Synthesis, structure and physical properties of the new Zintl phases Eu11Zn6Sb12 and Eu11Cd6Sb12

Reported are the syntheses, crystal structure determinations from single-crystal X-ray diffraction, and magnetic properties of two new ternary compounds, Eu₁₁Cd₆Sb₁₂ and Eu₁₁Zn₆Sb₁₂. Both crystallize with the complex Sr₁₁Cd₆Sb₁₂ structure type—monoclinic, space group C2/m (no. 12), Z=2, with unit cell parameters a=31.979(4) Å, b=4.5981(5) Å, c=12.3499(14) Å, β=109.675(1)° for Eu₁₁Zn₆Sb₁₂, and a=32.507(2) Å, b=4.7294(3) Å, c=12.4158(8) Å, β=109.972(1)° for Eu₁₁Cd₆Sb₁₂. Their crystal structures are best described as made up of polyanionic and ribbons of corner-shared ZnSb₄ and CdSb₄ tetrahedra and Eu²⁺ cations. A notable characteristic of these structures is the presence of Sb-Sb interactions, which exist between two tetrahedra from adjacent layers, giving rise to unique channels. Detailed structure analyses shows that similar bonding arrangements are seen in much simpler structure types, such as Ca₃AlAs₃ and Ca₅Ga₂As₆ and the structure can be rationalized as their intergrowth. Temperature-dependent magnetization measurements indicate that Eu₁₁Cd₆Sb₁₂ orders anti-ferromagnetically below 7.5 K, while Eu₁₁Zn₆Sb₁₂ does not order down to 5 K. Resistivity measurements confirm that Eu₁₁Cd₆Sb₁₂ is poorly metallic, as expected for a Zintl phase.     

Sn4As3 revisited: Solvothermal synthesis and crystal and electronic structure

A facile one pot method of synthesis of tin arsenide Sn₄As₃ starting from metallic tin and elemental arsenic under mild solvothermal conditions in ethylenediamine in the presence of ammonium chloride is offered. The dissolving of the tin metal in ethylenediamine and the role of NH₄Cl are discussed. The crystal structure of Sn₄As₃ has been re-determined. It is shown to crystallize in the trigonal non-centrosymmetric space group R3m, (a=4.089(1) Å, c=36.059(6) Å, Z=3), which differs from the previously reported centrosymmetric structure . The crystal structure of Sn₄As₃ consists of alternating layers of arsenic and tin atoms that are combined into seven-layer blocks and build up along the c-axis. The major structural feature is the short tin-tin distances (3.24 Å) between the adjacent blocks. The analysis of the density of states and band structure reveals that Sn₄As₃ should have metallic properties, which is in line with the previously reported experimental observations. Analysis of chemical bonding employing the electron localization function shows that only for the shortest Sn-As contacts the bonding is pairwise, while four-center bonds are formed between arsenic and tin atoms at relatively long distances (>2.85 Å). Moreover, each tin atom holds an electron lone-pair.     

Superstructure of a phosphor material Ba3MgSi2O8 determined by neutron diffraction data

Ba₃MgSi₂O₈, a phosphor host examined for use in white-light devices and plant-growth lamps, was synthesized at 1225 °C in air. Its crystal structure has been determined and refined by a combined powder X-ray and neutron Rietveld method (, Z=3, a=9.72411(3) Å, c=7.27647(3) Å, V=595.870(5) Å³; R_p/R_wp=3.79%/5.03%, χ²=4.20). Superstructure reflections, observed only in the neutron diffraction data, provided the means to establish the true unit cell and a chemically reasonable structure. The structure contains three crystallographically distinct Ba atoms—Ba1 resides in a distorted octahedral site with S₆ () symmetry, Ba2 in a nine-coordinate site with C₃ (3) symmetry, and Ba3 in a ten-coordinate site with C₁ (1) symmetry. The Mg atoms occupy distorted octahedral sites, and the Si atom occupies a distorted tetrahedral site.     

