L-Dopa Synthesis on Conducting Polymers

With regards to the synthesis of L-Dopa (l-3,4-dihydroxy phenylalanine) two types of biosensors were designed by immobilizing tyrosinase on conducting polymers; polypyrrole (PPy) and poly(3,4-ethylenedioxythiophene) (PEDOT). PPy and PEDOT were synthesized electrochemically and tyrosinase immobilized by entrapment during electropolymerization. The kinetic parameters of the designed biosensors, maximum reaction rate of the enzyme (V_max) and Michaelis Menten constant (K_m) were determined. V_max were found as 0.013 for PPy matrix and 0.041 μ mol/min.electrode for PEDOT matrix. K_m values were determined as 3.7 and 5.2mM for PPy and PEDOT matrices respectively. Calibration curves for enzyme activity vs. substrate concentration were drawn for the range of 0.8 to 2.5 mM L-Tyrosine. Optimum temperature and pH, operational and shelf life stabilities of immobilized enzyme were also examined.     

Poly(pyrrole) versus poly(3,4-ethylenedioxythiophene): amperometric cholesterol biosensor matrices

Two conducting polymers, poly(pyrrole) (PPy) and poly(3,4-ethylenedioxythiophene) (PEDOT) were used as immobilization matrices for cholesterol oxidase (ChOx). The amperometric responses of the enzyme electrodes were measured by monitoring oxidation current of H₂O₂ at +0.7 V in the absence of a mediator. Kinetic parameters, such as K _m and I _max, operational and storage stabilities, effects of pH and temperature were determined for both entrapment supports. K _m values are found as 7.9 and 1.3 mM for PPy and PEDOT enzyme electrodes, respectively; it can be interpreted that ChOx immobilized in PEDOT shows higher affinity towards the substrate.     

Potentiometric Ag+ Sensors Based on Conducting Polymers: A Comparison between Poly(3,4‐ethylenedioxythiophene) and Polypyrrole Doped with Sulfonated Calixarenes

Potentiometric Ag⁺ sensors were prepared by galvanostatic electropolymerization of 3,4‐ethylenedioxythiophene (EDOT) and pyrrole (Py) on glassy carbon electrodes by using sulfonated calixarenes as doping ions. Poly(3,4‐ethylenedioxythiophene) (PEDOT) and polypyrrole (PPy) doped with p‐sulfonic calix[4]arene (C4S), p‐sulfonic calix[6]arene (C6S) and p‐sulfonic calix[8]arene (C8S) were compared. PEDOT and PPy doped with poly(styrene sulfonate) (PSS) were also included for comparison. The analytical performance of the conducting polymer‐based Ag⁺ sensors was studied by potentiometric measurements. All conducting polymer and dopant combinations showed sensitivity and selectivity to Ag⁺ compared to several alkali, alkaline‐earth, and transition‐metal cations. The type of the conducting polymer used for the fabrication of the electrodes was found to have a more significant effect on the selectivity of the electrodes to Ag⁺ than the ring size of the sulfonated calixarenes used as dopants. Selected conducting polymer‐based sensors were studied by cyclic voltammetry (CV) and energy dispersive analysis of X‐rays (EDAX) measurements. Results from the EDAX measurements show that both PEDOT‐ and PPy‐based membranes accumulate silver.     

Patterning of conducting polymers using charged self-assembled monolayers

We introduce a new approach to pattern conducting polymers by combining oppositely charged conducting polymers on charged self-assembled monolayers (SAMs). The polymer resist pattern behaves as a physical barrier, preventing the formation of SAMs. The patterning processes were carried out using commercially available conducting polymers: a negatively charged PEDOT/PSS (poly(3,4-ethylene-dioxythiophene)/poly(4-stylenesulphonic acid)) and a positively charged polypyrrole (PPy). A bifunctional NH 2 (positively charged) or COOH (negatively charged) terminated alkane thiol or silane was directly self-assembled on a substrate (Au or SiO 2). A suspension of the conducting polymers (PEDOT/PSS and PPy) was then spin-coated on the top surface of the SAMs and allowed to adsorb on the oppositely charged SAMs via an electrostatic driving force. After lift-off of the polymer resist, i.e., poly(methyl methacrylate, PMMA), using acetone, the conducting polymers remained on the charged SAMs surface. Optical microscopy, Auger electron spectroscopy, and atomic force microscopy reveal that the prepared nanolines have low line edge roughness and high line width resolution. Thus, conducting polymer patterns with high resolution could be produced by simply employing charged bifunctional SAMs. It is anticipated that this versatile new method can be applied to device fabrication processes of various nano- and microelectronics.     

