions. Raman spectroscopy confirmed the peculiar platinum coordination environment.     

Crystal structure and phonon properties of noncentrosymmetric LiNaB4O7

A new borate, LiNaB₄O₇, has been synthesized and characterized by single-crystal X-ray structure determination. The material crystallizes in the orthorhombic system, noncentrosymmetric space group Fdd2, with unit cell dimensions a=13.325(2), b=14.099(2), c=10.243(2) Å, Z=16, and V=1924.3(7) Å³. Like Li₂B₄O₇, the structure is built of two symmetrically independent, interpenetrating polyanionic frameworks built from condensation of the B₄O₉ fundamental building block, which is comprised of two distorted BO₄ tetrahedra and two BO₃ triangles. The interpenetrating frameworks produce distinct tunnels that are selectively occupied by the Li and Na atoms. Large single crystals exhibiting an optical absorption edge with λ<180 nm have been grown via the top-seeded-solution-growth method. The SHG signal (0.15× potassium dihydrogen phosphate (KDP)) is consistent with the calculated components of the SHG tensor and the approximate centrosymmetric disposition of the independent and interpenetrating frameworks. A complete analysis of polarized IR and Raman spectra confirms a close relationship between the title compound and Li₂B₄O₇.     

The disordered cubic structure of Ca7Co3Ga5O18

The new mixed oxide having composition close to Ca₇Co₃Ga₅O₁₈ was synthesized from CaCO₃, Co₃O₄ and Ga₂O₃ at 1150 °C in air and studied by neutron and synchrotron X-ray powder diffraction, selected-area electron diffraction and high-resolution electron microscopy. The structure was refined, using time-of-flight (TOF) neutron powder diffraction data, in space group F432, with and Z=8, to R_F=0.7%. It is considerably disordered, with four different tetrahedral sites randomly occupied by Co and Ga atoms at a ratio of 1:2. The tetrahedra form a disordered (Co_1/3Ga_2/3)O₂ 3D-framework inside which isolated CoO₆ octahedra, surrounded by 8 Ca atoms, are located. The structure is related to the ordered structure of Ca₁₄Al₁₀Zn₆O₃₅. Electron diffraction patterns confirmed the symmetry and unit cell and revealed no diffuse scattering. High-resolution electron microscopy images showed the absence of extended structural defects.     

Structural studies on a high-pressure polymorph of NaYSi2O6

High-pressure synthesis experiments in the system Na₂O-Y₂O₃-SiO₂ revealed the existence of a previously unknown polymorph of NaYSi₂O₆ or Na₃Y₃[Si₃O₉]₂ which was quenched from 3.0 GPa and 1000 °C. Structural investigations on this modification have been performed using single-crystal X-ray diffraction data collected at ambient conditions. Furthermore, unpolarized micro-Raman spectra have been obtained from single-crystal material. The high-P modification of NaYSi₂O₆ crystallizes in the centrosymmetric space group C2/c with 12 formula units per cell (a=8.2131(9) Å, b=10.3983(14) Å, c=17.6542(21) Å, β=100.804(9)°, V=1481.0(3) Å³, R(|F|)=0.033 for 1142 independent observed reflections) and belongs to the group of cyclo-silicates. Basic building units are isolated three-membered [Si₃O₉] rings located in layers parallel to (010). Within a single layer the rings are concentrated in strings parallel to [100]. The sequence of directedness of up (U) or down (D) pointing tetrahedra of a single ring is UUU or DDD, respectively. Stacking of the layers parallel to b results in the formation of a three-dimensional structure in which yttrium and sodium cations are incorporated for charge compensation. In more detail, four non-tetrahedral cation positions can be differentiated which are coordinated by 6 and 8 oxygen ligands. Refinements of the site occupancies did not reveal any indication for mixed Na-Y populations on these positions. Finally, several geometrical parameters of rings occurring in cyclo-trisilicate structures have been compiled and are discussed.