Syntheses, crystal structures and Raman spectra of Ba(BF4)(PF6), Ba(BF4)(AsF6) and Ba2(BF4)2(AsF6)(H3F4); the first examples of metal salts containing simultaneously tetrahedral BF4 and octahedral AF6 anions

In the system BaF₂/BF₃/PF₅/anhydrous hydrogen fluoride (aHF) a compound Ba(BF₄)(PF₆) was isolated and characterized by Raman spectroscopy and X-ray diffraction on the single crystal. Ba(BF₄)(PF₆) crystallizes in a hexagonal space group with a=10.2251(4) Å, c=6.1535(4) Å, V=557.17(5) Å³ at 200 K, and Z=3. Both crystallographically independent Ba atoms possess coordination polyhedra in the shape of tri-capped trigonal prisms, which include F atoms from BF₄⁻ and PF₆⁻ anions. In the analogous system with AsF₅ instead of PF₅ the compound Ba(BF₄)(AsF₆) was isolated and characterized. It crystallizes in an orthorhombic Pnma space group with a=10.415(2) Å, b=6.325(3) Å, c=11.8297(17) Å, V=779.3(4) Å³ at 200 K, and Z=4. The coordination around Ba atom is in the shape of slightly distorted tri-capped trigonal prism which includes five F atoms from AsF₆⁻ and four F atoms from BF₄⁻ anions. When the system BaF₂/BF₃/AsF₅/aHF is made basic with an extra addition of BaF₂, the compound Ba₂(BF₄)₂(AsF₆)(H₃F₄) was obtained. It crystallizes in a hexagonal P6₃/mmc space group with a=6.8709(9) Å, c=17.327(8) Å, V=708.4(4) Å³ at 200 K, and Z=2. The barium environment in the shape of tetra-capped distorted trigonal prism involves 10 F atoms from four BF₄⁻, three AsF₆⁻ and three H₃F₄⁻ anions. All F atoms, except the central atom in H₃F₄ moiety, act as μ₂-bridges yielding a complex 3-D structural network.     

The structural investigation of Ba4Bi3F17

The anion-excess ordered fluorite-related phase Ba₄Bi₃F₁₇ has been synthesized by a solid state reaction of BaF₂ and BiF₃ at 873 K. The crystal structure of Ba₄Bi₃F₁₇ has been studied using electron diffraction and X-ray powder diffraction (a=11.2300(2) Å, c=20.7766(5) Å, S.G. , R_I=0.020, R_P=0.036). Interstitial fluorine atoms in the Ba₄Bi₃F₁₇ structure are considered to form isolated cuboctahedral 8 : 12 : 1 clusters. The structural relationship between Ba₄Bi₃F₁₇ and similar rare-earth-based phases is discussed.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Crystal growth, structural characterization and magnetic properties of Ca3CuRhO6, Ca3Co1.34Rh0.66O6 and Ca3FeRhO6

Single crystals of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ were synthesized by high temperature flux growth in molten K₂CO₃ and structurally characterized by single crystal X-ray diffraction. While Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ crystallize with trigonal (rhombohedral) symmetry in the space group , Z=6: Ca₃Co_1.34Rh_0.66O₆a=9.161(1) Å, c=10.601(2) Å; Ca₃FeRhO₆a=9.1884(3) Å, c=10.7750(4) Å; Ca₃CuRhO₆ adopts a monoclinic distortion of the K₄CdCl₆ structure in the space group C2/c, Z=4: a=9.004(2) Å, b=9.218(2) Å, c=6.453(1) Å, β=91.672(5). All crystals of Ca₃CuRhO₆ examined were twinned by pseudo-merohedry. Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are structurally related and contain infinite one-dimensional chains of alternating face-sharing RhO₆ octahedra and MO₆ trigonal prisms. In the monoclinic modification, the copper atoms are displaced from the center of the trigonal prism toward one of the rectangular faces adopting a pseudo-square planar configuration. The magnetic properties of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are discussed.     

The synthesis and structural characterization of the new ternary nitrides: Ca4TiN4 and Ca5NbN5

The ternary nitrides, Ca₄TiN₄ and Ca₅NbN₅, were synthesized in sealed niobium tubes using lithium nitride as a flux at 900 and 1050 °C, respectively. The structures of both compounds were solved from single-crystal X-ray diffraction data. Ca₄TiN₄ is the first example of a calcium group IV nitride; it crystallizes in the triclinic space group (No. 2) with cell parameters a=5.9757(5) Å, b=6.0129(5) Å, c=6.0116(12) Å, α=71.565(4)°, β=79.471(4)°, γ=68.258(4)° and Z=2. Ca₄TiN₄ is isostructural with Na₄TiO₄ and contains tetrahedral TiN₄ units connected through edges and corners to CaN₄ tetrahedra and CaN₅ square pyramids. Ca₅NbN₅ crystallizes in the monoclinic space group C2/m (No. 12) with cell parameters a=11.922(7) Å, b=6.878(5) Å, c=8.936(7) Å, β=101.22(3)° and Z=4. Ca₅NbN₅ is isostructural with Ba₅NbN₅; the structure contains NbN₄ tetrahedra that share vertices with CaN₅ trigonal bipyramids.     