Charge transport and structure in semimetallic polymers

Owing to changes in their chemistry and structure, polymers can be fabricated to demonstrate vastly different electrical conductivities over many orders of magnitude. At the high end of conductivity is the class of conducting polymers, which are ideal candidates for many applications in low‐cost electronics. Here, we report the influence of the nature of the doping anion at high doping levels within the semi‐metallic conducting polymer poly(3,4‐ethylenedioxythiophene) (PEDOT) on its electronic transport properties. Hall effect measurements on a variety of PEDOT samples show that the choice of doping anion can lead to an order of magnitude enhancement in the charge carrier mobility > 3 cm²/Vs at conductivities approaching 3000 S/cm under ambient conditions. Grazing Incidence Wide Angle X‐ray Scattering, Density Functional Theory calculations, and Molecular Dynamics simulations indicate that the chosen doping anion modifies the way PEDOT chains stack together. This link between structure and specific anion doping at high doping levels has ramifications for the fabrication of conducting polymer‐based devices. © 2017 The Authors. Journal of Polymer Science Part B: Polymer Physics Published by Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2018 , 56, 97–104     

导电聚合物的电化学制备和电化学性质研究——中国科学院有机固体重点实验室导电聚合物电化学研究工作简介(I)

简要介绍本研究组自上世纪80年代以来在导电聚合物的电化学制备和电化学性质研究中取得的一些主要成果,包括吡咯电化学聚合条件的影响、电化学聚合反应机理及其反应动力学、导电聚吡咯的两种掺杂结构及其两步电化学氧化还原过程和电化学过氧化的机理、导电聚苯胺的电化学性质、导电聚合物稳定性的电化学解释等等.     

Gradient doping of conducting polymer films by means of bipolar electrochemistry

In this paper, we report a novel electrochemical doping method for conducting polymer films based on bipolar electrochemistry. The electrochemical doping of conducting polymers such as poly(3-methylthiophene) (PMT), poly(3,4-ethylenedioxythiophene) (PEDOT), and poly(aniline) (PANI) on a bipolar electrode having a potential gradient on its surface successfully created gradually doped materials. In the case of PEDOT film, the color change at the anodic side was also observed to be gradually transparent. PANI film treated by the bipolar doping gave a multicolored gradation across the film. The results of UV-vis and energy dispersive X-ray analyses for the doped films supported the distribution of dopants in the polymer films reflecting the potential gradient on the bipolar electrode. Furthermore, the reversibility of the bipolar doping of the PMT film was demonstrated by a spectroelectrochemical investigation.     

Imparting Multifunctionality by Utilizing Biporosity in a Zirconium‐Based Metal–Organic Framework

In this work, we have synthesized nanocomposites made up of a metal–organic framework (MOF) and conducting polymers by polymerization of specialty monomers such as pyrrole (Py) and 3,4‐ethylenedioxythiophene (EDOT) in the voids of a stable and biporous Zr‐based MOF ( UiO‐66 ). FTIR and Raman data confirmed the presence of polypyrrole ( PPy ) and poly3,4‐ethylenedioxythiophene ( PEDOT ) in UiO‐66‐PPy and UiO‐66‐PEDOT nanocomposites, respectively, and PXRD data revealed successful retention of the structure of the MOF. HRTEM images showed successful incorporation of polymer fibers inside the voids of the framework. Owing to the intrinsic biporosity of UiO‐66 , polymer chains were observed to selectively occupy only one of the voids. This resulted in a remarkable enhancement (million‐fold) of the electrical conductivity while the nanocomposites retain 60–70 % of the porosity of the original MOF. These semiconducting yet significantly porous MOF nanocomposite systems exhibited ultralow thermal conductivity. Enhanced electrical conductivity with lowered thermal conductivity could qualify such MOF nanocomposites for thermoelectric applications.     