The mercury chromates Hg6Cr2O9 and Hg6Cr2O10—Preparation and crystal structures, and thermal behaviour of Hg6Cr2O9

The basic mercury(I) chromate(VI), Hg₆Cr₂O₉ (=2Hg₂CrO₄·Hg₂O), has been obtained under hydrothermal conditions (200 °C, 5 days) in the form of orange needles as a by-product from reacting elemental mercury and K₂Cr₂O₇. Hydrothermal treatment of microcrystalline Hg₆Cr₂O₉ in demineralised water at 200 °C for 3 days led to crystal growth of red crystals of the basic mercury(I, II) chromate(VI), Hg₆Cr₂O₁₀ (=2Hg₂CrO₄·2HgO). The crystal structures were solved and refined from single crystal X-ray data sets. Hg₆Cr₂O₉: space group P2₁2₁2₁, Z=4, a=7.3573(12), b=8.0336(13), , 3492 structure factors, 109 parameters, R[F²>2σ(F²)]=0.0371, wR(F² all)=0.0517; Hg₆Cr₂O₁₀: space group Pca2₁, Z=4, a=11.4745(15), b=9.4359(12), , 3249 structure factors, 114 parameters, R[F²>2σ(F²)]=0.0398, wR(F² all)=0.0625. Both crystal structures are made up of an intricate mercury-oxygen network, subdivided into single building blocks [O-Hg-Hg-O] for the mercurous compound, and [O-Hg-Hg-O] and [O-Hg-O] for the mixed-valent compound. Hg₆Cr₂O₉ contains three different Hg₂²⁺ dumbbells, whereas Hg₆Cr₂O₁₀ contains two different Hg₂²⁺ dumbbells and two Hg²⁺ cations. The Hg^I-Hg^I distances are characteristic and range between 2.5031(15) and 2.5286(9) Å. All Hg₂²⁺ groups exhibit an unsymmetrical oxygen environment. The oxygen coordination of the Hg²⁺ cations is nearly linear with two tightly bonded O atoms at distances around 2.07 Å. For both structures, the chromate(VI) anions reside in the vacancies of the Hg-O network and deviate only slightly from the ideal tetrahedral geometry with average Cr-O distances of ca. 1.66 Å. Upon heating at temperatures above 385 °C, Hg₆Cr₂O₉ decomposes in a four-step mechanism with Cr₂O₃ as the end-product at temperatures above 620 °C.     

Synthesis, structure, and magnetism of Tb4PdGa12 and Tb4PtGa12

Single crystals of Tb₄MGa₁₂ (M=Pd, Pt) have been synthesized. The isostructural compounds crystallize in the cubic space group , with Z=2 and lattice parameters: a=8.5940(5) and 8.5850(3) Å for Tb₄PdGa₁₂ and Tb₄PtGa₁₂, respectively. The crystal structure consists of corner-sharing MGa₆ octahedra and TbGa₃ cuboctahedra. Magnetic measurements suggest that Tb₄PdGa₁₂ is an antiferromagnetic metamagnet with a Néel temperature of 16 K, while the Pt analog orders at T_N=12 K.     

Subsolidus phase relations and crystal structures of the mixed-oxide phases in the In2O3-WO3 system

Subsolidus phase relationships in the In₂O₃-WO₃ system at 800-1400°C were investigated using X-ray diffraction. Two binary-oxide phases—In₆WO₁₂ and In₂(WO₄)₃—were found to be stable over the range 800-1200°C. Heating the binary-oxide phases above 1200°C resulted in the preferential volatilization of WO₃. Rietveld refinement was performed on three structures using X-ray diffraction data from nominally phase-pure In₆WO₁₂ at room temperature and from nominally phase-pure In₂(WO₄)₃ at 225°C and 310°C. The indium-rich phase, In₆WO₁₂, is rhombohedral, space group (rhombohedral), with Z=1, a=6.22390(4) Å, α=99.0338(2)° [hexagonal axes: a_H=9.48298(6) Å, c=8.94276(6) Å, a_H/c=0.9430(9)]. In₆WO₁₂ can be viewed as an anion-deficient fluorite structure in which 1/7 of the fluorite anion sites are vacant. Indium tungstate, In₂(WO₄)₃, undergoes a monoclinic-orthorhombic transition around 250°C. The high-temperature polymorph is orthorhombic, space group Pnca, with a=9.7126(5) Å, b=13.3824(7) Å, c=9.6141(5) Å, and Z=4. The low-temperature polymorph is monoclinic, space group P2₁/a, with a=16.406(2) Å, b=9.9663(1) Å, c=19.099(2) Å, β=125.411(2)°, and Z=8. The structures of the two In₂(WO₄)₃ polymorphs are similar, consisting of a network of corner sharing InO₆ octahedra and WO₄ tetrahedra.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

The crystal structure determinations and refinements of K2S2O7, KNaS2O7 and Na2S2O7 from X-ray powder and single crystal diffraction data

The crystal structures of K₂S₂O₇, KNaS₂O₇ and Na₂S₂O₇ have been solved and/or refined from X-ray synchrotron powder diffraction data and conventional single-crystal data. K₂S₂O₇: From powder diffraction data, monoclinic C2/c, Z=4, a=12.3653(2), b=7.3122(1), , β=93.0792(7)°, R_Bragg=0.096. KNaS₂O₇: From powder diffraction data; triclinic , Z=2, a=5.90476(9), b=7.2008(1), , α=101.7074(9), β=90.6960(7), γ=94.2403(9)°, R_Bragg=0.075. Na₂S₂O₇: From single-crystal data; triclinic , Z=2, a=6.7702(9), b=6.7975(10), , α=116.779(2), β=96.089(3), γ=84.000(3)°, R_F=0.033. The disulphate anions are essentially eclipsed. All three structures can be described as dichromate-like, where the alkali cations coordinate oxygens of the isolated disulphate groups in three-dimensional networks. The K-O and Na-O coordinations were determined from electron density topology and coordination geometry. The three structures have a cation-disulphate chain in common. In K₂S₂O₇ and Na₂S₂O₇ the neighbouring chains are antiparallel, while in KNaS₂O₇ the chains are parallel. The differences between the K₂S₂O₇ and Na₂S₂O₇ structures, with double-, respectively single-sided chain connections and straight, respectively, corrugated structural layers can be understood in terms of the differences in size and coordinating ability of the cations.     

Structure and properties of the CaFe2O4-type cobalt oxide CaCo2O4

The calcium cobalt oxide CaCo₂O₄ was synthesized for the first time and characterized from a powder X-ray diffraction study, measuring magnetic susceptibility, specific heat, electrical resistivity, and thermoelectric power. CaCo₂O₄ crystallizes in the CaFe₂O₄ (calcium ferrite)-type structure, consisting of an edge- and corner-shared CoO₆ octahedral network. The structure of CaCo₂O₄ belongs to an orthorhombic system (space group: Pnma) with lattice parameters, a=8.789(2) Å, b=2.9006(7) Å and c=10.282(3) Å. Curie-Weiss-like behavior in magnetic susceptibility with the nearly trivalent cobalt low-spin state (Co³⁺, 3d, S=0), semiconductor-like temperature dependence of resistivity (ρ=3×10⁻¹ Ω cm at 380 K) with dominant hopping conduction at low temperature, metallic-temperature-dependent large thermoelectric power (Seebeck coefficient: S=+147 μV/K at 380 K), and Schottky-type specific heat with a small Sommerfeld constant (γ=4.48(7) mJ/Co mol K²), were observed. These results suggest that the compound possesses a metallic electronic state with a small density of states at the Fermi level. The doped holes are localized at low temperatures due to disorder in the crystal. The carriers probably originate from slight off-stoichiometry of the phase. It was also found that S tends to increase even more beyond 380 K. The large S is possibly attributed to residual spin entropy and orbital degeneracy coupled with charges by strong electron correlation in the cobalt oxides.     

A new structure type of phosphate: Crystal structure of Na2Zn5(PO4)4

A new compound, Na₂Zn₅(PO₄)₄, was identified in the system ZnONa₂OP₂O₅ and high-quality crystal was obtained by the melt method. The crystal structure of this compound was solved by direct method from single crystal X-ray diffraction data. The structure was then refined anisotropically using a full-matrix least square refinement on F² and the refinement converged to R₁=0.0233 and wR₂=0.0544. This compound crystallizes in the orthorhombic system with space group Pbcn, lattice parameters a=10.381(2) Å, b=8.507(1) Å, c=16.568(3) Å and Z=4. The structure is made up of 3D [Zn₅P₄O₁₆]_n²ⁿ⁻ covalent framework consisting of [Zn₄P₄O₁₆]_n⁴ⁿ⁻ layers. The powder diffraction pattern of Na₉Zn₂₁(PO₄)₁₇ is explained by simulating a theoretical pattern with NaZnPO₄ and Na₂Zn₅(PO₄)₄ in the molar ratio of 1:4 and then by Rietveld refinement of experimental pattern. Na₂Zn₅(PO₄)₄ melts congruently at 855 °C and its conductivity is 5.63×10⁻⁹ S/cm.     