All-solid-state reference electrodes based on conducting polymers

A novel construction of solution free (pseudo)reference electrodes, compatible with all-solid-state potentiometric indicator electrodes, has been proposed. These electrodes use conducting polymers (CP): polypyrrole (PPy) or poly(3,4-ethylenedioxythiophene) (PEDOT). Two different arrangements have been tested: solely based on CP and those where the CP phase is covered with a poly(vinyl chloride) based outer membrane of tailored composition. The former arrangement was designed to suppress or compensate cation- and anion-exchange, using mobile perchlorate ions and poly(4-styrenesulfonate) or dodecylbenzenesulfonate anions as immobilized dopants. The following systems were used: (i) polypyrrole layers doped simultaneously by two kinds of anions, both mobile and immobilized in the polymer layer; (ii) bilayers of polypyrrole with anion exchanging inner layer and cation-exchanging outer layer; (iii) polypyrrole doped by surfactant dodecylbenzenesulfonate ions, which inhibit ion exchange on the polymer/solution interface. For the above systems, recorded potentials have been found to be practically independent of electrolyte concentration. The best results, profound stability of potentials, have been obtained for poly(3,4-ethylenedioxythiophene) or polypyrrole doped by poly(4-styrenesulfonate) anions covered by a poly(vinyl chloride) based membrane, containing both anion- and cation-exchangers as well as solid potassium chloride and silver chloride with metallic silver. Differently to the cases (i)-(iii) these electrodes are much less sensitive to the influence of redox and pH interferences. This arrangement has been also characterized using electrochemical impedance spectroscopy and chronopotentiometry.     

Electrochemistry of conductive polymers 39. Contacts between conducting polymers and noble metal nanoparticles studied by current-sensing atomic force microscopy

Electrical properties of contacts formed between conducting polymers and noble metal nanoparticles have been examined using current-sensing atomic force microscopy (CS-AFM). Contacts formed between electrochemically prepared pi-conjugated polymer films such as polypyrrole (PPy), poly(3-methylthiophene) (P3MeT), as well as poly(3,4-ethylenedioxythiophene) (PEDOT) and noble metal nanoparticles including platinum (Pt), gold (Au), and silver (Ag) have been examined. The Pt nanoparticles were electrochemically deposited on a pre-coated PPy film surface by reducing a platinum precursor (PtCl62-) at a constant potential. Both current and scanning electron microscopic images of the film showed the presence of Pt islands. The Au and Ag nanoparticles were dispersed on the P3MeT and PEDOT film surfaces simply by dipping the polymer films into colloid solutions containing Au or Ag particles for specified periods (5 to approximately 10 min). The deposition of Au or Ag particles resulted from either their physical adsorption or chemical bonding between particles and the polymer surface depending on the polymer. When compared with PPy, P3MeT and PEDOT showed a stronger binding to Au or Ag nanoparticles when dipped in their colloidal solutions for the same period. This indicates that Au and Ag particles are predominantly linked with the sulfur atoms via chemical bonding. Of the two, PEDOT was more conductive at the sites where the particles are connected to the polymer. It appears that PEDOT has better aligned sulfur atoms on the surface and is strongly bonded to Au and Ag nanoparticles due to their strong affinity to gold and silver. The current-voltage curves obtained at the metal islands demonstrate that the contacts between these metal islands and polymers are ohmic.     

Water‐Assisted Vapor Deposition of PEDOT Thin Film

The synthesis and characterization of poly(3,4‐ethylenedioxythiophene) (PEDOT) using water‐assisted vapor phase polymerization (VPP) and oxidative chemical vapor deposition (oCVD) are reported. For the VPP PEDOT, the oxidant, FeCl₃, is sublimated onto the substrate from a heated crucible in the reactor chamber and subsequently exposed to 3,4‐ethylenedioxythiophene (EDOT) monomer and water vapor in the same reactor. The oCVD PEDOT was produced by introducing the oxidant, EDOT monomer, and water vapor simultaneously to the reactor. The enhancement of doping and crystallinity is observed in the water‐assisted oCVD thin films. The high doping level observed at UV–vis–NIR spectra for the oCVD PEDOT, suggests that water acts as a solubilizing agent for oxidant and its byproducts. Although the VPP produced PEDOT thin films are fully amorphous, their conductivities are comparable with that of the oCVD produced ones.