Synthesis, crystal structure, infrared and Raman spectra of Sr5(As2O7)2(AsO3OH)

The new compound Sr₅(As₂O₇)₂(AsO₃OH) was synthesized under hydrothermal conditions. It represents a previously unknown structure type and belongs to a group of a few compounds in the system SrO-As₂O₅-H₂O; (As₂O₇)⁴⁻ besides (AsO₃OH)²⁻ groups have not been described yet. The crystal structure of Sr₅(As₂O₇)₂(AsO₃OH) was determined by single-crystal X-ray diffraction (space group P2₁/n, a=7.146(1), b=7.142(1), , β=93.67(3)°, , Z=4). One of the five symmetrically unique Sr atoms is in a trigonal antiprismatic (Inorg. Chem. 35 (1996) 4708)—coordination, whereas the other Sr atoms adopt the commonly observed (“Collect” data collection software, Delft, The Netherlands, 1999; Methods Enzymol. 276 (1997) 307)—coordination. The position of the hydrogen atom was located in a difference Fourier map and subsequently refined with an isotropic displacement parameter. Worth mentioning is the very short hydrogen bond length O_h-H?O(1) of 2.494(4) Å; it belongs to the shortest known examples where the donor and acceptor atoms are crystallographically different. This hydrogen bond was confirmed by IR spectroscopy. In addition, Raman spectra were collected in order to study the arsenate groups.     

Synthesis, crystal structure and optical properties of BiMgVO5

The new vanadate BiMgVO₅ has been prepared and its structure has been determined by single crystal X-ray diffraction: space group P2₁/n, , , , β=107.38(5)°, wR₂=0.0447, R=0.0255. The structure consists of [Mg₂O₁₀] and [Bi₂O₁₀] dimers sharing their corners with [VO₄] tetrahedra. The ranges of bond lengths are 2.129-2.814 Å for Bi-O; 2.035-2.167 Å for Mg-O and 1.684-1.745 Å for V-O. V-O bond lengths determined from Raman band wavenumbers are between 1.679 and 1.747 Å. An emission band overlapping the entire visible region with a maximum around 650 nm is observed.     

Crystal structure and phonon properties of noncentrosymmetric LiNaB4O7

A new borate, LiNaB₄O₇, has been synthesized and characterized by single-crystal X-ray structure determination. The material crystallizes in the orthorhombic system, noncentrosymmetric space group Fdd2, with unit cell dimensions a=13.325(2), b=14.099(2), c=10.243(2) Å, Z=16, and V=1924.3(7) Å³. Like Li₂B₄O₇, the structure is built of two symmetrically independent, interpenetrating polyanionic frameworks built from condensation of the B₄O₉ fundamental building block, which is comprised of two distorted BO₄ tetrahedra and two BO₃ triangles. The interpenetrating frameworks produce distinct tunnels that are selectively occupied by the Li and Na atoms. Large single crystals exhibiting an optical absorption edge with λ<180 nm have been grown via the top-seeded-solution-growth method. The SHG signal (0.15× potassium dihydrogen phosphate (KDP)) is consistent with the calculated components of the SHG tensor and the approximate centrosymmetric disposition of the independent and interpenetrating frameworks. A complete analysis of polarized IR and Raman spectra confirms a close relationship between the title compound and Li₂B₄O₇.     

Phase transitions in K3AlF6

Phase transitions in the elpasolite-type K₃AlF₆ complex fluoride were investigated using differential scanning calorimetry, electron diffraction and X-ray powder diffraction. Three phase transitions were identified with critical temperatures , and . The α-K₃AlF₆ phase is stable below T₁ and crystallizes in a monoclinic unit cell with a=18.8588(2)Å, b=34.0278(2)Å, c=18.9231(1)Å, β=90.453(1)° (a=2a_c−c_c, b=4b_c, c=a_c+2c_c; a_c, b_c, c_c—the basic lattice vectors of the face-centered cubic elpasolite structure) and space group I2/a or Ia. The intermediate β phase exists only in very narrow temperature interval between T₁ and T₂. The γ polymorph is stable in the T₂<T<T₃ temperature range and has an orthorhombic unit cell with a=36.1229(6)Å, b=17.1114(3)Å, c=12.0502(3)Å (a=3a_c−3c_c, b=2b_c, c=a_c+c_c) at 250 °C and space group Fddd. Above T₃ the cubic δ polymorph forms with a_c=8.5786(4)Å at 400 °C and space group . The similarity between the K₃AlF₆ and K₃MoO₃F₃ compounds is discussed.