     

Surface-enhanced Raman scattering of EDOT and PEDOT on silver and gold nanoparticles

Surface-enhanced Raman scattering (SERS) spectra of the conducting polymer poly(3,4-ethylenedioxythiophene) (PEDOT) and its monomer 3,4-ethylenedioxythiophene (EDOT) on Ag and Au nanoparticles presenting different morphologies and stabilizing agents have been obtained using the excitation radiation at 633 nm. The SERS spectra of the monomer and polymer are strongly dependent both on the metal and capping agent of the substrate. SERS spectra of EDOT on Au nanospheres indicates that adsorption occurs with the thiophene ring perpendicular to the metal surface. In contrast, polymerization takes place on the silver surface of Ag nanospheres. EDOT adsorption on Ag nanoprisms with polyvinylpyrrolidone (PVP) as capping agent occurs similarly to that observed on gold. Surface-enhanced resonance Raman scattering (SERRS) spectra of PEDOT on gold nanostars that present a thick layer of PVP show no chemical interaction of PEDOT with the metal surface; however, when PEDOT is adsorbed on citrate stabilized gold nanospheres, the SERRS spectra suggest that thiophene rings are perpendicular to the surface. Oxidation of PEDOT also is observed on Ag nanospheres. The investigation of the interface between PEDOT and metal surface is crucial for the development in polymer-based optoelectronic devices since this interface plays a crucial role in their stability and performance.     

反向胶束法制备聚3,4-乙烯二氧噻吩纳米粒子的光电性能和热稳定性

采用聚合和掺杂同时进行的反向胶束体系制备了粒径分散较小的聚3,4-乙烯二氧噻吩(PEDOT)纳米粒子, 利用紫外-可见光光谱(UV-Vis)、X射线衍射(XRD)和扫描电子显微镜(SEM)等分析方法对纳米粒子进行了表征. 实验结果发现, 氧化剂用量、超声处理、聚合温度及掺杂程度对PEDOT纳米粒子的形貌、电性能及热稳定性有不同程度的影响. 根据实验结果对反向胶束法制备PEDOT纳米粒子过程进行优化发现, 在PEDOT纳米粒子聚合过程中, 甲基苯磺酸有效掺杂浓度约为0.17 mol/L时, PEDOT链的取向最规则, 在6.7°, 12.7°, 25°出现衍射峰, 掺杂剂的有效掺杂使得纳米粒子中分子链的取向不同, 并可以获得较高的电导率(>100 S/cm)的PEDOT纳米粒子, 当粒子的尺寸小于20 nm后电导率降低; 热失重法(TG)分析结果表明, PEDOT纳米粒子的热稳定性比普通块材好, 掺杂剂浓度对纳米粒子的热稳定性有一定影响.     

Metal-like Charge Transport in PEDOT(OH) Films by Post-processing Side Chain Removal from a Soluble Precursor Polymer

Herein, a route to produce highly electrically conductive doped hydroxymethyl functionalized poly(3,4-ethylenedioxythiophene) (PEDOT) films, termed PEDOT(OH) with metal-like charge transport properties using a fully solution processable precursor polymer is reported. This is achieved via an ester-functionalized PEDOT derivative [PEDOT(EHE)] that is soluble in a range of solvents with excellent film-forming ability. PEDOT(EHE) demonstrates moderate electrical conductivities of 20–60 S cm⁻¹ and hopping-like (i.e., thermally activated) transport when doped with ferric tosylate (FeTos₃). Upon basic hydrolysis of PEDOT(EHE) films, the electrically insulative side chains are cleaved and washed from the polymer film, leaving a densified film of PEDOT(OH). These films, when optimally doped, reach electrical conductivities of ≈1200 S cm⁻¹ and demonstrate metal-like (i.e., thermally deactivated and band-like) transport properties and high stability at comparable doping levels.     

Ritter Reactions between Alcohols and Acetonitrile Mediated by the Conducting Polymer Poly-(3,4-ethylenedioxy Thiophene) (PEDOT)

Herein, we report new reactivity of the conducting polymer, poly-(3,4-ethylenedioxy thiophene) (PEDOT), where PEDOT mediates a Ritter reaction between alcohols and acetonitrile. The yields were variable and in most cases competitive with results obtained using sulfuric acid. Attempts at a stoichiometric reaction between benzonitrile and diphenylmethanol are also reported herein. Finally, described here are preliminary mechanistic studies that suggest PEDOT is behaving as an alcohol-selective or specific Lewis acid.

Supplementary materials are available for this article. Go to the publisher's online edition of Synthetic Communications® for full experimental and spectral details.     

Biomimetic Synthesis of Water Soluble Conductive Polypyrrole and Poly(3,4‐Ethylenedioxythiophene)

Abstract

A novel biomimetic method for the synthesis of conducting molecular complexes of polypyrrole (PPYR) and poly(3,4‐ethylenedioxythiophene) (PEDOT) in the presence of a polyelectrolyte, such as polystyrene sulfonate (SPS) is presented. A poly(ethylene glycol) modified hematin (PEG‐Hematin) was used to catalyze the polymerization of pyrrole (PYR) and 3,4‐ethylenedioxythiophene (EDOT) in the presence of SPS to form PPYR/SPS and PEDOT/SPS complexes. UV‐VIS, FT‐IR, and electrical conductivity studies for all complexes indicated the presence of a stable and electrically conductive form of these polymers. Furthermore, the presence of SPS in this complex provides a unique combination of properties such as processability and water‐solubility.     

Cyclopenta[c]selenophene based cooligomers and their polymers: comparative study with thiophene analogues

Selenophene and thiophene capped cyclopenta[c]selenophenes were synthesized and characterized. Crystal structure determination of some representative compounds revealed that the substitution at 3,4-position in the form of cyclopentane ring of selenophene or thiophene does not make any significant twist in the trimer backbone, making the cooligomer nearly planar. All the cooligomers were electrochemically polymerized and compared with thiophene capped cyclopenta[c]thiophene polymer. DFT calculations predict that the cyclopentane substitution on the third repeating unit (and in general) of one dimensional polymer neither disturb the planarity nor causes any significant twist on the polymeric backbone unlike the 3,4-dialkyl substitution. The electrochemically prepared selenophene based polymers showed low band gap compared to that of thiophene analogues. Cyclopentane substitution on selenophene as well as thiophene makes the resulting polymer oxidatively more stable when compared to more familiar poly-ethylenedioxythiophene (PEDOT) or poly-ethylenedioxyselenophene (PEDOS) systems. Alternate polymers of cyclopenta[c]selenophenes (CPS)/cyclopenta[c]thiophene (CPT) and thiophene/selenophene possess the energy of HOMO and LUMO significantly lower than that of homopolymers of CPS and CPT, however, possess higher band gap than PCPS.     

Electrochemical polymerization of substituted thiophenes

The electrochemical polymerization of 3-(n-butyl)thiophene and of several 3- or 3,4- substituted α, α'-terthienyls is described and the properties of the conducting polymers are discussed. A solution in acetonitrile of the terthienyl substituted by a potassium propylsulfonate group is polymerizable as such, and the polymer is the first proven example of a self-doped conducting polymer. This polymer dissolves readily in water and remains partially self-doped in solution.     

An Alternative Anionic Polyelectrolyte for Aqueous PEDOT Dispersions: Toward Printable Transparent Electrodes

Organic conducting polymers are promising electrode materials for printable organic electronics. One of the most studied conducting polymers is PEDOT:PSS, which is sufficiently conductive and transparent, but which shows some drawbacks, such as hygroscopicity and acidity. A new approach to stabilize PEDOT in aqueous dispersions involves the replacement of PSS with a basic polyanion based on a polystyrene backbone with (trifluoromethylsulfonyl)imide (TSFI) side groups. The PEDOT:PSTFSIK dispersions were obtained by oxidative polymerization of EDOT in an aqueous PSTFSIK solution and were characterized with regard to their composition, morphology, doping, rheological behavior, and optoelectronic performance. The PEDOT:PSTFSIK dispersions showed excellent printability and good optoelectronic performance (238 Ohm sq^?1 at 91 % transmittance, σ>260 S cm^?1) and were successfully integrated as flexible electrodes in OLED and OPV devices.     

Radiation‐Induced Synthesis of Nanostructured Conjugated Polymers in Aqueous Solution: Fundamental Effect of Oxidizing Species

Synthesis of conjugated poly(3,4‐ethylenedioxythiophene) (PEDOT) polymers is achieved through the radiolysis of N₂O‐saturated aqueous solutions of 3,4‐ethylenedioxythiophene by using two different oxidizing species: HO^. (hydroxyl) and N₃^. (azide) radicals. Both oxidative species lead to self‐assembled polymers that are evidenced in solution by cryotransmission electron microscopy and UV/Vis absorption spectroscopy and, after centrifugation and deposition, by scanning electron microscopy and attenuated total reflectance FTIR techniques. Whereas HO^. radicals lead to PEDOT‐OH globular nanostructures with hydrophilic properties, N₃^. radicals enable the formation of amphiphilic PEDOT‐N₃ fibrillar nanostructures. These results, which highlight the differences in the intermolecular interaction behaviors of the two kinds of PEDOT polymers, are discussed in terms of polymerization mechanisms.